DE2440217A1 - Bonded laminate for clothing and foundation garments - from fleeces and non-wovens without surface consolidation or thick covers - Google Patents

Bonded laminate for clothing and foundation garments - from fleeces and non-wovens without surface consolidation or thick covers

Info

Publication number
DE2440217A1
DE2440217A1 DE2440217A DE2440217A DE2440217A1 DE 2440217 A1 DE2440217 A1 DE 2440217A1 DE 2440217 A DE2440217 A DE 2440217A DE 2440217 A DE2440217 A DE 2440217A DE 2440217 A1 DE2440217 A1 DE 2440217A1
Authority
DE
Germany
Prior art keywords
fleece
layer
filling
woven
transparent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DE2440217A
Other languages
German (de)
Inventor
Alois Gmeiner
Hans Koller
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bunzl and Biach AG
Original Assignee
Bunzl and Biach AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bunzl and Biach AG filed Critical Bunzl and Biach AG
Publication of DE2440217A1 publication Critical patent/DE2440217A1/en
Pending legal-status Critical Current

Abstract

A bonded fabric produced from a fleece in combination with other fabrics such as wovens, knitted, foamed sheets and transparent films, etc., comprises a layer of a bulky fleece filling or foamed sheet on which a further non-woven fabric in the range between 15 and 50 g/m2 is placed, this layer being either dyed or printed on the face turned from the filling, the two being then covered by a transparent product such as a woven or knitted fabric or film. The fleece covering the filling should have an unornamented area of =15% and an opacity >=85%, whilst the transparent layer should have an open area of from 60-85%. Cheaper than known types of laminates, with better permeability and insulating qualities.

Description

Verbundstoff Die vorliegende Erfindung bezieht sich auf einen Verbundstoff, welcher zur Herstellung von insbesondere hochwärmeundurchlässigen Kleidungsstücken, jedoch auch für andere Zwecke, wie beispielsweise Bettwäsche, und letztlich auch für technische Zwecke bzw. Dekorationszwecke verwendet werden kann. Composite The present invention relates to a composite, which is used for the production of, in particular, highly heat-impermeable garments, but also for other purposes, such as bed linen, and ultimately also can be used for technical or decorative purposes.

Verbundstoffe dieser Art auf Basis eines wärmedämmenden voluminösen Vlieses wurden bisher so hergestellt, daß das betreffende Vlies ein- oder beidseitig mit bedruckten oder durchgefärbten Geweben, Gewirken, Filzen bzw. Vliesen oder anderen nach bekannten textiltechnischen Herstellungsverfahren erzeugten Flächengebilden belegt und die so erhaltenen doppelschichtigen Gebilde miteinander verbunden wurden. Auf diese Art wurden bisher Bekleidungsartikel (insbesondere Morgenröcke, Miederwaren u.dgl.), Steppdecken (hauptsächlich Tagesdecken) sowie Dekorationsmaterialien hergestellt. Die so erzeugten Verbundstoffe erfüllen zwar durchaus den gewünschten Zweck, jedoch weisen sie noch einige Nachteile auf: so muß beispielsweise das voluminöse Vlies, bevor es mit dem anderen Textilstoff belegt wird, oberflächenverfestigt werden, um zu vermeiden, daß Fasern des Vlieses durch den Oberstoff dringen. Composites of this type on the basis of a heat-insulating voluminous Fleece have been produced so far that the fleece in question on one or both sides with printed or dyed fabrics, knitted fabrics, felts or fleeces or others Flat structures produced by known textile manufacturing processes occupied and the double-layer structures thus obtained were connected to one another. Articles of clothing (especially dressing gowns, corsetry etc.), quilts (mainly bedspreads) and decorative materials. The composites produced in this way certainly fulfill the desired purpose, however they still have some disadvantages: for example, the voluminous fleece, before it is covered with the other textile, be surface-hardened, in order to avoid that fibers of the fleece penetrate through the outer fabric.

Weiterhin ist es notwendig, relativ dicke Oberstoffe zu verwenden, damit während des Gebrauches keine mechanischen Schäden daran auftreten.Furthermore, it is necessary to use relatively thick outer fabrics, so that no mechanical damage occurs to it during use.

Die Gewebegewirke müßten weiterhin so dicht gewebt oder gewirkt sein, daß die Farbdifferenz zu dem gebundenen synthetischen weißen Füllvlies nicht auftritt, d.h. daß ein buntes oder bedrucktes, also wenig transparentes Gewirke oder Gewebe voll abdeckt. Derartige Gebilde sind nicht nur teuer, sondern geringer atmungsaktiv und wärmestauend, was als unangenehm bei der Verwendung für Morgenröcke, Büstenhalterkörbchen usw. empfunden wird. Um diesem Mangel abzuhelfen, hatte man das Füllvlies entweder aus gefärbten Fasern oder durch farbpigmentierte Bindemittel dem Farbton des Oberstoffes anzugleichen. Die erste Methode ist sehr teuer bei Farbänderungen, insbesondere bei Um- oder Rückrüstung, z.B. von schwarz auf weiß; die zweite Möglichkeit ist in der Farbtontiefe begrenzt. The knitted fabrics should continue to be so tightly woven or knitted, that the color difference to the bound synthetic white filling fleece does not occur, i.e. that a colored or printed, i.e. not very transparent knitted fabric or fully covers tissue. Such structures are not only expensive, but also less expensive breathable and heat retaining, which is uncomfortable when used for dressing gowns, Bra cup etc. is felt. To remedy this deficiency, one had the filling fleece either from colored fibers or from color-pigmented binders to match the color of the outer fabric. The first method is very expensive for color changes, especially when upgrading or upgrading, e.g. from black to white; the second option is limited in the depth of the shade.

Die Abdeckung des voluminösen Grundfüllvlieses durch textile Vliese, sogenannte Non-woven-Stoffe, hat sich bisher auch nicht als zweckdienlich erwiesen, da diese Non-woven-Stoffe mechanisch nicht so widerstandsfähig sind wie die bisher bekannten gewebten bzw. gewirkten Stoffe. The covering of the voluminous basic filling fleece with textile fleece, so-called non-woven fabrics, has not yet proven to be useful, because these non-woven fabrics are not as mechanically resistant as they have been up to now known woven or knitted fabrics.

Es wurde nun gefunden, daß man auf überraschend einfache Art und Weise Flächengebilde erhalten kann, die sowohl in der Herstellung billiger sind als die bisher bekannten Verbundstoffe als auch die oben angeführten Nachteile nicht aufweisen, d.h. in ihren Gebrauchseigenschaften den herkömmlichen Verbundstoffen der obgenannten Art überlegen sind, wenn man einen sehr dünnen aber doch "hochopaken" weißen, farbigen oder bedruckten wasser- und reinigungsbeständigen Vliesstoff (Deckvlies), zweckmäßig aus Zellwollfasern, unter einem sogar schütteren, transparenten, bunten oder bedruckten Oberstoff (Gewirke oder Gewebe) etc. anordnet. Man erzielt dadurch sehr wohl die notwendige Opazität und das synthetische Füllvlies brauchtlimmer nur weiß erzeugt zu werden. It has now been found that in a surprisingly simple manner and Wise fabrics can be obtained that are both cheaper to manufacture than the previously known composites as well as the disadvantages listed above have, i.e. the properties of conventional composites in terms of their properties are superior to the above type if you have a very thin but "highly opaque" white, colored or printed water- and cleaning-resistant nonwoven (cover nonwoven), expediently made of cellulose fibers, even under one sparse, transparent, colorful or printed outer fabric (knitted or woven fabric) etc. arranges. One achieves thus the necessary opacity and the synthetic filling fleece needs mica only knows to be created.

Gegenstand der vorliegenden Erfindung ist somit ein Verbundstoff auf Vliesbasis in Kombination mit anderen Flächengebilden, wie Geweben, Gewirken, Schaumstoffschichten, Folien sowie transparenten Schichten, der dadurch gekennzeichnet ist, daß er wenigstens eine Schicht aus einem voluminösen Füllvlies bzw. Schaumstoff u.ä. -aufweist, auf welcher eine weitere Vliesschicht (Non-woven), vorzugsweise in der Grammatur von ca. 15 bis 50 g/m2, angeordnet ist, welche Deckvliesschicht an ihrer vom erstgenannten Füllvlies abgewandten Seite vorzugsweise gefärbt und/oder bedruckt ist, wobei über dieser zweitgenannten Deckvliesschicht ein transparentes Flächengebilde, z.B. ein Gewebe, Gewirke oder eine Folie, angeordnet ist. The present invention thus provides a composite based on fleece in combination with other fabrics, such as woven, knitted, Foam layers, foils as well as transparent layers, which are characterized is that it has at least one layer of a voluminous filling fleece or foam etc. - has, on which a further non-woven layer, preferably in the grammage of approx. 15 to 50 g / m2, which cover fleece layer preferably colored and / or on their side facing away from the first-mentioned filling fleece is printed, with a transparent over this second-mentioned cover fleece layer Flat structure, e.g. a woven fabric, knitted fabric or a film, is arranged.

Vorzugsweise sind die Schichten miteinander durch Steppen, Nähen, Kleben bzw. Kaschieren oder Schweißen verbunden. Preferably the layers are interlocked by quilting, sewing, Gluing or lamination or welding connected.

Wie bereits erwähnt, wird als Grundvlies ein möglichst voluminöses Füllvlies eingesetzt, um die gewünschten Wärmedämmeigenschaften zu erzielen. Besonders zweckmäßig ist es, wenn dieses voluminöse Füllvlies durch Nadeln verfestigt ist; selbstverständlich kann es darüber hinaus auch weiter durch aufgebrachte Adhäsionsmittel (Besprühung), durch Schmelzfasern oder dergleichen auf irgendeine der bekannten herkömmlichen Arten verfestigt sein, wobei jedoch immer darauf geachtet werden muß, daß bei der Verfestigung nicht die gewünschte Eigenschaft des fertigen Stoffes, insbesondere die bereits erwähnte Wärmedämmfestigkeit verlorengeht. As already mentioned, the base fleece is as voluminous as possible Filling fleece used to achieve the desired thermal insulation properties. Particularly It is useful if this voluminous filling fleece is solidified by needles; Of course, it can also be done by applying adhesives (Spraying), by fusible fibers or the like onto any of the known ones usual Kinds be solidified, but always on it Care must be taken that not the desired property of the solidification finished material, in particular the already mentioned thermal insulation strength is lost.

Das Deckvlies (Non-woven) hat nicht nur wärmedämmende Eigenschaften zu erfüllen, sondern soll auch einerseits dem Verbundgebilde eine gewisse mechanische Festigkeit verleihen, das Füllvlies optisch abdecken und weiterhin verhindern, daß.Einzelfasern des Füllvlieses nach außen dringen. Als Deckvliesschicht wird somit vorzugsweise ein relativ stark verfestigtes Vlies eingesetzt. Die Deckvliesschicht ist weiterhin an ihrer Außenseite, d.h. der Seite, die von der Füllvliesschicht abgewendet ist, vorzugsweise gefärbt, bedruckt oder irgendwie dessiniert, d.h. diese Schicht ist vor allem die Trägerin der geschmacklichen Ausführung des betreffenden Verbundstoffes. Er besitzt -vorzugsweise eine hohe Opazität bzw. Lichtundurchlässigkeit von 85 % oder mehr, d.h. es sind wenigstens 85 % der Gesamtfläche durch Fasern abgedeckt, was einer Leerfläche von 15 % entspricht. The cover fleece (non-woven) not only has thermal insulation properties to meet, but on the one hand should also give the composite structure a certain mechanical Lend strength, optically cover the filling fleece and furthermore prevent individual fibers of the filling fleece penetrate to the outside. The preferred non-woven cover layer is therefore a relatively strongly consolidated fleece is used. The top layer is still on their outside, i.e. the side that is turned away from the filling fleece layer, preferably colored, printed or somehow patterned, i.e. this layer is above all, the carrier of the taste execution of the composite in question. It has - preferably a high opacity or light impermeability of 85% or more, i.e. at least 85% of the total area is covered by fibers, which corresponds to an empty area of 15%.

Als transparentes Flächengebilde wird zur Herstellung von textilen Grundmaterialien vor allem eine Schicht aus einem Gewebe bzw. Gewirke verwendet; wesentlich dabei ist, daß die Ausführung hinsichtlich Fadenstärke bzw. Fadenzahl oder Maschenzahl pro cm2 so gewählt wird, daß diese letzte Schicht transparent ist und das Desmn der Deckvliesschicht (non-woven) durch diese oberste Schicht durchscheinen kann. As a transparent flat structure is used for the production of textile Basic materials mainly a layer of a woven or knitted fabric used; It is essential that the execution in terms of thread size or thread count or the number of meshes per cm2 is chosen so that this last layer is transparent and the design of the non-woven cover layer shines through this top layer can.

In diesem Fall liegt Leerfläche oder Transparenz bei ca. 60 bis 85 %. Insbesondere auf dem technischen Sektor ist es auch möglich, anstelle eines Gewebes oder Gewirkes als Obershicht eine transparente Folie zu wählen; die ihrerseits dann durch Verkleben, Verschweißen oder dergleichen mit der Deckvliesschicht (Non-woven) verbunden werden kann.In this case, void or transparency is around 60 to 85 %. In the technical sector in particular, it is also possible instead of a fabric or knitted fabric to choose a transparent film as the top layer; which in turn then by gluing, welding or the like with the cover fleece layer (non-woven) can be connected.

Derart hergestellte Verbundstoffe eignen sich insbesondere zur Herstellung von Dekorationsstoffen, oder anderen, auf dem technischen Gebiet verwendbaren Verbundstoffen.Composites produced in this way are particularly suitable for production of decorative fabrics or other composites that can be used in the technical field.

Selbstverständlich ist es möglich, das voluminöse Füllvlies nicht nur einseitig, sondern beidseitig auf die angegebene Art zu beschichten. Es ist jedoch auch möglich, die andere Seite des voluminösen Füllvlieses auf beliebige Art und Weise abzudecken. Of course, it is possible not to use the voluminous filling fleece only to be coated on one side, but on both sides in the specified manner. It is however, it is also possible to place the other side of the voluminous filling fleece on any Way to cover.

Die folgenden Beispiele sollen die vorliegende Erfindung näher erläutern, ohne daß diese jedoch hierauf beschränkt sein soll. The following examples are intended to explain the present invention in more detail. but without this being restricted to this.

B e i s p i e 1 1: Zur Erzeugung eines guten Morgenrocks verwendet man als Oberstoff ein 40 den Polyamidgewirke (bedruckt oder unbedruckt), welches mit einer Polyesterwatte oder einem ähnlichen Füllmaterial in einer Grammatur von ca. 70 g/m² 2 bis ca. 80 g/m² versteppt wird. Diese Watte muß beidseitig besprüht sein. Erfindungsgemäß kann man denselben Morgenrock wie folgt herstellen: Als Oberschicht verwendet man z.B. ein 20 den weißes Gewirke und als Zwischenlage einen bedruckten Vliesstoff in einer Grammatur von ca. 30 g/m². Bei der neuen Kombination kann man eine Watte in einer Grammatur von 50 g/m² verwenden, wobei man dieselben Wärmehalteeigenschaften wie bei der bisherigen Erzeugungsart erzielt.EXAMPLE 1 1: Used to create a good dressing gown the outer fabric is a 40 denier polyamide fabric (printed or unprinted), which with a polyester wadding or a similar filling material in a grammage of approx. 70 g / m² 2 to approx. 80 g / m² is quilted. This cotton wool must be sprayed on both sides be. According to the invention, the same dressing gown can be made as follows: As a top layer For example, a 20 denier white knitted fabric is used and a printed one as an intermediate layer Non-woven fabric with a grammage of approx. 30 g / m². With the new one combination you can use wadding with a grammage of 50 g / m², using the same Heat retention properties as achieved with the previous type of generation.

B e i s p i e 1 2: Ein weißes Polyamidgewirke mit hoher Transparenz von 80 % (d.h. nur 20 % der Fläche sind durch Fasern abgedeckt) wird mit einem Zellwoll-Abdeckvlies aus 1,5 den Fasern, 60 mm Stapel, mit vernetztem Acrylharz gebunden und rot bedruckt und einem m2-Gewicht von 40 g/m2 unterlegt und mit einem Polyesterfüllvlies von 60 g/m2 7,5 den 60 mm (im Sprühverfahren verfestigt) und einem lockeren Gewirke (Transparenz z.B. von 75 t) zusammen versteppt. Der Farbeindruck kommt voll zu tragen.Example 1 2: A white polyamide knitted fabric with high transparency 80% (i.e. only 20% of the area is covered by fibers) is covered with a cellulose fleece made of 1.5 fibers, 60 mm staple, bound with cross-linked acrylic resin and printed in red and a m2 weight of 40 g / m2 and lined with a polyester filler fleece from 60 g / m2 7.5 denier 60 mm (solidified by spraying) and a loose knitted fabric (Transparency e.g. of 75 t) stitched together. The color impression comes into its own.

B e i s p i e 1 3: Ein weißer Polyamid-Wirkstoff mit einer Transparenz von 70 % wird mit einem weißen Zellwollvlies mit 30 g/m2, 1,5 den, 60 mm Stapel, demselben weißen Füll-2 vlies, jedoch nur 50 g/m2 und einem Unterstoff höheer Transparenz unterlegt und die Schichten werden miteinander versteppt (geringe Transparenz des Oberstoffes und Absenkung der Opazität ergeben den gleichen Effekt).EXAMPLE 1 3: A white polyamide active ingredient with a transparency of 70% with a white cellulose fleece with 30 g / m2, 1.5 denier, 60 mm pile, the same white filling 2 fleece, but only 50 g / m2 and a lower material with higher transparency underlaid and the layers are quilted together (low transparency of the Outer fabric and lowering the opacity produce the same effect).

Bei der bisherigen Erzeugung kam es sehr oft zu einem Durchsteigen der feinen Wattefasern durch das Obergewirke. Aus diesem Grunde wurde die Watte beidseitig besprüht, aber auch dadurch wurde das Durchsteigen der Fasern nicht völlig vermieden. Erfindungsgemäß kann nun auf einer Seite der Watte das Besprühen weggelassen werden, wobei auf Grund der dichten Zwischenlage (Non-woven) ein Durchsteigen der Fasern durch den Vliesstoff nicht mehr auftritt. With the previous generation there was very often a step through the fine wadding fibers through the upper knitted fabric. Because of this, the cotton wool Sprayed on both sides, but this also did not allow the fibers to climb through completely avoided. According to the invention, spraying can now be omitted on one side of the wadding be, where due to the dense intermediate layer (non-woven) The fibers no longer climb through the nonwoven.

Weitere Vorteile, Merkmale und Anwendungsmöglichkeiten der Erfindung ergeben sich aus der beiliegenden Darstellung eines Ausfthrungsbeispiels und aus der folgenden Beschreibung.Further advantages, features and possible uses of the invention result from the attached illustration of an exemplary embodiment and from the following description.

Die einzige Figur zeigt eine schematische Darstellung des Verbundstoffs.The single figure shows a schematic representation of the composite.

Der Verbundstoff 1 besteht aus einer Schicht 2 aus voluminösem Füllvlies oder Schaumstoff und ähnlichem.The composite 1 consists of a layer 2 of voluminous filling fleece or foam and the like.

Auf dieser ist eine weitere Vlies schicht 5 (Non-woven) angeordnet, die auf der dem Füllvlies abgewandten Seite gefärbt und/oder bedruckt ist, und aus einem transparenten Flächengebilde 4.On this another fleece layer 5 (non-woven) is arranged, which is colored and / or printed on the side facing away from the filling fleece, and off a transparent sheet 4.

Claims (3)

Patentansprüche: Patent claims: 0 Verbundstoff auf Vliesbasis in Kombination mit anderen Flächengebilden, wie Geweben, Gewirken, Schaumstoffschichten, Folien sowie transparenten Schichten, dadurch gekennzeichnet, daß er wenigstens eine Schicht aus einem voluminösen Füllvlies bzw. Schaumstoff u.ä. aufweist, auf welcher eine weitere Vliesschicht(Non-woven), vorzugsweise in der Grammatur von ca. 15 bis 50 g/m², angeordnet ist, welche Deckvliesschicht an ihrer vom erstgenannten Füllvlies abgewandten Seite vorzugsweise gefärbt und/oder bedruckt ist, wobei über dieser zweitgenannten Deckvliesschicht ein transparentes Flächengebilde, z.B. ein Gewebe, Gewirke oder eine Folie, angeordnet ist.0 composite based on fleece in combination with other fabrics, such as woven, knitted, foam layers, foils and transparent layers, characterized in that it has at least one layer of a voluminous filling fleece or foam, etc. has, on which a further non-woven layer, preferably in the grammage of approx. 15 to 50 g / m², which cover fleece layer preferably colored and / or on their side facing away from the first-mentioned filling fleece is printed, with a transparent over this second-mentioned cover fleece layer Flat structure, e.g. a woven fabric, knitted fabric or a film, is arranged. 2. Verbundstoff nach Anspruch 1, dadurch gekennzeichnet, daß das Deckvlies eine Leerfläche von höchstens 15 % (Opazität mindestens 85 %) aufweist.2. Composite according to claim 1, characterized in that the cover fleece has an empty area of at most 15% (opacity at least 85%). 3. Verbundstoff nach Anspruch 1, dadurch gekennzeichnet, daß das transparente Flächengebilde eine Leerfläche von mindestens 60 %, vorzugsweise 60 bis 85 %, aufweist.3. Composite according to claim 1, characterized in that the transparent Flat structure has an empty area of at least 60%, preferably 60 to 85%.
DE2440217A 1973-11-06 1974-08-22 Bonded laminate for clothing and foundation garments - from fleeces and non-wovens without surface consolidation or thick covers Pending DE2440217A1 (en)