DE202013007234U1 - System for the production of profiled bodies from natural fiber compound - Google Patents
System for the production of profiled bodies from natural fiber compound Download PDFInfo
- Publication number
- DE202013007234U1 DE202013007234U1 DE201320007234 DE202013007234U DE202013007234U1 DE 202013007234 U1 DE202013007234 U1 DE 202013007234U1 DE 201320007234 DE201320007234 DE 201320007234 DE 202013007234 U DE202013007234 U DE 202013007234U DE 202013007234 U1 DE202013007234 U1 DE 202013007234U1
- Authority
- DE
- Germany
- Prior art keywords
- weight
- powder
- pvc
- rice husk
- extrusion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
System zur Herstellung von Profilkörpern aus Naturfaser-Compound mit einer holzähnlichen Oberfläche, aufweisend einen Vorratsbehälter für eine Extrusionszusammensetzung, die ein Gemisch aus 30–40 Gew.-% PVC-Pulver und 20–40 Gew.-% Reisschalenpulver enthält, und eine Zuführeinrichtung, die mit einem Einschneckenextruder verbunden ist.A system for producing profiled bodies of natural fiber compound having a wood-like surface, comprising a reservoir for an extrusion composition containing a mixture of 30-40% by weight of PVC powder and 20-40% by weight of rice husk powder, and a feeder, which is connected to a single-screw extruder.
Description
Die Erfindung bezieht sich auf ein System zur Herstellung von Profilkörpern aus Naturfaser-Compound wie in Schutzanspruch 1 definiert.The invention relates to a system for the production of profiled bodies of natural fiber compound as defined in protection claim 1.
Die bekannten Mischungen aus Holz und PE/PP (Polyethylen/Polypropylen) oder PVC (Polyvinylchlorid) (sog. ”WPCs” = ”Wood Plastic Composites” oder ”Naturfaser-Compounds”) können aufgrund des hohen Feuchteanteils nur mit Doppelschneckenextrudern zu Profilkörpern verarbeitet werden. Doppelschneckenextruder sind teuer in der Anschaffung und Wartung.The known mixtures of wood and PE / PP (polyethylene / polypropylene) or PVC (polyvinyl chloride) (so-called "WPCs" = "Wood Plastic Composites" or "natural fiber compounds") can be processed due to the high moisture content only with twin-screw extruders to profile bodies , Twin screw extruders are expensive to buy and maintain.
Der Erfindung liegt daher die Aufgabe zugrunde, ein wirtschaftliches System bereitzustellen, das sich zur Herstellung von Profilkörpern aus Naturfaser-Compound mit einer holzähnlichen Oberfläche, die wasserbeständig sind und auch andere vorteilhafte Eigenschaften haben, eignet.The invention is therefore based on the object to provide an economical system that is suitable for the production of profile bodies made of natural fiber compound with a wood-like surface, which are water resistant and also have other advantageous properties.
Die erfindungsgemäße Aufgabe wird gelöst durch das in Schutzanspruch 1 definierte System zur Herstellung von Profilkörpern mit einer holzähnlichen Oberfläche aus Naturfaser-Compound.The object of the invention is achieved by the defined in protection claim 1 system for the production of profile bodies with a wood-like surface of natural fiber compound.
Vorteilhafte und/oder bevorzugte Ausführungsformen des erfindungsgemäßen Systems sind Gegenstand der Unteransprüche.Advantageous and / or preferred embodiments of the system according to the invention are the subject of the dependent claims.
Vorteilhafterweise enthält die in dem erfindungsgemäßen System verwendete Extrusionszusammensetzung Reisschalenpulver mit einer Teilchengröße von 0,42–0,10 mm (40–140 mesh).Advantageously, the extrusion composition used in the system of the invention contains rice husk powder having a particle size of 0.40-0.40 mm (40-140 mesh).
Dem Prinzip der Erfindung folgend kann vorgesehen sein, dass die in dem erfindungsgemäßen System verwendete Extrusionszusammensetzung das PVC-Pulver und das Reisschalenpulver etwa im Verhältnis 50:50 gemischt enthält.Following the principle of the invention, it can be provided that the extrusion composition used in the system according to the invention contains the PVC powder and the rice husk powder mixed in about a ratio of 50:50.
Hierbei kann dem Gemisch aus PVC-Pulver und Reisschalenpulver auch noch einer oder mehrere der folgenden Zusatzstoffe beigemischt werden: chemische(r) Binder auf Thermoplastkunststoffbasis, Farbpigment(e), Gleit/Schmiermittel, Calciumcarbonat und PVC-Verarbeitungshilfsmittel.In this case, one or more of the following additives may also be added to the mixture of PVC powder and rice husk powder: thermoplastic binder (s) based on thermoplastic, color pigment (s), lubricant / lubricant, calcium carbonate and PVC processing aid.
Bei einer weiteren vorteilhaften Ausbildung der Erfindung kann vorgesehen sein, dass die in dem erfindungsgemäßen System verwendete Extrusionszusammensetzung ein Gemisch aus 30–40 Gew.-% PVC-Pulver und 20–40 Gew.-% Reisschalenpulver mit einer Teilchengröße von 0,42–0,10 mm (40–140 mesh), 8–14 Gew.-% chemische(r) Binder auf Thermoplastkunststoffbasis, 0,5–1 Gew.-% Farbpigment(e), 2–4 Gew.-% Gleit/Schmiermittel, 12–30 Gew.-% Calciumcarbonat und 8–12 Gew.-% PVC-Verarbeitungshilfsmittel enthält.In a further advantageous embodiment of the invention it can be provided that the extrusion composition used in the system according to the invention, a mixture of 30-40 wt .-% PVC powder and 20-40 wt .-% rice husk powder having a particle size of 0.42-0 , 10 mm (40-140 mesh), 8-14% by weight of thermoplastic-based binder (s), 0.5-1% by weight of colored pigment (s), 2-4% by weight of lubricant / lubricant, Contains 12-30 wt .-% calcium carbonate and 8-12 wt .-% PVC processing aid.
Hierbei kann die Extrusionszusammensetzung von Vorteil etwa 31–37 Gew.-% PVC-Pulver enthalten.In this case, the extrusion composition may advantageously contain about 31-37 wt .-% PVC powder.
Bei einer weiteren vorteilhaften Ausführung der Erfindung kann die in dem erfindungsgemäßen System verwendete Extrusionszusammensetzung 33–36 Gew.-% Reisschalenpulver enthalten.In a further advantageous embodiment of the invention, the extrusion composition used in the system according to the invention may contain 33-36% by weight of rice husk powder.
Hierbei kann die Extrusionszusammensetzung 7–9 Gew.-% chemische(n) Binder auf Thermoplastkunststoffbasis enthalten.Here, the extrusion composition may contain 7-9% by weight of thermoplastic-based thermoplastic binder (s).
Die Extrusionszusammensetzung kann beispielsweise etwa 12–15 Gew.-% Calciumcarbonat enthalten.For example, the extrusion composition may contain about 12-15 weight percent calcium carbonate.
Von Vorteil haben das PVC-Pulver und das Reisschalenpulver etwa die gleiche Korngröße.The advantage of the PVC powder and the rice husk powder about the same grain size.
Bei einer besonders bevorzugten Ausführung der Erfindung ist vorgesehen, dass nach der Extrusion die auf dem Profilkörper gebildete Kunststoffhaut entfernt wird. Von Vorteil wird die Kunststoffhaut durch Abschleifen entfernt, wobei das Abschleifen mit einem Schleifmaterial mit einer Körnung im Bereich von 24 bis 60, Fräsen, Hobeln oder Bürsten durchgeführt wird.In a particularly preferred embodiment of the invention, it is provided that after extrusion the plastic skin formed on the profile body is removed. Advantageously, the plastic skin is removed by abrading, wherein the abrading is performed with an abrasive material having a grain size in the range of 24 to 60, milling, planing or brushing.
Weiterhin kann vorgesehen sein, dass die Oberfläche des durch Extrusion gebildeten Profilkörpers lackiert oder lasiert wird.Furthermore, it can be provided that the surface of the profile body formed by extrusion is painted or varnished.
Die in dem erfindungsgemäßen System zur Herstellung eines Profilkörpers aus Naturfaser-Compound verwendete Extrusionszusammensetzung enthält ein Gemisch aus 30–40 Gew.-% PVC-Pulver (PVC = Polyvinylchlorid) und 20–40 Gew.-% Pulver aus Reisschalen bzw. -hülsen. Vorteilhafterweise weist das Reisschalenpulver eine Teilchengröße von 0,42–0,10 mm (40–140 mesh) auf. Die Bezeichnung ”mesh” kennzeichnet die Maschenweite bei Sieben und dient damit als Maß für die Angabe von Partikel- bzw. Korngrößen. Je kleiner der mesh-Wert, desto größer ist die Teilchengröße des zu beschreibenden Schüttguts. Für die Umrechnung von mesh-Werten in Maschenweiten in mm gibt es Tabellen, beispielsweise vom US Bureau of Standards.The extrusion composition used in the system according to the invention for producing a profile body of natural fiber compound contains a mixture of 30-40 wt .-% PVC powder (PVC = polyvinyl chloride) and 20-40 wt .-% powder rice husk or husk. Advantageously, the rice husk powder has a particle size of 0,42-0,10 mm (40-140 mesh). The term "mesh" indicates the mesh size of sieves and thus serves as a measure for specifying particle or grain sizes. The smaller the mesh value, the larger the particle size of the bulk material to be described. For the conversion of mesh values into mesh sizes in mm there are tables, for example from the US Bureau of Standards.
Das verwendete PVC-Material unterliegt keinen besonderen Beschränkungen. Insbesondere kann auch PVC-Recyclingmaterial verwendet werden. Beispielsweise eignet sich neben PVC-Pulver auch eine PVC-Harz-Suspension mit einem K-Wert von 60–70. Unter dem K-Wert versteht man eine Zahl, die aus Messungen der Viskosität verdünnter Lösungen eines Polymers berechnet wird und ein Maß für den Polymerisationsgrad bzw. die Molekülgröße ist. Der K-Wert wird zur Harzspezifikation verwendet.The PVC material used is not particularly limited. In particular, PVC recycling material can also be used. For example, besides PVC powder, a PVC resin suspension with a K value of 60-70 is also suitable. The K value is understood to mean a number which is calculated from measurements of the viscosity of dilute solutions of a polymer and a measure of the degree of polymerization or the degree of polymerization Molecular size is. The K value is used for resin specification.
Die verwendeten Reisschalen unterliegen ebenfalls keinen besonderen Beschränkungen, insbesondere nicht in Bezug auf bestimmte Reissorten. Reisschalen lassen sich sehr gut pulverisieren und optimal mit dem PVC-Pulver vermischen. Außerdem enthalten sie weniger Lignin (nur etwa 5%) und bleichen daher unter Witterungseinfluss (Sonne, Regen) weniger oder gar nicht aus.The rice husks used are likewise not subject to any particular restrictions, in particular not with regard to certain types of rice. Rice pots can be pulverized very well and optimally mixed with the PVC powder. In addition, they contain less lignin (only about 5%) and therefore bleach under the influence of the weather (sun, rain) less or not at all.
Bei einer Ausführungsform der in dem erfindungsgemäßen System verwendeten Extrusionszusammensetzung zur Herstellung eines Profilkörpers aus Naturfaser-Compound sind das PVC-Pulver und das Reisschalenpulver etwa im Verhältnis 50:50 gemischt. Die Mischungsreihenfolge ist dabei generell beliebig.In one embodiment of the extrusion composition used in the system according to the invention for producing a profile body made of natural fiber compound, the PVC powder and the rice husk powder are mixed approximately in a ratio of 50:50. The mixing order is generally arbitrary.
Bei einer weiteren Ausführungsform der in dem erfindungsgemäßen System verwendeten Extrusionszusammensetzung ist/sind dem Gemisch aus PVC-Pulver und/oder Reisschalenpulver auch noch einer oder mehrere der folgenden Zusatzstoffe bzw. Additive beigemischt: chemische(r) Binder auf Thermoplastkunststoffbasis (z. B. Poly(meth)acrylat), Farbpigment(e) (z. B. Kreide, Titandioxid, Rußschwarz, rotes Eisenoxid, Ocker), Schmier- bzw. Gleitmittel (z. B. Fettsäuresalze wie Calciumstearat, Fettsäureester, Fettsäureamide, Paraffinwachse, Polyethylenwachse, mikrokristallines Parafin), Calciumcarbonat und PVC-Verarbeitungshilfsmittel (”processing aids”) (z. B. Wärme- und Witterungsstabilisatoren, Antioxidantien, Alterungsschutzmittel, Lichtstabilisatoren, Ultraviolettabsorber, Antistatikmittel). Die vorgenannten Zusatzstoffe sind im Fachhandel erhältlich. Die zusätzlichen Komponenten können gleichzeitig mit dem PVC-Pulver und dem Reisschalenpulver oder auch in mehreren Stufen damit vermischt werden.In a further embodiment of the extrusion composition used in the system according to the invention, one or more of the following additives or additives are / are added to the mixture of PVC powder and / or rice husk powder: thermoplastic binder based on chemical (r) binders (eg poly (meth) acrylate), color pigment (s) (eg, chalk, titanium dioxide, carbon black, red iron oxide, ocher), lubricants (e.g., fatty acid salts such as calcium stearate, fatty acid esters, fatty acid amides, paraffin waxes, polyethylene waxes, microcrystalline Paraffin), calcium carbonate and PVC processing aids (e.g., heat and weathering stabilizers, antioxidants, anti-aging agents, light stabilizers, ultraviolet absorbers, antistatic agents). The aforementioned additives are available from specialist retailers. The additional components can be mixed simultaneously with the PVC powder and the rice husk powder or even in several stages with it.
Bei einer weiteren Ausführungsform des erfindungemäßen Systems wird eine Extrusionszusammensetzung verwendet, die ein Gemisch aus 30–40 Gew.-%, beispielsweise 31–37 Gew.-%, PVC-Pulver, 20–40 Gew.-%, beispielsweise 33–36 Gew.-%, Reisschalenpulver mit einer Teilchengröße von 0,42–0,10 mm (40–140 mesh), 8–14 Gew.-%, beispielsweise 7–9 Gew.-%, chemische(n) Binder auf Thermoplastkunststoffbasis, 0,5–1 Gew.-% Farbpigment(e), 2–4 Gew.-% Schmier- bzw. Gleitmittel, 12–30 Gew.-%, beispielsweise 12–15 Gew.-%, Calciumcarbonat und 8–12 Gew.-% PVC-Verarbeitungshilfsmittel, enthält.In a further embodiment of the system according to the invention, an extrusion composition is used which comprises a mixture of 30-40% by weight, for example 31-37% by weight, PVC powder, 20-40% by weight, for example 33-36% by weight %, Rice shell powder having a particle size of 40-140 mesh, 8-14% by weight, for example 7-9% by weight, thermoplastic-based chemical binders, 0 , 5-1% by weight of colored pigment (s), 2-4% by weight of lubricants, 12-30% by weight, for example 12-15% by weight, calcium carbonate and 8-12% by weight. -% PVC processing aids.
Der chemische Binder auf Thermoplastkunststoffbasis hat beispielsweise die Funktion, Feuchtigkeit oder Lösungsmittel von Naturstofffasern zu entfernen und verbindet bzw. vernetzt sich stark mit dem ”nonwoven web” bzw. Netzwerk aus Naturstofffasern. PVC-Verarbeitungshilfsmittel (”PVC processing aids”) können die Verschmelzung (”Fusion”) beschleunigen, die Schmelzstärke bw. Zähigkeit der Schmelze (”melt strenght”) verbessern, Oberflächendefekte eliminieren und das ”place out” verringern. Außerdem können sie im Produktionsprozess die Metallablösungseigenschaften verstärken. Geeignete Binder und Verarbeitungshilfsmittel sind dem Fachmann auf dem Gebiet der PVC-Verarbeitung geläufig und im Handel in großer Auswahl verfügbar.The chemical binder based on thermoplastic resin, for example, has the function of removing moisture or solvents from natural fibers and combines or crosslinks strongly with the "nonwoven web" or network of natural fibers. PVC processing aids can accelerate the fusion, the melt strength bw. Improve melt toughness, eliminate surface defects, and reduce place out. In addition, they can enhance the metal release properties in the production process. Suitable binders and processing aids are well known to those skilled in the art of PVC processing and are widely available commercially.
Bei einer weiteren Ausführungsform der in dem erfindungsgemäßen System verwendeten Extrusionszusammensetzung haben das PVC-Pulver und das Reisschalenpulver etwa die gleiche Korngröße.In another embodiment of the extrusion composition used in the system of the present invention, the PVC powder and the rice husk powder have about the same grain size.
Der in dem erfindungsgemäße System eingesetzte Einschneckenextruder unterliegt keinen besonderen Beschränkungen. Es können beliebige handelsübliche Einschneckenextruder eingesetzt werden. Die Bedienung erfolgt nach den Herstellerinstruktionen. Dem Fachmann ist klar, dass die in dem erfindungsgemäßen System verwendete Extrusionszusammensetzung unter den Extrusionsbedingungen (z. B. Temperatur und Druck) ausreichend homogenisiert und verflüssigt werden muss, so dass sie durch die Extruderdüse gepresst werden kann. Geeignete Extrusionsbedingungen sind entweder die vom Hersteller spezifizierten oder werden vom Fachmann durch einfache Routineversuche ermittelt. Die Geometrie der verwendeten Extrusionsdüse bestimmt bekanntermaßen die Form bzw. das Profil des erhaltenen Extrusionsprodukts.The single-screw extruder used in the system of the present invention is not particularly limited. Any commercial single-screw extruder can be used. Operation is according to the manufacturer's instructions. It will be understood by those skilled in the art that the extrusion composition used in the system of the present invention must be sufficiently homogenized and liquefied under the extrusion conditions (eg, temperature and pressure) so that it can be extruded through the extruder die. Suitable extrusion conditions are either those specified by the manufacturer or determined by one skilled in the art by simple routine experimentation. The geometry of the extrusion die used is known to determine the shape or profile of the resulting extrusion product.
Beispielsweise wird das PVC-Pulver in einem Hochgeschwindigkeitsmischer mit getrocknetem Reisschalenpulver (Teichengröße 40–140 mesh, Feuchtigkeitsgehalt z. B. 0,5 bis 1,0%) und optional Füllstoff (z. B. Calciumcarbonat) 5 min bei 125–140°C vermischt. Die optionalen Additive wie Farbpigment, Stabilisator, Verarbeitungshilfsmittel, Gleitmittel (z. B. Epoxy-Soyaöl, Wachs) werden in einem kleinen Mischer/Blender 10 min durchmischt und dann in den Hochgeschwindigkeitsmischer zu dem Gemisch aus PVC-Pulver/Reisschalenpulver/Füllstoff gegeben. Dann wird das gesamte Gemisch weitere 10 min homogen durchmischt. Schließlich wird das Gemisch in einem Kühltank ca. 30 min abkühlen gelassen und dann bei einer geregelten Temperatur im Bereich von beispielsweise 150–210°C oder 160–175°C mit dem in dem erfindungsgemäßen System eingesetzen Einschneckenextruder zu einem Profilkörper aus Naturfaser-Compound als Endprodukt extrudiert.For example, the PVC powder is dried in a high speed mixer with dried rice husk powder (pebble size 40-140 mesh, moisture content eg 0.5 to 1.0%) and optional filler (eg calcium carbonate) for 5 min at 125-140 ° C mixed. The optional additives such as color pigment, stabilizer, processing aid, lubricant (e.g., epoxy soybean oil, wax) are mixed in a small mixer / blender for 10 minutes and then added to the high speed mixer to the PVC powder / rice husk powder / filler mixture. Then the entire mixture is thoroughly mixed for a further 10 minutes. Finally, the mixture is allowed to cool in a cooling tank for about 30 min and then at a controlled temperature in the range of for example 150-210 ° C or 160-175 ° C with the single screw extruder used in the system according to the invention to a profile body of natural fiber compound as End product extruded.
Vorzugsweise wird nach der Extrusion die auf der Oberfläche des Extrusionsprodukts (Profilkörper) gebildete Kunststoffhaut entfernt. Dadurch entsteht die sehr holzähnliche Haptik und Optik der Profilkörper. Durch die Entfernung der Kunststoffhaut haben die Profilkörper auch eine gute Griff- bzw. Rutschfestigkeit. Der Farbton der Profilkörper kann durch die Farbpigmente gesteuert werden, welche in der zu ihrer Herstellung verwendeten Extrusionszusammensetzung enthalten sind. Praktischerweise wird kein intensiver Farbton eingestellt, sondern ein vergleichsweise eher blasserer. Der endgültige gewünschte Farbton wird dann durch Lackieren oder Lasieren der Profilkörper eingestellt. Dadurch erspart man sich die Herstellung und Lagerung einer Vielzahl von Profilkörpern mit unterschiedlichen Farbtönen.Preferably, after extrusion, the on the surface of the extrusion product (profile body) removed plastic skin. This creates the very wood-like feel and appearance of the profile body. By removing the plastic skin, the profile body also have a good grip or skid resistance. The hue of the profile bodies can be controlled by the color pigments contained in the extrusion composition used to make them. Practically, no intense hue is set, but a comparatively paler. The final desired color is then adjusted by painting or glazing the profile body. This saves you the production and storage of a variety of profile bodies with different shades.
Beispielsweise kann die Kunststoffhaut durch Abschleifen entfernt werden. Das Abschleifen kann z. B. mit einem Schleifmaterial wie Sand- oder Schleifpapier mit einer Körnung im Bereich von 24 bis 60 durchgeführt werden, beispielsweise unter Verwendung eines elektrisch betriebenen Handschleifers. Bei der Körnung steht ein kleinerer Zahlenwert für eine gröbere Körnung und ein höherer Zahlenwert für eine feinere Körnung. Eine Körnung von 24 ist eher grob und eignet sich z. B. zum Entfernen von Leim- oder Lackschichten, während eine Körnung von 60 eher mittel ist und beispielsweise zum groben Vorschleifen roher Holzflächen verwendet wird. Die geeignete Körnung wählt der Fachmann nach Maßgabe der praktischen Gegebenheiten bzw. des zu erzielenden Effekts.For example, the plastic skin can be removed by grinding. The grinding can z. Example, with an abrasive material such as sand or sandpaper with a grain size in the range of 24 to 60 are performed, for example using an electrically operated hand grinder. When grit is a smaller number for a coarser grit and a higher numerical value for a finer grit. A grain size of 24 is rather coarse and is suitable for. B. for removing glue or paint layers, while a grain size of 60 is rather medium and is used, for example, for rough roughing raw wood surfaces. The suitable grain size is selected by the person skilled in the art in accordance with the practical conditions or the effect to be achieved.
Alternativ kann die Kunststoffhaut auch auf andere Weise entfernt werden, beispielsweise durch Abfräsen, Abhobeln, Abbürsten oder Sandstrahlen.Alternatively, the plastic skin can be removed in other ways, for example by milling, shaving, brushing or sandblasting.
Die Profilkörper können auf ihrer Oberfläche, ggf. nach einer entsprechenden Vorbehandlung (z. B. Grundierung), lackiert oder lasiert bzw. geölt werden. Zum Lackieren eignen sich beispielsweise wasserbasierte einkomponentige Lacke. Für die Extrembenutzung eignen sich besonders zweikomponentige Lacke.The profiled bodies can be varnished, glazed or oiled on their surface, if appropriate after a corresponding pretreatment (eg priming). For example, water-based one-component paints are suitable for painting. Two-component paints are particularly suitable for extreme use.
Je nach Pigmentierung und Oberflächentönung lassen sich verschiedene Holzoptiken und -haptiken realisieren, z. B. von Tropenholz wie Burma Teak, Siam Teak, Java Teak oder Aged Teak.Depending on the pigmentation and surface tinting, different wood looks and haptics can be realized, eg. From tropical wood such as Burma teak, Siam teak, Java teak or Aged teak.
Die mit dem erfindungsgemäßen System hergestellten Profilkörper haben eine sehr holzähnliche Optik wie auch Haptik, und bieten gegenüber den allermeisten Holzarten in vielerlei Hinsicht wesentlich verbesserte Eigenschaften.The profile body produced with the system according to the invention have a very wood-like appearance as well as feel, and offer compared to the vast majority of wood species in many ways significantly improved properties.
Aufgrund der polaren Eigenschaften des verwendeten PVCs kann die Oberfläche der mit dem erfindungsgemäßen System hergestellten Profilkörper problemlos geölt, lasiert oder lackiert werden. Die polaren Eigenschaften erlauben auch eine leichte Verklebbarkeit und verleihen antistatische Eigenschaften. Konventionelle Holz/PE-Composite (WPCs) sind wegen der nichtpolaren Eigenschaften von PE nicht oder nur sehr schwer lackierbar, nicht verklebbar und nicht antistatisch.Due to the polar properties of the PVC used, the surface of the profile body produced by the system according to the invention can be oiled, varnished or painted without problems. The polar properties also allow for easy bondability and give anti-static properties. Conventional wood / PE composites (WPCs) are not or only very difficult to paint, not glued and not antistatic because of the non-polar properties of PE.
Durch ihre Stabilität, Formbeständigkeit und absolute Widerstandsfähigkeit gegenüber Feuchtigkeitseinflüssen wie Regen sind die mit dem erfindungsgemäßen System hergestellten Profilkörper den konventionellen Holz/PE-Compositen (WPCs) und auch vielen Holzarten weit überlegen. Die mit dem erfindungsgemäßen System hergestellten Profilkörper sind nahezu wasserdicht. Das verwendete PVC ist nicht hygroskopisch und nimmt kein Wasser auf und verhindert so das Eindringen von Wasser durch eine Verletzung der Oberfläche, so dass keine Unterwanderung von aufgetragenen Lackschichten erfolgt und keine Lackabplatzungen auftreten. Die mit dem erfindungsgemäßen System hergestellten Profilkörper sind daher auch dimensionsstabil, so dass eine Verformung auf natürlichem Wege (z. B. durch Aufquellen oder Schwinden) nicht möglich ist. Konventionelle Holz/PE-Composite quellen dagegen unter Feuchtigkeitseinfluß. Lacke haften nicht mehr, weil das eindringende Wasser diese unterwandert und dadurch ablöst.Due to their stability, dimensional stability and absolute resistance to moisture influences such as rain, the profiled bodies produced by the system according to the invention are far superior to conventional wood / PE composites (WPCs) and also many types of wood. The profile body produced with the system according to the invention are almost waterproof. The PVC used is non-hygroscopic and does not absorb water, thus preventing the ingress of water due to surface damage, so that there is no infiltration of applied layers of lacquer and no lacquer chips appear. The profile bodies produced with the system according to the invention are therefore also dimensionally stable, so that deformation by natural means (eg by swelling or shrinkage) is not possible. By contrast, conventional wood / PE composites swell under the influence of moisture. Lacquers no longer adhere because the penetrating water infiltrates and thereby dissolves.
Die mit dem erfindungsgemäßen System hergestellten Profilkörper eignen sich daher besonders für Anwendungen im maritimen Bereich, in Meeres- und Seenähe oder in Nassbereichen (z. B. Schwimmbad). Pilzbefall oder Insektenbefall tritt nicht auf.The profile body produced with the system according to the invention are therefore particularly suitable for applications in the maritime area, near the sea and near the lake or in wet areas (eg swimming pool). Fungus or insect infestation does not occur.
Aufgrund der hervorragenden Festigkeit ist das Einschlagen von Nägeln oder das Eindrehen von Schrauben in die mit dem erfindungsgemäßen System hergestellten Profilkörper wie bei üblichen Holzmaterialien möglich. Auch die maschinelle Bearbeitung ist problemlos, so dass einfaches Durchschneiden mit einer Säge, Bohren, Fräsen, Schleifen oder sogar Sandstrahlen möglich ist. Die mit dem erfindungsgemäßen System hergestellten Profilkörper reißen nicht und splittern nicht, und Schnittabfälle sind zu 100% recyclebar.Due to the excellent strength of the hammering of nails or the screwing of screws in the profile body produced by the system according to the invention as in conventional wood materials is possible. Also, the machining is easy, so that simple cutting with a saw, drilling, milling, grinding or even sandblasting is possible. The profile body produced with the system according to the invention do not tear and do not splinter, and cut waste is 100% recyclable.
Die Reisschalen in der in dem erfindungsgemäßen System verwendeten Extrusionszusammensetzung fungieren als eine Art ”aktiver Füllstoff” und verleihen den daraus hergestellten Profilkörpern für die meisten Anwendungsgebiete verbesserte Bearbeitungseigenschaften. Die thermische Ausdehnung ist geringer und es wird die Konsistenz und Haptik von Naturholz erzielt.The rice husks in the extrusion composition used in the system of the present invention act as an "active filler" and impart improved working characteristics to the molded articles made therefrom for most applications. The thermal expansion is lower and the consistency and feel of natural wood is achieved.
Konventionelle Holz/PE-Composite neigen wegen des hohen Ligningehalts im verwendeten Holz durch den Einfluss von Sonne und Regen, die das Lignin zersetzen, zum Vergrauen und Vergilben und sind dadurch schnell unansehnlich. Die mit dem erfindungsgemäßen System hergestellten Profilkörper enthalten dagegen sehr wenig Lignin, so dass sie nicht vergilben.Conventional wood / PE composites are prone to graying and yellowing due to the high lignin content in the wood used, as a result of the sun and rain that decompose the lignin, making them unsightly. On the other hand, the profiled bodies produced by the system according to the invention contain very little lignin, so that they do not yellow.
Auch andere Eigenschaften der mit dem erfindungsgemäßen System hergestellten Profilkörper wie Schall- oder Wärmedämmung sind den charakteristischen Eigenschaften von natürlichem Holz ähnlich.Other properties of the profile body produced by the system according to the invention such as sound or thermal insulation are similar to the characteristic properties of natural wood.
Bei der Herstellung der Profilkörper kann der in dem erfindungsgemäßen System verwendeten Extrusionszusammensetzung aus PVC-Pulver und Reisschalenpulver auch in gewissem Maße Recyclematerial, z. B. Abfälle vom Zuschneiden der Profilkörper beigemengt werden, was z. B. geschehen kann, wenn solches zur Entsorgung zur Verfügung steht.In the production of the profile body, the extrusion composition of PVC powder and rice husk powder used in the system according to the invention may also to a certain extent recycle material, e.g. As waste from cutting the profile body be added what z. B. can happen if such disposal is available.
Claims (12)