DE2424207A1 - Bonded laminate components for construction and repair - composite details of various shapes easily assembled in situ. - Google Patents

Bonded laminate components for construction and repair - composite details of various shapes easily assembled in situ.

Info

Publication number
DE2424207A1
DE2424207A1 DE2424207A DE2424207A DE2424207A1 DE 2424207 A1 DE2424207 A1 DE 2424207A1 DE 2424207 A DE2424207 A DE 2424207A DE 2424207 A DE2424207 A DE 2424207A DE 2424207 A1 DE2424207 A1 DE 2424207A1
Authority
DE
Germany
Prior art keywords
main body
product
fibers
film
produced
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DE2424207A
Other languages
German (de)
Inventor
Alan David Mccroft
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BRISTOL COMPOSITE MATERIALS LT
Original Assignee
BRISTOL COMPOSITE MATERIALS LT
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BRISTOL COMPOSITE MATERIALS LT filed Critical BRISTOL COMPOSITE MATERIALS LT
Publication of DE2424207A1 publication Critical patent/DE2424207A1/en
Pending legal-status Critical Current

Abstract

Laminated components with which structures can be assembled or reinforced and repaired comprise a body and a covering layer. The body may be made from short fibres bonded with a thermoplastic or thermosetting resin formed possibly in a mould, or from continuous fibres laid out in a definite shape, possibly on a thermoplastic film, consolidated and covered by an outer layer of a meltable matl. The body of the component is then hardened without the covering layer being melted and is ready for storing or immediate use.

Description

Verfahren zum Herstellen von Laminaten Die Erfindung bezieht sich auf Verfahren zum Herstellen eines Erzeugnisses, das im wesentlichen aus Fasern und einer festen Matrix besteht, in welcher die Fasern liegen, und sie betrifft insbesondere Verfahren zum Herstellen von Erzeugnissen, bei denen die Matrix aus einem gehärteten Kunststoffmaterial besteht. Bis jetzt ist es beim Herstellen solcher Erzeugnisse in einem erheblichen Ausmaß erforderlich, aus Fasern bestehende Körper zu handhaben, die mit einem noch nicht gehärteten Harz imprägniert bzw. Methods of Making Laminates The invention relates to to methods of making an article consisting essentially of fibers and a solid matrix in which the fibers lie and concerns them in particular processes for the manufacture of products in which the matrix consists of a hardened plastic material. So far it is in manufacturing such Products to a significant extent require bodies made of fibers to handle which is impregnated or not yet hardened with a resin.

getränkt sind. Ferner müssen solche Erzeugnisse nachbehandelt bzw. gehärtet werden, was sich als zeitraubend erweisen kann, und außerdem kann es erforderlich sein, komplizierte Maßnahmen zu treffen, um eine ausreichende Verfestigung der Erzeugnisse während des Härtens zu gewährleisten, damit bei den gehärteten Erzeugnissen keine schwachen Stellen entstehen.are soaked. Furthermore, such products must be post-treated or hardening, which can be time consuming and also required be to take complicated measures to solidify the products sufficiently to ensure during hardening so that there are no in the hardened products weak spots arise.

Der Erfindung liegt die Aufgabe zugrunde, Verfahren zu schaffen, die es ermöglichen, die Herstellung von Erzeugnis der genannten Art erheblich zu vereinfachen. The invention is based on the object of creating methods which make it possible to considerably increase the production of products of the type mentioned simplify.

Gemäß der Erfindung werden aus Schichten aufgebaute Erzeugnisse bZwo sogenannte Laminate nach einem Verfahren hergestelltg das Maßnahmen umfaßt., um ein "Vorlaminat" herzustellen, zu dem ein Hauptkörper und eine Verkleidung dergleichen gehören, bei dem der üauptkörper aus masern besteht, welche mit einer Matrix aus einem ersten Material getränkt sind, das sich im noch nicht gehärteten Zustand befindet, während die Verkleidung aus einem schmelzbaren, in Berührung mit dem Hauptkörper bestehenden zweiten Alaterial besteht, und um eine Härtung des genannten ersten materials zu bewirken, ohne daß das zweite i;aterial zum Schmelzen gebracht wird, so daß der Hauptkörper fest wird und sich mit der Verkleidung verbindet. According to the invention, products made up of layers are bZwo so-called laminates produced by a process which comprises measures. To make a "prelaminate" to which a main body and a panel like that belong, in which the main body consists of grains, which are made with a matrix are soaked in a first material that is not yet hardened, while the fairing is made of a fusible, in contact with the main body existing second Almaterial, and a hardening of said first to effect materials without the second i; aterial being melted, so that the main body solidifies and connects to the fairing.

Die so hergestellten Stzeugnisse können dann verwendet werden, um Konstruktionen der gewünschten Art aufzubauen. The products so produced can then be used to Build constructions of the desired type.

Der Ausdruck "Erzeugnis" bezeichnet hier allgemein Produkte der verschiedensten Form, z.B. in Gestalt von Flachmaterialstücken, Bändern, geformten Bahnen und dergleichen. Die brzeugnisse sind fest, da sie eine gehärtete matrix enthalten, doch können sie in einem Ausmaß flexibel sein, das sich nach den Eigenschaften der Fasern und in einem geringeren Ausmaß nach den Eigenschaften der matrix richtet.The term "product" here generally designates a wide variety of products Form, e.g., in the form of pieces of sheet material, tapes, shaped sheets and the like. The products are solid because they contain a hardened matrix, but they can be flexible to an extent that depends on the properties of the fibers and in to a lesser extent depends on the properties of the matrix.

Soll eine bestimmte Konstruktion aufgebaut werden, wird ein mit Hilfe eines erfindungsgemäßen Verfahrens hergestelltes Erzeugnis so behandelt, daß das zweite Material, d.h. If a certain construction is to be built, a with the help a product manufactured according to the invention treated so that the second material, i.e.

das material der Verkleidung bzw. des bberzuges, unter solchen Bedingungen zum Schmelzen und dann wieder zum Erstarren gebracht wird, daß sie mit einem anderen ähnlichen oder andersartigen Erzeugnis oder einem 'lleil des gleichen Erzeugnisses verklebt wird.the material of the cladding or covering, under such conditions to melt and then solidify again that it is with another similar or different product or part of the same product is glued.

Die Erfinaung bietet verschiedene Vorteile. DieErzeugnisse haben eine einfachere Gestalt als aus solchen Erzeugnissen aufgebaute sOnstruktionen. Daher können die Einrichtungen zum Verfestigen der Erzeugnisse während des Härtens erheDlich einfacher sein als Einrichtungen, die man zum Häuten einer vollständigen KOnstruktion benötigen würde. The invention offers several advantages. The products have a simpler form than instructions built from such products. Therefore, the means for solidifying the products during hardening Considerably simpler than the facilities that can be used to skinning a full one Would need construction.

In vielen Fällen wird zum Schmelzen und Erstarrenlassen der Verkleidung weniger Zeit benötigt als für das Aushärten.In many cases, it will melt and solidify the cladding takes less time than curing.

bies bedeutet, daß solche Erzeugnisse gleichzeitig an mehreren Stellen hergestellt werden können, um das @@sgangsmaterial bereitzustellen, das einer einzigen Station zugeführt wird, an der die gewünschten Konstruktionen auf gebaut werden. Die Tatsache, daß die matrix während der Herstellung jedes Erzeugnisses gehärtet wird, bedeutet, daß die Fasern in jedem Erzeugnis zuverlässig in der gewünschten Lage gehalten werden und sich daher während des Aufbaues einer Konstruktion nicht verlagern können. Dies ist insbesondere dann von Bedeutung, wenn als Fasern zahlreiche parallele monofile Fäden verwendet werden. Die Tatsache, daß die Matrix gehärtet wird, bedeutet, daß die Erzeugnisse von schlaffem oder klebrigem Material völlig frei sind, so daß sie sich leicht handhaben lassen. Praktisch ist es mit Hilfe des erfindungsgemäßen Verfahrens möglich, jeweils einen starren, trockenen Körper herzustellen, auf dem sich die Verkleidung in Form eines Überzugs befindet, der aus einem Material besteht, welches die Bigenschaften eines nicht klebrigen Klebstoffs hat, der sich mittels Wärme aktivieren läßt0 Ferner können die Erzeugnisse eine praktisch unbegrenzte Lagerfähigkeit aufweisen, so daß sie bis zu ihrer Weiterverarbeitung beliebig lange eingelagert werden können.bies means that such products can be used in several places at the same time can be made to provide the raw material that is a single Station fed is based on the desired constructions be built. The fact that the matrix is used during the manufacture of each product is cured means that the fibers in any product are reliably in the desired Are kept in position and therefore not during the construction of a construction can relocate. This is particularly important when the fibers are numerous parallel monofilament threads are used. The fact that the matrix has hardened means that the products are completely limp or sticky are free so that they can be easily handled. It is practical with the help of the method according to the invention possible to produce a rigid, dry body in each case, on which the cladding is in the form of a cover made of one material consists, which has the properties of a non-tacky adhesive, which can be activated by means of heat0 Furthermore, the products can have a practically unlimited Have shelf life, so that they can be used for any length of time can be stored.

Als Matrixmaterialien kann man Kunststoffe der verschiedensten Art verwenden, z.B. thermoplastische harze wie Polysulphone und polyimide, modifizierte thermoplastische Harze wie Polyamide und Silicone sowie Duroplaste wie Spoxy- und Phenolharze. A wide variety of plastics can be used as matrix materials use, e.g. thermoplastic resins such as polysulphones and polyimides, modified thermoplastic resins such as polyamides and silicones as well as thermosets such as spoxy and Phenolic resins.

Die Erfindung läßt sich ferner bei Erzeugnissen anwenden, bei denen als Latrixinaterial Zement verwendet wird. The invention can also be applied to products in which cement is used as the latrixin material.

Das Härten kann durch Erwärmen bewirkt werden, doch kann auch die Möglichkeit bestehen, daß sich die Härtung unter Umgebungsbedingungen abspielt. Die Verfestigung bzw. The hardening can be effected by heating, but the There is a possibility that the hardening takes place under ambient conditions. The solidification or

Verdichtung kann durch Aufbringen eines erheblichen Drucks gefördert werden0 Bezüglich der thermoplastischen Harze bezeichnet der Ausdruck "Härtung" die Zunahme des Molekulargewichts, die bei bestimmten Temperaturen eintritt.Compaction can be promoted by applying considerable pressure 0 With regard to thermoplastic resins, the term "hardening" denotes the increase in molecular weight that occurs at certain temperatures.

Ferner lassen sich Fasern der verschiedensten Art verarbeiten, z.B. Fasern aus Lohlenstoff, Glas, Bor und metallen. besonderte Vorteile bietet das Verfahren nach der Erfindung bei Flachmaterialstücken oder Bändern, die aus genau ausgerichteten parallelen Kohlenstoffasern bestehen, denn es ist möglich, zu gewährleisten, daß die Fasern genau die gewünschte Lage einnehmen, und diese Lage bleibt auch beim nachfolgenden Aufbauen einer Konstruktion unverändert. Furthermore, fibers of various kinds can be processed, e.g. Fibers made from carbon, glass, boron and metals. The process offers particular advantages according to the invention in flat pieces of material or strips made of precisely aligned parallel carbon fibers exist because it is possible to ensure that the fibers take up exactly the desired position, and this position remains with the subsequent building of a construction unchanged.

Daher läßt sich ein optimales Verhältnis zwischen der Festigkeit und dem Gewichterreichen. Jedoch kann sich die Tatsache, daß eine Gewähr dafür besteht, daß sich die Lage der Fasern nicht ändert, auch dann als vorteilhaft erweisen, wenn die Fasern verfilzt oder zu einem Gewebe, einem Gestrick oder einem Gewirk verarbeitet werden.Therefore, an optimal relationship between the strength and reaching weight. However, the fact that there is a guarantee that that the position of the fibers does not change, also prove to be advantageous if the fibers felted or processed into a fabric, a knitted fabric or a knitted fabric will.

Die Verkleidung kann aus einem beliebigen material bestehen, mit dem sich die verstärkte Matrix verbinden läßt, und das in einem späteren Zeitpunkt dadurch zum Schmelzen gebracht werden kann, daß es auf eine Temperatur erhitzt wird, die erheblich über der Härtungstemperatur der matrix liegt. Es ist möglich, ein beliebiges thermoplastisches oder aber ein ungehärtetes oder nur teilweise gehärtetes Duroplastharz oder ein beliebiges metall zu verwenden, das bei einer niedrigen Temperatur schmiltt. The cladding can be made of any material, with which the reinforced matrix can be connected, and that at a later point in time can be made to melt by heating it to a temperature which is considerably higher than the hardening temperature of the matrix. It is possible to have a Any thermoplastic or an uncured or only partially cured one Use thermoset resin or any metal that works at a low temperature smiles.

Im letzteren Fall ist natürlich eine gute elektrische neitfähigkeit und eine hohe Wärmeleitfähigkeit gewährleistet.In the latter case there is of course good electrical conductivity and ensures high thermal conductivity.

Es lassen sich zahlreiche verschiedene Verfahren anwenden, um gemäß der Erfindung ein Erzeugnis der genannten Art herzustellen. Insbesondere können Ausgangsmaterialien in den verschiedensten Formen verwendet werden. There are a number of different methods that can be used to get acc the invention to produce a product of the type mentioned. In particular, can Starting materials can be used in a wide variety of forms.

Bei einem wichtigen Verfahren werden als Fasern endlose Fäden verwendet, und um das erwähnte Vorlaminat herzustellen, baut man einen Körper als zusammenhängendes Formteil auf, woraufhin man das zweite Material in Form eines Films verwendet, der dann in berührung mit dem Körper gebracht wird. In an important process, endless threads are used as fibers, and in order to produce the aforementioned prelaminate, a body is built as a coherent one Molded part, whereupon the second material is used in the form of a film, the then brought into contact with the body.

Bei einem anderen 73erfahren werden cls t-sere cri~ lose £äden verwendet, das Vorlaminat wird aß e- etl hängender Körper aufgebaut, und dann wird das zweite Material auf eine Fläche des Körpers aufgespritzt. In another experience, cls t-sere cri ~ loose threads are used, the prelaminate is ate-etl hanging body built up, and then the second material is sprayed onto a surface of the body.

Bei einem weiteren Verfahren wird das zweite klaterial in Form eines Films verwendet, die den Körper bildenden Fasern haben eine geringe Länge, um das Vorlaminat herzustellen, wird der Film auf einer Unterlage angeordnet, und dann wird ein Gemisch aus den Fasern und dem ersten Material auf die Oberseite des Films aufgebracht. In another method, the second material is in the form of a Films used, the fibers forming the body have a short length to the To make pre-laminate, the film is placed on a base, and then puts a mixture of the fibers and the first material on top of the film upset.

Bei einem weiteren Verfahren wird das zweite Material in Form eines Films verwendet, die den Körper bildenden Fasern haben eine geringe Länge, und das Vorlaminat wird in der Weise hergestellt, daß man dem Film eine nicht ebene Form bzw. eine räumliche Form gibt, woraufhin ein Gemisch aus den Fasern und dem ersten Material zur Anlage an dem Film gebracht wird. In another method, the second material is in the form of a Film used, the fibers forming the body have a short length, and that Prelaminate is made to give the film a non-planar shape or a spatial shape, whereupon a mixture of the fibers and the first Material is brought to bear on the film.

Zum Aufbauen einer Konstruktion lassen sich zahlreiche verschiedene Verfahren anwenden. Hierbei ist es möglich, Erzeugnisse zu verwenden, die sich bezüglich ihrer Form unterscheiden. There are many different ways to build a structure Apply procedure. It is possible to use products that relate to differ in their shape.

Bei einem Verfahren zum Aufbauen einer Konstruktion, bei dem ein einem Flachmaterial ähnelndes Erzeugnis verwendet wird, wird das Erzeugnis in die Form eines Rohrs gebracht, und die einander benachbarten Ränder des Erzeugnisses werden längs des Rohrs dadurch aneinander befestigt, daß das zweite Material im Bereich der ränder zum Schmelzen gebracht wird, woraufhin man das zweite Material erstarren läßt. In a method of building a structure in which a a product similar to a flat material is used, the product is included in the Formed a tube, and the adjacent edges of the product are attached to each other along the pipe by the fact that the second material in the The area of the edges is melted, whereupon the second material is applied freezes.

Bei einem weiteren Verfahren, bei dem ein bandähnliches Erzeugnis verwendet wird, wird das erzeugnis schraubenlinienförmig auf einen es tragenden Zylinder so aufgewickelt, daß sieh einander benachbarte Ränder aufeinander folgender VJindungen des Erzeugnisses überlappen, und diese sich überlappenden Ränder werden dadurch aneinander befestigtX daß man das zweite Material im Bereich der ränder zum Schmelzen bringt, woraufhin zugelassen wird, daß das material wieder erstarrt. In another method in which a tape-like product is used, the product is helical on a supporting it Cylinder wound so that you see adjacent edges of one another VJindings of the product overlap, and these overlapping edges become attached to each otherX by placing the second material in the area of the edges melts, whereupon the material frozen again.

Im folgenden sind im einzelnen mehrere Beispiele für erfindungsgemäße Verfahren zum Herstellen von aus Schichten aufgebauten brzeugnissen beschrieben. The following are several examples of the present invention in detail Process for the production of products composed of layers described.

Beispiel 1 Es wird ein Band mit einer Breite von etwa 400 mm und einer Dicke von etwa 0,125 mm hergestellt, das aus Kohlenstoffasern besteht, die mit einer ungehärteten hpoxyharzmatrix imprägniert werden. Als kohlenstoffasern werden die unter der gesetzlich geschützten Bezeichnung "Hyfil" erhältlichen Fasern verwendet, die von der hyfil Ltd., Avonmouth, England, bezogen werden können. Die Ihatrix besteht aus " Shell 828 resin "(Harz) und "Shell DDS hardener" (Härter), die beide von der Shell Chemicals U.K.Example 1 It is a tape with a width of about 400 mm and a Thickness of about 0.125 mm, which consists of carbon fibers with a uncured HPoxy resin matrix are impregnated. As carbon fibers, the uses fibers available under the legally protected name "Hyfil", which can be obtained from hyfil Ltd., Avonmouth, England. The ihatrix exists made of "Shell 828 resin" (resin) and "Shell DDS hardener" (hardener), both from the Shell Chemicals U.K.

Ltd., London, England, bezogen werden können. Die Fasern werden in der Längsrichtung des Bandes genau ausgerichtet.Ltd., London, England. The fibers are in precisely aligned with the longitudinal direction of the belt.

Eine Flachseite des Bandes wird in Flächenberührung mit einem Nylonharzfilm mit einer Dicke von etwa 0,025 mm gebracht, und sämtliche Teile des so hergestellten Vorlaminats werden 60 min lang einer Temperatur von 1800 C und einem Druck von etwa 480 kN/m2 ausgesetzt. Bei dieser Temperatur wird das Epoxyharz gehärtet, doch wird das lXylonharz nicht zum Schmelzen gebracht.One flat side of the tape is in face-to-face contact with a nylon resin film brought with a thickness of about 0.025 mm, and all parts of the so produced Vorlaminats are 60 minutes at a temperature of 1800 C and a pressure of about 480 kN / m2 exposed. At this temperature the epoxy resin is cured, but will did not melt the nylon resin.

Beispiel 2 Ein gemäß dem Beispiel 1 hergestelltes Band aus Kohlenstoffasern wird mit einem phenolharz imprägniert. Beide Flachseiten des Bandes werden in Flächenberührung mit zugehörigen Flachmaterialstücken aus Lotfolie gebracht, die eine Dicke von etwa 0,025 mm haben, und das Phenolharz wird dann 30 min lang bei 1500 C und unter der Wirkung eines Drucks von etwa 700 kN/m2 gehärtet.Example 2 A tape made according to Example 1 made of carbon fibers is impregnated with a phenolic resin. Both flat sides of the tape are in surface contact Brought with associated pieces of flat material made of solder foil, which has a thickness of about 0.025 mm, and the phenolic resin is then 30 minutes at 1500 C and below Hardened effect of a pressure of about 700 kN / m2.

Beispiel 3 Ein Band, das in allen Punkten dem Beispiel 1 entspricht, wird auf einer Flachseite mit einer Auf auge aus pulverförmigem Nylonharz versehen, die durch ufsritzen oder elektrostatisches Niederschlagen oder mit Hilfe eines beliebigen anderen Verfahrens zum Aufbringen eines Pulvers aufgebracht wird. Das so hergestellte Vorlaminat wird dann zwischen beheizten Walzen hindurchgeführt, die bewirken, daß das Epoxyharz gehärtet und das Nylonpulver mit dem Band verbunden wird.Example 3 A tape that corresponds to example 1 in all points, is provided with an eye made of powdery nylon resin on one flat side, the through cracks or electrostatic deposition or with Any other method of applying a powder is applied will. The pre-laminate produced in this way is then passed between heated rollers, which cause the epoxy resin to cure and bond the nylon powder to the tape will.

Beispiel 4 Ein Film aus Nylonharz wird auf einem langgestreckten Formkörper angeordnet, der einen hutförmigen Querschnitt hat. Dann wird eine eine im wesentlichen gleichmäßige Dicke aufweisende Schicht einer zum Formen eines Flachmaterials dienenden Masse, die sich aus zerkleinerten Glasfasern zusammensetzt, welche mit einem Polyesterharz imprägniert sind, auf den Film aufgelegt und dann mit einem evakuierbaren Beutel bedeckt. Die Zuluft wird aus dem Raum zwischen dem Beutel und dem Formkörper abgesaugt, so daß das Vorlaminat bei atmosphärischem Druck verdichtet wird, und es wird dem Polyesterharz ermöglicht, bei Raumtemperatur auszuhärten. Das so hergestellte Erzeugnis ist geeignet, als Verstärkungsrippe mit einem kastenförmigen Querschnitt an einer Fläche, z.B. der Unterseite einer Bodentafel eines Flugzeugs, befestigt zu werden.Example 4 A film of nylon resin is formed on an elongated molded article arranged, which has a hat-shaped cross section. Then one becomes essentially one A layer of uniform thickness used for forming a flat material Mass composed of crushed glass fibers, which are coated with a polyester resin are impregnated, placed on the film and then with an evacuable bag covered. The supply air is sucked out of the space between the bag and the molded body, so that the prelaminate is densified at atmospheric pressure and it becomes the Polyester resin enables curing at room temperature. The product made in this way is suitable as a reinforcing rib with a box-shaped cross-section on one Surface, e.g. the underside of an aircraft floor panel.

Gemäß der Erfindung hergestellte Brzeugnisse können nicht nur zum Aufbauen von Konstruktionen verwendet werden, sondern sie ermöglichen auch ein schnelles Instandsetzen oder verstärken schon'vorhandener Konstruktionen. Hierbei ist es nur erforderlich, das Erzeugnis an der gewünschten Stelle zu befestigen und zu diesem Zweck den bzw. jeden ueberzug zeitweilig zum Schmelzen zu bringen. Products produced according to the invention can not only be used for Building constructions are used, but they also allow a quick Repair or strengthen existing structures. Here it is only required to attach the product to the desired location and to this Purpose to temporarily melt the or each coating.

Soll z.B. die Beplankung einer Tafel aus einer geschichteten Konstruktion mit einem abenmaterial repariert werden, wird die beschädigte 'läche und ihre Umgebung mit einem Flachmaterialstück bedeckt, das nach dem Beispiel 1 hergestellt worden ist, und um dieses Blachmaterialstück zu befestigen, wird es mit einem heißen Glättungswerkzeug aus Eisen angedrückt. Eine Verstärkung, die gemäß dem Beispiel 4 hergestellt worden ist, wird befestigt, dem man eine heiße Rolle über die Flansche des Profils führt, das einen hutförmigen Querschnitt hat. Should e.g. the paneling of a board made of a layered construction repaired with a material, the damaged area and its surroundings will be repaired covered with a piece of sheet material which was produced according to Example 1 is, and to secure this piece of sheet material, it is done with a hot smoothing tool pressed on from iron. A reinforcement made according to Example 4 is attached to which one is hot Roll over the flanges of the profile, which has a hat-shaped cross-section.

Da die Lberzüge sehr dünn sein können, führt das Vorhandensein des zweiten luaterials nicht zu einer bemerkbarren Beeinträchtigung der festigkeit und Steifigkeit der betreffenden Konstruktion. Des zweite Material wird vorzugsweise so gewählt, daß seine Scherfestigkeit in der gleichen Größenordnung liegt wie diejenige des ersten Materials, nachdem es gehärtet worden ist. Since the skin can be very thin, the presence of the Second luaterials do not cause a noticeable deterioration in strength and Rigidity of the construction in question. The second material is preferred chosen so that its shear strength is in the same order of magnitude as that of the first material after it has been hardened.

Es ist möglich, mehrere gemäß dem Beispiel 2 hergestellte Erzeugnisse aufeinanderzulegen und sie dadurch aneinander zu befestigen, daß man sie zwischen Walzen hindurchführt, durch die ein hochfrequenter elektrischer Strom geleitet wird, so daß das bot zeitweilig zum Schmelzen gebracht wird. Als Endprodukt erhält man hierbei ein leitfähiges Laminat, das z.B. bei einem Wirbelstrommotor verwendet werden kann. It is possible to produce several products according to example 2 put one on top of the other and fix them together by placing them between Rolls through which a high-frequency electric current is passed, so that the bot is temporarily melted. The end product is obtained here a conductive laminate that is used, for example, in an eddy current motor can.

Die Verkleidungen oder überzüge können auch auf andere Weise erhitzt werden, z.B. mit Hilfe von Ultraschallstrahlung. The linings or coatings can also be heated in other ways e.g. with the help of ultrasonic radiation.

Vorstehend wurde bereits die Verarbeitung eines Erzeugnisses in Gestalt eines Flachmaterials zu einem Rohr behandelt. wird ein Rohr von großer Länge benötigt, kann das Erzeugnis so gestaltet werden, daß es stärker einem Band ähnelt, und man kann das Erzeugnis dadurch in die gewünschte Form bringen, daß man es durch ein Werkzeug zieht, welches das flachliegende Band so verformt, daß es einen kreisrunden Querschnitt derart annimmt, daß sich seine Längsränder überlappen. The processing of a product has already been given in the foregoing of a flat material treated to form a tube. if a pipe of great length is required, the product can be made to resemble a ribbon more closely, and you the product can be brought into the desired shape by inserting it through a Tool pulls, which deforms the flat tape so that it becomes circular Assumes cross-section such that its longitudinal edges overlap.

Ferner wurde bereits erwähnt, daß es möglich ist, ein bandähnliches Erzeugnis schraubenlinienförmig auf einen Zylinder aufzuwickeln. Bei dem Zylinder kann es sich um einen Dorn handeln, doch benutzt man vorzugsweise ein rohr, das nach dem im vorstehenden Absatz behriebenen Verfahren hergestellt worden ist. In diesem Fall werden die Windungen des schraubenlinienförmig aufgewickelten Bandes nicht nur miteinander, sondern auch direkt mit dem Rohr verbunden. It has also already been mentioned that it is possible to use a tape-like Wind the product helically on a cylinder. By the cylinder it can be a mandrel, but it is preferable to use a tube that has been manufactured according to the process described in the previous paragraph. In this case will be the turns of the helically wound Band not only connected to each other, but also directly to the pipe.

Alternativ kann man ein solches hohr mit schraubenlinienförmigen Windungen aus "nassen" Fäden bedeckten, d.h. Alternatively, you can have such a hohr with helical lines Turns of "wet" threads covered, i.e.

aus Fäden, die mit ungehärtetem Harz imprägniert sind, das nach dem Aufwickeln der Fäden gehärtet wird0 Patentansprüche:made of threads impregnated with uncured resin, which after the Winding of the threads is hardened

Claims (8)

P Ä P A T E N T A N S P R Ü C H E Ti A ii 5 P R U C H E 1. Verfahren zum Herstellen eines Erzeugnisses in Enorm eines Laminats, dadurch g e k e n n z e i c h n e t , daß ein Vorlaminat hergestellt wird, das einen Hauptkörper und einen bberzug aufweist, bei dem der Hauptkörper aus Fasern besteht, die mit einer Matrix aus einem ersten Material im ungehärteten Zustand imprägniert sind, während der Uberzug aus einem in beruhrung mit dem Hauptkörper bestehenden schmelzbaren zweiten Material besteht, und daß dann das erste Material gehärtet wird, ohne daß das zweite Material zum Schmelzen gebracht wird, so daß der hauptkörper fest und mit dem tterzug verbunden wird. PÄ P A T E N T A N S P R Ü C H E Ti A ii 5 P R U C H E 1. Procedure to manufacture a product in the enormous size of a laminate, thereby g e k e n n z E i n e t that a prelaminate is made which has a main body and a Has covering in which the main body is made up of fibers bonded with a matrix impregnated from a first material in the uncured state, during the Coating of a second fusible in contact with the main body Material consists, and that then the first material is hardened without the second Material is melted so that the main body is solid and with the pull is connected. 2. Verfahren nach Anspruch 1, dadurch g e k e n n -z e i c h n e t , daß als Fasern andlose Fäden verwendet werden, und daß das Vorlaminat dadurch erzeugt wird, daß der Hauptkörper als zusammenhängender Formkörper hergestellt wird, daß das zweite Material in Form eines Films bereitgestellt wird, und daß dieser Film dann in Berührung mit dem Hauptkörper gebracht wird.2. The method according to claim 1, characterized in that g e k e n n -z e i c h n e t that as fibers andlose threads are used, and that the prelaminate thereby is generated that the main body is produced as a coherent molded body, that the second material is provided in the form of a film, and that this Film is then brought into contact with the main body. 3. Verfahren nach Anspruch 1, dadurch g e k e n n -z e i c h n e t , daß als Fasern endlose Fäden verwendet werden, und daß das Vorlaminat in der Weise erzeugt wird, daß der Hauptkörper als zusammenhängendes Formteil hergestellt wird, und daß dann das zweite laterial auf eine Fläche des Hauptkörpers aufgespritzt wird. 3. The method according to claim 1, characterized in that g e k e n n -z e i c h n e t that continuous filaments are used as fibers, and that the prelaminate in the Is produced way that the main body is made as a coherent molded part and that the second material is then sprayed onto a surface of the main body will. 4. Verfahren nach Anspruch 1, dadurch g e k e n n -z e i c h n e t , daß das zweite Material in Form eines Films verwendet wird, daß die masern des Hauptkörpers eine geringe Länge haben, und daß das Vorlaminat derart erzeugt wird, daß der Film auf einer Unterlage angeordnet wird, und daß dann ein Gemisch aus den Fasern und dem ersten Material auf die Oberseite des Films aufgebracht wird.4. The method according to claim 1, characterized in that g e k e n n -z e i c h n e t that the second material is used in the form of a film that the grain of the Main body have a short length, and that the prelaminate is produced in such a way that that the film is placed on a base, and that then a mixture of the Fibers and the first Material applied to the top of the film will. 5. Verfahren nach Anspruch 1, dadurch g e k e n n z e i c h n e t , daß das zweite Itlaterial in Form eines Films verwendet wird, daß die Fasern des Hauptkörpers eine geringe Länge haben, und daß das Vorlaminat derart erzeugt wird, daß dem Film eine räumliche Form gegeben wird, und daß dann ein Gemisch aus den Fasern und dem ersten ltaterial auf den Film aufgebracht wird0 5. The method according to claim 1, characterized g e k e n n z e i c h n e t that the second material is used in the form of a film that the fibers of the Main body have a short length, and that the prelaminate is produced in such a way that that the film is given a spatial shape, and that then a mixture of the Fibers and the first oil material is applied to the film0 6. Verfahren zum Aufbauen einer xonstruktBon unter Verwendung eines einem Flachmaterial ähnelnden Erzeugnisses, das mittels eines Verfahrens nach einem der Ansprüche 1 bis 5 hergestellt worden ist, dadurch g e k e n n -z e i c h n e t , daß das erzeugnis in die Form tees Rohres gebracht wird, und daß einander benachbarte Ränder des Erzeugnisses längs des Rohrs dadurch aneinander befestigt werden, daß das zweite Material im Bereich der Ränder zum Schmelzen und dann zum Erstarren gebracht wird.6. Procedure for Build an xonstruktBon using a flat material Product manufactured by means of a method according to one of Claims 1 to 5 has been given by the fact that the product is in the form tees pipe is brought, and that adjacent edges of the product are attached to each other along the pipe by the fact that the second material in the The area of the edges is melted and then solidified. 7. Verfahren zum Aufbauen einer Konstruktion unter Verwendung eines einem Band ähnelnden Erzeugnisses, das mittels eines Verfahrens aach einem der Ansprüche 1 bis 5 hergestellt worden ist, dadurch g e k e n n z e i c h -n e t , daß das Erzeugnis schraubenlinienförmig auf einen Zylinder so aufgewickelt wird, daß sich die einander benachbarten Ränder aufeinander folgender Windungen des Erzeugnisses überlappen, und daß die Windungen dadurch aneinander befestigt werden, daß das zweite Material im Bereich der Ränder zuerst zum Schmelzen und dann zum Erstarren gebracht wird.7. Method of building a structure using a A product resembling a band, which by means of a method according to one of the claims 1 to 5 has been produced, thereby g e k e n n n z e i c h -n e t that the product is wound helically on a cylinder so that the each other overlap adjacent edges of successive turns of the product, and in that the turns are secured together by the second material in the area of the edges is first made to melt and then to solidify. 8. Verfahren nach Anspruch 6 und 7, dadurch g e k e n n -z e i c h n e t , daß ein gemäß Anspruch 6 hergestelltes Rohr bei dem Verfahren nach Anspruch 7 als tragender Zylinder verwendet wird, so daß die durch das Band gebildeten windungen auch direkt an dem Rohr befestigt werden.8. The method according to claim 6 and 7, characterized in that g e k e n n -z e i c h n e t that a pipe produced according to claim 6 in the method according to claim 7 is used as a supporting cylinder, so that the turns formed by the tape can also be attached directly to the pipe.
DE2424207A 1973-05-22 1974-05-17 Bonded laminate components for construction and repair - composite details of various shapes easily assembled in situ. Pending DE2424207A1 (en)