DE3408237A1 - Process for improving the workability of luminous substances - Google Patents

Process for improving the workability of luminous substances

Info

Publication number
DE3408237A1
DE3408237A1 DE19843408237 DE3408237A DE3408237A1 DE 3408237 A1 DE3408237 A1 DE 3408237A1 DE 19843408237 DE19843408237 DE 19843408237 DE 3408237 A DE3408237 A DE 3408237A DE 3408237 A1 DE3408237 A1 DE 3408237A1
Authority
DE
Germany
Prior art keywords
phosphor
suspension
hydroxide
ultrasound
improving
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE19843408237
Other languages
German (de)
Inventor
Kanagaratnam 7915 Elchingen Anandasivam
Klaus 7900 Ulm Gerland
Irene 7958 Laupheim Kienle
Rainer 7910 Neu-Ulm Kolbeck
Ulrich 7900 Ulm Kube
Volker 7910 Neu-Ulm Sonntag
Hermann Dr. 7900 Ulm Widmann
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Licentia Patent Verwaltungs GmbH
Original Assignee
Licentia Patent Verwaltungs GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Licentia Patent Verwaltungs GmbH filed Critical Licentia Patent Verwaltungs GmbH
Priority to DE19843408237 priority Critical patent/DE3408237A1/en
Publication of DE3408237A1 publication Critical patent/DE3408237A1/en
Withdrawn legal-status Critical Current

Abstract

A process using ultrasound and simultaneous stirring is proposed, in which a luminous substance is deagglomerated and simultaneously improved with respect to its pourability by coating with a phosphate, oxide or hydroxide.

Description

BesclireibungDescription

Verfahren zum Verbessern der Verarbeitbarkeit von Leuchtstoffen Die vorliegende Erfindung betrifft ein Verfahren zum Verbessern der Verarbeitbarkeit von pulverförmigen Leuchtstoffen.Method for improving the processability of phosphors Die The present invention relates to a method of improving processability of powdered phosphors.

Käufliche Leuchtstoffe liegen zum größten Teil als Agglomerate vor und sind in diesem Zustand im allgemeinen nicht ohne weiteres zu verarbeiten. Durch Mahlvorgä.lg4 in Kugelmühlen und dergleichen lassen sich zwar die Agglomerate darill zerschlagen, jedoch wird dadurch ein Teil der Leucht stoffkörner in ihrem Kristallgefüge beschädigt, wodurch die Helligkeit der Leuchtstoffe nachläßt.Commercially available phosphors are for the most part in the form of agglomerates and are generally not easy to process in this state. By Mahlvorgä.lg4 in ball mills and the like, the agglomerates can be darill smashed, however, part of the phosphor grains in their crystal structure damaged, whereby the brightness of the phosphors decreases.

Der vorliegenden Erfindung liegt die Aufgabe zugrunde, ein Verfahren anzugeben, mit dessen Hilfe die Verarbeitbarkeit von käuflich erworbenen Leuchtstoffen wesentlich verbessert wird.The present invention is based on the object of a method indicate, with the help of which the processability of commercially acquired phosphors is significantly improved.

Die Aufgabe wird gemäß der Erfindung dadurch gelöst, daß der leuchtstoff ii wässeriger Suspension zunacht bei glei.chzeitigem Rühren mit Ultraschall beschallt wird, daß daiiii der Suspension eie anorganische Verbindung zugesetzt wird, die ein an die Oberfläche der Leuchtstoffkörner anlegbares und die Rieselfähigkeit verbesserndes Salz, Flytll.oxyd oder Oxyd abspaltet, daß dann die Suspension erneut: bei gleichzeitiger Beschallung mit Ultraschall gerührt wird und daß dann der Leuchtstoff filtriert, gewaschen und getrocknet wird.The object is achieved according to the invention in that the phosphor ii aqueous suspension first sonicated with simultaneous stirring with ultrasound is that daiiii the suspension an inorganic compound is added which one that can be applied to the surface of the phosphor grains and that improves the flowability Salt, Flytll.oxyd or Oxyd split off that then the suspension again: at the same time Sonication is stirred with ultrasound and that the phosphor is then filtered, washed and dried.

Durch das beschri ebene Verfahren 1 bei dem gleichzeitig ein Rühren und eine Ultraschallbehandlung erfolgt, wird eine äußest gründliche Doglomeri.sation des Leuchtstoffes bewii'kt:. Gleichzeitig wird durch das beschriebene Verfahren der Leuchtstoff mit einer Substanz ummantelt, die ihn verbessert rieselfähig macht, was insofern vorteilhaft ist, als dieser so bearbeitete Leuchtstoff auch bei längerer Lagerung nicht mehr dazu neigt, erneut Agglomerate zu bilden. Durch die nochmalige Anwendung von Ultraschall bei gleichzeitigem Rühren wird darüberhinaus eine äußerst haftfeste Ummantelung erreicht, die auch bei ggf. später notwendigen Wiedergewinnungsverfahren nicht von den Leucht stoffkörnern heruntergewaschen wird.By the described method 1 with the simultaneous stirring and ultrasound treatment is carried out, an extremely thorough doglomerization is required of the phosphor causes :. At the same time, the method described the luminescent material is coated with a substance that makes it more free-flowing, which is advantageous insofar as this luminescent material processed in this way is also used for a longer period of time Storage no longer tends to re-agglomerate. Through the repeated Moreover, application of ultrasound while stirring becomes extreme Adhesive coating achieved, which may also be necessary later in the recovery process is not washed down by the phosphor grains.

Anhebt des nachfolgenaen Ausführungsbeispiels wird die Erfindung näher erläutert.The invention becomes more detailed when the following exemplary embodiment is raised explained.

Gemäß einem bevorzugten Ausführungsbeispiel wird der Leuci>tstoff zunächst im Wasser aufgeschlämmt und in einem Ultraschallbad bei gleichzeitigem Rühren beschallt. Nach Zugabe von Kaliwasserglas z. B. wird kurzzeitig unter gleichzeitigem Rühren nochmals mit Ultrasc.;« beschallt.According to a preferred embodiment, the leucite is used first slurried in water and in an ultrasonic bath at the same time Stir sonicated. After adding potassium water glass z. B. is briefly under simultaneous Stirring again with Ultrasc .; «sonicated.

Ansclaließend wird SiO2 nach Zugabe von Alkohol bei erneuter IllEraschallbehandlung und gleichzeitigem Rühren auf die Oberfläche der einzelnen Leuchtstoffkörner gefällt.Then SiO2 becomes after adding alcohol with renewed ultrasonic treatment and simultaneous stirring on the surface of the individual phosphor grains.

Der so behandelte Leuchtstoff wird anschließend filtriert, gew.i:;cllen, mit Alkohol nachgewaschen und getrocknet. Man erhäl.t auf diese Weise einen mit Siliziumoxyd ummantelten Leuchtstoff, der äußerst rieselfähig ist und sich sehr gut weiterverarbeiten läßt. Die Weiterverarbeitung besteht tibewiegend darin, daß der Leuchtstoff nachirgend einem bekannten Verfahren auf die innere Oberfläche eines Leucht schirmträgers einer Kathodenstrahlröhre aufgebracht wird.The phosphor treated in this way is then filtered, wt. washed with alcohol and dried. This way you get one with Silicon oxide coated phosphor, which is extremely free flowing and very can be processed well. The further processing consists mainly in that the phosphor on the inner surface of a by any known method Luminous screen carrier of a cathode ray tube is applied.

Mit dem beschriebenen Verfahren können in gleicher Weise auch andere Ummantelungen der Leuchtstoffkörner erzielt werden, indem anstelle von Kaliwasserglas andere anorganische chemische Verbindungen zugesetzt werden, die dann zur Abfiltrierung und Anlagerung von Phosphaten, wie z. B.Others can use the described method in the same way Coating of the phosphor grains can be achieved by using instead of potassium silicate other inorganic chemical compounds are added, which are then filtered off and accumulation of phosphates, such as. B.

Zirkonphosphat oder aber zur Anlagerung von Hydroxyden, wie z.B. von Magnesiumhydroxyd, Yttriumhydroxyd, Berilliumnyaroxyd oder Aluminiumhydroxyd führen.Zirconium phosphate or for the addition of hydroxides, such as Magnesium hydroxide, yttrium hydroxide, beryllium oxide or aluminum hydroxide lead.

Das beschriebene Verfahren zur Verbesserung der Verarbeitbarkeit von Leuchtstoffen, insbesondere für Kathodenstrahl röhren, ist für nahezu alle Leuchtstoffe geeignet, insbesondere auch für solche, die verhältnismäßig empfindlich sind. Besonders vorteilhaft ist das Ummanteln mit Phosphaten, wodurch nicht nur die Verarbeitbarkeit verbessert wird, sondern auch die Einbrennfestigkeit der Leuchtstoffe wesentlich erhöht wird.The method described to improve the processability of Phosphors, especially for cathode ray tubes, are used for almost all phosphors suitable, especially for those who are relatively sensitive. Particularly The coating with phosphates is advantageous, which not only improves the processability is improved, but also the stoving resistance of the phosphors is significantly is increased.

Claims (3)

Patentansprüche 1. Verfahren zum Verbessern der Verarbeitbarkeit von pulverförmigen Leuchtstoffen, dadurch gekennzeichnet, daß der leuchtstoff i wässeriger Suspension zunächst bei gleichzeitigem Rühren mit Ultraschall beschallt wird, daß danii der Suspension eine anorganische Verbindung zugesetzt wird, die ein an die Oberfläche der Leuchtstoffkörner anlegbares und die Rieselfähigkeit verbesserndes Salz, Hydroxyd oder Oxyd abspaltet, daß dann die Suspension erneut bei gleichzeitiger Beschallung mit Ultraschall gerührt wird und daß dann der Leuchtstoff filtriert, gewaschen und getrocknet wird.Claims 1. A method for improving the processability of pulverulent phosphors, characterized in that the phosphor is aqueous Suspension is first sonicated while stirring with ultrasound that danii the suspension an inorganic compound is added to the Surface of the phosphor grains that can be laid on and that improves the flowability Salt, hydroxide or oxide splits off, that then the suspension again at the same time Sonication is stirred with ultrasound and that the phosphor is then filtered, washed and dried. 2. Vorfahren nach Anspruch 1, dadurch gekennzeichnet, daß an die Oberfläche der Leuchtstoffkörner Siliziumoxyd (SiO), Zirkonphosphat, Magnesiumhydroxyd (Mg(OH)2), Yttriumhyaroxyd (Y(OH)3), Berilliumhydroxyd (Be(OH)2) oder Aluminiumhydroxyd (A1(OH)3) oder dergleichen angelagert wird.2. Ancestors according to claim 1, characterized in that on the surface the phosphor grains silicon oxide (SiO), zirconium phosphate, magnesium hydroxide (Mg (OH) 2), Yttrium hyaroxide (Y (OH) 3), beryllium hydroxide (Be (OH) 2) or aluminum hydroxide (A1 (OH) 3) or the like is deposited. 3. Verfahren nach Anspruch 1 oder Anspruch 2, dadurch gekennzeichnet, daß zur Anlagerung von Siliziumoxyd (SiO2) der Suspension Kaliwassergias zugesetzt wird und das SiO2 nacli Zugabe von Alkohol auf die Oberfläche der Leuchtstoffkörner gefällt wird.3. The method according to claim 1 or claim 2, characterized in that that for the addition of silicon oxide (SiO2) to the suspension Kaliwassergias was added and the SiO2 after adding alcohol to the surface of the phosphor grains is felled.
DE19843408237 1984-03-07 1984-03-07 Process for improving the workability of luminous substances Withdrawn DE3408237A1 (en)