Description

KAISERLICHESIMPERIAL

PATENTAMT.PATENT OFFICE.

und Zündbänder.and detonating tapes.

Man hat schon vielfach versucht, den roten Phosphor zur Herstellung von an allen Reibflächen entzündlichen Zündhölzern geeignet zu machen; bis jetzt noch ohne wirklichen technischen Erfolg. Die bisher mit rotem Phosphor hergestellten Zündhölzer entzünden sich entweder zu schwer und vor allem nicht an den Kleidern, oder sie krachen, spritzen und verbrennen explosionsartig, so daß manMany attempts have been made to use red phosphorus for the production of all friction surfaces to make flammable matches suitable; so far without any real technical success. So far with red Matches made with phosphorus are either too difficult to ignite and, above all, do not ignite on clothes, or they crack, splash and burn explosively, so that you

ίο zur Zeit noch nicht davon reden kann, daß der rote Phosphor imstande wäre, den gelben Phosphor in der Streichholzindustrie zu ersetzen. ίο can't talk about that at the moment the red phosphorus would be able to replace the yellow phosphorus in the match industry.

Es wurde nun gefunden, daß man ausgezeichnete, an allen Reibflächen, auch an Kleiderstoffen sehr leicht entzündliche Zündhölzer herstellen kann, wenn man den roten Phos-¹ phor nicht für sich allein, · sondern gemischt mit Goldschwefel (Antimonpentasulfid) anwendet. It has now been found that excellent, can produce at all friction surfaces, even on clothing material very flammable matches, unless you apply the red phosphorus ¹ phor by itself, but · mixed with gold sulfur (antimony pentasulfide).

Die ganz eigenartige Wirkung des Goldschwefels war bisher nicht bekannt. In der englischen Patentschrift 22895/02 ist zwar der Ersatz von gewöhnlichem Schwefel durch GoIdschwefel in der Zündmasse vorgesehen. Allein es wird dabei gesagt, daß die Anwendung des Goldschwefels keine besonderen Vorteile biete. Bei dem in der englischen Patentschrift angegebenen Verhältnis von Schwefel bzw. GoIdschwefel zu rotem Phosphor (1 Teil Phosphor auf 0,25 — 0,5 Teile Goldschwefel) tritt auch die besondere Wirkung des Gold schwefels noch gar nicht in Erscheinung, weshalb seine Verwendung mit Recht dort als zwecklos bezeichnet wird.The very peculiar effect of gold sulfur was not previously known. In the English patent specification 22895/02 is the replacement of common sulfur with gold sulfur provided in the ignition mass. But it is said that the use of gold sulfur offers no particular advantages. With the ratio of sulfur or gold sulfur specified in the English patent red phosphorus (1 part phosphorus to 0.25-0.5 parts gold sulfur) also occurs the special effect of gold sulfur is not yet apparent, which is why it is used is rightly called useless there.

Es wurde jedoch gefunden, daß, wenn größere Mengen von Goldschwefel verwendet werden (mehr als 0,5 — 1,5 Teile Goldschwefel auf ι Teil Phosphor), man in ganz ungeahnter Weise eine Zündmasse von ausgezeichneten Eigenschaften erhält.However, it has been found that when larger amounts of gold sulfur are used (more than 0.5 - 1.5 parts of gold sulfur to ι part of phosphorus), one in completely unimagined Way, a primer with excellent properties is obtained.

Durch den Zusatz von Goldschwefel in der erwähnten Menge wird einerseits erreicht, daß man einen so hohen Prozentsatz roten Phosphors anwenden kann, daß die Hölzer sich leicht entzünden, und andererseits, daß das unangenehme und gefährliche Spritzen und Krachen, sowie das explosionsartige rasche Abbrennen der allein mit rotem Phosphor hergestellten Zündköpfe verhindert wird. Zugleich erniedrigt die Gegenwart von soviel Goldschwefel die Entzündungstemperatur des roten Phosphors, die bekanntlich etwa 300 ° C. ist, auf 160 bis 170 ° C, was natürlich ebenfalls noch sehr zur leichten Entzündbarkeit der Zündmasse beiträgt. Die unter solcher Verwendung von Goldschwefel hergestellten Zündmassen aus rotem Phosphor sind derartig leicht entzündlich, daß sie auch zum Ersatz der mit gelbem Phosphor hergestellten Zünd-By adding gold sulfur in the amount mentioned, it is achieved on the one hand that so high a percentage of red phosphorus can be used that the woods can easily ignite, and on the other hand that unpleasant and dangerous splashing and Cracking, as well as the explosive rapid burning of the red phosphorus alone produced ignition heads is prevented. At the same time, the presence of so much humiliates Gold sulfur is the ignition temperature of red phosphorus, which is known to be around 300 ° C. is to 160 to 170 ° C, which of course also still contributes greatly to the easy flammability of the primer. Those made with such use of gold sulfur Red phosphorus primers are so easily flammable that they can be used as a substitute of the ignition elements made with yellow phosphorus

bänder für Grubensicherheitslampen verwandt werden können.tapes for mine safety lamps can be used.

Ein weiterer Vorteil eines solchen Zusatzes von Goldschwefel zu rotem Phosphor besteht darin, daß man letzteren, um das unangenehme Krachen, Knallen und Spritzen zu vermeiden nicht mehr, wie dies bisher nötig war, aber sehr gefährlich ist, mit dem Sauerstoff abgebenden Körper (Kaliumchlorat, Και ο liumperchlorat) zusammen zu mahlen braucht, sondern, daß die Zündköpfe vielmehr auch beim einfachen Vermischen der Massen durch Rühren sich ohne jede unangenehme Nebenerscheinungen entzünden. Another advantage of such an addition of gold sulfur to red phosphorus is in that one can avoid the unpleasant cracking, popping and splashing of the latter no longer avoid, as was previously necessary, but is very dangerous, with the oxygen donating body (potassium chlorate, Και ο lium perchlorate) needs to grind together, Rather, that the ignition heads also by simply mixing the masses through Stir ignite without any unpleasant side effects.

Example:

Man mahlt die im nachfolgenden Rezept angegebenen Massen ι und 2 getrennt in der üblichen Weise und rührt sie dann einfach zusammen, wodurch die Fabrikation der Zündmasse gänzlich gefahrlos wird.The masses ι and 2 given in the following recipe are ground separately in the usual way and then simply stirs them together, thereby making the ignition material becomes completely safe.

Rezept.
Masse 1.Recipe.
Mass 1.

350 g roter Phosphor,350 g red phosphorus,

400 g Goldschwefel,
100 g Kreide,
100 g Zinkoxyd,
100 g Glaspulver.400 g gold sulfur,
100 g chalk,
100 g zinc oxide,
100 g glass powder.

Masse ι wird mit Wasser zu einem Brei anangerührt und vermählen.Mass ι is mixed with water to form a paste and marry.

₍ Masse 2. ₍ Mass 2.

500 g Leim werden in der üblichen Menge Wasser gelöst, dann werden eingerührt:500 g of glue are dissolved in the usual amount of water, then the following is stirred in:

1300 g Kaliumchlorat,
50 g Kreide,
50 g Zinkoxyd,
50 g Glaspulver.1300 g potassium chlorate,
50 g chalk,
50 g zinc oxide,
50 g glass powder.

Masse 2 wird ebenfalls vermählen und alsdann mit Masse 1 vermischt. Die paraffinierten oder geschwefelten Holzspäne werden in der gewöhnlichen Weise getunkt, getrocknet und verpackt.Mass 2 is also ground and then mixed with mass 1. The paraffined ones or sulphurized wood chips are dipped and dried in the usual way and packed.

Selbstredend kann dieses Rezept variiert werden. Nach vorliegender Erfindung ist es nur, wie Versuche ergeben haben, wesentlich, daß einerseits auf 1 Teil roten Phosphor mehr als 0,5 Teile und andererseits nicht erheblich mehr als 1,5 Teile Goldschwefel angewandt werden, weil im ersteren Falle die günstigen Wirkungen des Goldschwefels sich zu wenig bemerkbar machen und im letzteren Falle die Zündmasse unnötigerweise verteuert wird.Of course, this recipe can be varied. According to the present invention it is only, as experiments have shown, it is essential that on the one hand 1 part more red phosphorus than 0.5 part and, on the other hand, not significantly more than 1.5 parts of gold sulfur because in the first case the beneficial effects of gold sulfur are too little make noticeable and in the latter case the ignition mass is unnecessarily expensive.

Claims

Patent claim:

Ignition compound containing red phosphorus and gold sulfur for matches and ¹ ignition tapes, characterized in that more than 0.5 parts and not considerably more than 1.5 parts gold sulfur are added to the ignition material.