DE1694087C3 - - Google Patents
Info
- Publication number
- DE1694087C3 DE1694087C3 DE19661694087 DE1694087A DE1694087C3 DE 1694087 C3 DE1694087 C3 DE 1694087C3 DE 19661694087 DE19661694087 DE 19661694087 DE 1694087 A DE1694087 A DE 1694087A DE 1694087 C3 DE1694087 C3 DE 1694087C3
- Authority
- DE
- Germany
- Prior art keywords
- weight
- percent
- intermediate layer
- composite
- damping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Aus der deutschen Auslegeschrift 1200458 ist es bekannt, daß man hochwertige Temperaturbreitband-Entdröhnungsmittel zur Dämpfung der Biegeschwingungen von Blechkonstruktionen herstellen kann durch Abmischen von einer oder mehreren homo- und/oder copolymeren Komponenten, die mit geeigneten Weichmachern äußerlich weichgemacht sind, und einer oder mehreren homo- und/oder copolymeren Komponenten, die diese Weichmacher gar nicht oder nur wenig aufnehmen, wobei die einzelnen Komponenten sich in ihrer Einfriertemperatur um mindestens 10° C unterscheiden und ihre unterschiedlichen Einfriertemperaturen im wesentlichen beibehalten.From the German Auslegeschrift 1200458 it is known that high-quality temperature broadband anti-drumming agents are used to dampen the bending vibrations of sheet metal structures can be produced by mixing one or more homo- and / or copolymeric components that are externally plasticized with suitable plasticizers are, and one or more homo- and / or copolymeric components that even these plasticizers not or only little absorb, whereby the individual components change in their freezing temperature differ at least 10 ° C and their different freezing temperatures essentially maintained.
Ferner ist aus der britischen Patentschrift 968326 bekannt, daß solche Temperaturbreitband-Entdröhnungsmittel bestehen können aus einer Mischung von homo- und/oder copolymeren Komponenten, die in der Mischung mit geeigneten Weichmachern äußerlich weichgemacht sind, wobei sich im thermodynamischen Gleichgewicht die Weichmacher auf die in'einem geeigneten Mengenverhältnis gemischten Komponenten so verteilen, daß die Komponenten sich nach erfolgter Weichmacherwanderung in ihrer Einfriertemperatur um mindestens 10° C unterscheiden.It is also known from British patent specification 968326 that such broadband temperature deadening means can consist of a mixture of homo- and / or copolymeric components in the mixture are externally plasticized with suitable plasticizers, whereby in the thermodynamic Balance the plasticizers on the components mixed in a suitable proportion Distribute in such a way that the components are at their freezing point after the plasticizer has migrated differ by at least 10 ° C.
Ziel der vorliegenden Erfindung ist es, Entdröhnungsmittel mit einer erhöhten Temperaturbandbreite und einer verbesserten Temperaturstandfestigkeit zu erhalten.The aim of the present invention is to provide anti-drumming agents with an increased temperature range and improved thermal stability to obtain.
Diese Aufgabe wird gelöst durch ein Verbundsystern aus harten Platten, insbesondere Blechen, mit einer schwingungsdämpfenden, selbsthaftenden Zwischenschicht, das dadurch gekennzeichnet ist, daß die Zwischenschicht aus folgende, nach der Herstellung des Verbunds bei 150 bis 210° C thermisch nachbehandelten Stoffmischungen besteht:This object is achieved by a composite system made of hard plates, in particular sheet metal a vibration-damping, self-adhesive intermediate layer, which is characterized in that the Intermediate layer of the following, thermally aftertreated at 150 to 210 ° C after the production of the composite Mixtures of substances consists of:
a) 52 bis 70 Gewichtsprozent einer Komponente ausa) 52 to 70 percent by weight of a component
a) 1. 0 bis 50 Gewichtsprozent Copolymerisat I von Vinylacetat und Dibutylmaleinat mit einem Gewichtsverhältnis der Monomeren vona) 1. 0 to 50 percent by weight of copolymer I of vinyl acetate and dibutyl maleate with a Weight ratio of the monomers of
60 : 40 bis 80 : 20,60:40 to 80:20,
a) 2. 100 bis 50 Gewichtsprozent Copolymerisat Ila) 2. 100 to 50 percent by weight of copolymer II
von Vinylacetat und Crotonsäure mit einem Gewichtsverhältnis der Monomeren von 90 : 10 bis 96 : 4,of vinyl acetate and crotonic acid with a weight ratio of monomers of 90:10 to 96: 4,
b) 40 bis 22 Gewichtsprozent mindestens eines Weichmachers,b) 40 to 22 percent by weight of at least one plasticizer,
c) 8 bis 10 Gewichtsprozent eines bifunktionellen Epoxydweichharzes, insbesondere eines Di-c) 8 to 10 percent by weight of a bifunctional epoxy soft resin, in particular a di-
epoxyds eines aliphatischen Polyalkohols mit 6epoxyds of an aliphatic polyalcohol with 6
bis 10 Kohlenstoffatomen und einem xjehalt von 0,61 bis 0,72 Mol Epoxygruppen je 100 g Harz.up to 10 carbon atoms and a content of 0.61 to 0.72 moles of epoxy groups per 100 g of resin.
Die Zwischenschicht kann bezbgen auf die MengeThe intermediate layer can be related to the quantity
der Komponente a) bis zu 1 Gewichtsprozent Füllstoffe enthalten.of component a) up to 1 percent by weight of fillers contain.
Das Dickenverhältnis der äußeren Platten bzw. Bleche liegt zweckmäßig zwischen 1 : 1 und 1 : 4. Die thermische Nachbehandlung der Zwischenschicht bewirkt durch die Reaktion zwischen Epoxyd- und Carboxylgruppen eine Vernetzung. Dadurch wird die Temperaturstandfestigkeit der Zwischenschicht erheblich erhöht.The thickness ratio of the outer plates or sheets is expediently between 1: 1 and 1: 4. The thermal post-treatment of the intermediate layer is caused by the reaction between epoxy and carboxyl groups crosslink. This increases the temperature stability of the intermediate layer increased significantly.
Als Weichmacher kommen z. B. Ester der Phthalsäure in Frage, wie Uiamylphthalat, Dihexylphthalat,As a plasticizer z. B. Esters of phthalic acid in question, such as Uiamylphthalat, Dihexylphthalat,
Dioctyiphthalat, Dinonylphthalat, Didecylphthalat, Diisooctylphthalat, Diisononylphthaiat, Diisodecylphthalat, Dicyclohexylphthalat sowie gemischte Phthalsäureester, die verschiedene der aufgeführten Alkoholreste enthalten, ferner Trihexylphosphat, Diphenyl-kresyl-phosphat, Diphenyl-xylenyl-phosphat und Diphenyl-octyl-phosphat. Es ist im allgemeinen vorteilhaft, Weichmachergemische zu verwenden, vor allem Gemische, die aus Di-2-Äthylhexylphthalat und Trikresylphosphat bestehen, und insbesondere solche,Dioctyl phthalate, dinonyl phthalate, didecyl phthalate, diisooctyl phthalate, diisononyl phthalate, diisodecyl phthalate, Dicyclohexyl phthalate and mixed phthalic acid esters, the various of those listed Contains alcohol residues, also trihexyl phosphate, diphenyl cresyl phosphate, Diphenyl xylenyl phosphate and diphenyl octyl phosphate. It is in general advantageous to use plasticizer mixtures, especially mixtures composed of di-2-ethylhexyl phthalate and Tricresyl phosphate, and especially those
die die beiden zuletzt genannten Weichmacher in gleichen Anteilen enthalten.which contain the last two plasticizers mentioned in equal proportions.
Ein Vergleich der Fig. la und Ib veranschaulicht die überlegene Leistungsfähigkeit der neuen Systeme im Hinblick auf die schwingungsdämpfende Wirkung.A comparison of Fig. La and Ib illustrates the superior performance of the new systems with regard to the vibration-damping effect.
Fig. la zeigt den Verlustfaktor dcomb eines erfindungsgemäßen Verbundbleches in Abhängigkeit von der Temperatur. Zum Vergleich wurde eines der besten bekannten Entdröhnungsmittel für Verbundbleche, ein weichmacherhaltiges modifiziertes Vinylacetat-Copolymerisat (Fig. Ib) herangezogen. Bei dem Copolymerisat der Fig. 1 b handelt es sich um einen Schmelzkleber, der besonders gut für die Herstellung schwingungsgedämpfter Verbundbleche, bestehend aus zwei äußeren Blechen und einem selbsthaftenden Schmelzkleber als dämpfender Zwischenschicht, geeignet ist. Mit derartigen Systemen werden im Maximum extrem hohe Dämpfungen erreicht, die aus physikalischen Gründen nicht mehr übertroffen werdenFig. La shows the loss factor d comb of a composite sheet according to the invention as a function of the temperature. For comparison, one of the best known anti-drumming agents for composite sheets, a modified vinyl acetate copolymer containing plasticizer (FIG. Ib), was used. The copolymer of FIG. 1 b is a hot-melt adhesive which is particularly suitable for the production of vibration-damped composite sheets consisting of two outer sheets and a self-adhesive hot-melt adhesive as a damping intermediate layer. With such systems, extremely high attenuation can be achieved at maximum, which for physical reasons can no longer be exceeded
können. Siehe dazu H. Oberst und A. Schommer, Kunststoffe 55 (1965), 634, vor allem Abb. 9. Für eine symmetrische Anordnung, bestehend aus zwei 0,5 mm dicken Stahlblechen und einer Zwischenschicht von 0,3 mm Dicke, kommt der Verlustfaktor ^tom* <*es kombinierten Systems, gemessen im Biegeschwingungsverfahren(vgl.z. B.H.Oberst,L.Bohn BndF. Linhardt, Kunststoffe 51 (1961), 495), dem Wert dcomb = 1 schon nahe. Bei der seit langem bekannten Blechdämpfung durch einseitige dämpfende Beläge, die als rpritz-, spachtel- oder aufklebbare Schichten sogenannter Entdröhnungsmittel angewendet werden, sind die Verlustfaktoren des kombinierten Systems bei technisch vertretbaren Schichtdicken oder Verhältnissen der Belagmasse zur Blechmasse kn allgemeinen kleiner als dcomb = 0,2. Mit den neuerdings sich immer stärker durchsetzenden Verbundblechsystemen können, wie das hier angeführte Beispiel zeigt, bei optimaler Einstellung des Zv.ischenschichimateriaJs um ein Mehrfaches höhere Dämpfungswerte erreicht werden.be able. See H. Oberst and A. Schommer, Kunststoffe 55 (1965), 634, especially Fig. 9. For a symmetrical arrangement consisting of two 0.5 mm thick steel sheets and an intermediate layer 0.3 mm thick, the tom loss factor ^ * <* it combined system, measured in the bending vibration method, the value d = 1 comb (. BHOberst, L.Bohn B ndF. Linhardt, plastics, 51 (1961), 495 vgl.z) near already. In the case of sheet metal damping, known for a long time, using one-sided damping coverings, which are used as spray, trowel or adhesive layers of so-called anti-drumming agents, the loss factors of the combined system are generally less than d comb = 0 if the layer thicknesses or the ratios of the covering mass to the sheet mass kn are technically acceptable , 2. With composite sheet metal systems, which have recently become more and more popular, as the example given here shows, with optimal adjustment of the intermediate layer material, several times higher attenuation values can be achieved.
Die Temperaturbandbreite der Dämpfung des Verbundblechsystems hängt nicht nur von den viskoelastischen Kenngrößen der Zwischenschicht und der Stahlbleche, sondern auch stark von der »Geometrie« der Anordnung ab, d. h. von den Schichtdickenverhältnissen (vgl. Kunststoffe (1965), Abb. X bis 10). Bei Verbundblechsystemen ist es zweckmäßig, als Bandbreite die Breite des Temperaturintervalles zu definieren, in dem der Wert von dcomb = 0,05 überschritten wird. Die Dämpfung nicht durch zusätzliche Entdröhnungsmaßnahmen gedämpfter Bleche in Blechkonstruktionen verschiedener Art entspricht Werten dcomb = 0,01. Der Bezugswert dcamb = 0,05 bedeutet also eine beträchtliche Dämpfungserhöhung (um etwa 15 dB) gegenüber der »Nulldämpfung« dcomb = 0,01.The temperature range of the damping of the composite sheet system depends not only on the viscoelastic parameters of the intermediate layer and the steel sheets, but also heavily on the "geometry" of the arrangement, i.e. on the layer thickness ratios (see Kunststoffe (1965), Figs. X to 10). In the case of composite sheet metal systems, it is advisable to define the width of the temperature interval as the bandwidth in which the value of d comb = 0.05 is exceeded. The attenuation of sheet metal in sheet metal constructions of various types not dampened by additional anti-drumming measures corresponds to values d comb = 0.01. The reference value d camb = 0.05 means a considerable increase in attenuation (by around 15 dB) compared to the "zero attenuation" d comb = 0.01.
In Fig. Ib wird der Bezugswert dcomb = 0,05 im hauptsächlich interessierenden Frequenzbereich zwischen 100 und 1000 Hz bei den Temperaturen etwa zwischen 0° und 50° C überschritten, die Temperaturbandbreite beträgt also rund 50° C. Damit sind diese Verbundsysteme für zahlreiche technische Anwendungen geeignet. Durch Modifikation des Weichmachergehaltes kann das Temperaturband hoher dämpfender Wirkung nach höheren Temperaturen verschoben werden und damit speziellen technischen Anwendungen angepaßt werden, z. B. in Maschinenaggregaten mit erhöhter Betriebstemperatur. Dieses Beispiel von Verbundblechsystemen mit optimal eingestellter, selbsthaftender Zwischenschicht eines Temperaturbreitband-Dämpfungsstoffes, hergestellt durch Copolymerisation passend gewählter monomerer Komponenten, wird bisher von anderen Anordnungen ähnlicher Art nicht übertroffen und kann deshalb als Standardsystem angesehen werden, an dem die akustische Wirksamkeit des erfindungsgemäßen Systems durch Vergleich beurteilt werden kann.In Fig. Ib, the reference value d comb = 0.05 is exceeded in the frequency range between 100 and 1000 Hz, which is mainly of interest, at temperatures between 0 ° and 50 ° C, so the temperature range is around 50 ° C. This means that these composite systems are suitable for numerous suitable for technical applications. By modifying the plasticizer content, the temperature range with a high damping effect can be shifted to higher temperatures and thus adapted to special technical applications, e.g. B. in machine units with increased operating temperature. This example of composite sheet metal systems with an optimally adjusted, self-adhesive intermediate layer of a temperature broadband damping material, produced by copolymerization of suitably selected monomeric components, has not yet been surpassed by other arrangements of a similar type and can therefore be regarded as a standard system on which the acoustic effectiveness of the system according to the invention is compared can be judged.
In Fig. la und 1 b sind die Temperaturkurven des Verlustfaktors ccomb von Verbundblechsystemen aus 0,5 mm dicken Stahlblechen mit 0,3 mm dicken dämpfenden Zwischenschichten für 100 Hz und 1000 Hz wiedergegeben.In Fig. La and 1b, the temperature curves of the loss factor c comb of composite sheet systems made of 0.5 mm thick steel sheets with 0.3 mm thick damping intermediate layers for 100 Hz and 1000 Hz are shown.
Die Kurven wurden gemessen ?.n Verbundsystemen mitThe curves were measured in composite systems with
1 a) einer Mischung, bestehend 1. aus einem Gemisch aus 33 Gewichtsteilen eines Copolymerisates von Vinylacetat und Dibutylmaleinat im Gewichtsverhältnis 70/30 und 33 Gewichtsteile eines Copolymerisates von Vinylacetat und Crotonsäure im Gewichtsverhältnis 95/5, 2. aus 13 Gewichtsteilen Di-2-Äthylhexylphthalat und 13 Gewichtsteilen Trikresylphosphat als Weichma-1 a) a mixture consisting of 1. a mixture of 33 parts by weight of a copolymer of vinyl acetate and dibutyl maleate in a weight ratio of 70/30 and 33 parts by weight of a copolymer of vinyl acetate and crotonic acid in a weight ratio of 95/5, 2. from 13 Parts by weight of di-2-ethylhexyl phthalate and 13 Parts by weight of tricresyl phosphate as a soft
cbergemisch und 3. aus 8 Gewichtsteilen eines bifunktionellen Epoxydweichharzes, eines Diepoxyds eines aliphatischen Polyalkohols mit 6 bis 10 C-Atomen und einem Gehalt von 0,61 ίο bis 0,72 Molen Epoxydgruppe je 100 g Harz.Over mixture and 3. from 8 parts by weight of a bifunctional epoxy soft resin, a diepoxide of an aliphatic polyalcohol with 6 to 10 carbon atoms and a content of 0.61 ίο up to 0.72 moles of epoxy group per 100 g of resin.
Die für die Prüfung im Schwingungsversuch präparierten
Verbundblechsysteme wurden 15 Minuten bei 190° C thermisch nachbehandelt.
1 b) einem weichmacherhaltigen modifizierten Vi- »5 nylacetat-Copolymerisat als ZwischenschichtThe composite sheet metal systems prepared for testing in the vibration test were thermally aftertreated at 190 ° C. for 15 minutes.
1 b) a modified vinyl acetate copolymer containing plasticizer as an intermediate layer
(Vergleich).(Comparison).
Das erfindungsgemäße System 1 a) mit einer Stoffmischung als Zwischenschicht, deren Gewichtsverhältnisse im angegebenen optimalen Bereich liegen. ergibt glatte Dämpfungskurven und weist bei den technisch besonders interessierenden tiefen Frequenzen um 100 Hz eine überraschend große Temperaturbandbreite bei relativ hohen Dämpfungsmaxima (in der Umgebung von 20° C) auf, die als vergleichsweise »5 sehr hoch anzusehen sind, wenn sie auch die maximalen Dämpfungen der Fig. Ib nicht ganz erreichen. Die technisch sehr wichtige große Temperaturbandbreite von rund 100° C bei 100 Hz hängt physikalisch gesetzmäßig mit einer gewissen Abflachung der Maxima zusammen. Die Bandbreite ist bei tiefen Frequenzen von besonderer Bedeutung, weil es beim Aufbau der Resonanzschwingungen auf die Zahl der Biegewellenlängcn über die gegebenen Blechabmessungen ankommt; je mehr Wellenlängen auf die Abmessungen entfallen, desto stärker sind die Resonanzen bei gegebenem Verlustfaktor gedämpft. Bei tiefen Frequenzen sind aber die Wellenlängen am größten, und demgemäß ist ihre Zahl über Strukturen vergleichsweise klein. Fig. la zeigt, daß man noch bei etwa 100° C mit einer beträchtlichen Schwingungsdämpfung rechnen kann.The inventive system 1 a) with a mixture of substances as an intermediate layer, their weight ratios are in the specified optimal range. results in smooth damping curves and shows the Technically particularly interesting low frequencies around 100 Hz have a surprisingly large temperature range at relatively high attenuation maxima (in the vicinity of 20 ° C), which are considered to be comparatively »5 are very high, even if they are the maximum Do not quite reach the attenuations of Fig. Ib. the Technically very important large temperature range of around 100 ° C at 100 Hz depends on physical law with a certain flattening of the maxima. The bandwidth is at low frequencies of particular importance because it depends on the number of bending wavelengths in the build-up of the resonance vibrations over the given sheet metal dimensions arrives; the more wavelengths on the dimensions omitted, the more the resonances are damped for a given loss factor. At low frequencies but the wavelengths are greatest, and accordingly their number is comparative over structures small. Fig. La shows that one can still reckon with a considerable vibration damping at about 100 ° C can.
Ein weiterer akustischer Vorteil der erfindungsgemäß zu verwendenden Stoffmischung im Vergleich zu derjenigen der Fig. 1 b ist es, daß die dämpfende Wirkungsich weiter nach tieferen Temperaturen (bis unterhalb 0° C) erstreckt.Another acoustic advantage of the mixture of substances to be used according to the invention compared to that of Fig. 1b is that the damping effect continues after lower temperatures (to below 0 ° C).
Besonders hinzuweisen ist auf die technologischen Vorzüge des neuen Materials. Ein Hauptvorteil ist es, daß die Zwischenschicht nach der thermischen Nachbehandlung wegen der dann vorliegenden Vernetzung nicht mehr fließt, so daß technische Mangel bei hohen Temperaturen, z. B. infolge Austritts des verflüssigten Stoffes an den Rändern der Konstruktionen, nicht in Betracht gezogen zu werden brauchen. Ein weiterer Vorteil ist die haftverbessernde Wirkung der Epoxyd- und Carboxylgruppen sowie der aus diesen sich bildenden substituierten Ester. Bei der Verarbeitung bedeuten die haftverbessernden Gruppierungen gegebenenfalls eine Erleichterung insofern, daß die Entfettung der Bleche nicht mehr so kritisch ist.Special mention should be made of the technological advantages of the new material. One of the main advantages is that the intermediate layer after the thermal aftertreatment because of the crosslinking then present no longer flows, so that technical deficiencies at high temperatures, z. B. as a result of the leakage of the liquefied Fabric on the edges of the constructions need not be taken into account. Another The advantage is the adhesion-improving effect of the epoxy and carboxyl groups and those formed from them substituted ester. During processing, the adhesion-improving groups mean, if applicable a relief insofar as the degreasing of the sheets is no longer so critical.
Die notwendige thermische Nachbehandlung (zur Vernetzung) stellt für die Verarbeitung keine nennenswerte Erschwerung dar. Sie ergibt sich in vielen Anwendungsfällen von selbst, z. B. beim Einbrennen einer Lackierung. Bei der üblichen Herstellungsweise der Verbundsysteme und der üblichen Technik der Formgebung sind die Temperaturen noch tief genug, so daß die dabei erwünschte Fließfähigkeit noch nichtThe necessary thermal post-treatment (for crosslinking) is not significant for processing Difficulty. It arises in many applications by itself, z. B. when baking a paint job. With the usual production method of the composite systems and the usual technology of Shaping, the temperatures are still low enough that the desired flowability is not yet achieved
merklich durch die Vernetzung, die bei tieferen Temperaturen nur langsam fortschreitet, beeinträchtigt wird. Es handelt sich also bei der Verarbeitung bei der neuen Stoffmischung noch um ein thermoplastisches Material, einen »Schmelzkleber«, der bei genügend hohen Temperaturen aufgespachtelt, aufgestrichen oder aufgegossen werden kann.noticeable through the networking, which occurs at lower temperatures progresses slowly, is impaired. So it concerns with the processing the new mixture of substances still includes a thermoplastic material, a »hot melt adhesive«, which, if there is enough can be troweled, painted on or poured on at high temperatures.
Die Verarbeitbarkeit der Verbundblechc entspricht in weiten Grenzen der von normalen Blechen: d. h. die Verbundsysteme können abgekantet, gebogen, geformt, geschweißt und genietet werden. Bei nicht zu engen Krümmungsradien können sie auch tiefgezogen werden. Man erhält Verbundbleche mit einer Dämpfungshöhe und einem Temperaturbereich der Dämpfung, die für-zahlreiche Anwendungen sehr gut geeignet ist, insbesondere bei vergleichsweise hohen Betriebstemperaturen.The processability of composite sheets corresponds to that of normal sheets within wide limits: d. H. the composite systems can be folded, bent, shaped, welded and riveted. When not they can also be deep-drawn if the radii of curvature are too narrow. Composite sheets are obtained with a Attenuation level and a temperature range of the attenuation that are very good for numerous applications is suitable, especially at comparatively high operating temperatures.
Kleine Mengen Füllstoff, z. B. zur Vcrbessung der elektrischen Leitfähigkeit (Verbesserung der Widerstandsschweißung) können den Dämpfungsstoffen zugesetzt werden. Um die Dämpfungswirkung nicht zu verschlechtern, sollte die Füllstoffmenge aber untei 1 Gewichtsprozent, vorzugsweise unter 0,5 Gewichts prozent, bezogen auf das Polymerisat, gehalten wer den. Als Füllstoffe eignen sich beispielsweise Schwer spat. Kieselsäure, Graphit und Ruß.Small amounts of filler, e.g. B. to improve electrical conductivity (improve resistance welding) can be added to the damping materials. In order not to worsen the damping effect, the amount of filler should, however, be less 1 percent by weight, preferably below 0.5 percent by weight, based on the polymer, kept who the. Heavy late, for example, are suitable as fillers. Silica, graphite and carbon black.
Die Gesamtdicke des Verbundblechs liegt Vorzugs weise zwischen 1 und 6 mm. Die Zwischenschichter können 0,1 bis 1 mm. vorzugsweise 0,2 bis 0,5 mm betragen. Die maximale Dämpfung erhält man beThe total thickness of the composite sheet is preferred wise between 1 and 6 mm. The intermediate layers can be 0.1 to 1 mm. preferably 0.2 to 0.5 mm be. The maximum attenuation is obtained from be
ίο symmetrischen Verbundblechen. Die Biegesteifigkeii und Festigkeit ist aber bei gleichem Gewicht bei unsymmetrischen Verbundanordnungen größer. Be Anwendungen, bei denen, bezogen auf das Gewicht eine möglichst hohe Festigkeit erreicht werden soll wird man deshalb unsymmetrische Verbundbleche bevorzugen. Das Verhältnis der Blechdicken soll vorzugsweise zwischen 1 : 1 und 1 : 4 liegen.ίο symmetrical composite sheets. The bending stiffness and strength is greater for the same weight in asymmetrical composite arrangements. Be Applications in which, based on the weight, the highest possible strength should be achieved therefore asymmetrical composite sheets will be preferred. The ratio of the sheet thicknesses should preferably lie between 1: 1 and 1: 4.
Fig. 2 zeigt erfindungsgemäße Verbundsysteme ir symmetrischer (α) und unsymmetrischer (b) Anord-Fig. 2 shows composite systems according to the invention ir symmetrical (α) and asymmetrical (b) arrangement
ao nung. Zwischen den beiden äußeren Platten oder Blechen (1) liegt die Dämpfungsschicht (2).ao tion. The damping layer (2) lies between the two outer plates or sheets (1).
Hierzu 2 Blatt ZeichnungenFor this purpose 2 sheets of drawings
Claims (3)