DE228961C - - Google Patents
Info
- Publication number
- DE228961C DE228961C DENDAT228961D DE228961DA DE228961C DE 228961 C DE228961 C DE 228961C DE NDAT228961 D DENDAT228961 D DE NDAT228961D DE 228961D A DE228961D A DE 228961DA DE 228961 C DE228961 C DE 228961C
- Authority
- DE
- Germany
- Prior art keywords
- mold
- powder
- mold powder
- coke
- casting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
KAISERLICHESIMPERIAL
Omen=Omen =
PATENTAMT.PATENT OFFICE.
PATENTSCHRIFTPATENT LETTERING
- M 228961 KLASSE 31 c. GRUPPE- M 228961 CLASS 31 c. GROUP
LYCODINWERKE G. m. b. H. in BERLIN.LYCODINWERKE G. m. B. H. in BERLIN.
Formenpulver aus kohliger, mit Harzen durchtränkter Masse.Mold powder made from a carbonaceous mass soaked in resins.
Die Erfindung bezieht sich auf ein Formenpulver für Gießereien zum Einstäuben der Modelle, welches verhindern soll, daß der feuchte Formsand beim Herausnehmen des Modells aus der Sandform an dieser haftet. Man hat sich zu diesem Behufe bisher des Lykopodiumpulvers bedient und als Ersatz für diesen äußerst kostspieligen Stoff fein gepulverten Kohlenstaub oder auch Kieselgur vorgeschlagen,The invention relates to a mold powder for foundries for dusting the Models, which should prevent the damp molding sand when removing the model from the sand mold sticks to this. Lycopodium powder has hitherto been used for this purpose and suggested finely powdered coal dust or kieselguhr as a substitute for this extremely expensive substance,
ίο die mit Harz oder ölen ο. dgl. ausgefüllt "^ wurden.ίο those with resin or oils ο. like. filled out "^ were.
Solche Formenpulver wiesen mannigfache Mängel auf. An ein gutes Formenpulver stellt man nämlich folgende Anforderungen:Such mold powders had many defects. Ask a good mold powder namely the following requirements:
i. Es muß geeignet sein, die Feuchtigkeit abzuhalten; es darf nicht hygroskopisch sein; 2. muß das Formenpulver genügende Porosität besitzen, um die beim Guß entweichenden Gase hindurchzulassen;i. It must be able to keep moisture out; it must not be hygroscopic; 2. The mold powder must have sufficient porosity to prevent the escaping during casting To let gases pass;
3. darf das Pulver nicht zu schnell verbrennen oder schwinden, damit Unebenheiten an der Oberfläche des Gußstückes und ein Anhaften des Gusses an der Form vermieden werden; ■ .3. The powder must not burn or shrink too quickly, causing bumps avoided on the surface of the casting and sticking of the casting to the mold will; ■.
4. darf das Formenpulver nicht kleben, da auch hierdurch der Guß beeinträchtigt werden würde.4. The mold powder must not stick, as this also affects the casting would.
Diesen Anforderungen werden die bisher zur Verwendung gelangenden Ersatzmittel für Lykopodium nicht gerecht. Holzkohlenstaub und Steinkohlenstaub sind außerordentlich hy- ' groskopisch. Werden sie der bekannten Behandlung mit Harzen oder ölen unterworfen, so verlieren sie zwar ihre Wasseraufnahmefähigkeit, sie werden aber klebrig. Außerdem sind Kohlenstaubpulver nicht feuerbeständig genug; sie verbrennen außerordentlich schnell, so daß ihre Wirkung als Formenpulver nicht gut ist.The substitutes for lycopodium that have been used up to now do not meet these requirements. Charcoal dust and coal dust are extremely hy 'groskopisch. If they are subjected to the known treatment with resins or oils, they lose their ability to absorb water, but they become sticky. In addition, pulverized coal powders are not sufficiently fire resistant; they burn extremely quickly, so that their effect as a molding powder is not good.
Die zum Ersatz für Kohlenpulver vorgeschlagene Kieselgur besitzt einerseits wieder nicht genügende Porosität, anderseits ein zu hohes spezifisches Gewicht, so daß sie beim Einstäuben beispielsweise an vorspringenden Kanten und Ecken der Form nicht haftet, sondern von ihnen herunterfällt.On the one hand, the kieselguhr proposed as a substitute for carbon powder does not have it Sufficient porosity, on the other hand, too high a specific weight, so that they are dusted for example, does not adhere to protruding edges and corners of the mold, but falls off them.
Außerdem weist Kieselgur den Nachteil auf, daß sie sich chemisch so gut wie gar nicht von dem Sand der Form unterscheidet, so daß eine wirksame Trennung des Gusses von der Form durch diesen Stoff, der sich überdies in den Guß einbrennt, nicht bewirkt werden kann.In addition, diatomaceous earth has the disadvantage that it is chemically virtually non-existent the sand of the mold differs so that an effective separation of the cast from the mold this substance, which moreover burns itself into the casting, cannot be effected.
Die erwähnten Nachteile werden durch das Formenpulver nach der Erfindung vermieden, welches allen Anforderungen gerecht wird, die man an ein Formenpulver stellen kann.The mentioned disadvantages are avoided by the mold powder according to the invention, which meets all the requirements that can be placed on a mold powder.
Die Grundmasse des Formenpulvers. ist fein gemahlener Koksstaub, welcher einerseits die genügende Porosität besitzt, anderseits einen so hohen Schmelzpunkt, daß seiner Verwendung nichts entgegensteht.The basic mass of the mold powder. is finely ground coke dust, which on the one hand the has sufficient porosity, on the other hand, such a high melting point that its use nothing stands in the way.
Der hohe Schmelzpunkt des Kokspulvers hat die günstige Wirkung, daß eine dauernde
genügende Trennung des Gusses von dem feuchten Sand der Form bewirkt wird, so daß eine plötzliche Abkühlung des Gusses vermieden
wird, seine Oberfläche vielmehr einer Temperatur ausgesetzt wird, die für die zweckmäßigste
Härtung am geeignetsten ist. Die Porosität des Koksstaubes gestattet ein Entweichen
der beim Guß auftretenden Gase.
"Die übrigen Anforderungen, die man an einThe high melting point of the coke powder has the beneficial effect that a permanent sufficient separation of the cast from the moist sand of the mold is effected, so that a sudden cooling of the cast is avoided, its surface is exposed to a temperature that is most suitable for hardening is most suitable. The porosity of the coke dust allows the gases that occur during casting to escape.
"The rest of the requirements that one has of a
6565
gutes Formenpulver stellt, werden dem Koksstaub, soweit er sie noch nicht besitzt, durch vorbereitende Behandlung und Vermischung mit anderen geeigneten Stoffen gegeben.good mold powder, the coke dust, if it does not already have it, through preparatory treatment and mixing with other suitable substances.
Das Formenpulver nach der Erfindung enthält nämlich neben seinem Hauptbestandteil Kokspulver auch Beimischungen von Kohlenstaub, und Kieselgur. Das gesamte Gemisch ist in bekannter Weise mit Harzen getränkt.The mold powder according to the invention contains in addition to its main component Coke powder also admixtures of coal dust and kieselguhr. The whole mixture is impregnated with resins in a known manner.
Zur Herstellung des Formenpulvers nach der Erfindung geht man zweckmäßig in der Weise vor, daß man z. B. Koks unter Zumischung von Kohle und Kieselgur fein vermahlt, hierauf dem Gemisch in bekannter Weise eine Lösung von Sandarakharz in Spiritus oder anderen geeigneten Lösungsmitteln zugibt und alsdann wiederum mehrere Stunden lang nahezu bis zur Trockne in einer Trommel vermahlt.To prepare the mold powder according to the invention, it is expedient to proceed as follows before that one z. B. coke finely ground with the addition of coal and diatomaceous earth, then a solution of sandarak resin in alcohol or other suitable solvents is added to the mixture in a known manner and then ground again for several hours in a drum almost to dryness.
Claims (1)