DE3216634A1 - Method of sealing a crack or joint - Google Patents

Method of sealing a crack or joint

Info

Publication number
DE3216634A1
DE3216634A1 DE19823216634 DE3216634A DE3216634A1 DE 3216634 A1 DE3216634 A1 DE 3216634A1 DE 19823216634 DE19823216634 DE 19823216634 DE 3216634 A DE3216634 A DE 3216634A DE 3216634 A1 DE3216634 A1 DE 3216634A1
Authority
DE
Germany
Prior art keywords
plastic
crack
concrete
natural stone
masses
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE19823216634
Other languages
German (de)
Inventor
Othmar 1130 Wien Marek
Karl Dr. 2412 Wolfsthal Nay
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NGT NOVA GRUENDUNGSTECHNIK
Original Assignee
NGT NOVA GRUENDUNGSTECHNIK
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NGT NOVA GRUENDUNGSTECHNIK filed Critical NGT NOVA GRUENDUNGSTECHNIK
Publication of DE3216634A1 publication Critical patent/DE3216634A1/en
Withdrawn legal-status Critical Current

Description

GRÜNECKER, KINKELDEY,GRÜNECKER, KINKELDEY,

PA TENTANWALlIiPA TENTANWALlIi

A. GRÜNECKER, on»«; DR H. KINKELDEY. &.h..-ingA. GRÜNECKER, on »«; DR H. KINKELDEY. & .h ..- ing

DR W. STOCKMAIR1 OIPL-lt.'V.ÄEDR W. STOCKMAIR 1 OIPL-lt.'V.ÄE

DR K. SCHUMANN. chpl.-w'3 DR K. SCHUMANN. chpl.-w ' 3

P. H. JAKOB, am.-»«!P. H. JAKOB, am.- ""!

DR G. BEZOLD. »pl-che-mDR G. BEZOLD. »Pl-che-m

W. MEISTER. oipl-»/iW. MASTER. oipl - »/ i

H. HILGERS. [im.«H. HILGERS. [in the."

DR H. MEYER-PLATH. [»μι mgDR H. MEYER-PLATH. [»Μι mg

GESELLSCHAFT FÜR NEUE GRi3HDU¥GSTECfflIK GESELLSCHAFT H.B.E.
Hietzinger Hauptstraße 41
1130 Wien
ÖsterreichSOCIETY FOR NEW GRi3HDU ¥ GSTECfflIK SOCIETY HBE
Hietzinger Hauptstrasse 41
1130 Vienna
Austria

Terfahreix zur Abdichtung eines Risses oder FugeTerfahreix to seal a crack or Gap

8000 MÜNCHEN 228000 MUNICH 22

MAXIMIUANSTRASSE 43MAXIMIUANSTRASSE 43

4. Mai 1982 P 17 289-dgMay 4, 1982 P 17 289-dg

TELEFON iO 89) 22 2B 62TELEPHONE OK 89) 22 2B 62

TELEX 05-29 3ÖO TELEGRAMME; MONAPAT*TELEX 05-29 3ÖO TELEGRAMS; MONTH *

Beschreibungdescription

Die Erfindung bezieht sich auf ein Verfahren zur Abdichtung eines Risses oder einer Fuge in Beton oder Naturstein oder einer rißanfälligen Beton-, oder Natursteinstelle mittels Kunstharzmassen.The invention relates to a method for sealing a crack or a joint in concrete or natural stone or a crack-prone Concrete or natural stone area using synthetic resin compounds.

Infolge von Temperaturunterschieden, Belastungen u.dgl. treten in Beton- und Natursteinkörpern Risse auf, die abgedichtet werden müssen, um das Eindringen von Feuchtigkeit und damit eine weitere Zerstörung des Bauwerks, z.B. das Lecken von Staumauern zu verhindern. Die bisher angewendeten Methoden waren jedoch nicht zur Herstellung von Abdichtungen geeignet, die den im Bereich der Risse durch Spannungen und Scher- und Druckkräfte hervorgerufenen Bewegungen dauerhaft standhalten.As a result of temperature differences, loads and the like, cracks appear in concrete and natural stone bodies, which are then sealed must to prevent the ingress of moisture and thus further destruction of the structure, e.g. the leakage of dams to prevent. However, the methods used so far were not suitable for making seals that match those in the area the cracks permanently withstand movements caused by tension and shear and pressure forces.

Der Erfindung liegt die Aufgabe zugrunde, die Nachteile der bisherigen Verfahren zu vermeiden und eine den auftretenden Beanspruchungen gewachsene, dauerhafte Abdichtung eines Risses in Beton oder Naturstein oder einer rißanfälligen Beton- oder Natursteinstelle mittels Kunstharzmassen zu schaffen.The invention is based on the disadvantages of the previous Procedure to avoid and a permanent sealing of a crack in concrete that can cope with the stresses that occur or natural stone or a crack-prone concrete or natural stone area using synthetic resin compounds.

Zur Lösung dieser Aufgabe sieht das erfindungsgemäße Verfahren vor, daß zumindest auf die Seitenflächen einer vorgefertigten Einbuchtung im Bereich der abzudichtenden Stelle zunächst eine unter Bildung einer Haftbrücke mit guter Haftfestigkeit an BetonThe method according to the invention seeks to achieve this object before that at least on the side surfaces of a prefabricated Indentation in the area of the point to be sealed initially one with the formation of an adhesive bridge with good adhesion to concrete

und/oder Naturstein aushärtbare Kunststoffmasse aufgetragen und in die verbleibende Einbuchtung eine weitere, elastisch dshnbar aushärtende Kunststoffmasse eingebracht wird, und daß dann die beiden Kunststoffmassen gemeinsam aushärten gelassen werden. Die Haftfestigkeit der Haftbrücke am Naturstein oder Beton muß größer sein als die zur Dehnung der elastischen Kunststoffmasse aufzuwendenden Zugkräfte.and / or natural stone curable plastic compound applied and in the remaining indentation a further, elastically resiliently hardening plastic compound is introduced, and that then allowed to harden the two plastic masses together will. The adhesive strength of the adhesive bridge on natural stone or concrete must be greater than that required to stretch the elastic plastic compound tensile forces to be applied.

Vorzugsweise werden gemäß der Erfindung zwei Kunststoffmassen eingesetzt, die im wesentlichen aus gleichen Ausgangsmaterialien, jedoch mit unterschiedlichen Mengenverhältnissen gebildet werden. Auf diese Weise wird die gute Verbindung zwischen Haftbrücke und elastischer Kunststoffmasse gewährleistet.According to the invention, two plastic compounds are preferably used used, which are formed essentially from the same starting materials, but with different proportions. In this way, the good connection between the adhesive bridge and the elastic plastic compound is guaranteed.

Eine vorteilhafte Ausführungsform des erfindungsgemäßen Verfahrens besteht darin, daß man als Kunststoffmassen an sich bekannte, in Gegenwart von Polyaminen aushärtbare Massen auf Basis von Epoxidharz und Polybutadien oder Butadien-Styrol-Mischpolymerisat, gegebenenfalls mit geeigneten Füllstoffen, einsetzt. Dieses Verfahren ist auch auf nassem Grund und bei Temperaturen unter 00C anwendbar. Die erhaltenen Dichtungen haben einen dem pH-Wert des Betons oder Natursteins entsprechenden pH-Wert.An advantageous embodiment of the process according to the invention consists in using known plastics compositions which are curable in the presence of polyamines and are based on epoxy resin and polybutadiene or butadiene-styrene copolymer, optionally with suitable fillers. This method can also be used on wet ground and at temperatures below 0 ° C. The seals obtained have a pH value corresponding to the pH value of the concrete or natural stone.

Die vorstehend erwähnten, an sich bekannten, in Gegenwart von Polyaminen aushärtbaren Massen auf Basis von Epoxidharz und Polybutadien oder Butadien-Styrol-Mischpolymerisat haben z.B. folgende Zusammensetzungen:The above-mentioned, known per se, in the presence of Polyamines curable compositions based on epoxy resin and polybutadiene or butadiene-styrene copolymer have e.g. the following compositions:

Butadien-Styrole Epoxidharzgehalt Polyamine als Härter bzw. Polybutadien der erfindungsgemäßen MischungButadiene-styrenes Epoxy resin content Polyamines as hardeners or polybutadiene of the invention mixture

1.)1.) 5050 730730 220220 2.)2.) 100100 700700 200200 3.)3.) 150150 650650 200200 4.)4.) 200200 600600 200200 5.)5.) 250250 550550 200200

Diese Anteile sind jeweils auf 1000 Gewichtseinheiten bezogen.These proportions are each based on 1000 weight units.

Die Zusammensetzung 1.) ergibt ein sehr hartes Endprodukt. In der Reihenfolge der Zusammensetzungen^.), 3.), 4.) 5.) nimmt die Härte ab, und das Endprodukt wird dementsprechend elastischer sowie nachgiebiger und dehnbarer.The composition 1.) gives a very hard end product. In the order of the compositions ^.), 3.), 4.) 5.) takes the hardness decreases, and the end product becomes correspondingly more elastic, more flexible and more ductile.

Erfindungsgemäß kann an Stelle von Epoxidharz auch Methylmethacrylat verwendet werden. Ebenso können aber auch andere Duroplaste beim erfindungsgemäßen Verfahren Verwendung finden. Als Zuschlagstoffe bzw. Füllstoffe können verschiedene Asbestqualitäten, Gummigranulate, Farbpigmente u.dgl. verwendet werden.According to the invention, methyl methacrylate can also be used instead of epoxy resin be used. However, other thermosets can also be used in the method according to the invention. as Aggregates or fillers can contain various asbestos qualities, Rubber granules, color pigments and the like can be used.

Die erfindungsgemäß erhaltenen Abdichtungen weisen auch bei Temperaturen unter 00C eine Bruchdehnung von mindestens 15% auf und halten gleichzeitig einer Dauerdruckbelastung von mindestens 20 kg/cm stand.The seals obtained according to the invention have an elongation at break of at least 15% even at temperatures below 0 ° C. and at the same time withstand a permanent pressure load of at least 20 kg / cm.

Die Erfindung wird durch die folgenden Beispiele auf die sie jedoch nicht beschränkt ist, näher erläutert.The invention is illustrated by the following examples but is not limited, explained in more detail.

-β--β-

Beispiel 1: HaftbrückeExample 1: Bonding bridge

Man stellt eine Zwei-Komponenten-Spachtelmasse aus folgenden Bestandteilen her:A two-component filler is made from the following ingredients from:

Harzanteil (670 g niedermolekulares flüssiges Epoxidharz mit einem Epoxy-Äquivalentgewicht von 175-210 g + 30 g Asbestfaser, Faserlänge 1-2 mm) 700 gResin content (670 g of low molecular weight liquid epoxy resin with an epoxy equivalent weight from 175-210 g + 30 g asbestos fiber, fiber length 1-2 mm) 700 g

Härter (bestehend aus aliphatischem Polyamin und elastomeren Copolymerisaten als Modifizierungs- und Elastifizierungsmittel imHardener (consisting of aliphatic polyamine and elastomeric copolymers as modification and elasticizing agents im

Verhältnis 3:1) 300 gRatio 3: 1) 300 g

.Nach 24 h hat die ausgehärtete Mischung ca. 700 kg/cm Druckfestigkeit, 230 kg Biegezug- und 160 kg/m Zugfestigkeit undAfter 24 hours, the hardened mixture has a compressive strength of approx. 700 kg / cm, 230 kg flexural strength and 160 kg / m tensile strength and

2 eine Haftfestigkeit von ca. 110 kg/cm , sodaß immer der Beton2 an adhesive strength of approx. 110 kg / cm, so that the concrete is always

reißt.rips.

Beispiel 2: HaftbrückeExample 2: bonding bridge

Man stellt eine niedrig viskose und streichbare Masse aus den folgenden Bestandteilen her:A low-viscosity and spreadable mass is made from the the following components:

680 g niedrig viskoses modifiziertes Bisphenol A plus Epichlorhydrin Epoxidharz mit einem Epoxy-Äquivalentgewicht von 190-210 g680 g of low viscosity modified bisphenol A plus Epichlorohydrin Epoxy resin with an epoxy equivalent weight of 190-210 g

20 g Asbestfaser wie in Beispiel 1 300 g Härter wie in Beispiel 120 g asbestos fiber as in example 1 300 g hardener as in example 1

Nach 24 h hat die ausgehärtete Mischung ca. 600 kg Druck-,After 24 hours, the hardened mixture has approx. 600 kg of pressure,

2 210 kg Biegezug-, 150 kg Zug- und 96 kg/cm Haftfestigkeit, so daß der Beton reißt.2 210 kg flexural strength, 150 kg tensile strength and 96 kg / cm adhesive strength, so that the concrete cracks.

Beispiel 3: Elastische FugenmasseExample 3: elastic grout

Man stellt eine Mörtelmasse aus folgenden Bestandteilen her:A mortar mass is made from the following components:

250 g Epoxidharz wie in Beispiel 2 250 g Härter, bestehend aus250 g of epoxy resin as in Example 2 250 g of hardener, consisting of

500 g Aminobasisgemisch und500 g amino base mixture and

500 g Elastomeren Copolymerisaten500 g of elastomer copolymers

500 g Gummigranulat (250 g 0,5-3 mm Durchmesser500 g rubber granulate (250 g 0.5-3 mm diameter

25Og 5 - 8 mm Durchmesser).25Og 5 - 8 mm diameter).

Nach einer Aushärtungszeit von 24 h erreicht man bei einem Zug vonAfter a hardening time of 24 hours, one pull of

2
6-8 kg/cm eine Dehnung von 25%.2
6-8 kg / cm an elongation of 25%.

Beispiel 4: Elastische FugenmasseExample 4: elastic grout

Man stellt eine Spachtelmasse aus folgenden Bestandteilen her:A filler is made from the following components:

325 g Epoxidharz wie in Beispiel 2 325 g Härter wie in Beispiel 3 175 g Gummigranulat 0,5 - 3 mm 175 g Gummigranulat 5-8 mm Beispiel 5: Elastische Fugenmasse325 g epoxy resin as in example 2 325 g hardener as in example 3 175 g rubber granulate 0.5-3 mm 175 g rubber granulate 5-8 mm Example 5: Elastic joint compound

Man mischt folgende Bestandteile:Mix the following ingredients:

-SF--SF-

100 g Benzoylperoxydpulverhärtar 75% 300 g Gummigranulat (200 g 0,5 - 3 ram und100 g benzoyl peroxide powder hardener 75% 300 g rubber granulate (200 g 0.5 - 3 ram and

100 g 5 - 8 mm)100 g 5 - 8 mm)

500 g niedrig viskoses Methylmethacrylatharz 100 g Elastomeres Copolymerisat.500 g of low viscosity methyl methacrylate resin 100 g of elastomeric copolymer.

Diese Fugenmasse kann naß auf naß haftend mit einer Epoxidharzbrücke verbunden werden.This grout can be adhered wet on wet with an epoxy resin bridge get connected.

Claims (4)

NGT Gesellschaft für neue Gründungstechnik Gesellschaft m.b.H. in Wien (Österreich)NGT Society for New Foundation Technology Gesellschaft m.b.H. in Vienna (Austria) Verfahren zur Abdichtung eines Risses oder FugeMethod of sealing a crack or joint Patentansprüche :Patent claims: Verfahren zur Abdichtung eines Risses oder Fuge in Beton oder Naturstein oder einer rißanfälligen Beton- oder Natursteinstelle mittels Kunststoffmassen, dadurch gekennzeichnet, daß zumindest auf die Seitenflächen einer vorgefertigten Einbuchtung im Bereich der abzudichtenden Stelle zunächst eine unter Bildung einer Haftbrücke mit guter Haftfestigkeit an Beton und/oder Naturstein aushärtbare Kunststoffmasse aufgetragen und in die verbleibende Einbuchtung eine weitere elastisch dehnbar aushärtende Kunststoffmasse eingebracht wird, und daß dann die beiden KunststoffmassenProcess for sealing a crack or joint in concrete or natural stone or a crack-prone concrete or natural stone area by means of plastic compounds, characterized that at least on the side surfaces of a prefabricated indentation in the area of the point to be sealed initially a plastic mass which can be hardened to form an adhesive bridge with good adhesive strength on concrete and / or natural stone applied and in the remaining indentation another elastically stretchable hardening plastic compound is introduced, and that then the two plastic compounds gemeinsam aushärten gelassen werden.allowed to cure together. 2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß man zwei Kunststoffmassen einsetzt, die im wesentlichen aus gleichen Ausgangsmaterialien, jedoch mit unterschiedlichen Mengenverhältnissen bestehen.2. The method according to claim 1, characterized in that that you use two plastic compounds, which essentially consist of the same starting materials, but with different proportions. 3. Verfahren nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß als Kunststoffmassen an sich bekannte, in Gegenwart von Polyaminen aushärtbare Massen auf Basis von Epoxydharz und Polybutadien oder Butadien-Styrol-Mischpölymerisat mit geeigneten Füllstoffen eingesetzt werden.3. The method according to claim 1 or 2, characterized in that that known as plastic masses, curable in the presence of polyamines masses based on Epoxy resin and polybutadiene or butadiene-styrene mixed polymer can be used with suitable fillers. 4. Verfahren nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß als Kunststoffmassen an sich bekannte, in Gegenwart von Benzoylperoxid härtende Massen auf Basis von Methylmethacrylat und verträglichen elastomeren Copolymerisaten als Elastifizierungsmittel mit geeigneten Füllstoffen eingesetzt werden.4. The method according to claim 1 or 2, characterized in that that known as plastic masses, hardening in the presence of benzoyl peroxide masses based on Methyl methacrylate and compatible elastomeric copolymers as elasticizers with suitable fillers can be used.
DE19823216634 1981-05-12 1982-05-04 Method of sealing a crack or joint Withdrawn DE3216634A1 (en)