DE2142200C3 - Grinding compound - Google Patents
Grinding compoundInfo
- Publication number
- DE2142200C3 DE2142200C3 DE19712142200 DE2142200A DE2142200C3 DE 2142200 C3 DE2142200 C3 DE 2142200C3 DE 19712142200 DE19712142200 DE 19712142200 DE 2142200 A DE2142200 A DE 2142200A DE 2142200 C3 DE2142200 C3 DE 2142200C3
- Authority
- DE
- Germany
- Prior art keywords
- grinding
- oxide
- mno
- weight
- tool
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
S55T*1"dcr Masse'in GewichBprraei"» SHSSSi»:::::::::::: u S 8S55T * 1 " dcr mass ' in weight " »SHSSSi» :::::::::::: u S 8
Chromoxid Cr?O3 0,3 bis 0,7 enthält wobei das Manganoxid MnO völlig oder teil-Chromium oxide Cr ? Holds ent 3 O 0.3 to 0.7 wherein the manganese oxide MnO completely or partially
Siliziumoxid SiO2 J,0bi5 3,2 weise durch nach Marigan äquivalente Menge vonSilicon oxide SiO 2 J, 0bi5 3.2 wise by according to Marigan equivalent amount of
Manganoxid MnO 1,5 bis 2,5 Mangandioxid MnO4 ersetzt werden kann. Manganese oxide MnO 1.5 to 2.5 manganese dioxide MnO 4 can be replaced.
wobei das Manganmonoxid QvInO) vollständig 15 Zum Erreichen des gestellten Ziels ist es vorteilhaft,where the manganese monoxide QvInO) completely 15 To achieve the set goal, it is advantageous to
oder teilweise durch eine dem Mangan äquivalente daß die Schleifmasse in Gewichtsprozentor in part by an equivalent to manganese that the abrasive mass in percent by weight
Menge an Mangandioxid ersetzt werden kann.
2. Schleifmasse nach Anspruch 1, dadurch ge- Aluminiumoxid Al2O, 94,40Amount of manganese dioxide can be replaced.
2. Abrasive mass according to claim 1, characterized in aluminum oxide Al 2 O, 94.40
kennzeichnet, daß sie in Gewichtsprozent Chromoxid Cr8O3 0,49indicates that in percent by weight chromium oxide Cr 8 O 3 0.49
αϊ η 04 an αϊ η 04 at
/AIaVJn 74T1HU / AIaVJn 7 4 T 1 HU
8
Siliziumoxid SiO2 2,76 8th
Silicon oxide SiO 2 2.76
η 04 an η 04 on
aVJn 74T1HU .,, -J**/-! 1 ^r aVJn 7 4 T 1 HU. ,, -J ** / -! 1 ^ r
O 49 und Manganoxid MnO 2,35 O 49 and manganese oxide MnO 2.35
2e2e
Mn0 2'35 Die vorgeschlagene Schleif masse gewährleistet dank Mn0 2 '35 The proposed grinding mass guaranteed thanks
enthält. 35 einer solchen Zusammensetzung der in den vorge-contains. 35 such a composition of the
3. Schleifwerkzeug, hergestellt aus der Schleif- nannten Verhältnissen genommenen Komponenten3. Grinding tool, made from components taken from the grinding ratio
masse nach Anspruch 1 oder 2. die Herstellung eines Schleifwerkzeugs, das hohemass according to claim 1 or 2. the production of a grinding tool, the high
Schleif- und mechanische Eigenschaften besitzt, die .es gestatten, dieses Werkzeug beim Feinschleifen undHas grinding and mechanical properties that allow this tool to be used for fine grinding and
30 Polieren von Teilen aus verschiedenen schwer-30 Polishing of parts from various difficult
bearbeitbaren Metallen und deren Legierungen wirkungsvoll τ\ι verwenden.machinable metals and their alloys effectively τ \ ι use.
Durch unsere Untersuchungen ist festgestellt, daßOur investigations have shown that
Die Erfindung betrifft Schleifmassen auf der Basis wenn in der Schleifmasse auf der Basis von Aluminiumvon Aluminiumoxid (Al2O3). 35 oxid Al2O3, die als Legierungszusätze Chromoxid Diese Schleifmassen werden zur Herstellung ver- Cr2O3, Siliziumoxid SiO2 und Manganoxid MnO entschiedenartiger Schleifwerkzeuge verwendet. hält, der Gehalt von Cr2O3 weniger als 0,3 Gewichts-Die vorliegende Erfindung kann am vorteilhaftesten prozent oder mehr als 0,7 Gewichtsprozent beträgt, in verschiedenen Zweigen der metallverarbeitenden dies zu einem schroffen Abfall der Schleifwirkung des Industrie zum Feinschleifen und Polieren von Teilen 40 aus einer solchen Masse hergestellten Schleifwerkzeugs aus Stahl, insbesondere aus gehärtetem Stahl, sowie führt. Die Verminderung des SiOg-Gehaltes gegenüber aus Nichteisenmetallen und deren Legierungen ange- den oben angegebenen 2,0 Gewichtsprozent und des wendet werden. MnO-Gehalts gegenüber den angegebenen 1,5 Ge-A'lgemein bekannt sind Schleifmassen auf der Basis wichtsprozent führt zu einer starken Beeinträchtigung von Aluminiumoxid (Al2O3) mit Legierungszusätzen 45 der mechanischen Eigenschaften des Werkzeugs. Bei in Form von Manganoxid MnO (oder MnO2) oder der Erhöhung des SiO^Gehalts über 3,2 Gewichtsprovon Chromoxid Cr2O3. zent und des MnO-Gehalts über 2,5 Gewichtsprozent Solche Schleifmassen enthalten auch noch ein Binde- hinaus wird Verglasung beobachtet, was von einem mittel, beispielsweise Bakelit. Ein aus den erwähnten wesentlichen Abfall der Schleifeigenschaften des Massen hergestelltes Schleifwerkzeug kann zum Schlei- 50 Werkzeugs zeugt.The invention relates to aluminum-based aluminum oxide (Al 2 O 3 ) -based abrasive compounds, if in the abrasive compound. 35 oxide Al 2 O 3 , with chromium oxide as alloy additives. These grinding compounds are used for the production of decidedly Cr 2 O 3 , silicon oxide SiO 2 and manganese oxide MnO grinding tools. keeps the content of Cr 2 O 3 less than 0.3 weight- The present invention may be most advantageous percent or more than 0.7 weight percent, in various branches of metalworking this leads to a sharp drop in the grinding efficiency of the fine grinding and polishing industry of parts 40 made of such a mass of grinding tool made of steel, in particular of hardened steel, as well as leads. The reduction in the SiOg content compared to non-ferrous metals and their alloys should be the 2.0 percent by weight given above and should be used. MnO content compared to the specified 1.5 Ge-A'l are generally known grinding compounds on the basis of weight percent leads to a severe impairment of aluminum oxide (Al 2 O 3 ) with alloy additives 45 of the mechanical properties of the tool. In the form of manganese oxide MnO (or MnO 2 ) or the increase in the SiO 4 content above 3.2 per weight of chromium oxide Cr 2 O 3 . cent and the MnO content over 2.5 percent by weight. Such grinding compounds also contain a bond- addition, glazing is observed, which is from a medium, for example Bakelite. A grinding tool made from the aforementioned substantial drop in the grinding properties of the compound can be a grinding tool.
fen von Teilen aus verschiedenen Metallen und Legie- Das Obengesagte trifft im vollen Maße auch dann zu,manufacturing of parts made of different metals and alloys - The above also applies to the full extent,
rungen eingesetzt werden, ist jedoch zum Feinschleifen wenn die Schleifmasse als einen der LegierungszusätzeHowever, it is used for fine grinding if the grinding compound is used as one of the alloy additives
und Polieren infolge seiner ungünstigen mecha- nicht MnO, sondern MnO1 in einer zu Manganand polishing due to its unfavorable mecha- not MnO but MnO 1 in one to manganese
nischen Eigenschaften ungeeignet. äquivalenten Menge enthält.niche properties unsuitable. contains equivalent amount.
Außerdem verringert die Verwendung eines Binde- 55 Im folgenden wird die Erfindung an einem Aus-In addition, the use of a binding reduces the 55
mittels den Gehalt an Hauptkomponente (Aluminium- führungsbeispiel erläutert.by means of the content of the main component (aluminum guide example explained.
oxid Al2O3) und (oder) an Legierungsszuätzen in der Es wurde festgestellt, daß ein Schleifwerkzeug, dasoxide Al 2 O 3 ) and (or) of alloy additives in the It has been found that a grinding tool that
Schleifmasse, wobei infolgedessen der Bereich der aus einer Schleifmasse hergestellt wird, welche technologischen Möglichkeiten des aus diesen MassenAbrasive compound, as a result of which the area is made from an abrasive compound, which technological possibilities of the from these masses
hergestellten Werkzeugs eingeengt wird. 60 Al2O3 94,40produced tool is concentrated. 60 Al 2 O 3 94.40
Die Praxis zeigt, daß irr gewissen Zweigen des Ma- Cr2O3 0,49Practice shows that in certain branches of the Ma- Cr 2 O 3 0.49
schinenbaus bei der mec lanischen Bearbeitung von SiO2 2,76mechanical engineering during the mechanical processing of SiO 2 2.76
Metallen und deren Legierungen die größten techno- ur|d MnO 2,35Metals and their alloys are the greatest techno- ur | d MnO 2.35
logischen Schwierigkeiten gerade mit Feinschleifenlogical difficulties, especially with fine grinding
und Polieren verbunden sind. 65 in Gewichtsprozent enthält, beim Feinschleifen undand polishing are connected. 65 in percent by weight, for fine grinding and
Der Erfindung liegt die Aufgabe zugrunde, eine Polieren von Teilen aus gehärteten Stählen mit Vickers-The invention is based on the object of polishing parts made of hardened steels with Vickers
Schleifmasse auf der Bas-is von Aluminiumoxid mit härte 600 ... 800 kp/cma Oberflächen gewährleistet,Grinding compound on the basis of aluminum oxide with a hardness of 600 ... 800 kp / cm a surface guaranteed,
solchen Legierungszusätzm zu schaffen, die hohe die Unebenheiten (Rauhigkeit) mit mittlerer Höhe vonSuch alloy additions to create the high unevenness (roughness) with a medium height of
nicht mehr als 0,2 μΐη aufweisen. Der Verschleiß des Werkzeugs selbst ist so gering, daß er mit der Menge des abgehobenen Metalls nicht vergleichbar ist So z. B. beträgt die Lebensdauer einer Schleifscheibe von 70 mm Durchmesser nicht weniger als 1000 Arbeitsstunden. Das Werkzeug weist eine hohe Härte auf, die durch eine Mikrohärte von etwa 1500 kp/mro* gekennzeichnet ist, was eine stabile Maßgenauigkeit der zu bearbeitenden Teile in der Größenordnung von einigen Mikrometern gewährleistet.do not have more than 0.2 μΐη. The wear and tear of the Tool itself is so small that it cannot be compared with the amount of metal removed z. B. the service life of a grinding wheel with a diameter of 70 mm is no less than 1000 working hours. The tool has a high hardness, which is characterized by a micro hardness of around 1500 kp / mro *, which ensures stable dimensional accuracy of the parts to be machined in the order of a few micrometers guaranteed.
Claims (1)