DE2117449A1 - Decorating raw ceramic articles - with solns of metal salts - Google Patents

Decorating raw ceramic articles - with solns of metal salts

Info

Publication number
DE2117449A1
DE2117449A1 DE19712117449 DE2117449A DE2117449A1 DE 2117449 A1 DE2117449 A1 DE 2117449A1 DE 19712117449 DE19712117449 DE 19712117449 DE 2117449 A DE2117449 A DE 2117449A DE 2117449 A1 DE2117449 A1 DE 2117449A1
Authority
DE
Germany
Prior art keywords
ch3coo
decoration
raw ceramic
solution
ceramic pieces
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DE19712117449
Other languages
German (de)
Inventor
Auf Nichtnennung Antrag
Original Assignee
Lladro DoIz, Jose, Tabernes Blan ques, Valencia (Spanien)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lladro DoIz, Jose, Tabernes Blan ques, Valencia (Spanien) filed Critical Lladro DoIz, Jose, Tabernes Blan ques, Valencia (Spanien)
Priority to DE19712117449 priority Critical patent/DE2117449A1/en
Publication of DE2117449A1 publication Critical patent/DE2117449A1/en
Pending legal-status Critical Current

Abstract

Raw ceramic articles are decorated, after sizing or other processing by applying a soln. contg. an acetate, nitrate, sulphate and/or chloride of Cu, Co, Cr, Mn, Ni, Au Pt and/or uranyl, then drying and firing at 1380-1400 degrees C to thermally decompose the salt(s). Uniform colouration of ceramic surfaces or parts is achieved.

Description

Beschreibung betreffend "Verfahren für die Dekoration von Rohkeramikstücken" Die Erfindung bezieht sich auf ein Verfahren für Dekoration von Rohkeramikstücken unter Einsatz einer ausgedehnten Reihe von kombinierten chemischen Produkten, die, wie gesagt, auf Rohkeramikstücken aufgetragen werden können, mit anschließendem Trocknen und Brennen, wobei auf der ganzen Ausdehnung des Gegenstands oder der imprägnierten Zonen eine gleichmäßig verteilte Schicht entsteht.Description relating to "Process for the decoration of raw ceramic pieces" The invention relates to a method for decorating raw ceramic pieces using an extensive range of combined chemical products that, As I said, can be applied to raw ceramic pieces, with subsequent Drying and firing, taking on the whole extension of the object or the impregnated Zones an evenly distributed layer is created.

Bis jetzt sind für die Dekoration von Keramikstücken Verfahren bekannt, die sehr langsam und außerdem unzweckmäßig sind, weil die Farbe auf den zu dekorierenden Teilen ungleich verteilt wird, besonders bei relativ hohen Temperaturen.Up to now, methods are known for the decoration of ceramic pieces, which are very slow and also inconvenient because the paint on the ones to be decorated Sharing is unevenly distributed, especially at relatively high temperatures.

Die Bedeutung der Farbe bei keramischen Produkten ist offensichtlich.The importance of color in ceramic products is obvious.

Es ist bekannt, daß die Färbung der Substanzen wesentlich zur Fähigkeit gewisser Atome oder Atomgruppen zur Aufnahme elektromagnetischer Strahlungen mit bestimmter Wellenlänge beiträgt.It is known that the coloring of the substances is essential to the ability certain atoms or groups of atoms to absorb electromagnetic radiation certain wavelength contributes.

Dieselben invertieren sich, wenn sie den Elektronen der Atome die notwendige Energie zuführen zur Erreichung höherer Energiestufen, Wenn sie im sichtbaren Bereich liegen, führen die elektronischen Übergänge zur Entstehung der vom menschlichen Auge wahrnehmbaren Farbe. Dies ist der Fall bei den Atomen der dbergangselemente und vielen organischen Verbindungen.They invert themselves when they are the electrons of the atoms supply the necessary energy to achieve higher energy levels, if they are in the visible Area, the electronic transitions lead to the emergence of the human Eye perceptible color. This is the case with the atoms of the transition elements and many organic compounds.

Aber jedes Atom gibt nicht eine einzige Färbung, denn die elektronischen Systeme, die die Atome bilden, sind nicht in der Materie isoliert, sondern von anderen Atomen umgeben, die sich gegenseitig beeinflussen und die möglichen elektronischen Übergänge ändern. Die Farbe eines Atoms hängt also stark von der Umgebung ab, in der es sich befindet, und bei der Keramik ausserdem von den Wechselwirkungen gegenüber anderen Bestandteilen der Pasten und Lacke, sowie von den Ofenatmosphären und der Brenntemperatur.But every atom does not give a single color, because the electronic one Systems that make up the atoms are not isolated in matter, but from others Surrounding atoms that influence each other and the possible electronic Change transitions. The color of an atom therefore strongly depends on the environment in which it is located where it is located and, in the case of ceramics, also from the interactions opposite other components of the pastes and varnishes, as well as the furnace atmospheres and the Firing temperature.

Die Möglichkeiten, eine ausgedehnte Reihe von Farbtönen zu erzielen, ändern sich von einer Fabrikationstype zur andern und auch je nach der Dekorationsmethode. Die Festigkeit der Farben ändert sich nach Maßgabe der Erhöhung der Brenntemperatur. Das ist der Grund, weshalb sich die Mannigfaltigkeit und Stärke der Farben bei unter relativ hohen Temperaturen gebrannten Stücken, wie dies bei Porzellan, Steingut, usw. der Fall ist, stark vermindern.The possibilities of achieving an extensive range of shades, vary from one type of manufacture to another and also according to the method of decoration. The strength of the colors changes as the firing temperature increases. That is the reason why the variety and strength of the colors at under pieces fired at relatively high temperatures, as is the case with porcelain, earthenware, etc. is the case, greatly decrease.

Als gewöhnlich verwendete Rohstoffe, um den keramischen Artikeln die gewünschte Farbe zu geben, gibt es die Oxyde der Libergangsmetalle oder Farbstoffpräparate aufgrund von gefärbten Verbindungen, hauptsächlich anorganischer Natur. Mit denselben wird eine im allgemeinen wäßrige Aufschlämmung zubereitet, zusammen mit anderen Bestandteilen, in einem mehr oder weniger feinvermahlenen Zustand, die denjenigen der Pasten ähnlich sind.As commonly used raw materials to make the ceramic articles the To give the desired color, there are the oxides of transition metals or dye preparations due to colored compounds, mainly of an inorganic nature. With the same a generally aqueous slurry is prepared, along with others Ingredients, in a more or less finely ground state, those are similar to pastes.

Die erfindungsgemäße Methode bietet viele Vorteile gegenüber anderen herkömmlichen Verfahren für Dekoration, unter welchen wir folgende hervorheben können: 1. Mit der erfindungsgemäßen Methode wird eine große Regelmässigkeit im Ton erreicht; man erhält Ebenen und Linien mit gleichmäßig dekorierten Oberflächen und besonders schönen Effekten, was zu einem einzigartigen Dekorationsstil führt.The method of the invention offers many advantages over others traditional methods of decoration, among which we can highlight the following: 1. With the method according to the invention, a great regularity in the tone is achieved; you get levels and lines with evenly decorated surfaces and special beautiful effects, resulting in a unique style of decoration.

2. Die sehr einfache Anwendung derselben, wobei keine besonderen Zusätze notwendig sind, um Umrisse zu begrenzen oder ein übermäßiges Fließen der Farbe zu verhindern.2. The very simple application of the same, with no special additives necessary to limit outline or to cause excessive flow of paint impede.

3. Kann direkt auf die rohe oder Fliesenpaste aufgetragen werden, ohne die Einzelheiten der Oberfläche zu verändern, was mit aufgeschlämmten oder gewöhnlichen Farben schwer zu erreichen ist.3. Can be applied directly to the raw or tile paste, without changing the details of the surface, what with slurried or ordinary colors are difficult to achieve.

Die Salzlösungen, die die Grundlage der erfindungsgemäßen Methode bilden, haben Eigenschaften, die die Anwendungsmöglichkeiten anderer Verfahren verbessern und zwar sind es folgende: a) Sie haben eine geeignete Fließfähigkeit für eine zweckmäßige AuStragung, so daß sie weder zu leicht eindringen noch eine übermäíSige Viskosität mit den in diesen Fällen ungünstigen Folgen aufweisen.The salt solutions that form the basis of the method according to the invention form, have properties that improve the application possibilities of other processes namely, they are as follows: a) They have a suitable flowability for a useful one Application so that they neither penetrate too easily nor have excessive viscosity with the adverse consequences in these cases.

b) Der pH-Wert der Lösungen liegt innerhalb des sauren Bereiches, in einer Zone, wo sowohl die möglichen Probelme einer Reaktion mit den kalkhaltigen Pasten, sowie diejenigen bedingt durch fühlbare Temperatur-, Feuchtigkeitsänderungen, usw. der Umgebung praktisch Null sind.b) The pH of the solutions is within the acidic range, in a zone where both the possible problems of a reaction with the calcareous Pastes, as well as those caused by noticeable changes in temperature and humidity, etc. of the environment are practically zero.

c) Bei denselben sind die Hydrolyseerscheinungen auf ein Minimum beschränkt, wodurch deren unangenehme Folgen vermieden werden.c) With these, the hydrolysis phenomena are limited to a minimum, thereby avoiding their unpleasant consequences.

d) Die verwendeten Salztypen haben eine Löslichkeit, um genügend konzentrierte Lösungen zur Erreichung von geeigneten Färbungsstärken zu bekommen.d) The types of salts used have a solubility to be sufficiently concentrated Get solutions to achieve suitable staining strengths.

e) Sie zersetzten sich thermisch mit relativer Leichtigkeit, wodurch das ei'ärbte Oxyd auf dem Keramikkörper einwandfrei verteilt ist.e) They decompose thermally with relative ease, whereby the egg-colored oxide is perfectly distributed on the ceramic body.

Die empfehlenswertesten Salze sind: Acetate, Sulfate, Nitrate, Chloride und andere analoge, deren Löslichkeit und Erhältlichkeit im Handel dieselben als geeignet erscheinen lassen. Das Metall dieser Salze kann je nach der gewünschten Farbe irgendeines der Übergangsmetalle und sogar eine Kombination von zwei oder mehr Metallen, mit gemeinsamen oder verschiedenen Anionen, sein.The most recommended salts are: acetates, sulfates, nitrates, chlorides and other analogs whose solubility and commercial availability are the same as seem suitable. The metal of these salts can vary depending on the desired Color of any of the transition metals and even a combination of two or more more metals, with common or different anions.

Das Lösemittel ist nicht ein einziges, sondern man verwendet im allgemeinen eine Mischung von Substanzen, die fähig sind, die Salze aufzulösen und eine gegenseitige geeignete Mischbarkeit aufweisen. Das gemeinsame Merkmal ihrer chemischen Verbindung besteht darin, daß sie Oxhydrilgruppen in ihren Molekülen haben und schwache Elektrolyte sind. Unter den erfindungsgemäß am meisten verwendeten chemischen Verbindungen sind zu erwähnen: Wasser, Alkohole (Äthanol, Glykole, Glycerin), nichtreduzierende Disaccharidlösungen (wie Saccharose), Säfte, usw.The solvent is not a single one, but is used in general a mixture of substances capable of dissolving the salts and a mutual have suitable miscibility. The common feature of their chemical connection is that they have oxhydryl groups in their molecules and weak electrolytes are. Among the most widely used chemical compounds in the present invention are to mention: water, alcohols (ethanol, glycols, glycerine), non-reducing disaccharide solutions (like sucrose), juices, etc.

Der Anteil einer jeden derselben in den Lösemittelmischungen schwankt je nach der Salzkonzentration des Farbstoffes und der gewünschten Fließfähigkeit. In den Säften und Disaccharidlösungen kann er zwischen 50 und bO %o achwanken. In den alkoholischen wäßrigen Mischungen, kann der Anteil des Wassers bis 70 betragen.The proportion of each of these in the solvent mixtures varies depending on the salt concentration of the dye and the desired flowability. In the juices and disaccharide solutions it can fluctuate between 50 and 50%. In the alcoholic aqueous mixtures, the proportion of water can be up to 70%.

Das allgemeine Verfahren für das Ansetzen der Salzlösungen besteht im Lösen des Salzes oder der Salze in der entsprechenden Wassermenge, die genügend sein muß, und im anschließenden Zusetzen des Restes der Bestandteile des Lösemittels. In anderen Fällen erfolgt die Auflösung unmittelbar im Lösemittelgemisch.The general procedure for preparing the salt solutions is as follows in dissolving the salt or salts in the appropriate amount of water which is sufficient must be, and in the subsequent addition of the remainder of the components of the solvent. In other cases the dissolution takes place directly in the solvent mixture.

Am besten ist es dies bei Raumtemperatur durchzuführen, obwohl es in einigen Fällen notwendig ist, Wärme anzuwenden.It is best to do this at room temperature, even though it is in some cases it is necessary to apply heat.

Die Vervollkommnung der erfindungsgemäßen Methode konnte erst nach dberwindung zahlreicher Schwierigkeiten vor allem praktischer Natur erzielt werden. Hin Beweis für die zahlreichell Schwierigkeiten auf diesem Gebiete ist die Tatsache, daß, wenn auch in der wissenschaftlichen Literatur am Ende des vergangenen Jahrhunderts bereits die Rede von der Möglichkeit des Einsatzes dieser Salzlösungen für die Dekoration von Keramikstükken war, diese Methode doch nicht industriell eingesetzt wurde.The perfection of the method according to the invention could only after overcoming numerous difficulties mainly of a practical nature can be achieved. Hin proof of the numerous Difficulties in this area is the fact that, albeit in the scientific literature at the end of the Last century there was already talk of the possibility of using this Salt solutions for the decoration of ceramic pieces, this method was not was used industrially.

Die Art des Einsatzes dieser Dekorationsmittel kann nach irgendeinem der herkömmlicherweise in der Keramikindustrie angewendeten Verfahren wie durch Spritzen, Eintauchen, mit dem Pinsel, usw. erfolgen. Die Auftragung erfolgt sowohl am rohen wie auch am geformten Stücks Die Vorteile, die mit der erfindungsgemäßen Methode in der Dekoration erzielt werden, übersteigen 50 .The type of use of these decoration means can be according to any one of the processes conventionally used in the ceramics industry such as Spraying, dipping, using a brush, etc. The application takes place both on the raw as well as on the shaped piece The advantages obtained with the inventive Method in decoration exceed 50.

Das erfindungsgemäße Verfahren besteht in der Auflösung besonders von Metallsalzen in Flüssigkeiten wie Wasser, Glycerin, Äthanol, Zuckerlösungen, Säften und anderen ähnlichen Flüssigkeiten.The method according to the invention consists in particular in the dissolution of metal salts in liquids such as water, glycerine, ethanol, sugar solutions, Juices and other similar liquids.

Diese Auflösungen in den erwähnten Flüssigkeiten können mit einer einzigen dieser (flüssigen) Substanzen oder mit einer Mischung derselben erfolgen und ihr Anteil wird nach dem gewünschten Fließfähigkeitsgrad für eine jede derselben und Je nach den klimatischen Umgebungstemperaturen bemessen.These resolutions in the liquids mentioned can be achieved with a only one of these (liquid) substances or with a mixture thereof and their proportion will be according to the desired degree of fluidity for each of them and dimensioned according to the climatic ambient temperatures.

Nach Entnahme des Stückes aus der Form und nach den entsprechenden Klebe- und berarbeitungsprozessen durch fachkundiges Personal erfolgt eine erste Phase des empfohlenen Verfahrens, das darin besteht, daß der Handwerker auf dem Rohstück eine Farblösung aufträgt wie die bereits beschriebenen (je nach dem gewünschten Farb- oder Farbtontyp), bestehend aus hydrierten oder wasserfreien Salzen der Jbergangsmetalle, die im allgerneinen in wäßrigen Mischungen, Glycerin, äthanol, Zuckerlösungen, Säften und ähnlichen Flüssigkeiten, wie bereits erwähnt, aufgelöst werden.After removing the piece from the mold and following the appropriate Gluing and finishing processes by skilled staff are carried out first Phase of the recommended procedure, which consists in the craftsman being on the Apply a color solution to the raw piece as described above (depending on the desired Color or shade type), consisting of hydrogenated or anhydrous salts of transition metals, in general in aqueous mixtures, glycerine, ethanol, sugar solutions, juices and similar liquids, as already mentioned, are dissolved.

Die zum Einsatz gelangenden Lösungen enthalten spezifisch eines oder mehrere der Metallsalze, die in nicht einschränkender Weise wie folgt genannt werden: Kupferacetat (Cu(CHDC00)2; Kupfernitrat (Cu(NO3)2; Kupfersulfat CuSO4; Kupferchlorid CuC12; Kobaltacetat Co(CH3C00)2; Kobaltnitrat Co(NO)2; Kobaltsulfat CoSO4; Kobaltchlorid CoCl2; Chromnitrat Cr(NO3)3; Chromsulfat Cr2 (SO4)3; Chromchlorid CrCl3; Kaliumchromat K2CrO4; Kaliumdichromat K2Cr207; Eisennitrat Fe(NO»)3; Eisensulfat Fe2(SO4)3; Eisenchlorid FeCl3; Manganacetat Mn(CH3COO)2; Mangannitrat Mn(NO3)2; Mangansulfat MnS04; Manganchlorid MnC12; Nickelacetat Ni(CH3COO)2; Nickelnitrat Ni(NO3)2; Nickelsulfat NiSO4; Nickelchlorid NiCl2; Goldchlorid AuCl3.ClH-4H2O; Platinchlorid (Pt Cl6)H2.6H2O; Uranylacetat UO2 (CH3 COO)2; Uranylnitrat U02 (NO5)2.The solutions used contain specifically one or several of the metal salts, which are named in a non-limiting manner as follows: Copper acetate (Cu (CHDC00) 2; copper nitrate (Cu (NO3) 2; copper sulfate CuSO4; copper chloride CuC12; Cobalt acetate Co (CH3C00) 2; Cobalt nitrate Co (NO) 2; Cobalt sulfate CoSO4; Cobalt chloride CoCl2; Chromium nitrate Cr (NO3) 3; Chromium sulfate Cr2 (SO4) 3; Chromium chloride CrCl3; Potassium chromate K2CrO4; Potassium dichromate K2Cr207; Iron nitrate Fe (NO ») 3; Iron sulfate Fe2 (SO4) 3; Ferric chloride FeCl3; Manganese Acetate Mn (CH3COO) 2; Manganese nitrate Mn (NO3) 2; Manganese sulfate MnS04; Manganese chloride MnC12; Nickel acetate Ni (CH3COO) 2; Nickel nitrate Ni (NO3) 2; Nickel sulfate NiSO4; Nickel chloride NiCl2; Gold chloride AuCl3.ClH-4H2O; Platinum chloride (Pt Cl6) H2.6H2O; Uranyl acetate UO2 (CH3 COO) 2; Uranyl nitrate U02 (NO5) 2.

Zum besseren Verständnis der im folgenden vorgeschlagenen Idee werden in einer Tafel die für die Färbung der Rohkeramikstücke im allgemeinen und der geformten Keramikstücke vor dem endgültigen Brennen im besonderen eingesetzten Metallsalzprodukte, gebührend verteilt und geordnet, dargestellt. "METALLSALZE" METALLE ACETATE NITRATE SULFATE CHLORIDE Name Symbol Kupfer Cu Cu(CH3COO)2 Cu(NO3)2 CuSO4 CuCl2 Kobalt Co Co(CH3COO)2 Co(NO3)2 CoSO4 CoCl2 (K2CrO4 Kalium- Chrom Cr -- Cr(NO3)3 Cr2(SO4)3 CrCl3( chromat (K2Cr2O7 Kaliumdi- chromat Eisen Fe -- Fe(NO3)3 Fe2(SO4)3 FeCl3 Mangan Mn Mn(CH3COO)2 Mn(NO3)2 MnSO4 MnCl2 Nickel Ni Ni(CH3COO)2 Ni(NO3)2 NiSO4 NiCl2 Gold Au -- -- -- Au Cl3.ClH.4H2O Platin Pt -- -- -- (Pt Cl6)H2.6H2O Uran U UO2(CH3COO)2 UO2(NO3)2 -- -- (Uranylace- (Uranyl- tat) nitrat) Nach Beschreibung der Natur der Erfindung soll noch darauf hingewiesen werden, daß sich dieselbe nicht auf die genauen Einzelheiten dieser Darstellung beschränkt, sondern daß im Gegenteil in derselben diejenigen änderungen an Einzelheiten vorgenommen werden können, die wegen der Verhältnisse oder der praktischen Handhabung als ratsam erscheinen, sofern die wesentlichen Merkmale des beschriebenen Verfahrens nicht geandert werden.For a better understanding of the idea proposed below, the metal salt products used for coloring the raw ceramic pieces in general and the shaped ceramic pieces in particular before the final firing, appropriately distributed and arranged, are shown in a table. "METAL SALTS" METALS ACETATE NITRATE SULPHATE CHLORIDE Name symbol Copper Cu Cu (CH3COO) 2 Cu (NO3) 2 CuSO4 CuCl2 Cobalt Co Co (CH3COO) 2 Co (NO3) 2 CoSO4 CoCl2 (K2CrO4 potassium Chromium Cr - Cr (NO3) 3 Cr2 (SO4) 3 CrCl3 (chromat (K2Cr2O7 potassium di- chromate Iron Fe - Fe (NO3) 3 Fe2 (SO4) 3 FeCl3 Manganese Mn Mn (CH3COO) 2 Mn (NO3) 2 MnSO4 MnCl2 Nickel Ni Ni (CH3COO) 2 Ni (NO3) 2 NiSO4 NiCl2 Gold Au - - - Au Cl3.ClH.4H2O Platinum Pt - - - (Pt Cl6) H2.6H2O Uranium U UO2 (CH3COO) 2 UO2 (NO3) 2 - - (Uranylace- (uranyl- tat) nitrate) After describing the nature of the invention, it should be pointed out that the same is not limited to the exact details of this representation, but that, on the contrary, those changes to details can be made in the same which appear advisable due to the circumstances or practical handling, provided that the essential characteristics of the procedure described are not changed.

Patentansprüche: Patent claims:

Claims (4)

P A T E N T A N S P R Ü C H E 1. Verfahren für die Dekoration von Rohkeramikstücken, dadurch gekennzeichnet, daß anfänglich, wenn das Stück der Form entnommen wird, nach den Klebe- und Uberarbeitungsphasen, im wesentlichen auf den rohen Stücken und in besonderen Fällen auf den geformten Stücken, von Hand mit dem Pinsel, durch Eintauchen, Spritzen oder auf irgendeine andere zweckmäßige Weise eine Deckschicht der Farblösung in reichhaltigster Farbenreihe und im gewünschten Ton und Dichte aufgetragen wird. P A T E N T A N S P R Ü C H E 1. Process for the decoration of Raw ceramic pieces, characterized in that initially when the piece of the mold is removed, after the gluing and reworking phases, essentially on the raw pieces and in special cases on the shaped pieces, by hand with the Brush, dipping, splashing, or any other convenient means a top layer of the color solution in the richest color range and in the desired Clay and density is applied. 2. Verfahren für die Dekoration von Rohkeramikstücken nach Anspruch 1, dadurch gekennzeichnet, daß diese Lösung aus hydrierten oder wasserfreien Salzen der Übergangsmetalle besteht, welche im allgemeinen in wäßrigen Mischungen, Glycerin, Athanol, Zuckerlösungen, Säften und ähnlichen Flüssigkeiten aufgrund folgender Lösungsskalen gelöst werden, welche Lösung durch einfachen oder kombinierten Einsatz eines oder mehrerer der angegebenen Produkte gewonnen wird: METALLE ACETATE NITRATE SULFATE CHLORIDE Name Symbol Kupfer Cu Cu(CH3COO)2 Cu(NO3)2 CuSO4 CuCl2 Kobalt Co Co(CH3COO)2 Co(NO3)2 CoSO4 CoCl2 (K2CrO4 Kalium- Chrom Cr -- Cr(NO3)3 Cr2(SO4)3 CrCl3( chromat (K2Cr2O7Kaliumdi- chromat Eisen Fe -- Fe(NO3)3 Fe2(SO4)3 FeCl3 Mangan Mn Mn(CH3COO)2 Mn(NO3)2 MnSO4 MnCl2 Nickel Ni Ni(CH3COO)2 Ni(NO3)2 NiSO4 NiCl2 Gold Au -- -- -- Au Cl3.ClH.4H2O Platin Pt -- -- -- (Pt Cl6)H2.6H2O Uran U UO2(CH3COO)2 UO2(NO3)2 -- -- (Uranylace- (Uranyl- tat) nitrat)
2. A method for the decoration of raw ceramic pieces according to claim 1, characterized in that this solution consists of hydrogenated or anhydrous salts of the transition metals, which are generally dissolved in aqueous mixtures, glycerine, ethanol, sugar solutions, juices and similar liquids due to the following solution scales, which solution is obtained by simple or combined use of one or more of the specified products: METALS ACETATE NITRATE SULPHATE CHLORIDE Name symbol Copper Cu Cu (CH3COO) 2 Cu (NO3) 2 CuSO4 CuCl2 Cobalt Co Co (CH3COO) 2 Co (NO3) 2 CoSO4 CoCl2 (K2CrO4 potassium Chromium Cr - Cr (NO3) 3 Cr2 (SO4) 3 CrCl3 (chromat (K2Cr2O7 potassium di- chromate Iron Fe - Fe (NO3) 3 Fe2 (SO4) 3 FeCl3 Manganese Mn Mn (CH3COO) 2 Mn (NO3) 2 MnSO4 MnCl2 Nickel Ni Ni (CH3COO) 2 Ni (NO3) 2 NiSO4 NiCl2 Gold Au - - - Au Cl3.ClH.4H2O Platinum Pt - - - (Pt Cl6) H2.6H2O Uranium U UO2 (CH3COO) 2 UO2 (NO3) 2 - - (Uranylace- (uranyl- tat) nitrate)
3. Vefahren für die Dekoration von Rohkeramikstücken nach Anspruch 1, dadurch gekennzeichnet, daß die entsprechenden Teile des Stückes mit der geforderten Farbe und Verzierung dekoriert erden.3. The method for the decoration of raw ceramic pieces according to claim 1, characterized in that the corresponding parts of the piece with the required Earth decorated with color and ornament. 4. Verfahren für die Dekoration von Rohkeramikstücken nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, da3 das in der Lösung eingetauchte oder imprägnierte und dekorierte Stück nach Aufnahme dieser Substanzen durch den verwendeten Werkstoff dem Brennen zugeführt wird, wobei die einer Temperatur von 1D30 bis 1400°C ausgesetzten Salze sich thermisch zersetzen und Metalloxid in den größten Teil der Nasse des Stückes eindringt, wodurch sich eine äußere Oberfläche ergibt, die gleichmäßig und kontinuierlich gefärbt und mit der übrigen Masse fest verbunden ist.4. Process for the decoration of raw ceramic pieces according to one of the preceding claims, characterized in that the immersed in the solution or impregnated and decorated pieces after these substances have been absorbed by the The material used is fed to the firing, with a temperature of 1D30 to 1400 ° C exposed salts decompose thermally and metal oxide in the Most of the wetness of the piece penetrates, creating an outer surface results that are evenly and continuously colored and solid with the rest of the mass connected is.
DE19712117449 1971-04-08 1971-04-08 Decorating raw ceramic articles - with solns of metal salts Pending DE2117449A1 (en)