DE202012103291U1 - Reflector with polymer film - Google Patents

Reflector with polymer film Download PDF

Info

Publication number
DE202012103291U1
DE202012103291U1 DE201220103291 DE202012103291U DE202012103291U1 DE 202012103291 U1 DE202012103291 U1 DE 202012103291U1 DE 201220103291 DE201220103291 DE 201220103291 DE 202012103291 U DE202012103291 U DE 202012103291U DE 202012103291 U1 DE202012103291 U1 DE 202012103291U1
Authority
DE
Germany
Prior art keywords
layer
heat reflector
microns
heat
reflector according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE201220103291
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NMC SA
Original Assignee
NMC SA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NMC SA filed Critical NMC SA
Priority to DE201220103291 priority Critical patent/DE202012103291U1/en
Publication of DE202012103291U1 publication Critical patent/DE202012103291U1/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

Wärmereflektor, dadurch gekennzeichnet, dass er mindestens eine reflektierende Schicht sowie mindestens eine Polymerfolie als Trägerschicht umfasst.Heat reflector, characterized in that it comprises at least one reflective layer and at least one polymer film as a carrier layer.

Description

Die vorliegende Erfindung betrifft einen Wärmereflektor, der mindestens eine reflektierende Schicht sowie mindestens eine Polymerfolie als Trägerschicht umfasst.The present invention relates to a heat reflector comprising at least one reflective layer and at least one polymer film as a carrier layer.

Wärmereflektoren und deren Verwendung sind bekannt. Ein Wärmereflektor wird hinter einen Heizkörper beziehungsweise zwischen Wand und Heizkörper angebracht, um Wärme und insbesondere Infrarotstrahlung, die zur Wand hin abgegeben wird, in den Raum hinein zu reflektieren. Dabei soll die abgestrahlte Wärme vermindert in das Mauerwerk eindringen. Dadurch kann die vom Heizkörper abgegebene Wärme beziehungsweise Infrarotstrahlung besser und effizienter genutzt werden. Ein Raum kann somit besser und effizienter geheizt werden. Dadurch können die Heizkosten gegebenenfalls gesenkt werden.Heat reflectors and their use are known. A heat reflector is placed behind a radiator or between the wall and radiator to reflect heat and in particular infrared radiation emitted to the wall into the room. In this case, the radiated heat is reduced to penetrate into the masonry. As a result, the heat emitted by the radiator or infrared radiation can be used better and more efficiently. A room can thus be heated better and more efficiently. As a result, the heating costs can be reduced if necessary.

Die Wärmereflektoren werden mit der nicht reflektierenden Seite dank eines Klebers an die Wand geklebt, wobei die reflektierende Seite zum Heizkörper zeigt.The heat reflectors are glued to the non-reflective side thanks to an adhesive to the wall, with the reflective side facing the radiator.

Nach dem heutigen Stand der Technik werden Wärmereflektoren in Plattenform oder als Rollen bereitgestellt und verwendet. According to the state of the art, heat reflectors are provided and used in plate form or as rollers.

Zudem umfasst der Aufbau eines Wärmereflektors nach heutigem Stand der Technik zum Beispiel eine Papierträgerschicht, die mit einer reflektierenden Aluminiumfolie kaschiert ist. In addition, the structure of a heat reflector according to the current state of the art, for example, comprises a paper support layer which is laminated with a reflective aluminum foil.

Die Herstellung eines solchen Wärmereflektors ist durch die erforderliche Kaschierung relativ aufwendig. In der Tat müssen Trägerschicht und reflektierende Schicht jeweils flächig und effektiv miteinander verbunden werden. Diese Verbindung der Schichten wird durch die Kaschierung erreicht. Dabei können die Schichten miteinander verklebt (Trocken- oder Nasskaschieren) oder durch Wärme und/oder Druck miteinander verbunden werden (Thermokaschieren).The preparation of such a heat reflector is relatively expensive due to the required lamination. In fact, the carrier layer and the reflective layer must each be connected to each other in a planar and effective manner. This connection of the layers is achieved by the lamination. The layers can be glued together (dry or wet lamination) or joined together by heat and / or pressure (thermal lamination).

Die Kaschierung beziehungsweise die Verbindung der einzelnen Schichten des Wärmereflektors kann dabei eine Schwachstelle des Wärmereflektors darstellen. Die Schichten können sich insbesondere zum Beispiel durch längere Hitzeeinwirkung (nach längerer Benutzung des hinter einem Heizkörper angebrachten Wärmereflektors) voneinander lösen. Dadurch kann der Wärmereflektor gegebenenfalls zum Beispiel Wellen bilden. In jedem Fall kann die Effizienz der Wärmereflektion und/oder der Wärmedämmung durch die Trennung der Schichten des Wärmereflektors erheblich beeinträchtigt werden.The lamination or the connection of the individual layers of the heat reflector can represent a weak point of the heat reflector. In particular, the layers can separate from one another, for example, by prolonged exposure to heat (after prolonged use of the heat reflector mounted behind a radiator). As a result, the heat reflector may optionally form waves, for example. In any case, the efficiency of the heat reflection and / or the thermal insulation can be considerably impaired by the separation of the layers of the heat reflector.

Ferner können Wärmereflektoren beim Zurechtschneiden der Rollen- oder Plattenware und/oder beim Anbringen/Verlegen einfach reißen und/oder beschädigt werden. Furthermore, heat deflectors can easily tear when trimming the roll or plate and / or when attaching / laying and / or damaged.

Dadurch können an den Rissen beziehungsweise Beschädigungen der Wärmereflektoren Wärmebrücken entstehen, welche die Effizienz der Wärmereflektion und/oder der Wärmedämmung beeinträchtigen können.As a result, thermal bridges can occur at the cracks or damage to the heat reflectors, which can impair the efficiency of the heat reflection and / or the thermal insulation.

Bei großen Rissen und/oder schwereren Beschädigungen der Wärmereflektoren kann es sogar erforderlich werden, neue Wärmereflektoren zurechtzuschneiden beziehungsweise zu verlegen. Somit kann das Anbringen/Verlegen der Wärmereflektoren gegebenenfalls sehr aufwendig werden. In the case of large cracks and / or severe damage to the heat reflectors, it may even be necessary to cut or lay new heat reflectors. Thus, the attachment / installation of the heat reflectors may possibly be very expensive.

Es besteht demnach ein Bedarf an einem Wärmereflektor, der effizient sowie widerstandfähig ist und einfach, schnell und bequem zwischen Wand und Heizkörper angebracht werden kann.There is therefore a need for a heat reflector that is efficient and durable and can be easily, quickly and conveniently mounted between the wall and radiator.

Dies wird durch einen erfindungsgemäßen Wärmereflektor nach Anspruch 1 ermöglicht. Die Unteransprüche beschreiben weitere mögliche Ausgestaltungen eines erfindungsgemäßen Wärmereflektors.This is made possible by a heat reflector according to the invention. The subclaims describe further possible embodiments of a heat reflector according to the invention.

Ein erfindungsgemäßer Wärmereflektor kann insbesondere zum Beispiel mindestens eine reflektierende Schicht sowie mindestens eine Polymerfolie als Trägerschicht umfassen.A heat reflector according to the invention may in particular comprise, for example, at least one reflective layer and at least one polymer film as a carrier layer.

Eine reflektierende Schicht kann dabei mindestens eine Schicht sein, die Wärme und insbesondere Infrarotstrahlung reflektiert. Eine reflektierende Schicht kann bevorzugt zum Beispiel mindestens eine Metallschicht und/oder Metallfolie und insbesondere mindestens eine Aluminiumschicht beziehungsweise mindestens eine Aluminiumfolie umfassen. Dadurch kann eine möglichst hohe Wärmereflexion (beziehungsweise die Reflexion von Infrarotstrahlen) erreicht werden.A reflective layer may be at least one layer which reflects heat and in particular infrared radiation. A reflective layer may preferably comprise, for example, at least one metal layer and / or metal foil and in particular at least one aluminum layer or at least one aluminum foil. As a result, the highest possible heat reflection (or the reflection of infrared rays) can be achieved.

Die Dicke der reflektierenden Schicht kann zum Beispiel zwischen 0,005 µm und 2 mm, bevorzugt zwischen 0,01 µm und 1 mm, weiter bevorzugt zwischen 0,012 µm und 750 µm, weiter bevorzugt zwischen 0,015 mm und 500 µm, weiter bevorzugt zwischen 0,017 µm und 400 µm, weiter bevorzugt zwischen 0,020 µm und 350 µm, weiter bevorzugt zwischen 0,020 µm und 200 µm, weiter bevorzugt zwischen 0,025 µm und 150 µm, weiter bevorzugt zwischen 0,027 µm und 100 µm liegen, weiter bevorzugt zwischen 0,030 µm und 50 µm, weiter bevorzugt zwischen 0,035 µm und 25 µm, weiter bevorzugt zwischen 0,04 µm und 10 µm, weiter bevorzugt zwischen 0,05 µm und 5 µm liegen, weiter bevorzugt zwischen 0,055 µm und 1 µm liegen, weiter bevorzugt zwischen 0,06 µm und 0,1 µm liegen. Eine größere Dicke der Polymerfolie als Trägerschicht kann zum Beispiel zu einer besseren Wärmereflexion und/oder Wärmedämmung und/oder zu einer höheren mechanischen Stabilität beziehungsweise Widerstandsfähigkeit/Reißfestigkeit beitragen.The thickness of the reflective layer may, for example, be between 0.005 μm and 2 mm, preferably between 0.01 μm and 1 mm, more preferably between 0.012 μm and 750 μm, more preferably between 0.015 mm and 500 μm, more preferably between 0.017 μm and 400 μm, more preferably between 0.020 μm and 350 μm, more preferably between 0.020 μm and 200 μm, more preferably between 0.025 μm and 150 μm, more preferably between 0.027 μm and 100 μm, even more preferably between 0.030 μm and 50 μm, more preferably between 0.035 μm and 25 μm, more preferably between 0.04 μm and 10 μm, more preferably between 0.05 μm and 5 μm, more preferably between 0.055 μm and 1 μm preferably between 0.06 .mu.m and 0.1 .mu.m. A greater thickness of the polymer film as a carrier layer can contribute, for example, to a better heat reflection and / or thermal insulation and / or to a higher mechanical stability or resistance / tear resistance.

Eine Trägerschicht kann mindestens eine Schicht sein, welche die reflektierende Schicht unterstützt und die mechanische Stabilität der reflektierenden Schicht verbessert. Erfindungsgemäß kann als Trägerschicht insbesondere eine Polymerfolie verwendet werden. Eine Polymerfolie als Trägerschicht kann zum Beispiel eine Polyethylenfolie, eine Polypropylenfolie, insbesondre eine biaxial orientierte Polypropylenfolie (BOPP-Folie), oder eine PET-Folie umfassen. Dadurch kann die Stabilität/Widerstandsfähigkeit beziehungsweise die Reißfestigkeit des Wärmereflektors erhöht und das Anbringen/Verlegen des Wärmereflektors gegebenenfalls vereinfacht werden. Die Effizienz des Wärmereflektors kann somit verbessert werden.A carrier layer may be at least one layer which supports the reflective layer and improves the mechanical stability of the reflective layer. According to the invention can be used as a carrier layer in particular a polymer film. A polymer film as a carrier layer may comprise, for example, a polyethylene film, a polypropylene film, in particular a biaxially oriented polypropylene film (BOPP film), or a PET film. As a result, the stability / resistance or tear resistance of the heat reflector can be increased and the attachment / installation of the heat reflector can be simplified if necessary. The efficiency of the heat reflector can thus be improved.

Die Polymerfolie als Trägerschicht kann dabei erfindungsgemäß mit der reflektierenden Schicht beschichtet werden, um einen Verbund zu erhalten. Die Beschichtung der Polymerfolie als Trägerschicht kann zum Beispiel durch chemische Gasphasenabscheidung (CVD) oder durch physikalische Gasphasenabscheidung (PVD) und dabei insbesondere durch Sputtern erfolgen. Ein erfindungsgemäßer Wärmereflektor kann somit zum Beispiel auch mindestens eine metallbeschichtete Polymerfolie und insbesondere mindestens eine aluminiumbeschichtete Polymerfolie umfassen. Ein erfindungsgemäßer Wärmereflektor kann bevorzugt zum Beispiel mindestens eine metall- beziehungsweise aluminiumbeschichtete Polyethylen-, Polypropylen- oder PET-Folie und/oder mindestens eine metall- beziehungsweise aluminiumbeschichtete biaxial orientierte Polypropylenfolie (BOPP-Folie) umfassen. Dadurch kann gegebenenfalls eine besonders widerstandsfähige Verbindung der Schichten des Wärmereflektors erhalten werden.The polymer film as a carrier layer can be coated according to the invention with the reflective layer in order to obtain a composite. The coating of the polymer film as a carrier layer can be carried out, for example, by chemical vapor deposition (CVD) or by physical vapor deposition (PVD) and in particular by sputtering. A heat reflector according to the invention can therefore also comprise, for example, at least one metal-coated polymer film and in particular at least one aluminum-coated polymer film. A heat reflector according to the invention may preferably comprise, for example, at least one metal- or aluminum-coated polyethylene, polypropylene or PET film and / or at least one metal- or aluminum-coated biaxially oriented polypropylene film (BOPP film). As a result, if necessary, a particularly resistant connection of the layers of the heat reflector can be obtained.

Die Dicke der Polymerfolie als Trägerschicht kann zum Beispiel zwischen 0,5 µm und 2 mm, bevorzugt zwischen 1 µm und 1 mm, weiter bevorzugt zwischen 2 µm und 900 µm, weiter bevorzugt zwischen 3 µm und 700 µm, weiter bevorzugt zwischen 4 µm und 500 µm weiter bevorzugt zwischen 5 µm und 350 µm, weiter bevorzugt zwischen 6 µm und 200 µm, weiter bevorzugt zwischen 6,5 µm und 100 µm, weiter bevorzugt zwischen 7 µm und 50 µm, weiter bevorzugt zwischen 7,5 µm und 20 µm, weiter bevorzugt zwischen 7,7 µm und 15 µm, weiter bevorzugt zwischen 8 µm und 12 µm liegen. Eine größere Dicke der Polymerfolie als Trägerschicht kann zum Beispiel zu einer besseren Wärmereflexion und/oder Wärmedämmung und/oder zu einer höheren mechanischen Stabilität beziehungsweise Widerstandsfähigkeit/Reißfestigkeit beitragen.The thickness of the polymer film as a carrier layer may for example be between 0.5 μm and 2 mm, preferably between 1 μm and 1 mm, more preferably between 2 μm and 900 μm, more preferably between 3 μm and 700 μm, more preferably between 4 μm and 500 microns more preferably between 5 microns and 350 microns, more preferably between 6 microns and 200 microns, more preferably between 6.5 microns and 100 microns, more preferably between 7 microns and 50 microns, more preferably between 7.5 .mu.m and 20 microns , more preferably between 7.7 microns and 15 microns, more preferably between 8 microns and 12 microns. A greater thickness of the polymer film as a carrier layer can contribute, for example, to a better heat reflection and / or thermal insulation and / or to a higher mechanical stability or resistance / tear resistance.

Darüber hinaus kann ein erfindungsgemäßer Wärmereflektor bevorzugt auch mindestens eine zusätzliche Schicht eines Wärmedämmmaterials umfassen. Diese Schicht eines Wärmedämmmaterials kann bevorzugt zum Beispiel mit der Trägerschicht durch Verkleben und/oder durch Druck und/oder Hitze oder auf eine andere Weise verbunden werden. Dadurch können die Reflexion von Wärme beziehungsweise Infrarotstrahlen und die Wärmedämmung einer Wand, auf die der Wärmereflektor geklebt wird, gegebenenfalls verbessert werden.In addition, a heat reflector according to the invention may preferably also comprise at least one additional layer of thermal insulation material. This layer of thermal insulation material may preferably be bonded, for example, to the backing layer by gluing and / or by pressure and / or heat or in some other way. As a result, the reflection of heat or infrared rays and the thermal insulation of a wall, to which the heat reflector is glued, can optionally be improved.

Eine Schicht eines Wärmedämmmaterials kann insbesondere zum Beispiel mindestens eine Schicht aus einem Polymermaterial und/oder mindestens eine Schaumstoffschicht aus einem Polymermaterial umfassen. Dadurch kann gegebenenfalls zum Beispiel eine gute Wärmedämmung erreicht werden. Eine Schaumstoffschicht ermöglicht es, gegebenenfalls zum Beispiel eine besonders gute Wärmereflexion und/oder Wärmedämmung zu erreichen.In particular, for example, a layer of thermal insulation material may comprise at least one layer of a polymeric material and / or at least one foam layer of a polymeric material. This can optionally be achieved, for example, a good thermal insulation. A foam layer makes it possible, if appropriate, to achieve, for example, a particularly good heat reflection and / or thermal insulation.

Das Wärmedämmmaterial kann zum Beispiel mindestens ein biobasiertes Polymer, Polyethylen, Polyurethan, Ethylenvinylacetat (EVA), Polystyrol, insbesondere einen expandierten Polystyrolschaumstoff (EPS) oder einen extrudierten Polystyrolschaumstoff (XPS) und/oder Copolymere beziehungsweise Mischungen davon, umfassen. Bevorzugt kann gegebenenfalls auch mindestens ein expandierter Polystyrolschaumstoff mit einem oder mehreren Zusätzen, wie zum Beispiel Graphit, als Wärmedämmmaterial verwendet werden. Das Wärmedämmmaterial kann dabei gegebenenfalls zum Beispiel mindestens ein Material aus nachwachsenden Rohstoffen und insbesondere aus einem Dämmmaterial aus nachwachsenden Rohstoffen, wie zum Beispiel Holz- oder Naturfasern, Holzspäne oder Wolle, umfassen. Dadurch kann gegebenenfalls zum Beispiel eine weiter verbesserte Wärmereflexion und/oder Wärmedämmung erreicht werden.The thermal insulation material may comprise, for example, at least one bio-based polymer, polyethylene, polyurethane, ethylene vinyl acetate (EVA), polystyrene, in particular an expanded polystyrene foam (EPS) or an extruded polystyrene foam (XPS) and / or copolymers or mixtures thereof. If desired, at least one expanded polystyrene foam with one or more additives, such as, for example, graphite, may also be used as thermal insulation material. The thermal insulation material may optionally include, for example, at least one material from renewable raw materials and in particular from a damping material of renewable raw materials, such as wood or natural fibers, wood chips or wool. As a result, it is optionally possible, for example, to achieve a further improved heat reflection and / or thermal insulation.

Die Dicke der Schicht eines Wärmedämmmaterials kann zum Beispiel zwischen 0,1 mm und 50 mm, bevorzugt zwischen 0,2 mm und 30 mm, weiter bevorzugt zwischen 0,5 mm und 20 mm, weiter bevorzugt zwischen 1 mm und 15 mm, weiter bevorzugt zwischen 1,5 mm und 10 mm, weiter bevorzugt zwischen 1,75 mm und 5 mm, weiter bevorzugt zwischen 2 mm und 4 mm liegen. Eine größere Dicke der Trägerschicht kann zum Beispiel zu einer besseren Wärmereflexion und/oder Wärmedämmung und/oder zu einer höheren mechanischen Stabilität beziehungsweise Widerstandsfähigkeit/Reißfestigkeit beitragen.The thickness of the layer of thermal insulation material may, for example, be between 0.1 mm and 50 mm, preferably between 0.2 mm and 30 mm, more preferably between 0.5 mm and 20 mm, more preferably between 1 mm and 15 mm between 1.5 mm and 10 mm, more preferably between 1.75 mm and 5 mm, more preferably between 2 mm and 4 mm. A greater thickness of the carrier layer can contribute, for example, to a better heat reflection and / or thermal insulation and / or to a higher mechanical stability or resistance / tear resistance.

Ein erfindungsgemäßer Wärmereflektor kann dabei zum Beispiel auch mindestens eine zusätzliche Klebeschicht umfassen, die bevorzugt auf der der reflektierenden Schicht abgewandten Seite aufgebracht werden kann. Diese Klebeschicht kann zudem zum Beispiel durch eine geeignete Abziehfolie und/oder Abziehpapier geschützt werden. Dadurch kann der erfindungsgemäße Wärmereflektor sehr einfach und bequem angebracht werden. Die Abziehfolie und/oder das Abziehpapier werden dabei lediglich von der zusätzlichen Klebeschicht abgezogen, und der erfindungsgemäße Wärmereflektor kann bequem auf die Wand aufgebracht werden. Ein Auftragen von Kleber auf den Wärmereflektor ist in diesem Fall somit überflüssig.An inventive heat reflector can, for example, at least one comprise additional adhesive layer, which may preferably be applied to the side facing away from the reflective layer. This adhesive layer can also be protected, for example, by a suitable release liner and / or release paper. As a result, the heat reflector according to the invention can be attached very easily and conveniently. The peel-off film and / or the peel-off paper are only removed from the additional adhesive layer, and the heat reflector according to the invention can be conveniently applied to the wall. Applying glue to the heat reflector is thus superfluous in this case.

Erfindungsgemäße Wärmereflektoren können zum Beispiel als Platten, als Rollenware und/oder als gefaltete beziehungsweise mehrfach gefaltete Platten hergestellt werden. Letztere Form kann dabei im halb auseinandergefalteten Zustand bevorzugt eine Ziehharmonikaform aufweisen.Inventive heat reflectors can be produced, for example, as plates, as rolled goods and / or as folded or multiply folded plates. The latter form may preferably have a concertina form in the half unfolded state.

Ein erfindungsgemäßer Wärmereflektor kann zudem zum Beispiel auch mindestens eine Sollbruchstelle umfassen. Eine perforierte Trennlinie kann zum Beispiel eine Sollbruchstelle darstellen, die durch Perforation erhalten werden kann. Dadurch kann gegebenenfalls mindestens ein Teil eines erfindungsgemäßen Wärmekollektors bequem vom Rest des erfindungsgemäßen Wärmekollektors entlang einer Sollbruchstelle getrennt werden, um die Abmessungen des Wärmekollektors schnell und bequem zu ändern.In addition, a heat reflector according to the invention may, for example, also comprise at least one predetermined breaking point. For example, a perforated parting line may represent a predetermined breaking point that may be obtained by perforation. As a result, optionally at least a portion of a heat collector according to the invention can be conveniently separated from the rest of the heat collector according to the invention along a predetermined breaking point in order to change the dimensions of the heat collector quickly and conveniently.

Ein erfindungsgemäßer Wärmereflektor kann ferner gegebenenfalls so gestaltet sein, dass er zum Beispiel mindestens zwei plattenförmige Teile umfasst, die über mindestens eine Gelenkstelle zusammenfaltbar miteinander verbunden sind. Die Anzahl der Gelenkstellen (N – 1) eines Wärmereflektors kann dabei bevorzugt zum Beispiel mindestens der Anzahl der plattenförmigen Teile (N) minus eins entsprechen. Dadurch kann sichergestellt werden, dass der Wärmereflektor im auseinandergefalteten Zustand eine ebene/plane Fläche bilden kann, die schnell und bequem geklebt werden kann. Zudem kann somit auch erreicht werden, dass der Wärmereflektor im zusammengefalteten Zustand möglichst kompakt und platzsparend gelagert werden kann. Spannungen im Wärmereflektor, die durch das Verformen beim Aufrollen auftreten können, werden dabei vollständig vermieden. A heat reflector according to the invention may also optionally be designed such that it comprises, for example, at least two plate-shaped parts which are connected to each other in a collapsible manner via at least one hinge point. The number of hinge points (N-1) of a heat reflector can preferably correspond, for example, at least to the number of plate-shaped parts (N) minus one. This can ensure that the heat reflector in unfolded state can form a flat / flat surface that can be glued quickly and easily. In addition, it can thus be achieved that the heat reflector in the folded state can be stored as compact and space-saving as possible. Tensions in the heat reflector, which can occur due to deformation during rolling, are thereby completely avoided.

Eine Gelenkstelle kann dabei zum Beispiel eine Stelle sein, an der die Dicke mindestens einer Trägerschicht beziehungsweise einer Schicht eines Wärmedämmmaterials und bevorzugt aller entsprechenden Schichten reduziert ist. Eine Reduzierung der Dicke des Trägermaterials kann zum Beispiel durch mindestens einen Knick, einen Schnitt, eine Falzlinie oder eine Kerbe/Rille erreicht werden. Eine Kerbe/Rille kann zum Beispiel durch ein Prägeverfahren erreicht werden. Zudem kann bei mindestens einem Schnitt die gesamte Trägerschicht durchtrennt werden, sodass an der Gelenkstelle gegebenenfalls lediglich die reflektierende Schicht übrig bleibt, um mindestens zwei plattenförmige Teile eines Wärmereflektors miteinander zu verbinden. Eine Gelenkstelle kann zum Beispiel auch einer Sollbruchstelle entsprechen. Eine Gelenkstelle kann zum Beispiel vertikal oder horizontal angeordnet werden. Eine Gelenkstelle kann bevorzugt zum Beispiel parallel zu einem Rand des erfindungsgemäßen Wärmereflektors angeordnet sein. Zudem kann sich eine Gelenkstelle bevorzugt zum Beispiel entlang der gesamten Länge und/oder Breite des erfindungsgemäßen Wärmereflektors erstrecken. Ein erfindungsgemäßer Wärmereflektor kann gegebenenfalls zum Beispiel sowohl horizontal als auch vertikal angeordnete Gelenkstellen umfassen. Durch eine Gelenkstelle kann der erfindungsgemäße Wärmereflektor gegebenenfalls bequem zusammengefaltet werden, um eine einfache Lagerung zu ermöglichen. A joint may be, for example, a location at which the thickness of at least one carrier layer or a layer of thermal insulation material and preferably all corresponding layers is reduced. A reduction of the thickness of the carrier material can be achieved, for example, by at least one kink, a cut, a fold line or a notch / groove. A notch / groove can be achieved, for example, by a stamping process. In addition, in at least one cut, the entire carrier layer can be severed, so that at the hinge point, where appropriate, only the reflective layer remains to connect at least two plate-shaped parts of a heat reflector together. A joint point can for example also correspond to a predetermined breaking point. A hinge point can be arranged, for example, vertically or horizontally. A hinge point may preferably be arranged, for example, parallel to an edge of the heat reflector according to the invention. In addition, a hinge point may preferably extend, for example, along the entire length and / or width of the heat reflector according to the invention. Optionally, for example, a heat reflector according to the invention may comprise both horizontally and vertically arranged hinge points. By a hinge point, the heat reflector according to the invention can optionally be conveniently folded to allow easy storage.

Als Platte kann ein erfindungsgemäßer Wärmereflektor zum Beispiel Abmessungen von 0,1 m × 2,5 m, bevorzugt 0,2 × 2 m, weiter bevorzugt 0,3 × 1,5 m, weiter bevorzugt 0,4 × 1,0 m oder 0,5 m × 0,5 m aufweisen.As a plate, a heat reflector according to the invention may, for example, dimensions of 0.1 m × 2.5 m, preferably 0.2 × 2 m, more preferably 0.3 × 1.5 m, more preferably 0.4 × 1.0 m or 0.5 m × 0.5 m.

Als Rollenware kann ein erfindungsgemäßer Wärmereflektor zum Beispiel Abmessungen von 0,1 m × 50 m, bevorzugt 0,2 × 30 m, weiter bevorzugt 0,3 × 20 m, weiter bevorzugt 0,4 × 10 m, weiter bevorzugt 0,5 × 5 m, weiter bevorzugt 0,5 × 6 m oder 0,6 m × 5 m aufweisen.As roll goods, a heat reflector according to the invention may for example have dimensions of 0.1 m × 50 m, preferably 0.2 × 30 m, more preferably 0.3 × 20 m, more preferably 0.4 × 10 m, further preferably 0.5 × 5 m, more preferably 0.5 × 6 m or 0.6 m × 5 m.

Als gefaltete Platte kann ein erfindungsgemäßer Wärmereflektor zum Beispiel in den Abmessungen 10 m × 0,5 m, 10 × 0,75 m, 10 × 0,25 m, 5 m × 0,5 m, 5 m × 0,25 m, 5 m × 0,75 m, 2,5 m × 0,5 m, 2,5 m × 0,25 m oder 2,5 m × 0,75 m aufweisen. As a folded plate, a heat reflector according to the invention may be used, for example, in the dimensions 10 m × 0.5 m, 10 × 0.75 m, 10 × 0.25 m, 5 m × 0.5 m, 5 m × 0.25 m, 5 m × 0.75 m, 2.5 m × 0.5 m, 2.5 m × 0.25 m or 2.5 m × 0.75 m.

Sofern ein erfindungsgemäßer Wärmekollektor als gefaltete Platte gestaltet ist, können alle plattenförmigen Teile der gefalteten Platte gegebenenfalls zum Beispiel die gleichen Abmessungen aufweisen. Insbesondere können alle plattenförmigen Teile zum Beispiel die gleiche Breite aufweisen. Alternativ können bestimmte plattenförmige Teile auch unterschiedliche Abmessungen und insbesondere eine unterschiedliche Breite aufweisen. Ein plattenförmiges Teil kann dabei bevorzugt zum Beispiel eine rechteckige Form aufweisen. Die hohe Flexibilität bezüglich der Form, der Anzahl und der Abmessungen der plattenförmigen Teile trägt dazu bei, dass bevorzugt ein weitegehend durchgehendes Anbringen/Verlegen der Wärmereflektoren ermöglicht wird. Dadurch kann die Zahl der Übergänge/Spalten zwischen den angebrachten erfindungsgemäßen Wärmereflektoren reduziert und insbesondere zum Beispiel die Wärmereflexion sowie die Wärmedämmung verbessert werden.If a heat collector according to the invention is designed as a folded plate, all plate-shaped parts of the folded plate may optionally have, for example, the same dimensions. In particular, all plate-shaped parts may for example have the same width. Alternatively, certain plate-shaped parts may also have different dimensions and in particular a different width. A plate-shaped part may preferably have, for example, a rectangular shape. The high flexibility with regard to the shape, the number and the dimensions of the plate-shaped parts contributes to the fact that preferably a largely continuous attachment / laying of the heat reflectors is made possible. As a result, the number of transitions / gaps between the attached heat reflectors according to the invention can be reduced and, in particular, for example, the heat reflection and the thermal insulation can be improved.

Ein erfindungsgemäßer Wärmereflektors mit mindestens einer Polymerfolie als Trägerschicht und einer zusätzlichen Wärmedämmschicht kann zum Beispiel bei einer Prüfung durch das Fraunhofer-Institut einen Wärmereflexionsgrad von > 95% aufweisen. Dazu trägt neben der reflektierenden Schicht auch die Wärmedämmung durch die Trägerschicht und die zusätzliche Wärmedämmschicht sowie die weitgehend durchgehende Verlegung/Anbringung der erfindungsgemäßen Wärmereflektoren ohne Risse und/oder Beschädigungen bei. An inventive heat reflector with at least one polymer film as a carrier layer and an additional heat-insulating layer can, for example, have a degree of heat reflection of> 95% when tested by the Fraunhofer Institute. In addition to the reflective layer, the heat insulation through the carrier layer and the additional heat-insulating layer as well as the largely continuous installation / attachment of the heat reflectors according to the invention contribute to this without cracks and / or damage.

Claims (10)

Wärmereflektor, dadurch gekennzeichnet, dass er mindestens eine reflektierende Schicht sowie mindestens eine Polymerfolie als Trägerschicht umfasst.Heat reflector, characterized in that it comprises at least one reflective layer and at least one polymer film as a carrier layer. Wärmereflektor nach Anspruch 1, dadurch gekennzeichnet, dass die reflektierende Schicht mindestens eine Metallschicht und/oder eine Metallfolie und/oder mindestens eine Aluminiumschicht beziehungsweise mindestens eine Aluminiumfolie umfasst.A heat reflector according to claim 1, characterized in that the reflective layer comprises at least one metal layer and / or a metal foil and / or at least one aluminum layer or at least one aluminum foil. Wärmereflektor nach einem der Ansprüche 1 oder 2, dadurch gekennzeichnet, dass er mindestens eine metall- beziehungsweise aluminiumbeschichtete Polyethylen-, Polypropylen- oder PET-Folie und/oder mindestens eine metall- beziehungsweise aluminiumbeschichtete biaxial orientierte Polypropylenfolie (BOPP-Folie) umfasst. Heat reflector according to one of claims 1 or 2, characterized in that it comprises at least one metal or aluminum coated polyethylene, polypropylene or PET film and / or at least one metal or aluminum coated biaxially oriented polypropylene film (BOPP film). Wärmereflektor nach einem der vorangegangenen Ansprüche, dadurch gekennzeichnet, dass er mindestens eine zusätzliche Schicht eines Wärmedämmmaterials umfasst. Heat reflector according to one of the preceding claims, characterized in that it comprises at least one additional layer of thermal insulation material. Wärmereflektor nach einem der vorangegangenen Ansprüche, dadurch gekennzeichnet, dass die Schicht eines Wärmedämmmaterials mindestens eine Schicht aus einem Polymermaterial und/oder mindestens eine Schaumstoffschicht aus einem Polymermaterial und/oder mindestens eine Schicht aus einem Material aus nachwachsenden Rohstoffen umfasst. A heat reflector according to one of the preceding claims, characterized in that the layer of thermal insulation material comprises at least one layer of a polymer material and / or at least one foam layer of a polymer material and / or at least one layer of a material of renewable resources. Wärmereflektor nach Anspruch 5, dadurch gekennzeichnet, dass die Schicht eines Wärmedämmmaterials mindestens ein biobasiertes Polymer, Polyethylen, Polyurethan, Ethylenvinylacetat (EVA), Polystyrol, insbesondere einen expandierten Polystyrolschaumstoff (EPS) und/oder einen extrudierten Polystyrolschaumstoff (XPS) beziehungsweise einen expandierten Polystyrolschaumstoff mit Graphit als Zusatz und/oder Copolymere beziehungsweise Mischungen davon, umfasst.A heat reflector according to claim 5, characterized in that the layer of thermal insulation material at least one bio-based polymer, polyethylene, polyurethane, ethylene vinyl acetate (EVA), polystyrene, in particular an expanded polystyrene foam (EPS) and / or an extruded polystyrene foam (XPS) or an expanded polystyrene foam with Graphite as additive and / or copolymers or mixtures thereof. Wärmereflektor nach einem der vorangegangenen Ansprüche, dadurch gekennzeichnet, dass die Dicke der Schicht eines Wärmedämmmaterials zwischen 0,1 mm und 50 mm, bevorzugt zwischen 0,2 mm und 30 mm, weiter bevorzugt zwischen 0,5 mm und 20 mm, bevorzugt zwischen 1 mm und 15 mm, weiter bevorzugt zwischen 1,5 mm und 10 mm, weiter bevorzugt zwischen 1,75 mm und 5 mm, weiter bevorzugt zwischen 2 mm und 4 mm liegt und/oder die Dicke der Trägerschicht zwischen 0,5 µm und 2 mm, bevorzugt zwischen 1 µm und 1 mm, weiter bevorzugt zwischen 2 µm und 900 µm, weiter bevorzugt zwischen 3 µm und 700 µm, weiter bevorzugt zwischen 4 µm und 500 µm weiter bevorzugt zwischen 5 µm und 350 µm, weiter bevorzugt zwischen 6 µm und 200 µm, weiter bevorzugt zwischen 6,5 µm und 100 µm, weiter bevorzugt zwischen 7 µm und 50 µm, weiter bevorzugt zwischen 7,5 µm und 20 µm, weiter bevorzugt zwischen 7,7 µm und 15 µm, weiter bevorzugt zwischen 8 µm und 12 µm liegt und/oder die Dicke der reflektierenden Schicht zwischen 0,005 µm und 2 mm, bevorzugt zwischen 0,01 µm und 1 mm, weiter bevorzugt zwischen 0,012 µm und 750 µm, weiter bevorzugt zwischen 0,015 mm und 500 µm, weiter bevorzugt zwischen 0,017 µm und 400 µm, weiter bevorzugt zwischen 0,020 µm und 350 µm, weiter bevorzugt zwischen 0,020 µm und 200 µm, weiter bevorzugt zwischen 0,025 µm und 150 µm, weiter bevorzugt zwischen 0,027 µm und 100 µm liegen, weiter bevorzugt zwischen 0,030 µm und 50 µm, weiter bevorzugt zwischen 0,035 µm und 25 µm, weiter bevorzugt zwischen 0,04 µm und 10 µm, weiter bevorzugt zwischen 0,05 µm und 5 µm liegen, weiter bevorzugt zwischen 0,055 µm und 1 µm liegen, weiter bevorzugt zwischen 0,06 µm und 0,1 µm liegt. Heat reflector according to one of the preceding claims, characterized in that the thickness of the layer of thermal insulation material between 0.1 mm and 50 mm, preferably between 0.2 mm and 30 mm, more preferably between 0.5 mm and 20 mm, preferably between 1 mm and 15 mm, more preferably between 1.5 mm and 10 mm, more preferably between 1.75 mm and 5 mm, more preferably between 2 mm and 4 mm, and / or the thickness of the carrier layer is between 0.5 μm and 2 mm, preferably between 1 μm and 1 mm, more preferably between 2 μm and 900 μm, more preferably between 3 μm and 700 μm, more preferably between 4 μm and 500 μm, more preferably between 5 μm and 350 μm, further preferably between 6 μm and 200 μm, more preferably between 6.5 μm and 100 μm, more preferably between 7 μm and 50 μm, more preferably between 7.5 μm and 20 μm, more preferably between 7.7 μm and 15 μm, further preferably between 8 microns and 12 microns and / or the thickness of the reflective layer between 0.005 microns and 2 mm, preferably between 0.01 microns and 1 mm, more preferably between 0.012 microns and 750 microns, more preferably between 0.015 mm and 500 microns, more preferably between 0.017 microns and 400 microns, more preferably between 0.020 μm and 350 μm, more preferably between 0.020 μm and 200 μm, more preferably between 0.025 μm and 150 μm, more preferably between 0.027 μm and 100 μm, more preferably between 0.030 μm and 50 μm, further preferably between 0.035 μm and 25 μm , more preferably between 0.04 μm and 10 μm, more preferably between 0.05 μm and 5 μm, more preferably between 0.055 μm and 1 μm, more preferably between 0.06 μm and 0.1 μm. Wärmereflektor nach einem der vorangegangenen Ansprüche, dadurch gekennzeichnet, dass er mindestens eine Sollbruchstelle umfasst.Heat reflector according to one of the preceding claims, characterized in that it comprises at least one predetermined breaking point. Wärmereflektor nach einem der vorangegangenen Ansprüche, dadurch gekennzeichnet, dass er so gestaltet ist, dass er mindestens zwei plattenförmige Teile umfasst, die über mindestens eine Gelenkstelle zusammenfaltbar miteinander verbunden sind.Heat reflector according to one of the preceding claims, characterized in that it is designed so that it comprises at least two plate-shaped parts, which are connected to each other foldable via at least one hinge point. Wärmereflektor nach einem der vorangegangenen Ansprüche, dadurch gekennzeichnet, dass er mindestens eine zusätzliche Klebeschicht umfasst, die auf der der reflektierenden Schicht abgewandten Seite aufgebracht ist.Heat reflector according to one of the preceding claims, characterized in that it comprises at least one additional adhesive layer, which is applied on the side facing away from the reflective layer.
DE201220103291 2012-08-29 2012-08-29 Reflector with polymer film Expired - Lifetime DE202012103291U1 (en)