DE2045182A1

DE2045182A1 - Pressure transfer sheet and method of making it

Info

Publication number: DE2045182A1
Application number: DE19702045182
Authority: DE
Inventors: Robert John Tranmere South Australia Wnght (Australien)
Original assignee: Research Laboratories of Australia Pty Ltd
Current assignee: Research Laboratories of Australia Pty Ltd
Priority date: 1969-09-15
Filing date: 1970-09-12
Publication date: 1971-03-25
Also published as: NL7013575A; BE756189A; AT300855B; CA930255A; FR2061429A5; GB1320526A; CH530280A; DK124867B; ZA706214B; NO129617B; ES383627A1

Description

"Druckübertragungsblatt und Verfahren zu seiner Herstellung""Pressure transfer sheet and method of making it"

Die Erfindung befaßt sich allgemein' mit Vervielfältigungsverfahren und Vervielfältigungsmitteln und im besonderen mit einem Verfahren und Mitteln, durch die die Abbildungsschärfe verbessert werden kann, und zwar besonders in einem Informations-Reproduktions-Verfahren, in dem gleichzeitig mehrere Kopien durch'Druckübertragung angefertigt werden.The invention is generally concerned with methods of reproduction and reproduction means and in particular with a method and means by which the image sharpness can be improved, especially in an information reproduction process, in which several copies are made at the same time by means of pressure transfer.

In einer Vielzahl unterschiedlicher Fällen besteht ein Bedarf nach Kopien von Informationen, und solche multiplen Kopien sollen üblicherweise mögliehst gleichzeitig erstellt werden. Es ist beispielsweise sehr bekannt, solche Multi-There is a need for copies of information in a variety of different cases, and such multiple copies are usually intended to be made at the same time as possible. It is well known, for example, that such multi-

109813/1202109813/1202

kopien oder Mehrfachkopien gleichzeitig unter Verwendung einer Schreibmaschine oder einer Ausdruckvorrichtung eines Rechners herzustellen. Eine solche gleichzeitige Herstellung von Kopien wird dadurch ausgeführt, daß die Blätter oder Bögen·, auf die die Information aufgezeichnet werden soll., in Berührung mit einer Schicht aus einer pigmentierten oder sonstwie einge- färbten Stoffzusammenstellung gebracht und dabei in einem Stapel angeordnet v/erden_s der die für die Erzeugung der verlangten Zahl von Kopien ausreichende Zahl von Blättern enthält» Der Stapel wird auf eine geeignete Unterlage gebracht und eine Drucktype mit der den geforderten Buchstaben oder Zeichen entsprechenden Vorderfläche wird in Berührung mit der anderen Seite des Stapels, die also nicht mit der Unterlage in Berührung steht₉ gebracht. Durch Anwendung einer Relativbewegung sxtfisehen der Unterlage und der Drucktype wird ein Druck übertragen _s wobei entweder die Unterlage oder die Drucktype gegen das jeweils andere Element bewegt wird, und zwar so, daß ein scharfer Schlag entsteht.make copies or multiple copies at the same time using a typewriter or a computer printout device. Such a simultaneous production of copies is carried out in that the sheets or sheets on which the information is to be recorded are brought into contact with a layer of a pigmented or otherwise colored composition of matter and thereby arranged in a stack _s that contains the number of sheets sufficient to produce the required number of copies »The stack is placed on a suitable surface and a type of printing with the front surface corresponding to the required letters or characters is in contact with the other side of the stack, which is not is brought into contact with the substrate _9. By applying a relative movement of the pad sxtfisehen and the printing type is transmitted, a pressure _s wherein either the base or the printing type is moved against the respective other element, in such a way that a sharp impact is created.

Ein Nachteil des vorgeschriebenen Verfahrens liegt in der Geometrie des Stoßes bzw., der Einwirkung» Die erhabene Typenfläehe bildet einen verhältnismäßig scharfen Eindruck auf den zwei oder drei Blättern, die derjenigen Seite des Stapels am nächsten liegen, die der Typenfläche benachbart ist. Der Kantenverlauf des Eindrucks wird schrittweise weniger scharf, und swar SO₅-,wie der Eindruck durch den Stapel in Richtung auf die Unterlage fortschreitet. Dieses Merkmal wird weitgehend durch die verhältnismäßig ebene Form der Unterlage bewirkt, die die Zerstreuung der Stoßkräfte betont und hervorhebt, da bzw. wie die Blätter zunehmend weiter von der Fläche der Drucktype entfernt liegen oder sich entfernen. Die normalen Stoßkräfte können auch weiter durch die Eigenschaften des Papiers und der Zwischenlagen (Gewebe, Kohlepapier, Vervielfältigungspapier), wie sie für die Vervielfältigung benutzt werden, zerstreut werden« und zwar sogar dann, wenn besonders ausgewählte Papiere und Durchschlagpapiere (oder andersartige Zwischenlagen) verwendet werden« Normalesweise erlauben die Anforderungen an dieA disadvantage of the prescribed method lies in the geometry of the joint or the action. The raised type area forms a relatively sharp impression on the two or three sheets that are closest to the side of the stack that is adjacent to the type area. The edge contour of the indentation gradually becomes less sharp, and swar SO ₅ - as the indentation progresses through the stack towards the substrate. This feature is largely caused by the relatively planar shape of the pad, which emphasizes and emphasizes the dispersion of the impact forces as the sheets become progressively further removed from the face of the type or as they move away. The normal impact forces can also be further dissipated by the properties of the paper and the interlayers (fabric, carbon paper, duplicating paper) used for duplication, even if specially selected papers and cleavage papers (or other interleaving paper) are used will «Normally, the requirements for the

_ TC __ TC _

Lesbarkeit die Erzeugung von höchstens etwa zehn Kopien, besonders bei den allgemein in Gebrauch befindlichen Ausdruckvorrichtungen von Rechnern.Legibility the creation of a maximum of about ten copies, especially in the commonly used printing devices of computers.

Ein weiteres Merkmal dieses Stoßzerstreuungseffektes ist die Verminderung in der Normalstoßkraft oder dem Normalstoßdruck, die bzw. der den Verlust an Kantenschärfe begleitet. Dadurch wird die Wirksamkeit der Übertragung vermindert und es entsteht die Notwendigkeit, daß das Kohlepapier oder ein anderes Farbübertragungsmedium auf seiner Oberfläche einen schwereren oder dickeren Niederschlag des färbenden Stoffes enthält, als es notwendig wäre, wenn die gesamte Faksimileübertragung durch den ganzen Stapel erzielt werden könnte, wenn also ohne Schärfeverlust eine getreue Wiedergabe des Typenumrisses möglich wäre. Dadurch werden die Kosten für das Durchschlagpapier oder derglaichen sehr viel höher, als es notwendig wäre, wenn ein wirksameres übertragungssystem benutzt werden könnte. Es können zwar Durchschlagpapiere geschaffen werden, die unter Übertragungsdruck den Farbstoff sehr viel leichter · abgeben, aber solche Durchschläge lassen sich schlecht handhaben, eben' weil sie ihre Pigmentablagerung so leicht abgeben, diese also so leicht entfernt werden kann.Another feature of this shock dispersion effect is that Decrease in normal impact force or pressure accompanying the loss of edge sharpness. Through this the efficiency of the transfer is decreased and the need arises that the carbon paper or another Color transfer medium contains a heavier or thicker deposit of the coloring substance on its surface than it would be necessary if all facsimile transmission could be accomplished through the whole batch, if so without Loss of sharpness a faithful reproduction of the type outline is possible were. This makes the cost of the copy paper or the like much higher than necessary would be if a more efficient transmission system could be used. Carbon papers can be created, which release the dye much more easily under transfer pressure, but such copies are difficult to handle, precisely because they give off their pigment deposits so easily, it can be removed so easily.

Die vorliegende Erfindung lehrt ein Verfahren, durch das die nachteiligen Wirkungen der Übertragungsgeometrie möglichst klein gemacht werden; zusätzlich liefert die Anwendung der Lehre der Erfindung ein Kohleübertragungsblatt oder ein anderes Übertragungsblatt, das verbesserte aber gesteuerte Abgabeeigenschaften hat, die die Handhabung des übBrtragungsblattes erlauben, ohne daß übermäßig viel Farbsubstanz vom Blatt auf andere Objekte verlagert wird, die mit der beschichteten Oberfläche des Blattes in Berührung kommen.The present invention teaches a method by which the adverse effects of the transmission geometry are made as small as possible; in addition, the application of the Teaching of the invention a carbon transfer sheet or another Transfer sheet that has improved but controlled dispensing properties that allow handling of the transfer sheet, without excessive color substance being shifted from the sheet to other objects with the coated surface of the sheet come into contact.

Gemäß der vorliegenden Erfindung wird ein Gewebe oder eine andere Oberfläche, insbesondere ein Papier für einen Kohleüberzug oder FarbstoffÜberzug dadurch vorbereitet, daß zuerst According to the present invention, a fabric or a other surface, in particular a paper for a carbon coating or dye coating prepared by first

■ 1098 13/1?0?■ 1098 13/1? 0?

2045 Ί2045 Ί

die Oberfläche in gemusterter Form mit einem Trägermaterial oder Substrat überzogen wird, das eine andere Affinität zu dem Kohleüberzug als die Originalpberflache hat. Ein solches Substrat wird mit bekannten Mitteln aufgetragen, beispielsweise durch Rasterdruck, durch Buchstabendruck, durch Flexografie oder dergleichen, und zwar, wie gesagt, in gemusterter Form, also beispielsweise unter Verwendung eines 5Q%-P\xnktrasters mit 150 Linien pro Zoll der Rasiergröße. Es wurde gefunden, daß das Auflösungsvermögen mit Rastern verbessert wurde, die so grob wie ein 100 Linien/Zoll-Raster waren, und obgleich Raster feiner als 150 Linien mit vorteilhafter Wirkung verwendet werden können, falls dies verlangt wird, erwies sich für die meisten Zwecke ein 150-Linien-Raster als ausreichend fein, überdies muß das -Muster oder Raster, wie es gedruckt ist, nicht notwendigerweise ein 50^-Punktraster sein, jedoch sollte-es so beschaffen sein, daß die Flächenbereiche, von denen die Farbsubstanz (Kohle) letztlich abgegeben oder losgelassen werden soll, die Form von unzusammenhängenden, gleichmäßigen Punkten oder Flecken hat, die rechteckig, quadratisch, rund oder abgerundet sein können. In Fällen, in denen das gemusterte oder gerasterte Material eine leichtere Abgabe der farbgebenden Schicht erlaubt, sollte es somit diskontinuierlich sein, wogegen in jenen Fällen, in denen das gemusterte Material das farbgebende Material nicht so deutlich oder bereitwillig wie die Unterlage abgibt.oder losläßt, das Muster kontinuierlich sein sollte, und zwar mit unterbrochenen Flächenteilen der oben beschriebenen bevor- . zugten Gestalt, die als nicht beschichtete Flächenbereiche innerhalb des Musters eingeschlossen sein sollten.the surface is coated in patterned form with a carrier material or substrate which has a different affinity for the carbon coating than the original surface. Such a substrate is applied by known means, for example by raster printing, by letter printing, by flexography or the like, namely, as mentioned, in patterned form, for example using a 50% dot screen with 150 lines per inch of the razor size . It has been found that resolution was improved with screens as coarse as a 100 line / inch screen, and although screens finer than 150 lines can be used to advantage if required, this has been found for most purposes a 150-line screen is sufficiently fine, moreover the pattern or screen as it is printed need not necessarily be a 50 ^ dot screen, but it should be such that the areas of which the color substance (charcoal ) is ultimately to be released or released, which has the form of disjointed, even points or spots that can be rectangular, square, round or rounded. In cases in which the patterned or screened material allows an easier release of the coloring layer, it should thus be discontinuous, whereas in those cases in which the patterned material does not release the coloring material as clearly or willingly as the base. Or lets go, the pattern should be continuous, with interrupted areas of the above-described before. added shape, which should be included as uncoated areas within the pattern.

Der Überzug, hier der Einfachheit halber "Kohleüberzug" genannt, wird als gleichmäßige Schicht aufgebracht, die das gedruckte oder anders erzeugte Substratmuster überdeckt, also darauf aufliegt, und sie hat Loslaß- oder Abgabeeigenschaften, die in Raster- oder Musterform variieren. Wenn ein solches mit Kohle überzogenes Blatt zur Druckübertragung in einem Druckverfahren benutzt wird, wird die Abgabe von Kohle in weitem Maße be-The coating, here called "carbon coating" for the sake of simplicity, is applied as an even layer that covers the printed or otherwise produced substrate pattern is covered, that is, rests on it, and it has release or release properties that are shown in The grid or pattern shape may vary. If such a sheet coated with carbon for transferring pressure in a printing process is used, the delivery of coal is to a large extent

10 9 8 13/170?10 9 8 13/170?

grenzt auf solche Flächenteilei in denen die Bindung zwischen dem Kohleüberzug und der Unterlage am geringsten ist. Wenn ein solches Kohleblatt oder Kohlepapier oder Durchschlagpapier . für die übertragung von Druck in einem Druckverfahren benutzt wird, erlaubt die kontrollierte oder gesteuerte Abgabe die Erzeugung einer Kopie, deren Abbildkanten verhältnismäßig schärfer sind, als sie ohne Verwendung dieses neuen Substrates entstehen würden, da das Abgabemuster oder die Verteilung das · Muster der Abgabe oder Freigabe von Farbstoff tatsächlich im · wesentlichen gleichmäßige Frakturlinien (unterbrochene Linien) in dem Kohleüberzug erzeugt, wenn Druck aufgebracht wird. Vorausgesetzt, daß das Rastermuster genügend fein ist, wird der Verlauf der Kanten des Druckübertragungsbildes ganz scharf festgelegt (definiert) sein und somit sollte das Rastermuster vorzugsweise wenigstens so fein wie 100 Linien/Zoll sein.borders on such surface parts in which the bond between the carbon coating and the base is the least. If such a carbon sheet or carbon paper or carbon paper . is used for the transfer of pressure in a printing process, allows the controlled or controlled release the production of a copy whose image edges are relatively sharper than they would be without using this new substrate would arise because the delivery pattern or distribution would Pattern of the release or release of dye actually in the substantial even fracture lines (broken lines) generated in the carbon coating when pressure is applied. Provided that the screen pattern is sufficiently fine, will the course of the edges of the print transfer image should be very sharply defined (defined) and thus the raster pattern should preferably at least as fine as 100 lines / inch.

Als weiterer Vorteil der vorliegenden Erfindung erlaubt der Kohleüberzug, für den die Zusammensetzung angegeben wird, eine vollständige Abgabe des Farbstoffes in solchen Fällen, in· denen diese Abgabe unter abgewandelten oder mäßigeren Drücken gewünscht wird, ohne daß dadurch Schwierigkeiten bei der mechanischen Handhabung entstehen, da die Flächenbereiche, in denen die Abgabe nicht verlangt wird, tatsächlich und wirksam den Verschmierungswiderstand oder die Festigkeit der Kohleablagerung gegen Verschmieren erhöhen. Demnach ist es bei Benutzung dieser Erfindung auch möglich, das Gewicht des Kohleniederschlags auf der Unterlage, also dem Kohlepapier oder einem anderen blattförmigen Träger, zu vermindern und dennoch klar urnrissene, deutliche Druckübertriagungsbilder annehmbarer Dichte zu erreichen.As a further advantage of the present invention allows Coal coating for which the composition is specified, one Complete release of the dye in those cases in which this release takes place under modified or more moderate pressures is desired without causing difficulties in the mechanical handling arise because the surface areas in which the delivery is not required, actual and effective the smear resistance or the strength of the carbon deposit increase against smearing. Accordingly, using this invention, it is also possible to measure the weight of the coal deposit on the base, i.e. the carbon paper or another sheet-shaped carrier, to be reduced and yet to achieve clearly delineated, distinct pressure transmission images of acceptable density.

Ein weiteres Merkmal dieser Erfindung ist die Möglichkeit, in Rasterform oder gemusterter Form auf das Unterlagsblatt ein ■ Substratmaterial aufzudrucken, das nach Bedarf die Kohleabgabe entweder unterstützt oder hindert. Dadurch wird der Bereich der auswählbaren und in Betracht kommenden Unterlags-Another feature of this invention is the ability to in To print a substrate material on the backing sheet in a grid form or patterned form, which, as required, releases the coal either assists or hinders. As a result, the area of the selectable and relevant document

' 1 09811/ I20?'1 09811 / I20?

blätter oder Basisblätter, die beispielsweise für umgekehrte oder entgegengesetzte Kohledruckübertragung anwendbar sind, wesentlich erweitert, da ein Blatt mit schwachem Kohleabgabevermögen mit einem Substratmaterial mit verstärkten oder stärkeren Kohleabgabefähigkeiten in gemusterter o.der gerasterter Form überzogen werden kann, während ein Material mit einem Kohleabgabevermögen,das zu einer schwierigen Handhabung führt j eine Abgabebremse haben kann, die in Musteroder Rasterform vor dem Kohleüberzug aufgetragen wird, wodurch vorteilhafterweise ein gutes Kohleabgabevermögen der Basis möglich gemacht wird, ohne daß dadurch Schwierigkeiten für die Handhabusg in das Durchschlagmaterial hineingebracht werden οsheets or base sheets, which can be used, for example, for reverse or reverse carbon pressure transfer, significantly expanded, as a sheet with poor carbon releasing capacity with a substrate material with reinforced or stronger charcoal release capabilities in patterned or rasterized form can be coated while a material with a charcoal releasing ability that makes it difficult to handle leads j can have a release brake that is applied in pattern or grid form in front of the carbon coating, whereby advantageously, a good charcoal dispensing capacity of the base is made possible without thereby causing difficulties be brought into the coping material for handling ο

Um das volle Verständnis der vorliegenden Erfindung sicherer zu machen, wird sie nachstehend anhand der beigefügten Zeichnung erläutert. Darin zeigen:In order to make the present invention more certain to be fully understood, it will be described below with reference to the accompanying drawings explained. Show in it:

Fig, I einen Querschnitt eines DurchschlagmaterialsFigure I shows a cross section of a penetration material

(Papier oder Gewebe) (tissue) in Übereinstimmung mit der vorliegenden Erfindung unter Anwendung herkömmlicher Beschichtungstechnik,(Paper or tissue) (tissue) in accordance with the present invention using conventional coating technology,

Fig. 2 einen Querschnitt eines Durchschlagmaterials,2 shows a cross section of a penetration material,

das gemäß der Erfindung hergestellt ist und einen pigmentierten, durch Druck übertragbaren Überzug aufweist, der auf die ein Substrat tragende Basis unter Anwendung elektrostatischer Beschichtungstechnik aufgetragen oder aufgeschichtet ist.made in accordance with the invention and a pigmented, pressure transferable coating having the base carrying a substrate using electrostatic coating technology applied or piled up.

Fig. 3 den übertragungsmechanismus gemäß der Erfindung.3 shows the transmission mechanism according to the invention.

Wie Fig. 1 zeigt, ist eine Papiergrundlage (also ein Papierblatt) 1 auf einer Seite mit einem gemusterten oder gerasterten überzug 2 aus einem Werkstoff versehen_s dessen Abgabeeigenschaften in Bezug auf den nachfolgend aufgebrachten_s pigmentierten, durch Druck übertragbaren überzug 3 von' denjenigen der Papierbasis (Papiergrundlage) 1 abweichen.As Fig. 1 shows, a paper base (ie, a paper sheet) 1 on one side with a patterned or rasterized coating 2 is _s provided of a material whose release properties with respect to the subsequently applied _s pigmented transmitted by pressure coating 3 of 'those of the Paper base (paper base) 1.

10 9 8 11/12 0?10 9 8 11/12 0?

Aus Pig. 2 ist ersichtlich, daß die Anwesenheit eines gemusterten Substrates 2 mit höherem spezifischem elektrischem Widerstand _a als ihn das Unterlagspapier hat, eine elektrostatische Ablagerung in denjenigen Flächen hemmt oder hindert, die sich in dem pigmentierten, durch Druck übertragbaren Überzug ergeben, der eine größere Dicke als in jenen, nicht durch den gerasterten oder gemusterten Substratüberzug 2 überdeckten Fläehenteilen der Unterlage 1 hat. From Pig. 2 it can be seen that the presence of a patterned substrate 2 having a higher electrical resistivity _a than the base paper inhibits or prevents electrostatic deposition in those areas which result in the pigmented pressure transferable coating which is thicker than in those parts of the surface of the base 1 which are not covered by the screened or patterned substrate coating 2.

In Fig. 3 ist mit 4 ein Papierblatt bezeichnet, auf das ein Bild gedruckt werden soll, und zwar unter Benutzung von übertragungsverfahren, bei denen Drücke benutzt werden; die gekrümmte Linie 5 gibt den ungleichmäßigen Druck wieder; das I Durchschreibepapier gemäß der Erfindung erlaubt die Erzeugung scharfer Kanten und Linien auf dem durch Drucken geschaffenen Bild, also dem gedruckten Bild, wie es in dem Bildniederschlag 6 gezeigt ist.In Fig. 3, 4 denotes a paper sheet on which a Image is to be printed using transmission methods where pressures are used; the curved line 5 shows the uneven pressure; the I Carbonless paper according to the invention allows the creation of sharp edges and lines on that created by printing Image, i.e. the printed image, as shown in the image deposit 6.

Es wurde auch gefunden, daß es vorteilhaft wenngleich nicht notwendig ist, den Kohleüberzug unter dem Einfluß eines elektrostatischen Feldes aufzubringen. Dies erlaubt die Herstellung eines Kohleüberzuges, in dem die Scherkraft des Überzuges normal zur Basis oder Unterlage (1) geringer als die Bindekraft zwischen der Basis und der Kohleschicht ist. Dies erlaubt ferner die Ablagerung von Kohle in solchen . ^ Flächenbereichen, von denen aus die übertragung nicht stattfinden soll, und zwar so, daß dieser überzug oder Niederschlag oder diese Ablagerung geringer als in jenen Flächen ist, von denen aus die Übertragungsablagerung stattfinden soll, und zwar insbesondere dann, wenn das Substratmaterial so ausgewählt worden ist, daß die elektrische Leitfähigkeit der Flächenbereiche, von denen aus die Kohleübertragung ausgeführt werden soll, anders als von denjenigen Flächenbereichen ist, von denen aus oder von denen her keine übertragung stattfinden soll. Diese gemeinsam angewandten Merkmale erhöhen noch weitergehend die Rand- oder Kantenschärfe des durch Druck oder durch Drücke übertragenen Bildes undIt has also been found to be beneficial, although not is necessary to coat the coal under the influence of a Apply electrostatic field. This allows manufacture a carbon coating in which the shear force of the coating normal to the base or support (1) is less than is the binding force between the base and the carbon layer. This also allows coal to be deposited in them. ^ Areas from which the transfer should not take place, in such a way that this coating or precipitation or this deposit less than in those areas from which transfer deposition is to take place, particularly when the substrate material is has been selected so that the electrical conductivity of the surface areas from which the carbon transfer is carried out is different from those areas from which or from which no transmission to be held. These jointly applied features increase the edge or edge sharpness even further the image transferred by pressure or pressure, and

109813/170?109813/170?

vermindert den unnützen Verbrauch von Kohle durch Beschränkung der Menge₃ die in jenen Plächenbereichen abgelagert wird, von denen aus eine Übertragung nicht gefordert ist.reduces the unnecessary consumption of coal by limiting the amount ₃ that is deposited in those areas of the surface from which transfer is not required.

Verschiedene Substratwerkstoffe mit Kohleabgabevermögen, die von denjenigen des Papiers oder eines anderen Untergrundmaterials verschieden sind, konnten als brauchbar im Sinne der Grundzüge dieser Erfindung gefunden werden. Diese Werkstoffe sind auf verschiedene Unterlagen in gemusterter oder gerasterter Form zur Bildung eines Substrates aufgetragen worden und dann wurde darüber eine bei Anwendung von Drücken farbstoffabgebende Mischung, also eine Kohledrückabgabemischung geschichtet. Hier ist.darauf hinzuweisen, daß der Ausdruck "Kohledruckabgabemischung" in dieser Offenbarung in einem allgemeinen Sinne verstanden werden soll und gemeint ist, und daß der Ausdruck "Kohlepapier" allgemein Verwendung findet, und zwar selbst dann, wenn der jeweils betrachtete, durch Farbstoffabgabe ansprechende Überzug keinen Kohlenstoff als färbendes Material enthält. Ferner ist für die hier vorliegende Übersetzung ins Deutsche darauf hinzuweisen, daß in der die Priorität begründenden, englisch sprachigen Fassung nebeneinander, jedoch in verschiedenem Sinne die Wörter "pressure" und "printing" gebraucht sind, für die in der deutschen Übersetzung nur das Wort "Druck" zur Verfügung steht. Im vorliegenden Falle soll aber das Drucken durch Anwendung von Drücken geschehen, so daß dieser Unterschied hier nicht erheblich ist.Various substrate materials with carbon releasing capacity that are different from those of the paper or another background material, could be considered useful in the sense of the principles of this invention can be found. These materials are patterned or on various documents screened form has been applied to form a substrate and then one was applied over it with the application of pressure layered dye-donating mixture, i.e. a charcoal press-release mixture. It should be pointed out here that the The term "coal pressure delivery mixture" in this disclosure is intended to be understood and meant in a general sense and that the term "carbon paper" is used in general, even if the respective dye-releasing coating under consideration does not contain carbon as Contains coloring material. Furthermore, it should be pointed out for the present translation into German that in the Priority justifying, English-language version next to each other, but in different senses the words "pressure" and "printing" are used for which only the word "Druck" is available in the German translation. In the present In this case, however, the printing should be done by applying pressure, so that this difference is not significant here.

Werkstoffe, die in Versuchen im Zusammenhang mit der Ausführung der Erfindung in Form von Mustern oder Rastern auf verschiedene Papierstapel benutzt worden sind, die eine größere Affinität für den Kohleüberzug als diejenige des nicht überzogenen Papieres haben, schließen folgende Stoffe ein: Zellulose-Harze, Vinyl-Akryl-Emulsionen,Silikone und dergleichenj demgegenüber sind Stoffe, die Flächenbereiche schwächerer Bindungskraft als der nicht überzogene oder nicht beschichtete Stapel schaffen, unter anderem folgende: Molybdän-Sulfid, Polytetrafluoräthylen,Materials used in experiments in connection with the implementation of the invention in the form of patterns or grids on different Stacks of paper have been used which have a greater affinity for the carbon coating than that of the uncoated Paper include: cellulosic resins, vinyl-acrylic emulsions, silicones and the like, on the other hand are substances that create surface areas with a weaker binding force than the uncoated or uncoated stack, including the following: molybdenum sulfide, polytetrafluoroethylene,

1098 1 3/12021098 1 3/1202

- -■■?■-■- - ■■? ■ - ■

fluoriertes Äthylen-Propylen und dergleichen. Diese Stoffe wurden in Musterform auf verschiedene Unterlagen aufgeschichtet, so beispielsweise auf Zwiebelhaut, gebundenes Papier (bond paper), Bankpapier (bank paper), Papier als Basis für die Elektrofotografie, mit Ton oder anderer Schlämme überzogenes . Stapelpapier und dergleichen. Die gerasterten überzüge sind geschaffen worden durch Letterdruckverfahren, Schablonendruckverfahren (stencil printing methods), Rasterdruckverfahren und dergleichen.fluorinated ethylene-propylene and the like. These substances were piled up in the form of a sample on various substrates, for example on onion skin, bond paper, bank paper, paper as Base for electrophotography, coated with clay or other sludge. Stack paper and the like. The rasterized Coatings have been created by letter printing methods, stencil printing methods, and halftone printing methods and the same.

Die Kohleüberzüge sind auf die gerasterte Abgabeseite der /^ Unterlage durch Aufbürsten, Aufsprühen, kaltes oder heißes Aufwalzen und dergleichen aufgetragen worden, und es wurden auch zusätzlich elektrophorethische Beschichtungsmethoden mit den oben beschriebenen Vorteilen angewandt. Die verwendeten Kohleüberzüge bestanden allgemein aus der gut bekannten Art, die Pigment, synthetisches oder natürliches Wachs, Petroleum-Gelee, nicht trocknende öle, nicht trocknende synthetische Harze und dergleichen enthält. In vorteilhafterweise werden auch Stoffe, die die Polarität steuern, eingeschlossen, wenn verlangt wird, daß der Kohleüherzug . ' durch elektrophorethische Ablagerungsmethoden geschaffen wird.The charcoal covers are on the gridded delivery side of the / ^ Backing has been applied by brushing, spraying, cold or hot rolling and the like, and have been electrophoretic coating methods with the advantages described above are also used in addition. The used Charcoal coatings have generally been of the well-known type including pigment, synthetic or natural Wax, petroleum jelly, non-drying oils, non-drying ones synthetic resins and the like. Advantageously, substances that control polarity are also used included if the coal train is required. ' is created by electrophoretic deposition methods.

Die Zusammensetzung des Kohleüberzuges kann variiert werden, um mehr oder weniger starke Haftung an der Papierunterlage herbeizuführen und um unterschiedliche Grade des Widerstandes gegen ein Verschmieren zu schaffen. Solche Abwandlungen der Zusammensetzung haben Einfluß auf die Wahl des gerasterten Abgabestoffes, der als Substrat vor dem Kohleüberzug aufgetragen wird, und tatsächlich können einige der Stoffe, die schon erwähnt worden sind, weil sie eine größere Bindungskraft oder Festigkeit als diejenigen des Papiers haben, tatsächlich eine leichtere Abgabe bieten als das Papier, wenn sie in Verbindung mit bestimmten Kohleüberzugsmischungen verwendet werden.The composition of the carbon coating can be varied in order to achieve more or less strong adhesion to the paper base and to create varying degrees of resistance to smearing. Such modifications of the Composition have an influence on the choice of the screened Release substance that is applied as a substrate prior to the charcoal coating, and indeed some of the substances that have already been mentioned because they have a greater binding force or strength than that of paper, in fact provide easier delivery than paper when used in conjunction with certain charcoal coating mixtures will.

10 9813/120210 9813/1202

Zur weiteren Erläuterung der Erfindung wird nunmehr auf die nachfolgenden Beispiele Bezug genommen. Diese Beispiele sollen jedoch nur der Erläuterung diensn, da ein Fachmann in der Herstellung von überzügen, die unter Druck abgelöst werden können, in der Lage ist, andere Rezepte, Zusammenstellungen und Stoffe der vorliegenden Erfindung anzupassen, ohne dabei deren Bereich zu verlassen.To further explain the invention, reference is now made to the following examples. These examples however, they are only intended to be illustrative as one skilled in the art of making coatings that are pressurized can be replaced, is able to adapt other recipes, compositions and substances of the present invention, without leaving their area.

example 1

Ein Bogen aus Vervielfältigungspapier wurde in gerasterter Form dadurch beschichtet, daß ein 50%-Punktraster aus Äthyl-Zellulose auf die eine Seite des Bogens aufgedruckt wurde. Die Äthyl-Zellulose wurde für das Drucken als eine 10^-ige Lösung in Xylol zubereitet und wurde aufgedruckt durch Verwendung einer Flachbett-Letterdruckmaschine (flat bed letterpress printing machine). In dem aufgedruckten 50%-Punktraster blieben voneinander getrennte, abgerundete Punkte oder Flecke der Vervielfältigungspapierunterlage unbedeckt. Der Bogen wurde dann trocknen gelassen.A sheet of duplicating paper was coated in a screened form using a 50% dot screen made of ethyl cellulose printed on one side of the sheet. The ethyl cellulose was used for printing as a 10 ^ solution Prepared in xylene and was printed using a flat bed letterpress printing machine). In the printed 50% dot grid separated, rounded points or patches of the duplicating paper backing remained uncovered. The arc was then allowed to dry.

Ein unter Druck Farbe abgebender überzug wurde nach folgendem Rezept zubereitet:An ink releasing coating under pressure was made according to the following Prepared recipe:

64 g Paraffinwachs
56 g Spindelöl64 g paraffin wax
56 g spindle oil

26 g ' Petroleum-Gelatine (Gelee, Gallert) 40 g Viktoria-Blau, CI. Pigment Blau 2 It E Ruß
200 g geruchlose Mineral-Spiritus26 g of petroleum gelatin (jelly, jelly) 40 g of Victoria blue, CI. Pigment Blue 2 It E carbon black
200 g odorless mineral spirit

Die geruchlosen Mineral-Spiritus waren im wesentlichen ein aliphatisches Kohlenwasserstofflösungsmittel, Flammpunkt 54,4° G, KB-Wert 26, Wichte 0,76I₈ Anilinpunkt 35° C, von der Shell Co. unter der Bezeichnung Shellsol T in den Handel gebracht. The odorless mineral spirits were essentially an aliphatic hydrocarbon solvent, flash point 54.4 ° G, KB value 26, density 0.76 / ₈ aniline point 35 ° C, marketed by Shell Co. under the name Shellsol T.

109813/1202109813/1202

Die Bestandteile wurden in eine Kugelmühle gegeben · und 24 Stunden lang gemahlen, wonach die Mischung auf das mit Substrat versehene Blatt des Vervielfältigungspapieres aufgetragen wurde, wobei ein mit Draht der Nummer 20 umwickelter Stab benutzt wurde, um einen Überzug zu schaffen,The ingredients were placed in a ball mill and grind for 24 hours, after which the mixture is added to the substrateed sheet of duplicating paper was applied with one wrapped with number 20 wire Rod was used to create a coating

2
der ein Trockengewicht von 5 g/m hatte. Der Überzug, der unter Druck Kohle (Farbstoff) abgeben sollte, wurde getrocknet und das so hergestellte Durchschlagpapier wurde so geschnitten, daß genügend Durchschläge für einen Vielfachsatz von zehn Blatt erhalten wurde, der in einer Schreibmaschine beschrieben wurde. Infolge der Anwesenheit des gerasterten Substratüberzuges zeigte auch die zehnte Kopie noch eine brauchbare Schärfe, wogegen der gleiche durch Drucküber- ι tragung zu übertragende Kohleauftrag auf demselben Vervielfältigungspapier ohne das gerasterte Substrat keine lesbare zehnte Kopie erbrachte. .2
which had a dry weight of 5 g / m 2. The coating, which was supposed to release charcoal (dye) under pressure, was dried and the carbon copy paper thus produced was cut to give enough carbon copies for a multiple set of ten sheets written on in a typewriter. As a result of the presence of the screened substrate coating, the tenth copy also showed usable sharpness, whereas the same carbon application to be transferred by pressure transfer on the same duplication paper without the screened substrate did not produce a legible tenth copy. .

Example 2

Anstelle des in Beispiel 1 verwendeten Zellulose-Harzes wurde als Substrat eine Vinyl-Akryl-Harz-Emulsion benutzt. Das verwendete Vinyl-Akryl-Harz war ein Vinyl-Azetat-Akryl-Polymer, pH-Wert 4-5, Viskosität 3OOO-4OOO cp, Wichte 1,10, Feststoffgehalt 55$, geliefert durch Polymer Corporation unter dem Handelsnamen ACROPOL CA 103. ä Instead of the cellulose resin used in Example 1, a vinyl-acrylic resin emulsion was used as the substrate. The vinyl-acrylic resin used was a vinyl-acetate-acrylic polymer, pH 4-5, viscosity 3,000-4,000 cp, density 1.10, solids content $ 55, supplied by Polymer Corporation under the tradename ACROPOL CA 103. Ä

Beispiel 3 · Example 3

Das Zellulose-Harz-Substrat nach Beispiel 1 wurde ersetzt durch Silikonharz. Das verwendete Harz war Dow Corning 805 Resin, Wichte 1,01, Viskosität 80-150 cp, geliefert als 50%-ige Lösung in Xylol.The cellulose resin substrate according to Example 1 was replaced by silicone resin. The resin used was Dow Corning 805 resin, density 1.01, viscosity 80-150 cp, supplied as 50% solution in xylene.

Beispiele 4-6Examples 4-6

Die .Vervielfältigungspapierunterlage jedes der Beispiele 1-3 wurde durch 11 1/2 Ib. Finch Pruyn Multiform Papier .ersetzt,The duplicating paper backing of each of Examples 1-3 was replaced by 11 1/2 Ib. Finch Pruyn Multiform Paper .replaces,

10981 3/19.0210981 3 / February 19

das ist eine Durchschlagpapierunterlage, die besonders für die Verwendung in Verbindung mit durch Druck übertragbaren Kohleüberzügen hergestellt wird.This is a carbon copy paper pad especially for use in conjunction with pressure transferable Coal coatings is produced.

Beispiele -7-12Examples -7-12

Der Kohleüberzug in jedem der Beispiele 4-6 wurde ersetzt durch folgende Mischung:The charcoal coating in each of Examples 4-6 was replaced with the following mixture:

50 g Paraffinwachs50 g paraffin wax

80 g Spindelöl80 g spindle oil

¹JO g Petroleum Gelatine ¹ JO g of petroleum gelatin

40 g Viktoria Blau C.I. Pigment Blau 2 14 g Ruß40 g Victoria Blue C.I. Pigment blue 2 14 g of carbon black

2 g 6^-iges Zirkonium-Oktoat 200 g geruchlose Mineral-Spiritus2 g 6 ^ zirconium octoate 200 g odorless mineral spirit

Die geruchlosen Mineral-Spiritus, das Zirkonium-Oktoat, der Ruß und das Viktoria Blau wurden miteinander vermischt, damit das Zirkonium-Oktoat von den Pigmenten absorbiert wurde; danach wurden die restlichen Bestandteile hinzugegeben und die Mischung in einer Kugelmühle 24 Stunden lang vermählen.The odorless mineral spirits, the zirconium octoate, the soot and the Victoria blue were mixed together with it the zirconium octoate was absorbed by the pigments; then the remaining ingredients were added and the Grind the mixture in a ball mill for 24 hours.

Die Überzugsmischung wurde weiter verdünnt in geruchlosen Mineral-Spiritus im Verhältnis von 1-10 g Überzugsmischung auf 100 g Spiritus und dann in einen isolierenden Behälter gesetzt. Die mit Substrat überzogene Unterlage wurde so auf eine Elektrode, vorzugsweise eine Plattenelektrode gelegt, daß, die beschichtete Seite von der Elektrode abgewandt war, und so in den Behälter gesetzt, daß das Blatt einer weiteren Elektrode in einem Abstand von 2,5 cm zugewandt war. Die das zu beschichtende Blatt enthaltende Elektrode wurde an die negative Ausgangsklemme einer Hochspannungsquelle und die andere Elektrode an die positive Klemme derselben Quelle angeschlossen; die positive Klemme war zusätzlich geerdet. Mit Anlegen einer Spannung von 15 kV für die Dauer von zehn Sekunden wurde auf dem Papier ein Kohleüberzug mit einem mittleren GewichtThe coating mixture was further diluted in odorless mineral spirit in the ratio of 1-10 g coating mixture 100 g of alcohol and then put in an insulating container. The base coated with substrate was thus on a Electrode, preferably a plate electrode placed that, the coated side was facing away from the electrode, and placed in the container so that the sheet faced another electrode at a distance of 2.5 cm. That too The electrode containing the coating sheet was connected to the negative output terminal of a high voltage source and the other Electrode connected to the positive terminal of the same source; the positive terminal was also grounded. With mooring a voltage of 15 kV for a period of ten seconds a medium weight carbon coating on the paper

109813/17 0?109 813/17 0?

von 4 g/m geschaffen. Der überzug in den nicht durch das Substrat bedeckten Flächenbereichen war jedoch wesentlich schwerer als in den durch das Substrat bedeckten Bereichen und hatte demnach die richtige Stärke (oder Dicke) für die Verwendung als ein durch Druck übertragbarer überzug in den Flächenbereichen maximalen Abgabevermögens; der überzug war wesentlich dünner in den Bereichen, die keine Farbsubstanz abgeben sollten.of 4 g / m created. The coating in the not by that However, the surface areas covered by the substrate were significantly heavier than in the areas covered by the substrate and so was of the correct strength (or thickness) for use as a pressure transferable coating in the Areas of maximum dispensing capacity; the coating was much thinner in the areas that should not give off any color substance.

In jedem der Beispiele 1-12 war der Substratüberzug oder -auftrag so gewählt, daß er die Abgabe des durch Druck übertragbaren Überzugs in stärkerem Maße verzögerte oder bremste, als die nicht beschichteten oder nicht überzogenen Flächenbereiche der Unterlage.In each of Examples 1-12, the substrate coating or application was chosen to provide the release of the pressure transferable The coating delayed or slowed down to a greater extent than the uncoated or uncoated areas of the base.

Example 13

Der Substratüberzug des Beispiels 1 wurde durch Polytetrafluoräthylen ersetzt. Dieser Stoff hatte die Form einer Dispersion in.einem Fluorkohlenstofftreibmittel und wurde auf das Vervielfältigungspapier durch einen 100 Maschen-Seidenschirm (gemäß der in Australien geltenden Norm) gesprüht.The substrate coating of Example 1 was made of polytetrafluoroethylene replaced. This material was in the form of a dispersion in a fluorocarbon propellant and was applied to the duplicating paper Sprayed through a 100 mesh silk screen (per Australian standard).

Example lfl

Das Polytetrafluoräthylen des Beispiels 13 wurde durch fluorier tes Äthylen-Propylen ersetzt.The polytetrafluoroethylene of Example 13 was fluorinated by tes ethylene propylene replaced.

Example 15

Das Polytetrafluoräthylen des Beispiels 13 wurde durch eine ähnliche Suspension von Molybdän-Sulfid ersetzt.The polytetrafluoroethylene of Example 13 was through a similar suspension replaced by molybdenum sulfide.

Allgemein wurde gefunden, daß die Stärke des Substratüberzugs verhältnismäßig unkritisch ist; es wurden Überzugsgewichte äquivalent den gleichförmigen Überzügen im Bereich von 1-4 g/m ohne wesentliche Unterschiede in der Wirkung angewandt.In general, it has been found that the thickness of the substrate coating is relatively uncritical; coating weights equivalent to the uniform coatings have been in the range of 1-4 g / m applied without significant differences in effect.

109813/120 2109813/120 2

Die Erfindung bietet ein Mittel zur Verbesserung des Auflösungsvermögens und der Schärfe von durch Abgabe unter Druck gedruckten Bildern durch Verwendung eines neuen Basisblattes für den Kohleüberzug; das Basisblatt hat gesteuerte Kohleabgabeeigenschaften in gerasterter Form.The invention provides a means of improving the resolution and sharpness of by dispensing under Printing printed images by using a new carbon coating base sheet; the base sheet has controlled Charcoal release properties in grid form.

Im Zweifel sind alle hier offenbarten Merkmale für sich oder in beliebiger sinnvoller Kombination erfindungswesentlich. Schutz wird begehrt für das, was ohne Rücksicht auf die Kenntnis des Anmelders oder Erfinders über den Stand der Technik objektiv schutzfähig ist.In case of doubt, all of the features disclosed here are essential to the invention individually or in any meaningful combination. Protection is sought for what is regardless of the knowledge of the applicant or inventor about the state of the Technology is objectively protectable.

Zur Ergänzung der Offenbarung liegt eine Abschrift der prioritätsbegründenden Anmeldung bei.A copy of the priority registration is enclosed to supplement the disclosure.

Patentansprüche;Claims;

109813/1202109813/1202

Claims

Claim e. :

■ Transfer sheet for printing by transfer

under pressure, consisting essentially of a base or backing j to which is applied to be transmitted substance labeled in characterized i ze η et that a substrate layer is coated on the support in raster or pattern shape and in that as a further coating or as a further order a pressure-transferable pigmented layer is provided that the substrate layer is only present in the surface areas defined by the pattern or the grid in such a way that the print transferability of the pigmented, pressure-transferable layer is modified in accordance with the grid.

2. Transfer sheet according to claim l, .dadur.'ch

ge * denotes that the pressure-transferable pigmented layer more closely to the substrate coating than to Areas of the support that are not covered by the substrate or base is bound *

3. Transfer sheet according to claim!., Characterized in that the transferable by pressure pigmented layer is more firmly bound to the substrate than to the substrate coating material.

4. Transfer sheet according to claim 2, da.durch g e k e η η ζ e i c h η e t that the patterned or rasterized Substrate consists of a continuous grid or pattern made of a material selected from the group of cellulose resins, the vinyl acrylic resins and silicone resins are taken.

5. Transfer sheet according to claim 3 / characterized in that the screened substrate consists of a Pattern or grid of unconnected spots or dots made of a material that consists of

10 9 813/1702

the group molybdenum sulfide, polytetrafluoroethylene and
fluorinated ethylene-propylene is taken.

6. A method of making a transfer sheet for printing by means of transfer under pressure, thereby
marked that a pad or base
with a substrate layer in patterned or rasterized.
Form is coated, whereupon a pigmented, pressure transferable coating is applied to the same side of the backing or base.

7. A method of making a transfer sheet according to claim 6, further characterized in that that the pigmented, pressure transferable coating is applied to the base using electrostatic coating processes is applied.