DE3018764A1 - Dry paper esp. wall paper adhesive coating - comprises cellulose or starch ether, hydrocolloid, separating agent and filler - Google Patents

Dry paper esp. wall paper adhesive coating - comprises cellulose or starch ether, hydrocolloid, separating agent and filler

Info

Publication number
DE3018764A1
DE3018764A1 DE19803018764 DE3018764A DE3018764A1 DE 3018764 A1 DE3018764 A1 DE 3018764A1 DE 19803018764 DE19803018764 DE 19803018764 DE 3018764 A DE3018764 A DE 3018764A DE 3018764 A1 DE3018764 A1 DE 3018764A1
Authority
DE
Germany
Prior art keywords
weight
water
parts
paper
starch
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE19803018764
Other languages
German (de)
Inventor
Eberhard Dipl.-Chem. Dr. 4010 Hilden Grünberger
Roswitha 4006 Erkrath Müller
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Henkel AG and Co KGaA
Original Assignee
Henkel AG and Co KGaA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Henkel AG and Co KGaA filed Critical Henkel AG and Co KGaA
Priority to DE19803018764 priority Critical patent/DE3018764A1/en
Publication of DE3018764A1 publication Critical patent/DE3018764A1/en
Withdrawn legal-status Critical Current

Abstract

A dry coating materila for paper to be adhered esp. for the reverse side of wall paper comprises 100 pts.wt. water soluble, adhesive cellulose ether and/or starch ether or its degradation prod., 1-40 pts.wt. hydrocolloid (I) which produces a (practically) non-tacky highly viscous aq. soln., 10-50 pts.wt. water soluble and/or dispersible separating agent (II), 50-300 pts.wt. water soluble and/or -dispersible filler (III) and opt. other additives and preservatives. The cellulose ether is pref. hydroxyethyl cellulose, methylhydroxy alkyl cellulose and/or CMC. (I) is polyacrylamide with a mol.wt. of 500000-10 power 7, an alkali alginate and/or galactomannan. (II) is pref. alkali(ne earth) metal soaps, Al soaps, Al silicates and/or silica. (III) is starch and/or urea. The compsn. is applied as a 10-30% soln. or dispersion. The adhesive adheres well to the paper so that it swells rapidly when wetted with water but does not wash out. The wetted adhesive adheres well but the dried paper can still be easily removed.

Description

30197843019784

4000 Düsseldorf, den 12. Mai 1980 HENKELKGaA4000 Düsseldorf, May 12, 1980 HENKELKGaA

Henkelstraße 67 _ 3 _ ZR-FE/PatenteHenkelstrasse 67 _ 3 _ ZR-FE / Patents

Dr.SchOe/GeDr.SchOe / Ge

Patentanmeldung D 6175 Patent application D 6175

"Beschichtungsmaterial für zu verklebende Papiere""Coating material for papers to be glued"

Die vorliegende Erfindung betrifft ein Beschichtungsmaterial zur Kleb-Ausrüstung von Papier oder Pappe, insbesondere der Rückseiten von Tapeten. Bei den so präparierten Tapeten soll nach kurzem Tauchen in Wasser die Beschichtung rasch anquellen und ein gutes Verkleben in üblicher Art gewährleisten. Trotzdem sollen die Tapeten später einmal wieder trocken leicht abgezogen werden können. Die Ausrüstung soll also sowohl adhäsiv als aehäsiv machen.The present invention relates to a coating material for the adhesive finishing of paper or cardboard, in particular the backs of wallpaper. The wallpaper prepared in this way should be immersed in water for a short time the coating swell quickly and ensure good gluing in the usual way. Nevertheless they should Wallpaper can be easily peeled off when dry. The equipment should therefore be both adhesive make as adhesive.

Es ist bekannt, Papiere dadurch entsprechend auszurüsten, daß man sie mit wäßrigen Dispersionen auf Basis von Polymerisaten aus Styrol und (Meth)arylestern auch im Gemisch mit Paraffinemulsionen beschichtet und damit nach normaler Verklebung mit einem Kleister auf Basis einer wäßrigen Methylcelluloselösung einen Trermeffekt erreicht. Es ist auch versucht worden, durch schichtweisen Auftrag einer Trennemulsion und einer Klebstoff-Dispersion ein System zu finden, daß sowohl zu einer Verklebung als auch zu einer späteren trockenen Abziehbarkeit von Tapeten führt.It is known to equip papers accordingly by adding them with aqueous based dispersions of polymers made from styrene and (meth) aryl esters, also coated in a mixture with paraffin emulsions and thus, after normal gluing with a paste based on an aqueous methyl cellulose solution, a tremor effect achieved. Attempts have also been made by applying a release emulsion and a Adhesive dispersion to find a system that both to a bond and to a later dry Removability from wallpaper leads.

/2/ 2

1300A9/00A01300A9 / 00A0

3Q1875A3Q1875A

Patentanmeldung D 6l75 / L· HENKELKGaAPatent application D 6175 / L · HENKELKGaA

■"■■*■" ZR-FE/Patente■ "■■ * ■" ZR-FE / patents

Diese bekannte Art der Beschichtung weist Jedoch entscheidende Mängel auf. Eine entsprechend ausgerüstete Tapete muß zur Reaktivierung des Kleisters in Wasser getaucht werden, dabei wird der speziell bei mehrlagiger Beschichtung unzureichend auf der hydrophobierenden Trennschicht verankerte Kleister praktisch vollkommen abgewaschen. Eine ausreichende Verklebung der Tapete kann in diesem Falle nicht garantiert werden. Außerdem ist zur Gewährleistung eines guten Trenneffektes die Dehäsivbeschichtung grundsätzlich so hydrophob eingestellt, daß nach dem Tauchen der Tapete in Wasser, das notwendige sogenannte Ausquellen der zu verklebenden Tapeten stark verzögert wird. Während der verlängerten Ausquellzeit trocknet dann der Kleister von den Rändern her aus, und es kommt zu dem gefürchteten Aufspringen der Stoßkanten bei den verklebten Tapetenbahnen. However, this known type of coating has crucial Defects. A suitably equipped wallpaper must be used to reactivate the paste in water be immersed, especially in the case of multi-layer coating, inadequate on the hydrophobic Separating layer anchored paste is practically completely washed off. Adequate bonding of the Wallpaper in this case cannot be guaranteed. In addition, to ensure a good separation effect the adhesive coating is basically set so hydrophobic that after immersing the wallpaper in Water, the necessary so-called swelling of the wallpaper to be glued is greatly delayed. During the With a prolonged swelling time, the paste dries out from the edges, and the dreaded happens The abutting edges of the glued strips of wallpaper pop open.

Aufgabe der Erfindung war es, die bekannten Beschichtungen von Papieren beziehungsweise Rückseiten von Tapeten so zu verbessern, daß sie einmal in einem Arbeitsgang aufgetragen werden konnten und zum anderen der Klebstoffanteil so gut verankert ist, daß er beim Befeuchten in Wasser rasch anquillt, aber nicht ausgewaschen wird. Darüber hinaus sollte der geforderte Trenneffekt auch nach normaler Ausquellzeit der Tapeten beibehalten sein und eine einwandfreie Verklebung der Papiere beziehungsweise Tapeten möglich sein.The object of the invention was to provide the known coatings for papers or the backs of wallpapers to be improved so that they could be applied once in one operation and, on the other hand, the adhesive content is so well anchored that it swells quickly when moistened in water, but is not washed out. In addition, the required separation effect should be maintained even after the wallpaper has swelled normally and perfect bonding of the papers or wallpapers must be possible.

/3/ 3

130049/0040130049/0040

Sd 230 3. 02.80Sd 230 3. 02.80

Patentanmeldung D6175 f ~S HENKEL KGaAPatent application D6175 for S HENKEL KGaA

ZR-FE/PatenteZR-FE / patents

Diese Aufgabe wird erfindungsgemäß gelöst durch ein trockenes BeSchichtungsmaterial für zu verklebende Papiere, insbesondere Tapetenrückseiten, welches dadurch gekennzeichnet ist, das es besteht aus einer Kombination der folgenden Bestandteile:According to the invention, this object is achieved by a dry coating material for papers to be glued, in particular wallpaper backs, which is characterized in that it consists of a combination of the following components:

a) 100 Gewichtsteile wasserlösliche, klebende Celluloseether und/oder Stärkeether beziehungsweise Stärkeabbauprodukte und darauf bezogena) 100 parts by weight of water-soluble, adhesive cellulose ethers and / or starch ethers or starch degradation products and related thereto

b) 10 bis HO Gewichtsteile wenig beziehungsweiseb) 10 to HO parts by weight little respectively

nicht klebende hochviskose wäßrige Lösungen ergebende Hydrocolloide sowienon-sticky, highly viscous aqueous solutions, as well as hydrocolloids

c) 10 bis 50 Gewichtsteile wasserlösliche und/oder wasserdispergierbare Trennmittel sowiec) 10 to 50 parts by weight of water-soluble and / or water-dispersible release agents as well

d) 50 bis 300 Gewichtsteile wasserlösliche und/oderd) 50 to 300 parts by weight of water-soluble and / or

wasserdispergierbare Füllstoffe sowie gegebenenfallswater-dispersible fillers and optionally

e) weitere Hilfs- und Konservierungsmittel Nach einer bevorzugten Ausführungsform besteht das trockene Beschichtungsmaterial aus einer Kombination ause) further auxiliaries and preservatives after one preferred embodiment consists of the dry Coating material from a combination of

a) Methyl- beziehungsweise Hydroxyethylcellulosea) methyl or hydroxyethyl cellulose

beziehungsweise Methylhydroxyalkylcellulose und/ oder Carboxymethylcellulose undor methyl hydroxyalkyl cellulose and / or carboxymethyl cellulose and

b) Polyacrylamid mit einem Molgewicht zwischen 500 000 und 10 Millionen und/oder Alkalialginat und/oder Galactomannanen sowieb) polyacrylamide with a molecular weight between 500,000 and 10 million and / or alkali alginate and / or galactomannans as well

c) Alkali- beziehungsweise Erdalkaliseifen und/oderc) alkali or alkaline earth soaps and / or

Aluminiumseifen und/oder Aluminiumsilikat und/oder Kieselsäure sowie
d) native Stärke und/oder Harnstoff.Aluminum soaps and / or aluminum silicate and / or silica as well
d) native starch and / or urea.

130049/0040130049/0040

Patentanmeldung D 6l75 X~ G ~ HENKELKGaAPatent application D 6175 X ~ G ~ HENKELKGaA

ZR-FE/PatenteZR-FE / patents

.Als wasserlösliche klebende Celluloseether kommen in Frage Methylcellulose selbst beziehungsweise Hydroxyethylcellulose beziehungsweise Methylhydroxyalkylcellulose, also teilweise mit Propylenoxid beziehungsweise Ethylenoxid umgesetzte Methylcellulose. Derartige Celluloseether sind als Basis für wäßrige Kleblösungen allgemein üblich und bekannt. Weiterhin sind gut geeignet Carboxymethylcellulose oder im wesentlichen Carboxymethylgruppen enthaltende Cellulosemischether. Auch in diesem Fall kann es zweckmäßig sein, die Carboxymethylcellulose entweder vor ihrer Herstellung oder anschließend mit Propylenoxid oder Ethylenoxid umzusetzen. Als Stärkeether kommen ebenfalls Ethoxylierungs- und Propylierungsprodukte in Frage sowie auch Carboxymethy!stärke..As water-soluble adhesive cellulose ethers come in Question methyl cellulose itself or hydroxyethyl cellulose or methyl hydroxyalkyl cellulose, that is, methyl cellulose partially reacted with propylene oxide or ethylene oxide. Such Cellulose ethers are common and known as the basis for aqueous adhesive solutions. Furthermore are well suited Carboxymethyl cellulose or cellulose mixed ethers essentially containing carboxymethyl groups. Even in this case it may be appropriate to use the carboxymethyl cellulose to react either before their preparation or afterwards with propylene oxide or ethylene oxide. As a starch ether There are also ethoxylation and propylation products in question as well as carboxymethy! starch.

Entweder ganz oder teilweise können auch Stärkeabbauprodukte verwendet werden, welche ebenfalls gegenüber Papier eine gute Klebkraft entfalten. Dabei handelt es sich um Stärkehydrolysate wie etwa Dextrin.Starch degradation products can also be used either in whole or in part, which are also opposite Paper develop good adhesive strength. These are starch hydrolysates such as dextrin.

Als wenig beziehungsweise niehtklebende hochviskose wäßrige Lösungen ergebende Hydroeolloide kommen in erster Linie Polyacrylamidtypen in Frage, welche ein Molekulargewicht zwischen 500 000 und 10 Millionen aufweisen. In diesem Bereich sind bevorzugt allerdings Polyacrylamidtypen, die ein Molekulargewicht zwischen 2 und 5 Millionen haben. Die Polyacrylamidtypen können auch in bekannter Weise einer Teilhydrolyse unterzogen sein beziehungsweise durch Einbau von Comonomeren wie Acrylsäure oder Itaconsäure und dergleichen einen schwachanionenaktiven Charakter aufweisen. Geeignet sind fernerhin Natrium- oder Ammoniumalginate und/oder Galactomannan, beispielsweise vom Guartyp. Derartige Hydroeolloide weisen nur eine ganz geringe, praktisch zu vernachlässigende Klebkraft auf, beeinflussen aber die fertigen Kleblösungen hinsichtlich der Viskosität und des Wasserrückhaltevermögens günstig.Hydroeolloids which result in low or non-sticky, highly viscous aqueous solutions are used primarily polyacrylamide types in question, which have a molecular weight between 500,000 and 10 million. In this range, however, polyacrylamide types are preferred which have a molecular weight between Have 2 and 5 million. The polyacrylamide types can also be subjected to partial hydrolysis in a known manner be or by incorporating comonomers such as acrylic acid or itaconic acid and the like one have weak anion-active character. Sodium or ammonium alginates and / or are also suitable Galactomannan, for example of the guar type. Such hydroeolloids show only a very small, practical negligible bond strength, but affect the finished adhesive solutions in terms of viscosity and the water retention capacity.

/5/ 5

130049/0040130049/0040

Patentanmeldung DOITS ]f - J-- HENKELKGaAPatent application DOITS ] f - J-- HENKELKGaA

ZR-FE/PatenteZR-FE / patents

Weiterhin wirken sie hinsichtlich des Dispergierens auf die notwendigerweise einzuarbeitenden Füllstoffe positiv ein.Furthermore, with regard to dispersion, they have an effect on the fillers that must be incorporated positive one.

Als Trennmittel für den erfindungsgemäßen Zweck kommen beispielsweise Seifen des verschiedensten Typs vor. Unter Seifen sollen Alkali- beziehungsweise Erdalkaliseifen verstanden werden, die einen Alkylrest von 12 bis etwa 22, insbesondere 16 bis 18 Kohlenstoffatomen aufweisen. Derartige Fettsäuren werden aus natürlichen Fetten gewonnen, und es ist im allgemeinen nicht erforderlich, reine Seifen zu verwenden. Es hat sich aus praktischen Gründen bewährt, die Natriumseifen zu verwenden. Selbstverständlich ist es aber auch möglich, Kaliumseifen, Ammoniumseifen, Calciumseifen, Zinkseifen und/oder Aluminiumseifen einzusetzen. Eine weitere bewährte Gruppe von Trennmitteln sind Aluminiumsilikate der verschiedensten Art und die verschiedenen Typen von Kieselsäure, insbesondere solche, die zusätzlich einer Hydrophobierung unterzogen worden sind.Come as a release agent for the purpose of the invention for example soaps of various types. Soaps should be alkali or alkaline earth soaps are understood to have an alkyl radical of 12 to about 22, in particular 16 to 18 carbon atoms exhibit. Such fatty acids are obtained from natural fats and it is generally not necessary to use pure soaps. For practical reasons, sodium soaps have proven their worth to use. Of course, it is also possible to use potassium soaps, ammonium soaps, calcium soaps, zinc soaps and / or use aluminum soaps. Another tried and tested group of release agents are aluminum silicates of the most varied kinds and the different types of silica, especially those that are in addition have been subjected to a hydrophobic treatment.

Notwendig zur Herstellung der trockenen Beschichtungsmaterialien sind wasserlösliche und/oder wasserdispergierbare Füllstoffe. Zu den wasserlöslichen Füllstoffen ist in erster Linie Harnstoff zu rechnen. Unter den wasserdispergierbaren Füllstoffen, die ebenfalls eine Affinität zur wäßrigen Phase haben sollen, sind in erster Linie die nativen Stärkesorten zu verstehen, also beispielsweise Maisstärke, Kartoffelstärke, Tapiokastärke, Weizenstärke.Water-soluble and / or water-dispersible ones are necessary for the production of the dry coating materials Fillers. Urea is primarily one of the water-soluble fillers. Under the water-dispersible fillers, which are also a Should have affinity to the aqueous phase, the native starch types are to be understood primarily, for example corn starch, potato starch, tapioca starch, wheat starch.

Als weitere Hilfs- und Konservierungsstoffe kommen in Frage Farbpigmente, insbesondere hellfarbige wie Titandioxid und dergleichen, unter Umständen auch Farbstoffe in geringeren Mengen, um die Eigenfärbung der Beschichtung in wünschenswerter Weise zu beeinflussen.Other auxiliaries and preservatives that can be used are color pigments, in particular light-colored ones such as Titanium dioxide and the like, possibly also dyes in smaller quantities, to the inherent color of the To influence coating in a desirable way.

/ 6/ 6

130049/OCUQ130049 / OCUQ

Sd 230 3. 02.80Sd 230 3. 02.80

Patentanmeldung D 6*75 ßT-%- HENKELKGaAPatent application D 6 * 75 ßT -% - HENKELKGaA

ZR-FE/PatenteZR-FE / patents

In den meisten Fällen dürfte es ratsam sein, Konservierungsstoffe wie Natriumsalz des p-Chlor-m-kresol als Natriumfluorid oder dergleichen zu verwenden.In most cases it might be advisable to use preservatives such as sodium salt of p-chloro-m-cresol to be used as sodium fluoride or the like.

Die Herstellung der trockenen Beschiehtungsmaterialien erfolgt in bekannten Mischern, wobei die trockenen Einzelkomponenten miteinander gemischt werden.The dry coating materials are produced in known mixers, with the dry Individual components are mixed together.

Zum Beschichten von Papieren beziehungsweise Tapetenrückseiten wird das trockene, pulverförmige Beschichtungsmaterial mittels eines sehne!laufenden Rührers wasserdispergiert. Bevorzugt stellt man eine 10- bis 30$ige Lösung und/oder Dispersion dabei her. Beispielsweise hat eine 25£ige wäßrige Dispersion beziehungsweise Lösung nach einer Zeit von etwa 3 Stunden Je nach der Zusammensetzung eine Lösungsviskosität von 5 000 bis 30 000 mPas. Diese Ansätze können dann mittels Luftbürste, Sizepresse oder Rakel auf das Trägerpapier, insbesondere die Tapeten aufgetragen werden. Die Menge an aufgetragenem Feststoff soll zwischen etwa 6 bis 30, ■ insbesondere 12 bis 2k g, liegen. In der Praxis hat sich eine Beschichtung bewährt, bei der etwa I1I bis 18 gTo coat papers or the back of wallpaper, the dry, powdery coating material is dispersed in water by means of a tendon-running stirrer. Preference is given to preparing a 10 to 30 solution and / or dispersion. For example, a 25% aqueous dispersion or solution has a solution viscosity of 5,000 to 30,000 mPas after a time of about 3 hours, depending on the composition. These approaches can then be applied to the carrier paper, in particular the wallpaper, by means of an air brush, size press or squeegee. The amount of solid applied should be between about 6 and 30, in particular between 12 and 2 kg . In practice, a coating has proven itself in which about I 1 I to 18 g

ρ
pro m an Peststoff vorliegt. Anschließend werden dann die Papiere beziehungsweise Tapeten in üblicher Weise getrocknet. Das Trocknen erfolgt in bekannter Weise zwischen etwa 100 und 125° C. Sind Tapeten nach dem erfindungsgemäßen Verfahren beschichtet worden, so können sie wie üblich weiter verarbeitet werden.ρ
is present per m of pesticide. The papers or wallpapers are then dried in the usual way. Drying takes place in a known manner between about 100 and 125 ° C. If wallpapers have been coated according to the method according to the invention, they can be processed further as usual.

Nach dem Tauchen in Wasser - etwa 10 bis 30 see - erfolgt innerhalb von etwa 3 bis 8 Minuten starkes Anquellen des Klebstoffanteils. Der Kleister wird während des Tauchens praktisch nicht ausgewaschen oder abgelöst. Das Quellvolumen des Klebstoffes kann über denAfter diving in water - about 10 to 30 seconds - takes place Strong swelling of the adhesive component within about 3 to 8 minutes. The paste will be used during the Diving practically not washed out or peeled off. The swelling volume of the adhesive can be increased by the

/7/ 7

130049/0040130049/0040

30187843018784

T>*-J- HENKELKGaA T> * - J- HENKELKGaA

ZRFE/PatenteZRFE / patents

Patentanmeldung TS TJ Patent application TS TJ

ZR-FE/PatenteZR-FE / patents

sogenannten Abquetschwert ermittelt werden. Er liegt je nach Formulierung und Auftragsmenge zwischen 0,5 und 0,9 g. Die Tapetenbahn muß während des Tapeziervorgangs verschiebbar und durch wiederholtes kurzes Abziehen und Richten korrigierbar sein.so-called squeeze value can be determined. He is lying depending on the formulation and application quantity between 0.5 and 0.9 g. The wallpaper strip must be used during the wallpapering process be shiftable and correctable by repeated short pulling and straightening.

Nach dem Verkleben und Trocknen können die Tapeten wieder trocken abgezogen werden. Als Maß für die Haftung beziehungsweise Abziehbarkeit wird die Abzugskraft ermittelt. Wie sich aus Nachstehendem ergibt, liegt diese bei recht günstigen Werten, nämlich zwischen 200 und 1 000 g pro 10 cm Papierbreite.After gluing and drying, the wallpaper can be peeled off again dry. As a measure of liability or peelability, the pull-off force is determined. As can be seen from the following, lies these at very favorable values, namely between 200 and 1,000 g per 10 cm of paper width.

/8 130049/0040/ 8 130049/0040

Patentanmeldung D 6l75 /8^/0- HENKELKGaAPatent application D 6175/8 ^ / 0- HENKELKGaA

ZR-FE/PatenteZR-FE / patents

BeisDieleBeisDiele

In den nachstehenden Beispielen wurde die für die Anwendung des erfindungsgemäßens Verfahrens wichtigen Kriterien nach folgenden Methoden ermittelt:In the examples below, those that are important for the application of the method according to the invention were identified Criteria determined according to the following methods:

Bestimmung des Abquetschwertes:Determination of the squeeze value:

Streifen von 3 x 20 cm (5 Stück) werden 10 see. in Wasser (12 bis 15° C) untergetaucht. Anhaftendes Wasser auf der nicht beschichteten Seite des Papierstreifens wird mit einem Tuch abgestrichen. Nach 1 Min. Quellzeit wird der Streifen gewogen. Danach wird der Kleister zwischen 2 Walzen (Liniendruck: 60 N/cm) abgequetscht und erneut gewogen. Die Differenz zwischen beiden Wägungen ergibt den Abquetschwert. Je größer der Abquetschwert ist, desto besser 1st die Quellfähigkeit des Kleisters.Strips of 3 x 20 cm (5 pieces) become 10 see. in water (12 to 15 ° C) submerged. Adhering water on the uncoated side of the paper strip will be with wiped off with a cloth. After a swelling time of 1 minute, the strip is weighed. The paste is then applied between 2 Rollers (line pressure: 60 N / cm) squeezed off and weighed again. The difference between the two weighings results the squeeze value. The greater the squeeze-off value, the better the swellability of the paste.

Bestimmung der Abzugskraft:Determination of the pull-off force:

Papierabschnitte von 10 χ 45 cm werden auf Gipskartonplatten nach Untertauchen der Papiere in Wasser (Tauchzeit: 20 see) und Ausquellen (Quellzeit: 5 Min.) vollflächig verklebt. Die beklebten Gipskartonplatten werden nach 48 Std. Trockenzeit bei Zimmertemperatur in ein Abziehgerät eingespannt und der Papierabschnitt unter einem Winkel von 90° C mit einer Geschvrindigkeit von 10 cm/Min, abgezogen. Die Abzugskraft wird mit einem Dynamometer in einem Eereich von 0 bis 1 000 g gemessen und in g/10 cm Breite angegeben.Sections of paper measuring 10 χ 45 cm are placed on plasterboard after submerging the papers in water (immersion time: 20 seconds) and swelling (swelling time: 5 min.) Glued over the entire surface. The pasted plasterboard will be after 48 hours of drying time at room temperature in a Clamped peeler and the paper section at an angle of 90 ° C with a speed of 10 cm / min, peeled off. The pull-off force is measured with a dynamometer in a range from 0 to 1,000 g and given in g / 10 cm width.

Beispiel 1example 1

Ein Beschichtungsmaterial aus folgenden Bestandteilen wird trocken gemischt und dann unter Rühren in Wasser dispergiert:A coating material from the following components is dry mixed and then mixed in water with stirring dispersed:

/9/ 9

1 30049/00401 30049/0040

Patentanmeldung D 6175 V-M- HENKELKGaAPatent application D 6175 VM- HENKELKGaA

ZR-FE/PatenteZR-FE / patents

. 25,0 Gewichtsteile technische Natriumcarboxymethyl-. 25.0 parts by weight of technical sodium carboxymethyl

cellulosecellulose

(Lösungsviskosität: 200 mPas, 5 Brookfield, 20 UpM, 20° C, Aktivgehalt: 68 %) 8,5 Gewichtsteile Hydroxyethylcellulose (Lösungsviskosität: 1IOO mPasj 2 Brookfield, 20 UpM, 20° C, Aktivgehalt: 90 %) 0,5 Gewichtsteile Natriumalginat(Solution viscosity: 200 mPas, 5 Brookfield, 20 rpm, 20 ° C, active content: 68 %) 8.5 parts by weight of hydroxyethyl cellulose (solution viscosity: 1 100 mPasj 2 Brookfield, 20 rpm, 20 ° C, active content: 90 %) 0.5 Parts by weight of sodium alginate

(Lösungsviskosität von 1 300 mPas, 2 ?ig, Brookfield, 20 UpM, 20° C, Aktivgehalt von 85 %) (Solution viscosity of 1,300 mPas, 2? Ig, Brookfield, 20 rpm, 20 ° C, active content of 85 %)

0,3 Gewichtsteile schwach anionenaktives Polyacrylamid (Molgewicht 3 bis 4 Millionen) 30,0 Gewichtsteile gemahlener Harnstoff 27,2 Gewichtsteile native Kartoffelstärke 1,0 Gewichtsteile kolloidale Kieselsäure 2,5 Gewichtsteile Natriumstearatpulver 3,5 Gewichtsteile Natriumseife (^g^g)0.3 parts by weight of weakly anion-active polyacrylamide (molecular weight 3 to 4 million) 30.0 parts by weight of ground urea 27.2 parts by weight of native potato starch 1.0 part by weight of colloidal silica 2.5 parts by weight of sodium stearate powder 3.5 parts by weight sodium soap (^ g ^ g)

(Körnung 90 % < 0,2 mm)(Grain size 90 % <0.2 mm)

0,5 Gewichtsteile Natriumfluorid 1,0 Gewichtsteil Na-SaIz von p-Chlor-m-kresol0.5 part by weight of sodium fluoride 1.0 part by weight of sodium salt of p-chloro-m-cresol

Der Ansatz hat bei einem Feststoffanteil von 25 Gewichtsprozent eine Viskosität von 18 000 mPas (Brookfield, 20 UpM, 20° C). Mit ihm wurde Papier mit einem Blattgewicht von 130 g/m so beschichtet, daß ein AuftragWith a solids content of 25 percent by weight, the batch has a viscosity of 18,000 mPas (Brookfield, 20 rpm, 20 ° C). It was used to coat paper with a sheet weight of 130 g / m 2 so that an order

von 17 g/m Trockensubstanz resultierte. Die Trocknungstemperatur betrug 110° C. of 17 g / m dry matter resulted. The drying temperature was 110 ° C.

Bei'einem so beschichteten Papier wurde durch 20 see.With a paper coated in this way, 20 see.

Tauchen in Wasser der Kleberanteil reaktiviert. Er hatte einen Abquetschwert von 0,76 g. Das Papier ließ sich nach einer Quellzeit von 5 Min. beim Verkleben gut verschieben und in der Klebebahn korrigieren. Als TrägerImmersion in water reactivates the adhesive component. It had a squeeze value of 0.76 g. The paper let go After a swelling time of 5 minutes, move it well when gluing and correct it in the adhesive strip. As a carrier

/10 1 30049/0(HO/ 10 1 30049/0 (HO

Sri 930 3 0? ROSri 930 3 0? RO

30187843018784

Patentanmeldung D 6l75 V^ ~4%~ HENKELKGaAPatent application D 6175 V ^ ~ 4% ~ HENKELKGaA

ZR-FE/PatenteZR-FE / patents

diente eine Gipskartonplatte, Nach dem Auftragen der Papierbahn auf die Gipskartonplatte und dem Antrocknen ergab sich eine gleichmäßige Verklebung. Das Papier ließ sich später trocken von der Kartonplatte abziehen. Die Abzugskraft betrug im Mittel, aus 5 Proben gemessen, 450 g/10 cm Breite.served a plasterboard, after applying the paper web to the plasterboard and drying a uniform bond resulted. The paper could later be peeled dry from the cardboard panel. The average pull-off force, measured from 5 samples, was 450 g / 10 cm width.

Beispiel 2Example 2

Ein Beschichtungsmaterial aus folgenden Bestandteilen wird trocken gemischt und später unter Rühren in Wasser dispergiert:A coating material made up of the following components is dry mixed and then mixed in water with stirring dispersed:

20,0 Gewichtsteile Methylcellulose (Lösungsviskosität: 25 mPas, 2 £ig, Brookfield, 20 UpM, 20° C, Aktivgehalt: 92 %) 8,5 Gewicht steile Hydroxyethylcellulose20.0 parts by weight of methyl cellulose (solution viscosity: 25 mPas, 2 ig, Brookfield, 20 rpm, 20 ° C., active content: 92 %) 8.5 parts by weight of hydroxyethyl cellulose

(Lösungsviskosität: 1IOO mPasj 2 ?ig, · Brookfield, 20 UpM, 20° C, Aktivgehalt: 90 %) 0,5 Gewichtsteile Natriumalginat (Lösungsviskosität: 1 300 mPas, 2 Jfig,(Solution viscosity: 1 100 mPasj 2? Ig, Brookfield, 20 rpm, 20 ° C, active content: 90 %) 0.5 part by weight sodium alginate (solution viscosity: 1 300 mPas, 2 Jfig,

Brookfield, 20 UpM, 20° C, Aktivgehalt: 85 %) 0,3 Gewichtsteile schwach anionisches PolyacrylamidBrookfield, 20 rpm, 20 ° C., active content: 85 %) 0.3 part by weight of weakly anionic polyacrylamide

(Mol-Gew. 3 bis 4 Millionen) 30,0 Gewichtsteile gemahlener Harnstoff 24,7 Gewichtsteile native Mais-Stärke 1,0 Gewichtsteil Aluminiumsilikat 2,5 Gewichtsteile Natriumstearatpulver 3,5 Gewichtsteile Natriumseife (C^g/^ (Korngröße 90 % ^- 0,2 mm) 0,5 Gewichtsteile Natriumfluorid 1,0 Gewichtsteil Na-SaIz von p-Chlor-m-kresol(Molar weight 3 to 4 million) 30.0 parts by weight of ground urea 24.7 parts by weight of native corn starch 1.0 part by weight of aluminum silicate 2.5 parts by weight of sodium stearate powder 3.5 parts by weight of sodium soap (C ^ g / ^ (grain size 90 % ^ - 0.2 mm) 0.5 part by weight of sodium fluoride 1.0 part by weight of sodium salt of p-chloro-m-cresol

/11/ 11

1300A9/00A01300A9 / 00A0

30187^430187 ^ 4

Patentanmeldung D 6l75 I^Λ^> " HENKELKGaAPatent application D 6175 I ^ Λ ^> "HENKELKGaA

' ZR-FE/Patente ' ZR-FE / Patents

Dieser Ansatz hat bei einem Feststoffanteil von 25 % eine Viskosität von 25 000 mPas (Brookfield, 20 UpM, 20° C). Mit ihm wurde Papier mit einem Blattgewicht von 130 g/m2 so beschichtet, daß ein Auftrag von 16,5 g/m2 Trockensubstanz resultiert. Die Trocknungstemperatur lag bei 110° C.With a solids content of 25 %, this approach has a viscosity of 25,000 mPas (Brookfield, 20 rpm, 20 ° C.). It was used to coat paper with a sheet weight of 130 g / m 2 so that an application of 16.5 g / m 2 of dry substance resulted. The drying temperature was 110 ° C.

Bei einem so beschichteten Papier wurde durch 20 see. Tauchen in Wasser der Kleisteranteil reaktiviert. Er hatte einen Abquetschwert von 0,58 g. Das Papier ließ sich nach einer Quellzeit von 5 Min. beim Verkleben gut verschieben und in der Klebebahn korrigieren. Als Träger diente eine Gipskartonplatte. Nach dem Auftragen der Papierbahn auf die Gipskartonplatte und dem Antrocknen ergab sich eine gleichmäßige Klebung. Das Papier ließ sich später trocken von der Kartonplatte abziehen. Die Abzugskraft betrug im Mittel, aus 5 Proben gemessen, 600 g/10 cm Breite.With a paper coated in this way, 20 see. Immersion in water reactivates the paste. It had a squeeze value of 0.58 g. The paper let go After a swelling time of 5 minutes, move it well when gluing and correct it in the adhesive strip. As a carrier served a plasterboard. After applying the paper web to the plasterboard and drying a uniform bond resulted. The paper could later be peeled dry from the cardboard panel. the The average pull-off force, measured from 5 samples, was 600 g / 10 cm width.

Beispiel 3Example 3

Ein BeSchichtungsmaterial aus folgenden Bestandteilen wird trocken gemischt und später unter Rühren in Wasser dispergiert:A coating material made up of the following components is mixed dry and later dispersed in water while stirring:

20,0 Gewichtsteile technische Natriumcarboxymethyl-20.0 parts by weight of technical sodium carboxymethyl

cellulosecellulose

(Lösungsviskosität: 200 mPas, 5 3»ig, Brookfield, 20 UpM, 20° C,(Solution viscosity: 200 mPas, 5 3 ig, Brookfield, 20 rpm, 20 ° C,

Aktivgehalt: 68 %) 8,5 Gewichtsteile Hydroxyethylcellulose (Lösungsviskosität: 1IOO mPas 2 J6ig, Brookfield, 20 UpM, 20° C, Aktivgehalt: 90 %) 0,5 Gewichtsteile Natriumalginat (Aktivgehalt: 85 %) Active content: 68 %) 8.5 parts by weight hydroxyethyl cellulose (solution viscosity: 1 100 mPas 2 J6ig, Brookfield, 20 rpm, 20 ° C, active content: 90 %) 0.5 parts by weight sodium alginate (active content: 85 %)

(Lösungsviskosität: 1 300 mPas >(Solution viscosity: 1,300 mPas>

2 *ig, Brookfield, 20 UpM, 20° C )2 * ig, Brookfield, 20 rpm, 20 ° C)

/12/ 12

130049/0(HO130049/0 (HO

Patentanmeldung DÖ175 ^ -^ - HENKELKGaAPatent application DÖ175 ^ - ^ - HENKELKGaA

ZR-FE/PatenteZR-FE / patents

0,3 Gewichtsteile schwäch anionenaktives Polyacrylamid0.3 part by weight of weakly anion-active polyacrylamide

(Molekulargewicht 3 bis 1 Millionen) 30,0 Gewichtstelle gemahlener Harnstoff 30,0 Gewichtsteile native Kartoffelstärke 1,0 Gewichtsteil kolloidale Kieselsäure 2,5 Gewichtsteile Natriumstearatpulver 5,7 Gewichtsteile 'Natriumseife (Cjfi/l8^(Molecular weight 3 to 1 million) 30.0 parts by weight of ground urea 30.0 parts by weight of native potato starch 1.0 part by weight of colloidal silica 2.5 parts by weight of sodium stearate powder 5.7 parts by weight of sodium soap (C jfi / 18 ^

(Körnung 90 % ^-0,2 mm)(Grain size 90 % ^ -0.2 mm)

1,0 Gewichtsteil Na-SaIz von p-Chlor-m-kresol 0,5 Gewichtsteile NatriumfluorId1.0 part by weight of sodium salt of p-chloro-m-cresol 0.5 part by weight of sodium fluoride

Der Ansatz hat bei einem Peststoffanteil von 25 Gewichtsprozent eine Viskosität von 16 000 mPas (Brookfield, 20 UpM, 20° C). Mit ihm wurde Papier mit einem Blattge-The approach has a pesticide content of 25 percent by weight a viscosity of 16,000 mPas (Brookfield, 20 rpm, 20 ° C.). With him, paper with a sheet of paper was

2
wicht von 130 g/m so beschichtet, daß ein Auftrag von2
weight of 130 g / m coated so that an application of

1^ 18,6 g/m Trockensubstanz resultierte. Die Trocknungstemperatur betrug 110° C. 1 ^ 18.6 g / m dry matter resulted. The drying temperature was 110 ° C.

Durch 20 see. Tauchen in Wasser wurde der Kleberanteil reaktiviert. Er hatte einen Abquetschwert von 0,73 g· Das Papier ließ sich nach einer Quellzeit von 5 Min.By 20 see. Dipping in water became the glue portion reactivated. It had a squeeze value of 0.73 g. After a swelling time of 5 min.

beim Verkleben gut verschieben und in der Klebebahn korrigieren . Als Träger diente eine Gipskartonplatte. Nach dem Auftragen der Papierbahn auf die Gipskartonplatte und dem Antrocknen ergab sich eine gleichmäßige Klebung. Das Papier ließ sich später trocken von der Kartonplatte abziehen,. Die Abzugskraft betrug im Mittel, aus 5 Proben gemessen, 200 g/10 cm Breite.Move it well when gluing and correct it in the adhesive strip. A plasterboard was used as the carrier. After the paper web was applied to the plasterboard and dried, it was uniform Gluing. The paper could later be peeled dry from the cardboard plate. The average pull-off force was measured from 5 samples, 200 g / 10 cm width.

Beispiel M: Example M :

Ein Beschlchtungsmaterial aus folgenden Bestandteilen wird trocken gemischt und später unter Rühren in Wasser dispergiert:A sizing material made up of the following components is mixed dry and later in water with stirring dispersed:

/13 130049/0040 / 13 130049/0040

Sd 230 3. 02.80Sd 230 3. 02.80

Patentanmeldung D 617 5Patent application D 617 5

25,0 Gewichsteile 9,0 Gewichtsteile25.0 parts by weight 9.0 parts by weight

HENKELKGaAHENKELKGaA

ZR-FE/PatenteZR-FE / patents

technische Natriumcarboxymethylcellulose technical sodium carboxymethyl cellulose

(Lösungsviskosität von 200 mPas 5 %ig Brookfield, 20 UpM, 20° C, .Aktivgehalt: 68 %)
Galactomannan
. (Typ Guar Gum mit einer Lösungsviskosität von 1 300 mPas, bei 70° C aufgeschlossen und mit(Solution viscosity of 200 mPas 5 % Brookfield, 20 rpm, 20 ° C, active content: 68 %)
Galactomannan
. (Type guar gum with a solution viscosity of 1,300 mPas, digested at 70 ° C and with

10 einem Brookfield-Viskosimeter in10 a Brookfield viscometer in

3 iiger Lösung, 20 UpM, 20° C gemessen, Aktivgehalt: 90 % 3 iiger solution, 20 rpm, measured 20 ° C, active content: 90 %

0,3 Gewichtsteile schwach anionenaktives Polyacrylamid 0.3 parts by weight of weakly anion-active polyacrylamide

15 (Molekulargewicht von 3 bis Ί15 (molecular weight from 3 to Ί

Millionen)Millions)

gemahlener Harnstoff native Tapiokastärke kolloidale Kieselsäureground urea native tapioca starch colloidal silica

20 5,0 Gewichtsteile Natriumstearatpulver20 5.0 parts by weight of sodium stearate powder

Natriumseife (C^/^) (Körnung 90 % L· 0,2 mm) p-Chlor-m-kresol
NatriumfluoridSodium soap (C ^ / ^) (grain size 90 % L x 0.2 mm) p-chlorine-m-cresol
Sodium fluoride

25 Der Ansatz hat bei einem Peststoffanteil von 25 Gewichtsprozent eine Viskosität von 18 000 mPas (Brookfield, 20 UpM, 20° C). Mit ihm wurde Papier mit einem Blattgewicht von 130 g/m2 so beschichtet, daß ein Auftrag von 17 g/m Trockensubstanz resultierte. Die Trocknungs-25 With a pesticide content of 25 percent by weight, the batch has a viscosity of 18,000 mPas (Brookfield, 20 rpm, 20 ° C.). It was used to coat paper with a sheet weight of 130 g / m 2 in such a way that an application of 17 g / m of dry substance resulted. The drying

30 temperatur betrug 110° C.30 temperature was 110 ° C.

Durch 20 see. Tauchen in Wasser wurde der Kleberanteil reaktiviert. Er hatte einen Abquetschwert von 0,76 g. Das Papier ließ sich nach einer Quellzeit von 5 Min. beim Verkleben gut verschieben und in der Klebebahn 35 korrigieren. Als Träger diente eine Gipskartonplatte.By 20 see. Dipping in water became the glue portion reactivated. It had a squeeze value of 0.76 g. After a swelling time of 5 min. Move it well when gluing and correct it in the adhesive strip 35. A plasterboard was used as the carrier.

30,030.0 GewichtsteileParts by weight 24,724.7 GewichtsteileParts by weight 1,01.0 GewichtsteilPart by weight 5,05.0 GewichtsteileParts by weight 3,53.5 GewichtsteileParts by weight 1,01.0 GewichtsteilPart by weight 0,50.5 GewichtsteileParts by weight

130049/0040130049/0040

Sd 230 3. 02.80Sd 230 3. 02.80

Patentanmeldung DOITS 1^'4Q- HENKELKGaAPatent application DOITS 1 ^ '4Q- HENKELKGaA

ZR-FE/PatenteZR-FE / patents

Nach dem Auftragen der Papierbahn auf die Gipskartonplatte und dem Antrocknen ergab sich eine gleichmäßige Klebung. Das Papier ließ sich später trocken von der Kartonplatte abziehen. Die Abzugskraft betrug im Mittel, aus 5 Proben gemessen, 550 g/10 cm Breite.After the paper web was applied to the plasterboard and dried on, the result was a uniform bond. The paper could later be peeled dry from the cardboard panel. The average pull-off force was measured from 5 samples, 550 g / 10 cm width.

/15 130049/0040 / 15 130049/0040

Claims (3)

3Q187643Q18764 Patentanmeldung D 617 5 ¥? HENKELKGaAPatent application D 617 5 ¥? HENKELKGaA ZR-FE/PatenteZR-FE / patents "Beschichtungsmaterial für zu verklebende Papiere""Coating material for papers to be glued" PatentansprücheClaims Ql) Trockenes Beschichtungsraaterial für zu verklebende Papiere und dergleichen, insbesondere von Tapetenrückseiten, gekennzeichnet,durch eine Kombination '; der folgenden Bestandteile: Ql) dry coating material for papers to be bonded and the like, in particular for the back of wallpaper, characterized by “a combination”; of the following components: a) 100 Gewichtsteile wasserlösliche, klebende Cellulo.seether und/oder Stärkeether beziehungsweise Stärkeabbauprodukte und darauf bezogen b) 1 bis hO Gewichtsteile wenig beziehungsweisea) 100 parts by weight of water-soluble, adhesive Cellulo.seether and / or starch ethers or starch degradation products and based thereon b) 1 to 100 parts by weight or a little nicht klebende hochviskose wäßrige Lösung ergebende Hydrocolloide,
c) 10 bis 50 Gewichtsteile wasserlösliche und/oder wasserdispergierbare Trennmittel sowiehydrocolloids resulting in non-sticky, highly viscous aqueous solution,
c) 10 to 50 parts by weight of water-soluble and / or water-dispersible release agents as well d) 50 bis 300 Gewichtsteile wasserlösliche und/oder wasserdispergierbare Füllstoffe sowie gegebenenfalls
e) weitere Hilfs- und Konservierungsmittel.d) 50 to 300 parts by weight of water-soluble and / or water-dispersible fillers and optionally
e) other auxiliaries and preservatives. 2) Trockenes Beschichtungsmaterial nach Anspruch I3 gekennzeichnet durch eine Kombination aus2) Dry coating material according to claim I 3 characterized by a combination of a) Methyl- beziehungsweise Hydroxyethylcellulose beziehungsweise Methylhydroxyalkylcellulose und/ oder Carboxymethylcellulose unda) methyl or hydroxyethyl cellulose or methyl hydroxyalkyl cellulose and / or carboxymethyl cellulose and b) Polyacrylamid mit einem Molgewicht zwischen 500 und 10 Millionen und/oder Alkalialginat und/oder Galactomannanen sowieb) polyacrylamide with a molecular weight between 500 and 10 million and / or alkali alginate and / or Galactomannans as well c) Alkali- beziehungsweise Erdalkaliseifen und/oder Aluminiumseifen und/oder Aluminiumsilikat und/oder Kieselsäure sowiec) alkali or alkaline earth soaps and / or aluminum soaps and / or aluminum silicate and / or Silica as well d) native Stärke und/oder Harnstoff.d) native starch and / or urea. /16/ 16 -1-3O049/O0A0-1-3O049 / O0A0 ORIGINAL INSPECTEDORIGINAL INSPECTED 30187843018784 Patentanmeldung D 6l?5 *f-2- HENKELKGaAPatent application D 6l ? 5 * f-2- HENKELKGaA ZR-FE/PatenteZR-FE / patents 3) Verfahren zum Beschichten von Tapetenrückseiten, dadurch gekennzeichnet, daß man eine IO bis 30 iige Lösung und/oder Dispersion der trockenen Beschichtungsmaterialien nach Anspruch 1 bis 2 in Wasser in an sich bekannter Weise aufträgt und dann trocknet,3) Method for coating the back of wallpaper, characterized in that one IO to 30 iige Solution and / or dispersion of the dry coating materials according to Claims 1 to 2 in water applies in a known manner and then dries,
DE19803018764 1980-05-16 1980-05-16 Dry paper esp. wall paper adhesive coating - comprises cellulose or starch ether, hydrocolloid, separating agent and filler Withdrawn DE3018764A1 (en)