DE19809590B4 - Refractory moldings - Google Patents

Refractory moldings Download PDF

Info

Publication number
DE19809590B4
DE19809590B4 DE1998109590 DE19809590A DE19809590B4 DE 19809590 B4 DE19809590 B4 DE 19809590B4 DE 1998109590 DE1998109590 DE 1998109590 DE 19809590 A DE19809590 A DE 19809590A DE 19809590 B4 DE19809590 B4 DE 19809590B4
Authority
DE
Germany
Prior art keywords
refractory
weight
molded body
vermiculite
remainder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
DE1998109590
Other languages
German (de)
Other versions
DE19809590A1 (en
Inventor
Gerhard Schneider
Alfred Normann
Harry Schneider
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Viessmann Werke GmbH and Co KG
Original Assignee
Viessmann Werke GmbH and Co KG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Viessmann Werke GmbH and Co KG filed Critical Viessmann Werke GmbH and Co KG
Priority to DE1998109590 priority Critical patent/DE19809590B4/en
Publication of DE19809590A1 publication Critical patent/DE19809590A1/en
Application granted granted Critical
Publication of DE19809590B4 publication Critical patent/DE19809590B4/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

Wasser- und säurefester Feuerfestformkörper, insbesondere für die isolierende Auskleidung der Verschlüsse und Brennkammerböden von im Niedertemperaturbereich mit Taupunktunterschreitung betriebenen Heizkesseln, gebildet aus 2–20 , vorzugsweise 5–10 Gew.% Metakaolin, aus 0,5–10, vorzugsweise 2–5 Gew.% Siliziumdioxid, aus 25–54 Gew.% Wasserglas auf Basis von Natrium oder Kalium und einem Rest von 30–70 Gew.% aus mindestens Perlit und/oder Vermiculit, wobei das aus der Ferrosilizium- oder Siliziummetallherstellung stammende Siliziumdioxid mit großer spezifischer Oberfläche und in Feinstverteilung in den Formkörper eingebracht ist.Water- and more acid resistant Refractory shaped bodies, especially for the insulating lining of the closures and combustion chamber bottoms from operated in the low temperature range with falling below the dew point Boilers made up of 2–20 , preferably 5-10% by weight Metakaolin, from 0.5-10, preferably 2-5 % By weight of silicon dioxide, from 25-54 % By weight water glass based on sodium or potassium and a remainder from 30-70% by weight from at least pearlite and / or vermiculite, which is made from the ferrosilicon or silicon-metal-derived silicon dioxide with a large specific surface and is introduced into the shaped body in a very fine distribution.

Figure 00000001
Figure 00000001

Description

Die Erfindung betrifft einen Feuerfestformkörper, insbesondere Feuerfestformkörper für die Auskleidung der Verschlüsse und Brennkammerböden von im Niedertemperaturbereich mit Taupunktunterschreitung betriebenen Heizkesseln.The The invention relates to a refractory molded article, in particular a refractory molded article for the lining the closures and combustion chamber floors of those operating in the low temperature range below the dew point Boilers.

Aus der EP 0612954 A1 ist eine wärmedämmende gepreßte Verbundplatte aus einer wärmedämmenden Grundplatte aus Perlit und mindestens einer mit dieser im Verbund hergestellten thermischen oder mechanischen Schutzschicht bekannt. Die Verbundplatte kommt zur Wärmedämmung in elektrischen Koch- oder Heizgeräten zum Einsatz. Durch die entsprechende Schutzschicht wird erreicht, daß die Verbundplatte den dabei jeweils gestellten Anforderungen in wärmetechnischer und mechanischer Hinsicht gerecht wird. Der Versatz für die mechanische bzw. thermische Schutzschicht besteht aus wärmedämmenden Materialien (Gemisch aus Perlit und Reisschalenasche bzw. Gemisch aus Perlit, Kieselgur und Reisschalenasche), einem Reaktionsgemisch aus fünf Komponenten (a) einem feinteiligen Oxidgemisch mit Gehalten von amorphem Siliziumdioxid und Aluminium – gewonnen als Filterstaub aus der Kor- und- oder Mullitherstellung, b) glasartiger amorpher Elektrofilterasche aus Hochtemperatur-Steinkohlekraftwerken, c) gemahlenem kalziniertem Bauxit, d) ungelöstem, amorphem Siliziumdioxid, insbesondere aus einer amorphen, dispers-pulverförmigen, entwässerten oder wasserhaltigen Kieselsäure oder aus Hochtemperaturprozessen, e) Metakaolin) und einem Binder aus hoch alkalihaltigem Wasserglas. Eine derartige Verbundplatte ist für den Einsatz in Heizkesseln ungeeignet, da, bedingt durch die dort auftretenden Temperaturen, Temperaturwechsel und – bei im Niedertemperaturbereich mit Taupunktunterschreitung betriebenen Heizkesseln – Kondensateinwirkungen, die Gefahr von Rißbildung und Zersetzung besteht.From the EP 0612954 A1 is a heat-insulating pressed composite plate made of a heat-insulating base plate made of pearlite and at least one thermal or mechanical protective layer produced in conjunction with this. The composite panel is used for thermal insulation in electrical cooking or heating devices. The corresponding protective layer ensures that the composite panel meets the thermal and mechanical requirements in each case. The offset for the mechanical or thermal protective layer consists of heat-insulating materials (mixture of perlite and rice husk ash or mixture of perlite, kieselguhr and rice husk ash), a reaction mixture of five components (a) a finely divided oxide mixture with contents of amorphous silicon dioxide and aluminum as filter dust from the production of cor- and mullite, b) glass-like amorphous electrostatic precipitator ash from high-temperature coal-fired power plants, c) ground calcined bauxite, d) undissolved, amorphous silicon dioxide, in particular from an amorphous, disperse-powdery, dehydrated or water-containing silica or from high-temperature processes , e) metakaolin) and a binder made from high-alkali water glass. Such a composite panel is unsuitable for use in boilers because, due to the temperatures that occur there, temperature changes and - in the case of boilers operated in the low temperature range below the dew point - condensate effects, there is a risk of cracking and decomposition.

In modernen Heizkesseln wurden bislang überwiegend Keramikfaserformteile für hochwärmedämmende Versatzteile, sprich Feuerfestformkörper eingesetzt. Solche Keramikfasern stellen nach heutigem Wissensstand ein Gesundheitsrisiko dar, und zwar wenn solche lungengängige Keramikfasern eingeatmet werden.In Modern boilers have so far mainly been made of ceramic fiber for highly heat-insulating offset parts, i.e. fireproof molded body used. According to current knowledge, such ceramic fibers pose a health risk represents, and if such breathable ceramic fibers inhaled become.

Als Alternative zu solchen Keramikfaserteilen boten sich Isolierteile aus anorganischen Materialien wie Perlit, Vermiculit, Reisschalenasche, Hohlkugelsilikate, Leichtbetone usw. an, die auf geeignete Weise und mit geeigneten Bindemittel zu solchen Feuerfestformkörpern ausgeformt werden. Beispielsweise aus der DE 196 27 961 A1 ist ein Feuerfestformkörper bekannt, der aus einem mit hochtemperaturbeständigem Bindemittel (Kaliwasserglas) verpreßten Korpus aus Partikeln auf mineralischer Basis (Vermiculit, keramische Hohlkügelchen) besteht.As an alternative to such ceramic fiber parts, insulating parts made of inorganic materials such as perlite, vermiculite, rice husk ash, hollow spheresilicate, lightweight concrete, etc. were suitable, which are shaped in a suitable manner and with suitable binders to form such refractory bodies. For example from the DE 196 27 961 A1 a refractory molded body is known which consists of a body made of particles on a mineral basis (vermiculite, ceramic hollow spheres) pressed with a high-temperature-resistant binder (potash water glass).

Da der Betrieb moderner Heizkessel in der Regel mit sogenannter gleitender Temperatur erfolgt, führt eine solche Betriebsweise oftmals während der Heizphase in den Kesseln zu Taupunktunterschreitungen, wobei es nicht nur zu Durchfeuchtungen, sondern auch zu Schwefelsäurebelastungen der im Feuerraumbereich eingesetzten Feuerfestformkörper kommt, und zwar bedingt durch Schwefelanteile im Brennstoff. Bei wasserglasgebundenen Feuerfestformkörpern ist dieses mit hohem Festigkeitsverlust verbunden, da das Wasserglas rehydratisiert und sich die eingesetzten Iso lationsteile, wie sich gezeigt hat, früher oder später langsam auflösen.There the operation of modern boilers usually with so-called sliding Temperature takes place, leads such an operation often during the heating phase in the Boilers to drop below the dew point, not only causing moisture, but also to sulfuric acid pollution the refractory molded body used in the combustion chamber area comes due to the sulfur content in the fuel. With water glass bound Refractory moldings this is associated with a high loss of strength, because the water glass rehydrated and the insulation parts used, like yourself has shown earlier or later dissolve slowly.

Wie vorerwähnt, wird für die Ausbildung von Feuerfestformkörpern zwar bereits wasserglasgebundenes Vermiculit (Aluminium-Eisen-Magnesiumsilikat) eingesetzt, das in der bisher verwendeten Versatzform bei kondensatfreiem Brennbetrieb auch einsetzbar ist, sich jedoch bei Niedertemperatur-Kesselbetrieb im Taupunktbereich aus den genannten Gründen auf Dauer als ungeeignet erwiesen hat.How mentioned above, is for the formation of refractory bodies is already water glass bound Vermiculite (aluminum-iron-magnesium silicate) used in the previously used batch form with condensate-free Burning operation can also be used, however, with low-temperature boiler operation permanently unsuitable in the dew point area for the reasons mentioned has proven.

Der Erfindung liegt demgemäß die Aufgabe zugrunde, eine Zusammensetzung für Feuerfestformkörper, insbesondere für Feuerfestformkörper für im Niedertemperaturbereich mit Taupunktunterschreitung betriebene Heizkessel, zu finden bzw. bekannte Feuerfestformkörper dieser Art dahingehend zu verbessern, daß diese vergleichbare Isolationswerte wie die als gesundheitsschädlich erkannten Keramikfaserformteile aufweisen, dauerhaft ihre Festigkeit behalten und eine sehr hohe Temperaturwechselbeständigkeit verbunden mit guten Isoliereigenschaften besitzen.The The invention is accordingly based on the object a composition for Refractory shaped bodies, especially for Refractory molded body for in the low temperature range heating boilers operated below the dew point, or known refractory molded body to improve this type in such a way that these comparable insulation values like that as harmful to health recognized ceramic fiber molded parts, permanently their strength retain and a very high resistance to temperature changes combined with good insulation properties.

Diese Aufgabe ist nach der Erfindung mit einem wasser- und säurefesten Feuerfestformkörper gelöst, der in seinem Versatz bzw. seiner Zusammensetzung gebildet ist aus 2–20, vorzugsweise 5–10 Gew.% Metakaolin, aus 0,5–10, vorzugsweise 2–5 Gew.% Siliziumdioxid, aus 25–54 Gew.% Wasserglas auf Basis von Natrium oder Kalium und der Rest von 30–70 Gew.% aus mindestens Perlit und/oder Vermiculit, wobei das aus der Ferrosilizium- oder Siliziummetallherstellung stammende Siliziumdioxid mit großer spezifischer Oberfläche und in Feinstverteilung in den Formkörper eingebracht ist.This The object is according to the invention with a water and acid resistant Fireproof molded body solved, the in its offset or its composition is formed from 2-20, preferably 5-10% by weight Metakaolin, from 0.5-10, preferably 2-5% by weight Silicon dioxide, from 25-54 % By weight water glass based on sodium or potassium and the rest from 30-70 % By weight of at least perlite and / or vermiculite, which from the Ferrosilicon or Silicon metal manufacturing derived silicon dioxide with great specific surface and is introduced into the molded body in a very fine distribution.

Vorteilhaft spezifische Zusammensetzungen und auch Ausbildungen solcher Feuerfestformkörper ergeben sich dabei nach den Unteransprüchen, und zwar jeweils anpassungsorientiert hinsichtlich Festigkeit und spezieller Konstruktionsvorgaben.Advantageous specific compositions and designs of such refractory molded bodies result according to the subclaims, specifically in terms of strength and special design specifications.

Das verwendete amorphe Siliziumdioxyd wird dabei, wie erwähnt, vorzugsweise aus der Ferrosilizium- oder Siliziummetallherstellung gewonnen, und sämtliche an dieser erfindungsgemäßen Zusammensetzung beteiligten Komponenten sind im Feuerfestformkörper homogen verteilt.The The amorphous silicon dioxide used is, as mentioned, preferred obtained from the production of ferrosilicon or silicon metal, and all on this composition according to the invention The components involved are distributed homogeneously in the refractory molded body.

Von den zur Verfügung stehenden Isoliermaterialien haben sich Vermiculit, Perlit aber bspw. auch Reisschalenasche schon in der Vergangenheit bereits als sehr brauchbar erwiesen, da diese Materialien gute Festigkeiten bei hohem Dämmvermögen und eine ausreichende Dauerstandsfestigkeit besitzen.Of the available standing insulation materials have vermiculite, but perlite For example, rice bowl ash has already been used in the past proven to be very useful as these materials have good strengths with high insulation and have sufficient fatigue strength.

Überraschenderweise hat sich bei Versuchen herausgestellt, daß Siliziumdioxid aus der Ferrosilizium- oder Siliziummetallherstellung, wie bspw. Fesil-Silizia mit einer spezifischen Oberfläche > 10 m2/g, in Verbindung mit bei 900–1000°C kalziniertem Kaolin(also Metakaolin) und Wasserglas durch Bildung einer anorganischen Polymer-Gerüststruktur zu wasser- und säurefesten Verbindungen führen, bei denen das Wasserglas keiner Dehydration im feuchtem Zustand mehr unterliegt. Auch ist eine ungewöhnliche Resistenz gegen Schwefelsäure zu beobachten, die in Heizkesseln durch Verbrennung fossiler Brennstoffe mit Schwefelanteilen in Verbindung mit Kondensatanfall durch Taupunktunterschreitungen entsteht.Surprisingly, it has been found in tests that silicon dioxide from ferrosilicon or silicon metal production, such as, for example, Fesil-Silicia with a specific surface area> 10 m 2 / g, in conjunction with kaolin (ie metakaolin) calcined at 900-1000 ° C. and water glass lead to water and acid-resistant compounds by forming an inorganic polymer scaffold structure, in which the water glass is no longer subject to dehydration when wet. An unusual resistance to sulfuric acid can also be observed, which arises in boilers due to the combustion of fossil fuels with sulfur components in connection with the accumulation of condensate due to falling below the dew point.

Mit der erfindungsgemäßen Zusammensetzung wird erreicht, daß ein Vermiculit-, Perlit- oder Versatz aus Mischungen mit geeignet einschlägig anderen Rohstoffen gemäß der Unteransprüche durch Kombination mit Metakaolin und dem aus der Dampfphase abgeschiedenen Siliziumdioxyd aus der Ferrosilizium- oder Siliziummetallherstellung, also mit hoher spezifischer Oberfläche so ergänzt wird, daß durch die Reaktion zwischen diesen hochreaktiven Pulveroberflächen mit dem verwendeten Wasserglas eine chemische Verbindung eintritt, die einerseits eine Wasserunlöslichkeit und Säurefestigkeit bewirkt, andererseits die Festigkeiten der Formteile je nach Anteil der Zuschlagstoffe noch erhöht und die wärmetechnischen Eigenschaften, wie hohe Temperaturwechselbeständigkeit und Isolationsvermögen erhalten werden.With the composition of the invention is achieved that a Vermiculite, perlite or mixture of mixtures with suitable other relevant Combined raw materials according to the subclaims with metakaolin and the silicon dioxide separated from the vapor phase from ferrosilicon or silicon metal production, i.e. with high specific surface so added will that through the reaction between these highly reactive powder surfaces a chemical compound occurs in the water glass used on the one hand, water insolubility and acid resistance causes, on the other hand, the strength of the molded parts depending on the proportion of the aggregates increased and the thermal ones Properties such as high resistance to temperature changes and insulation properties become.

Nur der Vollständigkeit halber sind einige Ausführungsbeispiele von Formkörper 1 zeichnerisch dargestellt, wobei jeweils im Schnitt und in Ansicht 1 einen Formkörper 1 als Heizkesselverschlußauskleidung zeigt; 2 ebenfalls einen Formkörper 1 als Verkleidung eines kreisförmigen Heizkesselverschlusses; 3 einen Formkörper 1 als Verschlußauskleidung in anderer Ausführungsform; 4 einen Formkörper 1 als Verkleidung eines Brennkammerbodens und 5 im Teilschnitt die Einbindung von Befestigungselementen in den Formkörpern. Mit BS ist dabei jeweils die Wärmebeaufschlagungsseite bezeichnet.Only for the sake of completeness are some embodiments of molded articles 1 shown in drawings, each in section and in view 1 a molded body 1 shows as boiler lock lining; 2 also a molded body 1 as a cladding of a circular boiler lock; 3 a molded body 1 as a closure lining in another embodiment; 4 a molded body 1 as cladding of a combustion chamber floor and 5 in partial section, the integration of fasteners in the moldings. BS is the heat application side.

Was die Befestigungselemente 2 betrifft, so können diese bei der Ausformung der Formkörper, im Formwerkzeug entsprechend angeordnet, direkt in die Formkörper 1 eingebunden werden. Es ist aber auch möglich, beim Ausformen für entsprechend bemessene Aufnahmeausnehmungen 3 zu sorgen, in die dann die entsprechend gestalteten Befestigungselemente eingesetzt und bspw. durch Kleben, Reib- oder Formschluß fixiert werden.As for the fasteners 2 relates, they can be arranged directly in the molds when the moldings are arranged in the mold accordingly 1 be involved. It is also possible, however, when shaping for appropriately dimensioned receiving recesses 3 to worry, in which the appropriately designed fasteners are then inserted and fixed, for example by gluing, friction or positive locking.

Nicht besonders dargestellt ist die preßtechnisch ohne weiteres machbare Möglichkeit, die Formkörper 1 mit unterschiedlich verdichteten, zwischen 300–700 kg/m3 liegenden Bereichen auszustatten, und zwar mit Rücksicht auf unterschiedliche thermische und/oder konstruktive Belastungen. Ebenfalls nicht besonders dargestellt ist die Möglichkeit, die beteiligten Materialkomponenten in Form einer Platte zu verpressen, um dann aus einer solchen Platte einen oder mehrere Formkörper 1 als "Gebrauchsformkörper" mit gewünschter Kontur auszuschneiden.The molding, which is easily feasible in terms of compression technology, is not particularly shown 1 to be equipped with differently compressed areas between 300–700 kg / m 3 , taking into account different thermal and / or structural loads. Also not particularly shown is the possibility of pressing the material components involved in the form of a plate, in order to then use one or more shaped bodies from such a plate 1 cut out as a "molded article" with the desired contour.

Nachfolgend sind noch Ausführungsbeispiele möglicher Anteile der Versatzkomponenten in den Formkörpern angeführt, deren Auswahl sich ebenfalls nach den jeweiligen Anforderungen richtet.following are still examples potential Proportions of the offset components in the moldings listed, their selection also according to the respective requirements.

Versatzbeispiel auf Vermiculitbasis:
40–70 Gew. % Vermiculit, vorzugsweise 45 %–65 %;
2–20 Gew. % Metakaolin, vorzugsweise 5–10 %;
0,5–10 Gew. % amorphes Siliziumdioxid aus der Ferrosilizium- oder Siliziummetallherstellung, vorzugsweise 3–4 %;
25–54 Gew. % Wasserglas (optimale Menge ergibt sich aus den Feststoffanteilen) auf Basis von Natrium oder Kalium.Vermiculite-based offset example:
40-70% by weight vermiculite, preferably 45% -65%;
2-20% by weight metakaolin, preferably 5-10%;
0.5-10% by weight of amorphous silicon dioxide from ferrosilicon or silicon metal production, preferably 3-4%;
25–54% by weight of water glass (optimal amount results from the solids content) based on sodium or potassium.

Versatzbeispiel auf Perlitbasis:
30–60 Gew. % Perlit, vorzugsweise 35 %–40 %;
2–20 Gew. % Metakaolin, vorzugsweise 5 %;
0,5–10 Gew. % amorphes Siliziumdioxid aus der Ferrosilizium- oder Siliziummetallherstellung, vorzugsweise 3–4 %;
25–54 Gew. % Wasserglas auf Basis von Natrium oder Kalium.Perlite-based offset example:
30-60% by weight pearlite, preferably 35% -40%;
2-20% by weight metakaolin, preferably 5%;
0.5-10% by weight of amorphous silicon dioxide from ferrosilicon or silicon metal production, preferably 3-4%;
25–54% by weight water glass based on sodium or potassium.

Versatzbeispiel auf Vermiculit und Perlitbasis:
20 Gew. % Perlit plus 25 Gew. % Vermiculit;
2–20 Gew. % Metakaolin, vorzugsweise 5 %;
0,5–10 Gew. % amorphes Siliziumdioxid aus der Ferrosilizium- oder Siliziummetallherstellung, vorzugsweise 3–4 %;
40 Gew. % Wasserglas auf Basis von Natrium oder Kalium.Vermiculite and pearlite-based offset example:
20% by weight pearlite plus 25% by weight vermiculite;
2-20% by weight metakaolin, preferably 5%;
0.5-10% by weight of amorphous silicon dioxide from ferrosilicon or silicon metal production, preferably 3-4%;
40% by weight water glass based on sodium or Potassium.

Versatzbeispiel auf Vermiculit-, Perlit- und Reisschalenaschebasis:
20 Gew. % Perlit, 15 Gew. % Vermiculit und 10 Gew. % Reisschalenasche;
2–20 Gew. % Metakaolin, vorzugsweise 8 %;
0,5–10 Gew. % amorphes Siliziumdioxid aus der Ferrosilizium- oder Siliziummetallherstellung, vorzugsweise 2–3 %;
45 Gew. % Wasserglas auf Basis von Natrium oder Kalium.Offset example based on vermiculite, pearlite and rice bowl ash:
20% by weight pearlite, 15% by weight vermiculite and 10% by weight rice husk ash;
2-20% by weight metakaolin, preferably 8%;
0.5-10% by weight of amorphous silicon dioxide from ferrosilicon or silicon metal production, preferably 2-3%;
45% by weight water glass based on sodium or potassium.

Versatzbeispiel auf Perlit- und Reisschalenaschebasis:
30 Gew. % Perlit und 15 Gew. % Reisschalenasche;
2–20 Gew. % Metakaolin, vorzugsweise 8 %;
0,5–10 Gew. % amorphes Siliziumdioxid aus der Ferrosilizium- oder Siliziummetallherstellung, vorzugsweise 2–3 %;
45 Gew. % Wasserglas auf Basis von Natrium oder Kalium.Example of offset based on pearlite and rice bowl ash:
30% by weight pearlite and 15% by weight rice ash;
2-20% by weight metakaolin, preferably 8%;
0.5-10% by weight of amorphous silicon dioxide from the production of ferrosilicon or silicon metal, preferably 2-3%;
45% by weight water glass based on sodium or potassium.

Versatzbeispiel auf Vermiculit-, Hohlkugelsilikat- und Reisschalenaschebasis:
20 Gew. % Hohlkugelsilikat, 15 Gew. % Vermiculit und 10 Gew. Reisschalenasche;
2–20 Gew. % Metakaolin, vorzugsweise 10 %;
0,5–10 Gew. % amorphes Siliziumdioxid aus der Ferrosilizium- oder Siliziummetallherstellung, vorzugsweise 2–5 %;
40 Gew. % Wasserglas auf Basis von Natrium oder Kalium.Example of offset based on vermiculite, hollow spheresilicate and rice husk ash:
20% by weight of hollow sphere silicate, 15% by weight of vermiculite and 10% by weight of rice husk ash;
2-20% by weight metakaolin, preferably 10%;
0.5-10% by weight of amorphous silicon dioxide from ferrosilicon or silicon metal production, preferably 2-5%;
40% by weight water glass based on sodium or potassium.

Versatzbeispiel auf Perlit-, Hohlkugelsilikat- und Reisschalenaschebasis:
20 Gew. % Hohlkugelsilikat, 20 Gew. % Perlit und 5 Gew. Reisschalenasche;
2–20 Gew. % Metakaolin, vorzugsweise 8 %;
0,5–10 Gew. % amorphes Siliziumdioxid aus der Ferrosilizium oder Siliziummetallherstellung, vorzugsweise 3–5 %;
43 Gew. % Wasserglas auf Basis von Natrium oder Kalium.Offset example based on pearlite, hollow spheresilicate and rice bowl ash:
20% by weight of hollow ball silicate, 20% by weight of pearlite and 5% by weight of rice husk ash;
2-20% by weight metakaolin, preferably 8%;
0.5-10% by weight of amorphous silicon dioxide from ferrosilicon or silicon metal production, preferably 3-5%;
43% by weight water glass based on sodium or potassium.

Versatzbeispiel auf Vermiculit-, Perlit- und Hohlkugelsilikatbasis:
20 Gew. % Hohlkugelsilikat, 15 Gew. % Perlit und 10 Gew. Vermiculit;
2–20 Gew. % Metakaolin, vorzugsweise 10 %;
0,5–10 Gew. % amorphes Siliziumdioxid aus der Ferrosilizium oder Siliziummetallherstellung, vorzugsweise 3–4 %;
42 Gew. % Wasserglas auf Basis von Natrium oder Kalium.Offset example based on vermiculite, pearlite and hollow spheresilicate:
20% by weight of hollow spheresilicate, 15% by weight of pearlite and 10% by weight of vermiculite;
2-20% by weight metakaolin, preferably 10%;
0.5-10% by weight of amorphous silicon dioxide from ferrosilicon or silicon metal production, preferably 3-4%;
42% by weight water glass based on sodium or potassium.

Versatzbeispiel auf Hohlkugelsilikat, Vermiculit-, Perlit- und Reisschalenaschebasis:
20 Gew. % Hohlkugelsilikat, 1 0 Gew. % Perlit und 1 0 Gew. Vermiculit und 5 Gew. % Reisschalenasche;
2–20 Gew. % Metakaolin, vorzugsweise 10 %;
0,5–10 Gew. % amorphes Siliziumdioxid aus der Ferrosilizium oder Siliziummetallherstellung, vorzugsweise 3–5 %;
40 Gew. % Wasserglas auf Basis von Natrium oder Kalium.Offset example based on hollow spherical silicate, vermiculite, pearlite and rice bowl ash:
20% by weight of hollow spherical silicate, 1% by weight of pearlite and 10% by weight of vermiculite and 5% by weight of rice husk ash;
2-20% by weight metakaolin, preferably 10%;
0.5-10% by weight of amorphous silicon dioxide from ferrosilicon or silicon metal production, preferably 3-5%;
40% by weight water glass based on sodium or potassium.

Claims (15)

Wasser- und säurefester Feuerfestformkörper, insbesondere für die isolierende Auskleidung der Verschlüsse und Brennkammerböden von im Niedertemperaturbereich mit Taupunktunterschreitung betriebenen Heizkesseln, gebildet aus 2–20 , vorzugsweise 5–10 Gew.% Metakaolin, aus 0,5–10, vorzugsweise 2–5 Gew.% Siliziumdioxid, aus 25–54 Gew.% Wasserglas auf Basis von Natrium oder Kalium und einem Rest von 30–70 Gew.% aus mindestens Perlit und/oder Vermiculit, wobei das aus der Ferrosilizium- oder Siliziummetallherstellung stammende Siliziumdioxid mit großer spezifischer Oberfläche und in Feinstverteilung in den Formkörper eingebracht ist.Water and acid resistant Refractory molded articles, in particular for the insulating lining of closures and combustion chamber bottoms from operated in the low temperature range with falling below the dew point Boilers made up of 2–20 , preferably 5-10 % By weight metakaolin, from 0.5-10, preferably 2-5 % By weight of silicon dioxide, from 25-54 % By weight water glass based on sodium or potassium and a remainder from 30-70 % By weight of at least perlite and / or vermiculite, which from the Silicon dioxide originating from ferrosilicon or silicon metal production with great specific surface and is introduced into the molded body in a very fine distribution. Feuerfestformkörper nach jedem der Ansprüche 10 bis 12, dadurch gekennzeichnet, daß der Formkörper (1) aus einer aus den beteiligten Materialkomponenten gepreßten Platte ausgeschnitten ist.Refractory shaped body according to any one of claims 10 to 12, characterized in that the shaped body ( 1 ) is cut out of a plate pressed from the material components involved. Feuerfestformkörper nach Anspruch 1, dadurch gekennzeichnet, daß der Rest aus 40–70 Gew.% Vermiculit besteht.Refractory moldings according to claim 1, characterized in that the rest of 40-70 wt.% Vermiculite exists. Feuerfestformkörper nach Anspruch 1, dadurch gekennzeichnet, daß der Rest aus 30–60 Gew.% Perlit besteht.Refractory moldings according to claim 1, characterized in that the rest of 30-60 wt.% Perlite exists. Feuerfestformkörper nach Anspruch 1, dadurch gekennzeichnet, daß der Rest von 30–70 Gew.% aus einem variablen Gemisch aus Vermiculit und Reisschalenasche besteht.Refractory moldings according to claim 1, characterized in that the remainder of 30-70 wt.% from a variable mixture of vermiculite and rice bowl ash consists. Feuerfestformkörper nach Anspruch 1, dadurch gekennzeichnet, daß der Rest von 30–70 Gew.% aus einem variablen Gemisch aus Vermiculit, Reisschalenasche und Perlit besteht.Refractory moldings according to claim 1, characterized in that the remainder of 30-70 wt.% from a variable mixture of vermiculite, rice bowl ash and Perlite exists. Feuerfestformkörper nach Anspruch 1, dadurch gekennzeichnet, daß der Rest von 30–70 Gew.% aus einem variablen Gemisch aus Perlit und Reisschalenasche besteht.Refractory moldings according to claim 1, characterized in that the remainder of 30-70 wt.% consists of a variable mixture of pearlite and rice bowl ash. Feuerfestformkörper nach Anspruch 1, dadurch gekennzeichnet, daß der Rest von 30–70 Gew.% aus einem variablen Gemisch aus Vermiculit, Hohlkugelsilikat und Reisschalenasche besteht.Refractory moldings according to claim 1, characterized in that the remainder of 30-70 wt.% from a variable mixture of vermiculite, hollow spherical silicate and Rice bowl ash exists. Feuerfestformkörper nach Anspruch 1, dadurch gekennzeichnet, daß der Rest von 30–70 Gew.% aus einem variablen Gemisch aus Perlit, Hohlkugelsilikat und Reisschalenasche besteht.Refractory moldings according to claim 1, characterized in that the remainder of 30-70 wt.% made of a variable mixture of pearlite, hollow spheresilicate and rice bowl ash consists. Feuerfestformkörper nach Anspruch 1, dadurch gekennzeichnet, daß der Rest von 30–70 Gew.% aus einem variablen Gemisch aus Perlit, Hohlkugelsilikat und Vermiculit gebildet ist.Refractory moldings according to claim 1, characterized in that the remainder of 30-70 wt.% from a variable mixture of pearlite, hollow spheresilicate and vermiculite is formed. Feuerfestformkörper nach jedem der Ansprüche 1 bis 9, dadurch gekennzeichnet, daß das Siliziumdioxid mit einer spezifischen Oberfläche > 10 m2/g im Formkörper (1) enthalten ist.Refractory molded body according to any one of claims 1 to 9, characterized in that the silicon dioxide with a specific surface area> 10 m 2 / g in the molded body ( 1 ) is included. Feuerfestformkörper nach jedem der Ansprüche 1 bis 10, dadurch gekennzeichnet, daß der Formkörper (1) eine Dichte zwischen 300–700 kg/m3 aufweist.Refractory shaped body according to any one of claims 1 to 10, characterized in that the shaped body ( 1 ) has a density between 300-700 kg / m 3 . Feuerfestformkörper nach jedem der Ansprüche 1 bis 11, dadurch gekennzeichnet, daß im Formkörper (1) belastungsabhängig unterschiedlich zwischen 300–700 kg/m3 verdichtete Bereiche angeordnet sind.Refractory molded body according to any one of claims 1 to 11, characterized in that in the molded body ( 1 ) Depending on the load, different areas between 300–700 kg / m 3 of compacted areas are arranged. Feuerfestformkörper nach jedem der Ansprüche 10 bis 12, dadurch gekennzeichnet, daß im Formkörper (1) Befestigungselemente (2) mit eingepreßt angeordnet sind.Refractory molded body according to any one of claims 10 to 12, characterized in that in the molded body ( 1 ) Fasteners ( 2 ) are arranged with pressed in. Feuerfestformkörper nach jedem der Ansprüche 10 bis 12, dadurch gekennzeichnet, daß im Formkörper (1) Aufnahmeausnehmungen (3) für den Einsatz von Befestigungselementen (2) eingeformt sind.Refractory molded body according to any one of claims 10 to 12, characterized in that in the molded body ( 1 ) Recesses ( 3 ) for the use of fasteners ( 2 ) are molded.
DE1998109590 1998-03-06 1998-03-06 Refractory moldings Expired - Fee Related DE19809590B4 (en)