DE202009013059U1 - Wood strips composite element - Google Patents

Wood strips composite element Download PDF

Info

Publication number
DE202009013059U1
DE202009013059U1 DE202009013059U DE202009013059U DE202009013059U1 DE 202009013059 U1 DE202009013059 U1 DE 202009013059U1 DE 202009013059 U DE202009013059 U DE 202009013059U DE 202009013059 U DE202009013059 U DE 202009013059U DE 202009013059 U1 DE202009013059 U1 DE 202009013059U1
Authority
DE
Germany
Prior art keywords
wood
composite panel
composite
containing elements
panel according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE202009013059U
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from DE200910006834 external-priority patent/DE102009006834B4/en
Application filed by Individual filed Critical Individual
Priority to DE202009013059U priority Critical patent/DE202009013059U1/en
Publication of DE202009013059U1 publication Critical patent/DE202009013059U1/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

Verbundplatte, die holzhaltige Elemente (1) und ein in die Elementzwischenräume eingefülltes verfestigtes Material (2) aufweist, dadurch gekennzeichnet, daß die holzhaltigen Elemente (1) in einer Ebene angeordnet sind und auf mindestens einer der oberen und der unteren Oberfläche der Verbundplatte die holzhaltigen Elemente (1) und das Material (2) flächenbündig vorliegen.Composite panel comprising wood-containing elements (1) and a solidified material (2) filled in the element spaces, characterized in that the wood-containing elements (1) are arranged in one plane and on at least one of the upper and lower surfaces of the composite board the wood-containing ones Elements (1) and the material (2) are flush.

Figure 00000001
Figure 00000001

Description

Gebiet der ErfindungField of the invention

Die vorliegende Erfindung betrifft eine Verbundplatte, die holzhaltige Elemente (1) und ein in die Elementzwischenräume eingefülltes verfestigtes Material (2) aufweist, dadurch gekennzeichnet, daß die holzhaltigen Elemente (1) in einer Ebene angeordnet sind und auf mindestens einer der oberen und der unteren Oberfläche der Verbundplatte die holzhaltigen Elemente (1) und das Material (2) flächenbündig vorliegen.The present invention relates to a composite panel comprising wood-containing elements ( 1 ) and a solidified material filled in the element spaces ( 2 ), characterized in that the wood-containing elements ( 1 ) are arranged in one plane and on at least one of the upper and the lower surface of the composite panel the wood-containing elements ( 1 ) and the material ( 2 ) are flush.

Stand der TechnikState of the art

Hintergrund der ErfindungBackground of the invention

Im Stand der Technik sind Elemente bekannt, beispielsweise Plexiglasplatten, auf die Holzstreifen aufgeklebt werden, so daß sich die Optik eines Glas-Holz-Verbundes ergibt.in the Prior art elements are known, for example Plexiglas plates, be glued to the wooden strips, so that the Optics of a glass-wood composite results.

Diese Elemente sind jedoch mit dem Problem behaftet, dass deren Herstellung aufwändig und damit teuer ist, da die Plexiglaselemente sehr genau ausgefräst werden müssen, so daß die Holzstreifen passgenau angebracht werden können.These However, elements have the problem that their production consuming and therefore expensive, since the Plexiglas elements must be very precisely milled, so that the Wood strips can be fitted accurately.

Aufgabenstellungtask

Durch die Erfindung zu lösende AufgabeTo be solved by the invention task

Somit stellt sich die Aufgabe, derartige Verbundelemente aus Holz mit einem vorzugsweise durchscheinenden Kunststoff auf einfache Weise und kostengünstig herzustellen.Consequently sets itself the task of such composite elements made of wood a preferably translucent plastic in a simple manner and inexpensive to manufacture.

Zusammenfassende Darstellung der ErfindungSummary of the invention

Diese Aufgabe wird durch die vorliegende Erfindung gelöst.These Problem is solved by the present invention.

Die vorliegende Erfindung betrifft eine Verbundplatte, die holzhaltige Elemente (1) und ein in die Elementzwischenräume eingefülltes verfestigtes Material (2) aufweist, dadurch gekennzeichnet, daß die holzhaltigen Elemente (1) in einer Ebene angeordnet sind und auf mindestens einer der oberen und der unteren Oberfläche der Verbundplatte die holzhaltigen Elemente (1) und das Material (2) flächenbündig vorliegen.The present invention relates to a composite panel comprising wood-containing elements ( 1 ) and a solidified material filled in the element spaces ( 2 ), characterized in that the wood-containing elements ( 1 ) are arranged in one plane and on at least one of the upper and the lower surface of the composite panel the wood-containing elements ( 1 ) and the material ( 2 ) are flush.

Die Vorteile dieser Ausführungsform gegenüber herkömmlichen Kunststoffflächen mit Holzeinlagen sind die einfache Herstellung, die Stabilität sowie die Biegsamkeit des Elements.The Advantages of this embodiment over conventional Plastic surfaces with wood inserts are the simple production, the stability as well as the flexibility of the element.

Während herkömmlich aus Kunststoffflächen, z. B. aus Plexiglas, streifenförmige Aussparungen ausgeschnitten werden, die dann mit Holzstreifen gefüllt werden, besteht das erfindungsgemässe Verbundelement abwechselnd aus Holzstreifen und Kunststoffmaterial. Somit wird Material eingespart. Außerdem ist die Herstellung einfacher.While conventionally made of plastic surfaces, z. Made of Plexiglas, strip-shaped recesses are cut out, the then filled with strips of wood, the inventive consists Composite element alternately made of wood strips and plastic material. Thus, material is saved. Besides, the production is easier.

Ein weiterer Vorteil ist die Biegsamkeit des Elements. In herkömmlichen Elementen wird die Biegsamkeit durch die Eigenschaften der Kunststofffläche bestimmt. Außerdem sind diese Elemente nicht stabil und ohne Spannung verformbar.One Another advantage is the flexibility of the element. In conventional The flexibility of these elements is due to the properties of the plastic surface certainly. Moreover, these elements are not stable and without Tension deformable.

Beschreibung der ZeichnungDescription of the drawing

1 zeigt eine Ansicht eines erfindungsgemässen Verbundelements 1 shows a view of a composite element according to the invention

2 zeigt einen Querschnitt eines erfindungsgemässen 2 shows a cross section of an inventive

11
holzhaltiges Elementwood-containing element
22
eingefülltes verfestigtes Materialbeen completed solidified material

Eingehende Beschreibung der ErfindungDetailed description of the invention

Das Holzhaltige Element (1) kann aus einem beliebigen Material bestehen, beispielsweise Kunststoff oder Holz. Vorzugsweise ist das Element jedoch ein Holz enthaltendes Element. Dabei kann es sich um ein mit Holz furniertes Element oder um ein Massivholzelement handeln. Das Holz enthaltende Element besteht aus einem beliebigen Holz oder ist aus unterschiedlichen Hölzern zusammengesetzt. Das in der Erfindung eingesetzte Holzhaltige Element (1) ist bevorzugt ein streifenförmiges Holzelement, also ein Flachholzstück.The woody element ( 1 ) may be made of any material, such as plastic or wood. Preferably, however, the element is a wood-containing element. It may be a veneered with wood element or a solid wood element. The wood-containing element is made of any wood or is composed of different woods. The wood-containing element used in the invention ( 1 ) is preferably a strip-shaped wooden element, so a piece of flat wood.

Das Material (2) kann in einer Menge in die Zwischenräume eingefüllt werden, die ausreicht, um die Elementzwischenräume auszufüllen. Beim Aushärten des Materials verringert sich üblicherweise dessen Volumen, so dass eine meniskusartig zu den Kontaktflächen mit dem plattenförmigen Material hin gewölbte Fläche entsteht. Das so hergestellte Verbundmaterial kann als solches oder nach Planschleifen der Oberfläche eingesetzt werden. Es kann jedoch auch ein grössere Menge an flüssigem Material auf das holzhaltige Element (1) aufgetragen werden, so dass nicht nur die Elementzwischenräume ausgefüllt werden, sondern auch eine Überzugsschicht auf dem Element entsteht. Diese Ausführungsform lässt sich bevorzugt dann erzielen, wenn das holzhaltige Element (1) mindestens eine flächenförmige und plane Oberfläche aufweist.The material ( 2 ) can be filled in an amount in the spaces sufficient to fill the element spaces. During curing of the material usually reduces its volume, so that a meniscus-like arching to the contact surfaces with the plate-shaped material surface is formed. The composite material thus produced can be used as such or after surface grinding of the surface. However, it can also be a larger amount of liquid material on the wood-containing element ( 1 ) are applied, so that not only the element interstices are filled, but also creates a coating layer on the element. This embodiment can preferably be achieved if the wood-containing element ( 1 ) has at least one planar and planar surface.

Das einzufüllende Material kann auch aus zwei unterschiedlichen Materialien bestehen. Beispielsweise können die Elementzwischenräume in dem Element mit einem farbigen Material ausgefüllt und das so erhaltene Element mit einem klaren Material überzogen sein.The material to be filled can also be made of two different ones Materials exist. For example, the element spaces in the element filled with a colored material and coated the element thus obtained with a clear material be.

Als in das Holzelement einzufüllendes Material können bevorzugt übliche Harze, insbesondere Kunstharze, eingesetzt werden. Der hier verwendete Ausdruck ”Kunstharz” bezeichnet durch Polymerisation, Polyaddition oder Polykondensation gewonnene Harze (z. B. Aminoplaste, Epoxidharze, Phenolharze), die gegebenenfalls durch Naturstoffe (fette Öle, Naturharze) modifiziert sind. Ebenso umfassen Kunstharze auch durch chemische Umsetzung (z. B. Veresterung, Verseifung) veränderte Naturharze. Ein bevorzugtes Material ist ein Epoxidharz. Der Ausdruck ”Kunstharze” soll Kunststoffe, beispielsweise Polycarbonat, Acryl und dergleichen ausschliessen, da diese Materialien die für das einzufüllende Material gewünschten Eigenschaften nicht in dem Masse wie die Kunstharze aufweisen.When in the wood element einzufüllendes material can preferably customary resins, in particular synthetic resins used become. As used herein, the term "synthetic resin" obtained by polymerization, polyaddition or polycondensation Resins (eg, aminoplasts, epoxy resins, phenolic resins), optionally by natural substances (fatty oils, natural resins) are modified. Likewise, synthetic resins also include by chemical reaction (eg. Esterification, saponification) modified natural resins. A preferred one Material is an epoxy resin. The term "synthetic resins" is intended Exclude plastics, such as polycarbonate, acrylic and the like, because these materials are the ones to be filled in Material desired properties not in the crowd like have the synthetic resins.

Die Harze enthalten vorzugsweise einen Härter.The Resins preferably contain a hardener.

Das Material ist vorzugsweise ein Kunstharz mit niedriger Viskosität, beispielsweise einer Viskosität von weniger als 10.000 mPas (22°C), stärker bevorzugt von weniger als 5.000 mPas (22°C) und noch stärker bevorzugt von weniger als 2.000 mPas (22°C) ist.The Material is preferably a low viscosity resin, for example, a viscosity of less than 10,000 mPas (22 ° C), more preferably less than 5,000 mPas (22 ° C) and even more preferably from less than 2,000 mPas (22 ° C).

Wenn das Harz einen Härter enthält, ist das Kunstharz-Härter-Gemisch das einzufüllende Material. Die Viskosität des Kunstharz-Härter-Gemisches ist vorzugsweise weniger als 2.000 mPas (22°C), stärker bevorzugt weniger als 1.000 mPas (22°C) und noch stärker bevorzugt weniger als 600 mPas (22°C).If the resin contains a hardener is the resin-hardener mixture the material to be filled. The viscosity of the Resin-hardener mixture is preferably less than 2,000 mPas (22 ° C), more preferably less than 1,000 mPas (22 ° C) and even more preferably less as 600 mPas (22 ° C).

Ausserdem ist das einzufüllende Material vorzugsweise lösungsmittelfrei, um das plattenförmige Element nicht zu beeinträchtigen.Moreover the material to be filled is preferably solvent-free, so as not to interfere with the plate-shaped element.

Vorzugsweise ist das Material lösungsmittelfreies Epoxidharz-Härter-Gemisch mit einer Viskosität von weniger als 1.000 mPas (22°C), stärker bevorzugt von weniger als 600 mPas (22°C) und noch stärker von höchstens 500 mPas (22°C).Preferably the material is solvent-free epoxy resin hardener mixture having a viscosity of less than 1,000 mPas (22 ° C), more preferably less than 600 mPas (22 ° C) and even more than 500 mPas at most (22 ° C).

Das Epoxidharz ist vorzugsweise ein Epoxidharz auf Basis von Bisphenol A/Bisphenol F. Eine mögliche Zusammensetzung enthält oder besteht aus Bisphenol A-Epichlorhydrinharz, Bisphenol F-Epoxidharz und Hexandioldiglycidylether, wobei folgende Zusammensetzung bevorzugt ist:
Bisphenol A-Epichlorhydrinharz 40 bis 60%,
Bisphenol F-Epoxidharz weniger als 30%,
Hexandioldiglycidylether weniger als 20%.The epoxy resin is preferably an epoxy resin based on bisphenol A / bisphenol F. One possible composition comprises or consists of bisphenol A-epichlorohydrin resin, bisphenol F epoxy resin and hexanediol diglycidyl ether, the following composition being preferred:
Bisphenol A-epichlorohydrin resin 40 to 60%,
Bisphenol F epoxy less than 30%,
Hexanediol diglycidyl ether less than 20%.

Der vorzugsweise enthaltene Härter kann ein modifiziertes Polyamin, das bevorzugt folgende Zusammensetzung hat:
Benzylalkohol 25 bis 50%,
3-Aminomethyl-3,5,5-trimethylcyclohexylamin 25 bis 50%,
Trimethylhexamethylendiamin 2,5 bis 10%.The preferably contained hardener may be a modified polyamine which preferably has the following composition:
Benzyl alcohol 25 to 50%,
3-aminomethyl-3,5,5-trimethylcyclohexylamine 25 to 50%,
Trimethylhexamethylenediamine 2.5 to 10%.

Das vorstehend genannte Epoxidharz hat ausserdem vorzugsweise eine Dichte von 1,15 g/cm3, der vorstehend genannte Härter weist vorzugsweise ein Dichte von 1,00 g/cm3 auf.In addition, the above-mentioned epoxy resin preferably has a density of 1.15 g / cm 3 , and the above-mentioned hardener preferably has a density of 1.00 g / cm 3 .

Weitere bevorzugte Eigenschaften des vorstehend genannten Epoxidharzes sind: Shore-Härte D: 80 ( ISO 868 , EIN 53505 ) Zugfestigkeit: 64 N/mm2 ( DIN 53455 ) Druckfestigkeit: 85 N/mm2 ( DIN 53454 ) Biegefestigkeit: 92 N/mm2 ( DIN 53452 ) Martenstemperatur: 50°C ( DIN 53458 ) Linearer Wärmeaus dehnungskoeffizient: 65 × 10–5 K–1 ( DIN 53752 ) Further preferred properties of the above-mentioned epoxy resin are: Shore hardness D: 80 ( ISO 868 . A 53505 ) Tensile strenght: 64 N / mm 2 ( DIN 53455 ) Compressive strength: 85 N / mm 2 ( DIN 53454 ) Bending strength: 92 N / mm 2 ( DIN 53452 ) Martens Temperature: 50 ° C ( DIN 53458 ) Linear coefficient of thermal expansion: 65 × 10 -5 K -1 ( DIN 53752 )

Das Mischungsverhältnis von Epoxidharz und Härter ist nicht besonders eingeschränkt, es liegt jedoch, insbesondere bei den vorstehend genannten Substanzen, bevorzugt bei 100 Gew.-Teile Epoxidharz zu 45 Gew.-Teile Härter.The Mixing ratio of epoxy resin and hardener is not particularly limited, but it is, in particular in the case of the abovementioned substances, preferably at 100 parts by weight Epoxy resin to 45 parts by weight hardener.

Das als einzufüllendes Material einzusetzende Material wird so ausgewählt, dass es bei Raumtemperatur gefüllt werden kann und gegebenenfalls unter Einsatz eines Härters bei Raumtemperatur aushärtet. Ausserdem soll das Material sich nach dem Aushärten fest mit den Elementen (1) verbinden.The material to be used as the material to be filled is selected so that it can be filled at room temperature and optionally cured using a curing agent at room temperature. In addition, the material is after hardening firmly with the elements ( 1 ) connect.

Dadurch wird ein Herausfallen des eingefüllten Material nach dem Aushärten verhindert. Das vorstehend genannte Epoxidharz erfüllt diese Massgaben.Thereby is falling out of the filled material after the Curing prevented. The above-mentioned epoxy resin meets these requirements.

Das einzufüllende Material kann in Abhängigkeit von der vorgesehenen Verwendung des Verbundelements ausgewählt werden. Ist das Verbundelement beispielsweise als Trennwand vorgesehen, ist ein klarer, transparenter oder zumindest durchscheinender Kunststoff bevorzugt. Somit kann das eingefüllte Material auch klares Glas oder Milchglas ersetzen.The material to be filled in dependence of the intended use of the composite element selected become. If the composite element is provided, for example, as a partition, is a clear, transparent or at least translucent plastic prefers. Thus, the filled material can also be clear Replace glass or frosted glass.

Das eingefüllte Material kann auch Zusatzstoffe enthalten, wie Farbpigmente, Füllstoffe, zusätzliche Stabilisatoren oder Mittel zur Erhöhung der Festigkeit des Materials. Wird das Verbundelement beispielsweise als Fussbodenelement eingesetzt, wird das Material vorzugsweise nicht nur in die Elementzwischenräume des Holzelement eingefüllt, sondern auch als Überzug über das Holzelement ausgeführt. In diesem Fall enthält das Material vorzugsweise zusätzliche Mittel zur Erhöhung der Abriebfestigkeit und dergleichen. Ausserdem umfasst das erfindungsgemässe Verbundelement, insbesondere bei Verwendung als Fussbodenelement, vorzugsweise ein rückwärtiges Plattenelement, d. h. im Fall eines Fussbodenelements ein Bodenplattenelement, das aus beliebigem Material bestehen kann und beispielsweise beliebig gefärbt sein kann. Die rückwärtige Seite kann beispielsweise auch mit einer verspiegelten Platte versehen sein, so dass bei Verwendung eines klaren oder zumindest durchscheinenden einzufüllenden Materials ein Spiegeleffekt auftritt. Weitere optische Effekte sind denkbar, beispielsweise durch Zugabe von Substanzen mit Glitzereffekt in das einzufüllende Material.The filled material can also contain additives, such as color pigments, fillers, additional stabilizers or means for increasing the strength of the material. If the composite element is used, for example, as a floor element, the material is preferably not only in the element spaces filled in the wood element, but also as a cover over executed the wooden element. In this case contains the material preferably additional means for increasing abrasion resistance and the like. In addition, the invention includes Composite element, in particular when used as a floor element, preferably a rear plate element, d. H. in the case of a floor element, a floor panel element, the can consist of any material and, for example, any can be colored. The back side can for example also be provided with a mirrored plate so that when using a clear or at least translucent material to be filled a mirror effect occurs. Further optical effects are conceivable, for example by adding substances with glitter effect in the material to be filled.

Bei der praktischen Ausführung der Verbundelemente ist darauf zu achten, dass in Abhängigkeit von der vorgesehenen Verwendung des Verbundelements bestimmte physikalische Eigenschaften des Elemente (1) und des eingefüllten Materials ähnlich sind. Beispielsweise sollten die Wärmeausdehnungskoeffizienten ähnlich sein, so dass bei Temperaturschwankungen keine Risse zwischen den unterschiedlichen Materialien entstehen.In the practical implementation of the composite elements care must be taken that, depending on the intended use of the composite element, certain physical properties of the element ( 1 ) and the filled material are similar. For example, the coefficients of thermal expansion should be similar so that with temperature variations there are no cracks between the different materials.

Durch das Aushärten des Harzes entsteht eine feste Verbindung zwischen dem holzhaltigen Element und dem Harz. Das ausgehärtete Harz stabilisiert das holzhaltige Element. Dadurch ist es möglich, beim Schleifen des Verbundelements dessen Stärke erheblich zu verringern und trotzdem ein stabiles Verbundelement zu erhalten. Beispielsweise kann das Verbundelement aus einem holzholzhaltigen Element und einem Epoxidharz in einer Stärke von 0,4 cm stabil hergestellt werden.By the curing of the resin creates a strong bond between the wood-containing element and the resin. The cured one Resin stabilizes the wood-containing element. This makes it possible when grinding the composite element whose strength considerably to reduce and still obtain a stable composite element. For example, the composite element of a wood-containing Element and an epoxy resin in a thickness of 0.4 cm be made stable.

Die vorliegende Erfindung betrifft weiterhin eine Verbundplatte, herstellbar durch ein Verfahren zur Herstellung eines erfindungsgemässen Verbundelements, welches die Stufen umfasst, bei denen das zu verfestigende Material im nicht verfestigten Zustand in die Elementzwischenräume der Elemente (1) gefüllt wird und anschliessend das Material verfestigt wird.The present invention furthermore relates to a composite panel producible by a method for producing a composite element according to the invention, which comprises the stages in which the material to be solidified in the non-solidified state into the element interstices of the elements (US Pat. 1 ) is filled and then the material is solidified.

Die Elemente (1) werden vor dem Einfüllen des Materials vorzugsweise vorbehandelt, insbesondere, wenn es sich um ein holzhaltiges Element handelt. Dadurch kann beispielsweise verhindert werden, dass das einzufüllende Material in die Poren des Holzes oder in die Schlitze eindringt, die unvermeidlich zwischen den Einzelteilen, aus denen das holzhaltige Element zusammengesetzt ist, entstehen. Dies ist besonders dann ein Problem, wenn das eingefüllte Material farbig ist.The Elements ( 1 ) are preferably pretreated prior to filling the material, especially if it is a wood-containing element. This can be prevented, for example, that the material to be filled penetrates into the pores of the wood or into the slots, which inevitably arise between the individual parts of which the wood-containing element is composed. This is especially a problem when the filled material is colored.

Dieses sogenannte Abisolieren oder Grundieren kann mit einem herkömmlicherweise für diese Zwecke eingesetzten Lack, Harz oder dergleichen durchgeführt werden. Vorzugsweise ist das Abisoliermittel klar, so dass es optisch neutral ist.This So-called stripping or priming can be done conventionally lacquer, resin or the like used for these purposes be performed. Preferably, the stripping means clear, so that it is optically neutral.

Nach dem optionalen Vorbehandeln der holzhaltigen Elemente werden diese in einer erfindungsgemässen Ausführungsform auf eine glatte Unterlage gelegt und dann ausgefüllt. Die glatte Unterlage ist beispielsweise eine Kunststofffolie, von der das Verbundelement nach dem Einfüllen und Verfestigen des Harzes wieder leicht abgelöst bzw. abgezogen werden kann. In einer anderen erfindungsgemässen Ausführungsform wird auf einer Seite der holzhaltigen Elemente (1) eine Abdeckung, beispielsweise eine Holzplatte, beispielsweise durch Kleben aufgebracht und dann ausgefüllt.After the optional pretreatment of the wood-containing elements, they are placed in an inventive embodiment on a smooth surface and then filled. The smooth base is, for example, a plastic film, from which the composite element after filling and solidification of the resin can be easily peeled off or removed again. In another embodiment according to the invention, on one side of the wood-containing elements ( 1 ) a cover, such as a wood panel, for example, applied by gluing and then filled.

In der vorliegenden Erfindung umfasst der Ausdruck ”Einfüllen” des Materials das Giessen eines niedrigviskosen Materials oder, wenn die Viskosität des Materials entsprechend hoch ist, das Auftragen des Material mit einem Hilfsmittel, beispielsweise einem Spachtel, oder einer geeigneten Vorrichtung.In of the present invention includes the term "filling" the Material pouring a low-viscosity material or, if the viscosity of the material is correspondingly high, the Applying the material with a tool, such as a Spatula, or a suitable device.

Das eingefüllte Material wird anschliessend gehärtet. Dies kann in einer bevorzugten Ausführungsform, bei der ein Epoxidharz eingesetzt wird, durch Aushärten bei Raumtemperatur während mehrerer Stunden bis einiger Tage durchgeführt werden. Dabei wird bevorzugt ein Härter eingesetzt. Es kann jedoch auch jedes andere Verfahren zum Härten von Harzen eingesetzt werden.The filled material is then cured. This can be done in a preferred embodiment in which an epoxy resin is used by curing at room temperature performed for several hours to a few days become. In this case, a hardener is preferably used. It However, any other method of curing Resins are used.

Nach dem Aushärten des Harzes wird in einer erfindungsgemässen Ausführungsform das Verbundelement plangeschliffen. Dabei kann, wenn das Harz im Überschuss über das Volumen der Elementzwischenräume eingefüllt worden ist, so dass eine Seite der holzhaltigen Elemente vollständig mit einer Harzschicht überzogen worden sind, das Material der holzhaltigen Elemente wieder freigelegt werden. Dadurch entsteht eine Oberfläche des Verbundelements, auf der sich das eingefüllte Harz und die holzhaltigen Elemente abwechseln.To the curing of the resin is in an inventive Embodiment, the composite element ground flat. there can if the resin is in excess over the volume the element interspaces has been filled in, leaving one side of the wood-containing elements complete coated with a resin layer, the material the wood-containing elements are exposed again. This creates a Surface of the composite element on which the filled Resin and the wood-containing elements alternate.

In einer anderen erfindungsgemässen Ausführungsform wird nur ein Teil der Harzschicht abgeschliffen, so dass die Oberfläche einer Seite des Verbundelements aus einer Harzschicht besteht.In another embodiment of the invention Only a portion of the resin layer is abraded, leaving the surface one side of the composite element is made of a resin layer.

In einer bevorzugten Ausführungsform befinden sich zwischen den holzholzhaltigen Elementen durchgehende Elementzwischenräume und das zu verfestigende Material ist ein Epoxidharz, wobei das Herstellungsverfahren die folgenden Stufen umfasst: Legen der holzhaltgien Elemente auf eine glatte Oberfläche; Einfüllen des Harzes in die Elementzwischenräume und gegebenenfalls auf die Elemente; Aushärten des Harzes; und Schleifen des Verbundelements.In a preferred embodiment are between the timber-wood-containing elements continuous element gaps and the material to be solidified is an epoxy resin, wherein the Manufacturing process includes the following stages: laying the wood stoppers Elements on a smooth surface; pour in of the resin in the element spaces and optionally on the elements; Curing the resin; and grinding the Composite element.

Der in der vorliegenden Anmeldung verwendete Ausdruck „Schleifen des Verbundelements” umfaßt sowohl das Abtragen von überschüssigem Harz als auch das Schleifen der holzhaltigen Elemente.Of the used in the present application "loops the composite element "includes both the ablation of excess resin as well as the grinding the woody elements.

Eine anderen bevorzugte Ausführungsform ist eine Verbundplatte, herstellbar durch das Herstellungsverfahren mit den folgenden Stufen: Abisolieren mindestens der Stirnseiten des Holzes mit einem klaren Harz oder einem Klarlack; Einfüllen eines farbigen Harzes in die Elementzwischenräume; Aushärten des Harzes; Schleifen des Verbundelements; Überziehen des Verbundelements mit einem klaren oder durchscheinenden Harz; Aushärten des Harzes; und Schleifen des Verbundelements.A another preferred embodiment is a composite panel, producible by the manufacturing process with the following steps: Strip at least the front sides of the wood with a clear stripping Resin or a clearcoat; Fill in a colored resin in the element spaces; Curing the resin; grind the composite element; Coating the composite element with a clear or translucent resin; Curing the resin; and grinding the composite element.

Die obengenannte glatte Oberfläche, auf die das holzhaltige Element gelegt wird, kann eine kostengünstige Platte sein. Nach dem Aushärten des eingefüllten Materials ist diese Platte fest mit dem holzhaltige Element verbunden. Die Platte kann dann beispielsweise durch Abschleifen entfernt werden.The above-mentioned smooth surface on which the wood-containing Element is placed, can be a low-cost plate. After curing of the filled material this plate is firmly connected to the wood-containing element. The Plate can then be removed, for example, by grinding.

Die erfindungsgemässen Verbundplatten können in eine Flüssigkeit, z. B. Wasser, eingelegt werden. Dadurch werden die Elemente weich und können leicht verformt werden. Beim Trocknen entstehen dann Verbundplatten, die stabil und dauerhaft sowie ohne Spannung die gegebene Form beibehalten.The Composite panels according to the invention can be placed in a Liquid, e.g. As water, are inserted. This will be the elements are soft and can be easily deformed. At the Drying then produces composite panels that are stable and durable as well as maintaining the given shape without tension.

Verformt wird dabei im wesentlichen das Holzelement (1). Voraussetzung für die einfache Verformbarkeit ist, daß in den Holzstreifen die Markstrahlen des Holzes parallel zu der Achse verlaufen, um die das Element gebogen wird.Essentially, the wood element ( 1 ). Prerequisite for the simple deformability is that run in the wood strip, the pith rays of the wood parallel to the axis about which the element is bent.

Vorzugsweise verlaufen die Markstrahlen parallel zu der Kontaktfläche zwischen dem streifenförmigen Element (1) und dem verfestigten Material (2). Der Querschnitt eines solchen gebogenen Elements ist in 2 gezeigt.Preferably, the medullary rays are parallel to the contact surface between the strip-shaped element ( 1 ) and the solidified material ( 2 ). The cross section of such a curved element is in 2 shown.

Die in der vorliegenden Anmeldung genannten Verbundplatten können zur Stabilisierung bzw. zur leichteren Verarbeitbarkeit auf Trägermaterialien, z. B. Trägerplatten, aufgebracht sein. Diese Trägermaterialien können nach dem Einfüllen und Verfestigen des Materials (2) entweder als Träger an dem Verbundelement gebunden verbleiben oder abgeschliffen werden.The composite plates mentioned in the present application can be used for stabilization or for easier processability on support materials, for. As carrier plates, be applied. These support materials may after filling and solidifying the material ( 2 ) either remain bound as a carrier to the composite element or ground down.

ZITATE ENTHALTEN IN DER BESCHREIBUNGQUOTES INCLUDE IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list The documents listed by the applicant have been automated generated and is solely for better information recorded by the reader. The list is not part of the German Patent or utility model application. The DPMA takes over no liability for any errors or omissions.

Zitierte Nicht-PatentliteraturCited non-patent literature

  • - ISO 868 [0024] - ISO 868 [0024]
  • - EIN 53505 [0024] - ON 53505 [0024]
  • - DIN 53455 [0024] - DIN 53455 [0024]
  • - DIN 53454 [0024] - DIN 53454 [0024]
  • - DIN 53452 [0024] - DIN 53452 [0024]
  • - DIN 53458 [0024] - DIN 53458 [0024]
  • - DIN 53752 [0024] - DIN 53752 [0024]

Claims (27)

Verbundplatte, die holzhaltige Elemente (1) und ein in die Elementzwischenräume eingefülltes verfestigtes Material (2) aufweist, dadurch gekennzeichnet, daß die holzhaltigen Elemente (1) in einer Ebene angeordnet sind und auf mindestens einer der oberen und der unteren Oberfläche der Verbundplatte die holzhaltigen Elemente (1) und das Material (2) flächenbündig vorliegen.Composite panel, the wood-containing elements ( 1 ) and a solidified material filled in the element spaces ( 2 ), characterized in that the wood-containing elements ( 1 ) are arranged in one plane and on at least one of the upper and the lower surface of the composite panel the wood-containing elements ( 1 ) and the material ( 2 ) are flush. Verbundplatte nach Anspruch 1, wobei die holzhaltigen Elemente (1) einander nicht berühren.Composite panel according to claim 1, wherein the wood-containing elements ( 1 ) do not touch each other. Verbundplatte nach Anspruch 1 oder 2, wobei die holzhaltigen Elemente (1) langgezogen sind und in Längsrichtung parallel zueinander angeordnet sind.Composite panel according to claim 1 or 2, wherein the wood-containing elements ( 1 ) are elongated and arranged in the longitudinal direction parallel to each other. Verbundplatte nach einem der vorstehenden Ansprüche, wobei die holzhaltigen Elemente (1) und das Material (2) auf der oberen und unteren Oberfläche flächenbündig vorliegen.Composite board according to one of the preceding claims, wherein the wood-containing elements ( 1 ) and the material ( 2 ) are flush on the upper and lower surfaces. Verbundplatte nach einem der vorstehenden Ansprüche, wobei die holzhaltigen Elemente (1) einander nicht berühren und die jeweiligen Abschnitte des in die Elementzwischenräume eingefüllten verfestigten Materials (2) einander nicht berühren.Composite board according to one of the preceding claims, wherein the wood-containing elements ( 1 ) do not touch each other and the respective sections of the solidified material filled in the element spaces ( 2 ) do not touch each other. Verbundplatte nach einem der vorstehenden Ansprüche, wobei die holzhaltigen Elemente (1) aus Furnierholz bestehen.Composite board according to one of the preceding claims, wherein the wood-containing elements ( 1 ) consist of plywood. Verbundplatte nach einem der Ansprüche 1 bis 6, wobei die holzhaltigen Elemente (1) aus Massivholz bestehen.Composite board according to one of claims 1 to 6, wherein the wood-containing elements ( 1 ) consist of solid wood. Verbundplatte nach einem der vorstehenden Ansprüche, welches eine Dicke von 2 mm bis 20 mm hat.Composite panel according to one of the preceding claims, which has a thickness of 2 mm to 20 mm. Verbundplatte nach einem der vorstehenden Ansprüche, welches eine Dicke von 3 mm bis 8 mm hat.Composite panel according to one of the preceding claims, which has a thickness of 3 mm to 8 mm. Verbundplatte nach einem der vorstehenden Ansprüche, wobei die holzhaltigen Elemente (1) zwischen zwei Elementzwischenräumen eine Breite von 3 mm bis 100 mm aufweist.Composite board according to one of the preceding claims, wherein the wood-containing elements ( 1 ) between two element gaps has a width of 3 mm to 100 mm. Verbundplatte nach Anspruch 10, wobei die Breite 4 mm bis 50 mm ist.The composite panel of claim 10, wherein the width 4 mm to 50 mm. Verbundplatte nach Anspruch 11, wobei die Breite 10 mm bis 20 mm ist.The composite panel of claim 11, wherein the width 10 mm to 20 mm. Verbundplatte nach einem der vorstehenden Ansprüche, wobei die Elementzwischenräume zwischen zwei holzhaltigen Elementen (1) eine Breite von mindestens 5 mm aufweist.Composite panel according to one of the preceding claims, wherein the element spaces between two wood-containing elements ( 1 ) has a width of at least 5 mm. Verbundplatte nach Anspruch 13, wobei die Breite 10 mm bis 100 mm ist.The composite panel of claim 13, wherein the width 10 mm to 100 mm. Verbundplatte nach Anspruch 14, wobei die Breite 10 mm bis 50 mm ist.The composite panel of claim 14, wherein the width 10 mm to 50 mm. Verbundplatte nach einem der vorstehenden Ansprüche, welches eine Dicke von 4 bis 8 mm aufweist, wobei die Breite der holzhaltigen Elemente (1) 5 mm bis 50 mm und die Breite der Elementzwischenräume 5 bis 50 mm ist.A composite panel according to any one of the preceding claims, having a thickness of 4 to 8 mm, the width of the wood-containing elements ( 1 ) 5 mm to 50 mm and the width of the element interspaces is 5 to 50 mm. Verbundplatte nach einem der vorstehenden Ansprüche, wobei die Kontaktflächen der holzhaltigen Elemente (1) und des Materials (2) parallel zueinander sind.Composite panel according to one of the preceding claims, wherein the contact surfaces of the wood-containing elements ( 1 ) and the material ( 2 ) are parallel to each other. Verbundplatte nach einem der vorstehenden Ansprüche, wobei die obere oder die untere Oberfläche der Verbundplatte aus Material (2) besteht.A composite panel according to any one of the preceding claims, wherein the upper or lower surface of the composite panel of material ( 2 ) consists. Verbundplatte nach einem der vorstehenden Ansprüche, die auf einer Seite zusätzlich eine Trägerplatte (3) aufweist.Composite panel according to one of the preceding claims, which additionally has on one side a support plate ( 3 ) having. Verbundplatte nach einem der vorstehenden Ansprüche, wobei das Material (2) ein holzhaltiges Material ist.Composite panel according to any one of the preceding claims, wherein the material ( 2 ) is a wood-containing material. Verbundplatte nach einem der vorstehenden Ansprüche, wobei das Material (2) ein Kunststoff ist.Composite panel according to any one of the preceding claims, wherein the material ( 2 ) is a plastic. Verbundplatte nach einem der vorstehenden Ansprüche, wobei das Material (2) ein Kunstharz ist.Composite panel according to any one of the preceding claims, wherein the material ( 2 ) is a synthetic resin. Verbundplatte nach einem der vorstehenden Ansprüche, wobei das Material (2) ein lösungsmittelfreies Kunstharz ist.Composite panel according to any one of the preceding claims, wherein the material ( 2 ) is a solvent-free synthetic resin. Verbundplatte nach einem der vorstehenden Ansprüche, wobei das Material (2) ein Epoxidharz ist.Composite panel according to any one of the preceding claims, wherein the material ( 2 ) is an epoxy resin. Verbundplatte nach einem der vorstehenden Ansprüche, die (a) in einer Richtung der Plattenebene abwechselnd aus Elementen (1) und Material (2) und (b) gegebenenfalls einer Trägerplatte besteht.A composite panel according to any one of the preceding claims comprising: (a) in a direction of the plane of the panel alternating elements ( 1 ) and material ( 2 ) and (b) optionally a carrier plate. Verbundplatte, erhältlich nach einem Verfahren, welches die Stufen umfaßt, bei denen holzhaltige Elemente (1) nebeneinander auf eine glatte Oberfläche oder auf eine Trägerplatte (3) gegeben werden, das Material (2) im flüssigen Zustand in die Elementzwischenräume gegossen wird, das Material verfestigt wird, die Verbundplatte gegebenenfalls verformt wird, und die Verbundplatte auf mindestens einer Seite plangeschliffen wird.Composite board obtainable by a process comprising the stages comprising wood-containing elements ( 1 ) side by side on a smooth surface or on a carrier plate ( 3 ), the material ( 2 ) is poured in the liquid state in the element interstices, the material is solidified, the composite plate is optionally deformed, and the composite plate is ground flat on at least one side. Verbundplatte nach einem der vorstehenden Ansprüche, die Elemente (1) aus Furnierholz oder Massivholz und einen in die Elementzwischenräume eingefülltes verfestigtes Kunststoffmaterial (2) aufweist, dadurch gekennzeichnet, daß die Verbundplatte eine Dicke von 3 bis 15 mm aufweist, die Kontaktflächen der holzhaltigen Elemente (1) und des Materials (2) parallel zueinander sind, die holzhaltigen Elemente (1) sich in ihrer Länge über die gesamte Verbundplatte erstrecken, eine Breite von 5 mm bis 100 mm und dieselbe Dicke wie die Verbundplatte aufweisen, die Elemente (1) parallel zueinander in einem Abstand von 5 mm bis 100 mm in einer Ebene angeordnet sind und auf der oberen und/oder der unteren Oberfläche der Verbundplatte mit dem Material (2) flächenbündig vorliegen.Composite panel according to any one of the preceding claims, comprising elements ( 1 ) of plywood or solid wood and a solidified plastic material filled into the interstices ( 2 ), characterized in that the composite plate has a thickness of 3 to 15 mm, the contact surfaces of the wood-containing elements ( 1 ) and the material ( 2 ) are parallel to one another, the wood-containing elements ( 1 ) extend in length over the entire composite panel, have a width of 5 mm to 100 mm and the same thickness as the composite panel, the elements ( 1 ) are arranged parallel to one another at a distance of 5 mm to 100 mm in a plane and on the upper and / or the lower surface of the composite plate with the material ( 2 ) are flush.
DE202009013059U 2009-01-30 2009-09-28 Wood strips composite element Expired - Lifetime DE202009013059U1 (en)