DE1719203A1 - Polysulfide caulking or coating materials - Google Patents
Polysulfide caulking or coating materialsInfo
- Publication number
- DE1719203A1 DE1719203A1 DE19671719203 DE1719203A DE1719203A1 DE 1719203 A1 DE1719203 A1 DE 1719203A1 DE 19671719203 DE19671719203 DE 19671719203 DE 1719203 A DE1719203 A DE 1719203A DE 1719203 A1 DE1719203 A1 DE 1719203A1
- Authority
- DE
- Germany
- Prior art keywords
- sealing compound
- compound according
- sulfone
- plasticizer
- aryl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
Anmelder: United Shoe Machinery Corporation, 140 Federal Street, Boston, Mass., USA 02107Applicant: United Shoe Machinery Corporation, 140 Federal Street, Boston, Mass., USA 02107
Polysulfid-Abdichtungs- oder BeschichtungsmaterialienPolysulfide caulking or coating materials
Die Erfindung betrifft Polysulfid-Abdichtungs- oder Beschichtungsmaterialien, insbesondere für das Bauwesen.The invention relates to polysulphide sealing or coating materials, especially for the construction industry.
Abdichtungsmaterialien, die auf verschiedene Weise, z.B. manuell, mit einer Kelle oder einer Spritzpistole, in Fugen zwischen Bauteilen von beispielsweise Bauten aufgetragen und entsprechend den benachbarten Oberflächenteilen der Bauteile verformt v/erden können, werden in großen Mengen im Bauwesen verwendet. Einige dieser Abdichtungsmaterialien unterliegen einer chemischen Veränderung, nachdem sie zum Ausfüllen einer Fuge verwendet worden sind, so daß sie zu einer gummiartigen wetterfesten Abdichtung führen. Ein derartiges Abdichtungsmaterial, das einer chemischen Veränderung unterliegt, wird in zwei Bestandteilen geliefert, die kurz vor der Anwendung gemischt werden, wobei der eine Bestandteil ein flüssiges PoIysulfid-Polymer und der andere Bestandteil ein Kärtungsmittel für das Polymer ist, sowie ein oder beide Bestandteile einen Weichmacher für das Polysulfid-Polymer haben.Waterproofing materials that are used in various ways, e.g. manually, with a trowel or a spray gun, applied in joints between components of buildings, for example, and according to the neighboring ones Parts of the surface of the components that can be deformed are used in large quantities in construction. Some of these sealing materials undergo chemical change after they have been used to fill a joint so that they result in a rubber-like weatherproof seal. Such a sealing material, that is subject to chemical change is delivered in two parts, which are just before use be mixed, one component being a liquid polysulfide polymer and the other ingredient is a hardening agent for is the polymer as well as one or both of the components have a plasticizer for the polysulfide polymer.
Obwohl derartige Abdichtungsmaterialien in zunehmendem Maße im Bauwesen verwendet werden, beeinflussen ihre chemischen Eigenschaften in vielen Fällen ihre physikalischen Eigenschaften nachteilig.Although such sealing materials are increasingly used in construction, their chemical properties affect in many cases their physical properties are disadvantageous.
009809/1453009809/1453
Häufig werden diese Abdichtungsmaterialien unter dem Einfluß van Sonneneinstrahlung weich, bröckeln ab oder v/erden anderweitig schlechter. Die Verachiechterung ist in vielen Fällen auf die "Weichmacher zurückzuführen, die in derartigen Abdichtungsinaterialien verwendet werden, um ihnen eine gewisse Plastizität zu verleihen. Often these sealing materials soften, crumble or otherwise ground under the influence of solar radiation worse. The contempt is in many cases on the "Plasticizers attributed to such sealing materials can be used to give them a certain plasticity.
Es ist daher Aufgabe der Erfindung, ein AbdichtungsmaterialIt is therefore the object of the invention to provide a sealing material
anzugeben, das eine hohe iestLLndigkeit gegen Zersetzung, Abbröckelnindicate that there is a high degree of resistance to decomposition and crumbling
Be
usv/. durch V?trahlung hat.Be
usv /. by radiation.
Die folgende Beschreibung betrifft Ausführungsbeispiele von aus zwei Bestandteilen bestehenden Abdichtungsmaterialien mit einem ersten Bestandteil, der ein flüssiges Polysulfid-Polymer und als Weichmacher ein Diary1-Sulfon vie Xylolnaphtoalin-Sulfon enthält, und mit einem zv/eiten Bestandteil, der Bleidioxyd enthält, das ein Härtungsmitxel f Ir das Polysulfid-Polymer ist.The following description relates to embodiments of FIG Two component sealing materials with a first component being a liquid polysulfide polymer and as a plasticizer a diaryl sulfone such as xylene naphthoaline sulfone contains, and with a second component, which contains lead dioxide, which is a curing agent for Ir the polysulfide polymer.
Ferner ist ein Verfahren zur Anwendung des Ausführungsbeispiels des Abdichtungsmaterials gemäß der Erfindung zum Ausfällen einer Fuge beschrieben.Further, a method of using the embodiment of the sealing material according to the invention is to fail described in a fugue.
Durch die Erfindung wird unter anderem ein Abdichtungsmaterial angegeben, das ein flüssiges Polysulfid und als Weichmacher ein Diary1-Sulfon enthält.The invention provides, inter alia, a sealing material which is a liquid polysulfide and as a plasticizer Contains diary1 sulfone.
Abdichtungsmaterialien gemäJ der Erfindung haben vorzugsweise weniger als 100 Gewichtsteile Diaryl-Sulfon auf 100 Gewichtsteilen flüssigen Polysulfid-Polymers.Sealing materials according to the invention preferably have less than 100 parts by weight of diaryl sulfone per 100 parts by weight of liquid polysulfide polymer.
Die Bestandteile der Abdichtungsmaterialien gemäß der Er.1Mrdung sind kaum oder garnicht der Gefahr einer Veränderung oder Verschlechterung ihrer Eigenschaften bei monatelanger Aufbewahrung ausgesetzt.The components of the waterproofing materials according to the Er. 1 Millions are hardly or not at all exposed to the risk of a change or deterioration in their properties after months of storage.
Diaryl-Sulfone können als Weichmacher in AbdichtungsmaterialienDiaryl sulfones can be used as plasticizers in waterproofing materials
mit oder ohne eine bestimmte Menge üblicher Weichmacher oder eines *,<:#, ,* 009809/U53with or without a certain amount of common plasticizers or one *, <: #,, * 009809 / U53
üblichen Lösungsmittels, z.B. Toluol, verwendet werden.common solvents such as toluene can be used.
Aridere Diaryl-Sulfone, die als Weichmacher in den Abdichtungsinaterialien gem;L13 der Erfindung verwendet werden können, sind Xylylcuraol-Sulfon, Xylylüthylbensol-Sulfon und Xylylcymol-Sulfon.Other diaryl sulfones used as plasticizers in waterproofing materials according to; L13 of the invention can be used Xylyl curaol sulfone, xylyl ethylbene sulfone and xylyl cymol sulfone.
Die Erfindung soll anhand der folgenden Beschreibung zweier Ausi'ührungsbeispiele I und II des Abdichtungsmaterials gemäß der Erfindung und eines Ausführungsbeispiels des Anwendungsverfuhrens n;;her erläutert werden. Es ist ersichtlich, daß die angegebene,i Zusammensetzungen und das angegebene Verfahren keine Beschränkung der Erfindung darstellen.The invention is based on the following description of two exemplary embodiments I and II of the sealing material according to the invention and an exemplary embodiment of the application method n ;; are explained here. It can be seen that the stated compositions and the stated method do not constitute a limitation of the invention.
Thiokol LP32 100,0Thiokol LP32 100.0
Calciumcarbonat 45,0Calcium carbonate 45.0
Titandioxyd 15,0Titanium dioxide 15.0
P-Kresoldialkohol 0,3P-cresol dialcohol 0.3
Xylolnaphthalin-Sulfon 37,0Xylene naphthalene sulfone 37.0
Arocjilor 1254 ('.Weichmacher (chlorierterArocjilor 1254 ('. Plasticizer (chlorinated
Kohlenwasserstoff)) 37,0Hydrocarbon)) 37.0
Stearinsäure 0,2Stearic acid 0.2
Bleidioxyd 7,5Lead dioxide 7.5
Bleistearat 0,3Lead stearate 0.3
ArocKlor 1254 (V/eichmacher (chlorierterArocKlor 1254 (V / calibrator (chlorinated
Kohlenwasserstoff)) 7,5Hydrocarbon) 7.5
Thiokol LP 32 ist ein flüssiges Polysulfid-Polymer mit einem Molekulargewicht von 4000 und wird dargestellt durch Kondensation mit einem Alkalipolysulfid von 99f5 Mol-# von bis (2-Chloräthyl)- · Formal und 0,5 Mol-$ Trichlorpropan.Thiokol LP 32 is a liquid polysulfide polymer with a molecular weight of 4000 and is produced by condensation with an alkali polysulfide of 99 f 5 mol- # of bis (2-chloroethyl) - · formal and 0.5 mol- $ trichloropropane.
Nach dem Mischen der Bestandteile A und B bleibt das MaterialAfter mixing ingredients A and B, the material remains
009809/U53009809 / U53
•AD• AD
für etwa 1,25 Stunden bei 25 C einsatzfähig. Nach Beendigung desCan be used for about 1.25 hours at 25 C. After the
eine
Aushärtens gibt das Material/gifte Adhäsion auf entfettetem Aluminium
und Glas, wobei die Adhäsion sieben Tage lang bei einer Temperatur von 25 C aufrechterhalten wird.one
When hardened, the material gives / toxic adhesion to degreased aluminum and glass, the adhesion being maintained for seven days at a temperature of 25 ° C.
Thiokol LP 32 - 100,0Thiokol LP 32-100.0
Calciumcarbonat 45»OCalcium carbonate 45 »O
Titandioxyd 15,0Titanium dioxide 15.0
Xylolnaphthalin-Sulfon 70,0Xylene naphthalene sulfone 70.0
Toluol 6,0Toluene 6.0
Wie im Beispiel I.As in example I.
Nachdem die Bestandteile A und B gemischt worden Bind, bleibt das Material etwa 1,75 Stunden lang bei 25 C einsatzfähig.After ingredients A and B have been mixed, the material will remain operational for approximately 1.75 hours at 25 ° C.
Nach Beendigung des Aushärtens ist die Adhäsion dee Material II auf entfettetem Aluminium oder Glas befriedigend, wobei die Adhäsion bei einer Temperatur von 25 0C sieben Tage lang aufrechterhalten wird.After curing is complete, the adhesion of Material II to degreased aluminum or glass is satisfactory, the adhesion being maintained at a temperature of 25 ° C. for seven days.
Bei der Durchführung des Verfahrens gemäß der Erfindung werden die beiden Bestandteile A und B einer der beiden Abdichtungsmaterialien gemäß der Erfindung miteinander gemischt, und das erhaltene Gemisch wird z.B. mit einer Kelle zum Ausfüllen einer Fuge verwendet.When carrying out the method according to the invention, the two components A and B of one of the two sealing materials according to the invention are mixed with one another, and the result is Mixture is e.g. used with a trowel to fill a joint used.
009809/ U53009809 / U53
Claims (1)