DE3241516A1 - Multilayer system for thermal insulation application - Google Patents
Multilayer system for thermal insulation applicationInfo
- Publication number
- DE3241516A1 DE3241516A1 DE19823241516 DE3241516A DE3241516A1 DE 3241516 A1 DE3241516 A1 DE 3241516A1 DE 19823241516 DE19823241516 DE 19823241516 DE 3241516 A DE3241516 A DE 3241516A DE 3241516 A1 DE3241516 A1 DE 3241516A1
- Authority
- DE
- Germany
- Prior art keywords
- layer
- protective layer
- spectral range
- thickness
- protective
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Abstract
Description
9.11. 1982 Rs/Hm9.11. 1982 Rs / Hm
ROBERT BOSCH GMBH, 7OOO STUTTGART 1ROBERT BOSCH GMBH, 7OOO STUTTGART 1
Mehrschichtsystem für Wärmeschutzanwendung Stand der TechnikState-of-the-art multi-layer system for thermal insulation applications
Die Erfindung geht aus von einem Mehrschichtsystem nach der Gattung des Hauptanspruchs. Ein derartiges Mehrschichtsystem für Wärmeschutzanwendung ist beispielsweise bekannt aus der DE-OS 30 27 256. Diese Druckschrift beschreibt ein MehrSchichtsystem mit einem Träger, z.B. aus Polyester, auf den eine dielektrische Schicht zur Entspiegelung einer darüberliegenden Metallschicht aufgetragen ist. Durch geeignete Wahl der Dicke und der Bredhzahl der dielektrischen Schicht entsteht eine Interferenzwirkung, so daß durch den Träger einfallendes Licht im sichtbaren Spektralbereich an der Metallschicht nur zu einem sehr geringen Teil reflektiert wird und weitgehend ungehindert durch das Mehrschichtsystem hindurchtreten kann. Andererseits wird Infrarot-Wärmestrahlung,, welche von der vom Träger abgewandten Seite, z.B. von einem Innenraum her auf die Metallschicht auftrifft, in hohemThe invention is based on a multilayer system the genre of the main claim. Such a multi-layer system for thermal protection application is for example known from DE-OS 30 27 256. This document describes a multi-layer system with a Support, e.g. made of polyester, on which a dielectric layer for anti-reflective coating of an overlying metal layer is applied. By suitable choice of the thickness and Bredh number of the dielectric layer there is an interference effect so that only a very small amount of light in the visible spectral range is incident on the metal layer through the carrier Part is reflected and can pass largely unhindered through the multilayer system. on the other hand is infrared heat radiation, which comes from the side facing away from the wearer, e.g. from an interior forth on the metal layer, in high
BAD ORIGINALBATH ORIGINAL
Maße reflektiert. Die beschriebene Anordnung "besitzt eine weitere dielektrische Schicht entsprechend der erstgenannten dielektrischen Schicht auf der vom Träger abgewandten Seite der Metallschicht, welche das Transmissidnsvermögen für sichtbares Licht weiter erhöht und eine gewisse Korrosionsschutzwirkung ausübt ohne das Reflexionsvermögen für Infrarot-Strahlung nennenswert zu beeinträchtigen.Dimensions reflected. The arrangement described "has a further dielectric layer corresponding to the first-mentioned dielectric layer on the one facing away from the carrier Side of the metal layer that has the transmittance for visible light further increased and exerts a certain anti-corrosive effect without the reflectivity for infrared radiation noticeably impaired.
Aus der DE-OS 27 03 688 ist eine weitere Wärme-Schutzvorrichtung für lichtdurchlässig abgeschlossene Raumöffnungen bekannt. Diese Anordnung besitzt auf der Rauminnenseite, zu der die Infrarotstrahlung zurückgelenkt werden soll, eine Kunststoff-Schutzschicht mit niedrigem Absorptionsvermögen im Infrarot-Spektralbereich, so daß die Infrarotstrahlung die Kunststoff-Schutzschicht nicht erwärmt und weitestgehend ungehindert in den warmen Raum reflektiert wird. Auf der Kunststoff-Gehutzschicht sitzt eine Metallschicht und hierauf eine Deckschicht, welche ebenfalls aus einer Kunststoffolie, z.B. aus Polyäthylen bestehen kann. Diese Deckschicht hat die Funktion des mechanischen Trägers des Mehr Schichtsystems. Sie liegt auf der Außenseite, z.B. benachbart zu einer Glasscheibe. Eine derartige Anordnung hat zwar ein hohes Reflexionsvermögen im Infrarot-Spektralbereich, dagegen ist das Transmissionsvermögen im sichtbaren Spektralbereich relativ gering, weil einerseits nichts gegen die Reflexion des sichtbaren Lichtes an der Metallschicht getan ist und weil andererseits die nach außen gerichtete Träger-Deckschicht nicht für ein hohes Transmissionsvermögen für den sichtbaren Spektralbereich modifiziert ist.From DE-OS 27 03 688 is another heat protection device known for translucent closed room openings. This arrangement has on the inside of the room, to which the infrared radiation is to be deflected back, a plastic protective layer with low absorption capacity in the infrared spectral range, so that the infrared radiation does not heat the protective plastic layer and reflected largely unhindered in the warm room will. A metal layer sits on top of the plastic protective layer and on top of it a cover layer, which is also can consist of a plastic film, e.g. of polyethylene. This top layer has the function of mechanical carrier of the multi-layer system. It is on the outside, e.g. next to a pane of glass. Such an arrangement has a high reflectivity in the infrared spectral range, but it is Transmittance in the visible spectral range is relatively low because, on the one hand, nothing against reflection the visible light is done on the metal layer and because on the other hand the outwardly directed carrier cover layer is not modified for high transmittance for the visible spectral range.
IQIQ
Vorteile der ErfindungAdvantages of the invention
Das erfindungsgemäße Mehrschichtsystem mit den kennzeichnenden Merkmalen des Hauptanspruches hat demgegenüber den Vorteil, daß ohne nennenswerte Einbuße bezüglich des Transmissionsvermögens im sichtbaren Spektralbereich ein sehr guter mechanischer Schutz und ein Korrosionsschutz auf der Seite der Metallschicht erreicht wird, welche nicht durch den Träger geschützt ist. Zur Verbesserung des Korrosionsschutzes auf der vom Träger abgewandten Seite und zur Entspiegelung auf dieser Seite ist zweckmäßigerwise auch auf dieser Seite der Metallschicht noch eine dielektrische Deckschicht zwischen der Metallschicht und die Schutzschicht eingefügt. Vorteilhafte Weiterbildungen und Verbesserungen des im Hauptanspruch angegebenen Mehrschichtsystems sind in den Unteransprüchen und in der folgenden Beschreibung näher erläutert.The multilayer system according to the invention with the characteristic Features of the main claim has the advantage that without significant losses in terms of transmittance very good mechanical protection and corrosion protection in the visible spectral range the side of the metal layer which is not protected by the carrier is reached. To improve the Corrosion protection on the side facing away from the carrier and it is more practical to have an anti-reflective coating on this side also on this side of the metal layer a dielectric cover layer between the metal layer and inserted the protective layer. Advantageous further developments and improvements of the multi-layer system specified in the main claim are explained in more detail in the subclaims and in the following description.
Zeichnungdrawing
Ein Ausführungsbeispiel der Erfindung ist in der Zeichnung schematisch dargestellt und in der nachfolgenden Beschreibung näher erläutert. Die Figur zeigt eine Anordnung mit je einer dielektrischen Deckschicht auf beiden Seiten der Metallschicht und mit einer Polymerfilm-Schutzschicht auf der vom Träger abgewandten Oberfläche.An embodiment of the invention is shown in the drawing shown schematically and explained in more detail in the following description. The figure shows an arrangement each with a dielectric cover layer on both sides of the metal layer and with a polymer film protective layer on the surface facing away from the carrier.
Beschreibung des AusführungsbeispielesDescription of the embodiment
In der Figur ist mit 10 ein Träger bezeichnet, welcher vorzugsweise aus einer Polyesterfolie mit einer Dicke von 10 bis 200,um besteht. Alternativ kann als Träger 10 beispielsweise eine 10 bis 50,um dicke Acetatfolie oder eine 20 bis 100,um dicke PVC-Folie dienen. Auf demIn the figure, 10 denotes a carrier, which is preferably made of a polyester film with a thickness consists of 10 to 200 µm. Alternatively, a 10 to 50 .mu.m thick acetate film, for example, can be used as the carrier 10 or a 20 to 100 µm thick PVC sheet can serve. On the
ORIGINALORIGINAL
ό14.J O I Ö ό1 4th JOI Ö
Träger sitzt eine erste dielektrische Deckschicht 11 mit einer Dicke von 10 "bis U0,um, welche wenigstens ein Metalloxid enthält,, vorzugsweise jedoch eine Mischung aus Titanoxid und Wismutoxid oder gegebenenfalls separate Schichten aus diesen Metalloxiden aufweist. Auf der ersten dielektrischen Deckschicht 11 sitzt eine Metallschicht 12, vorzugsweise eine 5 bis 20 nm dicke Silberschicht, welche von einer zweiten dielektrischen Deckschicht 13 mit der gleichen Zusammensetzung wie die erste dielektrische Deckschicht 11 bedeckt ist. Den äußeren Abschluß auf der vom Träger 10 abgekehrten Seite bildet eine Schutzschicht 1h. Der Aufbau und die stoffliche Zusammensetzung der Schichtenfolge 10 bis 13 entspricht im wesentlichen der in der älteren Patentanmeldung P 31 hO 100 beschriebenen Ausführung. Dabei ist der Träger 10 dem einfallenden Licht zugewandt, die Schutzschicht 1U sitzt auf der einem Innenraum zugekehrten Seite des Meh*ischichtsystems, von welcher aus die Infrarotstrahlung auftrifft. Bei einer Umkehr des Strahlungsdurchgangs, derart, daß der Träger 10 der langwelligen Infrarotstrahlung ausgesetzt ist, erfolgt durch die Absorption im Träger eine stärkere Erwärmung der Folie Dann beruht die Wirkung der Wärmeschutzschicht auf deren geringem Emissionsvermögen für langwellige Strahlung.A first dielectric cover layer 11 with a thickness of 10 "to U0, which contains at least one metal oxide, but preferably a mixture of titanium oxide and bismuth oxide or optionally separate layers of these metal oxides, sits around the carrier Metal layer 12, preferably a 5 to 20 nm thick silver layer, which is covered by a second dielectric cover layer 13 with the same composition as the first dielectric cover layer 11. The outer termination on the side facing away from the carrier 10 is formed by a protective layer 1 hour and the material composition of the layer sequence 10 to 13 corresponds essentially to the design described in the earlier patent application P 31 hO 100. The carrier 10 faces the incident light, the protective layer 1U sits on the side of the multi-layer system facing an interior space from which the infrared radiation impinges ft. In the event of a reversal of the radiation passage, such that the carrier 10 is exposed to the long-wave infrared radiation, the absorption in the carrier causes greater heating of the film.
Die Wirkungsweise des Mehrschichtsystems ist derart, daß insgesamt ein hohes Reflexionsvermögen im Infrarot-Spektralbereich und ein hohes Transmissionsvermögen im sichtbaren Spektralbereich gewährleistet ist. Hierzu wird für den Träger 10 ein Material mit hohem Transmissionsvermögen für das sichtbare Licht ausgewählt, z.B. eine Polyesterfolie mit einer Dicke von 10 bis 200,um. Die Metallschicht 12, welche vorzugsweise aus Silber besteht, wird entspiegelt durch die dielektrischen Deckschichten 11 und 13, welche in ihrer DickeThe mode of operation of the multilayer system is such that overall a high reflectivity in the infrared spectral range and a high transmittance in the visible spectral range is guaranteed. For this a material with high transmittance for visible light is selected for the carrier 10, e.g. a polyester film having a thickness of 10 to 200 µm. The metal layer 12, which is preferably consists of silver, is anti-reflective by the dielectric cover layers 11 and 13, which in their thickness
Χ- 7.Ö18Χ- 7th Ö18
und in ihrem Material bezüglich der Brechzahl so ausgewählt sind, daß eine Interferenz entsteht und der an den Grenzflächen von der Metallschicht 12 reflektierte Anteil des sichtbaren Lichtes unterdrückt wird, so daß mit Ausnahme eines geringen Teiles praktisch alles einfallende Licht durch das Mehrschichtsystem hindurchtreten kann. Die dielektrische Deckschicht 11 ist hinsichtlich ihrer Zusammensetzung gleich aufgebaut wie die Deckschicht 13 und enthält vorzugsweise zwei Metalloxide, nämlich Titanoxid und Wismutoxid. Dabei kommt dem Titanoxid die Aufgabe zu,, die UV-Beständigkeit der Silberschicht zu erhöhen, während Wismutoxid eine stark korrosionshemmende Wirkung besitzt. In der gezeichneten Darstellung handelt es sich bei den Schichten 11 und 13 um Mischschichten der beiden Metalloxide, jedoch könnten die beiden Deckschichten 11 und 13 jeweils auch zweilagig mit getrennten Schichten der Metalloxide aufgebaut sein.and are selected in their material with respect to the refractive index so that an interference occurs and the At the interfaces of the metal layer 12 reflected portion of the visible light is suppressed, so that With the exception of a small part, practically all incident light pass through the multilayer system can. The dielectric cover layer 11 has the same structure as that in terms of its composition Cover layer 13 and preferably contains two metal oxides, namely titanium oxide and bismuth oxide. This is where the titanium oxide comes in the task of, to increase the UV resistance of the silver layer, while bismuth oxide has a strong anti-corrosive properties Has an effect. In the illustration shown, the layers 11 and 13 are mixed layers of the two metal oxides, but the two cover layers 11 and 13 could each also have two layers with separate layers of the metal oxides.
Die dielektrische Deckschicht 13 bewirkt für die Metallschicht einen Schutz gegen UV-Licht und einen Korrosionsschutz und ergänzt somit in vorzüglicher Weise die Schutzschicht lh, welche vorzugsweise dem mechanischen Schutz des Mehrschichtsystems dient. Da die Schichten 13 und 1k für Infrarotlicht ohne nennenswerte Absorption durchlässig sein müssen ist bei ihrem Aufbau und ihrer Stoffauswahl auf eine geringe Absorption im Bereich der Infrarotstrahlung, also etwa im Wellenlängenbereich zwischen 5 und 1+0,um zu achten. Hierbei haben sich neben dem bereits beschriebenen Aufbau für die dielektrische Deckschicht 13 hinsichtlich der Schutzschicht Ik Polymerfilme besonders bewährt, wobei die Bemessung der Schichtdicke und/oder die Materialauswahl des Polymerfilmes so gewählt ist, daß keine wesentliche Absorption von Infrarotstrahlung erfolgt. BesondersThe dielectric cover layer 13 provides protection against UV light and corrosion protection for the metal layer and thus complements the protective layer 1h in an excellent manner, which preferably serves to provide mechanical protection for the multilayer system. Since the layers 13 and 1 k have to be permeable to infrared light without significant absorption, a low absorption in the range of infrared radiation, i.e. in the wavelength range between 5 and 1 + 0, is to be observed in their structure and their choice of material. In addition to the structure already described for the dielectric cover layer 13 with regard to the protective layer Ik, polymer films have proven particularly useful, the dimensioning of the layer thickness and / or the material selection of the polymer film being chosen so that no significant absorption of infrared radiation occurs. Particularly
I ** IO 10 I ** IO 10
fafa
dünne Polymerfilm-Schutzschichten lassen sich aus Siloxan-Polymerisaten herstellen, wobei die Polymerisation vorzugsweise in einem Plasma erfolgt. Besonders bewährt hat sich hierbei Hexamethyldisiloxan (HMDS) welches einen ausreichenden Dampfdruck hat und somit ohne großen apparativem Aufwand als Dampf in die evakuierte Beschichtungsanlage eingelassen und in einer Glimmentladung als Schutzschicht ^h auf der dielektrischen Deckschicht 13 polymerisiert werden kann. Eine so hergestellte Schutzschicht 1U hat eine Dicke von vorzugsweise — 0,2/Um, im Höchstfall erreicht sie eine Schichtdicke - 1,um und gewährt als absolut porenfreie, dichte, hydrophobe Schutzschicht einen einwandfreien Schutz des darunterliegenden Schichtensystems. Die Schutzschicht lk kann weiterhin aus einem Lackfilm gebildet werden, welcher vorzugsweise auf die dielektrische Deckschicht 13 in einer Dicke zwischen 1 und 5,um aufgetragen, z.B. aufgesprüht wird.thin polymer film protective layers can be produced from siloxane polymers, the polymerisation preferably taking place in a plasma. Here, hexamethyldisiloxane (HMDS) has proved particularly suitable which has a sufficient vapor pressure and can thus be inserted without great expenditure on apparatus as a vapor in the evacuated coating system and in a glow discharge as a protective layer ^ h on the dielectric top layer 13 polymerized. A protective layer 1U produced in this way has a thickness of preferably -0.2 / .mu.m, at most it reaches a layer thickness of -.1. The protective layer 1k can furthermore be formed from a lacquer film, which is preferably applied, for example sprayed, to the dielectric cover layer 13 in a thickness between 1 and 5 μm.
Wenn andererseits die Schutzschicht "\k zur Erhöhung der mechanischen Stabilität dicker ausgebildet werden soll, erfolgt die Materialauswahl derart, daß ein Stoff mit geringer Absorption im Infrarot-Spektralbereich aufgebracht wird, vorzugsweise eine Schutzschicht 1U aus Polyäthylen oder Polypropylen. Hierbei wird die Schutzschicht 1k als Laminat mit dem restlichen Schichtsystem verbunden, wobei die Schutzschicht Ik selbst als Kunststoffolie ausgebildet ist. Eine andere Möglichkeit zum Auftragen einer derartigen Schutzschicht größerer Dicke besteht im Flammenspritzen.If, on the other hand, the protective layer "\ k is to be made thicker to increase the mechanical stability, the material is selected such that a substance with low absorption in the infrared spectral range is applied, preferably a protective layer 1U made of polyethylene or polypropylene. Here, the protective layer 1 k connected as a laminate to the rest of the layer system, the protective layer Ik itself being designed as a plastic film.
Das erfindungsgemäße Mehrschichtsystem betrifft also eine in Vakuumprozessen aufgebrachte Schichtenfolge 11, 12, 13, wobei auf den Träger 10 wenigstens eine Metallschicht 12 und vorzugsweise mehrere dielektrischeThe multilayer system according to the invention thus relates to a layer sequence 11, 12, 13 applied in vacuum processes, with at least one Metal layer 12 and preferably multiple dielectric
BADBATH
ΊΟΊΟ
Deckschichten 11 und 13 aufgedampft oder aufgestäubt sind. Die dielektrischen Deckschichten 11 und 13 sind nach Zusammensetzung bzw. schichtweisem Aufbau so optimiert, daß eine möglichst gute Beständigkeit gegen Umwelteinflüsse erreicht wird. Während die Schutzwirkung der dielektrischen Schichten 11 und 13 beim Einbau des Mehrschichtsystems zwischen Glas im allgemeinen ausreicht, ist bei Anwendung des Mehrschichtsystems auf Glas oder in Form von Rollos oder Vorhängen ein "zusätzlicher Schutz insbesondere gegen mechanische Beschädigungen notwendig. Hierzu wird auf den beschichteten Träger 10, d.h. beim Ausführungsheispiel auf die dielektrische Deckschicht 13 als Schutzschicht 1U ein Polymerfilm aufgetragen, der die optischen Eigenschaften des Schichtsystems nur wenig beeinträchtigt, jedoch einen sehr guten zusätzlichen mechanischen Schutz gewährleistet. Die Schichtdicke des Polymerfilms wird so eingestellt, daß zwar eine ausreichende mechanische Schutzwirkung erreicht wird, aber noch keine wesentliche Absorption der Infrarotstrahlung erfolgt und/oder das Material für diese zusätzliche Beschichtung wird so ausgewählt, daß eine möglichst gute Transmission der Schutzschicht 1 it im Infrarotbereich gegeben ist.Cover layers 11 and 13 are vapor-deposited or sputtered. The dielectric cover layers 11 and 13 are after Composition or layered structure optimized so that that the best possible resistance to environmental influences is achieved. While the protective effect of the dielectric layers 11 and 13 when installing the multilayer system between glass in general is sufficient when using the multilayer system Glass or in the form of roller blinds or curtains an "additional" Protection especially against mechanical damage is necessary. This is done on the coated Carrier 10, i.e. in the embodiment on the dielectric Cover layer 13 as protective layer 1U is a polymer film applied, which only slightly affects the optical properties of the layer system, but one very good additional mechanical protection guaranteed. The layer thickness of the polymer film is set so that that although a sufficient mechanical protective effect is achieved, but no significant absorption the infrared radiation takes place and / or the material for this additional coating is selected in such a way that that the best possible transmission of the protective layer 1 it is given in the infrared range.
Als Auftragsverfahren kommen Plasmapolymerisation, eine Beschichtung mit einem flüssigen Kunstharz nach einem der üblichen kontinuierlichen Auftragsverfahren oder z.B. auch die Bildung eines Laminates mit einer weiteren Kunststoffolie in Frage. ·Plasma polymerization, a coating with a liquid synthetic resin according to one of the usual continuous application processes or e.g. the formation of a laminate with a further plastic film in question. ·
Die durch Plasmapolymerisatiofi gebildeten Organosilikon-Filme erfüllen als Schutzschicht 1k die Bedingung einer geringen Infrarot-Absorption schon infolge der geringen Schichtdicke unter 1,um, die sich bei diesem Auftrags-The formed by Plasmapolymerisatiofi organosilicon films as a protective layer satisfy the condition 1 k a low infrared absorption already due to the small layer thickness of less than 1 in order to be in this order
324151Ü324151Ü
verfahren aus technischen Gründen ergibt. Kine derartige Schutzschicht 11I stellt aber infolge ihrer Dichtheit und ihrer mechanischen Eigenschaften trotz ihrer geringen Dicke einen Schutz gegen mechanische Einflüsse und einen zusätzlichen Schutz gegen korrosive Einflüsse dar. Nähere Einzelheiten über die Herstellung und die Eigenschaften solcher Filme sind z.B. in der Veröffentlichung "Plasma-Polymerisation" ACS Symposium Series 108, Washington D.C. 1979 beschrieben. Von den zur Verfügung stehenden Siloxanen hat sich insbesondere Hexamethyldisiloxan als Schutzschicht 1h bewährt, welches schon in einer Dicke von = 2,um einen guten Schutz gewährleistet und praktisch keine Veränderung der optischen Eigenschaften bewirkt.procedure for technical reasons. Kine Such a protective layer 1 1 I illustrates but due to its tightness and mechanical properties despite their small thickness provides protection against mechanical influences and an additional protection against corrosive influences represents. Further details about the preparation and properties of such films are, for example in the publication "Plasma -Polymerization "ACS Symposium Series 108, Washington DC 1979. Of the available siloxanes, hexamethyldisiloxane in particular has proven successful as a protective layer for 1 hour , which already at a thickness of 2 µm ensures good protection and practically does not change the optical properties.
Eine dickere Schutzschicht ^h ergibt sich beim Auftragen eines Lackfilms aus der flüssigen Phase, weil Lackfilme nicht in der zuvor beschriebenen geringen Dicke aufgebracht werden können. Bei Verwendung eines Acrylharzes, das im Sprühverfahren aufgetragen wird, nimmt die Infrarotabsorption der Schutzschicht 1h mit zunehmender Dicke rasch zu, wobei sich bei einer Schutzschichtdicke von 20,um bereits eine Absorption von etwa 50 % der Infrarotstrahlung in der Schutzschicht 1h ergibt. Dieser Absorptionswert sollte auf keinen Fall überschritten werden, wobei sich jedoch bei Verwendung anderer Lacke mit geringerer Infrarot-Absorption auch größere Schutzschichtdicken als zulässig erweisen können. Infrage kommen neben Acrylaten auch Lacke auf Fluorkohlenwasserstoff-Basis, Polyesterharze oder Epoxidharze. Da aber alle Lacksysteme starke Absorptionsbanden im Infrarotbereich besitzen ist eine sorgfältige Abstimmung der Dicke erforderlich, wenn eine Beeinträchtigung der IR-Reflexionseigenschaften der Metall- A thicker protective layer ^ h is obtained when applying a resist film from the liquid phase, because the coating films can not be applied in the above-described small thickness. When using an acrylic resin that is applied by spraying, the infrared absorption of the protective layer 1 h increases rapidly with increasing thickness, with a protective layer thickness of 20 µm already resulting in an absorption of about 50 % of the infrared radiation in the protective layer 1 h . This absorption value should not be exceeded under any circumstances, although if other lacquers with lower infrared absorption are used, thicker protective layers may prove to be permissible. In addition to acrylates, fluorocarbon-based paints, polyester resins or epoxy resins are also possible. However, since all paint systems have strong absorption bands in the infrared range, careful coordination of the thickness is necessary if the IR reflection properties of the metal
BAO ORIGINALBAO ORIGINAL
schicht 12 vermieden werden soll. Entsprechend den durchgeführten Versuchen sollte die Dicke der Schutzschicht 1^ bei Verwendung einer Lackschicht nicht unter 1 ,um liegen, damit noch ein geschlossener und porenfreier Auftrag möglich ist. Andererseits sollte die Lackschichtdicke nicht über 5/um betragen, damit das Infrarot-Reflexionsvermögen der Metallschicht 12 nicht unter einen Wert von ca 80 % des Mehrschichtsystems ohne Schutzschicht 1h absinkt. In diesem Dickenbereich ist auch die im sichtbaren Spektralbereich auftretende Beeinträchtigung der optischen Eigenschaften, insbesondere durch Streuung, Schlierenbildung und Absorption noch vernachlässigbar gering.layer 12 should be avoided. According to the tests carried out, the thickness of the protective layer should not be less than 1 μm when using a layer of lacquer, so that a closed and pore-free application is still possible. On the other hand, the lacquer layer thickness should not be more than 5 μm, so that the infrared reflectivity of the metal layer 12 does not drop below a value of about 80 % of the multilayer system without a protective layer for 1 hour . In this thickness range, the impairment of the optical properties occurring in the visible spectral range, in particular due to scattering, streaking and absorption, is still negligibly small.
Zur Herstellung eines Laminates aus der Schutzschicht 1h und den darunterliegenden Schichten des Mehrschichtsystems unter Verwendung einer Kunststoffolie wird als Folienmaterial vorzugsweise Polyäthylen verwendet, welches eine gute Durchlässigkeit für Infrarotstrahlung besitzt. Ähnliche gute Eigenschaften hat auch eine Polypropylenfolie. H for producing a laminate of the protective layer 1 and the underlying layers of the multilayer system by using a plastic film is used as film material, preferably polyethylene, which has a good permeability to infrared radiation. A polypropylene film also has similar good properties.
Claims (1)