DE3039526A1

DE3039526A1 - Fixative for anionic dyestuff applied to polyamide textile - is quat. cycloalkyl, phenyl or naphthyl chloro-hydroxypropyl di:alkyl ammonium salt

Info

Publication number: DE3039526A1
Application number: DE19803039526
Authority: DE
Inventors: Emil Binningen Engeler; Karl-Heinz Aesch Weible
Original assignee: Sandoz AG; Sandoz Patent GmbH
Current assignee: Sandoz AG; Sandoz Patent GmbH
Priority date: 1979-10-30
Filing date: 1980-10-20
Publication date: 1981-05-14

Abstract

Fixative used in dyeing textiles contg. natural and synthetic polyamides with anionic dyestuffs, is a quat. ammonium salt (I) of the formula (RCH2-N(+)R1R2-CH2-CH(OH)-CH2Cl) X(-) (in which R is 5 or 6 C cycloalkyl or a phenyl or naphthyl gp. with 0-3 1-4 C-alkyl, 0 1 or 2 Cl and/or 0, 1 or 2 Br substit(s). and a total of max. 3 substits. R1 and R2 are 1-4C alkyl. X(-) is an anion). Treatment is carried out in weakly acid to weakly alkaline medium. (I) is useful in dyeing wool, silk and esp. synthetic poly- amides, opt. mixed with other fibres, e.g. polyesters. It improves the fastness, esp. wet fastness, of the dyeing obtd. with anionic dyestuffs and also with 1:1 and 1:2 metal complex dyestuffs (with or without sulpho gps.).

Description

Verfahren zur TextilbehandlungProcess for textile treatment

Die vorliegende Erfindung betrifft ein Verfahren zum verbessarten Färben von natürliche und/oder synthetische Polyaiaide enthaltenden textilen Materialien.The present invention relates to a method for improving Dyeing of natural and / or synthetic polyamide-containing textile materials.

Insbesondere betrifft die vorliegende Erfindung ein Verfahren zum Färben von synthetische Polyamide enthaltenden textilen '.Iaterialien mit anionischen Farbstoffen, welches dadurch gekennzeichnet ist, dass man das gefärbte textile Material mit einem quaternierten Ammoniumsalz der Formel worin R Cycloalkyl (C5>6), unsubstituiertes Phenyl oder Naphtyl oder durch 1-3 Alkyl (C1 4), 1 oder 2 Chlor- und/oder 1 oder 2 Bromatome substituiertes Phenyl oder Naphtyl, wobei höchstens 3 dieser Substituenten anwesend sind, R1 und R2 unabhängig voneinander Alkyl (C1-4) und ein Anion bedeuten, im schwach sauren bis schwach alkalkalischen Medium behandelt Gegenstand der vorliegenden Erfindung sind weiter Mittel, welche die o.In particular, the present invention relates to a process for dyeing textile materials containing synthetic polyamides with anionic dyes, which is characterized in that the dyed textile material is treated with a quaternized ammonium salt of the formula wherein R is cycloalkyl (C5> 6), unsubstituted phenyl or naphthyl or phenyl or naphthyl substituted by 1-3 alkyl (C1 4), 1 or 2 chlorine and / or 1 or 2 bromine atoms, with at most 3 of these substituents being present, R1 and R2 are independently alkyl (C1-4) and an anion, treated in a weakly acidic to weakly alkaline medium.

g. Verbindungen enthalten sowie die vermittels dieser Verbindung gefärbten textilen Materialien.G. Contain compounds as well as those colored by means of this compound textile materials.

In den Verbindungen der Formel (I) bedeutet R vorzugsrweise Phenyl, Tolyl, Sylyl, Naphtyl, Methylnaphtyl, Chlornaphtyl, Cyclopentyl, Cyclo hexyl, vorzugsweise Phenyl, Naphtyl, Cyclohexyl, vorzugsweise Phenyl.In the compounds of the formula (I), R preferably denotes phenyl, Tolyl, sylyl, naphthyl, methylnaphthyl, chloronaphthyl, cyclopentyl, cyclohexyl, preferably Phenyl, naphthyl, cyclohexyl, preferably phenyl.

R1 und R2 sind unabhängig voneinander Methyl oder Aethyl, vorzugsweise Methyl, vorzugsweise bedeuten R1 und R2 Methyl.R1 and R2 are, independently of one another, methyl or ethyl, preferably Methyl, preferably R1 and R2 are methyl.

X ist ein nicht-chrom.ophores Anion, dessen Natur im übrigen nicht kritisch ist. Vorzugsweise bedeutet X- Cl-, Br- J- oder CH3SO4-, vorzugsweise C1 oder r.X is a non-chromophore anion, the nature of which is otherwise not is critical. X-Cl-, Br-J- or CH3SO4-, preferably C1 or r.

e e Brd e Von den Verbindungen (II), (III) und (IV), worin X1 Cl oder Br bedeuten, sind die Verbindungen (II) bevorzugt. ee Brd e Of the compounds (II), (III) and (IV) in which X1 is Cl or Br, the compounds (II) are preferred.

Die obgenannten Verbindungen sind teils bekannt oder können auf an sich bekannte Art hergestellt werden, wie dies z.B. in den US PS's 2 876 217 und 2 995 513 beschrieben ist.Some of the above-mentioned compounds are known or can be linked to known in the art, such as in U.S. Patents 2,876,217 and 2,995,513.

Erfindungsgemss färbt man textile Materialien, welche Fasern aus natürlichen oder synthetischen Polyamiden wie Wolle, Seide und vor allem Nylon, Perlon und ähnliche synthetische Polyamide enthalten. Solche testile GeweSe können auch im Gemisch mit anderen z.B. mit Polyesterfasern vorliegen. Die erfindungsgemäss zu verwendenden Verbindungen der Forsel(I) werden durch eine Nachbehanalung der gefärbten Tes.tilwateri21ien und in manchen Fällen auch zusammen mit dem Farbstoff aufgebrac'nt.According to the invention, textile materials are dyed, which fibers are made from natural fibers or synthetic polyamides such as wool, silk and especially nylon, perlon and the like contain synthetic polyamides. Such testile tissues can also be mixed with others e.g. with polyester fibers. The to be used according to the invention Compounds of Forsel (I) are made by re-treating the colored Tes.tilwateri21ien and in some cases also applied together with the dye.

Die Flotten oder Druckpasten enthalten vorzugsweise 0,05 - 10%, vorzugsweise 0,1- 5Z, vorzugsweise 0,2 - 2% der Verbindung der Formel (1) bezogen auf das Gesamtgewicht der Flotten oder Druckpasten.The liquors or printing pastes preferably contain 0.05-10%, preferably 0.1-5Z, preferably 0.2-2% of the compound of the formula (1) based on the total weight of the liquors or printing pastes.

Das Aufbringen der erfindungsgemäss zu verwendenden Hilfsmittel nach dem Färben kann durch Aufspritzen, Aufsprühen, Aufpflatschen, Foulardieren und Behandlungen im Bad, trocken oder nass-in-nass, x70rgenonnen werden. Die Fixierung des applizierten Produktes erfolgt entweder im Sattdampf bei 1020C während 6-10 Minuten oder im Heissdampf bei 120-1800C wärend 2-10 Minuten, vorzugsweise aber durch Trockenhitze-Behandlung bei 120-180"C während 1-10 Minuten Die benötigten Mengen, bezogen auf das Gewicht des Textilsubstraten in Abhängigkeit der färberischen Eigenschaften der vorangehend beschriebenen Farbstofftypen, der Substrateigenschaften und der geçunschten Echtheitsverbesserungen betragen 0,5 - 10%, vorzugsweise 1 - 4%.The application of the auxiliaries to be used according to the invention after The dyeing can be done by spraying on, spraying on, paddling, padding and treatments be soaked in the bathroom, dry or wet-on-wet. The fixation of the applied Product takes place either in saturated steam at 1020C for 6-10 minutes or in superheated steam at 120-1800C for 2-10 minutes, but preferably by dry heat treatment at 120-180 "C for 1-10 minutes The quantities required, based on weight of the textile substrate depending on the dyeing properties of the preceding types of dyes described, the substrate properties and the desired improvements in fastness are 0.5-10%, preferably 1-4%.

Der pH-Wert des Behandlungsbades liegt im allgemeinen zwischen 6 und 10. Zur Einstellung dieses pH-Wertes können Alkalien, alkalisch reagierende Salze oder auch Substanzen, die erst beim Erhitzen ein alkalisches Medium ergeben, wie z.B. Natriumbicarbonat oder Alkalisalze der Trichloressigsäure, zugesetzt werden.The pH of the treatment bath is generally between 6 and 10. Alkalis and alkaline-reacting salts can be used to adjust this pH value or substances that only produce an alkaline medium when heated, such as e.g. sodium bicarbonate or alkali salts of trichloroacetic acid can be added.

Die Temperatur der Behandlungsbäder liegt, vor allem wegen deren Haltbarkeit über einen langen Zeitraum, zwischen 0 - 40°C. Sie kann auch höher gewählt werden, sofern dies durch geeignete technische Massnahmen ersöglicht wird.The temperature of the treatment baths is low, mainly because of their durability over a long period of time, between 0 - 40 ° C. It can also be chosen higher, if this is made possible by suitable technical measures.

Den Behandlungsflotten können weiter Netzmittel und Produkte zugefügt werden, die die elektrostatische Aufladung der Fasern vermindern. Weiter können solche Mittel, die geeignet sind, den Griff der Fertigware zu verändern, wie Beschwerungsmittel, Füllmittel, Versteifungsmittel oder Schiebefestigkeit und/oder die Maschenfestigkeit erhöhende ("Antisnag-Hittel") sowie Weichmachungs:7ittel nach Bedarf der Behandlungsf lotte zugegeben werden.Wetting agents and products can also be added to the treatment liquors that reduce the electrostatic charge on the fibers. Can continue such means that are suitable for changing the feel of the finished product, such as weighting agents, Fillers, stiffeners or slip resistance and / or the mesh strength increasing ("Antisnag-Hittel") and softening agents as required by the treatment lotte to be admitted.

Hit Hilfe der beschriebenen Fixiermittel der Formel (1) wird ausser einer Farbvertiefung eine Verbesserung der Echtheiten, insbesondere der Nassechtheiten von mit anionischen Farbstoffen erzeugten Färbungen erzielt. Unter anionischen Farbstoffen werden hier die üblichen Säure-Farbstoffe verstanden, wie sie z.B. in Colour Index zusammengefasst sind.Hit the help of the fixatives of the formula (1) described is except a deepening of the color an improvement in the fastness properties, in particular the wet fastness properties achieved by dyeings produced with anionic dyes. Among anionic dyes the usual acid dyes are understood here, such as those in Color Index are summarized.

Auch sind 1:1 wie 1:2 ?ietallkomplexfarbstoffe geeignet (mit oder ohne Sulfogruppen).1: 1 and 1: 2 metal complex dyes are also suitable (with or without sulfo groups).

Die nachfolgenden Beispiele erläutern das Verfahren. Teile sind Gewichtsteile oder Volumenteile. Z-Angaben erfolgen in Gewichtsprozenten.The following examples explain the process. Parts are parts by weight or parts by volume. Z data are given in percent by weight.

Beispiel 1 1 000 T eines PA 6-Tuftingteppichs (mit Schlingen) (Perlonware), regular anfärbbar, 17 den., werden mit 20 T des sauren Egalisierungsfarbstoffes der nachfolgenden Formel 10 T eines sulfonierten Rizinolsäureesters in 40 000 T Wasser während 60 Minuten bei 980C gefärbt. Es wird wie üblich gespült und getrocknet. Die Ware zeigte eine Nassheitsnote von 3.EXAMPLE 1 1,000 T of a PA 6 tufted carpet (with loops) (Perlon fabric), can be dyed regularly, 17 denier, are mixed with 20 T of the acidic leveling dye of the formula below 10 parts of a sulfonated ricinoleic acid ester in 40,000 parts of water for 60 minutes at 980C. It is rinsed and dried as usual. The goods had a wetness rating of 3.

Durch Nachbehandlung dieser Ware auf dem Foulard mit 1 000 T einer Lösung, enthaltend 30 Teile der Verbindung II, (X1 = C1) und 15 Teile Natriumbikarbonat, und anschliessendes Trocknen bei 1405 am Spannrah:nen während 8 Minuten wird die Nassechtheit verbessert. By post-treating these goods on the padder with 1 000 T one Solution containing 30 parts of compound II, (X1 = C1) and 15 parts of sodium bicarbonate, and subsequent drying at 1405 on the tensioning frame for 8 minutes Improved wet fastness.

Beispiel 2 1 000 T eines Polyamides 6.6, (Nylon) regular anfärbbar, 17 den. Stapelgarn in Form eines getufteten Schnittflor-Teppichs, werden mit 5 000 T einer Lösung, enthaltdend 1,45 T des Handelsfarbstoffes C. I.Example 2 1,000 T of a polyamide 6.6, (nylon) regular dyeable, 17 den. Staple yarn in the form of a tufted cut pile carpet are valued at 5,000 T of a solution containing 1.45 T of the commercial dye C. I.

Acid Orange 156 1,05 T des Handelsfarbstoffes C. I. Acid Orange 156 1.05 T of C.I.

Acid Red 57 1,23 T des Handelsfarbstoffes C. I. Acid Red 57 1.23 T of the commercial dye C.I.

Acid Blue 72 4,0 T Kernmehlaether-Verdickung (Handelsware) 2,0 T Natriumlauryldiglycolaethersulfat 2,0 T Mononatriumphosphat 0,3 T Dinatriumphosphat begossen und anschliessend in einem Hängeschlaufendämpfer im Sattdampf von 1000C während 8 Minuten gedämpft, gewaschen, abgesaugt und getrocknet. Die Färbung weist eine Nassechtheit (streng) von 3,5 auf. Acid Blue 72 4.0 T core flour ether thickening (commercial goods) 2.0 T Sodium lauryl diglycola ether sulfate 2.0 T monosodium phosphate 0.3 T disodium phosphate doused and then in a hanging loop damper in saturated steam of 1000C steamed, washed, filtered off with suction and dried for 8 minutes. The coloring shows a wet fastness (strict) of 3.5.

Die Nachbehandlung erfolgt durch Besprühen mit 500 T einer Lösung, enthaltend 40 T der Verbindung II (X1 = Br) und 20 T Natriumbicarbonat Anschliessend wird der Teppich am Spannrahmen bei 1500C während 8 Minuten getrocknet. Es resultiert eine Verbesserung der Nassechtheit (streng). The aftertreatment is carried out by spraying with 500 T of a solution, Then containing 40 parts of compound II (X1 = Br) and 20 parts of sodium bicarbonate the carpet is dried on the tenter at 1500C for 8 minutes. It results an improvement in wet fastness (strict).

Beispiel 3 Eine Färbung auf einer Wirkware aus PA 6 (Perlon), regular färbbar, 2 den. (endlos-Faser), mit einer handelsüblichen Farbstoffkombination 3,4 % C. 1. Acid Orange 127 0,66 % C. I. Acid Red 299 1,68 % C. I. Acid Blue 280 ergibt eine Waschechtheit bei 600C von 3.Example 3 Dyeing on a knitted fabric made of PA 6 (Perlon), regular colorable, 2 den. (continuous fiber), with a commercially available dye combination 3,4 % C. 1. Acid Orange 127 0.66% C. I. Acid Red 299 1.68% C. I. Acid Blue 280 yields a wash fastness at 600C of 3.

Die Nachbehandlung erfolgt mit 1 000 T einer Flotte, enthaltend 40 T von Produkt II (X1 = C1) und 20 T Natriumbicarbonat am Foulard. (ilotten-Aufnahve 100%.) Anschliessend wird getrocknet (4 Minuten bei 1600C am Spannrahmen). Eine Erhöhung der Waschechtheit 600C resultiert. The aftertreatment is carried out with 1,000 T of a liquor containing 40 T of product II (X1 = C1) and 20 T sodium bicarbonate on a padder. (ilotten recording 100%.) It is then dried (4 minutes at 1600C on the stenter). One The result is an increase in wash fastness 600C.

Claims

Middle and method for textile treatment P a L entanspri che method for dyeing natural and synthetic polyamides containing textile materials with anionic dyes, characterized in that the dyed textile material with a quaternized ammonium salt of the formula wherein R is cycloalkyl (C5.6), unsubstituted phenyl or naphthyl or phenyl or naphthyl substituted by 1-3 alkyl (C1-4), 1 or 2 chlorine and / or 1 or 2 bromine atoms, with at most 3 of these substituents being present, R1 and R2, independently of one another, denote alkyl (C1) and 1-4 denote an anion, treated in a weakly acidic to weakly alkaline medium.

2. The textile materials dyed according to claim 1.

3. Textile treatment agents containing compounds of the formula (I) according to claim 1.