DE2614693B1 - - Google Patents

Info

Publication number
DE2614693B1
DE2614693B1 DE19762614693 DE2614693A DE2614693B1 DE 2614693 B1 DE2614693 B1 DE 2614693B1 DE 19762614693 DE19762614693 DE 19762614693 DE 2614693 A DE2614693 A DE 2614693A DE 2614693 B1 DE2614693 B1 DE 2614693B1
Authority
DE
Germany
Prior art keywords
molecular weight
parts
polypropylene
pressure polyethylene
low
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE19762614693
Other languages
German (de)
Inventor
Alexander 3400 Goettingen Betker
Helmut Dipl.-Ing. Dr. 3406 Bovenden Koenig
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Schoeller GmbH and Co KG Deutschland
Original Assignee
Schoeller GmbH and Co KG Deutschland
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Schoeller GmbH and Co KG Deutschland filed Critical Schoeller GmbH and Co KG Deutschland
Priority to DE19762614693 priority Critical patent/DE2614693B1/de
Publication of DE2614693B1 publication Critical patent/DE2614693B1/de
Withdrawn legal-status Critical Current

Description

Die Erfindung betrifft eine Palette aus Kunststoff, wobei der Kunststoff eine hohe Biegefestigkeit und Kälteschlagzähigkeit besitzt.The invention relates to a pallet made of plastic, the plastic having a high flexural strength and Has cold impact strength.

Die Grundabmessungen von genormten Pyleiten sind aus DlN 15 141 ersichtlich, und die Prüfungsrichtlinien ergeben sich aus DIN E 32 600 sowie den Gütcrichtlinien für Kunststoff-Paletten der Gütegemeinschaft Transport- und Lagerbehälter im Qualitätsverband Kunststofl'crzcugnisse e. V.The basic dimensions of standardized pyrelines can be seen from DlN 15 141, and the test guidelines result from DIN E 32 600 and the Quality guidelines for plastic pallets of the quality association for transport and storage containers in the quality association Plastic products e. V.

Hs wurden von der Anmelderin bereits Kunststoffpalette!! entwickelt, welche die Dimensionierungsmöglichkeiten von Konstruktionselementen voll ausschöpfen, d. h. eine weitere Schaffung hoher Trägheitsmomente, /.. B. eine weitere Erhöhung der Rippen im Ober- und Unterteil der Palette ist aus Normungsgründen nicht mehr möglich. The applicant already has plastic pallets !! developed, which fully exploit the dimensioning possibilities of construction elements, d. H. a further creation of high moments of inertia, / .. B. a further increase in the ribs in the upper and lower part of the pallet is no longer possible for reasons of standardization.

Da aber das Erreichen bestimmter Eigenschaften einer Kunststoff-Palette nicht nur eine Frage der Konstruktion ist, sondern insbesondere auch eine Folge konstruktiver Maßnahmen als Funktion von vorgegebenen RohstolVwerten, hat die Anmelderin sich die Aufgabe gestellt, eine Rohstoff-Kombination zu linden, die - mit ausreichenden Fließeigenschaften versehen - bei einer guten Kältekerbschlagzühigkeit ein Maximum an Steifigkeit im verarbeiteten Zustand im Fertigteil vermittelt.Since achieving certain properties of a plastic pallet is not just a question of design is, but in particular also a sequence of constructive measures as a function of predetermined ones Raw material values, the applicant has set itself the task of finding a raw material combination, which - provided with sufficient flow properties - with good cold notch impact strength Provides maximum rigidity in the finished part in the processed state.

Generell kommen als Material für Paletten thermoplastische RohstolTc zur Anwendung, vorzugsweise teilkristalline Thermoplaste. Von besonderem Interesse sind Niederdruck-Polyäthylen und Polypropylen, die schon in großen Mengen für die Herstellung von Paletten Verwendung linden.In general, thermoplastic raw materials are used as the material for pallets, preferably semi-crystalline thermoplastics. Of particular interest are low-pressure polyethylene and polypropylene, which are already used in large quantities for the production of pallets.

Nach der kürzlich abgeänderten DIN-Norm E 32 600 sind die folgenden Tests zu bestehen:According to the recently amended DIN standard E 32 600, the following tests must be passed:

1. Hubversuch 4-Punkt1. 4-point lifting attempt

(Belastung I I, RT, Zeit 30 Minuten, l"/ul. = 2,5%).(Exercise II, RT, time 30 minutes, 1 "/ ul. = 2.5%).

2. Bodenstapelung Deckplatte2. Bottom stacking cover plate

(Belastung 2 t, RT, Zeit 1000h, f zul. - 2,5%).(Load 2 t, RT, time 1000h, f perm. - 2.5%).

3. Bodenstapelung Bodenplatte3. Bottom stacking base plate

(Belastung 1,5 t, RT, Zeit 1000 h, I" zul. = 2,5%).(Load 1.5 t, RT, time 1000 h, I "perm. = 2.5%).

4. Regalstapclung4. Shelf stacking

(Flächen-Belastung 1 t, 40 C, Zeit K)OOh,
I" zul. - 2,5%).(Surface load 1 t, 40 C, time K) OOh,
I "perm. - 2.5%).

5. Druckversuch5. Attempt to print

(Belastung 5 t, RT, Zeit H)OO h, keine
Deformationen und Risse).(Load 5 t, RT, time H) OO h, none
Deformations and cracks).

6. Fallversuch6. Drop test

(5 x Fall auf jede Ecke aus 1 m Höhe, -15 C,
Stauchung 3,5%).(5 x falls on each corner from a height of 1 m, -15 C,
Compression 3.5%).

Zum Test 4 ist anzufügen, daß die Norm DIN E 32 600 zusätzlich dahingehend abgeändert wurde, daß die Regalstapelung nunmehr mit I t Flächenlast bei 40' C bestanden werden muß. Für die Durchführung vonIt should be added to test 4 that the DIN E 32 600 standard has also been modified so that the Rack stacking must now be passed with I t area load at 40 ° C. For the implementation of

Test6 (Fallversuch) ist jetzt anstelle von Zimmertemperatur eine Temperatur von -15'C erforderlich.Test6 (drop test) is now instead of room temperature a temperature of -15'C required.

An und für sich hat sich hochmolekulares Niederdruck-Polyäthylen, zum Beispiel vom Molekulargewicht 68 000 und einem MFl-Wert 190/5 von 6 als nützlich erwiesen, und die daraus gefertigte Palette entspricht den maßlichen Vorschriften. Hinsichtlich der Norm DIN F. 32 600 wird dem FaIItCSt(Y1) sowohl bei Raumtemperatur als auch bei -15 C entsprochen. Nicht erfüllt wird aber der Bodcnslapelupgstest Deckplatte (2) sowie der Bodenstapelungstest Bodenplatte (3).In and of itself, high molecular weight low-pressure polyethylene, for example with a molecular weight of 68,000 and an MFI value of 190/5 of 6, has proven to be useful, and the pallet made from it complies with the dimensional regulations. With regard to the DIN F. 32 600 standard, the FallCSt (Y 1 ) is complied with both at room temperature and at -15 C. However, the floor slap test for the cover plate (2) and the floor stacking test for the floor plate (3) are not fulfilled.

Stellt man andererseits Palellen aus Polypropylen, zum Beispiel mit einem Molekulargewicht von 340 000 und einem MFl-Werl 190/5 von 4,5 her, so entspricht auch diese Palette den mußlichen Vorschriften. Hinsichtlich der Norm DIN E 32 600 wird der Falllest weder bei Raumtemperatur noch bei -15 C erfüllt.On the other hand, if one makes pallets made of polypropylene, for example with a molecular weight of 340,000 and a MFI-Werl 190/5 of 4.5, then corresponds This range also complies with the mandatory regulations. With regard to the DIN E 32 600 standard, the drop test neither at room temperature nor at -15 C.

Es wurden auch schon bestimmte Abmischungen von Niederdruck-Polyäthylen und Polypropylen für Paletten vorgeschlagen (Patentanmeldung P 25 49 538.9). Die Paletten erfüllen last alle Forderungen nach Norm DIN E 32 600 mit den Testen 1 -6, d. h., der Falltest (6) wird wohl bei Zimmertemperatur erfüllt, nicht aber bei der neuen Forderung von -15 C.There have also been certain blends of low-pressure polyethylene and polypropylene for Pallets proposed (patent application P 25 49 538.9). The pallets meet all the requirements of the standard DIN E 32 600 with tests 1 -6, i.e. That is, the drop test (6) is fulfilled at room temperature, but not with the new demand of -15 C.

Es wurde nun überraschend gefunden, daß Paletten aus ganz bestimmten Abmischungen aus Niederdruck-Polyäthylen und Polypropylen nicht nur die Nachteile der einzelnen Komponenten nicht zeigen, sondern daß sie eine ausgezeichnete Kerbschlagfestigkeit und damit Kältel'allfestigkeit und gleichzeitig eine verbesserte Biegefestigkeit besitzen.It has now surprisingly been found that pallets made of very specific mixtures of low-pressure polyethylene and polypropylene not only do not show the disadvantages of the individual components, but that they have an excellent notched impact strength and thus cold resistance and at the same time an improved one Have flexural strength.

Gegenstand der Erfindung ist eine Kunststoffpalette, bestehend aus 70-90 Gewichtsteilen Niederdruck-Polyäthylen mit einem Molekulargewicht von 90 000 -100 000 und einem MFI-Wcrt von 190/5 von 0,5-3 sowie 10-30 Gewichtsleilen Polypropylen mit einem Molekulargewicht von 400 000-600 000 und einem MFl-Wert 190/5 von 0,5-3.The invention relates to a plastic pallet consisting of 70-90 parts by weight of low-pressure polyethylene with a molecular weight of 90,000-100,000 and an MFI Wcrt of 190/5 of 0.5-3 as well as 10-30 parts by weight of polypropylene having a molecular weight of 400,000-600,000 and one MFI value 190/5 of 0.5-3.

Paletten gemäß der Erfindung erfüllen alle Teste 1 -6 nach Norm DIN E 32 600, insbesondere den Kältefalltest auch bei -15'C.Pallets according to the invention meet all tests 1-6 according to DIN E 32 600, in particular the cold drop test even at -15'C.

Aus der nachstehenden Tabelle sind die Versuchsergebnisse gemäß der abgeänderten Norm DIN E 32 600, gemessen an Paletten aus Niederdruck-Polyäthylen, Polypropylen und erfindungsgemäßer Materialmischung zu entnehmen.The following table shows the test results according to the modified standard DIN E 32 600, measured on pallets made of low-pressure polyethylene, polypropylene and material mixture according to the invention refer to.

Prüfungtest NiederLow Poly- UrllnüungPoly-Urllnüung druck-pressure- propylenpropylene Pol y-Pole y- iilhyleniilhylen Hubversuch 4 PunktLift attempt 4 point ++ H- +H- + BodenstapelungBottom stacking -- ■1- +■ 1- + DeckplatteCover plate BodenstapünngBodenstapünng -- H- +H- + BodenplatteBase plate RegalstapelungShelf stacking -t--t- + ++ + (Flächenlast)(Area load) DruckversuchAttempt to print 1-1- + ++ + FallversuchDrop test ++ ++ ι ' Bestanden.ι ' Passed. - ■-■ Nicht bestanden.- ■ - ■ Failed.

Die Palette gemäß der Erfindung zeigt eine gute Kältcfestigkcit, Zähigkeit und Steifigkeit. Für die Steifigkeit sind die Bodenstapelungsteste die wesentliche Aussage.The pallet according to the invention exhibits good cold strength, toughness and rigidity. The bottom stacking tests are the most important information for the rigidity.

Das im Vergleichsversuch verwendete Niederdruck-Polyäthylen hat ein Molekulargewicht von 68 000 und einen MFI-Wert von 190/5 von 6, das im Vergleichsvcrsuch verwendete Polypropylen hat ein Molekulargewicht von 340 000 und einen MFI-Wcrt von 190/5 von 4,5.The low-pressure polyethylene used in the comparative experiment has a molecular weight of 68,000 and an MFI value of 190/5 out of 6, which is the same as in the comparison test The polypropylene used has a molecular weight of 340,000 and an MFI Wcrt of 190/5 from 4.5.

Die zu vergleichende Palette gemäß der Erfindung besteht aus 75 Gewichtsteilen Niederdruck-Polyäthylen mit einem Molekulargewicht von ca. 95 000 und einem MFI-Wert 190/5 von 1,8-2,2 sowie 25 Gewichtstcilcn Polypropylen miteinem Molekulargewicht von ca. 480 000 und einem MFI-Wert 190/5 von 3,0.The comparative pallet according to the invention consists of 75 parts by weight of low pressure polyethylene having a molecular weight of about 95 000 and an MFI 190/5 of 1.8-2.2 and 25 Gewichtstcilcn polypropylene having a molecular weight of about 480 000 and an MFI value 190/5 of 3.0.

Bezüglich der Zähigkeit ist der Fallversuch die wesentliche Aussage, bezüglich der Steifigkeit sind die Stapelungsteste die wesentliche Aussage.With regard to toughness, the drop test is the most important statement, with regard to stiffness they are Stacking tests the essential statement.

Die erfindungsgemäßc Kunststoffpalette enthält im Vorzugsbereich 85-75 Gewichtsteile des Niederdruck-Polyäthylens und 15-25 Gewichtsteile Polypropylen.The plastic pallet according to the invention contains 85-75 parts by weight of the low-pressure polyethylene in the preferred range and 15-25 parts by weight of polypropylene.

Es wurden noch weitere Paletten im Rahmen der Erfindung hergestellt, die alle die Tcstveirsuchc gemäß DIN-Norm E 32 600 bestanden.Still other pallets were manufactured within the scope of the invention, all of which conform to the specifications DIN standard E 32 600 passed.

Es handelte sich dabei um folgende Abmischungen:These were the following mixes:

1. 90 Teile Niederdruck-Polyäthylen mit
Molgewicht 96 000
10 Teile Polypropylen mit Molgewicht 57OOÜO1. 90 parts of low pressure polyethylene with
Molecular weight 96,000
10 parts of polypropylene with a molecular weight of 57OOÜO

Biegung:Bend:

Kerbschlagwerl bei +18 C:
Kerbschlagwert bei -20 C:
MFI-Wert 190/5:Notched hammer at +18 C:
Notched impact value at -20 C:
MFI value 190/5:

19,5 kp 13,7 13,4 2,119.5 kp 13.7 13.4 2.1

2. 80 Teile Niederdruck-Polyäthylen
mit Molgewicht 96 000
20 Teile Polypropylen mit Molgewicht 4072. 80 parts of low pressure polyethylene
with a molecular weight of 96,000
20 parts of polypropylene with a molecular weight of 407

Biegung:Bend:

Kerbschlag bei +18 C:
Kerbschlag bei -20 C:
MFI-Wert 1'.K)/5.Notched impact at +18 C:
Notched impact at -20 C:
MFI value 1'.K) / 5.

20
9,120th
9.1

6,7 2,26.7 2.2

3. 80 Teile Niederdruck-Polyäthylen
mit Molgewicht 960003. 80 parts of low pressure polyethylene
with molecular weight 96000

20 Teile Polypropylen mit Molgewicht 57000020 parts of polypropylene with a molecular weight of 570000

Biegung: 20Bend: 20

Kerbschlag bei +18 C: 12,1Notch impact at +18 C: 12.1

Kerbschlag bei -20 C: 8,3Notched impact at -20 C: 8.3

MFl-Werl 190/5: 2,1MFl-Werl 190/5: 2.1

4. 70 Teile Niederdruck-Polyäthylen
mit Molgewicht 96 0004. 70 parts of low pressure polyethylene
with a molecular weight of 96,000

30 Teile Polypropylen mit Molgewicht 40730 parts of polypropylene with a molecular weight of 407

Biegung: 26Bend: 26

Kerbschhiig bei +18 C: 11,3Notched at +18 C: 11.3

Kerbschlug bei -20 C: 6,7Notched impact at -20 C: 6.7

MFI-Wcrl 190/5: 2MFI-Wcrl 190/5: 2

Claims (1)

PaU iUunspruch:PaU iUunspruch: Kunststoffplatte, bestehend aus 70-90 Gewichtsteilen Niederdruck-Polyäthylen mit einem Molekulargewicht von 90 000- 100 000 und einem MFI-Wert 190/5 von 0,5-3 sowie 10-30 Gewichtsteilen Polypropylen mit einem Molekulargewicht von 400 000-600 000 und einem MFI-Wcrt 190/5 von 0,5-3.Plastic plate, consisting of 70-90 parts by weight of low-pressure polyethylene with a molecular weight from 90,000-100,000 and an MFI value 190/5 of 0.5-3 and 10-30 parts by weight Polypropylene with a molecular weight of 400,000-600,000 and an MFI Wcrt 190/5 of 0.5-3.
DE19762614693 1976-04-06 1976-04-06 Withdrawn DE2614693B1 (en)