DE2637223C2 - Process for the protection of wear pads against static charge as well as lining for spiral chutes - Google Patents

Process for the protection of wear pads against static charge as well as lining for spiral chutes

Info

Publication number
DE2637223C2
DE2637223C2 DE19762637223 DE2637223A DE2637223C2 DE 2637223 C2 DE2637223 C2 DE 2637223C2 DE 19762637223 DE19762637223 DE 19762637223 DE 2637223 A DE2637223 A DE 2637223A DE 2637223 C2 DE2637223 C2 DE 2637223C2
Authority
DE
Germany
Prior art keywords
conductive
resin
epoxy resin
hardener
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DE19762637223
Other languages
German (de)
Other versions
DE2637223A1 (en
Inventor
Des Erfinders Auf Nennung Verzicht
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kalenborn Kalprotect - Dr Mauritz & Co Kg 5 GmbH
Original Assignee
Schmelzbasaltwerk Kalenborn - Dr-Ing Mauritz Kg 5461 Vettelschoss De
Schmelzbasaltwerk Kalenborn Dr Ing Mauritz Kg 5461 Vettelschoss
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Schmelzbasaltwerk Kalenborn - Dr-Ing Mauritz Kg 5461 Vettelschoss De, Schmelzbasaltwerk Kalenborn Dr Ing Mauritz Kg 5461 Vettelschoss filed Critical Schmelzbasaltwerk Kalenborn - Dr-Ing Mauritz Kg 5461 Vettelschoss De
Priority to DE19762637223 priority Critical patent/DE2637223C2/en
Priority to GB2675377A priority patent/GB1584006A/en
Publication of DE2637223A1 publication Critical patent/DE2637223A1/en
Application granted granted Critical
Publication of DE2637223C2 publication Critical patent/DE2637223C2/en
Expired legal-status Critical Current

Description

1515th

2020th

2525th

3030th

3535

4040

4545

5050

DlR Erfindung betrifft ein Verfahren zum Schutz von Schlelßauflagen aus aus einem hochverschleißfesten Edelstahlguß, Grauguß oder dergleichen bestehenden In einem elektrisch Isolierenden Epoxidharz verlegten SchlelßaufladeplaHen.The invention relates to a method for protecting key supports from a highly wear-resistant Cast stainless steel, gray cast iron or the like laid in an electrically insulating epoxy resin KEY CHARGING PLATES.

Beim Verlegen von Schleißauflageplatten für Schüttgüter, wie Kohlen unter Tage, beispielsweise bei Wendel-· rutschen In Kammerbunkern, werden zumindest Im Bereich der horizontalen Flüchen der Rutschen, die eine Schlagbeanspruchung durch herabfallende Kohlen erleiden, bevorzugt Platten aus hochverschleißfestem Edelstahlguß, der warmvergütet und/oder Ölbadgehürtet wurde, sowie Platten aus gewöhnlichem Stahlguß oder Grauguß in Isolierendem Epoxidharzmörtel verwendet.When laying wear plates for bulk goods such as coal underground, for example for helical slide In chamber bunkers, at least in the area of the horizontal curses of the slides, the one Suffering impact from falling coals, preferably plates made of highly wear-resistant cast stainless steel, which has been heat-treated and / or oil-bath hardened, as well as plates made of ordinary cast steel or Gray cast iron used in insulating epoxy resin mortar.

Die Beschichtung wird Im Regelfälle einlagig von unten nach oben aufgebracht. Die Art der Auftragung erfolgt mit einem elastischen Spachtel. Wesentlich ist, daß der Untergrund staub-, fett- und ölfrei ist. Die Beschichtung ist so eingestellt, daß sie selbstverläufend glatt an der Oberfläche wird. Dies ist wesentlich für das Abrutschen im Anfahrzustand einer Neuanlage. Es tritt also weitgehend kein Anbacken der Feinkohle auf.The coating is usually a single layer of applied from the bottom to the top. The type of application is done with an elastic spatula. What is essential is that the surface is free of dust, grease and oil. The coating is adjusted so that it is self-leveling becomes smooth on the surface. This is essential for slipping when a new system is started up. It kicks so largely no caking of the fine coal.

Das Epoxidharz besteht hierbei im Allgemeinen aus einer Mischung aus einem Teil Harz und Härter, zu drei Teilen Quarzsand 0-3. Die Messung des Erdleitwiderstandes dieser Platten, gemessen von der Oberfläche einer Platte zu einem zugänglichen Eisen der Stahlbetonkonstruktion, beispielsweise des Bunkers, zeigt nun bei Messung über mehrere Platten mitunter einen Oberflächenwiderstand von mehr als 1010 Ohm. Der gemessene Erdungswiderstand von 1010 Ohm bedeutet aber offenbar eine Isolierung der Platten, was zur Aufladung der Platten, d. h. zur Bildung einer Art elektrisch^... Kondensators führt. Dabei Ist zumindest die Möglichkeit der Speicherung elektrischer Energie gegeben, die bei einer Entladung einen für Schlagwetter fähigen Funken ergeben kann.The epoxy resin generally consists of a mixture of one part resin and hardener, three parts quartz sand 0-3. The measurement of the ground resistance of these plates, measured from the surface of a plate to an accessible iron of the reinforced concrete structure, for example the bunker, now shows a surface resistance of more than 10 10 ohms when measured over several plates. The measured earth resistance of 10 10 ohms obviously means an insulation of the plates, which leads to the charging of the plates, ie to the formation of a kind of electrical ^ ... capacitor. There is at least the possibility of storing electrical energy, which in the event of a discharge can produce a spark capable of firedamp.

Eine solche Konstruktion kann also für den Bergbau nicht abgenommen werden.Such a construction can therefore not be removed for mining.

Das Problem der hohen elektrostatischen Aufladung kann nun bei einem Verfahren der eingangs genannten Art erfindungsgemäß dadurch beseitigt werden, daß die Schlelßauflageplatlen sowie deren Verfugungen mit Überdecküng zu den leitenden Bauwerkteilen mit einem leitfähigen organischen Harzüberzug versehen werden.The problem of the high electrostatic charge can now be found in a method of the type mentioned at the beginning Art can be eliminated according to the invention in that the Schlelßauflageplatlen and their grouting with Covering the conductive structural parts with a conductive organic resin coating.

Nach einer anderen Ausführungsform der Erfindung ist es möglich, nur die Fugen zwischen den leitfähigen sowie den isolierenden Platten und den leitfähigen Bauwerksteilen mit dem leitfähigen organischen Harzüberzug zu versehen bzw. zu beschichten.According to another embodiment of the invention, it is possible only the joints between the conductive as well as the insulating plates and the conductive structural parts with the conductive organic resin coating to be provided or coated.

Zweckmäßig verwendet man als leitfähigen Überzug ein Gemisch ausA mixture of these is expediently used as the conductive coating

EpoxidharzEpoxy resin

FeinsandFine sand

Feinmehl auf QuarzsandbasisFine flour based on quartz sand

ThixotropiermittelThixotropic agents

Rußsoot

und Epoxidharz-Härterand epoxy resin hardeners

Zweckmäßig verwendet man als Harz einen mit Butylglydlcylether auf die gewünschte Viskosität eingestellten Dlphenylolpropandlglycldylether und als Härter ein Insitu-Addukt eines Amingemisches aus 3-Aminoethyl-3.5.5.-trlmethyl-cyclohexylamln und 2.2.4-trimethylhexamethyldiamln mit einem Dlphen; 'olpropandiglycldylether und einem paratertiären Butylphenylglycidylether.It is expedient to use one with butyl glycol ether as the resin Dlphenylolpropandlglycldylether adjusted to the desired viscosity and an in situ adduct as hardener an amine mixture of 3-aminoethyl-3.5.5.-trmethyl-cyclohexylamine and 2.2.4-trimethylhexamethyldiamine with a diphen; 'ol propane diglycldyl ether and a paratertiary butylphenyl glycidyl ether.

Günstig ist ts, wenn die Komponenten Harz und Härter In einem Mischungsanteil von 100:17 verwendet werden.It is favorable if the components resin and hardener Used in a mixture ratio of 100: 17 will.

Zweckmäßig wird ein Harzantcll verwendet, der sich zusammensetzt aus:It is advisable to use a resin component made up of:

EpoxidharzEpoxy resin

FeinsandFine sand

Feinmehl auf QuarzsandbasisFine flour based on quartz sand

ThixotropiermittelThixotropic agents

LeltmßLeltmß

36,9 GT36.9 GT

25,2 GT25.2 GT

34,9 GT34.9 GT

1,0GT1.0GT

2.ÖGT2.ÖGT

Vorgesehen Ist auch eine Auskleidung für unter Tage verwendete Wendelrutschen oder dergleichen, bestehend aus In Epoxidharzkleber bzw. Zement verlegten Auskleidungsplatten aus Stahlguß. Schmelzbasalt oder Grauguß, gekennzeichnet durch eine leitfähige, die Auskleidung insgesamt überdeckende Beschichtung aus einem Gemisch ausA lining for underground is also planned used spiral chutes or the like, consisting of lining panels laid in epoxy resin adhesive or cement made of cast steel. Cast basalt or gray cast iron, characterized by a conductive lining total covering coating made of a mixture

EpoxidharzEpoxy resin

FeinsandFine sand

Feinmehl auf QuarzsandbasisFine flour based on quartz sand

ThlxytropiermittelThylxytropic agents

Leitruß undCarbon black and

Epoxidharz-HärterEpoxy resin hardener

Es ist auch möglich, Auskleidungspiatten für unter Tage verwendete Wendelrutschen aus Stahlguß, Grauguß, Schmelzbasalt und dergleichen herzustellen, die sich auszeichnen durch eine leitfähige Beschichtung auf der Oberseite der Platten bestehend ausIt is also possible to make lining panels for spiral chutes used underground made of cast steel, gray cast iron, Manufacture cast basalt and the like, which are characterized by a conductive coating the top of the panels consisting of

EpoxidharzEpoxy resin

FeinsandFine sand

Felnmeh! auf QuarzsandbasisFelnmeh! based on quartz sand

ThixotropiermittelThixotropic agents

LeitrußCarbon black

Expoxidharz-HärterEpoxy resin hardener

Durch die Ieit&Hge Beschichtung wird es möglich, Platten der angegebenen Art in Isolierendem Epoxidharz unter Tage ohne Schwierigkeiten zu verlegen.The Ieit & Hge coating makes it possible Boards of the specified type in insulating epoxy resin to be laid underground without difficulty.

Die leitfähige Beschichtung zeitigt ihre Wirkung vor allen Dingen bis zur Inbetriebnahme, um die Oberfläche leitend und gleitfreudig zu machen. Die Aufgabe der leitfähigen und glatten Beschichtung AS wird später durch die darüber gleitende. Insbesondere angefeuchtete Kohle übernommen. Die leitfähige Beschichtung verschließt anschließend.The conductive coating has its effect above all until it is put into operation on the surface to make it guiding and smooth. The task of the conductive and smooth coating AS is carried out later the one sliding over it. In particular, humidified charcoal is taken. The conductive coating seals afterward.

So wird es möglich. Stahlgußplatten oder Bauteile allgemein bei einem O:;rflächenwiderstand im ungünstigsten Falle unter 10* Ohm zu «erlege- Die Bildung von gefährlichen elektrostatischen Ladungen wird sicher verhindert. This is how it becomes possible. Cast steel plates or components in general with a surface resistance in the worst case Fall below 10 ohms to «kill. The formation of dangerous electrostatic charges is reliably prevented.

Die vorgeschlagene leitfähige Beschichtung ist auch deswegen von so großer Bedeutung, da bei Herstellung eines leitfähigen Mörtels dessen Klebkraft und Festigkeil in unzulässiger Weise vermindert würde.The proposed conductive coating is also of great importance because it is manufactured a conductive mortar whose adhesive strength and strength wedge would be reduced in an inadmissible manner.

Die erfindungsgemäße Beschichtung der Oberfläche wird so glatt, daß gleichzeitig ein Anbackeffekt der Kohle weitgehend vermieden wird und Rauhigkeiten der Schleißschichten im Anfahrstadium überbrückt werden.The inventive coating of the surface is so smooth that at the same time a caking effect Carbon is largely avoided and roughness of the wear layers is bridged in the start-up stage.

In praktischen Anwendungen werden nicht nur Stahlplatten sondern auch Flächen aus Zementmörtel, Schmelzbasaltplatten oder dergleichen beschichtet.In practical applications, not only steel plates but also surfaces made of cement mortar, Cast basalt slabs or the like coated.

Wichtig Ist die Aufbringung der leitfähigen Kunststoffbeschlchtung derart, daß stets eine ausreichende Überdeckung (mindestens 200 mm) aus leitenden Bauwerkstellen hergestellt wird.It is important to apply the conductive plastic coating in such a way that there is always a sufficient covering (at least 200 mm) of conductive structural parts will be produced.

Die Schichtstärke wird zwischen 500 und 2000 um gewählt.The layer thickness is between 500 and 2000 um chosen.

Das folgende Beispiel erläutert die Erfindung ohne sie zu begrenzen.The following example illustrates the invention without them to limit.

Die Beschichtung hatte die folgende Zusammensetzung: The coating had the following composition:

15 Komponente Harz: 15 component resin:

Epoxidharz: 36,9 GTEpoxy resin: 36.9 parts by weight

Das Harz Ist ein Diphenylolpropandiglycidylether, der mit einem Butylglycldylether auf die gewünschte Viskosität eingestellt worden ist;The resin is a diphenylol propane diglycidyl ether, the with a butylglycldylether to the desired viscosity has been discontinued;

Feinsand: 25,2 GTFine sand: 25.2 GT

34.9 GT Feinmehl auf Quarzsandbasis
1,0 GT Thixotropiermittel
2,0 GT Leitruß34.9 GT fine flour based on quartz sand
1.0 pbw of thixotropic agent
2.0 GT carbon black

Das reine Harz wies einen Flammpunkt von 90° C auf. Der Flammpunkt des gefüllten Systems ist noch nicht gemessen worden, dürfte aber aufgrund des hohen Füllgrades wesentlich höher sein.The pure resin had a flash point of 90 ° C. The flash point of the filled system is not yet measured, but due to the high degree of filling it should be considerably higher.

Komponente Härter
Epoxidharz-Härten 17,0 GTComponent hardener
Epoxy resin hardness 17.0 GT

Härter - »in-situ-Äddukt« eines Amingemisches (3-AminoäihyU.S.S-trimethyl-cyclohexylamln und 2.2.4-Trimethylhexamethyldiamin) mit einem Diphenylolpropandiglycidylether und einem paratertiären Butyl-phenyiglycidylether. Hardener - "in-situ adduct" of an amine mixture (3-AminoäihyU.S.S-trimethyl-cyclohexylamine and 2.2.4-trimethylhexamethyldiamine) with a diphenylolpropane diglycidyl ether and a paratertiary butyl phenyiglycidyl ether.

Der reine Härter wies einen Flammpunkt von über 10Or C auf.The pure hardener had a flash point of over 10OrC.

Es wurde ein Mischungsverhältnis von Komponente Harz: Komponente Härter = 100 : 17 gewählt.A mixing ratio of resin component: hardener component = 100: 17 was selected.

Topfzeit bei 25tC:
Trockenzeit:Pot life at 25tC:
Dry season:

Verlauf:Course:

Verarbeitbarkeit:
Ableitwiderstand
nach DIN 51953:Processability:
Leakage resistance
according to DIN 51953:

100 g Ansatz = 60 bis 85rC
T 1 = lh 30', T 7 = ca. nach 24 h100 g batch = 60 to 85rC
T 1 = 1h 30 ', T 7 = after approx. 24 h

3,50 - ΙΟ' Ohm3.50 - ΙΟ 'ohms

Die Gebindegrößen sind so aufeinander abgestimmt, daß der Härter stets in das thlxotroplerte leitfähige Harzgemisch gegeben werden muß. Eine Vermischung von Härter allein ist wegen der Geblndegröße und der Nichtaushärtung nicht möglich, eine Fehlmischung ist ausgeschlossen. Nach Vermischung der Komponenten Harz und Härter Im Harzgebinde und Auftragen auf die zu beschichtende Fläche, werden die Gebinde nicht mehr benutzt und die Behälter gesammelt und alsbald nach Übertage befördert.The container sizes are coordinated so that the hardener is always in the thlxotropic conductive resin mixture must be given. Mixing the hardener alone is due to the size of the pack and the lack of hardening not possible, a mix-up is impossible. After mixing the resin components and hardener In the resin container and application to the surface to be coated, the container is no longer used and the containers collected and immediately transported to the surface.

In Sonderfällen Ist es möglich, vorgefertigte Auskleidungen für dem Verschleiß ausgesetzte Fördereinrichtungen unter Tage herzustellen, die bereits mit dem antistatischen Überzug nach der Erfindung versehen ist, wobei bei der Montage dafür gesorgt werden muß, daß beispielsweise über Schrauben oder dergleichen eine sichere Verbindung zu den leitfähigen Bauwerkstellen aus Stahl gewährleistet Ist.In special cases it is possible to use prefabricated linings to produce underground conveyor systems that are exposed to wear and tear that are already equipped with the antistatic Cover is provided according to the invention, it must be ensured during assembly that For example, a secure connection to the conductive building sites via screws or the like steel is guaranteed.

Claims (6)

' Patentansprüche:'Patent claims: 1. Verfahren zum Schutz von Schleißauflagen aus einem hochverschleißfesten Edelstahlguß, Grauguß oder dergleichen bestehenden, in einem elektrisch Isolierenden Epoxidharz verlegten Schleißauflageplatten, dadurch gekennzeichnet, daß die Schleißauflageplatten sowie deren Verfügungen mit Überdeckung zu den leitenden Bauwerksteilen mit einem leitfähigen organischen Harzüberzug versehen werden.1. Process for the protection of wear pads made of a highly wear-resistant cast stainless steel, gray cast iron or similar existing wear plates laid in an electrically insulating epoxy resin, characterized in that the wear plates and their dispositions with overlap be provided with a conductive organic resin coating to the conductive parts of the building. 2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß nur die Fugen zwischen den leitfähigen sowie den isolierenden Platten und den leitfähigen Bauwerkteilen mit dem leitfähigen organischen Harzüberzug versehen bzw. beschichtet werden.2. The method according to claim 1, characterized in that that only the joints between the conductive and the insulating plates and the conductive Structural parts are provided or coated with the conductive organic resin coating. 3. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß als leitfähiger Überzug ein Gemisch aus3. The method according to claim 1, characterized in that a mixture of as a conductive coating EpoxidharzEpoxy resin FeinsandFine sand Feinmehl auf Quarzsandbasis Thixotropiermittel undFine flour based on quartz sand and thixotropic agents Leitruß sowieCarbon black as well Epoxidharz-HärterEpoxy resin hardener verwendet wird.is used. 4. Verfahren nach Anspruch 3, dadurch gekennzeichnet, daß als Harz ein mit Butylglycidylether auf die gewünschte Viskosität eingestellter Diphenylolpropandlglycidylether und als Härter ein in-situ-Addukt eines Amingemisches aus 3-Amlnoethyl-3.5.5-trimethyl-cyclohexylamin und 2.2.4-Trimethylhexamethyldlamin mit einem Diphenylolpropandiglycidylether und einem paratertiären Butylphenylglycldylether verwendet wird.4. The method according to claim 3, characterized in that a resin with butyl glycidyl ether Diphenylolpropandlglycidylether adjusted to the desired viscosity and as a hardener an in-situ adduct of an amine mixture of 3-aminoethyl-3.5.5-trimethyl-cyclohexylamine and 2.2.4-trimethylhexamethyldlamine with a diphenylolpropane diglycidyl ether and a paratertiary butylphenyl glycldyl ether is used. 5. Verfahren nach Anspruch 3 oder 4, dadurch gekennzeichnet, daß die Komponenten Harz und Härter in einem Mischungsanteil von 100 : 17 verwendet werden.5. The method according to claim 3 or 4, characterized in that the components resin and Hardener in a mixture ratio of 100: 17 can be used. 6. Verfahren nach Anspruch 5, dadurch gekennzeichnet, daß ein Harzanteil verwendet wird, der sich zusammensetzt aus:6. The method according to claim 5, characterized in that a resin portion is used which is composed of: EpoxidharzEpoxy resin FeinsandFine sand Feinmehl auf Quarzsandbasis ThixotropiermittelFine flour based on quartz sand, thixotropic agent LeitrußCarbon black 36,9 GT36.9 GT 25,2 GT25.2 GT 34,9 GT34.9 GT 1,0GT1.0GT 2,0 CiT2.0 CiT IOIO
DE19762637223 1976-08-18 1976-08-18 Process for the protection of wear pads against static charge as well as lining for spiral chutes Expired DE2637223C2 (en)