DE202009018006U1 - Implant made of an intermetallic titanium aluminide alloy - Google Patents

Implant made of an intermetallic titanium aluminide alloy Download PDF

Info

Publication number
DE202009018006U1
DE202009018006U1 DE202009018006U DE202009018006U DE202009018006U1 DE 202009018006 U1 DE202009018006 U1 DE 202009018006U1 DE 202009018006 U DE202009018006 U DE 202009018006U DE 202009018006 U DE202009018006 U DE 202009018006U DE 202009018006 U1 DE202009018006 U1 DE 202009018006U1
Authority
DE
Germany
Prior art keywords
implant according
alloy
implant
temperature
phase
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE202009018006U
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to DE202009018006U priority Critical patent/DE202009018006U1/en
Publication of DE202009018006U1 publication Critical patent/DE202009018006U1/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

Implantat, hergestellt aus einer Titanaluminid(TiAl)-Legierung.Implant made of a titanium aluminide (TiAl) alloy.

Description

Die Erfindung betrifft ein Implantat, insbesondere ein künstliches Knie- oder Hüftgelenk.The The invention relates to an implant, in particular an artificial one Knee or hip joint.

Nach dem Stand der Technik ist es bekannt, ein künstliches Knie- oder Hüftgelenk beispielsweise aus einer Kobalt-Chromlegierung herzustellen. Eine solche Legierung weist keine besonders gute Biokompatibilität auf. Insbesondere darin enthaltenes Chrom oder auch Nickel können zur Entstehung von Allergien beitragen.To It is known in the art to have an artificial knee or hip joint for example, to produce a cobalt-chromium alloy. Such Alloy has no particularly good biocompatibility. Especially Chromium or nickel contained therein can lead to allergies contribute.

Zur Überwindung dieses Nachteils werden Knie- oder Hüftimplantate heute im Wesentlichen aus Titan hergestellt. Titan hat allerdings den Nachteil, dass es relativ weich ist. Die Herstellung von Implantaten aus Titan erfolgt mittels spanabhebender Verfahren. Das ist äußerst kosten- und zeitaufwändig.To overcome This disadvantage is knee or hip implants today essentially made of titanium. However, titanium has the disadvantage that it is relatively soft. The production of titanium implants takes place by means of cutting processes. This is extremely costly and time consuming.

Aufgabe der Erfindung ist es, die Nachteile nach dem Stand der Technik zu beseitigen. Es soll insbesondere ein Implantat mit verbesserten Eigenschaften angegeben werden.task The invention is to the disadvantages of the prior art remove. It is intended in particular an implant with improved Properties are specified.

Diese Aufgabe wird durch die Merkmale des Anspruchs 1 gelöst. Zweckmäßige Ausgestaltungen der Erfindung ergeben sich aus den Merkmalen der Ansprüche 2 bis 12.These The object is solved by the features of claim 1. Advantageous embodiments of Invention emerge from the features of claims 2 to 12th

Nach Maßgabe der Erfindung wird ein aus einer Titanaluminid(TiAl)-Legierung hergestelltes Implantat vorgeschlagen. Bei Titanaluminid handelt es sich um eine intermetallische Verbindung aus Titan und Aluminium. Ein aus einer Titanaluminid-Legierung hergestelltes Implantat weist im Vergleich zu Implantaten nach dem Stand der Technik erheblich verbesserte Verschleißeigenschaften auf.To proviso The invention is a made of a titanium aluminide (TiAl) alloy Implant proposed. Titanium aluminide is a intermetallic compound of titanium and aluminum. One from one Titanium aluminide alloy manufactured implant has compared to implants after State of the art significantly improved wear properties on.

Nach einer vorteilhaften Ausgestaltung weist ein Gefüge der Titanaluminid-Legierung zwei Phasen auf. Dabei kann eine erste Phase γ-TiAl und eine zweite Phase α2-Ti3Al sein. Es hat sich als zweckmäßig erwiesen, ein Verhältnis α2/γ zwischen 0,03 und 0,15 einzustellen.According to an advantageous embodiment, a structure of the titanium aluminide alloy has two phases. In this case, a first phase can be γ-TiAl and a second phase can be α 2 -Ti 3 Al. It has proven to be expedient to set a ratio α 2 / γ of between 0.03 and 0.15.

Nach einer weiteren Ausgestaltung ist das Gefüge ein near-Gamma-Gefüge. Ein solches Gefüge weist äquiaxiale γ-Körner und an den Korngrenzen oder Tripelpunkten befindliche α2-Körner auf. Bei dem Gefüge kann es sich aber auch um ein Duplex-Gefüge handeln. Ein solches Gefüge weist globulare γ-Körner und α2/γ-Körner auf.According to a further embodiment, the microstructure is a near gamma microstructure. Such a structure has equiaxed γ grains and α 2 grains at the grain boundaries or triple points. The structure may also be a duplex structure. Such a structure has globular γ grains and α 2 / γ grains.

Nach einer besonders vorteilhaften Ausgestaltung weist die TiAl-Legierung die folgende Zusammensetzung auf:
Al (45–49 at%), X1 (2–4 at%), X2 (1–8 at%), X3 (≤ 1 at%),
Rest Ti sowie unvermeidbare Verunreinigungen, wobei
X1 = Seltenerdmetalle, z. B. Yttrium, Praseodym
X2 = Niob (Nb), Wolfram (W), Tantal (Ta), Rhenium (Rh)
X3 = O, C.According to a particularly advantageous embodiment, the TiAl alloy has the following composition:
Al (45-49 at%), X1 (2-4 at%), X2 (1-8 at%), X3 (≤ 1 at%),
Residual Ti as well as unavoidable impurities, wherein
X1 = rare earth metals, e.g. Yttrium, praseodymium
X2 = niobium (Nb), tungsten (W), tantalum (Ta), rhenium (Rh)
X3 = O, C.

Nach einer weiteren vorteilhaften Ausgestaltung wird das Implantat, vorzugsweise für eine Dauer von 1 bis 200 Stunden, besonders bevorzugt für eine Dauer von 80 bis 150 Stunden, auf eine Temperatur aufgeheizt, welche im Bereich der eutektischen Temperatur liegt und geringer als die alphatransus Temperatur ist. Die Temperatur kann 10 bis 50°C höher oder niedriger als die eutektische Temperatur liegen.To In a further advantageous embodiment, the implant, preferably for one Duration of 1 to 200 hours, more preferably for a duration from 80 to 150 hours, heated to a temperature in the Range of eutectic temperature is lower and lower than the alphatransus Temperature is. The temperature can be 10 to 50 ° C higher or lower than that eutectic temperature are.

Nach einer weiteren besonders vorteilhaften Ausgestaltung wird das Implantat als Gussteil aus der Titanaluminid-Legierung hergestellt. Zur Herstellung eines solchen Gussteils wird zweckmäßigerweise ein Schleudergussverfahren verwendet.To Another particularly advantageous embodiment is the implant produced as a casting from the titanium aluminide alloy. For the production such a casting is suitably a centrifugal casting process used.

Es kann aber auch sein, dass das Implantat mittels Schmieden unter isothermen oder quasi-isothermen Bedingungen im Bereich der Temperatur der (α + γ)-Phase der Titanaluminid-Legierung hergestellt wird. Die entsprechende Temperatur der (α + γ)-Phase kann aus dem TiAl-Phasendiagramm entnommen werden.It But it can also be that the implant by forging under isothermal or quasi-isothermal conditions in the temperature range the (α + γ) phase of Titanium aluminide alloy is produced. The corresponding temperature the (α + γ) phase can be derived from the TiAl phase diagram are taken.

Nach einer weiteren Ausgestaltung kann zumindest eine tribologisch beanspruchte Oberfläche des Implantats mit einer aus Al2O3 gebildeten Schicht versehen sein. Die vorerwähnte Al2O3-Schicht kann aus dem Grundwerkstoff über den bekannten Halogeneffekt erzeugt werden.According to a further embodiment, at least one tribologically stressed surface of the implant can be provided with a layer formed from Al 2 O 3 . The aforementioned Al 2 O 3 layer can be produced from the base material via the known halogen effect.

Beispiellegierung:Example Alloy:

  • 49 at% Al, 8 at% Nb, Rest Ti sowie unvermeidbare Verunreinigungen49 at% Al, 8 at% Nb, balance Ti and unavoidable impurities

Die vorgenannte Legierung kann im Schleudergussverfahren vergossen werden. Ein daraus hergestelltes Gussteil, welches beispielsweise die Form eines Knieimplantats aufweisen kann, kann nachfolgend einer Wärmebehandlung unterzogen werden. Dazu wird das Gussteils für eine Dauer von 5 Stunden auf eine Temperatur aufgeheizt, welche etwa 20°C höher als die eutektische Temperatur ist. Mit der Wärmebehandlung kann das Gefüge eingestellt werden. Ferner kann damit eine Übergangstemperatur für den Spröd-Duktil-Übergang der Legierung herabgesetzt und gleichzeitig die Zugfestigkeit sowie die Duktilität erhöht werden.The The aforementioned alloy can be cast by centrifugal casting. A casting made therefrom, which, for example, the shape a knee implant may subsequently undergo a heat treatment be subjected. This is the casting for a period of 5 hours heated to a temperature which is about 20 ° C higher than the eutectic temperature is. With the heat treatment can the structure be set. Furthermore, thus a transition temperature for the brittle-ductile transition reduced alloy while the tensile strength and the ductility elevated become.

Zur weiteren Verbesserung der Qualität des Gussteils ist es auch möglich, dieses mittels heißisostatischem Pressen (HIP) zu verdichten. Damit können insbesondere im Gussteil befindliche Poren und Lunker geschlossen werden.to further improvement of the quality the casting is also possible this by means of hot isostatic Compacting presses (HIP). This can be especially in the casting located pores and voids are closed.

Nach einer weiteren Ausgestaltung kann zumindest eine tribologisch beanspruchte Oberfläche des Implantats mit einer aus Al2O3 gebildeten Schicht versehen sein. Die vorerwähnte Al2O3-Schicht kann aus dem Grundwerkstoff über den bekannten Halogeneffekt erzeugt werden.According to a further embodiment, at least one tribologically stressed surface of the implant can be provided with a layer formed from Al 2 O 3 . The aforementioned Al 2 O 3 layer can be produced from the base material via the known halogen effect.

Claims (12)

Implantat, hergestellt aus einer Titanaluminid(TiAl)-Legierung.Implant made of a titanium aluminide (TiAl) alloy. Implantat nach Anspruch 1, wobei es ein zwei Phasen umfassendes Gefüge aufweist.An implant according to claim 1, wherein it is a two-phase comprehensive structure having. Implantat nach einem der vorhergehenden Ansprüche, wobei eine erste Phase γ-TiAl und eine zweite Phase α2-Ti3Al ist.An implant according to any one of the preceding claims, wherein a first phase is γ-TiAl and a second phase is α 2 -Ti 3 Al. Implantat nach einem der vorhergehenden Ansprüche, wobei ein Verhältnis α2/γ zwischen 0,03 und 0,15 ist.An implant according to any one of the preceding claims, wherein a ratio α 2 / γ is between 0.03 and 0.15. Implantat nach einem der vorhergehenden Ansprüche, wobei das Gefüge ein near-Gamma-Gefüge ist.Implant according to one of the preceding claims, wherein the structure is a near-gamma structure. Implantat nach einem der vorhergehenden Ansprüche, wobei das Gefüge ein Duplex-Gefüge ist.Implant according to one of the preceding claims, wherein the structure a duplex structure is. Implantat nach einem der vorhergehenden Ansprüche, wobei die TiAl-Legierung die folgende Zusammensetzung aufweist: Al (45–49 at%), X1 (2–4 at%), X2 (1–8 at%), X3 (≤ 1 at%), Rest Ti sowie unvermeidbare Verunreinigungen, wobei X1 = Seltenerdmetalle, z. B. Yttrium, Praseodym X2 = Niob (Nb), Wolfram (W), Tantal (Ta), Rhenium (Rh) X3 = O, C.Implant according to one of the preceding claims, wherein the TiAl alloy has the following composition: al (45-49 at%), X1 (2-4 at%), X2 (1-8 at%), X3 (≤ 1 at%), rest Ti and unavoidable impurities, where X1 = rare earth metals, z. Yttrium, praseodymium X2 = niobium (Nb), tungsten (W), tantalum (Ta), rhenium (Rh) X3 = O, C. Implantat nach einem der vorhergehenden Ansprüche, wobei es, vorzugsweise für eine Dauer von 1 bis 200 Stunden, besonders bevorzugt für eine Dauer von 80 bis 150 Stunden, auf eine Temperatur aufgeheizt wird, welche im Bereich der eutektischen Temperatur liegt und geringer als die alphatransus Temperatur ist.Implant according to one of the preceding claims, wherein it, preferably for a duration of 1 to 200 hours, more preferably for a duration from 80 to 150 hours, is heated to a temperature which is in the range of eutectic temperature and less than that alphatransus temperature is. Implantat nach einem der vorhergehenden Ansprüche, wobei es als Gussteil aus der TiAl-Legierung hergestellt ist.Implant according to one of the preceding claims, wherein it is made as a casting of the TiAl alloy. Implantat nach einem der vorhergehenden Ansprüche, wobei es mittels Schmieden unter isothermen oder quasi-isothermen Bedingungen im Bereich einer Temperatur der (α + γ)-Phase der TiAl-Legierung hergestellt ist.Implant according to one of the preceding claims, wherein it by means of forging under isothermal or quasi-isothermal conditions in the range of a temperature of the (α + γ) phase of TiAl alloy is made. Implantat nach einem der vorhergehenden Ansprüche, wobei zumindest an einer tribologisch beanspruchten Oberfläche eine aus Al2O3 gebildete Schicht vorgesehen ist.Implant according to one of the preceding claims, wherein at least on a tribologically stressed surface, a layer formed from Al 2 O 3 is provided. Implantat nach einem der vorhergehenden Ansprüche, wobei es Bestanteil eines künstlichen Knie- oder Hüftgelenks ist.Implant according to one of the preceding claims, wherein it best part of an artificial knee or hip joint is.
DE202009018006U 2009-05-13 2009-06-18 Implant made of an intermetallic titanium aluminide alloy Expired - Lifetime DE202009018006U1 (en)