NL8200991A

NL8200991A - MECHANICALLY COMPACTABLE MATERIAL.

Info

Publication number: NL8200991A
Application number: NL8200991A
Authority: NL
Original assignee: Knauf Westdeutsche Gips
Priority date: 1981-03-13
Filing date: 1982-03-10
Publication date: 1982-10-01
Also published as: DE3109632C2; DE3109632A1

Description

' *' · % ΗΤ.Ο. 30837 ' Mechanisch verdichtbaar materiaal.'*' ·% ΗΤ.Ο. 30837 'Mechanically compactable material.

Uit het Amerikaanse octrooischrift 3-855»391 is bekend, uit de suspensie, die big de ontzwaveling van rookgas langs de natte weg verkregen wordt, een gedeelte af te takken, te drogen en het daarin verkregen calciumsulfaat-dihydraat door 5 thermische behandeling tot calciumsulfaat-halfhydraat te di-hydrateren. Het hierbij verkregen product wordt vervolgens onder mengen weer aan de resthoeveelheid van de suspensie toegevoegd en wel in hoeveelheden van 1 tot 20% betrokken op het gehalte vaste stof van de suspensie. Het verkregen 10 mengsel wordt dan verder tot een materiaal ontwaterd, dat als landaanvulling geschikt is. Een wezenlijke voorwaahde voor de succesvolle.uitvoering van deze werkwijze is de volledige oxidatie van het bij de rookgasontzwaveling eerst gevormde calciumsulfiet tot calciumsulfaat-dihydraat. Om deze 15 oxidatie met zekerheid te waarborgen is het noodzakelijk aan de voor de rookgasontzwaveling gebruikte calciumcarbo-naat of calciumhydroxide bevattende wasvloeistof 0,1 tot 1000 dpm fijn verdeelde oxidatiekatalysatoren, zoals b.v. oxiden, sulfaten of nitraten van ijzer, nikkel, koper of ko-20 balt, toe te voegen.From U.S. Pat. No. 3-855,391, it is known to branch off from the suspension obtained from the desulphurisation of flue gas by the wet route, to dry and the calcium sulfate dihydrate obtained therein by heat treatment to calcium sulfate dihydrate. The product obtained in this way is then added to the residual amount of the suspension with mixing, in amounts of 1 to 20%, based on the solid content of the suspension. The resulting mixture is then further dewatered to a material suitable as land supplement. An essential condition for the successful implementation of this process is the complete oxidation of the calcium sulfite first formed in the flue gas desulfurization to calcium sulfate dihydrate. In order to ensure this oxidation with certainty, it is necessary for the calcium carbonate used for the flue gas desulfurization or washing liquid containing calcium hydroxide containing 0.1 to 1000 ppm of finely divided oxidation catalysts, such as e.g. oxides, sulfates or nitrates of iron, nickel, copper or cobalt.

Onderwerp van het Duitse Offenlegungsschrift 2.357-4-07 zijn cementachtige, hardbare massa's voor bouwdoeleinden, uit een waterige suspensie met een vaste stoffen gehalte van 30 tot 90 gew.% bestaan, die uit 0,25 tot 70 gew.% aard-25 alkalimetaalhydroxiden, 10 tot 99»5 gew.% vliegas en 0,25 tot 70 gew.% aardalkalimetaalsulfieten zijn samengesteld.The subject of German Offenlegungsschrift 2.357-4-07 are cementitious, curable building materials, consisting of an aqueous suspension with a solids content of 30 to 90% by weight, consisting of 0.25 to 70% by weight of alkaline earth metal hydroxides. 10 to 99% by weight of fly ash and 0.25 to 70% by weight of alkaline earth metal sulfites are composed.

Bij voorkeur zijn als aardalkalimetaalverbindingen de overeenkomstige calciumverbindingen in de suspensie aanwezig.Preferably, as alkaline earth metal compounds, the corresponding calcium compounds are present in the suspension.

3ehalve de genoemde verbindingen kunnen de suspensies 30 ook nog aardalkalimetaalsulfaten, bijvoorkeur calciumsulfaat, bevatten, waarbij echter in de suspensie aanwezige hoeveelheid aardalkalimetaalsulfiet tenminste 10% van de totale hoeveelheid aardalkalimetaalsulfaat en aardalkalimetaalsulfiet dient te bedragen. In het bijzonder wordt voor het ver-35 krijgen van de suspensie aanbevolen, de afvalgassen van een kolenstookinrichting in een waterige suspensie van verpoe-derde kalksteen of kalk te leiden, de verkregen suspensie tot een gehalte vaste stoffen van 80 gew.% te ontwateren en 8200991 * 2 veelheden onder mengen toe te voegen, dat het verkregen mengsel 40 gew.% vliegas, 3 gew.% gebluste kalk en 25 gew.% gehydrateerd calciumsulfiet resp.- sulfaat bevat. Afhankelijk van de samenstelling van deze massa's kunnen deze zon-5 der in vaste toestand brengen ondoordringbaar en monolytisch worden of na langere veroudering vast worden en verdichten. Uit een massa van geschikte samenstelling kunnen ook korrels worden gevormd, die na langere opslag een zodanige hardheid hebben verkregen, dat zij als toeslag in gestabiliseerde on-dergrond, asfaltachtig beton en dergelijke gebruikt kunnen worden.In addition to the said compounds, the suspensions can also contain alkaline earth metal sulphates, preferably calcium sulphate, however, the amount of alkaline earth metal sulphite present in the suspension must be at least 10% of the total amount of alkaline earth metal sulphate and alkaline earth sulphite. In particular, in order to obtain the suspension, it is recommended to pass the waste gases from a coal firing device into an aqueous suspension of pulverized limestone or lime, to dehydrate the resulting suspension to a solids content of 80% by weight and 8200991 * 2 multiples with mixing, that the resulting mixture contains 40 wt% fly ash, 3 wt% slaked lime and 25 wt% hydrated calcium sulfite or sulfate. Depending on the composition of these masses, these solidification processes can become impermeable and monolytic or solidify and densify after prolonged aging. Granules can also be formed from a mass of suitable composition which, after longer storage, have obtained such hardness that they can be used as an additive in stabilized substrate, asphalt-like concrete and the like.

In het Duitse Offenlegungsschrift 2.400.350 wordt aanbevolen vliegas met gedroogde en eventueel gebrande residuen uit de rookgas ontzwaveling gemengd en blijkbaar onder toe--*-5 voeging van vloeistof te granuleren. Hierbij zouden steenachtige korrels ontstaan.German Offenlegungsschrift 2,400,350 recommends that fly ash be mixed with dried and possibly burnt residues from the flue gas desulphurisation and apparently granulate with the addition of liquid. This would result in stony granules.

Volgens het Duitse Offenlegungsschrift 2.408.827 zouden van vliegasvrije suspensies afkomstig van de natte ontzwaveling van rookgassen of afvalwatersuspensies anorganische 20 calciumverbindingen bevatten, na ontwatering op een vaste stoffen gehalte van 25 tot 50 gew.% met 1 tot 20 gew.%, betrokken op dit gehalte vaste stoffen, basische, glasachtige hoogovenslakken in gegranuleerde vorm gemengd worden, om het gehalte vaste stoffen van deze suspensie zodanig te verste-25 vigen, dat dit een verhoogde schuifsterkte bezit. Het verkregen produkt kan dan goed opgeslagen worden.According to German Offenlegungsschrift 2,408,827, fly ash-free suspensions from the wet desulfurization of flue gases or waste water suspensions contain inorganic calcium compounds, after dewatering at a solids content of 25 to 50% by weight with 1 to 20% by weight, based on this solids, basic, glassy blast furnace slag in granulated form are mixed to enhance the solids content of this slurry to have increased shear strength. The product obtained can then be stored well.

Uit het Duitse Auslegeschrift 2.432.572 is een werkwijze voor het nuttig gebruik van de bij de natte zuivering van rookgassen verkregen en in hun watergehalte verminderde 30 suspensies bekend, volgens welke werkwijze deze suspensie in het watergehalte op 15 tot 30 gew.% zijn verminderd, met een bindmiddel zoals b.v. cement of waterglas, gemengd en gekorreld worden, de korrels vervolgens gedroogd en eventueel zelfs gebrand worden. Aan het korrelvormingsmengsel kan ook 35 vliegas onder mengen worden toegevoegd. Er ontstaan op deze wijze harde korrels, waarvan de hardheid door het brandings-proces nog kan worden vergroot. Deze korrels zullen voor de opvulling van landverdiepingen, mijnbouwtunnels, moerassen, meren en dergelijke geschikt zijn, evenals als toeslagstof 40 voor de wegenbouw of aan beton, in het laatste geval alleen, 82 0 0 99 1 * Λ 3 wanneer voor tiet beton geen grote sterkte verlangd wordt. Daaruit valt af te leiden, dat de sterkte van de korrels voor bouwdoeleinden niet voldoende is.German Auslegeschrift No. 2,432,572 discloses a process for the useful use of the suspensions obtained in the wet purification of flue gases and reduced in their water content, according to which process this suspension in the water content is reduced to 15 to 30% by weight, with a binder such as e.g. cement or water glass, are mixed and granulated, the granules are then dried and possibly even roasted. Fly ash can also be added to the granulation mixture with mixing. In this way, hard granules are formed, the hardness of which can be further increased by the branding process. These granules will be suitable for the filling of land floors, mining tunnels, swamps, lakes and the like, as well as as additive 40 for road construction or on concrete, in the latter case only, 82 0 0 99 1 * Λ 3 if not large for tit concrete. strength is required. It can be deduced from this that the strength of the granules for building purposes is not sufficient.

In bet Duitse Offenlegiingsschrift 2.803*764 wordt een 5 werkwijze beschreven voor het nuttig gebruik van bij kolenstookinrichtingen verkregen vliegstof en van het uit rookgasinrichtingen, waarin kalk verwerkt wordt, te onttrekken calciumsulfaat, waarbij de vliegstof tesamen met het in de rookgassen aanwezige zwaveldioxide tot een waterbevattende 10 suspensie uitgewassen wordt. Deze suspensie wordt vervolgens thermisch zodanig behandeld, dat het daarin aanwezige calrr.„. ciumsulfaat-dihydraat in de waterarmere vormen van het an-hydriet of halfhydraat overgaat. De op deze wijze verkregen suspensie hardt dan na vormgeving tot bouwmateriaal, zoals 13 b.v. platen of bouwstenen. Het aandeel van het vliegas betrokken op het gehalte vaste stoffen van de uitgangssuspen-sie dient daarbij tussen 10 en 70 gew.$, betrokken op het gehalte vaste stoffen, te liggen.In German Offenlegiingsschrift 2.803 * 764 a method is described for the useful use of fly-dust obtained from coal-fired plants and of the calcium sulfate to be extracted from flue-gas plants in which lime is processed, wherein the fly dust together with the sulfur dioxide present in the flue gases to form a water-containing 10 suspension is washed. This suspension is then thermally treated so that the calrr contained therein. cium sulfate dihydrate into the leaner forms of the anhydrite or semi-hydrate. The suspension obtained in this way then hardens after molding into building material, such as 13 e.g. plates or building blocks. The proportion of the fly ash based on the solids content of the starting suspension should be between 10 and 70% by weight, based on the solids content.

Tenslotte is uit het Duitse Offenlegungsschrift 20 2.810.173 een werkwijze voor de vervaardiging van verstevig-r de produkten uit water bevattende, suspensievormige of pas-ta-achtige stoffen en verstevigingsmiddelen voorgesteld, volgens welke aan de suspensievormige of pasta-achtige stoffen calciumsulfaat, bijvoorkeur in een vorm wordt toegevoegd, 25 die minder kristalwater bevat dan calciumdihydraat. Bovendien kunnen aan de mengsels uit deze componenten ook onder hydraatvorming reagerende aluminaat- silicaat bevattende stoffen, stoffen met een groter specifiek oppervlak onder mengen toegevoegd worden. Deze maatregelen hebben ten doel 30 het in de suspensie-achtige of pasta-achtige stoffen aanwezige water te binden en het vaste stoffen gehalte van deze suspensie-achtige of pasta-achtige stoffen zodanig te verstevigen, dat de ontstaande en eventueel gevormde producten gemakkelijk te hanteren, op te stapelen resp. te deponeren 35 zijn.Finally, German Offenlegungsschrift No. 20 2,810,173 has proposed a process for the production of stiffening products from water-containing, suspension-like or paste-like substances and reinforcing agents, according to which the suspension-like or paste-like substances contain calcium sulphate, preferably is added in a form containing less crystal water than calcium dihydrate. In addition, to the mixtures of these components, substances having a greater specific surface area which react under hydrate formation, substances having a larger surface area, can be added with mixing. The purpose of these measures is to bind the water present in the suspension-like or paste-like substances and to strengthen the solids content of these suspension-like or paste-like substances in such a way that the resulting and possibly formed products are easy to handle. , to be stacked resp. to be deposited 35.

Voorzover in deze bekende werkwijzen calciumsulfaten als bindmiddel voor de mengsels uit vaste stoffen water toepassing vinden, zijn zij in de te verstevigen uitgangsmen-sèls fijn verdeeld en met een in vergelijking tot het cal-40 cium-dihydraat geringer gehalte kristalwater aanwezig, zo- 8200991 4- dat zij in staat zijn door herhydratering tot het hydraat aan deze mengsels water te onttrekken en ze tegelijktijdig te verstevigen. Ook bij toepassing van de combinatie van vliegas en alkalisch reagerende calciumverbindingen, zoals 5 b.v. calciumoxide of calciumhydroxide, als verstevigend bindmiddel, zijn deze uitgangsmaterialen in de te verstevigen pasta-achtige suspensies in fijn verdeelde vorm aanwezig en reageren slechts dan tot het verstevigende Ettringit JCaÖ.A^O^.JCaSO^^lï^O, wanneer in de suspensie ook sulfaat-10 ionen in voldoende hoeveelheid aanwezig zijn. In de plastische materiaaltoestand leidt de Ettringit vorming tot geen uitzetting van het materiaal. Kristalliseert het Ettringit plaatselijk onder toename van het volume van de vaste stof, dan gaat dit proces met uitzetting gepaard, omdat 31 mole-15 culen water als kristalwater gebonden worden. Na opvulling van de ter beschikking staande holle ruimten wordt met toenemende kristallisatiedruk de treksterkte van het bouwmateriaal overschreden, wat tenslotte tot scheurvormingen en uit-zettingsverschijnselen leidt. Daarbij kan het kristalwater 20 van het Ettringit uit water voor de verdichting of voor het doordrenken met vocht van het bouwlichaam afkomstig zijn..Inasmuch as in these known processes calcium sulphates are used as a binder for the mixtures of solids water, they are finely divided in the starting materials to be reinforced and are present with a smaller amount of crystal water in comparison with the calcium dihydrate, such as 8200991. 4- that they are able to extract water from these mixtures by rehydration to the hydrate and at the same time strengthen them. Also when using the combination of fly ash and alkaline reacting calcium compounds, such as e.g. calcium oxide or calcium hydroxide, as a strengthening binder, these starting materials are present in the paste-like suspensions in finely divided form to be strengthened and only react until the strengthening Ettringit JCa0.A ^ O ^ .JCaSO ^ ^ l ^ ^ when in the suspension sulfate-10 ions are also present in sufficient quantity. In the plastic material state, the Ettringit formation results in no expansion of the material. If the Ettringit crystallizes locally with an increase in the volume of the solid, this process is accompanied by expansion, because 31 molecules of water are bound as water of crystallization. After filling in the cavities available, the tensile strength of the building material is exceeded with increasing crystallization pressure, which finally leads to cracks and expansion phenomena. In addition, the crystal water 20 of the Ettringit can come from water for compaction or impregnation with moisture of the building body.

De volgens deze bekende werkwijze verkregen en verstevigde produkten kunnen slechts in beperkte omvang voor landaan-vulling en de wegenbouw worden gebruikt, omdat zij slechts 25 slecht en onvoldoende verdicht kunnen worden en als gevolg daarvan treden inzakkingen en zettingen op, die niet gewenst zijn. Een vergaande consolidatie van lagen uit deze materialen treedt meestal na een bewaartijd van jaren op. Bovendien zijn de volgens de bekende werkwijzen verkregen produkten 30 tegen water niet bestand en worden dientengevolge door regen en in contact met grondwater uitgeloogd. Hierdoor wordt de sterkte van de lagen uit dergelijke produkten eveneens op ' ongewenste wijze verminderd en wordt het zoutgehalte van het grondwater verhoogd. Ettringit zelf maakt het materiaal niet 35 vorstgevoelig. Het watergehalte is chemisch gebonden aanwezig. De vatbaarheid voor vorst is op de poreusheid resp. instabiliteit (scheuren) van de materialen terug te voeren. Wanneer in de volgens de bekende werkwijzen verkregen produkten Ettringit aanwezig is, dan zijn deze ten opzichte van 4-0 koolstofdioxide bevattend water, zoals b.v. regenwater, niet 82 0 0 9 9 1 5 stabiel, omdat Ettringit met koolstofdioxide onder aanzienlijke vergroting van het volume ervan ontleedt.The products obtained and reinforced according to this known method can only be used to a limited extent for land replenishment and road construction, because they can only be poorly and insufficiently compacted, and consequently collapses and settlements occur which are not desirable. A far-reaching consolidation of layers from these materials usually occurs after a storage period of years. In addition, the products obtained according to the known methods are not resistant to water and are consequently leached out by rain and in contact with groundwater. This also undesirably reduces the strength of the layers from such products and increases the salt content of the groundwater. Ettringit itself does not make the material sensitive to frost. The water content is chemically bound. The susceptibility to frost is on the porosity resp. return instability (cracks) of the materials. When Ettringit is present in the products obtained by the known methods, these are water relative to 4-0 carbon dioxide, such as e.g. rainwater, not 82 0 0 9 9 1 5 stable, because Ettringit decomposes with carbon dioxide with considerable increase in its volume.

Hieruit volgt>het probleem, om onder toepassing van chemisch vergelijkbare uitgangsmaterialen een mechanisch met 5 gebruikelijke bouwapparatuur verdichtbaar materiaal mengsel te vinden, dat vormvast is, waarbij het gevaar van penetraties of verzakkingen even weinig bestaat als het gevaar van uitloging.It follows from this that the problem is found, using chemically comparable starting materials, to find a mixture of materials which can be mechanically compacted with conventional construction equipment and which retains its shape, the danger of penetrations or subsidence being as little as the risk of leaching.

Er werd een mechanisch dicht materiaal uit synthetische XO puzzolanen, calciumsulfaat en alkalisch reagerende calcium-verbindingen gevonden. Volgens de uitvinding dient dit materiaal het calciumsulfaat als calciumsulfaat-dihydraat en/of anhydriet in korrelgrootten van 4 tot 32 mm te bevatten.A mechanically dense material of synthetic XO pozzolanes, calcium sulfate and alkaline reacting calcium compounds was found. According to the invention, this material should contain the calcium sulfate as calcium sulfate dihydrate and / or anhydrite in grain sizes from 4 to 32 mm.

Bij voorkeur dient de korrelgrootte van de volgens de X5 uitvinding te gebruiken calciumsulfaten in het traject van 4 tot 16 mm te liggen.Preferably, the grain size of the calcium sulfates to be used according to the X5 invention should be in the range of 4 to 16 mm.

Voor het mechanisch verdichtbare materiaal van de uitvinding kan een gebroken ruwe gips of natuuranhydriet gebruikt worden, waarvan de verdeling van de korrelgrootte met 20 de aangegeven grenzen overeenkomt. Het is echter ook mogelijk dit ruwe gips resp. dit natuurlijke anhydriet geheel of tendele door synthetisch calciumsulfaat-dihydraat of synthetisch anhydriet te vervangen, dat bij talrijke chemische processen als bijprodukt verkregen wordt. Omdat deze synthetische cal-25 ciumsulfaten, die als bijprodukten, b.v. bij de bereiding van fosforzuur, uit onzuiver fosfaat en zwavelzuur, bij de ontzwaveling van rookgassen met calciumcarbonaat of calciumhydroxide, meestal als fijn verdeelde kristallijne produk-ten ontstaan, is het noodzakelijk, deze kristallijne:': pro-30 dukten na de afscheiding uit het reactiemengsel en het daarop volgend wassen op een op zichzelf bekende wijze te comprimeren, te briketteren, te granuleren of te korrelen, om op deze wijze uit deze kristallijne produkten een korrelachtig produkt te verkrijgen, waarvan de korrelgrootte in 33 het beoogde traject van 4 tot 32 mm, bijvoorkeur 4 tot 16 mm, ligt.For the mechanically compactable material of the invention, a broken raw gypsum or natural anhydrite can be used, the distribution of the grain size of which corresponds to the indicated limits. However, it is also possible to use this raw plaster resp. to replace all or part of this natural anhydrite with synthetic calcium sulfate dihydrate or synthetic anhydrite, which is obtained as a by-product in numerous chemical processes. Because these synthetic calcium sulfates, which are used as by-products, e.g. in the preparation of phosphoric acid, from impure phosphate and sulfuric acid, in the desulphurisation of flue gases with calcium carbonate or calcium hydroxide, usually as finely divided crystalline products, it is necessary, these crystalline products, after separation from the reaction mixture and subsequent washing in a manner known per se to compress, briquette, granulate or granulate, in order to obtain a granular product from these crystalline products, the grain size of which in the intended range from 33 to 32 mm, preferably 4 to 16 mm.

Als bindmiddel en als fijnkorrelig deel bevatten de mechanisch verdichtbare materialen van de uitvinding bovendien puzzolanen, zoals bijvoorbeeld door malen van het granulaat 40 van een basische hoogovenslak bevattend slakkenmeel. In 8200991 ν' 6 plaats van dit slakkenmeel kunnen de materialen volgens de uitvinding ook glasachtige, bijvoorkeur calciumoxide bevattend vliegas bevatten, waaraan nog alkalische stoffen als initiator kunnen zijn bijgemengd, die vrije kalk bevatten of 5 als deze werken. Als bindmiddel en fijn korrelig deel kunnen de materialen van de uitvinding ook cement bevatten, waarbij een tricalciumaluminaat-arm cenent, zoals bijvoorbeeld cement HS, volgens DIN 1164, met een hoge sulfaat weerstand de voorkeur verdient, wanneer de materialen van de uitvinding als 10 onderbouw van wegen of voor soortgelijke doeleinden dienen te worden gebruikt.As a binder and as a fine-grained part, the mechanically compactable materials of the invention also contain pozzolans, such as, for example, by grinding the granulate 40 of a basic blast furnace slag containing slag flour. Instead of this slag meal, the materials according to the invention may also contain glassy fly ash, preferably containing calcium oxide, to which alkaline substances may also be added as an initiator, which contain or act as free lime. As binder and fine granular part, the materials of the invention may also contain cement, with a low tricalcium aluminate cenent, such as cement HS, according to DIN 1164, having a high sulphate resistance, when the materials of the invention are used as a substructure. of roads or for similar purposes.

Tenslotte kunnen aan de mechanische verdichtbare materialen van de uitvinding ter verbetering van de voor de mechanische verdichting gunstige korrelrangschikking nog ande-15 re vulmaterialen zijn bijgemengd, zoals bijvoorbeeld gebroken smeltkamergranulaat, bijprodukten resp. afvalstoffen van de mijnbouw resp. winning van natuurlijke gesteenten, uit staalfabrieken en andere metallurgische bedrijven, uit vuilverbrandings inrichtingen en/of puin.Finally, in order to improve the grain arrangement favorable for the mechanical compaction, further filling materials may be mixed in with the mechanically compactable materials of the invention, such as, for example, crushed melting chamber granulate, by-products or by-products. waste from mining or. extraction of natural rocks, from steel mills and other metallurgical companies, from incinerators and / or rubble.

20 De mechanisch verdichtbare materialen worden uit hun componenten, die in de bekende korrelgrootte en betrokken op deze korrelgrootte in overeenkomende hoeveelheden te gebruiken zijn, door intensief mengen in gebruikelijke menginrich-tingen verkregen. Deze verhoudingen van hoeveelheden en kor-25 relgrootten zijn in hoofdzaak gericht op het toepassingsdoel van de mechanisch verdichtbare materialen van de uitvinding. Zo is het bijvoorbeeld voor een onderbouw van wegen goed gebleken een mechanisch verdichtbaar materiaal te gebruiken, dat de volgende componenten in de aangegeven hoeveelheden en 50 korrelgrootten bevat: 55 gew.% vliegas van steenkolen 1,25 mm 10 gew.% roostsintels of smeltkamer granulaat8 mm 29 gew.% calciumsulfaat stukken (split uit gips, ruwe steen of natuurlijk anhydriet van 4-32 mm) 35 6 gew.% cement met grote sulfaatweerstand, b.v.The mechanically compactable materials are obtained from their components, which can be used in corresponding amounts in the known grain size and based on this grain size, by intensive mixing in conventional mixing devices. These ratios of amounts and grain sizes are directed primarily to the application of the mechanically compactable materials of the invention. For example, for a road substructure, it has been found to be advantageous to use a mechanically compactable material containing the following components in the indicated amounts and 50 grain sizes: 55% by weight of coal fly ash 1.25mm 10% by weight roasting embers or melting chamber granulate8 mm 29 wt% calcium sulphate pieces (split from plaster, rough stone or natural anhydrite of 4-32 mm) 35 6 wt% cement with high sulphate resistance, eg

HoZ 35 - HSHoZ 35 - HS

+ 15 gew.% water, betrokken op het totale vaste stof atro, (watergehalte volgens Proctordichtheid).+ 15 wt.% Water, based on the total solid atro, (water content according to Proctor density).

Inbouw van het vochtige mengsel met een verdichtingsgraad 40 groter 98% Protordichtheid. De korrelingslijn van het mate- 82 0 0 99 1Installation of the moist mixture with a degree of compaction 40 greater than 98%. The grain line of the material 82 0 0 99 1

VV

7 riaal voor de onderbouw van wegen verloopt soortgelijk aan het zeeflijn traject voor hydraulisch gebonden draaglagen van grint 0/32 mm volgens TVT 72 (Techn. Vorschriften und Richtlinien für die Ausführung von Tragschichten im Stras-5 senbau).7 road substructure is similar to the sieve line path for hydraulically bonded gravel layers 0/32 mm according to TVT 72 (Techn. Vorschrift und Richtlinien für die Ausführung von Tragschichten im Stras-5 senbau).

Yoor een onderbouw van een afzetting heeft het mechanisch verdichtbare materiaal met voordeel de volgende samenstelling: 50 gew.% vliegas van steenkolen/ 1,25 mm 10 10 gew.% roostsintels of smeltkamergranulaat/ 8 mm 35 gew.% calciumsulfaat stukken (korrels, granulaten, split uit gips, ruwe steen of natuurlijk anhy-driet van 4-16 mm).For a deposit substructure, the mechanically compactable material advantageously has the following composition: 50 wt.% Coal fly ash / 1.25 mm 10 10 wt.% Roast embers or melting chamber granulate / 8 mm 35 wt.% Calcium sulfate pieces (granules, granulates , split from plaster, rough stone or natural anhydrite of 4-16 mm).

Als vulmateriaal wordt met voordeel een mechanisch ver-15 dichtbaar materiaal gebruikt, dat uit de volgende componenten bestaat: 40 gew.% vliegas van steenkolen / 1,25 nun 7,5gew.% roostsintels of smeltkamergranulaat (. 8 mm 50 gew.% calciumsulfaat stukken (schubben, briketten, 20 korrels, granulaten, split uit ruwe steen of natuurlijk anhydriet van 4-32 mm)As a filling material, a mechanically sealable material is advantageously used, which consists of the following components: 40 wt.% Coal fly ash / 1.25 nun 7.5 wt.% Roast embers or melting chamber granulate (8 mm 50 wt.% Calcium sulphate pieces (scales, briquettes, 20 grains, granulates, split from rough stone or natural anhydrite of 4-32 mm)

2,5gew.% PZ 35 F2.5 wt% PZ 35 F

+15- 20 gew.% betrokken op totale vaste stof atro.+ 15-20 wt% based on total solid atro.

Alle materialen zijn in verse toestand kruimelachtig.All materials are crumbly when fresh.

25 In verharde toestand zijn de materialen vast tot steenachtig resp. betonachtig.In the hardened state, the materials are solid to stony or. concrete-like.

Overeenkomstig de uitvinding kan filtraat uit rookgas ontzwavelingsinrichtingen voor verdichting resp. chemische stabilisatie toegepast worden. Het chloridegehalte dient 30 volgens de uitvinding niet 30-000 dpm (30.000 mg Cl per kg filtraat) te overschrijden. Het chloride kan als CaCl2 of MgCl2 of CaCl2 en MgCl2 aanwezig zijn.In accordance with the invention, filtrate from flue gas desulfurization devices for densification or. chemical stabilization. According to the invention, the chloride content should not exceed 30-000 ppm (30,000 mg Cl per kg filtrate). The chloride can be present as CaCl2 or MgCl2 or CaCl2 and MgCl2.

Ter vervaardiging van vullingen, onderbouw voor wegen en afzettingen met weinig holle ruimte wordt aan het materi-35 aal volgens de uitvinding nog water, dat met voordeel chlo-ride-ionen bevat, toegevoegd, waarbij het watergehalte volgens de Proctordichtheid bepaald wordt. Het is goed gebleken hiervoor chloride bevattende filtraten volgens chemische werkwijzen te gebruiken, zoals bijvoorbeeld de chloride be-40 vattende filtraten uit een rookgas-ontzwavelingsinrichting.For the manufacture of fillings, substructure for roads and deposits with little void space, water, which advantageously contains chloride ions, is added to the material according to the invention, the water content being determined according to the Proctor density. It has been found to be advantageous to use chloride-containing filtrates for this purpose by chemical methods, such as, for example, the chloride-containing filtrates from a flue gas desulfurization device.

8200991 v y 88200991 v y 8

Het op de plaats van zijn toepassing uitgespreide, mechanisch. verdichtbare materiaal wordt in overeenstemming met de uit de steenslag bekende werkwijze met gebruikelijke apparatuur, zoals trilinrichtingen, walsinrichtingen en derge-5 lijke mechanisch zoveel mogelijk verdicht. Met deze verdichting begint, in het bijzonder bij aanwezigheid van water resp. waterbevattende, chloride-bevattende oplossingen, ook een chemische stabilisatie van het materiaal en wel door de 10 hydratering van het cement en/of de puzzolaanreaktie van het vliegas, die het materiaal een boven de door de mechanische verdichting bereikte sterkte uitgaande sterkte en draagvermogen verleent. De Ettringitvorming beperkt zich in de mechanisch verdichtbare materialen van de uitvinding slechts 15 tot het oppervlak van de gebruikte calciumsulfaatkorrels en op de geringe hoeveelheden van het fijn verdeelde calciumsulfaat, die tijdens ..de mechanische verdichting van het materiaal van de uitvinding door afwrijven zijn ontstaan. Door de chemische binding, die door de hydratering van het cement 20 resp. de puzzolaanreactie bewerkstelligd wordt, worden de toeslagen in een zodanig vast verband aaneengesloten, dat penetraties of verzakkingen niet optreden. Voor het overige kan dit vaste verband niet door uitlogen verstoord of vernietigd worden. De geringe hoeveelheden van het aanwezige 25 Ettringit beïnvloeden de sterkte van de materiaalverbinding niet. Het mechanisch verdichte en chemisch versterkte materiaal van de uitvinding is een ruimtelijk stabiel dek of vullichaam. Bij toepassing voor landaanvulling kunnen de mechanisch verdichte en chemisch versterkte materialen van de 50 uitvinding na het opbrengen van bodem op bekende wijze met groen bedekt worden.It spread mechanically at the site of its application. Compressible material is compacted as much as possible in accordance with the method known from the crushed stone with conventional equipment, such as vibrators, rollers and the like. This compaction begins, particularly in the presence of water or water. water-containing, chloride-containing solutions, also a chemical stabilization of the material, namely by the hydration of the cement and / or the pozzolane reaction of the fly ash, which gives the material a strength and load-bearing capacity exceeding the strength achieved by the mechanical compaction. Ettritit formation is limited in the mechanically compactable materials of the invention to the surface of the calcium sulfate granules used and to the small amounts of the finely divided calcium sulfate which have been produced by rubbing during the mechanical compaction of the material of the invention. Due to the chemical bond produced by the hydration of the cement 20 resp. When the pozzolan reaction is effected, the supplements are connected in such a tight connection that penetrations or subsidence do not occur. Otherwise, this fixed relationship cannot be disturbed or destroyed by leaching. The small amounts of the Ettringit present do not affect the strength of the material compound. The mechanically compacted and chemically reinforced material of the invention is a spatially stable deck or filler body. When used for land replenishment, the mechanically compacted and chemically reinforced materials of the invention can be coated in green in a known manner after soil application.

82009918200991

Claims

1. Mechanically compactable material from synthetic pozzolanes, calcium sulfate and alkaline reacting calcium compounds, characterized in that the material contains the calcium sulfate as calcium sulfate dihydrate and / or anhydrite in granules of 4 to 32 mm.

2. Material according to claim 1, characterized in that it contains the synthetic pozzolanes in finely divided form.

3. Material according to claim 1 or 2, characterized in that it contains finely divided calcium oxide and / or calcium hydroxide as alkaline-reacting calcium compounds.

4. Material according to claims 1 to 3, characterized in that the material contains inert additives. 8200991