DE29924702U1 - Thin-bed mortar layer covering vertically cored plane brick is produced by mixing of dry mortar containing mineral binder, lightweight aggregate, and as additive a microbial polysaccharide thickening agent - Google Patents

Thin-bed mortar layer covering vertically cored plane brick is produced by mixing of dry mortar containing mineral binder, lightweight aggregate, and as additive a microbial polysaccharide thickening agent Download PDF

Info

Publication number
DE29924702U1
DE29924702U1 DE1999224702 DE29924702U DE29924702U1 DE 29924702 U1 DE29924702 U1 DE 29924702U1 DE 1999224702 DE1999224702 DE 1999224702 DE 29924702 U DE29924702 U DE 29924702U DE 29924702 U1 DE29924702 U1 DE 29924702U1
Authority
DE
Germany
Prior art keywords
layer according
coating layer
adhesive coating
thin
mortar
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE1999224702
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FRANKEN MAXIT MAUERMOERTEL GMB
Franken Maxit Mauermortel & Co GmbH
Original Assignee
FRANKEN MAXIT MAUERMOERTEL GMB
Franken Maxit Mauermortel & Co GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FRANKEN MAXIT MAUERMOERTEL GMB, Franken Maxit Mauermortel & Co GmbH filed Critical FRANKEN MAXIT MAUERMOERTEL GMB
Priority to DE1999224702 priority Critical patent/DE29924702U1/en
Priority claimed from DE1999116117 external-priority patent/DE19916117B4/en
Publication of DE29924702U1 publication Critical patent/DE29924702U1/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

The thin-bed mortar layer covering vertically cored plane brick (1) is produced by the mixing of dry mortar which containing mineral binder, lightweight aggregate(s), and as an additive microbial polysaccharide thickening agent(s) plus selected minerals from smectite, bentonite, montmorillonite, and natural and/or synthetic fibers. The thin-bed mortar layer covering vertically cored plane brick (1) is produced by the mixing of dry mortar which containing mineral binder, lightweight aggregate(s), and as an additive microbial polysaccharide thickening agent(s) selected from smectite, bentonite, montmorillonite, and natural and/or synthetic fibers. The additive is contained in such amounts that after the preparation of the mixing of the dry mortar with water a film-like self-supporting, gluey consistency of a fresh mortar thin bed application is created in such a way that the fresh mortar (2) does not flow into the holes (3) of the vertically cored brick.

Description

Die Erfindung betrifft eine Hochlochplanziegel deckelnde Dünnbettmörtelauftragsschicht.The The invention relates to a deep hole topcoat lidding thin bed grout application layer.

Auf dem Sachgebiet ist aus der DE 44 43 907 C2 ein Verfahren zur die Hochlöcher von Hochlochplanziegeln abdeckenden (deckelnden) Dünnbettvermörtelung bekannt, das den Stand der Technik überholen soll, indem ein Mörtel mit Leichtzuschlagstoffen verwendet wird, die eine zerbrechliche oder zusammendrückbare räumliche Struktur aufweisen, wobei beim Aufeinandersetzen der Planziegel zunächst ein Teil des Mörtels ausgedrückt und in der verbleibenden Mörtelmenge die räumliche Struktur von den Stegen zwischen den Hohlräumen der Planziegel zerbrochen oder zusammengedrückt wird, hingegen im Bereich der Hohlräume erhalten bleibt. Der verwendete Trockenmörtel kann Portlandzement, Sand, Perlite, Fasern, Celluloseether zur Verbesserung des Wasserrückhaltevermögens, Verdickungsmittel zur Thixotropierung, z.B. Stärkeether, Polyacrylamid, Montmorillonit, und Aluminiumpulver, um das Abrutschen des Mörtels in den Kammern zu erschweren, enthalten. Nachteilig ist, daß die Qualität der Dünnbettschicht vom Zerstörungsgrad der Leichtstoffe abhängig ist, der nicht gleichmäßig sein kann, so daß auch die Festmörteleigenschaften nicht homogen sind.In the subject area is from the DE 44 43 907 C2 discloses a method of covering the high holes of high density roofing (capping) thin bed cementation which is to surpass the state of the art by using a mortar with lightweight aggregates having a fragile or compressible spatial structure, wherein when laying the facing brick first a portion of the mortar is expressed and in the remaining amount of mortar, the spatial structure is broken or compressed by the webs between the cavities of the flat roof, however, is maintained in the region of the cavities. The dry mortar used may include Portland cement, sand, perlite, fibers, cellulose ethers to improve water retention, thixotropic thickeners, eg, starch ethers, polyacrylamide, montmorillonite, and aluminum powder to make it difficult for the mortar to slip in the chambers. The disadvantage is that the quality of the thin-bed layer depends on the degree of destruction of the light materials, which may not be uniform, so that the solid mortar properties are not homogeneous.

Bekannt ist zudem, mit Frischmörtel getränkte textile Flächengebilde, z.B. Vliese zum deckelnden Dünnbettvermörteln von Hochlochplanziegeln zu verwenden. Diese bekannten Verfahren sind materialmäßig teuer und erfordern besondere komplizierte Auftragsvorrichtungen sowie hohes handwerkliches Können.Known is also, with fresh mortar impregnated textile fabrics, e.g. Nonwovens for covering thin bed mortar from To use high perforation plates. These known methods are materially expensive and require special complex application devices as well high craftsmanship.

Aufgabe der Erfindung ist, eine Hochlochplanziegel deckelnde Dünnbettmörtelauftragsschicht zu schaffen, die einen deckelnden Dünnbettauftrag des Frischmörtels mit üblichen Einrichtungen, wie z.B. mit Mörtelschlitteln, ermöglicht, ohne daß der Frischmörtel nennenswert in die Löcher der Hochlochplanziegel fließt.task The invention is a thin hole topcoat lidding thin bed grout application layer to create a top-hating thin-bed order of the fresh mortar with standard Facilities such as e.g. with mortar slippers, allows without that fresh mortar worth mentioning in the holes the high-perforation plate flows.

Diese Aufgabe wird durch die Merkmale des Anspruchs 1 gelöst. Vorteilhafte Weiterbildungen der Erfindung werden in den Unteransprüchen gekennzeichnet.These The object is solved by the features of claim 1. advantageous Further developments of the invention are characterized in the subclaims.

Die erfindungsgemäße Schicht enthält im Minimum ein mineralisches hydraulisches Bindemittel, insbesondere Portlandzement und mindestens einen geblähten Leichtzuschlagstoff sowie eine Zusatzmittelkombination aus mindestens einem Polysaccharid-Verdickungsmittel und mindestens einem aktivierten mineralischen Verdicker.The inventive layer contains at least a mineral hydraulic binder, in particular Portland cement and at least one expanded lightweight aggregate as well an additive combination of at least one polysaccharide thickener and at least one activated mineral thickener.

In überraschender Weise ergibt diese Kombination der Verdickungsmittel nach dem Anmachen bzw. intensivem Verrühren des Trockenmörtels mit Wasser einen Frischmörtel, der mit einer Mörtelkelle oder einem üblichen Mörtelschlitten oder einem anderen üblichen Auftragsmittel als Dünnbett auftragbar ist und eine selbsttragende Konsistenz bis zum ausgehärteten Zustand des Festmörtels aufweist, die verhindert, daß Frischmörtel in die Hochlöcher der Ziegel abfließt. Der Frischmörtel verhält sich genauso wie ein mörtelgetränktes textiles Flächengebilde, z.B. wie ein mörtelgetränktes Vlies, in dem der Frischmörtel in den Poren und Freiräumen des textilen Flächengebildes gespeichert und festgehalten wird, so daß er nicht in die Hochlöcher abfließen kann. Nach der Erfindung ist es gelungen, einen sich selbsttragenden und klebrigen Frischmörtel ohne textiles Flächengebilde zu schaffen, der wie jeder normale Frischmörtel im Dünnbett auftragbar ist.In surprising Manner gives this combination of thickener after mixing or intensive mixing of the dry mortar a fresh mortar with water, the one with a mortar trowel or a usual one mortar carriage or another usual Ordering agent as a thin bed can be applied and a self-supporting consistency until cured of the mortar which prevents fresh mortar in the high holes the brick drains off. The fresh mortar behave just like a mortar soaked textiles Fabrics, e.g. like a mortar-soaked fleece, in which the fresh mortar in the pores and open spaces of the textile fabric stored and held so that he can not drain into the high holes. After the invention succeeded in becoming self-supporting and sticky fresh mortar without textile fabric to create, which is like any normal fresh mortar in the thin bed orderable.

Als aktivierte mineralische Verdicker werden bevorzugt Smektite, Bentonite, Montmorillonite sowie natürliche und synthetische Hectorite verwendet.When activated mineral thickeners are preferred smectites, bentonites, Montmorillonite as well as natural and synthetic hectorites used.

Bevorzugte Polysaccharide sind mikrobielle Biopolymere insbesondere der Gruppe der Xanthane und Succinoglykane.preferred Polysaccharides are microbial biopolymers, especially the group the xanthan and succinoglycans.

Als geblähte Leichtzuschlagstoffe werden vorzugsweise Blähglas, z.B. ein in einer Körnung bis 0,25 mm, und/oder Blähperlit, z.B. in einer Körnung bis 1 mm, und/oder Vermiculit, z.B. in einer Körnung bis 1 mm, verwendet.When distended Lightweight aggregates are preferably expanded glass, e.g. one in a grain until 0.25 mm, and / or expanded perlite, e.g. in a grain to 1 mm, and / or vermiculite, e.g. in a grain size up to 1 mm.

Zweckmäßig ist zudem, fein gemahlene mineralische Zusatzstoffe wie Kalksteinmehl und/oder Flugasche mit Feinheiten von z.B.Is appropriate In addition, finely ground mineral additives such as limestone flour and / or fly ash with subtleties of e.g.

3 000 bis 4 000 Blaine (cm2/g), zuzumischen.3,000 to 4,000 Blaine (cm 2 / g), to mix.

Zudem ist zweckmäßig, wenn der Dünnbettmörtel Kunststoffasern, z.B. Polypropylenfasern mit z.B. Faserlängen von 2,4 bis 6,4 mm und Faserdurchmessern von 0,015 bis 0,025 mm enthält.moreover is appropriate if the thin-bed mortar plastic fibers, e.g. Polypropylene fibers with e.g. Fiber lengths from 2.4 to 6.4 mm and Fiber diameters from 0.015 to 0.025 mm.

Neben den genannten Verdickungsmitteln kann der Mörtel zweckmäßigerweise übliche Zusatzmittel, insbesondere auch ein Wasserrückhaltemittel, z.B. Celluloseether, enthalten.Next the said thickening agents, the mortar expediently conventional additives, in particular also a water retention agent, e.g. Cellulose ethers, included.

Bevorzugte mit Wasser. anzumachende Mischungen sind wie folgt zusammengesetzt:preferred with water. Mixtures to be made are composed as follows:

Figure 00030001
Figure 00030001

Bevorzugt werden Mischungen der folgenden Zusammensetzung:Prefers are mixtures of the following composition:

Figure 00040001
Figure 00040001

Es liegt im Rahmen der Erfindung, aus dem erfindungsgemäßen Mörtel ein Mauerwerk aus Planziegeln und deckelndem Dünnbettmörtel zu erstellen, wobei der Dünnbettmörtel auf die Planziegel in einer Dicke von 1 bis 3 mm aufgegeben wird und die gesamte Oberfläche deckelnd verschließt und somit eine geschlossene, kraftübertragende Verbindung der Planziegel erzeugt. Der erfindungsgemäße Dünnbettmörtel besteht insbesondere aus einer gezielten Abmischung von Blähglas, Blähperliten, Vermiculiten, Portlandzement und Fasern sowie der Verdickungsmittelkombination.It is within the scope of the invention, from the mortar of the invention Masonry of Planziegeln and lidding thin-bed mortar to create, the Thin bed mortar on the plane roof is given in a thickness of 1 to 3 mm and the entire surface closing lid and thus a closed, force-transmitting connection of Planziegel generated. The thin-bed mortar according to the invention consists in particular of a targeted blend of expanded glass, inflatable perlites, vermiculites, Portland cement and fibers and the thickener combination.

Der erfindungsgemäße Frischdünnbettmörtel ermöglicht auch Toleranzen auszugleichen und einen Planziegel nach dem Aufsetzen entsprechend der Maßhaltigkeit noch zu korrigieren. Der Mörtel bleibt nach seinem Auftrag in seiner Struktur erhalten. Er wird vorzugsweise mit einem Mörtelschlitten aufgegeben, wobei die Befüllung des Mörtelschlittens konventionell aus einem Mörtelkübel oder durch Schlauchförderung erfolgen kann. Ein Auftrag mit auf die Steinbreite ausgelegter Mörteldüse mit Schlauchförderung ist ebenfalls ohne weiteres möglich.Of the Fresh-lime mortar according to the invention also allows To compensate for tolerances and a plane seal after touchdown according to the dimensional accuracy still to be corrected. The mortar remains in its structure according to its mission. He will preferably with a mortar carriage abandoned, with the filling of the mortar sled conventionally from a mortar bucket or by hose delivery can be done. An order with a mortar nozzle with hose delivery designed for the stone width is also possible without further ado.

Beim Aufsetzen der Planziegel erfolgt keine Veränderung der Struktur des Mörtels, insbesondere keine Zerstörung der Leichtzuschlagstoffkörner.At the Placing the plain brick takes place no change in the structure of the mortar, in particular no destruction the lightweight aggregate grains.

Die Kornzusammensetzung der geblähten Zuschlagstoffe sollte der folgenden Sieblinie entsprechen: M% <0,91 72– 77 0,09– 0,2 3 – 6 0,2 – 0,63 15– 18 0,63– 1,0 2 – 4 The grain composition of the expanded aggregates should be in accordance with the following grading curve: M% <0.91 72-77 0.09-0.2 3 - 6 0.2 - 0.63 15-18 0.63-1.0 2 - 4

Anstelle eines einzigen mineralischen hydraulischen Bindemittels kann auch ein Bindemittelgemisch oder ein nicht hydraulisches, mineralisches Bindemittel verwendet werden.Instead of a single mineral hydraulic binder can also a binder mixture or a non-hydraulic, mineral Binders are used.

Durch die Leichtzuschlagstoffe ist das Eigengewicht des Frischmörtels gering, was dazu beiträgt, daß in Kombination mit der Verdickerkombination der Frischmörtel selbsttragend folienartig ausgebildet ist. Ein Abfließen des Mörtels in die Hochlöcher erfolgt nicht. Allenfalls ergibt sich ein geringfügiger Durchhang. In jedem Fall werden die Hochlöcher deckelnd abgedeckt.By the lightweight aggregates the weight of the fresh mortar is low, which helps that in Combination with the thickener combination of the fresh mortar self-supporting is formed like a film. A drainage of the mortar in the high holes is done Not. At most, there is a slight sag. In any case become the high holes Covered covered.

Anhand der Zeichnung wird die Erfindung im folgenden beispielhaft näher erläutert. Es zeigen:Based the drawing of the invention is explained in more detail below by way of example. It demonstrate:

1 perspektivisch eine Planziegellage beim Auftragen des erfindungsgemäßen Frischmörtels; 1 in perspective, a plane-bearing layer during application of the fresh mortar according to the invention;

2 schematisch im Querschnitt zwei aufeinander gesetzte Hochlochplanziegel mit Frischmörtelauftrag zwischen den Ziegeln. 2 schematically in cross-section two successive high perforated plates with fresh mortar application between the bricks.

Die Hochlochplanziegel 1 werden ohne Vermörtelung zusammensto ßend nebeneinander gesetzt, wobei die Hochlöcher 3 vertikal ausgerichtet sind. Auf die Oberfläche 4, in die die Hochlöcher münden, wird eine Dünnbettfrischmörtelschicht 2 mit einem Mörtelschlitten 5 aufgetragen.The high-perforation plate seal 1 are placed side by side without grouting together, with the high holes 3 are vertically aligned. On the surface 4 into which the high-holes open, becomes a Dünnbettfrischmörtelschicht 2 with a mortar sled 5 applied.

Auf die Mörtelschicht 2 wird eine weitere Hochlochplanziegellage aufgesetzt (2). Der Frischmörtel 2 verhält sich selbsttragend. Er fließt nicht in die Hochlöcher 3 aus. Die Schichtdicke bleibt erhalten. Es ergibt sich allenfalls ein geringfügiger Durchhang im Bereich der Hochlöcher 3 (nicht dargestellt).On the mortar layer 2 another high-level position is set up ( 2 ). The fresh mortar 2 behaves self-supporting. He does not flow into the high holes 3 out. The layer thickness is retained. At best, there is a slight sag in the area of the high holes 3 (not shown).

Claims (23)

Hochlochplanziegel deckelnde Dünnbettmörtelauftragsschicht, hergestellt durch Anmachen eines Trockenmörtels, der – mindestens ein mineralisches Bindemittel, – mindestens einen Leichtzuschlagstoff – und als Zusatzmittel mindestens ein mikrobielles Polysaccharid-Verdickungsmittel in Kombination mit mindestens einem aktivierten mineralischen Verdicker, ausgewählt aus Smektit,Bentonit, Montmorillonit sowie natürlichen und/oder synthetischen Hectorit, enthält, wobei das Zusatzmittel in solchen Mengen enthalten ist, dass sich nach dem Anmachen des Trockenmörtels mit Wasser eine folienartig selbsttragende klebrige Konsistenz eines Frischmörteldünnbettauftrags derart ergibt, dass der Frischmörtel nicht in die Löcher der Hochlochplanziegel fließt.High-perforation tile covering thin-bed mortar application layer, made by mixing a dry mortar, the - at least a mineral binder, - at least one lightweight aggregate - and as Additive at least one microbial polysaccharide thickener in combination with at least one activated mineral thickener, selected from smectite, bentonite, montmorillonite and natural and / or synthetic hectorite, contains wherein the additive is contained in such amounts that after mixing the dry mortar with water a film-like self-supporting sticky consistency of a Frischmörteldünnbettauftrags such that gives the fresh mortar not in the holes the high-perforation plate flows. Dünnbettmörtelauftragsschicht nach Anspruch 1, dadurch gekennzechnet, dass das Bindemittel Portlandzement ist.Thin bed adhesive coating layer according to claim 1, characterized in that the binder Portland cement is. Dünnbettmörtelauftragsschicht nach Anspruch 1 und/oder 2, dadurch gekennzechnet, dass als mikrobielles Polysaccharid-Verdickungsmittel Xanthan enthalten ist.Thin bed adhesive coating layer according to claim 1 and / or 2, characterized gekennzechnet that as microbial Polysaccharide thickener xanthan gum is included. Dünnbettmörtelauftragsschicht nach Anspruch 1 und/oder 2, dadurch gekennzechnet, dass als mikrobielles Polysaccharid-Verdickungsmittel Succinoglycan enthalten ist.Thin bed adhesive coating layer according to claim 1 and / or 2, characterized gekennzechnet that as microbial Polysaccharide thickener succinoglycan is included. Dünnbettmörtelauftragsschicht nach einem oder mehreren der Ansprüche 1 bis 4, gekennzechnet durch ein Massenverhältnis von organischem Verdickungsmittel zu mineralischem Verdickungsmittel von 0,2 : 2 bis 1 : 5 vorliegt.Thin bed adhesive coating layer according to one or more of claims 1 to 4, gekennzechnet by a mass ratio from organic thickener to mineral thickener from 0.2: 2 to 1: 5. Dünnbettmörtelauftragsschicht nach einem oder mehreren der Ansprüche 1 bis 5, dadurch gekennzechnet, dass als Leichtzuschlagstoff mindestens ein geblähter, mineralischer Leichtzuschlagstoff enthalten ist.Thin bed adhesive coating layer according to one or more of claims 1 to 5, characterized that as light aggregate at least one expanded, lightweight mineral aggregate is included. Dünnbettmörtelauftragsschicht nach Anspruch 6, dadurch gekennzechnet, dass als Leichtzuschlagstoff Blähglas enthalten ist.Thin bed adhesive coating layer according to claim 6, characterized gekennzechnet that contain as lightweight aggregate expanded glass is. Dünnbettmörtelauftragsschicht nach Anspruch 6, dadurch gekennzechnet, dass als Leichtzuschlagstoff Blähperlit enthalten ist.Thin bed adhesive coating layer according to claim 6, characterized in that the lightweight aggregate is expanded perlite is included. Dünnbettmörtelauftragsschicht nach Anspruch 6, dadurch gekennzechnet, dass als Leichtzuschlagstoff geblähter Vermiculit enthalten ist.Thin bed adhesive coating layer according to claim 6, characterized in that as a lightweight aggregate expanded vermiculite is included. Dünnbettmörtelauftragsschicht nach einem oder mehreren der Ansprüche 1 bis 9, dadurch gekennzechnet, dass ein modifizierter Celluloseether als Wasserrückhaltemittel enthalten ist.Thin bed adhesive coating layer according to one or more of claims 1 to 9, characterized that a modified cellulose ether as a water retention agent is included. Dünnbettmörtelauftragsschicht nach einem oder mehreren der Ansprüche 1 bis 10, dadurch gekennzechnet, dass zur Festigkeitssteigerung organische Fasern enthalten sind.Thin bed adhesive coating layer according to one or more of claims 1 to 10, characterized that organic fibers are included to increase the strength. Dünnbettmörtelauftragsschicht nach Anspruch 11, dadurch gekennzechnet, dass Polypropylenfasern mit einer Länge bis zu etwa 5 mm und einer Dicke bis zu etwa 0,03 mm enthalten sind.Thin bed adhesive coating layer according to claim 11, characterized gekennzechnet that polypropylene fibers with a length up to about 5 mm and a thickness of up to about 0.03 mm. Dünnbettmörtelauftragsschicht nach einem oder mehreren der Ansprüche 1 bis 12, dadurch gekennzechnet, dass mindestens ein feingemahlener, mineralischer Zusatzstoff enthalten ist.Thin bed adhesive coating layer according to one or more of claims 1 to 12, characterized that contain at least one finely ground, mineral additive is. Dünnbettmörtelauftragsschicht nach Anspruch 13, dadurch gekennzechnet, dass der Zusatzstoff eine Feinheit von 3000 bis 4000 Blaine aufweist.Thin bed adhesive coating layer according to claim 13, characterized in that the additive is a fineness from 3000 to 4000 blaine. Dünnbettmörtelauftragsschicht nach Anspruch 13 und/oder 14, dadurch gekennzechnet, dass als Zusatzstoff Kalksteinmehl enthalten ist.Thin bed adhesive coating layer according to claim 13 and / or 14, characterized gekennzechnet that as additive Limestone flour is included. Dünnbettmörtelauftragsschicht nach einem oder mehreren der Ansprüche 13 bis 15, dadurch gekennzechnet, dass als Zusatzstoff Flugasche enthalten ist.Thin bed adhesive coating layer according to one or more of claims 13 to 15, characterized that fly ash is included as an additive. Dünnbettmörtelauftragsschicht nach einem oder mehreren der Ansprüche 1 bis 16, dadurch gekennzechnet die folgende Zusammensetzung: Portlandzement 69,43–89,78M% geblähter Zuschlagstoff 10–30M% aktivierter mineralischer Verdicker 0,2–0,5M% Polysaccharid-Verdickungsmittel 0,02–0,1M% feingemahlener Zusatzstoff 0–20M% Wasserrückhaltemittel 0–0,5M% organische Fasern 0–2,5M%.
Thin-bed mortar application layer according to one or more of claims 1 to 16, characterized by the following composition: Portland cement 69,43-89,78M% blown aggregate 10-30m% activated mineral thickener 0,2-0,5M% Polysaccharide thickener 0,02-0,1M% finely ground additive 0-20M% Water retention agents 0-0,5M% organic fibers 0-2,5M%.
Dünnbettmörtelauftragsschicht nach einem oder mehreren der Ansprüche 1 bis 17, gekennzeichnet durch die folgende Zusammensetzung: M% Blähglas Körnung: bis 0,5 mm 10–20 Portlandzement 60–80 Blähperlit Körnung: bis 1 mm 2–5 Vermiculit Körnung: bis 1 mm 1–4 Kalksteinmehl und/oder Flugasche 3000 – 4000 cm2/g 5–20 modifizierter Celluloseether 0,2–0,5 aktivierte mineralische Verdicker 0,2–0,5 Polysaccharid-Verdickungsmittel 0,02–0,1 Polypropylenfasern Länge: 2,4 – 4,6 mm > 1.
Dünnbettmörtelauftragsschicht according to one or more of claims 1 to 17, characterized by the following composition: M% Blähglas Grit: up to 0.5 mm 10-20 Portland cement 60-80 Blähperlit grain size: up to 1 mm 2-5 Vermiculite grain size: up to 1 mm 1-4 Limestone meal and / or fly ash 3000 - 4000 cm 2 / g 5-20 modified cellulose ether 0.2-0.5 activated mineral thickener 0.2-0.5 Polysaccharide thickener 0.02-0.1 Polypropylene fibers Length: 2,4 - 4,6 mm > 1.
Dünnbettmörtelauftragsschicht nach Anspruch 18, gekennzeichnet durch die folgende Zusammensetzung: M% Blähglas Körnung: bis 0,5 mm 12–18 Portlandzement 65–75 Blähperlit Körnung: bis 1 mm 2,5–4 Vermiculit Körnung: bis 1 mm 1,5–3,5 Kalksteinmehl und/oder Flugasche 3000 – 4000 cm2/g 8–18 modifizierter Celluloseether 0,3–0,4 aktivierte mineralische Verdicker 0,3–0,4 Polysaccharid-Verdickungsmittel 0,03–0,06 Polypropylenfasern Länge: 2,4 – 4,6 mm 1,66–2,5.
Thin-bed mortar application layer according to claim 18, characterized by the following composition: M% Blähglas Grit: up to 0.5 mm 12-18 Portland cement 65-75 Blähperlit grain size: up to 1 mm 2,5-4 Vermiculite grain size: up to 1 mm 1.5-3.5 Limestone meal and / or fly ash 3000 - 4000 cm 2 / g 8-18 modified cellulose ether 0.3-0.4 activated mineral thickener 0.3-0.4 Polysaccharide thickener 0.03-0.06 Polypropylene fibers Length: 2,4 - 4,6 mm 1.66 to 2.5.
Dünnbettmörtelauftragsschicht nach Anspruch 18 und/oder 19, dadurch gekennzechnet, dass das Blähglas eine Körnung bis 0,25 mm aufweist.Thin bed adhesive coating layer according to claim 18 and / or 19, characterized gekennzechnet that the expanded glass a granulation to 0.25 mm. Dünnbettmörtelauftragsschicht nach einem oder mehreren der Ansprüche 17 bis 20, dadurch gekennzechnet, dass die Dicke des Frischmörtels 0,5 bis 4 mm beträgt.Dünnbettmörtelauftragsschicht according to one or more of claims 17 to 20, characterized gekennzechnet that the thickness of the fresh mortar 0 . 5 up to 4 mm. Dünnbettmörtelauftragsschicht nach Anspruch 21, dadurch gekennzechnet, dass die Dicke des Frischmörtels 1 bis 3 mm beträgt.Thin bed adhesive coating layer according to claim 21, characterized gekennzechnet that the thickness of the fresh mortar. 1 to 3 mm. Dünnbettmörtelauftragsschicht nach einem oder mehreren der Ansprüche 18 bis 22, dadurch gekennzechnet, dass der Frischmörtel 55 bis 65 Masse-% Wasser aufweist.Dünnbettmörtelauftragsschicht according to one or more of claims 18 to 22, characterized gekennzechnet that the fresh mortar 55 to 65 Has mass% water.
DE1999224702 1999-04-09 1999-04-09 Thin-bed mortar layer covering vertically cored plane brick is produced by mixing of dry mortar containing mineral binder, lightweight aggregate, and as additive a microbial polysaccharide thickening agent Expired - Lifetime DE29924702U1 (en)