DE3048506C2 - Dry powder plaster mixture and process for its preparation - Google Patents

Dry powder plaster mixture and process for its preparation

Info

Publication number
DE3048506C2
DE3048506C2 DE19803048506 DE3048506A DE3048506C2 DE 3048506 C2 DE3048506 C2 DE 3048506C2 DE 19803048506 DE19803048506 DE 19803048506 DE 3048506 A DE3048506 A DE 3048506A DE 3048506 C2 DE3048506 C2 DE 3048506C2
Authority
DE
Germany
Prior art keywords
weight
plaster
hemihydrate
flue gas
mixture
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DE19803048506
Other languages
German (de)
Other versions
DE3048506A1 (en
Inventor
Des Erfinders Auf Nennung Verzicht
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Saint Gobain Rigips GmbH
Original Assignee
Rigips GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Rigips GmbH filed Critical Rigips GmbH
Priority to DE19803048506 priority Critical patent/DE3048506C2/en
Priority to DK532581A priority patent/DK157446C/en
Priority to NL8105454A priority patent/NL191628C/en
Priority to BE0/206889A priority patent/BE891555A/en
Publication of DE3048506A1 publication Critical patent/DE3048506A1/en
Application granted granted Critical
Publication of DE3048506C2 publication Critical patent/DE3048506C2/en
Expired legal-status Critical Current

Description

rial aus einer Verfahrensstufe entnommen und einer anderen wieder zugeführt wird. Hier handelt es sich im wesentlichen um ein Brennverfahren, über die Herstellung einer halbhydrathaltigen Putzmischung ist hier nichts zu finden. Die Gipskomponente allein bestimmt s nicht die Eigenschaften eines Putzgipses.rial taken from one process stage and another is fed back. This is essentially a combustion process through production There is nothing to be found here with a plaster mixture containing semi-hydrates. The plaster component alone determines p not the properties of plaster of paris.

Auch aus der Literatlirstelle »Silikattechnik 22 (1971). Heft 7» S. 225 ff.« sind lediglich Brennverfahren oder Dehydrationen von Gips beschrieben und zwar insbesondere im sogenannten Schwebeverfahren und es sind Körnungen genannt, wie man sie in Putzgipsen verwenden kann.Also from the literature section »Silikattechnik 22 (1971). Issue 7 »p. 225 ff.« Are only combustion processes or Described dehydration of plaster of paris, in particular in the so-called suspension process and there are Called grains, as they are used in plaster of paris can.

Ein Putzgemisch ist jedoch ein Mehrkomponentengemisch, in dem sich alle Komponenten mehr oder weniger stark beeinflussen und aufeinander abgestimmt sein müssen, damit optimale Ergebnisse erzielt werden.However, a plaster mixture is a multi-component mixture, in which all components influence each other to a greater or lesser extent and are coordinated with one another must be used in order to achieve optimal results.

Es ist daher Aufgabe der vorliegenden Erfindung ein solches Putzgemisch vorzuschlagen, das aus speziell aufbereitetem Gips und weiteren Zusätzen besteht und sich durch eine besondere Standfestigkeit bzw. Zerfallsfestigkeit, ein gut« Auftragsvermögen auszeichnet und sich anschließend zu einer fehlerlosen, glätten, weißen Oberfläche abziehen, kartätschen und filzen läßt.It is therefore the object of the present invention to propose such a plaster mixture that consists of specifically prepared gypsum and other additives and is characterized by a special stability or decay resistance, a good “ability to contract and then turn into a flawless, smooth, white Peel off the surface, let it be patted and felted.

Gelöst wird diese Aufgabe durch die in den Ansprüchen gekennzeichneten Mischungen und Verfahrensmaßnahmen. This object is achieved by the mixtures and process measures characterized in the claims.

Das Kontaktieren des feinteiligen ,<?-Kalziumsulfat-Halbhydrats erfolgt trocken, jedoch wird zur besseren Trennung der Briketts von der Matrizenoberfläche diese angefeuchtet Die Briketts haben vorzugsweise eine Größe von 38 χ 32 χ 16 mm.Contacting the finely divided, <? - calcium sulfate hemihydrate takes place dry, but for a better separation of the briquettes from the die surface it is moistened The briquettes preferably have a size of 38 32 χ 16 mm.

Die Dichte liegt et*a bei 2,1 g/m3.The density is et * a at 2.1 g / m 3 .

Diese verfahrensmäßig gevsonnenr Körnung des ß-Halbhydrats kann nun mit anderen Bestandteilen der Putzmischung vermischt werdeir, be'-pielsweise mit Kalksteingries, Kalk, Andicker in Form von Stärkeäther mit einem Beschleuniger, einem wasserlöslichen Zeliuloscderivat, einem Netzmittel, einem Verzögerer, einem sonstigen Füllstoff, beispielsweise Perlit und dgL mehr. ' 'This process-wise grain of the ß- hemihydrate can now be mixed with other components of the plaster mixture, for example with limestone gauze, lime, thickener in the form of starch ether with an accelerator, a water-soluble cellulose derivative, a wetting agent, a retarder, another filler, for example perlite and dgL more. ''

In Verfolg des Erfindungsgedankens ist es aber auch möglich, daß man dem in der Ausgangsphase feinteilig anfallenden /?-Halbhydrat vor der Kontaktierung gewisse Bestandteile zumischt, beispielsweise die geringen Mengen von Netzmitteln. Beschleuniger und Verzöge-* rer oder andere für das Material zweckdienliche Stoffe.In pursuit of the inventive concept, however, it is also possible that the finely divided one in the initial phase accruing /? - hemihydrate before contacting certain Mixing ingredients, for example the small amounts of wetting agents. Accelerator and deceleration * rer or other substances useful for the material.

Bei dem Kalksteingries handelt es sich um feingemahlenes Kalziumkarbonat, das in seiner Korngrößenverteilung möglichst fein vorliegt, damit eine Beeinträchtigung der Putzoberfläche beim Glätten durch zu große Körner nicht stattfindet, d. h. die Körner sich nicht in der so geglätteten Oberfläche abzeichnen. Der Kalk kann Kalziumhydroxid oder Weiükalk sein.The limestone gravel is finely ground calcium carbonate, the grain size distribution of which is as fine as possible so that it is impaired the plaster surface does not take place when smoothing due to grains that are too large, d. H. the grains are not in that way Draw off the smoothed surface. The lime can be calcium hydroxide or white lime.

Bei dem wasserlöslichen Zellulosederivat handelt es sich vorzugsweise um eine Meihylzellulose. Wird als . ' Füllstoff Perlit verwendet, so handelt es sich in jedem Falle u«n vorgeblähten Perlit ebenfalls in feiner Korngröße entsprechend dem Kalksteingries. Statt des natürlichen Kalksteingrieses kann natürlich auch ein synthetisches Präparat verwandt werden oder auch Kreide oder Dolomit. Die Teilchengröße sollte keinesfalls 3?als 0,15 mm sein.The water-soluble cellulose derivative is preferably a methyl cellulose. Used as. ' If the filler perlite is used, it is in any case a pre-expanded perlite, likewise in a fine grain size corresponding to the limestone gravel. Instead of the natural limestone giant, a synthetic one can of course also be used Preparation can be used or also chalk or dolomite. The particle size should by no means be 3? Be 0.15 mm.

Der Zusatz des Zellulosederivats zur Mörtelmischung hat den Vorteil, daß Nachteile, die u. U. durch die Anwesenheit einer größeren Menge Kalziumhydroxid bestehen, beseitigt werden. Der Zusatz an Zellulosederivat es wirkt sich auch vorteilhaft auf das Haften des Mörtelgemisches beim Anwerfen oder Auftragen aus, denn selbst Mörtcleemische. die keinen Kalk enthalten und nur Halbhydrat als Bindemittel, haften besser auf bestimmten Untergründen, wenn sie einen Anteil eines Zellulosederivats enthalten. Das Zellulosederivat sollte wie bereits erwähnt wasserlösliche Methylzellulose sein mit einer Viskosität von 2000 bis 10 000 cp in einer 2%igen wäßrigen Lösung bei 200CThe addition of the cellulose derivative to the mortar mixture has the advantage that disadvantages which may arise from the presence of a relatively large amount of calcium hydroxide are eliminated. The addition of the cellulose derivative also has a beneficial effect on the adhesion of the mortar mixture when it is started or applied, because even mortar mixtures. which contain no lime and only hemihydrate as a binding agent, adhere better to certain substrates if they contain a proportion of a cellulose derivative. As already mentioned, the cellulose derivative should be water-soluble methyl cellulose with a viscosity of 2000 to 10,000 cp in a 2% aqueous solution at 20 ° C

Die Herstellung des Hauptbestandteiles des trockenen Möitelgemisches, nämlich des ^Kalziumsulfat-Halbhydrats^gcschieht in der folgenden Weise. Der beispielsweise in einem Kraftwerk anfallende, von eiu£r Schubzentrifuge abgegebene Gips (Kalziumsulfat-Dihydrat) fällt mit einem Wassergehalt von < als 10 Gew.-% in großstückiger Form an. Diese Stücke sind aufgrund ihrer Entstehungsgeschichte natürlich erheblich weniger dicht als natürlicher Gipsstein. Sie werden daher nach dem Brennen in einem bekannten Brennaggregat, beispielsweise Kocher oder Drehrohrofen, und nach dem Mahlen in äußerst feinteiliger staubförmiger Gestalt anfallen, weil der Brennvorgang den ohnehin porösen Gips durch das austretende Kristallwasser noch stärker aunockert und den Gefugezusammenhang zerstört Sehn Mahlen fälh dann ein praktisch staubfSrmiges Produkt an, das, wie alle Versuche gezeigt haben, für die Herstellung von Putzen nicht brauchbar istThe main component of the dry mortar mixture, namely calcium sulphate hemihydrate, is produced in the following way. The accumulating in a power plant, for example, from eiu £ r Pusher centrifuge dispensed gypsum (calcium sulfate dihydrate) is obtained in large pieces with a water content of <10% by weight. These pieces are of course, due to the history of its origins, it is considerably less dense than natural gypsum stone. you will be therefore after firing in a known firing unit, for example cooker or rotary kiln, and after grinding in extremely finely divided powdery Shape accrue because the firing process removes the already porous gypsum through the emerging crystal water loosens even more and destroys the structure Product which, as all tests have shown, cannot be used for the production of plasters

Erfindungsgemäß wird dann dieses feimeilige Material ohne Bindemittel trocken in einer entsprechenden Presse kompaktien zu nußgroßen Stücken, wobei lediglich die MatrizenoberfläcÄe angefeuchtet wird.According to the invention, this fine-grained material is then used dry without binding agent in an appropriate press compact to nut-sized pieces, with only the die surface is moistened.

Wie bereits oben erwähnt, kann diessm feinteiligen Halbhydratprodukt bereits vor dem Kontaktieren das eine oder das andere, oder auch mehrere Zusatzmittel zugemischt werden, die für das Putzgemisch erforderlich sind, beispielsweise Netzmittel, Beschleuniger und Verzögerer.As already mentioned above, this can be finely divided Hemihydrate product one or the other, or even several additives, even before contacting are added, which are necessary for the plaster mixture, such as wetting agents, accelerators and Retarder.

Die nach der Kontaktierung anfallenden äußerst festen und dichten Briketts werden nun in bekannten Aggregaten gemahlen und auf die oben aufgeführten Korngrößenverteilung gebracht.
. Das nunmehr vorliegende Korngcmisch aus dem gemahlenen kömpaktierten KaJziumsuifathalbhydrat kann'nun in überraschend vorteilhafter Weise zur Herstellung von Trockenputzmischungen eingesetzt und wie ein Produkt verarbeitet werden, das aus natürlichem Gipsgestein hergestellt ist.The extremely solid and dense briquettes obtained after contacting are now ground in known units and brought to the particle size distribution listed above.
. The grain mixture now available from the ground, compacted calcium sulfate hemihydrate can now be used in a surprisingly advantageous manner for the production of dry plaster mixtures and processed like a product made from natural gypsum rock.

Falls gewünscht, kann die Verwendung dieses Materials auch für andere Zwecke erfolgen mit den gleichen günstigen Eigenschaf ten, beispielsweise zur Herstellung von Formkörpern.If desired, you can use this material also for other purposes are made with the same favorable properties, for example for production of molded bodies.

Claims (3)

1 2 ren zur Herstellung des für die Putzmischung verwcn-Patentansprüche: deten Kalziumsulfat-Halbhydrats- Trockene pulverförmige Mischungen unter Verwen-1 2 ren for the production of the plaster mixture used for the patent claims: Deten calcium sulfate hemihydrate dry powder mixtures using 1. Trockene pulverförmige Putzmischung unter dung von Kalzuimsulfat-Haibhydrat als wesentlichen Verwendung von bei der Rauchgasentschwefelung 5 Bestandteil und mit verschiedenen Zusätzen, wie Kalkanfallendem Gips, dadurch gekennzeich- stein und Kalk und anderen das Abbinden des Halbhyn e t. daß sie die folgende Zusammensetzung hat: drats beeinflussenden Stoffes, sind an sich bekannt und1. Dry powdery plaster mixture with calcium sulphate shark hydrate as essential Use of a component in the flue gas desulphurisation 5 and with various additives, such as lime-based gypsum, which characterizes stone and lime and other types of hardening of the Halbhyn e t. that it has the following composition: drats influencing substance are known per se and werden zur Herstellung sehr feiner glatter Oberflächenare used to produce very fine, smooth surfaces Bis 75 Gew.-% /-Halbhydrat aus bei der Rauchgas- verwandt. Solche Putzmörtelgemische werden durch entschwefelung anfallendem Gips, der in an sich be- 10 Zugabe von Wasser in eine breiige oder pastöse Konsikannter Weise zu Halbhydrat gebrannt ist das anfal- stenz überführt und von Hand oder vermittels gccignelende y^-Halbhydrat kompaktiert und erneut auf die ter Maschinen auf die zu verputzende Fläche aufgetrafolgende Sicblinie vermählen ist gen und in bekannter Weise verarbeitet.Up to 75% by weight / hemihydrate from related to the flue gas. Such plaster mixes are through desulphurisation of the gypsum that occurs in itself. 10 Adding water to a pasty or pasty consistency Burned to hemihydrate in a way, the initial stiffness is transferred by hand or by means of gccignelende y ^ -Hemihydrate compacted and applied again to the machines on the surface to be plastered Sizing lines are milled and processed in a known manner. _ Unter Berücksichtigung der heute erforderlichen_ Taking into account the 0—0.03 mm 30—40Gew.-% 15 Überlegungen, insbesondere auf dem Gebiet des Bau-0-0.03 mm 30-40% by weight 15 considerations, especially in the field of construction 0.03—0.06 mm 5—12Gew.-% wesens. ist man aber nach und nach dazu übergegangen,0.03-0.06 mm 5-12% by weight essential. but one gradually went over to 0,06—0,1 mm 10—20Gew.-% diese Putzmörtelgemische, die Kalziumsulfat-Haibhy-0.06-0.1 mm 10-20% by weight of these plaster mortar mixtures, the calcium sulfate Haibhy 0,1—02 mm 9—15Gew.-% drat als Bindemittel enthalten, maschinell aufzuvragen.0.1-02 mm 9-15% by weight drat as a binding agent, applied by machine. 0^—03 mm 8—18Gew.-% Diese maschinelle Auftragung, die eine erhebliche Ra-0 ^ - 03 mm 8 - 18% by weight This mechanical application, which has a considerable 0,5—1.0 mm 7—15 Gew.-% 20 tionalisierung des Verputzvorganges bewirkt, erfordert0.5-1.0 mm 7-15% by weight 20 functionalization of the plastering process, requires jedoch eine ganz spezielle, auf die maschinelle Auftra-however, a very special one, to which machine application 15 bis 22 Gew.-% Kslkstcingrics, in Form von ehe- gong abgestnnnue Zusammensetzung des Mörteigemimisch gefälltem Kaliumcarbonat, Kreide oder ge- sches, damit der maschinelle Auftragungsvorgang ohne mahienem Dolomit mit einer Teilchengröße von Nachteile für das aufgetragene plastische Mörtelgehöchstens 0,15 mm 25 misch vorsieh geht, d.h. das Mörtelgemisch insbesonde-15 to 22% by weight Kslkstcingrics, in the form of ehe-gong cut-off composition of the mortar mix Precipitated potassium carbonate, chalk or other things, so that the machine application process without mahienem dolomite with a particle size of disadvantages for the applied plastic mortar at most 0.15 mm 25 mix, i.e. the mortar mix in particular 1 bis 5 Gew.-% Kalk, in Form von Kalziumhydroxid re auf den unterschiedlichsten Untergründen schnell oder Weißkalk mit einer Korngröße von höchstens und gut ansetzt, d. h. haftet, nicht spritzt, sich anschlie-0.10 mm ßend auch gut verarbeiten und glätten läßt1 to 5% by weight of lime, in the form of calcium hydroxide, quickly on a wide variety of substrates or white lime with a grain size of at most and well sets, d. H. adheres, does not splash, then follows-0.10 mm ßend can also be processed and smoothed well Es ist ferner wichtig, daß die Putzmörtelmischung einIt is also important that the mortar mix is one 0,01 bis 0,03 Gew.-% Andicker (Stärkeäther) 30 Halbhydratkorn aufweist, welches eine gewisse Stand-0.01 to 0.03% by weight thickener (starch ether) 30 hemihydrate grains, which have a certain stand- 0,1 bis 0,5 Gew.-% Beschleuniger festigkeit bzw. Zerfallfestigkeit hat, damit das breiig auf0.1 to 0.5 wt .-% accelerator strength or decay strength, so that the pulpy 0.1 bis 0,5 Gew.-% wasserlösliches Zellulose- die zu verputzende Fläche aufgetragene Mörtelgemisch0.1 to 0.5% by weight of water-soluble cellulose - the mortar mixture applied to the surface to be plastered derivat in ordnungsgemäßer Weise abgezogen, kardätscht, ge-derivative properly withdrawn, kardätscht, processed 0,p<, bis 0.05 Gew.-% Netzmittel filzt usw. werden kann, damit eine makellose glatte wei-0, p <, up to 0.05% by weight of wetting agent, etc. can be felted, so that a flawless smooth white 0,05 bis 0,5 Gew.-% Verzögererund ' ■ 35 ße Oberfläche entsteht Es hat sich gezeigt, daß für einen0.05 to 0.5 wt .-% retarder and '■ 35 ße surface results. It has been shown that for one 1 bis 2 Gew.-% geblähtes Perlit als Füll-. solchen Bearbeitungsvorgang gerade die Körnung, bes-1 to 2% by weight of expanded perlite as filler. such a machining process precisely the grain, especially stoff. ser gesagt, die physikalischen und morphologischen Eimaterial. that is, the physical and morphological egg genschaften des Korns des Bindemittels, von großer Be-properties of the grain of the binder, of great importance 2. Putzmischung nach Anspruch 1, dadurch ge-. ■ deutungsind.2. plaster mixture according to claim 1, characterized in that. ■ are meaningful. kennzeichnet, daß das in der Putzmischung enthalte- 40 Nun ist es zwar möglich, unter Verwendung von ausne /-Halbhydrai die folgende Kornverteilung auf- gesuchten Materialien, beispielsweise von Hochbranntweist: gipsen, die z.B. in einer Claudius-Peters-Mühle hergeindicates that this is contained in the plaster mixture / -Halbhydrai the following particle size distribution of the materials found, for example from Hochbranntweise: plaster, which e.g. here in a Claudius Peters mill stellt sind, solche Mörtelgemische herzustellen, jedochplaces are to produce such mortar mixes, however 0—0,03 mm 35—38Gew.-% · · · gehen diese Halbhydrate immer von natürlichem, schon0-0.03 mm 35-38% by weight · · · these hemihydrates always come from natural, already 0,03—0,06 mm 6—10Gew.-% 45 von Haus aus gutem Gipsgestein aus. Andererseits cnt-0.03-0.06 mm 6-10% by weight 45 made from good gypsum stone by default. On the other hand cnt- 0,06—0,1 mm 12—17Gew.-% . stehen gerade in der heutigen Zeit aufgrund der bcson-0.06-0.1 mm 12-17 wt%. are currently due to the bcson- 0,1 —02 mm . 10— 15Gew.-% deren Umweltschutzbestimmungen größere Gipsmcn- 0.1-02 mm. 10-15% by weight whose environmental protection regulations 0,2—0.5 mm 14—18Gew.-% gen aus der Entschwefelung der Abgase, die ebenfalls0.2-0.5 mm 14-18% by weight from the desulphurisation of the exhaust gases, which also 0,5— 1.0 mm 8—12Gew.-% . einer umweltschonenden Verwertung zugeführt wer-0.5-1.0 mm 8-12% by weight. can be recycled in an environmentally friendly manner 50 den müssen..50 den must .. 3. Verfahren zur Herstellung des y?-Halbhydrats Solche, aus der Rauchgasentschwefelung stammennach Anspruch 1. dadurch gekennzeichnet, daß der den Gipse lassen sich aber nicht ohne weiteres für Putzbci der Rauchgasentschwefelung mit einer Feuchte gipse verarbeiten, u. a. wegen ihrer Feinheiten.3. Process for the production of the y? Claim 1. characterized in that the plasters can not be easily used for Putzbci the flue gas desulphurisation process with a damp plaster, among other things. because of their subtleties. von < 10 Gew.-% anfallende Gips in an sich bekann- . Die Ver- bzw. Bearbeitung von Rauchgasentschwefcter Weise zu Halbhydrat gebrannt wird, das anfal· 55 lungsgips ist in der Literatur beschrieben, beispielsweise lende feinteilige /-Halbhydrat trocken bei Raum- in der Offenlegungsschrift DE-OS 28 26 769. nach der temperatur durch Pressen zu Briketts kompaktiert der Rauchgasentschwefelungsgips kompaktiert wird, zu wird, wobei die Matrizenoberflächen vor dem Korn- Anhydrit gebrannt wird und anschließend auf eine bepaktieren angefeuchtet werden und die Briketts zu stimmte Körnung gemahlen wird. Dieses Produkt aus einer Körnung vermählen werden, die eine Korn- ω der Rauchgasentschwefelung wird dann mil /f-Kalgrößenverteilung gemäß Anspruch f aufweist. ziumsulfai-Halbhydrai in bestimmter Menge vermischt.of <10 wt .-% accruing gypsum in per se known. The processing of flue gas desulfurizers If it is burned to hemihydrate, the plaster of paris is described in the literature, for example loin finely divided / hemihydrate dry in space in the laid-open application DE-OS 28 26 769. after temperature by pressing the flue gas desulphurisation gypsum is compacted into briquettes is, the die surfaces are burned before the grain anhydrite and then packaged on one moistened and the briquettes are ground to the correct grain size. This product from one grain size is ground, the one grain ω of the flue gas desulphurisation is then mil / f cal size distribution according to claim f having. ziumsulfai hemihydra mixed in a certain amount. Dies mag eine Methode sein, den Rauchgasentschwcfc-This may be a method of exhausting the flue gas ' lungsgips zu verwerten, jedoch ergibt sich daraus noch'to utilize lung plaster, however, still results from it keine für Putze geeignete Mischung.not a mixture suitable for plasters. 65 Aus der DE-AS 21 37 860 ist ein Puizgips bekanntgc-65 From DE-AS 21 37 860 a plaster of paris is knowngc- Die Erfindung betrifft eine trockene pulverförmige worden auf der Basis von Kalziumsulfat-HalbhydratThe invention relates to a dry powdered product made on the basis of calcium sulfate hemihydrate Putzmischung unter Verwendung von bei der Rauch- durch Teilentwässerung des Dihydrats in ein oder zweiPlaster mixture using in the smoke through partial drainage of the dihydrate in one or two gasemschwefelung anfallendem Gips sowie ein Verfah- Temperaturstufen und wobei das dehydratisieric Mate-gypsum accumulating gas sulphurisation as well as a process temperature stages and whereby the dehydrating material
DE19803048506 1980-12-22 1980-12-22 Dry powder plaster mixture and process for its preparation Expired DE3048506C2 (en)