DE202004014293U1 - Dyed fiber plate on the basis of fibers containing ligno-cellulose includes dye pigments and a bonding agent containing an isocyanate resin - Google Patents
Dyed fiber plate on the basis of fibers containing ligno-cellulose includes dye pigments and a bonding agent containing an isocyanate resin Download PDFInfo
- Publication number
- DE202004014293U1 DE202004014293U1 DE200420014293 DE202004014293U DE202004014293U1 DE 202004014293 U1 DE202004014293 U1 DE 202004014293U1 DE 200420014293 DE200420014293 DE 200420014293 DE 202004014293 U DE202004014293 U DE 202004014293U DE 202004014293 U1 DE202004014293 U1 DE 202004014293U1
- Authority
- DE
- Germany
- Prior art keywords
- fiberboard
- color
- basis
- bonding agent
- binder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
Description
Die Erfindung betriefft eine durchgefärbte Faserplatte mit den Merkmalen des Schutzanspruchs 1.The Invention relates to a solid-colored fiberboard with the features of protection claim 1.
STAND DER TECHNIKSTATE OF TECHNOLOGY
Bei einer durchgefärbten Faserplatte ist ein Farbpigmentanteil so über das gesamte Volumen der Faserplatte verteilt, dass diese nicht nur an ihren Hauptflächen sondern auch an ihren durch Besäumen oder Ablängen entstandenen Schmalseiten oder an anderen durch Bearbeitung entstandenen Oberflächen eingefärbt ist. Dies ermöglicht ein Bearbeiten der Faserplatte, ohne dass hierdurch Oberflächenbereiche mit unterschiedlicher Farbe entstehen. Eine einheitliche Farbe der Oberfläche ist insbesondere dann wichtig, wenn die Faserplatte anschließend lackiert wird, weil die Farbwirkung der Lackierung, soweit diese nicht eine sehr hohe eigene Flächendichte an Farbpigmenten aufweist, von der Einfärbung der von ihr überzogenen Oberfläche abhängt. Die Durchfärbung einer Faserplatte ermöglicht es, sehr gute Farbwirkungen mit nur dünnen Lackierungen zu erreichen, wenn die Farbe der durchgefärbten Faserplatte an der zu lackierenden Oberfläche der gewünschten Farbe der lackierten Oberfläche bereits nahe kommt. Bei einer Farbe der Oberfläche, die schon der gewünschten Farbe der lackierten Oberfläche entspricht, kann auch ein Klarlack ohne eigenen Farbpigmentanteil eingesetzt werden. Von besonderem Interesse für Anwendungen z. B. im Möbel- oder Küchenbau sind lackierte Oberflächen in Farben mit großer Farbtiefe, wie beispielsweise schwarz.at a solid color Fiberboard is a color pigment component over the entire volume of the fiberboard distributed that this not only on their main surfaces but also on their by trimming or cutting to length resulting narrow sides or on other surfaces created by processing is colored. this makes possible machining the fiberboard without causing surface areas with different colors. A uniform color of the surface is particularly important if the fiberboard is then painted is because the color effect of the paint, insofar as this is not a very high own area density of color pigments, from the coloring of the coating they cover surface depends. The colouration a fiberboard enables achieve very good color effects with only thin paints, if the color of the solid color Fiberboard on the surface to be painted the desired color of the painted surface already comes close. With a color of the surface that is already the desired Color of the painted surface corresponds to a clear coat without its own pigment component be used. Of particular interest for applications such. B. in furniture or Kitchen cabinets are painted surfaces in colors with great Color depth, such as black.
Durchgefärbte mitteldichte Faserplatten mit den Merkmalen des Oberbegriffs des Schutzanspruchs 1 sind bekannt. Es handelt sich um Faserplatten, deren Bindemittelanteil aus einem Harnstoff-Formaldehyd-Harz und deren Farbpigmentanteil aus Farbpartikeln besteht. Durch einen Farbpigmentanteil von ca. 3 Gewichtsprozent, der grundsätzlich ausreichend sein sollte, um die Faserplatten farbig durchzufärben wird bei dünneren Faserplatten ein Gelbstich beobachtet, der bei dickeren Faserplatten in einen Braun-/Graustich umschlägt. Dieser Farbumschlag mag auf die Temperaturen bzw. die Presszeiten zurückzuführen sein, die auf die Oberflächen von Faserplatten bei deren Herstellung einwirken und zu einer teilweisen thermischen Zersetzung des Bindemittels führen.Solid medium density Fiberboard with the features of the preamble of the protection claim 1 are known. It is fiberboard, the proportion of binder from a urea-formaldehyde resin and its color pigment content consists of color particles. With a color pigment content of approx. 3 percent by weight, basically should be sufficient to color the fiberboard for thinner ones Fiberboard a yellow tinge is observed in thicker fiberboard turns into a brown / gray cast. This change in color may affect the temperatures or press times to be attributed the on the surfaces of fiberboard in their manufacture and to some extent cause thermal decomposition of the binder.
Grundsätzlich ist auch die Herstellung von Faserplatten, einschl. mitteldichter Faserplatten, unter Verwendung eines PMDI-Harzes für den Bindemittelanteil bekannt. Ein derartiges Isocyanat-Harz wird verwendet, um Formaldehydausdünstungen aus dem Bindemittelanteil der Faserplatten zu vermeiden und um Faserplatten mit erhöhter Feuchtigkeitsbeständigkeit herzustellen. Das Handhaben von PMDI-Harz als Bindemittel ist aber aufgrund dessen sehr großen Reaktivität aufwändiger als das von Harnstoff-Formaldehyd-Harz.Basically is also the production of fiberboard, including medium density fiberboard, known using a PMDI resin for the binder portion. Such an isocyanate resin is used to release formaldehyde to avoid from the binder portion of the fiberboard and around fiberboard with increased moisture resistance manufacture. However, handling PMDI resin as a binder is because of its very large Reactivity complex than that of urea-formaldehyde resin.
Die bekannte höhere Feuchtigkeitsbeständigkeit von isocyanatgebundenen Faserplatten gegenüber Harnstoffformaldehydharz gebundenen Faserplatten wird für typische Anwendungen von MDF-Platten im Möbel- und Küchenbau nicht benötigt, da mitteldichte Faserplatten regelmäßig nicht höheren Feuchtigkeitsbelastungen ausgesetzt sind, sondern typischerweise für Frontverkleidungen wie Möbeltüren und dergleichen eingesetzt werden.The known higher moisture resistance of isocyanate-bound fiberboard versus urea formaldehyde resin bound fiberboard is used for typical applications of MDF boards in furniture and kitchen construction are not required because medium-density fiberboard regularly not higher Are typically exposed to moisture for front panels like furniture doors and the like are used.
AUFGABE DER ERFINDUNGTASK OF INVENTION
Der Erfindung liegt die Aufgabe zugrunde, eine durchgefärbte Faserplatte mit verbesserter Farbwirkung des Farbpigmentanteils bereitzustellen.The The invention has for its object a solid-colored fiberboard to provide with improved color effect of the color pigment portion.
LÖSUNGSOLUTION
Die Aufgabe wird erfindungsgemäß durch eine durchgefärbte Faserplatte mit den Merkmalen des Schutzanspruchs 1 gelöst. Vorteilhafte Ausgestaltungen der neuen durchgefärbten Faserplatte sind in den Schutzansprüchen 2 bis 7 beschrieben.The The object is achieved by a by colored Fiberboard with the features of claim 1 solved. advantageous Refinements of the new solid-colored fibreboard are in the protection claims 2 to 7 described.
BESCHREIBUNG DER ERFINDUNGDESCRIPTION THE INVENTION
Eine mit Isocyanat gebundene durchgefärbte Faserplatte weist völlig überraschend eine unerwartete große Farbtiefe auf. Der Farbpigmentanteil entwickelt die an sich erwartete Farbwirkung der Farbpigmente ohne die in der bisherigen Praxis durchgefärbter Faserplatten beobachtete Farbverschiebung nach gelb oder grau/braun.A Colored fiberboard bound with isocyanate points out completely surprising an unexpected big one Color depth on. The color pigment portion develops the expected Color effect of the color pigments without the fiberboard dyed through in previous practice observed color shift to yellow or gray / brown.
Dieser überraschende Effekt wird bei an sich üblichen Bindemittelzusammensetzungen, d. h. z.B. bei der Verwendung herkömmlicher PMDI-Harze für den Bindemittelanteil beobachtet.This surprising one The effect becomes usual Binder compositions, i.e. H. e.g. when using conventional PMDI resins for the Binder content observed.
Worauf die überraschend große Farbtiefe der neuen isocyantgebundenen durchgefärbten Faserplatten zurückzuführen ist, ist unklar. Von der reinen Bindemittelchemie her ist dieser Effekt nicht zu erklären, da Isocyanatharz bekanntermaßen deutlich reaktiver als Harnstoff-Formaldehyd-Harze ist und von daher auch stärker mit dem Farbpigmentanteil reagieren sollte. Möglicherweise beruht die größere Farbtiefe der neuen durchgefärbten Faserplatte darauf, dass der Bindemittelanteil einer isocyanatgebundenen Faserplatte relativ niedrig ist und damit die Umhüllung der Pigmente in geringerem Maße auftritt. Diese stärkere Umhüllung der Pigmente in Verbindung mit der geringere thermische Stabilität des Harnstoffformaldeyhdleimes mag die Ursache für die im Stand der Technik beobachteten ungewollten Farbverschiebungen sein.It is unclear what the surprisingly large depth of color of the new isocyanate-bonded through-dyed fiberboard is due to. This effect cannot be explained from the pure binder chemistry, since isocyanate resin is known to be significantly more reactive than urea-formaldehyde resins and should therefore also react more strongly with the color pigment component. The greater depth of color of the new solid-colored fiberboard may be due to the fact that the proportion of binder in an isocyanate-bonded fiberboard is relatively low and that the coating of the pigments occurs to a lesser extent. This stronger coating of the pigments in connection with the lower thermal stability of the urea formaldeyhdleimes may be the cause of the unwanted color shifts observed in the prior art.
Der Farbpigmentanteil der neuen Faserplatte kann bei sehr guter Farbtiefe kleiner 4 Gewichtsprozent sein. Bereits bei einem Farbpigmentanteil von etwa 2,5 Gewichtsprozent werden sehr gute Farbwirkungen mit großer Farbtiefe erreicht. Dies konnte sowohl bei der Verwendung von schwarzem als auch bei der Verwendung von andersfarbigen Farbpigment beobachtet werden.The Color pigment portion of the new fiberboard can with very good depth of color be less than 4 percent by weight. Even with a color pigment content of about 2.5 percent by weight will have very good color effects with great depth of color reached. This could happen when using black as well also observed when using different colored pigment become.
Die neue Faserplatte ist vorzugsweise eine mitteldichte Faserplatte zur Verwendung im Möbel- und Küchenbau.The new fiberboard is preferably a medium density fiberboard for use in furniture and Kitchen.
Aufgrund ihrer feuchtigkeitsbeständigen Isocyanatbindung, die für den Einsatz von MDF-Platten im Küchen- und Möbelbau an sich unnötig ist, ist die neue Faserplatte ohne Probleme direkt mit einem Wasserlack lackierbar. Das heißt, Quellungen an der Oberfläche der Faserplatte aufgrund des Wasseranteils aufgetragener Wasserlacke treten nicht in relevantem Umfang auf.by virtue of your moisture-resistant Isocyanate bond, which for the use of MDF boards in kitchen and furniture making in itself unnecessary is, the new fiberboard is without problems directly with a water-based paint paintable. This means, Swelling on the surface the fiberboard due to the water content of water-based paints applied do not occur to a relevant extent.
BEISPIELEEXAMPLES
Im Folgenden wird die Erfindung anhand von bevorzugten Ausführungsbeispielen und Vergleichsbeispielen weiter erläutert und beschrieben.in the The invention is based on preferred exemplary embodiments and comparative examples further explained and described.
Beispiel 1example 1
Bei der Herstellung einer isocyanatgebundenen mitteldichten Faserplatte unter Verwendung eines üblichen PMDI-Harzes für deren Bindemittelanteil wurden 2,5 Gewichtsprozent schwarzes Farbpigment zugegeben und homogen in der Fasermatte vor deren Verpressen verteilt. Hieraus resultierten unabhängig von der Dicke der Faserplatte unterhalb oder oberhalb 10 mm tiefschwarz durchgefärbte Faserplatten mit sehr guter Farbwirkung und großer Farbtiefe.at the production of an isocyanate-bound medium-density fiberboard using a usual PMDI resin for their binder content was 2.5 percent by weight of black color pigment added and distributed homogeneously in the fiber mat before pressing. This resulted independently of the thickness of the fiberboard below or above 10 mm deep black by colored Fiberboard with a very good color effect and great depth of color.
Beispiel 2Example 2
In Abweichung vom Beispiel 1 wurde statt eines schwarzen ein grünes Farbpigment zur Ausbildung eines 2,5 gewichtsprozentigen Farbpigmentanteils zugeschlagen. Das Resultat waren dunkelgrün durchgefärbte Faserplatten, die ebenfalls unabhängig von ihrer Dicke eine sehr gute Farbwirkung und sehr große Farbtiefe aufwiesen.In In deviation from Example 1, a green color pigment was used instead of a black one to form a 2.5 percent by weight color pigment slammed shut. The result was dark green colored fiberboard, which also independently a very good color effect and very great depth of color due to its thickness exhibited.
VergleichsbeispielComparative example
Bei der bekannten Herstellung von mitteldichten Faserplatten mit Harnstoff-Formaldehyd-Harzbindung führt ein Zuschlag von 2,5 Gewichtsprozent und auch mehr schwarzgefärbtem Farbpigment bei Dicken der Faserplatten unter 10 mm zu Faserplatten, die grau/schwarz durchgefärbt sind, während bei Faserplattendicken ab etwa 10 mm die Farbe an die Hauptflächen der Faserplatten nach gelbbraun/schwarz umschlägt.at introduces the known production of medium density fiberboard with urea-formaldehyde resin bond Surcharge of 2.5 percent by weight and also more black colored pigment at fiberboard thicknesses below 10 mm to fiberboard, the gray / black are colored through while with fiberboard thicknesses from about 10 mm the color on the main surfaces of the Fiberboard turns yellow-brown / black.
Claims (7)