DE3109632C2 - Mechanically compressible material - Google Patents
Mechanically compressible materialInfo
- Publication number
- DE3109632C2 DE3109632C2 DE3109632A DE3109632A DE3109632C2 DE 3109632 C2 DE3109632 C2 DE 3109632C2 DE 3109632 A DE3109632 A DE 3109632A DE 3109632 A DE3109632 A DE 3109632A DE 3109632 C2 DE3109632 C2 DE 3109632C2
- Authority
- DE
- Germany
- Prior art keywords
- calcium
- weight
- fly ash
- sludge
- anhydrite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
Es wird ein mechanisch verdichtbares Material aus künstlichen Puzzolanen, Calciumsulfat, alkalisch reagierenden Calciumverbindungen und Zuschlagstoffen beschrieben, das das Calciumsulfat als Dihydrat und/oder Anhydrit in Korngrößen von 4 bis 32 mm enthält und sich nach der mechanischen Verdichtung noch chemisch verfestigt.A mechanically compressible material made of artificial pozzolans, calcium sulfate, alkaline reacting calcium compounds and additives is described which contains calcium sulfate as dihydrate and / or anhydrite in grain sizes of 4 to 32 mm and which is chemically solidified after mechanical compression.
Description
3 43 4
Flugstaub und des aus Rauchgasentschwefelungsanla- Konsolidierung von Schichten aus diesen Materialien
gen, in denen Kalk verarbeitet wird, entnehmbarem CaI- tritt meist erst nach einer Standzeit von Jahren ein. Auciumsulfats,
wobei der Flugstaub zusammen mit dem in ßerdetn sind die nach den vorerwähnten Verfahren erden
Rauchgasen enthaltenen Schwefeldioxid zu einem zeugten Produkte gegen Wasser nicht beständig und
wasserhaltigen Schlamm ausgewaschen wird. Dieser 5 werden demzufolge durch Regen und im Kontakt mit
Schlamm wird anschließend thermisch so behandelt, Grundwaser ausgelaugt Hierdurch wird die Festigkeit
daß das darin enthaltene Cakäumsulfat-Dihydrat in die der Schiebten aus solchen Produkten ebenfalls in unerwasseränneren
Formen des Anhydrits oder Halbhy- wünschter Weise vermindert und der Salzgehalt des
drats übergeht. Die auf diese Art erhaltene Suspension Grundwassers erhöht Ettringit selbst macht das das
härtet dann nach Formgebung zu Baumaterialien, wie io Material nicht frostempfindlich. Der Wasseranteil liegt
beispielsweise Platten oder Bausteine aus. Der Anteil chemisch gebunden vor. Die Anfälligkeit gegen Frost ist
der Flugasche an dem Feststoffgehalt der Ausgangs- auf die Porosität bzw. Instabilität (Risse) der Materischlämme
soD dabei zwischen 10 und 70 Gew.-% — alien zurückzufuhren. Wenn in den gemäß den vorbebezogen
auf den Feststoffanteil — liegen. kannten Verfahren erzeugten Produkten Ettringit vor-LetztIkhistinderDE-OS28
10 173 ein Verfahren zur is liegt, so sind diese gegenüber Kohlendioxid enthalten-Hersteliung
verfestigter Produkte aus wasserhaltigen, dim Wasser, wie beispielsweise Regenwasser, instabil,
schlammförmigen oder pastösen Stoffen und Verfesti- da sich Ettringit mit Kohlendioxid unter wesentlicher
gungsmitteln vorgeschlagen, nach dem den schlammför- Vergrößerung seines Volumens zersetzt
migen oder pastösen Stoffen Calciumsulfat vorzugswei- Hieraus ergibt sich die Aufgabe, unter Verwendung
se in einer Form zugesetzt wird, die weniger Kristall- 20 chemisch vergleichbarer Ausgangsmatenalien ein mewasser
enthält .*ts Calciumsulfat-Dihydrat Zusätzlich chanisch mit gebräuchlichen Baugeräten verdichtbares
iiöTiTicn des Gstiischsr! sus disssa Ko^npcnsnten »tu»h Matsrialgenüsch zu finden, das raumstabil ist, bei dem
unter HydratbDdung reagierende aluminat- und silicat- die Gefahr von Einbrüchen oder Setzungen ebensowehaltige
Stoffe, oder Stoffe mit hoher spezifischer Ober- nig besteht, wie die Gefahr der Auslaugung,
fläche, zugemischt werden. Diese Maßnahmen haben 25 Es wurde ein mechanisch verdichtbares Material für
zum Ziel, das in den schlammförmigen oder pastösen Straßen-, Landschafts- und Deponiebau oder für Zwek-Stoffen
enthaltene Wasser zu binden und den Feststoff- ke der Verfüllung aus künstlichen Puzzolanen, Calciumanteil
dieser schlammförmigen oder pastösen Stoffe so sulfat und alkalisch reagierenden Calciumverbindungen
zu verfestigen, daß die entstehenden und gegebenenfalls gefunden. Erfindungsgemäß muß dieses Material das
geformte Produkte leicht zu handhaben und zu stapeln 30 Calciumsulfat als Calciumsulfat-Dihydrat und/oder An-
bzw. zu deponieren sind. hydrit in Korngrößen von 4 bis 32 mm enthalten.Airborne dust and the calcium that can be removed from flue gas desulphurization systems, in which lime is processed, usually only occurs after a period of years. Aucium sulphate, the flue dust and the sulfur dioxide contained in the flue gases contained in the above-mentioned processes being washed out to form a product that is not resistant to water and water-containing sludge. This 5 is consequently thermally treated by rain and in contact with mud, ground water is leached. This reduces the strength of the calcium sulfate dihydrate contained in it in that of the products from such products, likewise in unsanitary forms of anhydrite or semi-hygienic the salinity of the drats passes over. The suspension of groundwater obtained in this way increases ettringite itself, which then hardens after shaping into building materials, such as material not sensitive to frost. The water content is made up of panels or building blocks, for example. The proportion chemically bound before. The susceptibility to frost of the fly ash is attributable to the solids content of the initial alien to the porosity or instability (cracks) of the material sludge soD between 10 and 70% by weight. If in the according to the referred to the solid content - lie. Known processes produced products Ettringit before-Last IkhistinderDE-OS28 10 173 a process is available, so these are against carbon dioxide-Production of solidified products from water-containing, dim water, such as rainwater, unstable, sludge-like or pasty substances and solidification because Ettringit Proposed with carbon dioxide under essential supply agents, after which decomposes the sludge för- enlargement of its volume
is-shaped or pasty substances calcium sulfate vorzugswei- Hence the task se using added in a form which contains less crystal 20 chemically similar starting matenals a mewasser. * ts calcium sulfate dihydrate addition mechanically compressible with conventional Equipment iiöTiTicn of Gstiischsr! sus disssa Ko ^ npcnsnten »tu» h Matsrialgenüsch, which is spatially stable, in which there is a risk of hydrate and silicate reacting with hydrated dung, the danger of break-ins or settlements, or substances with a high specific surface, as there is the danger of Leaching,
surface to be mixed in. These measures have 25 A mechanically compressible material for the goal of binding the water contained in the muddy or pasty road, landscaping and landfill construction or for secondary materials and the solids of the backfill from artificial pozzolans, calcium content of these muddy or pasty substances to solidify sulphate and alkaline reacting calcium compounds that the resulting and possibly found. According to the invention, the molded product must be easy to handle and stack. contains hydrite in grain sizes from 4 to 32 mm.
sulfate als Bindemittel für die Gemische aus Feststoffen maß einzusetzenden Calciumsulfate im Bereich von 4Sulphates as binders for the mixtures of solids measured calcium sulphates in the range of 4
und Wasser Verwendung finden, hegen sie in den zu bis 16 mm liegen.and water are used, they are up to 16 mm.
verfestigenden Ausgar.gsgemischen feinteilig und mit 35 Für das mechanisch verdichtbare Material der Erfineinem im Vergleich zu Calciumsulfat-Jihydrat geringe- dung kann ein gebrochener Rohgips oder Naturanhren Kristallwassergehalt vor, so daß sie in der Lage sind, ydrit eingesetzt werden, dessen Korngrößenverteilung durch Rehydratation zum Dihydrat diesen Gemischen den angegebenen Grenzen entspricht Es ist jedoch Wasser zu entziehen und sie gleichzeitig zu verfestigen. auch möglich, diesen Rohgips bzw. Naturanhydrit ganz Auch bei Verwendung der Kombination von Flugasche 40 oder teilweise durch synthetisches Oiteiumsulfat-Dih- und alkalisch reagierenden Calciumverbindungen, wie ydrat oder synthetischen Anhydrit zu ersetzen, der bei beispielsweise Calciumoxid oder-hydroxid, als verfesti- zahlreichen chemischen Verfahren als Nebenprodukt gendes Bindemittel, liegen diese Ausgangsmatenalien in anfällt Da diese synthetischen Calciumsulfate, die als den zu verfestigenden pastösen Schlämmen in feinteili- Nebenprodukte — beispielsweise bei der Erzeugung ger Form vor und reagieren nur dann zu dem verfesti- 45 von Phosphorsäure — aus Rohphosphat und Schwefeigenden Ettringit säure, bei der Entschwefelung von Rauchgasen mit CaI-solidifying Ausgar.gsgemischen finely divided and with 35 For the mechanically compressible material of the inventions In comparison to calcium sulphate jihydrate, a broken raw plaster of paris or natural grain can be reduced Water of crystallization content before, so that they are able to be used ydrite, its grain size distribution however, by rehydration to the dihydrate these mixtures correspond to the specified limits To withdraw water and to solidify them at the same time. also possible to use this raw plaster of paris or natural anhydrite entirely Even when using the combination of fly ash 40 or partly through synthetic Oiteiumsulfat-Dih- and alkaline calcium compounds such as ydrate or synthetic anhydrite to replace the for example calcium oxide or hydroxide, as a solidification numerous chemical process as a by-product As these synthetic calcium sulfates, which are used as the pasty sludge to be solidified into fine-particle by-products - for example during production 45 of phosphoric acid - from rock phosphate and sulphurous substances Ettringit acid, in the desulfurization of flue gases with CaI
ciumcarbonat oder -hydroxid, meist als feinteilige Kri-cium carbonate or hydroxide, usually as finely divided
3 CaO · Al2O3 ■ 3 CaSO4 · 31 H2O stallisate entstehen, ist es notwendig, diese Kristallisate3 CaO · Al 2 O 3 ■ 3 CaSO 4 · 31 H 2 O crystallizates arise, it is necessary to these crystallizates
nach der Abtrennung aus dem Reaktionsgemisch undafter separation from the reaction mixture and
wenn in dem Schlamm auch Sulfationen in ausreichen- so folgendem Waschen in an sich bekannter Weise zu kom-if sulphate ions in the sludge are also sufficient, the following washing can be done in a manner known per se.
der Menge vorhanden sind. Im plastischen Materialzu- paktieren, brikettieren, granulieren oder zu pelletisie-the crowd are available. Packing, briquetting, granulating or pelletizing in plastic material
stand führt die Ettringit-Bildung zu keiner Materialex- ren, um auf diese Weise aus diesen Kristallisa ten einThe ettringite formation does not lead to any material extrusion in this way from these crystallites
pansion. Kristallisiert der Ettringit örtlich unter VoIu- körniges Produkt zu erhalten, dessen Korngrößen impansion. If the ettringite crystallizes locally to obtain a solid product whose grain sizes are in
menzunahme des Feststoffs, so ist dieser Vorgang mit beanspruchten Bereich von 4 bis 32 ram, vorzugsweise 4If there is an increase in the solids content, this process is with a claimed range of 4 to 32 ram, preferably 4
stallwasser gebunden werden. Nach Auffüllung der zur der Erfindung ist lediglich Magerungskomponente undstall water are bound. After filling the for the invention is only lean component and
Kristallisationsdruck die Zugfestigkeit des Baustoffes Als Bindemittel und Feinkornanteil enthalten die rneüberschritten, was letztlich zu Rissebildungen und chanisch verdichtbaren Materialien der Erfindung au-Treiberscheinungen führt Dabei kann das Kristallwas- 60 ßerdem Puzzolane, wie beispielsweise ein durch Verser des Ettringits aus Wasser für Verdichtung oder aus mahlen des Granulats einer basischen Hochofenschlak- ;'■'· Durchfeuchtung des Baukörpers stammen. Die nach ke erhaltenes Schlackenmehl. Ansteile dieses Schlak- !·_. diesen vorbekannten Verfahren erzeugten und verfe- kenmehls können die erfindungsgemäßen Materialien ψ stigten Produkte können nur in begrenztem Umfang zur auch glasige, vorzugsweise Calciumoxid enthaltende y Landverfüllung und im Straßenbau eingesetzt werden, 65 Flugasche enthalten, der noch alkalische Stoffe als An-■'; da sie sich nur schlecht und unzureichend verdichten reger zugemischt sein können, die freien Kalk enthalten fj lassen, und als Folge davon treten Einbrüche oder Set- oder wie dieser wirken. Als Bindemittel und Feinkorn-Il zungen auf, die nicht erwünscht sind. Eine weitgehende anteil können die Materialien der Erfindung auch Ze-Crystallization pressure, the tensile strength of the building material. As a binder and fine-grain fraction, the excess contains, which ultimately leads to the formation of cracks and mechanically compressible materials of the invention the granulate of a basic blast furnace slag; '■' · moisture penetration of the building. The slag meal obtained after ke. Raising this slap-! · _. these previously known processes generated and verfe- kenmehls materials of the invention can ψ stigten products can only to a limited extent also glassy, preferably calcium oxide containing y landfill and used in road construction, containing 65 fly ash, the more alkaline substances as arrival ■ '; Since they can only be compressed poorly and inadequately, they can be mixed in more intensely , which allow free lime to contain fj, and as a result of this break-in or set-in or act like this. As binders and fine grain Il tongues, which are not desired. A large proportion of the materials of the invention can also ze-
5 65 6
ment enthalten, wobei ein an Tricalciumaluminat anner £5Gew.-% PZ 35 Fment, with a tricalcium aluminate anner £ 5 wt .-% PZ 35 F
y 1164, mit hohem Sulfatwiderstand zu bevorzugen ist, stoff atro
% wenn die Materialien der Erfindung als Strafienunter-y 1164, with high sulphate resistance, is preferable, fabric atro
% if the materials of the invention are used as criminal offenses
ί| Letztlich können den mechanisch verdichtbaren Ma- erdartig. Im erhärteten Zustand sind die Materialien festί | Ultimately, the mechanically compactable corn-like. When hardened, the materials are solid
fyj terialieu der Erfindung zur Verbesserung der für eine bis stein- bzw. betonartig.fyj terialieu of the invention to improve the for one to stone or concrete-like.
|| mechanische Verdichtung günstigen Kornabstufung Entsprechend der Erfindung kann Ffltrat aus Rauch-H
noch andere VerfüUmaterialien zugemischt sein, wie gasentschwefelungsanlagen zur Verdichtung bzw. che-
|*1 beispielsweise gebrochenes Schmelzkammergranulat, to mischen Stabilisierung verwendet werden. Der Chloridt|
Nebenprodukte bzw. Abfallstoffe aus dem Bergbau gehalt sollte erfindungsgemäß 30 000 ppm (30 000 mg
m bzw. der Natursteingewinnung, aus Eisen- und anderen α pro kg Fütrat) nicht überschreiten. Das Chlorid kann
rl Hüttenbetrieben, aus Müllverbrennungsanlagen und/ als CaQz oder MgCb oder CaCU und MgCh vorliegen.
ff oder Bauschutt. Zur Herstellung hohlraumarmer VerfüUungen, Strahl
Die mechanische verdichtbaren Materialien werden 15 Ben- oder Deponieunterbaue wird dem erfindungsge-Ii
aus ihren Komponenten, die in den bekannten Korngrö- mäßen Material noch Wasser, das vorteilhaft Chloridio-H
ßen und bezogen auf diese Korngrößen in entsprechen- nen enthält, zugesetzt, wobei sich der Wassergehalt
ffiä den Mengen einzusetzen sind, durch intensives Vermi- nach der Proctordichte bestimmt Es hat sich bewährt,
fÜ sehen in gebräuchlichen Mischgeräten erhalten. Diese hierfür chloridhaltige Filtrate nach chemischem Verfah-
'0 Mengen- und Korngrößenverhältnisse richten sich im 20 ren einzusetzen, wie beispielsweise die chloridhaltigen
fl wesentlichen nach dem Anwendungszweck der mecha- Filtrate aus einer Rauchgas-Entschwefelungsanlage.
ψ- nisch Vcfdiehibaren Materialien der firRüdung. So hat Das am Ort seiner Verwendung ausgebreitete mecha-JS
es sich beispielsweise bewährt, für einen Strc ^enunter- nisch verdichtbare Material wird entsprechend der aus
% bau ein mechanisch verdichtbares Material einzusetzen, der Gesteinsschotter bekannten Arbeitsweise mit den
; das folgende Komponenten in den angegebenen Men- 25 gebräuchlichen Geräten, wie Rüttler, Walzen vad dgL
i>1 gen und Korngrößen enthält: mechanisch möglichst weitgehend verdichtet Mit dieser
;U Verdichtung setzt, insbesondere in Gegenwart von
hi 55Gew.-% Steinkohlenflugasche
< 1,25 mm Wasser bzw. wäßrigen, chloridhaltigen Lösungen, auch
H 10 Gew.-% Rostasche o. Schmelzkammergranulat eine chemische Stabilisierung des Materials ein, und
i ■' <8 mm 30 zwar durch die Hydratation des Zements urid/oder die
■■■■": 29 Gew.-% stückiges Calciumsulfat (Splitt aus Puzzolanreaktion der Flugasche, die dem Material eine
Gips-, Rohstein o. Naturanhydrit von über die durch die mechanische Verdichtung erreichte
': 4—32 mm) Festigkeit hinausgehende Festigkeit und Tragfähigkeit
6Gew.-% Zement mit hohen Sulfatwiderstand, verleiht|| mechanical compaction with favorable grain gradation According to the invention, fltrate from Rauch-H can also be mixed with other filler materials, such as gas desulphurisation systems for compaction or chemical stabilization, for example broken melting chamber granulate. The chloride | By-products or waste materials from mining should, according to the invention, not exceed 30,000 ppm (30,000 mg m or from natural stone extraction, from iron and other α per kg of feed). The chloride can be present in smelters, from waste incineration plants and / as CaQz or MgCb or CaCU and MgCh.
ff or rubble. For the production of void-free fillings, jet The mechanically compressible materials are used in the invention from their components, which in the known grain size material are still water, which is advantageously chlorinated and, based on these grain sizes, in corresponding contains, added, the water content and the quantities are to be used, determined by intensive dilution according to the Proctor density. These filtrates containing chloride for this purpose according to chemical process- '0 quantitative and grain size ratios are to be used, such as, for example, the chloride-containing filtrates essentially according to the intended use of the mechanical filtrates from a flue gas desulphurisation system. ψ- nisch Vcfdiehibaren materials of the firRüdung. Thus, the spread at the place of its use mecha-JS, it has proved, for example, for a STRC ^ enunter- nisch compactible material of a mechanically compressible material construction of% is according to employ, the crushed rock of known procedure with the; the following components in the specified quantitative 25 commonly used devices such as vibrators, rollers vad like i> 1 gene and contains particle sizes: mechanically as much as possible condensed therewith; sets U compression, especially in the presence of hi 55Gew .-% coal fly ash <1, 25 mm of water or aqueous, chloride-containing solutions, also H 10% by weight of bottom ash or melting chamber granulate, a chemical stabilization of the material, and i ■ ' <8 mm 30 by the hydration of the cement uride / or the ■■■■ ": 29% by weight calcium sulphate in lumps (chippings from the pozzolan reaction of the fly ash, which give the material a gypsum, raw stone or natural anhydrite of over the strength achieved by mechanical compression : 4-32 mm) strength and load-bearing capacity 6 wt. % Cement with high sulphate resistance
z. B. HoZ 35—HS 35 Die Ettringitbildung beschränkt sich in den mecha-z. B. HoZ 35 — HS 35 The ettringite formation is limited in the mechanical
' ca. 15 Gew.-% Wasser — bezogen auf Gesamtfest- nisch verdichtbaren Materialien der Erfindung nur aufApprox. 15% by weight of water, based on the total solid compressible materials of the invention only
stoff atro — (Wassergehalt nach die Oberfläche der eingesetzten Calciumsuifat-Körnerstoff atro - (water content according to the surface of the calcium sulfate grains used
Proctordichte) und auf die geringen Anteile des feinteiligen Calciumsulfate, die während der mechanischen Verdichtung desProctor density) and the small proportions of finely divided calcium sulfate, during the mechanical compaction of the
Einbau des feuchten Gemisches mit Verdichtungsgrad 40 Materials der Erfindung durch Abrieb entstanden sind >98% von i'roctordichte. Die Körnungslinie des Stra- Durch die chemische Bindung, die durch die Hydrataßenunterbaumaterials verläuft ähnlich dem Sieblinien- tioi des Zements bzw. die Puzzolanreaktion bewirkt bereich für hydraulisch gebundene Kiestragschichten wird, sind die Zuschlagstoffe in so festem Verbund zu-0/32 mm nach TVT 72 (Techn. Vorschriften und Richtli- sammengeschlossen, daß Einbrüche oder Setzungen nien für die Ausführung von Tragschichten im Straßen- 45 nicht eintreten. Im übrigen kann dieser feste Verbund bau). nicht durch Auslaugen ge- oder zerstört werden. Die Für einen Deponieunterbau hat das mechanisch ver- geringen Mengen des vorhandenen Ettringits beeinflusdichtbare Material vorteilhaft folgende Zusammenset- sen die Festigkeit der Materialverbindung nicht Das zung: mechanisch verdichtete und chemisch verfestigte Mateso rial der Erfindung ist ein raumstabilier Belag oder Füll-Installation of the moist mixture with degree of compaction 40 material of the invention were created by abrasion > 98% of i'roctor density. The grading curve of the road through the chemical bond created by the hydrated sub-structure runs similar to the sieblinien- tioi of cement or causes the pozzolan reaction area for hydraulically bound gravel base layers, the aggregates are so firmly bonded to-0/32 mm in accordance with TVT 72 (technical regulations and guidelines that collapse or subsidence Never advocate the execution of base courses in the road 45. In addition, this fixed connection can building). cannot be leached or destroyed. the For a landfill substructure, the mechanically reduced quantities of the existing ettringite can be influenced Material advantageous the following compositions do not have the strength of the material connection tion: mechanically compacted and chemically solidified material of the invention is a space-stable covering or filling
50 Gew.-% SteinkoiJenflugasche < 1,25 mm körper. Bei Verwendung zur Landverfüllung können die50% by weight rocky fly ash <1.25 mm body. When used for land backfilling, the
10 Gew.-% Rostasche o. Schmelzkammergranulat mechanisch verdichteten und chemisch verfestigten10 wt .-% bottom ash or melting chamber granulate mechanically compacted and chemically solidified
<8mm Materialien der Erfindung nach Auftrag von Mutterbc-<8mm materials of the invention after application by mother
35Gew.-% stückiges Calciumsulfat (Pellets, Gra- den in bekannter Weise begrünt werden,
nalien, Split aus Gips-, Rohstein oder 55
Naturanhydrit von 4—16 mm).35% by weight calcium sulphate in lumps (pellets, grades are greened in a known manner,
nalien, split from gypsum, rough stone or 55
Natural anhydrite from 4-16 mm).
Als Verfüllmaterial wird vorteilhaft ein mechanisch
verdichtbares Material eingesetzt, das aus folgenden
Komponenten besteht: 60A mechanical filler material is advantageous
compressible material used, which consists of the following
Components consists of: 60
40 Gew.-% Steinkohlenflugasche < 1,25 mm
7,5Gew.-% Rostasche oder Schmelzkammergranulat
< 8 mm40% by weight hard coal fly ash <1.25 mm
7.5% by weight grate ash or melting chamber granulate <8 mm
50Gew.-% stückiges Calciumsulfat (Schülpen, 65
Briketts Pellets, Granalien, Spütt
aus Rohstein oder Naturanhydrit
vor··'-—32 mm)50% by weight calcium sulphate in lumps (Schülpen, 65
Briquettes Pellets, Granules, Spütt
made of raw stone or natural anhydrite
before ·· '-— 32 mm)
Claims (5)
und/oder Anhydrit in Korngrößen von 4 bis 32 mm to Außer den genannten Verbindungen können die Susenthält Pensionen auch noch Erdalkalisulfate, vorzugsweise1. Mechanically compressible material for the suspension with 30 to 90 wt .-% solids content best-SiraSen-, landscaping and landfill construction or for s hen, which consists of 0.25 to 70 wt .-% alkaline earth metal hydroxide purposes of backfilling from artificial Pozzolans, composed of 10 to 99.5% by weight of fly ash and 0.25 to 70% calcium sulfate and alkaline calcium% by weight of alkaline earth sulfites Calcium sulfate dihydrate contains calcium compounds in the suspension,
and / or anhydrite in grain sizes from 4 to 32 mm to. In addition to the compounds mentioned, the Susenthalt pensions can also contain alkaline earth sulfates, preferably
basische Schlacke enthält wobei diesem Bindemittel In der DE-OS 24 00 350 wird empfohlen. Flugasche noch Flugasche, Zement gelöschter Kalk oder Kydroxi- mit getrockneten und gegebenenfalls gebrannten Rückdt anderer Erdalkalien zugemischt sein kann. Dieses 35 ständen aus der Rauchgasentschwefelung vermischt Bindemittel enthält den Anhydrit als bindewirksamen und offenbar unter Zusatz von Flüssigkeit zu granulie-Bestandteil und bindet zu harten und wasserbeständi- ren. Hierbei sollen steinartige Granalien entstehea
gen Festkörpern ab. Nach der DE-OS 24 08 827 sollen von Flugasche freieThere are known binders which are best made from anhydrite, including pels, which after prolonged storage or which contain this from the main component. Such a card was so popular that it was written in DE-AS10 18 775 as a binding agent that used little aggregate in stabilized subsoil, asphaltic at least 65% by weight anhydrite and at most 35% by weight concrete and the like can be
contains basic slag, this binder in DE-OS 24 00 350 is recommended. Fly ash or fly ash, cement, slaked lime or kydroxy can be mixed with dried and possibly burnt residue of other alkaline earths. This binder, mixed with the flue gas desulphurisation, contains the anhydrite as a binding agent and evidently with the addition of liquid to form granules and binds to hard and water-resistant ones. Stone-like granules are supposed to arise here
gen solids. According to DE-OS 24 08 827, fly ash is said to be free