CH654322A5 - DISPERSION COLOR. - Google Patents
DISPERSION COLOR. Download PDFInfo
- Publication number
- CH654322A5 CH654322A5 CH802/83A CH80283A CH654322A5 CH 654322 A5 CH654322 A5 CH 654322A5 CH 802/83 A CH802/83 A CH 802/83A CH 80283 A CH80283 A CH 80283A CH 654322 A5 CH654322 A5 CH 654322A5
- Authority
- CH
- Switzerland
- Prior art keywords
- dispersion
- water
- solution
- emulsion paint
- titanium dioxide
- Prior art date
Description
Die vorliegende Erfindung betrifft eine Dispersionsfarbe für Innen- und Aussenanstriche. The present invention relates to a dispersion paint for interior and exterior painting.
Die bisher bekannten Dispersionsfarben bzw. Dispersionsanstriche haben den Nachteil, dass sie einen ungenügenden Schutz gegen äussere Einflüsse bieten, wenn sie aufgetragen sind. Auch ist ihre thermische und/oder akustische Isolierfähigkeit in vielen Fällen ungenügend. Weiterhin fehlen ihnen die gewünschten Auftragungseigenschaften und auch Eigenschaften im aufgetragenen Zustand in verschiedenen Anwendungsbereichen. So entspricht auch ihre Standfestigkeit nicht in allen Fällen den an Dispersionsfarben gestellten Anforderungen. The previously known emulsion paints or emulsion paints have the disadvantage that they offer insufficient protection against external influences when they are applied. In many cases, their thermal and / or acoustic insulation ability is also insufficient. Furthermore, they lack the desired application properties and also properties in the applied state in various areas of application. So their stability does not always meet the requirements placed on emulsion paints.
Es ist daher die Aufgabe der vorliegenden Erfindung eine Dispersionsfarbe ohne die vorstehend aufgezeigten Nachteile zu schaffen, welche die Anforderungen als Innen- und Aus-senanstrich erfüllen soll. It is therefore the object of the present invention to provide an emulsion paint without the disadvantages outlined above, which is intended to meet the requirements for interior and exterior painting.
Diese Aufgabe wird für die Dispersionsfarbe der eingangs genannten Art erfindungsgemäss dadurch gelöst, dass sie auf der Basis von Wasser vorliegt und in einer in Wasser disper-gierbaren Grunddispersion mindestens Methylcellulose, Acrylharz und Glykol sowie ein Pigment oder Sand und Additive enthält. This object is achieved according to the invention for the emulsion paint of the type mentioned at the outset in that it is water-based and contains at least methylcellulose, acrylic resin and glycol and a pigment or sand and additives in a water-dispersible base dispersion.
In vorteilhafter Weise ist die Dispersionsfarbe nach der Erfindung mit ihren Bestandteilen in Wasser dispergiert, wobei das Wasser ein wohlfeiles Dispersionsmittel darstellt. Auf Grund der Bestandteile der Grunddispersion, die vorzugsweise als Kunststoffdispersion bezeichnet werden kann, kann mit der Dispersionsfarbe nach der Erfindung ein Dis-persionsanstrich erreicht werden, der den Wünschen nach einer thermischen und/oder akustischen Isolierung entspricht. In vorteilhafter Weise liegt eine Kombination, aus der synthetisches Kunstharz, d.h. die Acrylkomponente enthaltenden Grunddispersion und dem Pigment, vor, was einen breiten Anwendungsbereich der Dispersionsfarbe zulässt. Dieser lässt sich durch Auswahl der entsprechenden Additive erweitern. The dispersion paint according to the invention with its constituents is advantageously dispersed in water, the water being a cheap dispersing agent. Because of the constituents of the basic dispersion, which can preferably be referred to as a plastic dispersion, the dispersion paint according to the invention can be used to achieve a dispersion coating which corresponds to the requirements for thermal and / or acoustic insulation. Advantageously, there is a combination of which synthetic resin, i.e. the basic dispersion containing the acrylic component and the pigment, which permits a wide range of uses of the emulsion paint. This can be expanded by selecting the appropriate additives.
So kann die Grunddispersion bzw. die Dispersionsfarbe ein Pigment, vorzugsweise aus einem anorganischen Material enthalten. Als Pigment kann Titandioxid, vorzugsweise in Form von Rutil, und/oder Sand, z.B. Quarzsand, vorliegen. Der Dispersionsfarbe können Entschäumungsmittel zugesetzt sein. Weiterhin kann die Dispersionsfarbe bzw. die Grunddispersion Fungizide und/oder Weichmacher und/oder Natriumphosphat und/oder Karbonat und/oder ein Benetzungsmittel enthalten. Vorzugsweise liegt die Grunddispersion als Pulver vor, das in Wasser dispergiert ist bzw. in diesem dispergiert werden kann. For example, the basic dispersion or the emulsion paint can contain a pigment, preferably made of an inorganic material. Titanium dioxide, preferably in the form of rutile and / or sand, e.g. Quartz sand. Defoamers can be added to the emulsion paint. Furthermore, the emulsion paint or the base dispersion may contain fungicides and / or plasticizers and / or sodium phosphate and / or carbonate and / or a wetting agent. The basic dispersion is preferably in the form of a powder which is or can be dispersed in water.
Die Erfindung ist nachstehend in Ausführungsbeispielen näher erläutert. The invention is explained in more detail below in exemplary embodiments.
Beispiel 1 example 1
Es wurden nachfolgende Komponenten und deren Mengen in Kilogramm in Wasser zu einer Dispersionsfarbe ange- The following components and their quantities in kilograms in water were added to a dispersion paint.
setzt: puts:
Wasser water
7,500 7,500
Natriumhexametaphosphat als l0%ige Sodium hexametaphosphate as 10%
Lösung solution
7,500 7,500
Methylcellulose Kulminal 6000 Methyl cellulose culminal 6000
0,300 0.300
Antischaummittel Antifoam L 802 Antifoam L 802 antifoam
0,375 0.375
Benetzungsmittel Disperwet CO-76 Wetting agent Disperwet CO-76
0,750 0.750
Äthylenglykol, technisch rein Ethylene glycol, technically pure
0,750 0.750
Weichmacher Plasticom Plasticizer plasticizer
0,750 0.750
Fungizid Cocid T-350 Fungicide Cocid T-350
0,150 0.150
Talkum, fein Talc, fine
18 18th
Talkum, grob Talc, rough
12 12
Calciumcarbonat Calcit, mikrokristallin Calcium carbonate calcite, microcrystalline
24 24th
Acryldispersion Wallpol A 600 Acrylic dispersion Wallpol A 600
48 48
Ammoniak, 24/25%ige Lösung in Wasser Ammonia, 24/25% solution in water
0,300 0.300
Pigmentfarbe Mandarin, 20%ige Lösung Pigment color mandarin, 20% solution
30 30th
Das Natriumhexametaphosphat wird als weisses Pulver eingesetzt mit einem pH-Wert von 7,2 bei einer Konzentration von 2,5 g je Liter Lösung. Die Kulminal-Methylcellulose 6000 ist von der Henkel, Basel, Schweiz, erhältlich. Das Entschäumungsmittel Antifoam L-802, das Benetzungsmittel Dis-perwet CO-76, der Weichmacher Plasticom und das Fungizid Cocid T-350 sind bei der Firma Comiel, Mailand, Italien, erhältlich. The sodium hexametaphosphate is used as a white powder with a pH of 7.2 at a concentration of 2.5 g per liter of solution. Kulminal-Methylcellulose 6000 is available from Henkel, Basel, Switzerland. The anti-foaming agent Antifoam L-802, the wetting agent Dis-perwet CO-76, the plasticizer Plasticom and the fungicide Cocid T-350 are available from Comiel, Milan, Italy.
Das feine und grobe Talkum ist durch die Plüss-Stauffer AG, CH-4665 Oftringen, zu erhalten, und Wallpol A 600 kann von der Reichhold Chemie AG, CH-5212 Hausen bei Brugg, bezogen werden. Das Calciumcarbonat Calcit wird mikrokristallin von der S.I.M.F. Calcit S.R.L., Canevy di Sacile (PN) C.a.p., 33070, Italien, geliefert. The fine and coarse talc can be obtained from Plüss-Stauffer AG, CH-4665 Oftringen, and Wallpol A 600 can be obtained from Reichhold Chemie AG, CH-5212 Hausen near Brugg. The calcium carbonate calcite is microcrystalline by the S.I.M.F. Calcit S.R.L., Canevy di Sacile (PN) C.a.p., 33070, Italy.
Auch in den nachfolgenden Beispielen wurde die Methylcellulose Kulminal 6000 in einer Lösung von 10% Kuliminal 6000 auf 1001 Wasser angesetzt. In the following examples too, the methyl cellulose Kulminal 6000 was prepared in a solution of 10% Kuliminal 6000 to 1001 water.
Die Pigmentfarbe Mandarin besass die folgende Zusammensetzung (Mengen in Kilogramm): The pigment color Mandarin had the following composition (amounts in kilograms):
Methylcellulose Kulminal 6000 12,600 Methyl cellulose culminal 6000 12,600
Weichmacher Plasticom 1,900 Plasticizer 1,900
Äthylenglykol, technisch rein 1,900 Ethylene glycol, technically pure 1,900
Bamax 6,500 Bamax 6,500
Diorin 6,500 Diorin 6,500
Eisenoxidgelb (Firma Vogel, Zürich) 6,500 Iron oxide yellow (Vogel company, Zurich) 6,500
Rutil 3,800 Rutile 3,800
Kaolin 34,800 Kaolin 34,800
Colanylgelb 20,000 Colanyl yellow 20,000
Die Komponenten Bamax und Diorin sind von der Super-colori S.A., Mailand, Italien, erhältlich, und Rutil (Titandioxid), Kaolin und das Colanylgelb sind durch die Firma Plüss-Stauffer AG, CH-4665 Oftringen, zu erhalten. The components Bamax and Diorin are available from Super-colori S.A., Milan, Italy, and rutile (titanium dioxide), kaolin and the colanyl yellow are available from Plüss-Stauffer AG, CH-4665 Oftringen.
Beispiel 2 Example 2
Ein Polystyrol-Baukleber enthielt als Bindemittelleim ver-seifungsbeständige Kunststoffdispersion mit den nachfolgenden Komponenten und deren Mengen in Kilogramm: A polystyrene construction adhesive contained the soap-resistant plastic dispersion with the following components and their quantities in kilograms:
Wasser 10,000 Water 10,000
Kulminal Methylcellulose 6000 0,210 Kulminal methyl cellulose 6000 0.210
Acryldispersion Wallpol A 600 12 Acrylic dispersion Wallpol A 600 12
Wasser 1,750 Water 1,750
5 5
10 10th
15 15
20 20th
25 25th
30 30th
35 35
40 40
45 45
50 50
55 55
60 60
65 65
3 3rd
654 322 654 322
Entschäumungsmittel Antifoam L-802 0,009 Defoamer Antifoam L-802 0.009
Leophen (Firma Bayer AG, Zürich, Schweiz) 0,006 Leophen (Bayer AG, Zurich, Switzerland) 0.006
Alkohol, denaturiert 0,705 Alcohol, denatured 0.705
Propylenglykol 0,705 Propylene glycol 0.705
Karbonat Calcit 5,750 Carbonate calcite 5,750
Sand 76 Sand 76
Shellsol A (Shell-Switzerland, Zürich) 0,100 Shellsol A (Shell-Switzerland, Zurich) 0.100
Amm 0,100 Amm 0.100
Arbocel (Firma Emil Weiss, Basel, Schweiz) 0,600 Arbocel (company Emil Weiss, Basel, Switzerland) 0.600
Weichmacher Plasticom 0,500 Plasticizer 0.500
Dieser Dispersion wurden dann 20% Portlandzement, knötchenfrei, zugemischt. Nach der Zementzugabe konnte die Masse verarbeitet werden. This dispersion was then mixed with 20% Portland cement, knot-free. After adding the cement, the mass could be processed.
Die mit Beispiel 1 gleichen Komponenten können von den dort angeführten Firmen bezogen werden. Die anderen Komponenten sind auf dem Markt erhältlich. The same components as in Example 1 can be obtained from the companies listed there. The other components are available on the market.
Beispiel 3 Example 3
Eine Dispersionsfarbe wurde mit den nachfolgenden A dispersion paint was used with the following
Komponenten und deren Mengen in Kilogramm angesetzt: Components and their quantities in kilograms:
Pigmentpaste Pigment paste
4,000 4,000
Acryldispersion Wallpol A 600 Acrylic dispersion Wallpol A 600
13,000 13,000
Titandioxid Titanium dioxide
3,500 3,500
Karbonat Calcit Carbonate calcite
7,000 7,000
gemahlener Marmorstein ground marble stone
71 71
Die Pigmentpaste war mit den folgenden Komponenten und Mengen in Kilogramm angesetzt: The pigment paste was made up in kilograms with the following components and quantities:
Wasser water
890,000 890,000
Methylcellulose Kulminal 20 000 Methyl cellulose culminal 20,000
21 21st
Natriumhexametyphosphat, Pulver Sodium hexametyphosphate, powder
34,500 34,500
Fungizid Cocid T-350 Fungicide Cocid T-350
18 18th
Entschäumungsmittel Antifoam L-802 Antifoam L-802 defoamer
20 20th
Benetzungsmittel Disperwet CO-76 Wetting agent Disperwet CO-76
eine Lösung von Lapponit in Wasser a solution of lapponite in water
50 50
Wasser water
200 200
Lapponit Lapponite
13,800 13,800
Äthylenglykol, technisch rein Ethylene glycol, technically pure
104 104
Ammoniaklösung, 24/25% Ammonia solution, 24/25%
17 17th
Die Komponente Lapponit ist von der Plüss-Stauffer AG. The component Lapponit is from Plüss-Stauffer AG.
CH-4665 Oftringen, erhältlich. Zur Herkunft der anderen CH-4665 Oftringen, available. The origin of the others
Komponenten, auch derjenigen der Dispersionsmischung wird auf Beispiel 1 verwiesen. Components, including those of the dispersion mixture, are referred to Example 1.
Beispiel 4 Example 4
Eine Dispersionsfarbe wurde aus den nachfolgenden A dispersion paint was made from the following
Bestandteilen und deren Mengen in Kilogramm angesetzt: Components and their quantities in kilograms:
Wasser water
100,000 100,000
Methylcellulose Kulminal 6000 Methyl cellulose culminal 6000
2,100 2,100
Natriumhexametaphosphat in Lösung (10%) Sodium hexametaphosphate in solution (10%)
7,000 7,000
Entschäumungsmittel Antifoam L-802 Antifoam L-802 defoamer
1,000 1,000
Fungizid Cocid T-350 Fungicide Cocid T-350
0,800 0.800
Benetzungsmittel Disperwet CI-76 Wetting agent Disperwet CI-76
2,100 2,100
Äthylenglykol, technisch rein Ethylene glycol, technically pure
3,100 3,100
Weichmacher Plasticom Plasticizer plasticizer
1,400 1,400
Titandioxid als Rutil No. 376 Titanium dioxide as rutile no. 376
75,000 75,000
Kaolin kaolin
14,000 14,000
Talkum, grob Talc, rough
14,000 14,000
Karbonat, mikrokristallin Carbonate, microcrystalline
105,000 105,000
Acryldispersion Wallpol A 600 Acrylic dispersion Wallpol A 600
196,000 196,000
Quarzsand, Reibungspunkt 16 000 Quartz sand, friction point 16,000
300,000 300,000
Ammoniak in wässriger Lösung 24/25% Ammonia in aqueous solution 24/25%
0,800 0.800
Shellsol A (Shell-Switzerland, Zürich) Shellsol A (Shell-Switzerland, Zurich)
2,500 2,500
Zur Herkunft der einzelnen Bestandteile wird wiederum auf Beispiel 1 verwiesen. Auch bei dieser Dispersionsfarbe liegt eine Kombination aus einer Emulsion eines synthetischen Harzes (Kunstharz) und einem Edelpigment und hoch-5 reinem Quarzsand vor, d.h. Pigmenten, die unveränderlich und daher für die Dispersionsfarbe bzw. den Dispersionsanstrich von Vorteil sind. For the origin of the individual components, reference is again made to Example 1. This emulsion paint also has a combination of an emulsion of a synthetic resin (synthetic resin) and a noble pigment and high-5 pure quartz sand, i.e. Pigments that cannot be changed and are therefore advantageous for the emulsion paint or coating.
Beispiel 5 Example 5
io Eine Dispersionsfarbe enthielt die nachfolgend aufgeführten Komponenten und deren Mengen in Kilogramm : io An emulsion paint contained the components listed below and their quantities in kilograms:
Wasser 260,000 Water 260,000
Methylcellulose Kulminal 6000 2,000 15 Lösung von Natriumhexametaphosphat (10%) 3,000 Methyl cellulose culminal 6000 2,000 15 solution of sodium hexametaphosphate (10%) 3,000
Entschäumungsmittel Antifoam L-802 0,500 Antifoam L-802 0.500 defoamer
Benetzungsmittel Disperwet CO-76 0,800 Wetting agent Disperwet CO-76 0.800
Fungizid Cocid T-350 0,600 Fungicide Cocid T-350 0.600
Äthylenglykol, technisch rein 1,500 Ethylene glycol, technically pure 1,500
20 Weichmacher Plasticom 0,600 20 plasticizers plasticom 0.600
Titandioxid-Paste 28,000 Titanium dioxide paste 28,000
Quarzsand, Reibungspunkt 16 000 100,000 Quartz sand, friction point 16,000 100,000
Kaolin 50,000 Kaolin 50,000
Karbonat, mikrokristallin «Red Line» 50,000 Carbonate, microcrystalline «Red Line» 50,000
25 Acryldispersion Wallpol A 600 160,000 25 Wallpol A 600 160,000 acrylic dispersion
Ammoniak-Lösung 24/25% 0,500 Ammonia solution 24/25% 0.500
Shellsol A 2,000 Shellsol A 2,000
Das Karbonat «Red Line» ist von der Umbria Mineraria 3o S.p.A., Mailand, Italien, erhältlich. Zur Herkunft der anderen Bestandteile wird auf die vorstehenden Beispiele verwiesen. The “Red Line” carbonate is available from Umbria Mineraria 3o S.p.A., Milan, Italy. For the origin of the other constituents, reference is made to the examples above.
Beispiel 6 Example 6
Eine Dispersionsfarbe enthielt die nachfolgenden Kom-35 ponenten und deren Mengen in Kilogramm: An emulsion paint contained the following components and their quantities in kilograms:
Wasser 165,000 Water 165,000
Methylcellulose Kulminal 6000 2,550 Lösung von Natriumhexametaphosphat (10%) 7,500 Methyl cellulose Kulminal 6000 2.550 solution of sodium hexametaphosphate (10%) 7.500
40 Benetzungsmittel Disperwet CO-76 2,250 40 wetting agents Disperwet CO-76 2,250
Entschäumungsmittel Antifoam L-802 1,400 Antifoam L-802 1,400 defoamer
Fungizid Cocid T-350 0,900 Fungicide Cocid T-350 0.900
Äthylenglykol, technisch rein 2,250 Ethylene glycol, technically pure 2.250
Weichmacher Plasticom 2,250 Plasticizer 2.250
45 Titandioxid 376 150,000 45 titanium dioxide 376 150,000
Kaolin 37,500 Kaolin 37,500
Talkum, grob 37,500 Talc, roughly 37,500
Calciumcarbonat Calcit 75,000 Durcal WS (Plüss-Stauffer, CH-Oftringen) 75,000 Calcium carbonate calcite 75,000 Durcal WS (Plüss-Stauffer, CH-Oftringen) 75,000
so Acryldispersion 203 200,000 so acrylic dispersion 203 200,000
Ammoniak-Lösung 1,800 Ammonia solution 1,800
Acryldispersion 201 25,000 Acrylic dispersion 201 25,000
Shellsol A 2,600 Shellsol A 2,600
55 Titandioxid 376 kann ebenfalls von der Plüss-Stauffer AG, CH-4665 Oftringen, bezogen werden. Die Acryldisper-sionen 203 und 201 sind von der Reichhold Chemie AG, CH-5212 Hausen bei Brugg erhältlich. Zur Herkunft der übrigen Bestandteile wird auf die vorstehenden Beispiele verwiesen. 60 Shellsol A wird als letzte Komponente zugesetzt, wonach die Dispersion gebrauchsfertig ist. 55 Titanium dioxide 376 can also be obtained from Plüss-Stauffer AG, CH-4665 Oftringen. Acrylic dispersions 203 and 201 are available from Reichhold Chemie AG, CH-5212 Hausen near Brugg. With regard to the origin of the remaining constituents, reference is made to the examples above. 60 Shellsol A is added as the last component, after which the dispersion is ready for use.
Beispiel 7 Example 7
Eine Dispersionsfarbe bestand aus den nachfolgend auf-65 geführten Komponenten und deren Mengen in Kilogramm: A dispersion paint consisted of the components listed below and their quantities in kilograms:
Wasser water
Methylcellulose Kulminal 6000 Methyl cellulose culminal 6000
200,000 2,800 200,000 2,800
654 322 654 322
4 4th
Lösung von Natriumhexametaphosphat (10%) 9,600 Solution of sodium hexametaphosphate (10%) 9,600
Benetzungsmittel Disperwet CO-76 1,600 Wetting agent Disperwet CO-76 1,600
Entschäumungsmittel Antifoam L-802 0,800 Antifoam L-802 0.800 defoamer
Fungizid Cocid T-350 0,800 Fungicide Cocid T-350 0.800
Äthylenglykol, technisch rein 2,800 Ethylene glycol, technically pure 2,800
Titandioxid G 55,000 Titanium dioxide G 55,000
Komponente P 820 (Degussa, Zürich) 15,000 Component P 820 (Degussa, Zurich) 15,000
Calciumcarbonat Calcit 150,000 Calcium carbonate calcite 150,000
Talkum, grob 25,000 Talc, roughly 25,000
Calciumcarbonat, Bianco Typ A 250,000 Calcium carbonate, Bianco type A 250,000
Acryldispersion Wallpol A 600 100,000 Acrylic dispersion Wallpol A 600 100,000
Ammoniak-Lösung 1,000 Ammonia solution 1,000
Shellsol A (Shell-Switzerland, Zürich) 1,500 Shellsol A (Shell-Switzerland, Zurich) 1,500
Zur Herkunft der einzelnen Bestandteile und ihre Spezifikationen wird auf die vorstehenden Beispiele verwiesen. For the origin of the individual components and their specifications, reference is made to the examples above.
Beispiel 8 Example 8
Eine Dispersionsfarbe enthielt die nachfolgend aufgeführ- An emulsion paint contained the following
ten Komponenten und deren Mengen in components and their quantities in
Kilogramm: Kilogram:
Wasser water
70,000 70,000
Methylcellulose Kulminal 6000 Methyl cellulose culminal 6000
0,600 0.600
Lösung von Natriumhexametaphosphat ( 10%) 8,000 Solution of sodium hexametaphosphate (10%) 8,000
Entschäumungsmittel Antifoam L-802 Antifoam L-802 defoamer
0,500 0.500
Fungizid Cocid T-350 Fungicide Cocid T-350
0,700 0.700
Benetzungsmittel Disperwet CO-76 Wetting agent Disperwet CO-76
0,900 0.900
Lösung von Lapponit Lapponit solution
3,600 3,600
Äthylenglykol, technisch rein Ethylene glycol, technically pure
1,800 1,800
Titandioxid G Titanium dioxide G
24,000 24,000
Calciumcarbonat, Bianco Typ A Calcium carbonate, Bianco type A
120,000 120,000
Calciumcarbonat Calcit Calcium carbonate calcite
120,000 120,000
Sand sand
120,000 120,000
Quarzsand, Reibungspunkt 16 000 Quartz sand, friction point 16,000
120,000 120,000
Acryldispersion Wallpol A 600 Acrylic dispersion Wallpol A 600
72,000 72,000
Ammoniak-Lösung Ammonia solution
0,300 0.300
Polystyrol Polystyrene
9,600 9,600
Das in den Beispielen 7 und 8 angeführte Calciumcarbonat, Bianco Typ A kann von der Umbria Mineraria S.p.A., Mailand, Italien, als amorphes Calciumcarbonat bezogen werden. Zur Herkunft der übrigen Bestandteile wird auf die vorstehenden Beispiele verwiesen. The calcium carbonate, Bianco type A listed in Examples 7 and 8, can be obtained from Umbria Mineraria S.p.A., Milan, Italy, as amorphous calcium carbonate. With regard to the origin of the remaining constituents, reference is made to the examples above.
Beispiel 9 Example 9
Eine Dispersionsfarbe auf der Grundlage eines Weissers bzw. Weissmachers hatte die nachfolgende Zusammensetzung von Komponenten und deren Mengen in Kilogramm: An emulsion paint based on a whitener or whitener had the following composition of components and their quantities in kilograms:
Wasser 200,000 Water 200,000
Methocel K4 (Firma Daw, Schweiz) 3,700 Lösung von Natriumhexametaphosphat ( 10%) 13,000 Methocel K4 (Daw company, Switzerland) 3,700 solution of sodium hexametaphosphate (10%) 13,000
Benetzungsmittel Disperwet CO-76 1,600 Wetting agent Disperwet CO-76 1,600
Entschäumungsmittel Antifoam L-802 0,800 Antifoam L-802 0.800 defoamer
Fungizid Cocid T-350 0,800 Fungicide Cocid T-350 0.800
Äthylenglykol, technisch rein 1,500 Ethylene glycol, technically pure 1,500
Titandioxid G 25,000 Titanium dioxide G 25,000
Calciumcarbonat, Bianco A 500,000 Calcium carbonate, Bianco A 500,000
Acryldispersion Wallpol A 600 45,000 Acrylic dispersion Wallpol A 600 45,000
Ammoniak-Lösung 0,700 Ammonia solution 0.700
Zur Herkunft der einzelnen Bestandteile wird auf die vorstehenden Beispiele verwiesen. For the origin of the individual components, reference is made to the examples above.
Beispiel 10 Example 10
Eine weisse Dispersionsfarbe hatte die nachfolgende Zusammensetzung und Mengen in Kilogramm: A white emulsion paint had the following composition and quantities in kilograms:
Wasser 210,000 Water 210,000
Methocel K4 (Firma Daw, Schweiz) 3,700 Methocel K4 (Daw company, Switzerland) 3,700
Lösung von Natriumhexametaphosphat (10%) 15,000 Solution of sodium hexametaphosphate (10%) 15,000
Entschäumungsmittel L-802 0,600 Defoamer L-802 0.600
Fungizid Cocid T-350 0,800 Fungicide Cocid T-350 0.800
Äthylenglykol, technisch rein 3,000 Ethylene glycol, technically pure 3,000
5 Benetzungsmittel Disperwet CO-76 1,000 5 wetting agents Disperwet CO-76 1,000
Titandioxid G 15,000 Titanium dioxide G 15,000
Calciumcarbonat, Bianco A 500,000 Calcium carbonate, Bianco A 500,000
Acryldispersion Wallpol A 600 30,000 Acrylic dispersion Wallpol A 600 30,000
Ammoniak-Lösung 0,500 Ammonia solution 0.500
Zur Herkunft und Spezifikation der einzelnen Bestandteile wird auf die vorstehenden Beispiele verwiesen. For the origin and specification of the individual components, reference is made to the examples above.
Beispiel 11 Example 11
Eine Dispersionsfarbe wurde mit den nachfolgend aufgeführten Komponenten .und deren Mengen in Kilogramm angesetzt: A dispersion paint was prepared with the components listed below and their quantities in kilograms:
Wasser 200,000 Water 200,000
Methylcellulose Kulminal 6000 3,100 20 Lösung von Natriumhexametaphosphat (10%) 12,000 Methyl cellulose culminal 6000 3,100 20 solution of sodium hexametaphosphate (10%) 12,000
Entschäumungsmittel Antifoam L-802 1,000 Antifoam L-802 1,000 defoamer
Ammoniak-Lösung 1,200 Ammonia solution 1,200
Titandioxid G 85,000 Titanium dioxide G 85,000
Kaolin 50,000 Kaolin 50,000
25 Mica 50,000 25 mica 50,000
Talkum, fein 50,000 Talc, fine 50,000
Calciumcarbonat, Bianco A 100,000 Calcium carbonate, Bianco A 100,000
Carbonat Calcit 100,000 Carbonate Calcite 100,000
Benetzungsmittel Disperwet CO-76 1,600 Wetting agent Disperwet CO-76 1,600
30 Fungizid Cocid T-350 0,800 30 fungicide Cocid T-350 0.800
Äthylenglykol, technisch rein 3,200 Ethylene glycol, technically pure 3,200
Weichmacher Plasticom 2,000 Plasticizer 2,000
Acryldispersion Wallpol A 600 160,000 Acrylic dispersion Wallpol A 600 160,000
Shellsol A 2,000 Shellsol A 2,000
35 Zur Herkunft der einzelnen Bestandteile und ihrer Spezifikation wird auf die vorstehenden Bestandteile verwiesen. Das Titandioxid, Kaolin, Mica (Glimmer), Talkum und der Weissmacher können aus geriebenem bzw. gemahlenem Stein erzeugt werden. 35 For the origin of the individual components and their specification, reference is made to the above components. The titanium dioxide, kaolin, mica (mica), talc and the whitening agent can be produced from grated or ground stone.
40 Wie auch in den vorstehenden Beispielen werden die Komponenten in der aufgeführten Reihenfolge nacheinander zugesetzt. Die Zugabe von Shellsol A erfolgt als letzte Komponente. 40 As in the previous examples, the components are added one after the other in the order listed. Shellsol A is added as the last component.
45 Beispiel 12 45 Example 12
Mit den nachfolgenden Bestandteilen in Kilogramm wurde die folgende Dispersionsfarbe angesetzt: The following emulsion paint was used with the following ingredients in kilograms:
Wasser 180,000 Water 180,000
50 Budit (Firma Aseol AG, Schweiz) 2,000 50 budit (company Aseol AG, Switzerland) 2,000
Methocel K4 3,600 Lösung von Natriumhexametaphosphat (10%) 11,000 Methocel K4 3,600 solution of sodium hexametaphosphate (10%) 11,000
Entschäumungsmittel Antifoam L-802 0,800 Antifoam L-802 0.800 defoamer
Ammoniak, wässrige Lösung 24/25% 1,600 Ammonia, aqueous solution 24/25% 1,600
55 Titandioxid No. 376 134,000 55 titanium dioxide No. 376 134,000
Komponente P 820 15,000 Component P 820 15,000
Benetzungsmittel Disperwet CO-76 1,200 Disperwet CO-76 1,200 wetting agent
Bamax 0,500 Bamax 0.500
Fungizid Cocid T-350 0,900 Fungicide Cocid T-350 0.900
60 Äthylenglykol, technisch rein 5,000 60 ethylene glycol, technically pure 5,000
Weichmacher Plasticom 1,600 Plasticizer 1,600
Acryldispersion Wallpol A 600 114,000 Acrylic dispersion Wallpol A 600 114,000
Talkum, fein 80,000 Talc, fine 80,000
Durcal W.S. 200,000 Durcal W.S. 200,000
65Shell-Sol A 2,500 65 Shell Sol A 2,500
Zur Herkunft der einzelnen Bestandteile wird wiederum auf die vorherigen Beispiele verwiesen. For the origin of the individual components, reference is again made to the previous examples.
G G
Claims (5)