DE2535593A1 - PROCESS FOR THE PRODUCTION OF A AREA WITH A DEGREE OF STiffening OVER THE AREA - Google Patents
PROCESS FOR THE PRODUCTION OF A AREA WITH A DEGREE OF STiffening OVER THE AREAInfo
- Publication number
- DE2535593A1 DE2535593A1 DE19752535593 DE2535593A DE2535593A1 DE 2535593 A1 DE2535593 A1 DE 2535593A1 DE 19752535593 DE19752535593 DE 19752535593 DE 2535593 A DE2535593 A DE 2535593A DE 2535593 A1 DE2535593 A1 DE 2535593A1
- Authority
- DE
- Germany
- Prior art keywords
- stiffening
- fabric
- production
- crosslinking
- areas
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Description
PATENTANWÄLTE
HENKEL - KERN - FEILER - HÄNZFT, · 2535593PATENT LAWYERS
HENKEL - KERN - FEILER - HÄNZFT, 2535593
8 München 90 ■ Eduard-Schmid-Str. 28 Munich 90 ■ Eduard-Schmid-Str. 2
Stotz & Co. AG, Zürich (Schweiz) Stotz & Co. AG , Zurich (Switzerland)
L 8. Aus. 1975L 8. Off. 1975
Verfahren zur Herstellung eines Flächengebildes mit über die Fläche unterschiedlichem VersteifungsgradProcess for the production of a flat structure with a degree of stiffening that varies over the surface
Die Erfindung betrifft ein Verfahren zur Herstellung eines Flächengebildes mit über die Fläche unterschiedlichem Versteifungsgrad, die Anwendung des Verfahrens zur Herstellung von Versteifungseinlagen für Kleidungsstückteile sowie eine Vorrichtung zur Durchführung des Verfahrens.The invention relates to a method for producing a sheet-like structure with a degree of stiffening that varies over the surface, the application of the method for the production of stiffening inserts for garment parts and a device for carrying out the method.
Es hat bisher nicht an Versuchen gefehlt, Flächengebilden über ihre Fläche unterschiedlichen Versteifungsgrad zu verleihen. Solche Flächengebilde sind insbesondere als Versteifungseinlage für Kleidungsstück.teile von Bedeutung.There has so far been no lack of attempts to impart different degrees of stiffening to flat structures over their surface. Such flat structures are particularly important as a stiffening insert for pieces of clothing.
Aus der CH-PS 208 304 ist ein Verfahren zum Versteifen von Gegenständen aus schmiegsamen Geweben bekannt, bei dem auf die halbfertigen bzw. fertigen Gegenstände ein flüssiges, farbloses, nach dem Verdunsten des Lösungsmittels keine Klebewirkung auf benachbarte Gewebelagen ausübendes Versteifungsmittel aufgetragen wird, wobei das Auftragen derart vorgenommen wird, dass eine abgestufte bzw. unterschiedliche, dem Gebrauch angepasste Steifheit oder Schmiegsamkeit erzielt wird. Die unterschiedlicheFrom CH-PS 208 304 is a method for stiffening Objects made of pliable fabrics known, in which on the semi-finished or finished objects a liquid, colorless, After the solvent has evaporated, no stiffening agent is applied to adjacent fabric layers is, the application being carried out in such a way that a graduated or different, adapted to the use Rigidity or flexibility is achieved. The different
609809/0392609809/0392
Versteifung.wird durch Abdecken einzelner Bereiche beim Aufbringen des Versteifungsmittels, durch verschiedene Konzentration der aufzubringenden Lösung oder durch Variationen an der Aufsprühvorrichtung erzielt.Stiffening. Is made by covering individual areas when applying of the stiffening agent, through different concentrations of the solution to be applied or through variations on the spraying device achieved.
Vernetzbare Harze werden seit langem vor allem zum Knitterfreiausrüsten von cellulosehaltigen Textilien verwendet. Dabei galt es, die in manchen Fällen durch die Ausrüstung verursachte unerwünschte Versteifung des Textilmaterials zu vermeiden.Crosslinkable resins have long been used primarily for anti-crease finishing used by cellulosic textiles. The aim was to address the undesirable effects caused in some cases by the equipment To avoid stiffening of the textile material.
Aus der DT-OS 2 116 631 ist es bekannt, vernetzbare Harze zur Versteifung von Textilgebilden einzusetzen. Dabei wird das Flächengebilde ganzflächig mit dem vernetzbaren Harz versehen. Die Vernetzung an den zu versteifenden Stellen erfolgt durch stellenweise abgestufte Wärmebehandlung. Dieses Verfahren weist verschiedene grundlegende Nachteile auf. So findet schon während der Lagerung des ausgerüsteten Materials eine teilweise Vernetzung statt. Um eine weitere unbeabsichtigte Vernetzung der unvernetzten Stellen zu vermeiden, muss das Textilmaterial nach der Wärmebehandlung gewaschen werden. Entsprechend kann das Aufbringen einer thermoplastischen für eine eventuelle Verklebung erforderlichen Schicht,und somit auch das Verkleben, erst nach der Wäsche erfolgen, da sonst durch die Wärmebehandlung eine unerwünschte Vernetzung bzw. Versteifung entstehen würde.It is known from DT-OS 2 116 631, crosslinkable resins to be used for stiffening textile structures. The surface structure is provided with the crosslinkable resin over its entire surface. The cross-linking at the points to be stiffened is carried out by means of graded heat treatment in places. This procedure has various basic disadvantages. So even during the storage of the finished material there is a partial Networking takes place. In order to avoid further unintentional crosslinking of the uncrosslinked areas, the textile material must after washed after heat treatment. Correspondingly, the application of a thermoplastic can be used for possible gluing required layer, and thus also the gluing, only after the laundry, as otherwise the heat treatment would result in undesired crosslinking or stiffening.
609809/0392 . '609809/0392. '
Ausserdem ist es apparativ schwierig und aufwendig, die Wärmeeinwirkung nur auf die gewünschten Stellen und im erwünschten Masse einzuschränken.In addition, it is difficult and expensive in terms of apparatus to apply heat only to the desired places and to the desired extent.
Aufgabe der Erfindung ist es, ein Verfahren zur Herstellung von Flächengebilden, insbesondere Versteifungseinlagen für Kleidungsstückteile, zu schaffen, welches die obengenannten Nachteile der bekannten Verfahren hinsichtlich Herstellung und apparativem Aufwand nicht aufweist.The object of the invention is to provide a method for the production of flat structures, in particular stiffening inserts for garment parts, to create, which the above-mentioned disadvantages of the known methods in terms of production and apparatus Does not show any effort.
Gegenstand der Erfindung ist nun ein Verfahren zur Herstellung eines Flächengebildes mit über die Fläche unterschiedlichem Versteifungsgrad, das dadurch gekennzeichnet ist, dass man auf die zuThe subject of the invention is a method for the production of a flat structure with a different degree of stiffening over the surface, which is characterized by the fact that one is approaching
versteifenden Stellen des Flächengebildes eine Zubereitung, die wenigstens eine vernetzbare Substanz enthält, mittels eines Druckverfahrens aufbringt und einer die Vernetzung bewirkenden Behandlung unterwirft.stiffening points of the planar structure a preparation which contains at least one crosslinkable substance, by means of a Applying printing process and subjecting it to a treatment causing the crosslinking.
Das neue Verfahren eignet sich insbesondere zur Herstellung von Versteifungseinlagen für Kleidungsstückteile wie Kragen, Manschetten, Taschenpatten, Fronten und anderen Besatzteilen von Oberbekleidung, z.B. von Blusen, Hemden, Mänteln, Sakkos und Kostümen. Im Falle von schweren Oberstoffen kann die Verwendung einer Versteifungseinlage entfallen, indem die vernetzend wirkende Substanz direkt auf den Oberstoff aufgetragen und vernetzt wird.The new process is particularly suitable for the production of stiffening inserts for garment parts such as collars, cuffs, Pocket flaps, fronts and other trimmings of outerwear, e.g. blouses, shirts, coats, jackets and costumes. In the case of heavy outer fabrics, the use of a stiffening insert can be dispensed with by adding the crosslinking insert The substance is applied directly to the outer fabric and cross-linked.
609809/0392609809/0392
Als Flächengebilde können alle zweidimensional ausgebildeten Materialien wie Textilien (Vliese, Gewebe, Gewirke), Leder, Kunstleder oder Folien verwendet werden. Die Textilien können aus reiner Cellulose, Eiweiss-, Polyolefin-, Polyester-, Polyacryl-, Polyurethan- oder Glasfasern oder deren Gemischen bestehen. All two-dimensional materials such as textiles (fleeces, woven fabrics, knitted fabrics), leather, Synthetic leather or foils can be used. The textiles can be made of pure cellulose, protein, polyolefin, polyester, polyacrylic, Polyurethane or glass fibers or their mixtures exist.
Die Flächengebilde können vor dem Durchführen des erfindungsgemässen Verfahrens allen bekannten Ausrüstungs- oder Veredlungsoperationen unterworfen werden. So können textile Flächengebilde gefärbt oder knitterfrei ausgerüstet sein. Insbesondere werden dimensionsstabil ausgerüstete Flächengebilde, d.h. solche, die gegenüber thermischen, mechanischen und anderweitigen Beanspruchungen, sowie auch gegenüber den Beanspruchungen, welchen das Flächengebilde bei Wasch- und Reinigungsprozessen der verschiedensten Arten ausgesetzt sind, stabil sind, bevorzugt.The planar structures can before the implementation of the invention Procedure for all known finishing or finishing operations be subjected. Textile fabrics can be colored or made crease-free. In particular are dimensionally stable surfaces, i.e. those that are resistant to thermal, mechanical and other Stresses, as well as the stresses that the fabric is exposed to during washing and cleaning processes are exposed to a wide variety of species, are stable, preferred.
Die Dimensionsstabilisierung kann nach bekannten Methoden erfolgen. Solche Methoden sind z.B.: Eintauchen, des Flächengebildes in eine geeignete flüssige Substanz oder in eine Lösung einer geeigneten festen Substanz, oder in eine Mischung mehrerer fester und/oder flüssiger Substanzen, und anschliessend Entfernen der überschüssigen Flüssigkeit mittels zweier Quetschwalzen, zwischen denen das Flächengebilde durchgeführt wird; Aufsprühen einer Lösung einer geeigneten Substanz auf das Flächengebilde; Aufstreuen einer geeigneten pulverförmigen Substanz aufThe dimensional stabilization can take place according to known methods. Such methods are e.g .: immersing the fabric in a suitable liquid substance or in a solution a suitable solid substance, or in a mixture of several solid and / or liquid substances, and then Removal of the excess liquid by means of two nip rollers, between which the sheet is passed; Spray on a solution of a suitable substance on the sheet; Sprinkle on a suitable powdery substance
609809/0392609809/0392
253B593253B593
das Flächengebilde oder Anwendung anderer geeigneter Prozesse. Die aufgebrachten Substanzen werden dann gewünschtenfalls Bedingungen unterworfen, bei denen eine Umsetzung der Substanzen in sich, z.B. Polymerisation oder Umsetzung mit dem Flächengebilde, z.B. Vernetzen, erfolgt. Diese der Dimensionsstabilisierung dienende Grundausrüstung bewirkt vorteilhaft die Hydrophilisierung der Flächengebilde, wodurch letztere eine grössere Affinität gegenüber der versteifend wirkenden Zubereitung zeigt.the fabric or use of other suitable processes. The applied substances then become conditions if desired in which a reaction of the substances in itself, e.g. polymerisation or reaction with the flat structure, e.g. networking, takes place. This basic equipment, which is used for dimensional stabilization, advantageously brings about the hydrophilization the flat structure, whereby the latter shows a greater affinity for the stiffening preparation.
Nachdem das Fläehengebilde mit einer bestimmten Menge einer geeigneten Substanz imprägniert ist, wird diese zur gewünschten chemischen Reaktion gebracht, welche weiter unten näher beschrieben ist.After the sheet structure has been impregnated with a certain amount of a suitable substance, this becomes the desired one Brought chemical reaction, which is described in more detail below is.
Die für die Dimensionsstabilisierung geeigneten Substanzen sind vorzugsweise Produkte, welche unter geeigneten Bedingungen entweder mit dem Material des verwendeten Flächengebildes, mit anderen auf das Fläehengebilde aufgebrachten Produkten oder mit sich selber eine chemische Bindung eingehen können, welche imstande ist, die Dimensionen der Fläehengebilde zur Zeit der Reaktion stabil gegenüber den weiter oben erwähnten Beanspruchungen zu halten. Verwendung finden können z.B. in der Textilindustrie gebräuchliche Produkte wie: Harnstoff-Formaldehyd-Vorkondensate, Melamin-Verbindungen, Carbamide, Acetale, Verbindungen der Typen Aethylenharnstoff, Dihydroxydiäthylenharnstoff, Dihydroxydimethyldiäthylenharnstoff und alle HomologenThe substances suitable for dimensional stabilization are preferably products which, under suitable conditions, either with the material of the flat structure used, with other products applied to the flat structure or with be able to enter into a chemical bond which is capable of changing the dimensions of the surface structure at the time of To keep the reaction stable against the stresses mentioned above. Can be used e.g. in the textile industry Common products such as: urea-formaldehyde precondensates, Melamine compounds, carbamides, acetals, compounds of the types ethylene urea, dihydroxydiethylenurea, Dihydroxydimethyl diethylene urea and all homologues
609809/0392609809/0392
"" b —"" b -
2 b 3 5 5 9 32 b 3 5 5 9 3
dieser oder ähnlicher Konfigurationen allein oder in Kombination mit anderen erwähnten Produkten und/oder in Kombination mit einem geeigneten Katalysator. Als Katalysator kommen organische oder anorganische Säuren, oder die Metallsalze einer organischen oder anorganischen Säure, wie z.B. ein Alkali- oder Erdalkali-Halogenid oder aber ein Ammoniumsalz infrage. Es können aber auch andere Produkte Verwendung finden, wie z.B. Monomere, welche mit dem Material des Fläch.engebildes oder mit sich selber unter Ablauf einer Kondensation oder Polykondensation, Addition oder Polyaddition oder einer Polymerisation oder sonstiger chemischer Reaktionen, welche mit oder ohne Abspaltung eines weiteren Reaktionsprodukts ablaufen, umgesetzt werden können. Als Beispiele seien hier genannt: Styrol, Aethylen, Propylen und andere.these or similar configurations alone or in combination with other mentioned products and / or in combination with a suitable catalyst. Organic or inorganic acids, or the metal salts, can be used as the catalyst organic or inorganic acid, such as an alkali or alkaline earth metal halide or an ammonium salt. It can but other products are also used, such as monomers that work with the material of the flat structure or with itself itself with the course of a condensation or polycondensation, addition or polyaddition or a polymerization or other chemical reactions, which take place with or without splitting off a further reaction product, are implemented can. Examples include: styrene, ethylene, propylene and others.
Der weiter oben erwähnte Behandlungsschritt, welcher das oder die auf das Flächengebilde aufgebrachten Substanzen zur gewünschten chemischen Reaktion bringt, kann z.B. sein: die Einwirkung erhöhter Temperatur während einer bestimmten Zeit, z.B. eine Erhitzung auf 200 C während 10 Sekunden, die Einwirkung erhöhten Drucks, die Einwirkung von Strahlung, oder von energiereichen Strahlen im Zentimeter- oder Dezimeterbereich des elektromagnetischen Spektrums oder von Röntgenstrahlen, oder eine Kombination einer oder mehrerer der vorgenannten Einwirkungen.The treatment step mentioned above, which the or brings the substances applied to the surface structure to the desired chemical reaction, can be, for example: the effect increased temperature for a certain time, e.g. heating to 200 C for 10 seconds, increased the effect Pressure, the effect of radiation, or of high-energy rays in the centimeter or decimeter range of the electromagnetic Spectrum or X-rays, or a combination of one or more of the aforementioned effects.
Die erfindungsgemäss verwendeten Flächengebilde können in Gross-The planar structures used according to the invention can be used in large
809809/0392809809/0392
format, beispielsweise Textilbahnen, oder, insbesondere bei einer Anwendung in der Textilkonfektion, als Stänzlinge oder zugeschnittene Stücke vorliegen.format, for example textile webs, or, especially in an application in textile manufacture, as seedlings or cut pieces are available.
Die Versteifung der Flächengebilde in den zum voraus bestimmten Bereichen wird durch Aufdrucken einer Zubereitung, welche mindestens eine vernetzbare Substanz enthält, und Vernetzen derselben, herbeigeführt.The stiffening of the planar structures in the areas determined in advance is achieved by printing a preparation which at least contains a crosslinkable substance, and crosslinking the same brought about.
Als Druckverfahren kommen alle bekannten drucktechnischen Methoden wie Hochdruck, Tiefdruck oder Siebdruck infrage, wobei letzterer bevorzugt wird. Beim Hochdruck können beispielsweise Stempel verwendet werden, deren beim Druckvorgang wirksame Stellen aus saugfähigem Material bestehen. Die Schablonen für den Siebdruck können nach dem Reserve-, Vorlackier- oder vorzugsweise Potoverfahren hergestellt und je nach Betriebsbedingungen mit Müllergaze, einem synthetischen Gewebe oder Metallsiebgewebe, beispielsweise aus Bronze, bespannt sein. Als Rakel kommen Holz-Gummi- oder Rollrakel infrage. Das Fortbewegen der Ware an der Druckvorrichtung kann mittels einem endlosen Band, beispielsweise aus Gummi, Greifern, Saugelementen oder Nadelwalzen erfolgen.All known printing methods are used as the printing process such as letterpress, gravure or screen printing are possible, the latter being preferred. With high pressure, for example Stamps are used, the areas of which are effective during the printing process are made of absorbent material. The templates for the Screen printing can be produced according to the reserve, pre-painting or, preferably, Poto method and, depending on the operating conditions, with Müller gauze, a synthetic fabric or metal mesh, for example made of bronze, be covered. Wood-rubber or squeegee. Moving the goods on the printing device can be by means of an endless belt, for example made of rubber, grippers, suction elements or needle rollers.
Der Druckvorgang kann in einem oder mehreren Schritten erfolgen. Ist an einer bestimmten Stelle eine erhebliche Versteifung erforderlich, so kann das Flächengebilde mehrere Male mit der gleichen oder nacheinander mit verschiedenen Zubereitungen bedruckt werden. Die Menge der aufgedruckten versteifend wirken-The printing process can take place in one or more steps. If significant stiffening is required at a certain point, so the surface structure can be printed several times with the same or successively with different preparations will. The amount of stiffening printed
609809/0392609809/0392
— O ~- O ~
den Zubereitung kann durch deren Viskosität und beim Siebdruckverfahren auch durch Härte, Form, Druckkraft, Auflagewinkel und Geschwindigkeit der Rakel sowie durch die Dichte des Siebes variiert werden.The preparation can be influenced by its viscosity and the screen printing process also by hardness, shape, pressure force, support angle and speed of the squeegee as well as by the density of the screen can be varied.
Die aufgebrachte Zubereitung kann neben einer oder mehreren vernetzbaren Substanzen Katalysatoren, Weichmacher, Stabilisatoren, Emulgatoren und andere für die Ausrüstung brauchbare Stoffe enthalten. Sie liegt in flüssiger oder pastöser Form vor. Die Viskosität der Zubereitung kann durch Zugabe von Lösungsoder Verdickungsmittel^ eingestellt werden. The preparation applied can, in addition to one or more crosslinkable substances, catalysts, plasticizers, stabilizers, Contain emulsifiers and other substances useful for finishing. It is available in liquid or paste form. The viscosity of the preparation can be adjusted by adding a solvent or thickener ^.
Als vernetzbare Substanzen kommen Monomere und Polymere infrage; als Beispiele seien diejenigen,die oben für die Dimensionsstabilisierung angegeben wurden,genannt. Insbesondere werden Harze des Reaktanttyps bevorzugt. Die geeigneten Katalysatoren, wie Ammoniumsalze und Metallhalogenide, sind aus der Textilveredlung bekannt. Die Zubereitung kann auch Substanzen enthalten,, die den Versteifungseffekt für eine kurze Zeitspanne, z.B. bis zur ersten Wäsche, verstärken. Für diesen Zweck kommen beispielsweise native oder in verschiedenen Graden aufgebaute Stärken, Polyvinylalkohole von verschiedenem Hydrolisierungsgrad, Stärkeäther, Tragent, Celluloseäther, Algxnsäureprodukte, Eiweisskörper, Acetylcellulosen, Aminoplaste, Acry!verbindungen, Copolymere und Homologe obiger Verbindungen infrage.Monomers and polymers can be used as crosslinkable substances; Examples are those given above for dimensional stabilization. In particular, be Reactant type resins are preferred. The suitable catalysts, such as ammonium salts and metal halides, are from textile finishing known. The preparation can also contain substances that have the stiffening effect for a short period of time, e.g. for the first wash, reinforce. For this purpose, for example, native strengths or strengths built up in different degrees are used, Polyvinyl alcohols of various degrees of hydrolysis, starch ethers, carriers, cellulose ethers, alginic acid products, protein bodies, Acetyl celluloses, aminoplasts, acrylic compounds, copolymers and homologues of the above compounds.
609809/0392609809/0392
2B355932B35593
Das Aufdrucken der versteifend wirkenden Zubereitung kann vor oder nach Aufbringen eines thermoplastischen Klebers erfolgen. Das vorherige Aufbringen dieses Klebers hat den Vorteil, dass beim Aufdrucken der Zubereitung auf die dem Kleberauftrag entgegengesetzte Fläche ein Durchfliessen der Zubereitung verhindert wird.The stiffening preparation can be printed on before or after a thermoplastic adhesive has been applied. The prior application of this adhesive has the advantage that when the preparation is printed on the opposite to the adhesive application The preparation is prevented from flowing through the surface.
Die die Vernetzung bewirkende Behandlung kann sofort nach dem Aufdrucken der Zubereitung oder aber auch in einem späteren Zeitpunkt erfolgen. Sofern die Vernetzung durch Wärmebehandlung bewirkt wird, kann diese gleichzeitig mit dem Trocknen,unmittelbar nach dem Trocknen oder zu einem beliebigen späteren Zeitpunkt nach dem Trocknen erfolgen. Dieser spätere Zeitpunkt kann beispielsweise das Auftragen einer themoplastischen Masse oder das Verkleben der Flächengebilde mittels dieser Masse sein.The treatment which brings about the crosslinking can take place immediately after the preparation has been printed on or else at a later point in time take place. If the crosslinking is brought about by heat treatment, this can be done at the same time as drying, immediately after drying or at any time after drying. This later point in time can, for example be the application of a thermoplastic mass or the gluing of the surface structure by means of this mass.
Die Vernetzung kann nach bekannten Methoden, so nach der CASING-Methode (Crosslinking by Activated S_pecies of _INert Gases), mittels γ-Strahlung, UV-Strahlung oder vorzugsweise durch Wärmeeinwirkung erfolgen. Für die Uebertragung der Wärme sind verschiedene Vorrichtungen wie Walzen, Pressen, Trockenschränke, Thermofixieranlagen, Kondensierapparate geeignet. Wie schon weiter oben ausgeführt wurde, kann die Vernetzung zu jedem beliebigen Zeitpunkt nach dem Bedrucken herbeigeführt werden. Die Vernetzung kann zusammen mit einem anderen Verfahrensschritt, bei dem Wärmeanwendung auch erforderlich ist, erfolgen. So kann bei Versteifungseinlagen für Kleidungsstückteile die Vernetzung und die Verklebung der Einlage mit dem Oberstoff gleichzeitig erfolgen.The networking can be carried out using known methods, such as the CASING method (Crosslinking by Activated S_pecies of _INert Gases), by means of γ-radiation, UV-radiation or preferably through the action of heat take place. Various devices such as rollers, presses, drying cabinets, thermosetting systems, Suitable for condensing equipment. As already explained above, the networking can take place at any point in time be brought about after printing. The crosslinking can be carried out together with another process step in which heat is applied also required to be done. For example, in the case of stiffening inserts for garment parts, the networking and the The insert is glued to the outer fabric at the same time.
609809/0392609809/0392
Die nach dem erfindungsgemässen Verfahren hergestellten Flächengebilde sind unbeschränkt lagerbar, da, sofern während der Lagerung eine Vernetzung eintritt, .dies nur an den Stellen erfolgen kann, wo sie ohnehin erwünscht ist. Das neue Verfahren ist auch wirtschaftlicher als die oben angegebenen bekannten Verfahren, da die Zubereitung nur auf die zu versteifenden Stellen aufgebracht wird, wodurch ein Verfahrensschritt, nämlich das Auswaschen der unvernetzten Stellen, en-tfällt und gleichzeitig Chemikalien gespart werden. Die Positionierung für die Vernetzung muss nicht mehr sorgfältig von Hand ausgeführt werden, da die Vernetzung nur an den bedruckten Stellen möglich ist.The flat structures produced by the process according to the invention can be stored indefinitely, since if cross-linking occurs during storage, this only takes place at the points can where it is desired anyway. The new process is also more economical than the known processes given above, since the preparation is only applied to the areas to be stiffened, whereby a process step, namely the Washing out of the non-crosslinked areas, not applicable and at the same time Chemicals are saved. The positioning for networking no longer has to be carefully carried out by hand, since networking is only possible at the printed areas.
Die erfindungsgemäss hergestellten Versteifungseinlagen sind chemisch-reinigungs- und waschbeständig und können, wie weiter oben angegeben, dimensionsstabil ausgerüstet sein.The stiffening inserts produced according to the invention are Resistant to chemical cleaning and washing and, as stated above, can be made dimensionally stable.
Die Erfindung betrifft weiterhin eine Vorrichtung zur kontinuierlichen Durchführung des erfindungsgemässen Verfahrens,The invention also relates to a device for continuous Implementation of the method according to the invention,
welche folgende, in Durchlaufrichtung des Flächengebildes nacheinander angeordnete Elemente aufweist:which follow one after the other in the direction of passage of the fabric has arranged elements:
eine Materialzufuhr;a material supply;
eine Vorrichtung zur Positionierung der Flächengebilde; einen ersten Förderer;a device for positioning the fabrics; a first conveyor;
eine Vorrichtung zum Bedrucken der Flächengebilde; eine erste Abnahmevorrichtung zur Abnahme der bedruckten Flächengebilde; a device for printing the sheet-like structures; a first removal device for removing the printed sheet-like structures;
609809/0392609809/0392
2 b 3 5 5 9 32 b 3 5 5 9 3
- li -- li -
einen weiteren Förderer;another sponsor;
eine Vernetzungsvorrichtung;a networking device;
eine weitere Abnahmevorrichtung zur Abnahme der Flächengebilde von der Vernetzungsvorrichtung.a further removal device for removing the sheet-like structures from the crosslinking device.
Nach einer bevorzugten Ausführungsform des erfindungsgemässen Verfahrens werden Versteifungseinlagen für Hemden- und Blusenkragen hergestellt. Als Flächengebilde werden Gewirke oder Vliese mit dem Fläehengewicht von 15 bis 300 g/m oder Gewebe mit einemAccording to a preferred embodiment of the invention This process produces stiffening inserts for shirt and blouse collars. Knitted fabrics or fleeces are used as flat structures with a basis weight of 15 to 300 g / m or fabric with one
Fläehengewicht von 50 bis 300 g/m eingesetzt. Das Flächengebilde wird durch Eintauchen in eine flüssige Zubereitung mit einem Mittel zur dimensionsstabilen Ausrüstung imprägniert und dann auf eine Flüssigkeitsaufnahme von 25 bis 37 Gew.-^, bezogen auf das Flächengebilde, abgequetscht. Das Flächengebilde wird getrocknet und einer Wärmebehandlung unterworfen, die die Trocknung sowie die Aushärtung des aufgebrachten Harzes bewirkt. Das so dimensionsstabil ausgerüstete Flächengebilde kann jetzt oder zu einem späteren Zeitpunkt einseitig mit einem thermoplastischen Kleber versehen werden. Die thermoplastischen Kleber wie Polyäthylen, Polyvinylchlorid und Polyamid sind dem Fachmann bekannt.Area weight of 50 to 300 g / m used. The flat structure is impregnated with an agent for dimensionally stable finishing by immersion in a liquid preparation and then based on a liquid uptake of 25 to 37 wt .- ^, based on the flat structure, squeezed off. The fabric is dried and subjected to a heat treatment which causes the drying and curing of the applied resin. That so A dimensionally stable surface structure can now or at a later point in time on one side with a thermoplastic Glue can be provided. The thermoplastic adhesives such as polyethylene, Polyvinyl chloride and polyamide are known to the person skilled in the art.
Die Flächengebilde werden dann einem oder mehreren Druckvorgängen unterworfen. Das Zuschneiden oder Zustanzen der Einlagen erfolgt vor, während oder nach dem Druckvorgang. Das Bedrucken erfolgt mit einem oder mehreren Sieben, wobei diese so gewählt werden, dass ein Auftrag von 1 bis 4 g Flüssigkeit pro 400 cmThe fabrics are then subjected to one or more printing processes. The inserts are cut or stamped before, during or after printing. The printing is done with one or more screens, these being chosen that an application of 1 to 4 g of liquid per 400 cm
609809/0392609809/0392
2S355932S35593
Fläche resultiert.Area results.
Das Drucksieb ist vorzugsweise so ausgebildet, dass neben Bereichen ohne Flüssigkeitsauftrag auch Bereiche mit kleinerem und grösserem Flüssigkeitsauftrag mit dem gleichen Sieb in einem einzigen Druckvorgang erzielt werden können. Die Rakelgeschwindigkeit kann 0,3 bis 3 m/sek. betragen. Die Trocknung nach dem Bedrucken erfolgt etwa bei 100° bis 1300C in einem Ofen. Soll die Vernetzung gleichzeitig erfolgen, so wird vorzugsweise während 4 bis 5 Minuten auf etwa 150 C im Ofen erwärmt. Bei der Erwärmung auf einer Presse, d.h. durch Kontakt, genügen 20 bis 100 Sekunden. Wird ein thermoplastischer Kleber schon vor dem Bedrucken auf das Flächengebilde aufgetragen, so sollte das Trocknen unterhalb 1300C erfolgen. In diesem Falle kann das Vernetzen gleichzeitig mit dem Verkleben bewirkt werden. Da während dem Verkleben jedoch nur kurz, vorzugsweise während 18 bis 22 Sekunden, auf 150° bis l80°C erwärmt wird, müssen im letztgenannten Fall schnellvernetzende Harze und/oder Katalysatoren eingesetzt, werden. Das Vernetzen kann gewünschtenfalls auch beim Aufbringen des thermoplastischen Klebers bewirkt werden, da auch dieser Schritt unter Wärmeeinwirkung erfolgt.The printing screen is preferably designed in such a way that, in addition to areas without liquid application, areas with smaller and larger liquid application can also be achieved with the same screen in a single printing process. The squeegee speed can be 0.3 to 3 m / sec. be. The drying after printing is performed at about 100 ° to 130 0 C in an oven. If the crosslinking is to take place at the same time, it is preferably heated to about 150 ° C. in the oven for 4 to 5 minutes. When heating on a press, ie by contact, 20 to 100 seconds are sufficient. If a thermoplastic adhesive applied to the fabric before the printing, the drying below 130 0 C should be performed. In this case, the crosslinking can be effected simultaneously with the gluing. However, since the adhesive is only heated briefly, preferably for 18 to 22 seconds, to 150 ° to 180 ° C., rapidly crosslinking resins and / or catalysts must be used in the latter case. If desired, the crosslinking can also be brought about when the thermoplastic adhesive is applied, since this step also takes place under the action of heat.
Die nachfolgenden Beispiele veranschaulichen die Erfindung:The following examples illustrate the invention:
609809/0392609809/0392
Ein Baumwollgewebe mit einem Plächengewicht von I50 g/m wird mit einer wässrigen Zubereitung, enthaltendA cotton fabric with a surface weight of 150 g / m 2 is used with an aqueous preparation containing
imprägniert, getrocknet und kondensiert.impregnated, dried and condensed.
Die Hälfte des formstabil ausgerüsteten Gewebes wird einseitig mit Niederdruckpolyäthylenpulver der Dichte 0,964 und des Schmelzbereiches 127 bis 130 C beschichtet.Half of the dimensionally stable fabric is coated on one side with low-pressure polyethylene powder with a density of 0.964 and des Melting range 127 to 130 C coated.
Sowohl das beschichtete wie auch das unbeschichtete Gewebe werden an den zu versteifenden Stellen mit einer wässrigen Zubereitung, enthaltendBoth the coated and the uncoated fabric are applied to the areas to be stiffened with an aqueous preparation, containing
mittels eines Siebes bedruckt. Die Viskosität der Zubereitung beträgt 128 cps. Beim Sieb handelt es sich um ein Polyestersiebprinted by means of a screen. The viscosity of the formulation is 128 cps. The sieve is a polyester sieve
609809/0392609809/0392
mit der Einstellung 100 Faden/cm, 100 Schuss/cm. Die Rakelgeschwindigkeit beträgt 0,7 m/sek. und der Rakelwinkel 35°·with the setting 100 threads / cm, 100 weft / cm. The squeegee speed is 0.7 m / sec. and the squeegee angle 35 °
Die Trocknung der einzelnen Proben erfolgt zwischen 100 und 13O0C während jeweils 20 bis 120 Sekunden im Ofen, wo auch bei 150 C während 4 Minuten vernetzt wird.The drying of each sample is carried out between 100 and 13O 0 C, respectively during 20 to 120 seconds in the oven, where it is crosslinked at 150 C for 4 minutes.
Ein Baumwollgewebe mit einem Flächengewicht von 250 g/m wird wie in Beispiel 1 beschrieben behandelt.A cotton fabric with a weight per unit area of 250 g / m 2 is treated as described in Example 1.
Die Zubereitung für die formstabile Ausrüstung enthält:The preparation for the dimensionally stable finish contains:
Die aufzudruckende Zubereitung enthält:The preparation to be printed contains:
Fixapret AC I60 g/lFixapret AC I60 g / l
Fixapret CPNS 120 g/lFixapret CPNS 120 g / l
Vinerol FV 80 g/lVinerol FV 80 g / l
Salvitose HSD βθ g/lSalvitose HSD βθ g / l
MgCl2 30 g/l.MgCl 2 30 g / l.
Die Viskosität der Zubereitung beträgt 1 750 cps.The viscosity of the formulation is 1,750 cps.
609809/0392609809/0392
Ein Baumwollgewebe mit einem Flächengewicht von .160 g/m wird mit einer wässrigen Zubereitung, enthaltendA cotton fabric with a basis weight of .160 g / m 2 is mixed with an aqueous preparation containing
imprägniert, bei 100° bis 13O0C bis auf eine Restfeuchtigkeit von 6 bis 8 % getrocknet und bei l60°C 4 Minuten im Ofen kondensiert.impregnated, at 100 ° to 13O 0 C to a residual moisture content of 6 to 8% and dried at l60 ° C for 4 minutes in the oven condensed.
Das Gewebe wird dann mit einem thermoplastischen Kleber beschichtet. The fabric is then coated with a thermoplastic adhesive.
Auf die der beschichteten entgegengesetzte Fläche wird eine wässrige Zubereitung, enthaltendOn the surface opposite to the coated one is applied an aqueous Preparation containing
Finish KVS (flüssig) 100 g/l
Razefix F (flüssig) 25 g/l
Teranin KFP (Paste) 30 g/l
Sandozin NIT (flüssig) 1 g/l,Finish KVS (liquid) 100 g / l
Razefix F (liquid) 25 g / l
Teranin KFP (paste) 30 g / l
Sandozin NIT (liquid) 1 g / l,
mit einem Sieb aufgedruckt. Der pH-Wert der Zubereitung ist mit Essigsäure auf 3»9 eingestellt. Die Trocknung erfolgt bei 80 C während 1 bis 2 Minuten. Gleichzeitig mit dem Verkleben der erhaltenen Flächengebilde mit einem weiteren Flächengebilde wird auf einer Presse bei l80°C während 20 Sekunden fixiert.imprinted with a sieve. The pH of the preparation is adjusted to 3-9 with acetic acid. Drying takes place at 80 ° C for 1 to 2 minutes. Simultaneously with the gluing of the sheet-like structure obtained to a further sheet-like structure fixed on a press at 180 ° C for 20 seconds.
609809/039 2609809/039 2
Das Verfahren nach Beispiel 3 wird mit einem Gewebe mit einemThe procedure of Example 3 is carried out with a fabric with a
2 Plachengewicht von 250 g/m wiederholt.2 tarpaulin weights of 250 g / m repeated.
Für die Formfestausrüstung wird eine Zubereitung3 enthaltend A preparation 3 is contained for the dimensionally stable finishing
Die Zubereitung zum Bedrucken enthält:The preparation for printing contains:
Fixapret KVS (flüssig) l60 g/lFixapret KVS (liquid) l60 g / l
Razefix F (flüssig) 40 g/lRazefix F (liquid) 40 g / l
Teranin KFP (Pas'te) 50 g/lTeranin KFP (pas'te) 50 g / l
Sandozin NIT (flüssig) 1 g/lSandozin NIT (liquid) 1 g / l
und wird mit Essigsäure auf einen pH-Wert von 3»9 eingestelltand is adjusted to a pH of 3 »9 with acetic acid
6 0 9809/0396 0 9809/039
Claims (13)