DE2300513C3

DE2300513C3 - Process for the production of blast furnace slag of uniform composition, which is to be used in particular for glass production

Info

Publication number: DE2300513C3
Application number: DE19732300513
Authority: DE
Inventors: Raymond H. Yardley Pa. Evans (V.St.A.)
Original assignee: The Calumite Co. Europe, Antwerpen (Belgien)
Priority date: 1972-01-07
Filing date: 1973-01-05
Publication date: 1976-08-19

Description

ÄTcSerg senkrecht zn den horizontalen .5 tehe "„el ^e, ^ ^f_nStÄTcSerg perpendicular to the horizontal .5 tehe "" el ^ e, ^ ^ f _n St

Schichten Schlacke abgenommen wird. Sodiotoschlacke nach diesem Verfahren nichtLayers of slag are removed. Sodio slag after this process does not

Lä^ft^e^ÄÄzeÄ4: vegleich-ige- _{Aufgabe ist} Lä ^f t ^e ^ ÄÄzeÄ4: the same _{task is}

M«.er übereinander- ^*«,«,. _2U ⁸ _5ε&η ein^gta-_Ä ·^
-Spruch 1 ode, ₂ dadurchM «.er one on top of the other- ^ *«, «,. _2U ⁸ _5ε & η a ^ gta- _Ä · ^
- Say 1 or ₂ thereby

in Gewich,_Sp,ozen,=n durch_g=mh_n *„d. g ^Ä^in Gewich, _Sp , ozen, = n by _g = mh _n * “d. g ^ Ä ^

20 bis 50·/. ^^'"^„"unMmengen ve,schiedencr Chargen20 to 50 · /. ^^ '"^" "Lots of different batches

15 bis 650/0 2 Sttens drei solche Schichten übereinander-15 to 650/0 2 three such layers on top of each other

Seäsiä=ässsSeäsiä = ässs

_FeO 0,1 bis 5,0·/. ^"'"Xch. zu den horizontalen _FeO 0.1 to 5.0 · /. ^ "'" Xch. to the horizontal

: :0 bis 13,0,. »abgenommene ^ ^^:: 0 to 13.0 ,. »Removed ^ ^^

0 bis W* , ^S0 to W * , ^ S

sehen «ta Untermengen der Chargen und damit der Chargen selbst erhalten. Dabei wird durch die Ver-6o teSuS einei Charge auf mehrere Felder einer Schicht da Auf chichten eines Schlackenberges nur unwesentHch oder gar nicht verteuert. Durch das Abtragen des Schlackenberges senkrecht zu den honzonu . ι iaipn Schichten wird zudem eine zusatzliche Vermi-see «ta subsets of the batches and thus the Receive batches yourself. The Ver-6o TeSuS one batch on several fields of one shift since the layers of a mountain of cinder are only insignificant or not at all expensive. By removing the mountain of cinder perpendicular to the honzonu . ι iaipn layers is also an additional reduction

Die Erfindung betrifft ein Verfahren zur Herstel- ^ Schichten w. ^ _nachrutscht.The invention relates to a method for manufacturing ^ layers w. ^ _Nachrutscht .

lune von Hochofenschlacke vergleichmaßigter Zu- 65 saling ern , _{fi d maßen} Verfahren ver-lune of blast furnace slag from standardized feeders, _{fi d measured} processes

sammeSsetzung, die insbesondere zur Glasherste ung τ*™*^^^** genügt den hohenComposition, particularly for glass production τ * ™ * ^^^ ** satisfies the high

ÄÄ^ ^{tforderuneen an glcichbleibende} "ÄÄ ^ ^{requirements for consistent} "

23 OO 51323 OO 513

:ung, die von zum Herstellen von Glas verwendeter iochofenschlacke zu erfüllen sind. Dort haben ichon Schwankungen der Zusammensetzung von weliger als einem Bruchteil eines Prozentes einen Ein- !uß auf die Farbe, die Qualität und die physikalischen Eigenschaften des Glases und der aus ihm hergestellten Erzeugnisse. Bisher war es nicht möglich, Hochofenschlacke in großen Mengen zur industriellen Glasherstellung zu verwenden, da die Zusammensetzung der als Nebenprodukt im Hochofen anfallenden Hochofenschlacke je nach dem verwendeten Eisenerz und den zur Verhüttung desselben erforderlichen Koks- und Flußmittelzuschiägen sowie den Betriebsbedingungen des Hochofens sogar bei ein und demselben Hochofen beträchtlichen Schwankungen unterliegt. Bei dem erfindungsgemäßen Verfahren werden nun die innerhalb eines vorgegebenen Schwankungsbereiches ihrer Zusammensetzung nach für die Glasherstellung geeigneten Hochofenschlacken ausgewählt und durch das oben beschriebene Ablagern und Abtragen so gut vergleichmäßigt, daß eine stetige Glasherstellung in industriellem Ausmaße unter Verwendung der vergleichmäßigten Hochofenschlacke möglich ist, ohne daß die der Glasschmelze zuzusetzenden Zuschläge stündlich oder täglich geändert werden müssen, um hierdurch Schwankungen in der Zusammensetzung der verwendeten Hochofenschlacke auszugleichen.: ung to be met by furnace slag used for making glass. Have there Ion fluctuations in the composition of less than a fraction of a percent It affects the color, quality and physical properties of the glass and that made from it Products. So far it was not possible to use blast furnace slag in large quantities for industrial purposes To use glass production, as the composition of the by-product in the blast furnace Blast furnace slag depending on the iron ore used and that required to smelt it Coke and flux additives and the operating conditions of the blast furnace even at a and the same furnace is subject to considerable fluctuations. In the method according to the invention are now within a given range of fluctuation according to their composition Blast furnace slag suitable for glass production is selected and deposited by the above-described process and erosion so well uniform that glass production on an industrial scale is steady using the equalized blast furnace slag is possible without that of the molten glass Surcharges to be added must be changed hourly or daily to avoid fluctuations balance in the composition of the blast furnace slag used.

Bevorzugt werden zwischen drei und zehn Schichten mit schachbrettartigem Muster übereinandergelegt. In dem erhaltenen Schlackenberg weist keine der abgelegten Untermengen die gleiche Zusammensetzung wie eine andere daneben-, darüber- oder darunterliegende Untermenge auf.Preferably between three and ten layers with a checkerboard pattern are placed one on top of the other. In the mountain of slag obtained, none of the deposited subsets has the same composition like another subset next to, above, or below.

Weitere vorteilhafte Ausbildungen dir Erfindung sind in weiteren Unteransprüchen angegeben.Further advantageous developments of the invention are specified in further subclaims.

Das Abtragen des Schlackenberges kann mittels eines Löffelbaggers oder einer anderen Vorrichtung in senkrechter Richtung, d. h. quer zu den horizontalen Schichten des Schlackenberges, erfolgen. Die so abgetragene Hochofenschlacke enthält Anteile verschiedener Charge, deren jeweilige Zusammensetzung innerhalb ei'ies vorgegebenen Schwankungsbereiches lag. Wiesen die abgelagerten Untermengen der Chargen Partikeln mit einem Durchmesser von 0,5 bis 10 cm auf, um die Durchmischung und die Verwitterung zu fördern, so kann die vom Schlackenberg abgetragene Hochofenschlacke noch weiter vermählen werden und — falls erforderlich — über einen Magnetabscheider geführt werden. Die gemahlene Hochofenschlacke vergleichmäßigter Zusammensetzung wird dann zur Glasherstellung verwendet.The slag dump can be removed using a backhoe or some other device in the vertical direction, d. H. across the horizontal layers of the slag mountain. The so removed blast furnace slag contains proportions of different batches, their respective composition was within a specified range of fluctuation. Had the deposited subsets of the batches Particles with a diameter of 0.5 to 10 cm to prevent mixing and weathering to promote, the blast furnace slag removed from the slag mountain can grind even further and - if necessary - passed through a magnetic separator. The ground blast furnace slag more uniform composition is then used for glass production.

Im folgenden wird die Erfindung an Hand eines Ausführungsbeispieles und unter Bezugnahme auf die Zeichnung näher erläutert. In dieser zeigtIn the following the invention on the basis of an exemplary embodiment and with reference to the Drawing explained in more detail. In this shows

F i g. 1 eine Aufsicht auf die Felder einer Schicht, in der Untermengen zweier Chargen abgelegt sind,F i g. 1 a plan view of the fields of a layer, in which subsets of two batches are stored,

F i g. 2 einen transveisalen Schnitt durch einen mehrere schachbrettartige Schichten aufweisenden Schlackenberg,F i g. 2 shows a transveisal section through a layer having several checkerboard-like layers Slag mountain,

F i g. 3 eine schematische Ansicht, in der das Abtragen der Hochofenschlacke von einem Schlackenberg dargestellt ist undF i g. 3 is a schematic view in which the removal of the blast furnace slag from a mountain of slag is shown and

F i g. 4 bis 7 grafisiche Darstellungen der Schwankung in der Zusammensetzung der Schichten und in der Zusammenstellung der abgetragenen Hochofenschlacke. F i g. 4 to 7 graphical representations of the variation in the composition of the layers and in the composition of the removed blast furnace slag.

F)ie zu vorwendenden Hochofenschlacken können zunächst von unterschiedlichen Hochöfen und verschiedenen Orten kommen; sie können ferner aus Schlakkeagruben entnommen sein, in denen die Schlacken luftgekühlt wurden, oder sie können in Form von S »Klinkern« vorliegen, die dadurch hergestellt wurden, daß die Schlacke in Wasser geworfen wurde, oder die Schlacke kann geschäumt sein, wie dies der Fall ist, wenn die geschmolzene Schlacke einem Wasser-Sprühstrahl ausgesetzt wird, wenn sie von einer Gießpfanne in eine Schlackengrube gegossen wird.F) he blast furnace slag to be used can initially come from different blast furnaces and different locations; they can also mine from Schlakkea be taken in which the slags have been air-cooled, or they can be in the form of S "clinkers" are present that have been produced by throwing the slag into water, or the Slag can be foamed, as is the case when the molten slag is sprayed with water exposed when poured from a ladle into a cinder pit.

In jedem Fall wird die zu verwendende Schlacke analysiert, und es werden die Schlacken oder Schlakken-Chargen ausgewählt, deren Zusammensetzung innerhalb eines vorgegebenen Schwankungsbereichs liegt. Der Bereich der Zusammensetzung der zur Verwendung ausgewählten Schlacken ist in Gewichtsprozenten vorzugsweise wie folgt:In each case the slag to be used is analyzed and it becomes the slag or slag batches selected, the composition of which is within a given range of fluctuation located. The range of composition of the slags selected for use is in percent by weight preferably as follows:

SiO₂ 20 bis5O°/oSiO ₂ 20 to 50%

Al₂O₃+ TiO₂ 2 bis30»/„Al ₂ O ₃ + TiO ₂ 2 to 30 »/„

CaO 15 bis 65%CaO 15 to 65%

MgO 0 bis26°/oMgO 0 to 26%

Fe₂O₃ 0,1 bis 5,0'/OFe ₂ O ₃ 0.1 to 5.0 '/ O

MnO 0 bis 13,0·/»MnO 0 to 13.0 / »

Ma₂O+ K₂O 0 bis 5,0%Ma ₂ O + K ₂ O 0 to 5.0%

SO₃ 0 bis 3,0%SO ₃ 0 to 3.0%

S" 0 bis 3,0%S "0 to 3.0%

Freies Eisen + magnetisicr-Free iron + magnetisicr-

bares Material 0,7 %available material 0.7%

Um die Auswahl der Schlacken mit einer Zusammensetzung innerhalb des angegebenen Bereiches zu erleichtern, wird üblicherweise vom Bedienungsmann des Hochofens ein »Beschickungsformular« angefordert, in dem die Mengen und Eigenschaften des Eisenerzes, des Kokses, des Kalksteins und anderer Rohmaterialien, mit denen der Hochofen beschickt wurde, sowie Angaben über den Betriebsverlauf des Hochofens während der Zeitdauer, in der Schlacke erzeugt wird, aufgeführt sind. Eine tägliche, vom Stahlwerk vorgenommene Analyse der Schlacke wird ebenfalls angezogen, um die Auswahl der zu verwendenden Schlacken zu erleichtern und eine Vonussage über jede merkliche, zu erwartende Änderung in der Schlackenzusammensetzung zu vermitteln.To make the selection of slags with a composition within the specified range make it easier, the operator of the blast furnace usually requests a »loading form«, in which the quantities and properties of iron ore, coke, limestone and others Raw materials with which the blast furnace was charged, as well as information about the operating history of the Blast furnace during the period in which slag is generated are listed. A daily, dated Analysis of the slag made by steel mills is also attracted to the selection of which to use To facilitate slag and a statement of every noticeable, expected change to convey in the slag composition.

Die von dem Beschickungsformular und der Schlackenanalyse erhaltenen Informationen ermöglichen es dem Verbraucher festzustellen, ob irgendwelche Änderungen in der Schlackenzusammen-Setzung vorübergehend oder von längerer Dauer sind und ob die von irgendeinem Hochofen kommende Schlacke teilweise oder gänzlich verwendet werder kann oder unbrauchbar ist. Die Schlacken werder ferner einer Sichtkontrolle unterworfen, um das Vor handensein von Fremdstoffen wie Schamottestein Abfallstahl, unverbranntem Koks, Kalkstein od. dgl auszuschließen. Gewöhnlich eignen sich lediglicl etwa 25 % der von einem Hochofen erzeugte] Gesamt-Schlackenmenge zur Durchführung de Erfindung.Allow the information obtained from the loading form and slag analysis it allows the consumer to determine if there are any changes in the slag composition are temporary or of longer duration and whether they come from any blast furnace Part or all of the slag can be used or is unusable. The slag will be also subjected to a visual inspection to ensure that foreign matter such as firebrick is present Exclude waste steel, unburned coke, limestone or the like. Usually only about 25% of the total amount of slag produced by a blast furnace to carry out de Invention.

Die auf diese Weise als verwendungsfähig ausgc wählten Schlacken werden von der Sammelgrube en' nommen, in Stücke geschlagen und zerkleinert, 3The slag selected as usable in this way is removed from the sump. taken, chopped into pieces and chopped up, 3

23 OO 51323 OO 513

~~ DD.

daß ein Produkt entsteht, das aus SchlackcnsUicken gelegt, so daß ein Schlackenberg entsteht. Der herin der Größe zwischen etwa 0,6 bis 7,5 oder 10 cm gestellte Schlackenberg kann somit insgesamt zwibesteht, wobei die Hauptmenge der Schlackenstücke sehen etwa 30 000 und 50 000 t Schlacke enthalten vorzugsweise eine Größe von etwa 5 cm hat. Die Jc größer der Lagerplatz ist, desto mehr Charger auf diese Weise aufbereitete Schlacke kann ferner ι :,\~ύ zur Herstellung jeder Schlackcnschicht crfordcrüber einen Magnetabscheider geführt werden, um lieh und desto langer dauert es, den gesamten, aus zumindest einen Teil des in der Schlacke vornan- zahlreichen Schichten bestehenden Schlackenberg denen freien Eisens oder magnetisierbaren Materials aufzubauen. So kann die Herstellung eines derartigen zu entfernen. Schlackenberges drei oder vier Monate dauern, und Daraufhin wird die Schlacke zu einem Lagerplatz 4 io in dieser Zeit ist die Schlacke Witterungseinflüssen geführt, und es werden, wie Fig. 1 zeigt, nachein- ausgesetzt, und jede Schlackenschicht kann ein oder ander Untermengen einer Charge innerhalb des zwei Wochen lang dem Einfluß von Luft oder Regen Lagerplatzes in auf Abstand gehaltenen Feldern 2 ausgesetzt sein, bevor sie durch die nächste Schlak- und 6 bis 14 abgelegt. So kann die erste Untermenge kenschicht bedeckt wird. Infolgedessen kann zuminim Feld 2, die zweite Untermenge im Feld 6, die 15 dest ein Teil der in der Schlacke enthaltenen Stalfide dritte Untermenge im Feld 8 usw. abgelegt werden, in Sulfate umgewandelt werden, und eine Schlacke, bis die gesamte ausgewählte Charge den an einem die zunächst 0,9 °/o Sulfide enthält, kann dann einen einzigen Tag oder von einer einzigen Beschickung Sulfatgehalt von 0,8 Vo haben. Während der Vereines Hochofens erzeugten und aufbereiteten Schlacke Witterung der Schlacke sucht ferner jegliches frei an auf Abstand gehaltenen Feldern des Lagerplatzes 20 vorhandene Eisen zu oxydieren,
abgelegt worden ist. Anschließend werden andere Der gesamte, auf diese Weise hergestellte Schlak-Untermengen von Chargen, die an anderen Tagen, kenberg besteht aus einer Vielzahl von Schlackenzu anderen Zeitpunkten oder von anderen Schlacken- Untermengen, deren Zusammensetzung sich jeweils quellen ausgewählt wurden, in weiteren, auf Abstand mehr oder weniger von der Zusammensetzung irgendgehaltenen Feldern des Lagerplatzes abgelegt, bei- 25 einer anderen, entweder ir, der gleichen Schicht oder spielsweise den Feldern 10,12,14 usw. irgendeiner darüber- oder darunterliegenden Schicht Auf diese Weise werden die Untermengen der liegenden benachbarten Untermenge unterscheidet. Chargen auf dem Lagerplatz im wesentlichen schach- Darüber hinaus bildet jede Untermenge lediglich brettartig abgelegt, und zwar derart, daß die Unter- einen geringen Teil der auf dem Lagerplatz abgemengen der Schlacke, die an einem einzigen Tag 30 legten Schlacken-Gesamtmenge. Wenn die abgelegte erhalten werden oder die im wesentlichen die gleiche Schlacke zur Glasherstellung benötigt wird, wird Zusammensetzung haben, jeweils im Lagerplatz auf sie von dem Schlackenberg mittels eines Löffel-Felder zu liegen kommen, die von Untermengen baggers, eines Frontladers od. dgl. entnommen, der anderer unterschiedlicher Chargen umgeben sind, an einer Seite des Schlackenberges arbeitet und die weiche zu anderen Zeiten oder von anderen Schlak- 35 Schlacke vertikal oder in Querrichtung der honzonkenquellen erhalten werden und in der Zusammen- talen Schlackenschichten entnimmt, so daß die entsetzung zumindest geringfügig unterschiedlich sind, nommene Schlacke Anteile zahlreicher, den Schlakjedoch ebenfalls innerhalb des annehmbaren Schwan- kenberg bildender Scnlacken-Untermengen enthält, kungsbereichs der Zusammensetzung liegen. Jedes von dem Schkxkenberg entnommene Schlak-Je größer der Lagerplatz ist, des'o mehr Schlacken- 40 kenquantum kann sr nit tatsächlich zehn, zwanzig Einzelladungen werden benötigt, um den Lagerplatz oder vielleicht dreiLüa unterschiedliche Schlacken abzudecken; bei einem typischen Ausführungsbei- enthalten, die bei der Herstellung des Schlackenspiel jedoch, bei dem der Lagerbereich eine Größe berges verwendet wurden.that a product is created which is laid out of cinder blocks, so that a mountain of cinder arises. The slag mountain, which is between about 0.6 to 7.5 or 10 cm in size, can thus stand in between, with the majority of the slag pieces containing about 30,000 and 50,000 t of slag, preferably having a size of about 5 cm. The Jc is greater the storage bin, the more Charger thus treated slag may further ι: '\ ~ ύ be performed to prepare each Schlackcnschicht crfordcrüber a magnetic separator to lent and the more long it takes the whole, of at least a portion of the in the slag in front to build up numerous layers of slag piles of free iron or magnetizable material. So can the manufacture of such a remove. Slag mountain last three or four months, and thereupon the slag is taken to a storage place 4 be exposed to the influence of air or rain for two weeks in the storage space in spaced fields 2, before being deposited by the next Schlak and 6 to 14. In this way, the first subset can be covered with a layer. As a result, at least in field 2, the second subset in field 6, the 15 at least part of the stalfide contained in the slag, the third subset in field 8, etc. can be converted into sulphates, and a slag until the entire selected batch is used one which initially contains 0.9 per cent sulphides can then have sulphate content of 0.8 vol . per day or from a single charge. During the association blast furnace produced and processed slag weathering the slag also seeks to oxidize any free iron present in spaced-apart fields of the storage area 20,
has been filed. Then other slag subsets of batches produced in this way, which on other days, kenberg consists of a large number of slag at other times or of other slag subsets, the composition of which has been selected to swell, at further intervals more or less of the fields of the storage space that are held by the composition are deposited in another, either in the same layer or, for example, in fields 10, 12, 14 etc. of any layer above or below Subset is different. Batches in the storage place essentially check- In addition, each sub-quantity is only stored in the manner of a board, in such a way that the sub- a small part of the slag mixed in the storage place, the total amount of slag placed in a single day. If the discarded are obtained or the essentially the same slag is required for glass production, composition will have to come to lie in the storage place on them from the mountain of slag by means of a spoon fields that are taken from subsets of excavators, a front loader or the like that is surrounded by other different batches, works on one side of the slag mountain and the soft slag is obtained at other times or from other slag vertically or in the transverse direction of the mineral springs and collectively removes layers of slag, so that the relief is at least slightly are different, slag taken proportions of numerous, the slag, however, also within the acceptable range of slag-forming slag subsets, lie in the composition range. Each slag taken from the Schkxkenberg the larger the storage place, the more slag quantity can actually be ten or twenty individual loads are needed to cover the storage place or perhaps three different slag; in a typical embodiment, which were used in the manufacture of the cinder block, however, in which the storage area one size mountain was used.

von 160 Ar hat, werden etwa 160 Untermengen zum Das entnommene Material wird weiter aufbereitet Bedecken des Lagerplatzes benötigt. Um in dem 45 und zu diesem Zweck vorzugsweise auf eine Tempefertigen Produkt die erwünschte Gleichmäßigkeit zu ratur von etwa 120 bis 150⁰C frhitzt um die erhalten, ist es im allgemeinen erforderlich, beim Feuchtigkeit zu entfernen, und ferner bis zu einer Aufbau jeder Schlackenschicht mindestens 15 oder Korngröße zerkleinert oder pulverisiert bei welcher 20 Untermengen abzulegen. Anschließend werden die 95 »Ό ein 16maschiges US-Standardsieb jedoch nicht Untermengen der Schicht geglättet, so daß eine hon- 50 mehr als 50 «Λ, der Teilchen ein lOOmaschiges Sieb zontale Schicht von im wesentlichen gleichförmiger passieren. Das Material wird ferner wiederholt einer Dicke entsteht, die eine ebene Oberfläche hat. Die intensiven Magnetabscheidung ausgesetzt, um freies Menge der diese Schicht bildenden Schlacke wird Eisen und andere magnetisierbare Stoffe zu entdann notiert, und aus der Schicht werden Schlacken- fernen, bis das Produkt nicht mehr als 0 7 Gewichtsproben an zahlreichen, über die Schicht verteilten 55 prozent freies Eisen und andere magnetisierbare Punkten, nämlich etwa 50 Punkten, entnommen, wo- Stoffe enthält. Während dieses Arbertsschrittes kann bei darauf geachtet wird, daß die Proben das gleiche ferner von der Schlacke ein Teil des an das Eisen Gewicht haben. Diese Proben werden dann sorg- gebundenen Kohlenstoffs entfernt werden fältig gemischt, und das Gemisch wird analysiert, um In der Praxis wird üblicherweise em zweiter, aus die durchschnirüiche Zusammensetzung der die 60 mehreren Schichten bestehender Schlackenberg auf Schicht bildenden Schlacken zu ermitteln. die oben beschriebene Weise aufgebaut, während aus Nachdem eine erste Schicht 16 auf die beschriebene dem vorher erstellten Schlackenberg Schlacke zur Weise aufgebaut worden ist, werden auf dies« andere weiteren Aufbereitung und zum Versand entnommen Untermengen von Chargen abgelegt so daß auf die wird, so daß kontinuierlich derartige Schlacken zur gleiche Weise darüberliegende Schichten gebildet 6₅ weiteren Aufbereitung und zum Versand zur Verwerden, wie dies ra Fi g. 2 durch 18, 20 usw. darge- fügung stehen. of 160 ares, about 160 subsets are needed to cover the storage area. In order to obtain the desired uniformity to temperature of about 120 to 150 ⁰ C in the 45 and for this purpose preferably to a tempered product, it is generally necessary to remove moisture and furthermore to build up each slag layer at least 15 or grain size crushed or pulverized at which 20 subsets should be deposited. Then the 95 »of a 16-mesh US standard sieve, but not subsets of the layer, are smoothed so that a more than 50« of the particles pass through a 100-meshed sieve zontal layer of essentially more uniformity. The material is also repeatedly formed to a thickness that has a flat surface. The intense magnetic separation exposed to free amount of the slag forming this layer, iron and other magnetizable substances are then noted, and slag is removed from the layer until the product is no more than 0.7% by weight of numerous 55 percent distributed over the layer free iron and other magnetisable points, namely about 50 points, taken from which contains substances. During this work step, care can be taken to ensure that the samples have the same weight as well as some of the weight of the slag on the iron. These samples are then carefully removed, the carbon is carefully mixed, and the mixture is analyzed to determine in practice a second, from the average composition of the slag piles consisting of the 60 multilayered slag on layer. After a first layer 16 has been built up in the manner described for the previously created slag mountain of slag, subsets of batches are deposited on this other further processing and removed for dispatch so that it is so that continuously such slag is formed in the same way overlying layers 6 ₅ further processing and for dispatch to Vererden, as ra Fi g. 2 through 18, 20 etc. are available.

stellt is«LEs werden zamindestdrei und vorzugsweise Das Schlackenprodukt verfugt nach der Aufbe- is “ LEs are at least three and preferably The slag product grouts after

acht oder zehn Schlackenschichten übereinander- reitung und dem Versand zulinem Glashersteflereight or ten layers of slag on top of each other and sent to the glass manufacturer

über eine beträchtliche Gleichförmigkeit in der Zusammensetzung. Wie F i g. 4 zeigt, ist der Gehalt an SiO₂ in jeder Schlackenschicht eines aus zehn Schichten bestehenden, nach dem oben beschriebenen Verfahren hergestellten Vorratshaufens, wie er sich durch Analyse jeder Schlackenschicht bestimmen läßt, durch die gestrichelte Linie A dargestellt, während der Gehalt an SiO₂ in dem fertigen Produkt, wie er durch Analyse im versandfertigen Zustand festgestellt wird, durch die Linie B in F i g. 4 dargestellt ist. Der Gehalt an Al₂O₃ in jeder Schicht ist in entsprechender Weise durch die gestrichelte Linien gemäß F i g. 5 dargestellt, während der AI₂O₃-Gehalt des fertiggestellten Produktes, wie er sich durch eine Analyse des versandfertigen Materials ergibt, durch die Linie B dargestellt ist. In entsprechender Weise ist die CaO-Analyse der einzelnen Schichten und des fertiggestellten Produktes in F i g. 6 dargestellt, und der MgO-Gehalt der Schichten und des fertigen Produktes sind durch die Linien A bzw. B in F i g. 7 ao gezeigt.have considerable uniformity in composition. Like F i g. 4 shows, the SiO ₂ content in each slag layer of a storage heap consisting of ten layers and produced by the method described above, as can be determined by analyzing each slag layer, is shown by the dashed line A , while the SiO _{2 content in FIG} the finished product, as determined by analysis in the ready-to-ship state, by line B in FIG. 4 is shown. The content of Al ₂ O ₃ in each layer is indicated in a corresponding manner by the dashed lines in FIG. 5, while the Al ₂ O ₃ content of the finished product, as it results from an analysis of the material ready for dispatch, is shown by the line B. The CaO analysis of the individual layers and the finished product is shown in a corresponding manner in FIG. 6, and the MgO content of the layers and the finished product are indicated by lines A and B, respectively, in FIG. 7 ao shown.

Da die Dicke jeder Schicht und die Menge der in jeder Schicht des Vorratshaufens enthaltenen Schlacke ebenso wie die Zusammensetzung der Schlacke in jeder Schicht bekannt sind, läßt sich die Zusammen- as setzung des fertiggestellten Produktes leicht ermitteln und seine Verwendungsfähigkeit für irgendeinen betrachteten Glasherstellungsvorgang in einfacher Weise vom Glashersteller feststellen.As the thickness of each layer and the amount of slag contained in each layer of the storage heap Just as the composition of the slag in each layer is known, the composition can be as Easily determine the placement of the finished product and its suitability for any can easily be determined by the glass manufacturer.

Die Zusammensetzung irgendeiner Probe des auf diese Weise erhaltenen Produkts hängt natürlich von der Menge und der Zusammensetzung der Schlacken ab, die ausgewählt und gemischt wurden, um den Schlackenberg aus aufzubereitenden Schlacken zu erzeugen. In jedem Fall wird die V/ahl und der Mengenanteil der Schlacken derart überwacht, daß ein Endprodukt erhalten wird, welches eine derart definierte, bekannte und gleichförmige Zusammensetzung hat, daß der Anteil jedes der: Hauptoxide (SiO₂, Al₂O₃, CoO und MgO) in jeder von dem Schlackenprodukt entnommenen Probe um nicht mehr als etwa ± 0,3 %>, der Anteil an Eisenoxid (Fe₂O₃) um nicht mehr als etwa ± 0,04 °/o, der Anteil an Manganoxid um nicht mehr als etwa ± 0,05 °/o und der Anteil jedes der anderen oder Nebenoxide (Na₂O und K₂O) um nicht mehr als etwa ± 0,02 % schwankt, während Auf diese Weise erhaltene, typische Endprodukte können die folgenden Zusammensetzungen haben:The composition of any sample of the product obtained in this way will of course depend on the amount and composition of the slags which have been selected and mixed in order to produce the mountain of slag from slag to be treated. In any case, the volume and the proportion of the slag is monitored in such a way that an end product is obtained which has such a defined, known and uniform composition that the proportion of each of the: main oxides (SiO ₂ , Al ₂ O ₃ , CoO and MgO) in each sample taken from the slag product by no more than about ± 0.3%, the proportion of iron oxide (Fe ₂ O ₃ ) by no more than about ± 0.04%, the proportion of manganese oxide by no more than about ± 0.05% and the proportion of each of the other or minor oxides (Na ₂ O and K ₂ O) does not vary by more than about ± 0.02%, while typical end products obtained in this way may have the following compositions:

Beispielexample UU IIIIII IVIV II. 37,8537.85 32,3532.35 38,4538.45 SiOj,SiOj, 38,8038.80 7,107.10 14,8014.80 11,1011.10 Al₂O. + TiO₂ Al ₂ O. + TiO ₂ 9,759.75 38,3538.35 33,0033.00 44,1544.15 CaOCaO 40,6040.60 14,2014.20 17,0017.00 2,502.50 MgOMgO 8,208.20 0,300.30 0,270.27 0,250.25 Fe₈O,Fe ₈ O, 0,250.25 0,350.35 0,150.15 0,620.62 MnOMnO 0,500.50 0,690.69 0,620.62 0,900.90 Na₂O + K₈ONa ₂ O + K ₈ O 0,700.70 0,170.17 0,330.33 0,300.30 So₃ Sun ₃ 0,140.14 0,450.45 0,900.90 1,241.24 S"S " 0,750.75

Die besondere Zusammensetzung eines erfindungsgemäß hergestellten Produktes, das zur Glasherstellung verwendet werden soll, kann gewöhnlich aus irgendeiner der verschiedenen Mischungen oder Zusammensetzungen ausgewählt werden, die innerhalb dieses Gesamtbereiches liegen. Diese Flexibilität in der Zusammensetzung und Verwendung der auf die erfindungsgemäße Weise hergestellten Hochofen-Schlackenprodukte beruht auf der bekannten und gleichförmigen Zusammensetzung jedes einzelnen, dem Glashersteller zugelieferten Produktes. Der Glashersteller kann dann die Zusammensetzung des gesamten Gemischs der Glaserzeugungsmaterialien mit absoluter Sicherheit einstellen, indem er die Anteile irgendwelcher Oxydations-, Reduktions- oder weiterer, dem Gemisch beigegebener Zusätze verändert, bevor die Gesamtmischung in der. Glaserzeugungsofen eingeführt wird. Auf diese Weise werden Schwierigkeiten und Unsicherheiten, die bisher bei der Verwendung von Hochofenschlacke in der Glasherstellung auftraten, ausgeschaltet.The special composition of a product manufactured according to the invention that is used for glass manufacture to be used can usually be of any of various mixtures or compositions be selected that are within this total range. This flexibility in the composition and use of the blast furnace slag products produced in the manner according to the invention is based on the known and uniform composition of every single product supplied to the glass manufacturer. The glass maker can then use the composition of the entire mixture of glass-making materials set absolute security by determining the proportions of any oxidation, reduction or other the mixture added additives changed before the total mixture in the. Glass making furnace is introduced. In this way, difficulties and uncertainties that were previously encountered in the Use of blast furnace slag in glass production occurred turned off.

Dem Glashersteller wird nicht nur die spezifische Zusammensetzung des besonderen, angelieferten, modifizierten Hochofenschlackenprodukts übermittelt, sondern er wird auch von der Art der bei der Herstellung des Produkts verwendeten Schlacke unterrichtet. Diese Information ist deswegen von Bedeutung, da sich die Zusammensetzung von Erzeugnissen, die aus der gleichen Schlacke hergestellt werden, je nachdem, ob diese luftgekühlt, geschäumtThe glass manufacturer not only receives the specific composition of the special, delivered, modified blast furnace slag product, but it will also depend on the type of the Manufacture of the slag used in the product. This information is important as the composition of products made from the same slag are foamed, depending on whether they are air-cooled

der Anteil an SO₃ undthe proportion of SO ₃ and sulfidischem Schwefel umsulphidic sulfur oder granuliert wird,or is granulated, gemäß folgendem typischenaccording to the following typical 609634/213609634/213 nicht mehr als etwa ± 0,1'no more than about ± 0.1 ' Vo schwankt.Vo fluctuates. Beispiel ändert:Example changes: Beispiel VExample V (Gewichtsprozente)(Percentages by weight) LuftgekühltAir cooled GranuliertGranulated GewichtsprozenteWeight percent SiO₂ SiO ₂ 32,30 ± 0,3032.30 ± 0.30 32,17 + 0,3032.17 + 0.30 32,04 + 0,3032.04 + 0.30 Al₂O₃ + TiO₂ Al ₂ O ₃ + TiO ₂ 18,80 + 0,3018.80 + 0.30 18,74 ± 0,3018.74 ± 0.30 18,68 ± 0,3018.68 ± 0.30 CaOCaO 41,00 ± 0,3041.00 ± 0.30 40,84 + 0,3040.84 + 0.30 40,68 ± 0,3040.68 ± 0.30 MgOMgO 4,15 ± 0,204.15 ± 0.20 4,14 ± 0,204.14 ± 0.20 4,11 + 9,204.11 + 9.20 Fe₈O₈ Fe ₈ O ₈ 0,26 ± 0,020.26 ± 0.02 0,26 ± 0,020.26 ± 0.02 0,26 ± 0,020.26 ± 0.02 MnOMnO 1,05 ± 0,051.05 ± 0.05 1,05 ± G,051.05 ± G.05 1,05 ± 0,051.05 ± 0.05 Ns₂O + K₂ONs ₂ O + K ₂ O 1,07 ± 0,101.07 ± 0.10 1,07 ± 0,101.07 ± 0.10 1,07 ± 0,101.07 ± 0.10 SO₃ SO ₃ 0,15 ± 0,100.15 ± 0.10 0,12 ± 0,100.12 ± 0.10 0,09 ± 0,100.09 ± 0.10 S"S " 0,55 ± 0,050.55 ± 0.05 1,00 ± 0,051.00 ± 0.05 1,40 ± 0,051.40 ± 0.05

23 OO 51323 OO 513

ίοίο

Die Menge des erfindungsgemäß hergestellten, modifizierten Hochofenschlackenprodukts, die sich bei irgendeinem Glasherstellungsprozeß verwenden läßt, kann in einem weiten Bereich geändert werden. So kann beispielsweise lediglich 0,5 % Schlackenprodukt, bezogen auf das Gewicht des in der Gesamtmischung vorhandenen Sandes, verwendet werden, oder der Anteil kann bis zu 40 %> betragen. Selbst wenn nur ein sehr geringer Anteil des vergleichmäßigten Schlackenproduktes verwendet wird, verringert sich die Menge der »Blasen« in dem entstehenden Glaserzeugnis beträchtlich, und die Ofentemperatur, die zum Schmelzen und Frischen des Glases erforderlich ist, wird ebenfalls reduziert. Dies beruht vermutlich auf der Reduktionswirkung des Schlackenprodukts, das die Umwandlung von in der Glasschmelze vorhandenen Sulfaten in SO₂ in einem Zustand des Schmelzprozesses unterstützt, bei dem das entstehende SO₂-GaS leicht freigesetzt werden kann. Bei Verwendung größerer Anteile des Schlakkenprodukts werden natürlich die Glasherstellungskosten weiter gesenkt. Im allgemeinen ist der Anteil des Schlackenprodukts bei der Herstellung von Weißglas geringer als der, der sich bei der Herstellung von Ambra- oder anderem, dunkel getöntem GlasThe amount of the modified blast furnace slag product made in accordance with the present invention which can be used in any glass making process can be varied over a wide range. For example, only 0.5% slag product, based on the weight of the sand present in the total mixture, can be used, or the proportion can be up to 40%. Even if only a very small proportion of the leveled slag product is used, the amount of "bubbles" in the resulting glass product is considerably reduced and the furnace temperature required to melt and refine the glass is also reduced. This is presumably based on the reducing effect of the slag product, which supports the conversion of sulfates present in the glass melt into SO ₂ in a state of the melting process in which the SO _{2 gas that is formed can easily be released.} If larger proportions of the slag product are used, the glass production costs are of course further reduced. In general, the proportion of the slag product in the manufacture of white glass is less than that found in the manufacture of amber or other dark-tinted glass

ίο verwenden läßt.ίο lets use.

Die Größe und Form des Lagerplatzes und die Anzahl und Anordnung der dort abgelagerten Schlakken-Untermengen lassen sich natürlich ebenso wie die Anzahl und Dicke der verschiedenen Schlacken-The size and shape of the storage space and the number and arrangement of the slag subsets stored there can of course, as well as the number and thickness of the various slag

lj schichten in einem Schlackenberg in vielfacher Weise auswählen und verändern.lj layers in a mountain of cinder in many ways select and change.

Hierzu 3 Blatt ZeichnungenFor this purpose 3 sheets of drawings

Claims

Patent claims:

_{Em that} kind of thing

across the extension

r5: d. f **

". _{isl every} layer in

Shift at least

therefore had to