DE2636376A1 - Hot pressing organic and-or inorganic materials into panels - using water glass mixed with fluorspar as the binder - Google Patents
Hot pressing organic and-or inorganic materials into panels - using water glass mixed with fluorspar as the binderInfo
- Publication number
- DE2636376A1 DE2636376A1 DE19762636376 DE2636376A DE2636376A1 DE 2636376 A1 DE2636376 A1 DE 2636376A1 DE 19762636376 DE19762636376 DE 19762636376 DE 2636376 A DE2636376 A DE 2636376A DE 2636376 A1 DE2636376 A1 DE 2636376A1
- Authority
- DE
- Germany
- Prior art keywords
- water glass
- binder
- vermiculite
- fluorspar
- carrier material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
Verfahren zur Herstellung von mineralisch gebundenenProcess for the production of mineral-bound
Platten und anderen Formkörpern Die Erfindung betrifft ein Verfahren zur Herstellung von mineralisch gebundenen Platten und anderen Pormkörpern unter Verwendung eines organischen und/oder anorganischen Trägermaterials, wie Holzspäne, Vermicalit, Perlit, Tonniehl und dgl., wobei das Trägermaterial beleimt, zu Platten gestreut und unter Einwirkung von Wärme verpreßt wird.Sheets and other molded articles The invention relates to a method for the production of mineral-bonded panels and other Pormkkörper under Use of an organic and / or inorganic carrier material, such as wood chips, Vermicalite, perlite, Tonniehl and the like. The carrier material is glued to form sheets is scattered and pressed under the action of heat.
Die Erfindung zeigt gleichzeitig eine auf diese Weise hergestellte Platte bzw. einen anderen Formkörper.The invention also shows one produced in this way Plate or another shaped body.
Es ist bekannt, daß mineralische Bindemittel, wie Gips, Wasserglas und dgl. den besonderen Vorzug der Billigkeit haben.It is known that mineral binders such as plaster of paris, water glass and the like have the special advantage of cheapness.
Als Nachteil tritt dabei auf, daß die FestiCkeitseigens¢ha£-ten in den meisten Fällen nicht ausreichend sind und daher die Platten und Baukörper entweder nur für untergeordnete Zwecke eingesetzt werden können oder aber eine zusätzliche Maßnahme zur Steigerung der Festigkeit auf ausreichende Werte erfordert (DT-PS 847 496).The disadvantage here is that the strength properties have in Most of the time they are insufficient and therefore the panels and structures either Can only be used for subordinate purposes or an additional one Measure required to increase strength to sufficient values (DT-PS 847 496).
Aus der bekanntgemachten Patentanmeldung R 6145 IVb/39b der Klasse 39b, Gruppe 2201 ist ein Verfahren zur Herstellung von Leichtbaukörpern bekannt, bei dem Materialien pflanzlicher Herkunft, wie Faserstoffe, Kork, TorSmull mit mineralischen Stoffen, wie Sand, Ton, Kitt, Asbest usw. vermischt und mit Kunstharz als Bindemittel gebunden werden. Neben dem Kunstharz als Bindemittel wird hierbei ein Bindemittelzusatz, wie Wasserglas, hinzugegeben. Das Wasserglas soll dabei als Imprägniermittel wirken und die Art und Zeitdauer der Abbindung der Platte beeinflussen.From the published patent application R 6145 IVb / 39b of the class 39b, group 2201, a method for producing lightweight structures is known, in the case of materials of vegetable origin, such as fiber, cork, TorSmull with mineral Materials such as sand, clay, putty, asbestos, etc. mixed and with synthetic resin as a binder be bound. In addition to the synthetic resin as a binder, a binder additive is used here, like water glass, added. The water glass should act as an impregnating agent and affect the type and duration of the setting of the plate.
Andererseits ist auch schon vorgeschlagen worden, neben der Verwendung üblicher Kunstharze als Bindemittel Wasserglas bei der Herstellung der Platten zuzasetzen, um die Härte der Einzelplatten zu steigern: Aus der DT-OS 1 653 165 ist ein Verfahren zur Herstellung schwer entflammbarer Holzwerkstoffe bekannt, bei dem die Holzfasern oder -späne mit Alkalisilikatlösungen versetzt werden und zusätzlich Alkalisilicofluoride und/oder Tetrachlorphthalsäure hinzugeführt wird. Dies soll die Flammfestigkeit der auf diese Weise hergestellten Spanplatten verbessern, deren Flammverhalten von Hause aus schlecht ist, weil sie zum überwiegenden Teil aus organischen Substanzen bestehen.On the other hand, it has also already been proposed, in addition to the use conventional synthetic resins as a binder to add water glass in the production of the panels, To increase the hardness of the individual panels: A process is from DT-OS 1 653 165 known for the production of flame-retardant wood-based materials, in which the wood fibers or chips are mixed with alkali silicate solutions and also alkali silicofluorides and / or tetrachlorophthalic acid is added. This is said to be flame resistance improve the chipboard produced in this way, their flame behavior of Home made is bad because it consists predominantly of organic matter exist.
Weiterhin ist es bekannt, Papier und Kartonagen mit Wasserglas zu kleben. Auch in der Wellpappherstellung wird Wasserglas eingesetzt. Wasserglas dient dabei als Hauptbestandteil der in irgendeiner Form modifizierten Klebstoffe. Es ist weiterhin bekannt, daß die Verwendung von Wasserglas als Bindemittel in der Spanplattenherstellung nicht zu brauchbaren Ergebnissen führt, weil insbesondere die erreichbaren Festigkeiten nicht ausreichend sind. Darüber hinaus bietet das Wasserglas auch in verarbeitungstechnischer Hinsicht Schwierigkeiten.It is also known to cover paper and cardboard with water glass glue. Water glass is also used in the manufacture of corrugated cardboard. Water glass is used as the main component of the adhesives modified in any way. It is also known that the use of water glass as a binder in the Chipboard production does not lead to useful results because in particular the achievable strengths are not sufficient. In addition, the Water glass also has difficulties in terms of processing technology.
Der Erfindung liegt die Aufgabe zugrunde, ein Verfahren der eingangs beschriebenen Art aufzuzeigen, mit dem Platten mit organischem und/oder anorganischem Trägermaterial herstellbar sind, die mit einem billigen nicht brennbaren Wasserglasbinder beleimt und gebunden werden können.The invention is based on the object of a method of the above to show the type described, with the plates with organic and / or inorganic Carrier material can be produced with a cheap non-flammable waterglass binder can be glued and bound.
Erfindungsgemäß wird dies dadurch erreicht, daß als Bindemittel eine wässrige Lösung von Wasserglas und Flußspalt Verwendung findet. Durch die Verwendung dieser wässrigen Lösung wird überraschenderweise eine für die praktischen Bedürfnisse ausreichende Verarbeitbarkeit erreicht.According to the invention this is achieved in that as a binder aqueous solution of water glass and river gap is used. By using this aqueous solution surprisingly becomes one for practical needs sufficient workability achieved.
Insbesondere ist die Lagerfähigkeit des beleimten Gutes gegeben, während eine reine Wasserglasbindung ja die sofortige Verarbeitung erfordert, weil die flebeneigung mit der Zeit abnimmt. Weiterhin erniedrigt der Flußspat die Viskosität des Wasserglases in vorteilhafter Weise.In particular, the glued goods can be stored while A pure water glass bond requires immediate processing because the tendency to flatten decreases over time. The fluorspar also lowers the viscosity of the water glass in an advantageous manner.
Das Wasserglas wird vorzugsweise in etwa 50%-iger Lösung eingesetzt, in dieser Lösung werden 5 bis 10% Flußspat gelöst und das so gebildete Bindemittel wirdin einem Anteil von 25 bis 50% bezogen auf das Trägermaterial eingesetzt.The water glass is preferably used in a 50% solution, 5 to 10% fluorspar and the binder formed in this way are dissolved in this solution is used in a proportion of 25 to 50% based on the carrier material.
Mit besonderem Vorteil kann das Trägermaterial aus einem Gemisch von Vermiculit und Calziumcarbonat bestehen, wobei vorzugsweise 30% Vermiculit mit 50% Calziumcarbonat eingesetzt werden. Die Reaktion des Calziumcarbonates ist in zweifacher Weise denkbar. Entweder reagiert es mit dem Wasserglas, so daß Calziumderivate kettenförmiger oder blättchenförmiger Silikate entstehen, was eine starke Erhöhung der Vernetzungswirkung hervorrufen muß. Andererseits kann es auch möglich sein, daß Sauerstoffatome durch Fluor ersetzt werden, so daß Fluorsilikate entstehen, die einen ähnlich verstärkenden Bindungseffekt erzeugen.With particular advantage, the carrier material can consist of a mixture of Vermiculite and calcium carbonate consist, preferably 30% vermiculite with 50% Calcium carbonate can be used. The reaction of calcium carbonate is twofold Way conceivable. Either it reacts with the water glass, making calcium derivatives more chain-like or platelet-shaped silicates are formed, which greatly increases the crosslinking effect must evoke. On the other hand, it can also be possible that oxygen atoms through Fluorine can be replaced, so that fluorosilicates are formed, which have a similarly reinforcing effect Create a binding effect.
Die unter Einsatz eines beleimten Trägermaterials hergestellte mineralisch gebundene Platte kennzeichnet sich dadurch, daß sie mit einer wässrigen Lösung aus Wasserglas und Fluoriden gebunden ist. Insbesondere wird dabei eine Lösung aus 50%-igem Wasserglas eingesetzt, in der 5 bis 10 Flußspat'gelöst sind. Dieses Bindemittel wird in einem Anteil von 25 bis 50% bezogen auf das Trägermaterial eingesetzt. Das Trägermaterial kann ein Gemisch aus Vermiculit und Calziumcarbonat, vorzugsweise 30% Vermiculit und 50 Calziumcarbonat, sein.The mineral produced using a glued carrier material Bound plate is characterized by the fact that it is made with an aqueous solution Water glass and fluorides are bound. In particular, a solution of 50% Water glass used in which 5 to 10 fluorspar 'are dissolved. This binder is used in a proportion of 25 to 50% based on the carrier material. That Carrier material can be a mixture of vermiculite and calcium carbonate, preferably 30% vermiculite and 50% calcium carbonate.
Die Erfindung wird anhand einiger Beispiele erläutert.The invention is illustrated by means of a few examples.
Es wurden dabei jeweils Platten mit einer Fläche von m m2 sowie 7> 89 m2 und 20 mm Stärke angefertigt.In each case, plates with an area of m m2 and 7> 89 m2 and 20 mm thick.
Die in den Beispielen angegebenen Mengen beziehen sich auf die Platten mit der Fläche von 0, 5 m2.The amounts given in the examples relate to the plates with the area of 0.5 m2.
Beispiel 1 : Wasserglas, Flußspat, Vermiculit und Calziumcarbonat.Example 1: water glass, fluorspar, vermiculite and calcium carbonate.
Eine Wasserglaslösung von 50% wird mit Flußspat und Wasser im Verhältnis 15 : 1 : 1 unter Rühren erwärmt. Das so erhaltene Bindemittel läßt sich bei einer Temperatur 0 von 40 bis 50 durch Preßluftdüsen versprühen.A water glass solution of 50% is made with fluorspar and water in the ratio 15: 1: 1 heated with stirring. The binder obtained in this way can be used in a Spray temperature 0 from 40 to 50 through compressed air nozzles.
2400 g geblähter Vermiculit werden in einer Mischtrommel mit 2000 g des oben beschriebenen Bindemittels besprüht. Nach Zugabe von 3800 g Calziumcarbonat werden weitere 1000 g Bindemittel zugegeben. Das geleimte Mischgut kann sofort oder nach einer Lagerung von bis zu 60 Minuten weiter verarbeitet werden. Bei einem Versuch wurden nach 30 Minuten 8800 g in einen auf einem Aluminiumblech liegenden Formrahmen gleiehmäßig eingestreut. Nach Vrpressen des Mischgutes auf einen um etwa 50 höher liegenden Wert als das gewünschte Endmaß, wird der Formrahmen entfernt und ein weiteres Blech aufgelegt. Der vorgefertigte Preßling wird nun in eine auf 170 bis 1800 vorgeheizte Presse geschoben und auf das gewünschte Endmaß zusammengepreßt, das durch seitlich zwischen den Blechen liegende Distanzstahlschienen erreicht werden kann. Nach etwa 5 Minuten ist ein anfangs zu verzeichnender Wasserdampfdruck weitgehend abgebaut. Die Platte wird nach 15 Minuten der Presse entnommen und nach dem Erkalten auf ihre Eigenschaften untersucht.2400 g of expanded vermiculite are mixed in a drum with 2000 sprayed g of the binder described above. After adding 3800 g of calcium carbonate a further 1000 g of binder are added. The glued mix can be immediately or can be processed further after storage for up to 60 minutes. In one attempt After 30 minutes, 8,800 g were placed in a mold frame lying on an aluminum sheet evenly interspersed. After compressing the mix to about 50 higher than the desired final dimension, the mold frame is removed and another sheet is placed. The prefabricated compact is now in a 170 up to 1800 preheated press pushed and pressed together to the desired final dimension, that can be achieved by spacer steel rails lying laterally between the sheets can. After about 5 minutes, an initially recorded water vapor pressure is largely reduced. The plate is removed from the press after 15 minutes and allowed to cool examined for their properties.
Es wurden folgende Durchschnittswerte festgestellt: 2 Querzugsfestigkeit = 8,6 kg/cm2 bei einer Rohdichte von 820 kg/m3 2 Abhebefestigkeit = 8,8 kg/cm2 bei einer Rohdichte von 763/kg/m3 Die Dickenquellung betrug nach 2-stündiger Lagerung unter Wasser bei 200C = 0,7%.The following average values were found: 2 Transverse tensile strength = 8.6 kg / cm2 at a bulk density of 820 kg / m3 2 lift-off strength = 8.8 kg / cm2 at a bulk density of 763 / kg / m3. The thickness swell after 2 hours of storage under water at 200C = 0.7%.
Beispiel 2 wie Beispiel 1, jedoch zusätzlich Glasgewebematten.Example 2 as in Example 1, but with additional glass fabric mats.
Hier handelt es sich um eine Platte mit gleichen Mengenterhältnissen, jedoch wurden zwei Glasgewebematten eingelegt. Nach Einfüllung eines Drittels des Streutgutes in den Formrahmen wurde die erste, nach einem weiteren Drittel die zweite Matte eingelegt. Darauf wurde der Rest gestreut. Nach weiterer Behandlung wie vorher, wurden folgende Meßwerte ermittelt: Querzugsfestigkeit = 6,2 kg bei Rohdichte 802 kg/m3 Abhebefestigkeit = 8,7 kg bei Rohdichte 787 kg/m3 Biegefestigkeit = 41,0 kg bei Rohdichte 846 kgXm3 Beispiel 3 : Kombination wie Platte 1 und 2 In dieser Platte wird das Mengenverhältnis Vermiculit und Calziumcarbonat verändert.This is a plate with the same quantity ratios, however, two glass fabric mats were inserted. After filling in a third of the Scattered material in the mold frame was the first, after a further third the second Mat inserted. The rest was scattered on top. After further treatment as before, the following measured values were determined: Transverse tensile strength = 6.2 kg with a bulk density of 802 kg / m3 lift-off strength = 8.7 kg for a bulk density of 787 kg / m3 flexural strength = 41.0 kg at a bulk density of 846 kgXm3 Example 3: Combination as panel 1 and 2 In The proportion of vermiculite and calcium carbonate is changed on this plate.
2000 g Vermiculit werden zunächst mit etwa 2000 g Bindemittel besprüht. Nach Beimischung von 4200 g Calziumcarbonat wird der Rest Bindemittel zugegeben und nach 45 Minuten der Preßvorgang eingeleitet.2000 g of vermiculite are first sprayed with about 2000 g of binding agent. After adding 4200 g of calcium carbonate, the remainder of the binder is added and after 45 minutes the pressing process is initiated.
2 Diese Platte ergibt eine Querzugsfestigkeit von 11,5 kg/cm2, bei einer Rohdichte von 807 kg/m3. 2 This plate gives a transverse tensile strength of 11.5 kg / cm2, at a bulk density of 807 kg / m3.
Beispiel 4 s Wasserglas, Flußspat, Vermiculit und Tonmehl.Example 4 s water glass, fluorspar, vermiculite and powdered clay.
Diese Kombination erwies sich als weniger gut geeignet, da durch das Tonmehl hervorgerufen, leicht Entmischung eintrat.This combination turned out to be less suitable because the Clay flour caused, slight segregation occurred.
Bei der folgenden Platte wurden ca. 20% des Vermiculits durch Tonmehl ersetzt.In the case of the following plate, approx. 20% of the vermiculite was caused by powdered clay replaced.
5000 g Vermiculit werden mit 2300 g Bindemittel behandelt Nach Zugabe von 1200 g Tonmehl werden weitere 700 g Bindemittel zugesprüht, wonach die Platte sofort gepreßt wird.5000 g of vermiculite are treated with 2300 g of binder. After addition 1200 g of powdered clay are sprayed with a further 700 g of binder, after which the plate is pressed immediately.
2 Die Querzugsfestigkeit liegt mit 3,8 kg/cm2 erheblich unter den vorherigen Werten. 2 At 3.8 kg / cm2, the transverse tensile strength is considerably below the previous values.
Beispiel 5 Wasserglas, Vermiculit und Calziumcarbonat Um eine Verdüsung mit etwa gleicher Geschwindigkeit zu erreichen, wurde die Wasserglaslösung auf 40% eingestellt.Example 5 Water glass, vermiculite and calcium carbonate To create an atomization to achieve at about the same speed, the water glass solution was reduced to 40% set.
2900 g Vermiculit werden mit 2500 g Wasserglas besprüht.2900 g of vermiculite are sprayed with 2500 g of water glass.
Anschließend werden 3300 g Calziumcarbonat eingegeben und weitere 1200 g Wasserglas zugesetzt. Die Preßzeit dieser Platte wird auf 20 Minuten verlängert, um den höheren Wasseranteil zu verdampfen.Then 3300 g calcium carbonate are entered and more 1200 g of water glass added. The pressing time of this plate is extended to 20 minutes, to evaporate the higher proportion of water.
Die Oberfläche der fertigen Platte war leicht spröde, die Festigkeit war niedriger als bei den mit Flußspat behandelten Platten.The surface of the finished board was slightly brittle, the strength was lower than the fluorspar treated panels.
Beispiel 6 Vermiculit und Wasserglas Es wird hier wie in Beispiel 5 verfahren. Die fertige Platte wies eine weichere Oberfläche auf und hatte eine Festigkeit von 7,6 kg/cm2 bei einer Rohdichte von 740 kg/m3.Example 6 Vermiculite and water glass It is here as in example 5 procedure. The finished plate had a softer surface and one Strength of 7.6 kg / cm2 with a bulk density of 740 kg / m3.
Beispiel 7 t Wasserglas, Flußspat und Holzspäne Wasserglas vermag in Verbindung mit Flußspat auch Holzspäne ausreichend zu verkleben.Example 7 t water glass, fluorspar and wood shavings water glass is capable of in combination with fluorspar to glue wood shavings sufficiently.
Es wurden 6000 g Mittellagenholzspäne mit 2700 g des beschriebenen Bindemittels behandelt und unter gleichen Bedingungen wie beschrieben weiter verarbeitet. Die erhal-2 tene Platte hatte eine Querzugsfestigkeit von 6,8 kg/cm2.There were 6000 g middle layer wood chips with 2700 g of the described Treated binder and processed further under the same conditions as described. The plate obtained had a transverse tensile strength of 6.8 kg / cm2.
Beispiel 8 : Wasserglas, Flußspat, Holzspäne und Calziumcarbonat Etwa die Hälfte der Holzspäne läßt sich durch anorganische Mineralien ersetzen, wobei man noch in einem Rohdichtebereich von 850 bis 950 kg/m3 liegt.Example 8: Water glass, fluorspar, wood chips and calcium carbonate Approx half of the wood chips can be replaced by inorganic minerals, whereby one is still in a bulk density range of 850 to 950 kg / m3.
4200 g Holzspäne werden mit 2000-g Bindemittel besprüht.4200 g of wood chips are sprayed with 2000 g of binder.
Nach Zugabe von 4200 g Calziumcarbonat werden weitere 1600 g Bindemittel zugemischt. Eine Einwaage von 9200 g Streutgut ergibt eine Platte mit einer Rohdichte von 870 kg/m3 und einer Festigkeit von 6,o kg/cm2. Die 2 Durchbiegefestigkeit~beträgt 133 kg/cm2.After adding 4200 g of calcium carbonate, a further 1600 g of binder are used mixed in. A weight of 9200 g grit results in a plate with a bulk density of 870 kg / m3 and a strength of 6.0 kg / cm2. The 2 deflection strength is ~ 133 kg / cm2.
Beispiel 9 Wasserglas, Holzspäne und Calziumcarbonat Eine Verklebung von Wasserglas mit Holzspänen ohne Flußspat erwies sich als nicht ausreichend.Example 9 Water glass, wood chips and calcium carbonate A bond of water glass with wood shavings without fluorspar turned out to be insufficient.
2 Es wurde Je eine kleine runde Platte von 50 cm2 hergestellt. 2 A small round plate of 50 cm2 each was produced.
Die erste Platte wurde hergestellt aus Holzspänen mit 22% Wasserglas, atro. Bei der zweiten Platte wurden 50 der Holzspäne durch Calziumcarbonat ersetzt. Beide Platten zeigten eine sprUde und abbröckelnde Oberfläche. Die 2 Festigkeiten lagen unter 3,0 kg/cmThe first plate was made from wood chips with 22% water glass, On the second plate, 50 of the wood chips were replaced by calcium carbonate. Both plates showed a brittle and crumbling surface. The 2 strengths were below 3.0 kg / cm
Claims (8)