DE2254420A1

DE2254420A1 - Glass bead contg enamel - is super imposed by transfer techniques on ena-mel layers on metal bases

Info

Publication number: DE2254420A1
Application number: DE19722254420
Authority: DE
Inventors: Hans Haase
Original assignee: DEUTSCHES EMAIL ZENTRUM E V
Current assignee: DEUTSCHES EMAIL ZENTRUM E V
Priority date: 1972-11-07
Filing date: 1972-11-07
Publication date: 1974-05-22
Also published as: DE2254420B2

Abstract

Retro-reflecting glass enamel layer consists of >=1 layers burnt on to an enamellable metal base. At least at the locations requiring reflective prop., a further layer of glass enamel cont. uniformly distributed identical size 20 mu dia. glass pearl is applied. The enamel layer with the beads is pref. applied like a transfer as a reflex foil. It may be clear or colourless as may be the beads. The layer thus applied and fired is smooth and has good adhesion and weathering prop. It is used for lampshades etc.

Description

Retro-reflektierende Deckschicht aus Glasemail auf Gegenständen, insbesondere Tafeln, aus Metall, Eisen, Aluminium oder anderen emaillierfähigen Metallen sowie Verfahren zu ihrer Herstellung.Retro-reflective top layer of glass enamel on objects, in particular Panels, made of metal, iron, aluminum or other enamelled metals as well Process for their manufacture.

Aus der österreichischen Patentschrift 172 261 ist ein Verfahren zur Herstellung von Emailtafeln mit retro-reflektierender Oberfläche bekannt geworden, das darin besteht, daß auf die Tafel wenigstens an den Stellen, an denen Glaslinsen befestigt werden sollen, eine keramische Bindemittelschicht aufgetragen wird und dann die Glaslinsen auf die Tafel gebracht werden, worauf die Tafel einem Brennprozeß unterworfen wird, wobei das als Bindemittel verwendete keramische Material beim Brennen erweicht und glasartig wird und die Linsen mit der Tafel fest verbindet. Das Verfahren hat keinen Eingang in die Praxis gefunden, da ihm und den nach ihm hergestellten Tafeln erhebliche Nachteile anhaften. So hat sich gezeigt, daß eine gleichmäßig re.troreflektierende Emailfläche nach diesem Verfahren nicht mit Sicherheit herstellbar ist, da sich die Glaslinsen beim Aufbringen auf der Tafel nicht einheitlich gleich verteilen.From the Austrian patent specification 172 261 is a method for Manufacture of enamel panels with a retro-reflective surface has become known, that consists in that on the board at least in the places where glass lenses are to be attached, a ceramic binder layer is applied and then the glass lenses are placed on the board, whereupon the board undergoes a firing process is subjected, the ceramic material used as a binder in Burning softens and becomes vitreous and firmly bonds the lenses to the board. The procedure has not found its way into the practice, since him and those after him produced panels adhere to considerable disadvantages. So it turned out that a evenly re-reflective enamel surface after this process not with certainty can be produced because the glass lenses are not uniform when applied to the board distribute evenly.

Infolgedessen hatte das Verfahren eine ungewöhnlich (bis zu 90 %) hohe Ausschußquote. Auch ist die Haftung der Glaslinsen auf der Bindeschicht ungenügend und nicht genügend haftende Glaslinsen bröckeln darum, z.B. beim Reinigen der Tafeln, leicht ab, wodurch die retro-reflektierende Wirkung ebenfalls nachteilig gestört wird. Schließlich besitzen die nach dem bekannten Verfahren hergestellten, insbesondere im Preien benutzten Tafeln eine starke Neigung zum Verschmutzen.As a result, the procedure had an unusual (up to 90%) high reject rate. The adhesion of the glass lenses to the binding layer is also insufficient and insufficiently adhering glass lenses crumble, e.g. when cleaning the blackboard, slightly, which also adversely affects the retro-reflective effect will. Finally, have those produced by the known method, in particular In Preien, panels used a strong tendency to get dirty.

Die Erfindung betrifft eine retro-reflektierende Glas-Emaillierung, bei der die beschriebenen Nachteile nicht auftreten und die darin besteht, daß auf einer in bekannter Weise nach dem Ein- oder Mehrschichtverfahren emaillierte Fläche, die ein- oder mehrfach farbig getönt sein undoder mit einer Bild- oder Zeichendarstellung versehen sein kann, eine mit Perlen gleichmäßig durchsetzte, tranparente Emailglasur eingebrannt ist. Bei einer so,hergestellten Emaildecke sind die Reflexionsperlen von dem transparenten Email bedeckt und sie besitzt infolgedessen eine glatte und porenfreie Oberfläche von einer bisher nicht erreichten Witterungsbeständigkeit und eine fest haftende Glasperlenfüllung, der u.a. auch eine intensive Reinigungsbehandlung nicht schadet. Die gleichmäßige Durchsetzung init Glasperlen hat weiterhin eine durchgehend gleiche retroreflektierende Wirkung zur Polge.The invention relates to a retro-reflective glass enamelling, in which the disadvantages described do not occur and which consists in that on a surface enamelled in a known manner using the single or multi-layer process, which are tinted in one or more colors and or with an image or character representation can be provided, a transparent enamel glaze evenly interspersed with pearls is burned in. With an enamel ceiling made in this way, the reflective beads are covered by the transparent enamel and consequently it has a smooth and pore-free surface with a previously unattained weather resistance and a firmly adhering glass bead filling, which also includes an intensive cleaning treatment does not hurt. The uniform penetration with glass beads continues to have a consistently same retroreflective effect to the pole.

Zur Erzeugung der retro-reflektierenden Oberfläche dient erfindungsgemäß eine nach Art eines Abziehbildes ausgebildete Reflexfolie, die einen Belag aus einer farblosen oder farbigen, mit feinen Glasperlen gleichruü!3ig durchsetzten, transparenten Emailfritte aufweist und auf der in bekannter We-ise voremaillierten Metallfläche aufgebracht und eingebrannt wird. Anstelle einer transparenten mit Glasperlen durchsetzten Farbemailfritte kann auch eine transparente farblose Fritte vorgesehen sein, die mit farbigen Glasperlen durchsetzt ist.The purpose of the invention is to generate the retro-reflective surface a reflective film designed in the manner of a decal, which has a covering made of a colorless or colored, evenly interspersed with fine glass beads, transparent Has enamel frit and on the metal surface pre-enamelled in the known manner is applied and baked. Instead of a transparent one interspersed with glass beads Color enamel frit can also be provided with a transparent colorless frit is interspersed with colored glass beads.

Für die Glasperlenfüllung der transparenten Deckglasur kommen Glasperlen von einem sehr geringen, annähernd gleichen Durchmesser, von vorzugsweise ca0 20 U und einem über der Einbrenntemperatur der transparenten Fritte liegenden Schmelzpunkt in Betracht. Der Brechungsindex der Glasperlen sollte etwa doppelt so groß wie der des Transparentemails sein. Die Aufbringung der mit Perlen durchsetzten transparenten Emailfritte auf die Reflexfolie erfolgt vorteilhaft mit Hilfe des Siebdruckverfahrens, mit dem eine Belaschicht erzeugt werden kann, die gleichmaßig von Glasperlen durchsetzt ist, so daß eine durch einen Transparentemailiiberzug geschützte, gleich+.aßig ret-ro-reflektierende Oberfläche entsteht.Glass beads are used for the glass bead filling of the transparent cover glaze of a very small, approximately the same diameter, preferably about 0 20 U and a melting point above the baking temperature of the transparent frit into consideration. The refractive index of the glass beads should be about twice that of the of the transparent enamel. The application of the transparent, interspersed with pearls Enamel frit on the reflective film is advantageously carried out with the help of the screen printing process, with which a lamination layer can be created that is evenly interspersed with glass beads is, so that a protected by a transparent enamel cover, equal + .assig ret-ro-reflective Surface is created.

Als Träger für die transparente, von Glasperlen durchsetzte Emailfritte kann eine mit einem Haftmittelbelag, beispielsweise Gelatine, versehene abziehbare Unterlage aus Papier oder einem anderen geeigneten Material dienen. ¢in unschdlich abbrennbares Haftmittel kann auch der fritte beifflemischt satin, wie überhaupt die Reflexfolie in verschiedener Weise hergestellt sein kann.As a carrier for the transparent enamel frit interspersed with glass beads can be a peelable one provided with an adhesive coating, for example gelatin A base made of paper or another suitable material can be used. ¢ in harmless Burnable adhesive can also be used in the frit with mixed satin, as at all the reflective film can be produced in various ways.

Das Verfahren der Erfindung, die im wesentlichen in der neuartigen Verwendung einer Reflexfolie nach Art eines Abziehbildes liegt, läßt sich in mannigfacer Weise durchführen. So kann auf eine im Sin- oder Mehrsc-hichtverfahren auf einem metallischen Gegenstand, beispielsweise einer Tafel aus Eisen, Aluminium oder einem anderen emaillierfähigen Metall erzeugte weiße oder farbige Emailglasur in bekannter Weise, z.B. durch Malen, Spritzen, Drucken oder vermittels eines herkömmlichen Abziehbildes ein Bild, eine Zeichendarstellung oder dgl. aufgebracht und danach eingebrannt werden, worauf vermittels einer erfindungsgemäßen Reflexfolie eine Schicht einer transparenten, farblosen oder farbigen, mit Glasperlen durchsetzten Pritte aufgebracht und ebenfalls eingebrannt wird. Es kann aber auch auf einer - wie beschrieben - weiß oder farbig voremaillierten Fläche ein Abziehbild, dessen Abziehschicht von einer transparenten, mit Glasperlen gleichmäßig durchsetzten Farbemailfritte gebildet ist, abgezogen und danach eingebrannt wird. Auf einer Emailfläche kann auch ein .Nbziehbild abgezogen und eingebrannt werden, dessen Abziehschicht aus einem transparenten Frittebelag besteht, in dtn ildliche Darstellungen, Zeichendrstellunen od.dgl. aus farbigen Glasperlen, z.B. im Siebdruckverfahren eingebettet sind. In gleicher Weise kann eine durchgehend gleichfarbige reflektierende Oberfläche durch Aufbrennen einer gefärbten, transparenten Glasperlen-Emailfritte oder einer fritte vit fqrbigen Glasperlen erzeugt werden.The method of the invention, essentially in the novel The use of a reflective film in the manner of a transfer picture can be varied in many ways Way to perform. This means that one can use a single or multi-layer process on one metallic object, for example a sheet made of iron, aluminum or a other enamelled metal produced white or colored enamel glaze in well-known Way, e.g. by painting, spraying, printing or by means of a conventional decal an image, a character representation or the like. are applied and then burned in, whereupon by means of a reflective film according to the invention a layer of a transparent, colorless or colored pritte interspersed with glass beads and also applied is burned in. But it can also on one - as described - white or colored pre-enamelled surface a decal, the peelable layer of a transparent colored enamel frit evenly interspersed with glass beads is peeled off and then burned in. A .Nbziehbild can be peeled off and baked in, the peel-off layer of which is made of a transparent There is frit covering, in dtn ildliche representations, Zeichenendrstellunen or the like. the end colored glass beads, e.g. embedded in the screen printing process. In the same way can create a continuously reflective surface of the same color by burning on a colored, transparent glass bead enamel frit or a frit vit colored glass beads be generated.

Außer den beschriebenen Ausführungsformen ergeben sich weitere Höglichkeiten zur Ausführung der von dem Abziehbildprinzip Gebrauch machenden Erfindung, zu deren bereits beschriebenen Vorteilen auch der Vorteil einer betriebstechnischen Vereinfachung kommt, die darin besteht, daß die zu ihrer Ausführung erforderlichen, bestimmte Bilder, Zeichendarstellungen oder Farbgebungen aufweisenden Reflexfolien vorgefertigt, in Vorrat gehalten und bedarfsweise ihrer Bestimmung zugeführt werden können.In addition to the embodiments described, there are further possibilities to carry out the invention making use of the decal principle, to their advantages already described also the advantage of an operational simplification comes, which consists in the specifics necessary for their execution Pre-fabricated reflective foils showing pictures, drawings or colors, can be kept in stock and, if necessary, supplied to their destination.

Claims

PATENT CLAIMS

1. Retro-reflective top layer made of glass enamel, consisting of a in a known manner in a single or four-layer process on a metallic base , e.g. made of iron, aluminum or another metal that can be enamelled Glass enamel pad on which, at least at the points intended for reflection, glass beads are fused, characterized in that the glass enamel with a transparent further glass enamel layer is covered, which is evenly covered with glass beads is penetrated by a small diameter, preferably about 20.

2. Process for the production of a retro-reflecting enamel overlay according to claim 1, characterized in that in a known manner, white or colored opaque glass enamel layer evenly interspersed with glass beads colorless or colored transparent enamel frit applied and at temperatures above 500 ° C is burned in.

3. The method according to claim 2, characterized in that the transparent, enamel frit interspersed with glass beads by means of an enamel frit according to Art a decal applied as a reflective film bearing the image layer will.

4. The method according to claims 2 and 3, characterized in that on a white or colored glass enamel layer, e.g. by painting, spraying, printing or a picture, a character representation, by means of a conventional decal Or the like. Are applied and then baked, whereupon by means of a Type of a decal formed reflective film, the image layer of which consists of a transparent, colorless or colored enamel frit evenly interspersed with glass beads, a top layer is applied and baked.

5. The method according to claim 2 to s, characterized in nß a white or colored pre-enameled surface is peeled off and burned in whose peel layer consists of a transparent Pritte coating, into the pictorial Representations, character representations or the like. embedded from colored glass beads are.

6. The method according to claims 3 to 5, characterized by dis Use of reflective foils on which the FritiDelag interspersed with glass beads is produced by means of the screen printing process.

7. The method according to claims 2 to 6, characterized in that that the glass beads used have a baking temperature above the transparent one Enamel frit lying melting point and a refractive index about twice as large like that of transparent enamel.

L e r s e i t e