DE1916893A1

DE1916893A1 - Uniform cheap and highly reproducible slouration of - sand limestone brick by addn of mineral pigments

Info

Publication number: DE1916893A1
Application number: DE19691916893
Authority: DE
Inventors: Bjoern Gising
Original assignee: YTONG AB
Current assignee: YTONG AB
Priority date: 1968-04-04
Filing date: 1969-04-02
Publication date: 1970-03-05
Also published as: AT288230B

Abstract

Uniform cheap and highly reproducible colouration of sand limestone brick by addn of mineral pigments. G6A. Diluted pigment batch with particle size above 0.1 min. (1 to 25 wt.% on dry brick batch) is added to the main batch, to reduce sensitivity of brick colour to pigment wt. variation. Pref. pigment is slate-fires, which is cheap, easily milled and imparts a dense black colour. (Others are felspar, glass foil and slag). More vivid surface effect is produced using a i size fractions of pigments i.e. (1) fine and (2) coarse (above 1 mm yields a flasked highlighted surface).

Description

Verfahren zur Herstellung von Kalksandstein. Process for the production of sand-lime brick.

Die Erfindung bezieht sich auf ein Verfahren zur Herstellung von Kalksandstein mit einer Farbgebung, die von der normalen vom Grundmaterial des Kalksandsteines herrührenden Farbgebung abweicht.The invention relates to a method for producing sand-lime brick with a coloring that differs from the normal of the base material of the sand-lime brick originating coloring deviates.

Die Herstellung von Halksandstein erfolgt im allgemeinen in der Weise, daß ein kalkhaltiges Bindemittel3 vorzugsweise Kalk oder Kombinationen aus Kalk und Zement, in trockenem Zustand mit einem Zuschlagstoff in Form von kieseldioxydhaltigem Material, wie Sand, gemischt wird, worauf die so gebildete Mischung mit Wasser versetzt wird. Hierbei erhält man eine formbare Rohmasse, die zu Bausteinen gewünschter Formate in Hochdruckpressmaschinen bearbeitet wird. Nach der Formung werden die bis zu einem gewissen Grad abge bundenen Bausteine im Härtekessel mit Wasserdampf unter erhöhtem Druck und- erhöhter Temperatur gehärtet.The production of limestone sandstone is generally carried out in such a way, that a calcareous binder3 preferably lime or combinations of lime and cement, when dry, with an aggregate in the form of silica Material, such as sand, is mixed, whereupon the mixture thus formed is mixed with water. Here you get a malleable raw material that becomes building blocks desired formats is processed in high pressure press machines. After molding the building blocks, which are bound to a certain extent, are included in the hardening kettle Water vapor cured under increased pressure and temperature.

Hierbei reagieren die Grundmaterialien, Zuschlagstoffe und Bindemittel miteinander unter Bildung eines Ealziunhydrosilikatproduktes mit guten Festigkeitseigenschaften.The basic materials, aggregates and binders react here with each other to form an alkaline hydrosilicate product with good strength properties.

Kalksandstein, der auf die oben beschriebene Weise hergestellt wird, weist eine weiße bis graue Färbung auf, Je nachdem, welche Rohstoffe verwendet werden und je nachdem, welche Mengen Rohstoffe im Grundmaterial enthalten sind. In der letzten Zeit ist aus architektonischen Grundes ein Bedarf an Kalksandstein mit verschiedenen Farben entstanden. Um diesen Bedarf zu befriedigen, ist es bereits bekannt, den Kalksandstein durch Zugaben von Pigmenten zur Rohmasse einzufärben. Die Pigmente bestanden hierbei z.B. aus Eisenvitriol, Kupfervitriol. Eisenoxyd, Natriumsulfat und dgl. Der auf diese Weise pigmentierte Kalksandstein wird durch und durch homogen gefärbt, was darauf beruht, daß die Pigmente in äußerst feinverteilter Form vorliegen, so daß sie im Anmachwasser vollständig suspendiert werden.Sand-lime brick manufactured in the manner described above, has a white to gray color, depending on the raw materials used and depending on the amount of raw materials contained in the base material. In the For architectural reasons there has recently been a need for sand-lime bricks with various Colors emerged. In order to meet this need, it is already known to use the To color sand-lime brick by adding pigments to the raw material. The pigments consisted of e.g. iron vitriol, copper vitriol. Iron oxide, sodium sulfate and the like. The sand-lime brick pigmented in this way becomes homogeneous through and through colored what is based on that the pigments are extremely finely divided Form so that they are completely suspended in the mixing water.

Es hat jetzt sich jedoch herausgestellt, daß dieses Verfahren, Kalksandstein zu pigmentieren, mit gewissen Schwierigkeiten verbunden ist. Demnach ist es oft nicht immer mögliche ein und dieselben Farbton bei Serienproduktion von Millionen oder Zehnmillionen Steinen einzuhalten. Jede kleinere oder größere Veränderung in der Zusammensetzung des Grundmateriales, bzw. der Pigments und der Menge wirkt sich nämlich nachteilig auf die endgtiltige Farbgebung der Steine aus. Ferner hat es sich gezeigt, daß pigmentierte Kalksandsteine Oberflächen mit schwach unterschiedlichen Farbtönen auf ein und demselben Stein aufweisen, je nachdem, ob die Oberflächen vor dem Dampfhärten der Atmosphäre ausgesetzt waren oder nicht. Ein anderer, nicht unwesentlicher Nachteil des bekannten Verfahrens besteht in der Tatsache, daß Pigmente der oben aufgeftihrten Art verhältnismäßig teuer sind.However, it has now been found that this method, sand-lime brick pigmenting is associated with certain difficulties. So it is often not always possible one and the same color shade in series production of millions or ten million stones to adhere to. Any minor or major change in the composition of the base material or the pigment and the amount has an effect namely detrimental to the final coloring of the stones. Furthermore, it has It has been shown that pigmented sand-lime bricks have slightly different surfaces Shades of color on the same stone, depending on whether the surfaces whether or not exposed to the atmosphere prior to steam curing. Another, don't An insignificant disadvantage of the known process consists in the fact that pigments of the kind listed above are relatively expensive.

Die vorliegende Erfindung betrifft daher ein Verfahren zur Herstellung von Kalksandstein mit einer Farbgebung, die von der normalerweise vom Grundmaterial des Kalksandsteines herrührenden Farbgebund abweicht, bei dem die Schwierigkeiten der herkömmlichen Pigmentierung von Kalksandstein-vermieden werden und das außerdem zum mindesten einen vorher nicht bekannten Farbeffekt mit sich bringt.The present invention therefore relates to a method of manufacture of sand-lime brick with a coloring different from that normally of the base material of Sand-lime brick originating color bond differs, in which the Difficulties of conventional pigmentation of sand-lime brick-avoided and that with at least a previously unknown color effect brings.

Das Verfahren zur Herstellung von Kalksandstein mit einer Farbgebung die von der normalen vom Grundmaterial des Kalkeandeteines herrührenden Farbgebung abweicht, zeichnet sich gemäß der Erfindung dadurch aus, daß das Grundmaterial mit Farbkörpern einer Farbe, die sich von der Farbe des Grundmateriales wesentli¢h unterscheidet, zusammengesetzt wird, deren Korngröße 0,01 mm überschreitet.The process of making sand-lime brick with a coloring the color scheme, which comes from the normal coloring of the base material of the lime stone differs, is characterized according to the invention in that the base material with Color bodies of a color that differs significantly from the color of the base material, is composed, the grain size of which exceeds 0.01 mm.

Nach einer besonderen Ausführungsform der Erfindung können die Farbkörper aus zerkleinerten und/oder feingemahlenen Körnern aus minderalischen Stoffen bestehen.According to a particular embodiment of the invention, the color bodies consist of crushed and / or finely ground grains from minor substances.

Das erfindungsgemäße Verfahren bedeutet, daß der Kalksandstein eine "mechanische" Farbgebung erhält, d.h. das Grundmaterial des Kalksandsteines wird mit einem weiteren Füllmaterial, das dem Charakter von Zuschlagstoffen entspricht, ergänzt, welches je nach Menge und Korngrßenzusammensetzung dem fertigen Kalksandstein eine Farbe oder ein Farbbild erteilt, das sich von den, vom Grundmaterial herrührenden Farbtnen unterscheidet. Hierbei ist der Farbton weit weniger empfindlich gegenüber Variationen der Mengen des Grundmaterials und der Farbkdrper, als dieses beim Färben von Kalksandstein mit dem herkömmlichen, äußerst stark wirkenden Pigment der Fall ist.The inventive method means that the sand-lime brick a "mechanical" coloring is given, i.e. the basic material of the sand-lime brick becomes with another filler material that corresponds to the character of aggregates, supplements which one depends on Amount and grain size composition dem finished sand-lime brick is given a color or color image that differs from, from Color tones originating from the base material differs. Here the hue is wide less sensitive to variations in the amounts of the base material and the Color body, as this when coloring sand-lime brick with the conventional, extremely strong pigment is the case.

Gemäß einer weiteren AusfUhrungsform der Erfindung liegt das mineralische Zusatzmaterial gleichzeitig in zerkleinertem und feingemahlenem Zustand vor.According to a further embodiment of the invention, the mineral lies Additional material in a crushed and finely ground state at the same time.

Bei derartigen Zugaben von mineralischem Material mit differenzierter Korngrößenzusammensetzung erhält nämlich die Oberfläche des Kalksandsteines, speziell in gebrochenem Zustand eine Oberfläche mit lebendigem und damit ästhetisch ansprechendem Aussehen. Versuche haben ergeben, daß es, um die gewünschte Wirkung zu erzielen, wichtig ist, daß das mineralische Material nicht feiner als bis auf eine Korngröße von 0,01 mm gemahlen wird. Diese Versuche haben auch ergeben, daß die Gesamtmenge von mineralischem Zusatzmaterial am besten in den Grenzen 1 bis 25 Gew.-* bezogen auf das Trockensubstanzgewicht des Basis-Materials gehalten wird.With such additions of mineral material with differentiated The grain size composition specifically preserves the surface of the sand-lime brick When broken, a surface that is lively and therefore aesthetically pleasing Appearance. Tests have shown that in order to achieve the desired effect, It is important that the mineral material is not finer than a grain size of 0.01 mm is milled. These tests have also shown that the total amount based on mineral additive material, preferably within the limits of 1 to 25% by weight * is maintained at the dry matter weight of the base material.

Wenn der größte Teil des mineralischen Zusatzmateriales hierbei aus feingemahlenen Bestandteilen besteht, d.h. aus Körnern mit der Größe 0,01 bis 1,0 mm, wird die Farbe des Kalksandsteines radikal von grauweiß in die Farbe verändert, die das Zusatzmaterial aufweist. Wenn der größte Teil des Zusatzmateriales dagegen aus gröberen zerkleinerten Körnern besteht, d.h. aus Körnern mit der Größe größer als 9 mm, wird die natürliche grau-weiß Tönung des Kalksandsteines einerseits etwa wie die Grundfarbe getönt, und andererseits erhält sie einen starken Einschlag der Farbe des Zusatzmateriales in Form von Punkten oder Flecken in den Steinoberflächen. Durch Variation der Menge des zerkleinerten Materiales im Verhältnis zu der Menge des feingemahlenen Materiales, kann die Farbe des Kalksandsteines nach Wunsch abgestimmt werden.If most of the mineral additive material is out of here finely ground components, i.e. grains with a size of 0.01 to 1.0 mm, the color of the sand-lime brick is radically changed from gray-white to color, which has the additional material. If most of the additional material is against it consists of coarser chopped grains, i.e. grains of the larger size than 9 mm, the natural gray-white tint of the sand-lime brick is on the one hand about tinted like the base color, and on the other hand it receives a strong impact of the Color of the additional material in the form of points or spots in the stone surfaces. By varying the amount of shredded material in relation to the amount of the finely ground material, the color of the sand-lime brick can be matched as desired will.

Als mineralisches Zusatzmaterial kann gemäß der Erfindung vorteilhafterweise Feinschiefer verwendet werden. Der Beinsohiefer, der tiefschwarz ist, hat die Eigenschaft, daß er leicht auf eine geeignete Korngröße zerkleinert bzw. feingemahlen werden kann.According to the invention, the mineral additive material can advantageously Fine slate can be used. The lower leg, which is jet black, has the property that it can be easily crushed or finely ground to a suitable grain size can.

Außerdem ist der Feinschiefer vorteilhaft, einmal aufgrund seines niedrigen Preises und zum adern, weil er in großen Mengen zur Verfügung steht.In addition, the fine slate is advantageous, once because of its at a low price and because it is available in large quantities.

Andere Materialien die laut der Erfindung zur Anwendung kommen können, sind z.B. Diabas, Feldspat, Glasbruch, Schlacke, wie Hochofenschlacke und dgl.Other materials that can be used according to the invention, are e.g. diabase, feldspar, broken glass, slag such as blast furnace slag and the like.

Gemäß einer weiteren Ausführungsform der Erfindung kann das für den Zweck vorgesehene mineralische Material, das in zerkleinertem Zustand vorliegt, aus einer anderen Art bestehen, als das Material, das in feingemahlenem Zustand vorliegt. Hierdurch entsteht eine weitere Möglichkeit, die Farbgebung der Steine zu variieren.According to a further embodiment of the invention, this can be for the Purpose-intended mineral material that is in a crushed state, consist of a different species than the material that is finely ground is present. This creates another possibility, the coloring of the stones to vary.

Claims

1. Process for the production of sand-lime brick with a coloring, the normal coloration resulting from the base material of the sand-lime brick differs, characterized in that the base material with color bodies of one color, which differs significantly from the color of the base material, mixed together whose grain size exceeds 0.01 mm.

2. The method according to claim 1, characterized in that the color bodies made of crushed and / or finely ground components of mineral substances exist.

3. The method according to claim 2, characterized in @mineral The substance is present in a crushed and finely ground state at the same time.

1 @other than that in finely ground @metal.

5. The method according to any one of claims 2-3, characterized in that that the mineral is fine slate.