DE2025163A1 - Bullet guide ring - Google Patents
Bullet guide ringInfo
- Publication number
- DE2025163A1 DE2025163A1 DE19702025163 DE2025163A DE2025163A1 DE 2025163 A1 DE2025163 A1 DE 2025163A1 DE 19702025163 DE19702025163 DE 19702025163 DE 2025163 A DE2025163 A DE 2025163A DE 2025163 A1 DE2025163 A1 DE 2025163A1
- Authority
- DE
- Germany
- Prior art keywords
- fragments
- guide ring
- molding device
- fibrous material
- thermosetting resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
.-ING. FINSTERWALD DiPL-ING. GSXMSCOW 2025163 PATENTANWÄLTE.-ING. FINSTERWALD DiPL-ING. GSXMSCOW 2025163 PATENT LAWYERS
Lo/tii - H ^Q^- Lo / tii - H ^ Q ^ -
HStJBY CROSSLEY (PACKINGS) LIHlTSBHStJBY CROSSLEY (PACKINGS) LIHlTSB
P.O. Box Nrο 7, Hill Mill, Astley Bridge, Boltcm, Bancaehir©, *· GroßbritannienP.O. Box No. 7, Hill Mill, Astley Bridge, Boltcm, Bancaehir ©, *· Great Britain
GeschoßfülirungBringBullet Filler Bring
Priorität: Großbritannien vom 23* Hai 1969 Hr. 26 582/69Priority: Great Britain from 23 * Shark 1969 Mr. 26 582/69
Die Erfindung betrifft (teeelwJMHQuningtriege rad ren zur Herstellung soldierThe invention relates to (teeelwJMHQuningtriege rad ren for making soldier
Bei Artilleriewaffen, wie Kanone»» Gewehren» dergle ißt die Genauigkeit bj&w« Treffsicfeerteit schlaggebender Bedeutung und ei« wird aardh, Abs V: .:-:. <ü,oo GeechoBsee unterstütst. BfftmimtHc3ierw#ie® wkr& &e& £:;a=ö dee Geechossea dadurch "bewirkt f daß der Lauf &er W£e . ' Keilnut en oder epix«XfSxaig@£i fertiefm^«! τοηιβίιια iMr wobei der Spiralwickel min voi-aiiebeetifflc^fc:1; Γε«:-·- ' Is^9 von den betllietiec&tn SrforioriifeBesi abM>· Um ■■'·■'In the case of artillery weapons, such as cannon "" rifles "dergle, the accuracy bj &w" accuracy is crucial and ei "becomes aardh, paragraph V:.: - :. <ü, oo GeechoBsee support. BfftmimtHc3ierw # ie® wkr & & e £:;.! F a = ö dee Geechossea thereby causing "that the course he & W £ e 's keyway or Epix" XfSxaig @ £ i fertiefm ^ «τοηιβίιια IMR wherein the spiral winding min voi-aiiebeetifflc ^ fc: 1 ; Γε «: - · - 'Is ^ 9 from the betllietiec & tn SrforioriifeBesi abM & gt · Um ■■' · ■ '
j,j,
009848/1382009848/1382
7 ' * * - „ Γ ■ Ί7 '* * - "Γ ■ Ί
ttlV TotMWi IMI) aSII^TotW flMSabsv» Mp «χ^Γ,Ίΐ' "ηttlV TotMWi IMI) aSII ^ TotW flMSabsv »Mp« χ ^ Γ, Ίΐ '"η
st mit ä®m B^gfest with ä®m B ^ gfe
©2© 2
iier-geet©llt etesels, iier-geet © llt etesels,
liltlilt
Ils. solcherIls. such
dl©dl ©
füg1 mmdh add 1 mmdh
is 4qsb &sbx£ gü^isag aitis 4qsb & sbx £ gü ^ isag ait
ag wirdag becomes
?©2?ti©fyss©a? © 2? Ti © fyss © a
wis?ä9 e@wis? ä 9 e @
p±®g@p ± ®g @
(Md(Md
<x<x
_r dJ. Tozzi z3G_ r dJ. Tozzi z3G
,oß, oss
fcifci
©tu© do
ia iia i
©iso© iso
S2,2,£S@&CBS2,2, £ S @ & CB
■-* i'i - % r ·„.. 4 ν"■ - * i'i - % r · ".. 4 ν"
BAD ORfGtNALBAD ORfGtNAL
Lie Erfindung liefert einen nicht-metallischen oder im wesentlichen iiicht-ttetalliaclieB., hiilseEartigen der an der Mündung in eine Vielzahl von sehr kleine» Stücke Ri:eeinandergeht und zerfallt und der daher von eis« "Dauer r XtI4Jj" vollständig verschieden ißt« Sin solcher Ffitaaagsieiiig v\ra im folgenden ein "hillseiiartiger Filling ering" genannt.The invention provides a non-metallic or essentially non-ttetalliaclieB., Sleeve-like type which at the mouth merges and disintegrates into a multitude of very small "pieces" and which therefore eats completely different from ice "" duration r XtI 4 Jj "" Such a Ffitaaagsieiiig v \ ra called a "hillseii-like filling ering" in the following.
der Erfindung ■ v:ird ein liülsenartigerof the invention ■ v: ird a sleeve-like
Abwe rf· Führung aring·, wie er zuvor erläutert .wurde» gelie wobei der Führungsring verdichtet©», einzelne Bruch-Rejection · guidance ring ·, as it was previously explained .was »gelie whereby the guide ring compresses © », individual fracture
Ton iaaerförmisem Material umfaßt» die in iiriregex- :rK0i§er WoIl-ö angeordnet und untereinander mittels eiaem .-b* tzchärtbaren Har-ü verhundon sind.Iaaerförmisem clay material comprises "in iiriregex-: * tz chärtbaren Har-ü verhundon are rK0i§er WoIl ö-arranged and mutually-b. Eiaem means.
betrifft die Erfindung ein Verfahren zut Herstellun eine ε hüloenartdgenThe invention relates to a method for producing a sleeve type
wie er zuvor ■beeehritbiffi-mirxle, ¥ol>e4 das Verfahren sieh (T.iidurch auezeichnet,· aai? j?:Ine Tielsahl■ iron Biftiiihe'fetickeii kür faserartigem Haterisl &„„ < -ri3m liitssiii»"^'*^ ;k Btrs ' ■" iiaprägniert werden» eine vorgegöbens Ii@sg© ii*25 !«■aeiiitCAiiio. in ein ringförmiges Preßformwerkiseug eingegeben imd Hitze •and Brack an das Formwerkzeug angelegt werden, um die Bruch» stücke unter Bildung eines starren Führungsringeβ zu verdichten und miteinander zu verbinden«as he previously ■ beeehritbiffi-mirxle, ¥ ol> e4 see the procedure (T.iidurch auezeich, · aai? j?: Ine Tielsahl ■ iron Biftiiihe'fetickeii kür fibrous hatsl &""< - r i3m liitssiii »" ^ '* ^; k Btrs' ■ "iiapregniert» a given Ii @ sg © ii * 2 5 ! «■ aeiiitCAiiio. entered into a ring-shaped press mold and heat and brackets are applied to the mold in order to keep the fragments forming a rigid To compress guide rings and to connect to each other «
Vorzugsweise wird als faserartiges Material ein Aabestgarn, welches auf kurze Langen geschnitten wurde, verwendet, und es hat sich herausgestellt, daß die Verwendung einer Anordnung von Textilgarnen, wie in der britischen Patentschrift 474 beschrieben, geeignet ist, die eine Art Kotorenverdichtungsring mit einem angenäherten Querschnitt von 4,76 mm (3/16") im Quadrat wiedergibt. Anstelle der Verwendung von AsbestAabest yarn is preferably used as the fibrous material, which has been cut to short lengths, and it has been found that the use of an arrangement of textile yarns as in British Patent 474 described, is suitable, which is a kind of Kotoren compression ring with an approximate cross-section of 4.76 mm (3/16 ") in the square. Instead of using asbestos
00984 8-/1382 _ΛΛ 00984 8- / 1382 _ ΛΛ
ist ®s jedoch möglich^is ® however possible ^
diesen 2week künstlichthis 2week artificial
Z0 3o Kohle fades*, ejmas^gfemlfeig® l®@©sa0 <äo ^0 §2 ider sgsattietiselM! Hates'lüliQa ui©Z 0 3o coal fades *, ejmas ^ gfemlfeig® l® @ © sa 0 <äo ^ 0 §2 ider sgsattietiselM! Hates'lüliQa ui ©
od©r ÄcrylfiisQra, ©©Lqz1 rcDgQa©!0!©!^© Sisaa^f/ C ©11*3,1© SQ9 VisköS© QÜ,<BS A©OtQ^f SIf^gS9" sin© Kombinationod © r ÄcrylfiisQra, © © Lqz 1 rcDgQa ©! 0 ! ©! ^ © Sisaa ^ f / C © 11 * 3.1 © SQ 9 VisköS © QÜ, <BS A © OtQ ^ f SIf ^ gS 9 "sin © combination
faserartig© feterial ιή.τ& fibrous © feterial ιή.τ &
QB geringe imsseralssior-biQ^eMQ QB low imsseralssior-biQ ^ eMQ
sichersustellen^ daB d©r ^©©tlieSiö Foueh"öi^©its@<^ialt la dem P5aterial 1 % nickt übersteigtp kasa fi©@ Hateri©! füs»ensure ^ that d © r ^ © © tlieSiö Foueh "öi ^ © its @ <^ ialt la dem P5material 1% nods exceeds p kasa fi © @ Hateri ©! feet»
überschüssigen Sexcess S
Bas hitzerhärtend©Bas thermosetting ©
der Phenolharze ansiof phenolic resins ansi
ist Ereßol-1is Ereßol-1
verwendet werde»®will be used »®
bevorzugte Gewich'preferred weight
nachdem das Kars getrockast ißt, zwischenafter the kars eats dry, between
Anstelle der Verwendung einer Anordmmg voa TestUgarnen, wie in der "britischen Pateatecisrift 474 909 gezeigt, ist os möglich, andere weniger kosplisierte Garnen anzuwenden, z« B» andere Ibesponnene dicht gezwirnten Strang oder für diesen Ware« Ee wurde ebenfalls gefunden, daß dme in Itasäe tuck®·*· gehen des Führungsbandes leicht auftritt, fell© ün^elgame verwendet werden* Palis ein dicht gezwirnter Strang verwendet wird, kann es sich als erforderlich herausstellen, ein Bindemittel zu verwenden, um zu verhüten, da£ eich der gezwirnte Strang in Einzelgarne auflöst· Sia geeignetesInstead of using an arrangement of test yarns, as shown in "British Pateatecisschrift 474 909" os possible, others less complex To use yarns, eg «B» other ibespun tightly twisted strand or for this product «Ee was also found that dme in Itasäe tuck® · * · walking of the guide band occurs easily, fell © ün ^ elgame * Palis a tightly twisted strand is used it may be found necessary to use a binding agent to prevent this Dissolves twisted strand into single yarns · Sia suitable
009848/1382009848/1382
S ■ ; S ■ ;
Bindemittel ist ein Hartgummimaterial, ζ. B. S1O9A, das wie folgt zusammengesetzt ißtsBinder is a hard rubber material, ζ. B. S1O9A, the It is composed as follows
Fester Kautschuk (Handelsmarke Hycar 1041) Butadien-Acrylnitril^Jopoljmexriäat 50,0% Butyraldehyd/Anilinkomplex (Vulcaf or ) 1,0 %Solid rubber (trademark Hycar 1041) Butadiene-acrylonitrile ^ Jopoljmexriäat 50.0% Butyraldehyde / aniline complex (Vulcaf or) 1.0%
ZnO 2,5 %ZnO 2.5%
leichte kalzinierte Magnesia 2,0%light calcined magnesia 2.0%
rotes Eisenoxyd 17,5 %red iron oxide 17.5%
Dibutylphthalat · 7,0 %Dibutyl phthalate 7.0%
Ruß (P,53-Euß) . 2,5 %Soot (P, 53-black). 2.5%
Schwefel (MC-Schwefel) 17,5%Sulfur (MC-sulfur) 17.5%
100,0% i 100.0% i
Dies wird dann in eine 20 %ige Lösung gebracht, indem 4,54 kg (10 lbs.) hiervon zu 15,9 1 (3,5 britogall,) Toluol und 3,4 1 (0,75 britogall,,} Äthylendiehlorid zur Herst@13.img einer Eintauchlösung zugesetzt werden«,This is then brought into a 20% solution by adding 4.54 kg (10 lbs.) Of which to 15.9 liters (3.5 britogall,) toluene and 3.4 1 (0.75 britogall ,,} ethylene dichloride to Herst@13.img added to an immersion solution «,
Vorzugsweise werden die Bruchstücke aus faser&rtigem fftteariil mit Polytetrafluoräthylenpulverf welches im folgmtai als TTSlL bezeichnet werden wird, beschichtet, üb das Zerfallen des Führungsring«a nach dem Abfeuern in Bruchstücks ku unterstützeno Anstelle der Verwendung von PTFl-Pnlver können Glimmer, Talkum, Graphit oder andere gleichartlgo. Rcodukte | verwendet werden. .Preferably, the fragments of fiber & rtigem fftteariil with polytetrafluoroethylene powder are will be f denoting the folgmtai as TTSlL coated, the disintegration of the sabot "a üb after firing in fragment ku support o Instead of using Ptfl-Pnlver can mica, talc, graphite, or others of the same kind. Products | be used. .
Xm folgenden wird ein Beispiel tür Herstellung eiate l3Üie«a<-> artigen, auseinandergeheodea GeselioS*?uhruz^ariiig<i· der Erfindung gegeben»The following is an example of the manufacture of a l3Üie «a <-> like, apartheodea GeselioS *? uhruz ^ ariiig <i given to the invention »
£ine Anordnung von Textilgarsent wie in der britischen Patentschrift 474909 gezeigt, die einen ring mit einem angenSherten Querschnitt von 4,76£ ine arrangement of Textilgarsen t as shown in British Patent No. 474909 which has a ring with a cross-section of 4.76 angenSherten
003848/1382003848/1382
im Quadrat ergeben, wird darauf Überprüft, daß sein Feuchtigkeitβ* gehalt 1 % sieht übersteigt« falls di®s der Fall ists wird die Packung sin? EatferaaTung der übersdiüssigea Feuchtigkeit erhitzt» Die Packung wird dann mit eift@r lösung imprag&iert, S0 BQ mit einer ©le 85 technischem, ¥örgällt©M Alkohol geliefert© J 4-940/85 (Ha&d@lsbeseiehmmg), «ai di©@ weiter Me aaf eiae 50 Ag© LSguBg ¥i»ifs»t9 mn Sie in the square, it is checked that its moisture content exceeds 1 % «if di®s is the case s will the package be ? EatferaaTung the excess moisture is heated » The pack is then impregnated with a ift @ r solution, S 0 B Q delivered with a © le 85 technical, ¥ örgallen © M alcohol © J 4-940 / 85 (Ha & d @ lsbeseiehmmg) ," ai di © @ next Me aaf eiae 50 Ag © LSguBg ¥ i »ifs» t 9 mn you
a u 5lQj> «.ae e^.olisjato Uoaa <äao Ia5?aau 5lQj> «.ae e ^ .olisjato Uoaa <äao Ia5? a
3lae Sö^jleMDimaDtoo Mo ds 13lae Sö ^ jleMDimaDtoo Mo ds 1
▼ft ι rrc _ ui also^ iSs^-δο vc^öäö^o^o Sao Ir τ Uli," LiU^! <QcT7i3EäKas υ®ο Ϊ5Π3ΠΧ) cb2 <üo an r;eari υθί,β tdbol die Erzrosate? vseci^D^QlGQ▼ ft ι rrc _ ui also ^ iSs ^ -δο vc ^ öäö ^ o ^ o Sao Ir τ Uli, "LiU ^! <QcT7i3EäKas υ®ο Ϊ5Π3ΠΧ) cb2 <üo an r; eari υθί, β tdbol die Erzrosate? Vseci ^ D ^ QlGQ
«Se«Se
Auf dies® To this®
vorliegt Φ Imm οωσσα
de« toeekoB
nut anis available Φ Imm οωσσα de «toeekoB
nut on
ORIGINAL.ORIGINAL.
Xn der Zeichnung ist in Fig. 1 ein Qesehoß (1) alt einen Fit» rungering (2) wiedergegeben. Dieser Führungsring (2) 1st in Fig.- 2 in der Aufsicht gezeigt. Flg. 3 zeigt einen <fceveo.hBit& des Führungsrings β (2) längs der Schnittlinie I-X der Flu· Hierin ist ait (2) wieder der Führungsring bsjMlelmet» alt {f-ty die einzelnen Pellets bsw. Bruchstüole«, wobei bei tiaist stück (3) die alt Schrägstrichen elng«s«l©hatt« Btest%: rung wiedergegeben ist. Kit (5) 1st die oberflftflluleii· B·· schichtung mit PT7l-Pulver angedeutet. (6) »teilt Ä· beschriebenen, gegebenenfalls vorliegend« dar« Fig. 4- stellt ein Flleßsoheaa ä*r, 'veldiea 4Le Stufen bei den erflndungsgemäSen YefftaJarea wiederglbte M@ zelnen Verfahrensschritte sind in den Kästen eiajgeäßeleteii^ Ve Terfahrensablauf ergibt sich aus der ?f«ilriehtu&g® Ss sei darauf hingewiesen,In the drawing, FIG. 1 shows a sleeve (1) old a fitting ring (2). This guide ring (2) is shown in Fig. 2 in plan view. Flg. 3 shows a <fceveo.hBit & of the guide ring β (2) along the section line IX of the river. Here ait (2) is again the guide ring bsjMlelmet »alt { f -ty the individual pellets bsw. Bruchstüole «, where the old slashes elng« s «l © hatt« Btest%: rung are reproduced at tiaiststück (3). Kit (5) the surface layering with PT71 powder is indicated. (6) "shares the described, possibly present" ? f «ilriehtu & g® Ss should be noted
daß jedes der imprägnierten Bruchstücke des faserartigen Materials, wenn sie verdichtet usA erhitzt werden, in seine? Form verändert wird und mit bemchbarteo. 3rudb,ettiel»n andergreift, -so daß-n&eh dem volletliiilg«! Aushärten dee Harzes- eine zähe., aechap/ »r*5. MafeeelÄfiSsS.« gepreßte Struktur auegeOxlfiV '~*&!v falle &ß verwendet worden wäre, würde die Stmidfiii? b&tf« *d?. Awffess in Einzelstücke zerfallen. Ok ^edoÄ aieli«?eu®t®llea, QmB das Harz in benachbarten firuohstttöken keine Binteag derselben Festigkeit zwischen den Bruchstücken ausbildet, wie innerhalb der Bruchstücke selbst, die sehr zäh sind, wird es vorgezogen, Jedes Bruchstück mit FTFl-Pulver oder 'that each of the impregnated fragments of the fibrous material, when compacted and heated, will fall into its? Shape is changed and with bemchbarteo. 3rudb, ettiel "n other grabs, -so that-n & eh the completely"! Hardening of the Harz - a tough one., Aechap / »r * 5. MafeeelÄfiSsS. «Pressed structure auegeOxlfiV '~ * &! V falle & ß would have been used, would the Stmidfiii? b & tf «* d ?. Awffess disintegrate into individual pieces. Ok ^ edoÄ aieli «? Eu®t®llea, QmB the resin in neighboring firuohstttöken does not develop a binteag of the same strength between the fragments as within the fragments themselves, which are very tough, it is preferred, each fragment with FTFl powder or '
eines gleichartigen Aatlhaftmittel einsupudern, so daß schwache Flächen «wischen benachbarten Bruchstücken vorgesehen werden.of a similar type of adhesive so that weak areas can be provided between neighboring fragments.
Venn ein solcher Führungsring für Geschoss« für relativ groß· GeschoSkallber benötigt wird, kann es vorteilhaft sein, eine vergleichsweise kleine Menge von metallischen Fäden, z· B. aus Kupferfin die faserart igen Mater ialbruchstücke einzubauen· In der Zeichnung 3 sind diese MetallverstärkungenVenn such a guide ring for floor "is needed for relatively large · GeschoSkallber, it may be advantageous to use a relatively small amount of metallic filaments, for · example, copper f in the type of fiber strength Mater ialbruchstücke incorporate · In the drawing, 3 is these metal reinforcements
• ^v 009848/13 82• ^ v 009848/13 82
mit (6), wie bereite zuvor erläutert» angedeutet· Hüleenartige» Abwarf-Geechoßfülirung«ringe, die genäfi der Erfindung hergestellt wurden, haben unter sehr vielen Vorteilen die folgenden:with (6), as already explained »indicated · Hüleen-like» Discarded echo guiding rings which were produced according to the invention have many advantages the following:
a) Zerfall in kleine !Peiletücke nach dem Abfeuern;a) Disintegration into small pieces of the DF after firing;
b) sehr gute Feuchtigkeitebestä&dlgkeitseigenschaften;b) very good moisture resistance properties;
c) die Fähigkeit« hohen Kanonenteaperaturen. en widerstehen;c) the ability to have high cannon temperatures. to resist en;
d) gute aerodynamische Form für das Geschoß und infolgedessen eine bessere Treffgenauigkeit, da der Hingd) good aerodynamic shape for the projectile and consequently better accuracy because the Hing
- von dem Geschoß weggeht, unmittelbar nachdem das Geschoß die Kündung verläßt;- moves away from the projectile immediately after the projectile leaves the bullet;
e) einfache überwachungevorgängeje) simple monitoring processes j
f) nach dem Festmachen an dem Geschoß sind keine weiteren Bearbeitungevorgänge erforderlich;f) after the mooring to the floor there are no more Editing operations required;
g) im Falle der Beschädigung einfacher und leichter Ersatz im Felde;g) simple and easy replacement in case of damage in the field;
h) zufriedenstellende Funktion des Geschosses bei niedrigen Kammerdrucken. -h) Satisfactory function of the projectile at low levels Chamber printing. -
-Patentansprüche- - 8 - -Patent claims- - 8 -
009848/1382009848/1382
Claims (1)