DE3323133A1 - Emulsion paints - Google Patents
Emulsion paintsInfo
- Publication number
- DE3323133A1 DE3323133A1 DE19833323133 DE3323133A DE3323133A1 DE 3323133 A1 DE3323133 A1 DE 3323133A1 DE 19833323133 DE19833323133 DE 19833323133 DE 3323133 A DE3323133 A DE 3323133A DE 3323133 A1 DE3323133 A1 DE 3323133A1
- Authority
- DE
- Germany
- Prior art keywords
- dispersion
- emulsion paint
- water
- solution
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
DispersionsfarbeEmulsion paint
Die'· vorliegende Erfindung betrifft eine Dispersionsfarbs für Innen- und Außenanstriche.The present invention relates to a disperse paint for interior and exterior paints.
Die bisher bekannten Dispersionsfarben bzw. Dispersionsanstriche haben den Nachteil, daß sie einen ungenügenden Schutz gegen äußere Einflüße bieten, uenn sie aufgetragen sind. Auch ist ihre thermische und/oder akustische Isolierfähigkeit in vielen Fällen ungenügend. Ueiterhin fehlen ihnen die gewünschten Auftragungseigenschaften und auch Eigenschaften im aufgetragenen Zustand in verschiedenen Anwendungsbereichen. So entspricht auch ihre Standfestigkeit nicht in allen Fällen den an Dispersionsfarben gestellten Anforderungen.The previously known emulsion paints or emulsion paints have the disadvantage that they are insufficient Provide protection against external influences when they are applied. Also their thermal and / or acoustic insulation capacity in many cases insufficient. Furthermore, they lack the desired application properties and properties when applied in various areas of application. Their stability does not always correspond to that of emulsion paints Requirements.
Es ist daher die Aufgabe der vorliegenden Erfindung eine Dispersionsfarbe ohne die vorstehend aufgezeigten Nachteile zuschaffen, welche die Anforderungen als Innen- und Außenanstrich erfüllen soll.It is therefore the object of the present invention to provide an emulsion paint without the disadvantages indicated above create, which should meet the requirements as an interior and exterior paint.
Diese Aufgabe wird für die Dispersionsfarbe der eingangs genannten Art erfindungsgemäß dadurch gelöst, daß sie auf der Basis von Uasser vorliegt und in einer in Uasser dispergierbaren Grunddispersion mindestens Methylcellulose, Acryldispersion und Glykol sowie Pigment und Additive enthält.This object is achieved according to the invention for the emulsion paint of the type mentioned in that it has the base of water is present and is dispersible in water Basic dispersion at least methyl cellulose, acrylic dispersion and glycol as well as pigment and additives.
In vorteilhafter Ueise ist die Dispersionsfarbe nach der Erfindung mit ihren Bestandteilen in Uasser dispergiert, wobei das Uasser ein wohlfeiles Dispersionsmittel darstellt. Auf Grund der Bestandteile der Grunddispersion, die vorzugsueise als Kunststoffdispersion bezeichnet werden kann, kann mit der Dispersionsfarbe nach der Erfindung ein Dispersionsanstrich erreicht werden, der den Uünschen nach einer thermischen und/oder akustischen Isolierung entspricht. In vorteilhafter Ueise liegt eine Kombination aus der synthetisches Kunstharz, d.h. die Acrylkomponente enthaltenden Grunodispersion und dem Pigment vor, was einen breiten Anwendungsbereich der Dispersionsfarbe zuläßt. Dieser läßt sich durch Auswahl der entsprechenden Additive erweitern.Advantageously, the emulsion paint is after of the invention dispersed with their constituents in water, the water being an inexpensive dispersant. Due to the constituents of the basic dispersion, the preferred can be referred to as a plastic dispersion, a dispersion paint can be achieved with the emulsion paint according to the invention, which the desires for a thermal and / or acoustic insulation. A combination of the synthetic is advantageous Synthetic resin, i.e. the green dispersion containing the acrylic component and the pigment, which allows the emulsion paint to be used in a wide range of applications. This can be done by selection the corresponding additives.
So kann die Grunddispersion bzw. die Dispersionsfarbe ein Pigment, vorzugsweise aus einem anorganischen Material enthalten. Als Pigment kann Titanoxid, vorzugsweise in Form von Rutil, und/oder Sand, ζ.B. Quarzsand, vorliegen. Der Dispersionsfarbe können Entschäumungsmittel zugesetzt sein. Ueiterhin kann die Dispersionsfarbe bzw. die Grunddispersion Fungizide und/oder Ueichmacher und/oder Natriumphosphat und/oder Karbonat und/oder ein Benetzungsmittel enthalten. Vorzugsweise liegt die Grunddispersion als Pulver vor, das in Uasser dispergiert ist bzw. in diesem dispergiert werden kann.So the base dispersion or the emulsion paint can be a Pigment, preferably made of an inorganic material. Titanium oxide, preferably in the form of Rutile, and / or sand, ζ.B. Quartz sand. The emulsion paint defoaming agents can be added. Furthermore the emulsion paint or the base dispersion can be fungicides and / or leveling agents and / or sodium phosphate and / or Contain carbonate and / or a wetting agent. The basic dispersion is preferably in the form of a powder that is contained in Uasser is dispersed or can be dispersed in this.
Die nethylcellulose kann als Carboxymethylcellulose vorliegen. Es kann aber auch Propylmethylcellulose verwendet werden. Uorteilhaft werden vorzugsweise 3% an Methylcellulose eingesetzt. Glykol wird vorzugsweise als Ä'thylenglykol eingesetzt.The ethyl cellulose can be in the form of carboxymethyl cellulose. However, propylmethyl cellulose can also be used. Advantageously, 3% methyl cellulose is preferably used. Glycol is preferably used as the ethylene glycol.
Ueitere vorteilhafte Ausführungsformen der Dispersionsfarbe nach der Erfindung können mit den Merkmalen der Ansprüche 2 bis 6 erreicht werden. In bevorzugten Ausführungsformen liegen die Bestandteile nach den Ansprüchen 3 und/oder 5 vor.Other advantageous embodiments of the emulsion paint according to the invention can have the features of the claims 2 to 6 can be achieved. In preferred embodiments, the components are according to claims 3 and / or 5 before.
Die Erfindung ist nachstehend in Ausführungsbeispielen näher erläuteret.The invention is illustrated below in exemplary embodiments explained in more detail.
Es wurden nachfolgende Komponenten und deren Mengen in Kilogramm in Uasser zu einer Dispersionsfarbe angesetzt:The following components and their quantities in kilograms in water were used to make an emulsion paint:
Uasser 7,500Uasser 7,500
Natriumhexametaphosphat als 10^-ige LösungSodium hexametaphosphate as a 10 ^ solution
nethylcellulose Kulminal 6000 Antischaummittel Antifoam L 802 Benetzungsmittel Disperwet CO-76Nethylcellulose Kulminal 6000 antifoam agent Antifoam L 802 Wetting agent Disperwet CO-76
Äthylenglykol, technisch rein Ueichmacher Plasticom Fungizid COCID T-350 Talkum, feinEthylene glycol, technically pure leveler Plasticom Fungicide COCID T-350 Talc, fine
Talkum, grobTalc, coarse
Calciumcarbonat CALCIT,mikrokristallin Acryldispersion UALLPOL A 600 Ammoniak, 24/25^-ige Lösung in Uasser Pigmentfarbe Mandarin, 20^-ige LösungCalcium carbonate CALCIT, microcrystalline Acrylic dispersion UALLPOL A 600 ammonia, 24/25 solution in water Pigment color mandarin, 20% solution
Das Natriumhexmetaphosphat wird als wei3es Pulver eingesetzt mit einem pH-Uert von 7,2 bei einer Konzentration von 2,5 g je Liter Lösung. Die Kulminal-Methylceliulose 6000 ist von der Henkel 4 Cie,AG, CH 4133 Pratteln,Schweiz, erhältlich. Sie kann einen mittleren Polymerisationsgrad von DP 70 - 750, vorzugsweise etwa 500, aufweisen. UALLPOL A 600 kann von der Reichhold Chemie AG, CH 5212 Hausen bei Brugg, bezogen werden. Es ist im Allgemeinen ein Copolymer aus Buthylacrylat und Methacrylat, deren Verhältnis zueinander z.B. von dem jeweils verwendeten Emulgator und/oder dem Bedarf abhängt. Das Calciumcarbonat CALCIT wird mikrokristallin von der S.I.R.F. CALCIT S.R.L., Canevy di Sacile(PN) Ca.p., 33070, Italien, geliefert.The sodium hexmetaphosphate is used as a white powder with a pH of 7.2 at a concentration of 2.5 g per liter of solution. The Kulminal Methylceliulose 6000 is from Henkel 4 Cie, AG, CH 4133 Pratteln, Switzerland. It can have an average degree of polymerization of DP 70-750, preferably about 500. UALLPOL A 600 can be used from from Reichhold Chemie AG, CH 5212 Hausen near Brugg. It is generally a copolymer of buthylacrylate and methacrylate, the ratio of which depends, for example, on the particular emulsifier used and / or the need. The calcium carbonate CALCIT is microcrystalline from the S.I.R.F. CALCIT S.R.L., Canevy di Sacile (PN) Ca.p., 33070, Italy, delivered.
Auch'in den nachfolgenden Beispielen wurde die Methylcallulose Kuiminal 6000 in einer Lösung von 10% Kuliminal 6000 auf 100 1 Uasser angesetzt.In the following examples, too, the methylcallulose Kuiminal 6000 was made up in a solution of 10% Kuliminal 6000 to 100 liters of water.
Die Pigmantfarbe Mandarin besau die folgende Zusammensetzung(Mengen in Kilogramm):The pigment color mandarin has the following composition (quantities in kilograms):
S-S-
Methylcellulose Kulminal 6D00 12,600Methyl cellulose Kulminal 6D00 12,600
Ueichmachsr Plasticom 1,900Verified Plasticom 1.900
Äthylenglykol, technisch rein 1,900Ethylene glycol, technically pure 1,900
Bamax 6,500Bamax 6,500
Diorin 6,500Diorin 6,500
Eisenoxidgelb (Firma Vogel, Zürich) 6,500Iron oxide yellow (Vogel, Zurich) 6.500
Rutil 3,800Rutile 3,800
Kaolin 34,800Kaolin 34,800
Colanylgelb 20,000Colanyl Yellow 20,000
Die Komponenten Bamax und Diorin sind von der Suaercolori
S.A., Mailand, Italien, erhältlich, und Rutil
(Titanoxid), Kaolin und das Colanylgelb sind durch die Firma Plüss-Stauffer Ag, CH 4665 Oftringen,zu erhalten.The components Bamax and Diorin are available from Suaercolori SA, Milan, Italy, and rutile
(Titanium oxide), kaolin and Colanyl yellow are available from Plüss-Stauffer Ag, CH 4665 Oftringen.
Ein Polystyrol-Baukleber enthielt als Bindemittsileim ; verseifungsbeständige Kunststoffdispersion mit den nachfol-. genden Komponenten und deren Mengen in Kilogramm:A polystyrene construction adhesive contained glue as a bonding agent; saponification-resistant plastic dispersion with the following. The following components and their quantities in kilograms:
Uasser 10,0GOUasser 10.0GO
Kulminal Methylcellulose 6000 0,210Kulminal methyl cellulose 6000 0.210
Acryldispersion UALLPOL A 600 12Acrylic dispersion UALLPOL A 600 12
Uasser 1,7501.750
Entschaumungsmittel Antifoam L-802 0,009 Leophen (Firma Bayer AG, Zürich,Schweiz) 0,0C6Defoamer Antifoam L-802 0.009 Leophen (Bayer AG, Zurich, Switzerland) 0.0C6
Alkohol, denaturiert 0,705Alcohol, denatured 0.705
Propylenglykol 0,7OSPropylene glycol 0.7OS
Karbonat CALCIT 5,750Carbonate CALCIT 5,750
Sand 76Sand 76
Shellsol A (Shell-Suitzerland,Zürich) 0,100Shellsol A (Shell-Switzerland, Zurich) 0.100
Amm 0,1C0 Arbocel (Firma Emil Ueiss,Basel,Schweiz) 0,600Amm 0.1C0 Arbocel (Emil Ueiss, Basel, Switzerland) 0.600
Ueichrnacher Plasticom 0,500Ueichrnacher Plasticom 0.500
Dieser Dispersion wurden dann 20^ Portlandzement, knötchenfrei, zugemischt. Nach der Zementzugabe konnte cie Masse verarbeitet werden.This dispersion was then 20 ^ Portland cement, free of pebbles, mixed in. After the addition of cement, the mass could are processed.
Die mit Beispiel 1 gleichen Komponenten können von den dort angeführten Firmen bezogen werden. Die anderen Komponenten sind auf dem Mnrkt erhältlich.The same components as in Example 1 can be obtained from the companies listed there. The other components are available on the Mnrkt.
Eine Dispersionsfarbe uurde mit den nachfolgenden Komponenten und deren Mengen in Kilogramm angesetzt:An emulsion paint was made with the following components and their quantities in kilograms:
Pigmentpaste 4,000Pigment paste 4,000
Acryldispersion UALLPOL A 600 13,000Acrylic dispersion UALLPOL A 600 13,000
Titanoxid . 3,500Titanium oxide. 3,500
Karbonat CALCIT 7,000Carbonate CALCIT 7,000
gemahlener Marmorstein 71ground marble stone 71
Die Pigmentpaste uar mit den folgenden Komponenten und Mengen in Kilogramm angesetzt:The pigment paste uar with the following components and Quantities in kilograms:
UasserUasser
Methylcellulose Kulminal 20'0OO Natriumhexametyphqsphat, Pulver Fungizid COCID T-350Methyl cellulose Kulminal 20'0OO Sodium hexametyphqsphat, powder fungicide COCID T-350
Entschäumungsmittel Antifoam L-B02 Benetzungsmittel Disperuet CO-76 eine Lösung von Lapponit in Uasser UasserDefoaming agent Antifoam L-B02 wetting agent Disperuet CO-76 a solution of lapponite in Uasser Uasser
LapponitLapponite
Ä'tylenglykol, technisch rein Ammoniaklösung, 24/25$Ethylene glycol, technically pure ammonia solution, $ 24/25
■ Die Komponente Lapponit ist von der Plüss-Stauffer AG, CH 4665 Oftringen, erhältlich. Zur Herkunft der anderen Komponenten, auch derjenigen der Dispersionsmischung uird auf Beispiel 1 veruiesen.■ The component Lapponit is from Plüss-Stauffer AG, CH 4665 Oftringen, available. About the origin of the other components, including those of the dispersion mixture refer to example 1.
Eine Dispersionsfarbe uurde aus den nachfolgenden Bestandteilen und deren Mengen in Kilogramm angesetzt:An emulsion paint was made from the following ingredients and their quantities in kilograms:
Uasser 100,000Uasser 100,000
Methylcellulose Kulminal 6000 2,100Methyl cellulose Kulminal 6000 2.100
Natriumhexmetaphosphat in Lösung (10$) 7,000Sodium Hexmetaphosphate in Solution ($ 10) 7,000
Entschäumungsmittel Antifoam L-802 1,000Defoaming agent Antifoam L-802 1,000
Fungizid -.COCID T-35*0 0,800Fungicide -.COCID T-35 * 0 0.800
Benetzungsmittel Disperuet CI-76 2,100Wetting agent Disperuet CI-76 2.100
Ätylenglykol, technisch rein 3,100Ethylene glycol, technically pure 3.100
Weichmacher Plasticom 1,400Plasticizer Plasticom 1,400
Titanoxid als Rutil No 376 75,000Titanium oxide as rutile No 376 75,000
Kaolin 14,000Kaolin 14,000
Talkum, grob . 14,000Talc, coarse. 14,000
Karbonat, mikrokristallin 105,000Carbonate, microcrystalline 105,000
Acryldispersion UALLPOL A 600 196,000Acrylic dispersion UALLPOL A 600 196,000
Quarzsand, Reibungspunkt 16.000 300,000Quartz sand, friction point 16,000 300,000
Ammoniak in wässriger Lösung 24/25$ 0,800Ammonia in Aqueous Solution 24/25 $ 0.800
Shellsol A (Shell-Suitzerland,Zürich) 2,500Shellsol A (Shell-Switzerland, Zurich) 2,500
Zur Herkunft der einzelnen Bestandteile wird wiederum auf Beispiel 1 verwiesen. Auch bei dieser Dispersionsfarbe liegt eine Kombination aus einer Emulsion eines synthetischen Harzes (Kunstharz) und einem Edelpigment und hochreinem Quarzsand vor, d.h.Pigmenten, die unveränderlich und daher für die Dispersionsfarbe bzu. den Dispersionsanstrich von Vorteil sind.For the origin of the individual components, refer to Example 1 referenced. This emulsion paint is also a combination of an emulsion of a synthetic resin (Synthetic resin) and a noble pigment and high-purity quartz sand, i.e. pigments that are immutable and therefore for the Emulsion paint bzu. the dispersion coating is an advantage are.
Eine Dispersionsfarbe enthielt die nachfolgend aufgeführten Komponenten und deren Mengen in Kilogramm:An emulsion paint contained the following components and their quantities in kilograms:
Wasser 260,000Water 260,000
Methylcellulose Kulminal 6000 2,000Methyl cellulose Kulminal 6000 2,000
Lösung von Natriumhexametaphosphat (10$) 3,000Solution of Sodium Hexametaphosphate ($ 10) 3,000
Entschäumungsmittel Antifoam L-802 0,500Defoaming agent Antifoam L-802 0.500
Benetzungsmittel Disperuet CO-76 0,800Wetting agent Disperuet CO-76 0.800
Fungizid COCID T-350 0,600Fungicide COCID T-350 0.600
Äthylenglykol, technisch rein 1,500Ethylene glycol, technically pure 1,500
Weichmacher Plasticom 0,600Plasticizer Plasticom 0.600
Titanoxid-Paste 28,000Titanium Oxide Paste 28,000
Quarzsard, Reibungspunkt 16.000 100,000Quartz sard, friction point 16,000 100,000
Kaolin 50,000Kaolin 50,000
Karbonat, mikrokristallin "Red Line" 50,000Carbonate, microcrystalline "Red Line" 50,000
ι w m « «· t ι wm «« · t
Acryldispersion UALLPOL A 600 160,000Acrylic dispersion UALLPOL A 600 160,000
Ammoniak-Lösung 24/25% 0,500Ammonia solution 24/25% 0.500
Shellsol A ' 2,000Shellsol A '2,000
Das Karbonat "Red Line" ist von der UMBRIA NINERARIA S.p.Α., Mailand, Italien, erhältlich. Zur Herkunft der anderen Bestandteile .uird auf die vorsthenden Beispiele veruiesen. The carbonate "Red Line" is from UMBRIA NINERARIA S.p.Α., Milan, Italy. To the origin of the other Components. Refer to the examples above.
Eine Dispersionsfarbe enthielt die nachfolgenden Komponenten und deren Mengen in Kilogramm:An emulsion paint contained the following components and their quantities in kilograms:
Uasser 165,000Uasser 165,000
Methylcellulose Kulminal 6000 2,550Methyl cellulose Kulminal 6000 2,550
Lösung von Natriumhexametaphosphat (10%) 7,500Solution of sodium hexametaphosphate (10%) 7,500
Benetzungsmittel Disperuet CQ-76 2,250Wetting agent Disperuet CQ-76 2.250
Entschalungsmittel Antifoam L-802 1,400Release agent Antifoam L-802 1,400
Fungizid COCID T-350 0,900Fungicide COCID T-350 0.900
Äthylenglykol, technisch rein 2,250Ethylene glycol, technically pure 2.250
Ueichmacher Plasticom 2,250Verifier Plasticom 2.250
Titanoxid 376 150,000Titanium oxide 376 150,000
Kaolin 37,500Kaolin 37,500
Talkum, grob 37,500Talc, coarse 37,500
Calciumcarbonat CALCIT 75,000Calcium carbonate CALCIT 75,000
Durcal US (Plüsa-Stauffer^H-Oftringen) 75,000Durcal US (Plüsa-Stauffer ^ H-Oftringen) 75,000
■ Acryldispersion .203 200,000■ Acrylic dispersion .203 200,000
Ammoniak-Lösung 1,800Ammonia solution 1,800
Acryldispersion 201 25,000Acrylic Dispersion 201 25,000
Shellsol A - 2,600Shellsol A - 2,600
Tintanoxid 376 kann ebenfalls von der Plüss-Stauffer AG CH 4665 Oftringen, bezogen werden. Die Acrydispersionen und 201 sind von der Reichhold Chemie AG, CH 5212 Hausen bei Brugg erhältlich. Zur Herkunft der übrigen Bestandteile uird auf die vorstehenden Beispiele verwiesen.Tintanoxid 376 can also be obtained from Plüss-Stauffer AG CH 4665 Oftringen. The acrylic dispersions and 201 are from Reichhold Chemie AG, CH 5212 Hausen available from Brugg. For the origin of the other constituents, reference is made to the above examples.
Shellsol A uird als letzte Komponente zugesetzt, uonach die Dispersion gebrauchsfertig ist.Shellsol A is added as the last component, after which the dispersion is ready to use.
Eine Dispersionsfarbe bestand aus den nachfolgend aufgeführten Komponenten und deren Mengen in Kilogramm:An emulsion paint consisted of the following components and their quantities in kilograms:
Wasser · 200,000Water 200,000
Methylcellulose Kulminal 6000 2,800Methyl cellulose Kulminal 6000 2,800
Lösung von Natriumhexametaphosphat (10$) 9,600Sodium hexametaphosphate solution ($ 10) 9,600
Benetzungsmittel Disperuet CO-76 1,600Wetting agent Disperuet CO-76 1,600
Entschäumungsmittel Antifoam LtB02 0,800Defoaming agent Antifoam LtB02 0.800
Fungizid COCID T-350 " 0,800Fungicide COCID T-350 "0.800
Äthylenglykol, technisch rein 2,800Ethylene glycol, technically pure 2,800
Titanoxid G 55,000Titanium oxide G 55,000
Komponente P 820 (Degussa, Zürich) 15,000Component P 820 (Degussa, Zurich) 15,000
Calciumcarbonat CALCIT 150,000Calcium carbonate CALCIT 150,000
Talkum, grob 25,000Talc, coarse 25,000
Calciumcarbonat,Bianco Typ A 250,000Calcium carbonate, Bianco type A 250,000
Acryldispersion UALLPOL A 600 100,000Acrylic dispersion UALLPOL A 600 100,000
Ammoniak-Lösung 1,000Ammonia solution 1,000
Shellsol A (Shell-Suitzerland,Zürich) 1,500Shellsol A (Shell-Switzerland, Zurich) 1,500
Zur Herkunft der einzelnen Bestandteile und ihre
Spezifikatimnen uird auf die vorstehenden Beispiele veruiesen.
The origin of the individual components and their
For specifics, see the examples above.
Eine Dispersionsfarbe enthielt die nachfolgend aufgeführten Komponenten und deren Mengen in Kilogramm:An emulsion paint contained the following components and their quantities in kilograms:
Uasser 70,00070,000
Methylcellulose Kulminal 6000 0,600Methyl cellulose Kulminal 6000 0.600
Lösung von Natriumhexametaphosphat (10$) 8,000Solution of Sodium Hexametaphosphate ($ 10) 8,000
Entschäumungsmittel Antifoam L-802 0,500Defoaming agent Antifoam L-802 0.500
Fungizid COCID T-350 0,700Fungicide COCID T-350 0.700
Benetzungsmittel Disperuet CO-76 0,900Wetting agent Disperuet CO-76 0.900
Lösung von Lapponit 3,600Solution of Lapponite 3,600
Äthylenglykol, technisch rein 1,800Ethylene glycol, technically pure 1,800
Titanoxid G 24,000Titanium oxide G 24,000
Calciumcarbonat, Bianco Typ A 120,000Calcium carbonate, Bianco type A 120,000
Oas in den Beispielen 7 und 8 angeführte Calciumcarbonat, Bianco Typ A kann von der Umbria Mineraria S.p.A., Mailand, Italien, als amorphes Calciumcarbonat bezogen werden. Zur Herkunft der übrigen Bestandteile wird auf die vorstehenden Beispiele verwiesen.The calcium carbonate listed in Examples 7 and 8, Bianco Type A can be purchased from Umbria Mineraria S.p.A., Milan, Italy, as amorphous calcium carbonate. For the origin of the other components, reference is made to the above Examples referenced.
Eine Dispersion3farbe auf der Grundlage eines UeiQers bzu. Weißmachers hatte die nachfolgende Zusammensetzung von Komponenten und deren Mengen in Kilogramm:A dispersion paint based on a UeiQer bzu. Weißmachers had the following composition of components and their amounts in kilograms:
Wasser 200,000Water 200,000
Methocel K4(Firrna DAU, Schueiz) 3,700 Lösung von Natriutnhexametaphosphat (10/ζ) 13,000Methocel K4 (Firrna DAU, Schueiz) 3.700 Solution of sodium hexametaphosphate (10 / ζ) 13,000
BenetzunsmittBl Disperuet CO-76 1,600Wetting agent Disperuet CO-76 1,600
Entschäumungsmittel Antifoam L-802 0,800Defoaming agent Antifoam L-802 0.800
Fungizid COCIO T-350 0,800Fungicide COCIO T-350 0.800
Äthylenglykol, technisch rein 1,500Ethylene glycol, technically pure 1,500
Titanoxid G 25,000Titanium oxide G 25,000
Calciumcarbonat, Bianco A 500,000Calcium carbonate, Bianco A 500,000
Acryldispersion UALLPOL A 600 45,000Acrylic dispersion UALLPOL A 600 45,000
Ammoniak-Lösung 0,700Ammonia solution 0.700
Zur Herkunft der einzelnen Bestandteile, wird auf die vorstehenden Beispiele verwiesen.For the origin of the individual components, reference is made to the referenced above examples.
Eine weiße Oispersionsfarbe hatte die nachfolgende Zusammensetzung und Mengen in Kilgramm:A white emulsion paint had the following composition and quantities in kilograms:
Uasser 210,000Uasser 210,000
Methocel K4 (Firma DAU, Schueiz) 3,700Methocel K4 (DAU, Schueiz) 3.700
Lösung von Natriumhexametaphosphat (10$) 15,000Solution of sodium hexametaphosphate ($ 10) 15,000
Entschäumungsmittel L-802 0,600Defoaming agent L-802 0.600
Fungizid COCID T-350 0,800Fungicide COCID T-350 0.800
Äthylenglykol, technisch rein 3,000Ethylene glycol, technically pure 3,000
Benetzungsmittel Disperuet CO-76 1,000Wetting agent Disperuet CO-76 1,000
Titanoxid G 15,000Titanium oxide G 15,000
Calciumcarbonat, Bianco A 500,000Calcium carbonate, Bianco A 500,000
Acryldispersion UALLPOL A 600 30,000Acrylic dispersion UALLPOL A 600 30,000
Ammoniak-Lösung 0,500Ammonia solution 0.500
Zur Herkunft und Spezifikation der einzelnen Bestandteile uird ' auf die vorstehenden Beispiele verwiesen.About the origin and specification of the individual components Reference is made to the above examples.
Eine Dispersionsfarbe uurde mit den nachfolgend aufgeführten Komponenten und deren Mengen in Kilogramm angesetzt:An emulsion paint was made with the ones listed below Components and their quantities in kilograms:
Uasser 200,000Uasser 200,000
Nethylcellulose Kulminal 6000 3,100 Lösung von Natriumhexametaphosphat (1O?£) 12,000Nethylcellulose Kulminal 6000 3,100 Solution of Sodium Hexametaphosphate (1O? £) 12,000
Entschäumungsmittel Antifoam L-802 1,000Defoaming agent Antifoam L-802 1,000
Ammoniak-Lösung 1,200Ammonia solution 1,200
Titanoxid G 85,000Titanium oxide G 85,000
Kaolin 50,000Kaolin 50,000
Mica 50,000Mica 50,000
Talkum, fein 50,000Talc, fine 50,000
Calciuracarbonat, Bianco A 100,000Calciuracarbonate, Bianco A 100,000
Carbonat CALCIT 100,000Carbonate CALCITE 100,000
Benetzungsmittel Disperuet CO-76 1,600Wetting agent Disperuet CO-76 1,600
Fungizid COCID T-350 0,800Fungicide COCID T-350 0.800
Äthylenglykol, technisch rein 3,200Ethylene glycol, technically pure 3,200
Weichmacher Plasticom 2,000Plasticizer Plasticom 2,000
Acryldispersion UALLPOL A 600 160,000Acrylic dispersion UALLPOL A 600 160,000
Shellsol A 2,000Shellsol A 2,000
Zur Herkunft der einzelnen Bestandteile und ihrer
Spezifikation uird auf die vorstehenden Bestandteile veruiesen.
Das Titanoxid, Kaolin, Mica(Glimmer), Talkum undThe origin of the individual components and their
For specification reference is made to the above items. The titanium oxide, kaolin, mica (mica), and talc
der Ueißmacher können aus geriebenem bzw. gemahlenem Stein erzeugt werden.the Ueißmacher can use grated or ground stone be generated.
Wie auch in den vorstehenden Beispielen werden die Komponenten in der aufgeführten Reihenfolge nacheinander zugesetzt. Die Zugabe von Shellsol A erfolgt als letzte Komponente.As in the previous examples, the components added one after the other in the order listed. Shellsol A is added as the last component.
Mit den nachfolgenden Bestandteilen in Kilogramm wurde die folgende Dispersionsfarbe angesetzt:With the following components in kilograms was the following emulsion paint is used:
Uasser 180,000 180,000Uasser 180,000 180,000
Budit (Firma Aseol AG,Schweiz) 2,000Budit (company Aseol AG, Switzerland) 2,000
Methocel KA 3,600Methocel KA 3,600
Lösung von Natriumhexametaphosphät(10$) 11,000Solution of Sodium Hexametaphosphate ($ 10) 11,000
Entschäumungsmitt.el Antifoam L-802 0,800Defoaming agent Antifoam L-802 0.800
Ammoniak, wässrige Lösung 24/25% 1,600Ammonia, aqueous solution 24/25% 1,600
Titanoxid No. 376 134,000Titanium oxide No. 376 134,000
Komponente P B20 15,000Component P B20 15,000
Benetzungsmittel Disperwet CO-76 1,200Wetting agent Disperwet CO-76 1,200
Bamax 0.500Bamax 0.500
Fungizid COCID T-350 0,900Fungicide COCID T-350 0.900
Äthylenglykol, technisch rein 5,000Ethylene glycol, technically pure 5,000
Weichmacher Plasticom 1,600Plasticizer Plasticom 1,600
Acryldispersion UALLPOL A 600 114,000Acrylic dispersion UALLPOL A 600 114,000
Talkum, fein 80,000 Durcal U.S. · 200,000Talc, fine 80,000 durcal U.S. 200,000
Shell-Sol A 2,500Shell-Sol A 2,500
Zur Herkunft der einzelnen Bestandteile wird wiederum auf die vorherigen Beispiele verwiesen.For the origin of the individual components, reference is again made to the previous examples.
Claims (6)