DE1469112C - Process for increasing the absorption capacity of acrylonyl polymer fibers and threads for basic dyestuffs - Google Patents
Process for increasing the absorption capacity of acrylonyl polymer fibers and threads for basic dyestuffsInfo
- Publication number
- DE1469112C DE1469112C DE1469112C DE 1469112 C DE1469112 C DE 1469112C DE 1469112 C DE1469112 C DE 1469112C
- Authority
- DE
- Germany
- Prior art keywords
- dye
- bath
- sodium
- threads
- acrylonitrile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
1 21 2
Die Schwierigkeiten beim Färben von Tcxtilfasern, viskos. Der pH-Wert des Ausrüstungsbades ist für die aus Polymerisaten mit mindestens 75 % aus Acryl- das Verfahren gemäß der Erfindung nicht von Benitril hergestellt sind, stellten lange eine ernstliche deutung; jedoch wird zur Vermeidung einer ,BeBeeinträchtigung der vollen Ausnutzung der Ver- Schädigung der Fasern das Bad auf einem pH-Wert in Wendung dieser Fasern auf dem Textilgebiet dar. Diese 5 dem Bereich von 2 bis 7 gehalten. Die Temperatur des Fasern sind hydrophob und widerstehen so den üb- Ausrüstungsbades liegt zweckmäßig zwischen 15 und liehen Textilfärbearbeitsweisen. Es sind bisher zahl- 5O0C, der Temperaturbereich hat jedoch keine Wirreiche Arbeitsweisen zum Färben von Acrylnitril- kung auf das Verfahren gemäß der Erfindung. AII-polymerisatfasern entwickelt worden. Jedoch waren gemein dauert es nur 1 bis 2 Sekunden, um die Fasern diese Arbeitsweisen nicht erfolgreich, da der Farbstoff io durch das Ausrüstungsbad zu bewegen, es ist jedoch nicht vollständig und tief in die Fasern eindrang, was festgestellt worden, daß, wenn man die Fasern 1 oder zu ungleichmäßigen Färbungen und zur Bildung von 2 Minuten lang in dem Bad mit dem Reduktionsmittel Streifen und Flecken auf den Fasern führt. Außerdem beläßt, eine .Verbesserung im Weißheitsgrad der Faser sind die Lichtechtheit und die Waschbeständigkeit, auftritt, d. h. eine Verstärkung oder Vertiefung, die durch diese früheren Arbeitsweisen erzielt werden, 15 Wenn die Fasern nach dem Leiten durch das Ausschlecht, da die Farbstoffe sich auf der Außenfläche rüstungsbad getrocknet worden sind, ist die Farbstoffder Fasern befinden und so gegenüber jeder physika- aufnahme von basischen Farbstoffen beachtlich erlischen Einwirkung, welche die Oberfläche der Fasern höht. So werden durch das Verfahren gemäß der beschädigt, empfindlicher sind. Nach den früheren Erfindung Verfärbungen auf tragbare technische Arbeitsweisen konnte man auch keine Färbung in 20 Grenzen verringert oder vollständig beseitigt. Die kräftigeren Tönend wie Schwarz, Braun, Rotbraun Lichtbeständigkeit und die Waschbeständigkeit ist oder Dunkelblau, erhalten. verglichen mit den bisher gefärbten Acrylfasern aus-.The difficulties in dyeing textile fibers, viscous. The pH of the finishing bath has long been a serious concern for those made from polymers with at least 75% acrylic - the process according to the invention is not made from benitrile; however, in order to avoid impairment of the full utilization of the damage to the fibers, the bath is set to a pH value in the direction of these fibers in the textile field. These are kept in the range from 2 to 7. The temperature of the fibers are hydrophobic and so withstand the over-treatment bath is expediently between 15 and borrowed textile dyeing methods. There are numerous previously 5O 0 C, the temperature range, however, has not tangled oak working methods for dyeing acrylonitrile effect on the process according to the invention. All polymer fibers have been developed. However, in common it only takes 1 to 2 seconds for the fibers to be unsuccessful in this way of working as the dye io to move through the finishing bath, however, it did not penetrate completely and deeply into the fibers, which has been found that when the Fibers 1 or uneven dyeing and the formation of streaks and stains on the fibers for 2 minutes in the bath with the reducing agent. In addition, an improvement in the whiteness of the fiber, the lightfastness and the wash resistance, occurs, ie a reinforcement or deepening, which is achieved by these earlier methods If the outer surface of the armor bath has been dried, the dyestuff of the fibers is present and so considerably expires against any physical absorption of basic dyestuffs, which increases the surface of the fibers. So are damaged by the procedure according to which are more sensitive. According to the earlier invention, discoloration by portable technical methods could not be reduced or completely eliminated within 20 limits. The stronger tones like black, brown, red-brown lightfastness and the washfastness is or dark blue, are preserved. compared to the previously dyed acrylic fibers.
Der Erfindung liegt die Aufgabe zugrunde, die gezeichnet. Zusätzlich können, was von außerordent-The invention is based on the object drawn. In addition, what is extraordinarily
Aufnahmefähigkeit von Acrylnitrilpolymerisatfasern- licher Wichtigkeit ist, durch das Verfahren gemäß derAbsorption capacity of acrylonitrile polymer fibers is important because of the method according to
und -fäden für basische Farbstoffe zu erhöhen, so daß 25 Erfindung Acrylfasern nun in erfolgreicher Weise inand threads for basic dyes, so that acrylic fibers can now be used successfully in
nicht verfärbte, lichtecht und waschecht gefärbte kräftigeren oder schwereren Farbtönungen, die nichtnot discolored, lightfast and washfast dyed stronger or heavier shades that are not
Fasern und Fäden erhalten werden, die auch in auslaufen, keine Verfärbung zeigen, und ausgezeichneteFibers and filaments are obtained which also leak, show no discoloration, and are excellent
stärkeren oder kräftigeren Farbtönen gefärbt werden Waschbeständigkeit und Lichtbeständigkeit beibe-dyed stronger or stronger shades of color, washfastness and lightfastness
können. halten, gefärbt werden.be able. hold to be colored.
Das Verfahren gemäß der Erfindung zur Erhöhung 30 Das erfindungsgemäße Verfahren zur Erhöhung der Aufnahmefähigkeit von Acrylnitrilpolymerisat- der' Aufnahmefähigkeit von Acrylnitrilpolymerisatfasern und -fäden für basische Farbstoffe ist dadurch fasern und -fäden für basische Farbstoffe eignet sich gekennzeichnet, daß man im Zuge des üblichen Naß- besonders für Fasern oder Fäden aus Acrylnitril-, Spinnens die noch gequollenen Fäden in einem Aus- Homo- und -Mischpolymerisaten,-einschließlich birüstungsbad behandelt, das neben den üblichen Aus- 35 nären und ternären Polymerisaten, welche mindestens rüstungsmitteln mindestens 0,1%, bezogen auf das 80 Gewichtsprozent Acrylnitrileinheiten im polymeren Volumen des Ausrüstungsbades, eines Reduktions- Molekül enthalten, oder aus einer Mischung von mittels enthält, wobei man als Reduktionsmittel Acrylnitril-Homo oder -Mischpolymerisaten mit 2 bis Natriumhydrosulfit, Natriumsulfoxylatformaldehyd, 50% eines anderen polymeren Materials, wobei die Zinksulfoxylatformaldehyd, Zinkhydroxysulfoxylat- 40 Mischung einen Gesamtgehalt an polymerisiertem formaldehyd, modifizierte Hydrosulfite, Zinkhydro- Acrylnitril von mindestens 80 Gewichtsprozent aufsulfit, Mischungen von N.itrium- und Zinksulfoxylat- weist. Obwohl es sich bei den Polymerisaten, die bei formaldehyd, Thioharnstoffdioxyd, Natriumthiosulfat dem Verfahren gemäß der Erfindung verwendet oder Natrium-m-bisulfit verwendet. werden, vorzugsweise um solche handelt, welcheThe method according to the invention for increasing 30 The method according to the invention for increasing the absorption capacity of acrylonitrile polymer the 'absorption capacity of acrylonitrile polymer fibers and threads for basic dyes is therefore fibers and threads for basic dyes characterized that in the course of the usual wet especially for fibers or threads made of acrylonitrile, Spinning the still swollen threads in a homopolymers and copolymers, including armor bath treated, in addition to the usual external and ternary polymers, which at least Armor at least 0.1%, based on the 80 percent by weight of acrylonitrile units in the polymer Volume of the equipment bath, contain a reducing molecule, or a mixture of contains means, being used as reducing agent acrylonitrile homopolymers or copolymers with 2 to Sodium hydrosulfite, sodium sulfoxylate formaldehyde, 50% of another polymeric material, the Zinc sulfoxylate formaldehyde, zinc hydroxysulfoxylate 40 mixture has a total content of polymerized formaldehyde, modified hydrosulphites, zinc hydro-acrylonitrile of at least 80 percent by weight on sulphite, Mixtures of nitrium and zinc sulfoxylate. Although the polymers used in formaldehyde, thiourea dioxide, sodium thiosulphate are used in the process according to the invention or sodium m-bisulfite is used. are, preferably those which
Die noch gequollenen Fäden, d. h. nicht zusammen- 45 mindestens 80% Acrylnitril enthalten, die allgemeinThe threads that are still swollen, d. H. do not contain at least 80% acrylonitrile altogether, in general
gefallenen Fäden, können nach dem Verlassen des als die faserbildenden Acrylnitrilpolymerisate be-Fallen threads can after leaving the as the fiber-forming acrylonitrile polymer
N;ißspinnsystems durch ein übliches Ausrüstungsbad kannt sind, kann die Erfindung selbstverständlich inN; ßspinnsystems are known by a common finishing bath, the invention can of course in
geleitet werden, das allgemein ein Faserschmälzmittel, gleicher Weise auf Polymerisate angewandt werden,are passed, which is generally a fiber lubricant, applied in the same way to polymers,
z.B. eine Wachsemulsion, einen Faserweichmacher, die weniger als 80% Acrylnitril enthalten.e.g. a wax emulsion, a fiber softener containing less than 80% acrylonitrile.
z.B. Äthylenglykol, und ein antistatisch machendes 5< > Die Acrylnitrilpolymerisate, die weniger als 80%E.g. ethylene glycol, and an antistatic 5 < > The acrylonitrile polymers, which contain less than 80%
Mittel, z. B. eine quaternäre Ammoniumverbindung Acrylnitrileinheiten enthalten, sind auch zur BildungMedium, e.g. B. containing a quaternary ammonium compound acrylonitrile units are also used to form
enthält, wobei dem Bad erfindungsgemäß-ein Reduk- von Filmen, überzugszusammensetzungen, bei Form-contains, wherein the bath according to the invention-a reduction of films, coating compositions, in the case of form-
tionsmittel zugesetzt ist, das aus Natriumhydrosulfit, oder Preßarbeitsweisen und bei Lacken usw. brauchbar.tion agent is added, which is made of sodium hydrosulfite, or pressing methods and in paints, etc. usable.
Natriumsulfoxylat, Formaldehyd, Zinksulfoxylatform- Beispielsweise kann das faserbildende PolymerisatSodium sulfoxylate, formaldehyde, zinc sulfoxylate form- For example, the fiber-forming polymer
aldehyd, Zinkhydroxysulfoxylatformaldehyd, modifi- 55 ein Mischpolymerisat aus 80 bis 98% Acrylnitril undaldehyde, zinc hydroxysulfoxylate formaldehyde, modified 55 a copolymer of 80 to 98% acrylonitrile and
zierten Hydrosulfiten, Zinkhydrosulfit, einer Mischung 2 bis 20% eines anderen Monomeren sein, welches dieadorned hydrosulfites, zinc hydrosulfite, a mixture of 2 to 20% of another monomer, which is the
von Natrium- und Zinksulfoxylatformaldehyd, Thio- > C = C c-Bindung enthält und mit Acrylnitrilof sodium and zinc sulfoxylate formaldehyde, thio- > C = C contains c bond and with acrylonitrile
harnstoffdioxyd, N.itriumthiosulfat oder Natrium- mischpolymerisierbar ist. Geeignete monoolefinischeurea dioxide, nitrium thiosulphate or sodium is copolymerizable. Suitable monoolefinic
m-bisulfit bestehen kann. Unter den bei dem Ver- Monomere umfassen Acrylsäure, oc-Chloracrylsäurem-bisulfite can exist. Among the monomers in the Ver include acrylic acid, oc-chloroacrylic acid
fahren gemäß der Erfindung verwendeten Färbe- 6° und Methacrylsäure. Die Acrylate, wie Methyl-drive according to the invention used dye 6 ° and methacrylic acid. The acrylates, such as methyl
bedingungen, zersetzen sich die Farbstoffe nicht. Sie methacrylat, Äthylmethacrylat, Butylmethacrylat, Me-conditions, the dyes do not decompose. You methacrylate, ethyl methacrylate, butyl methacrylate, methacrylate
dringen entweder in die Faser ein, oder sie bleiben in thoxymethylmethacrylat, /7-Chloräthylmethacrylat undpenetrate either into the fiber, or they stay in thoxymethyl methacrylate, / 7-chloroethyl methacrylate and
Lösung. Die Menge an Reduktionsmittel, bezogen auf dis entsprechenden Ester der Acryl- und «-Chloracryl-Solution. The amount of reducing agent, based on the corresponding esters of acrylic and «-chloroacrylic-
das Volumen des Ausrüstungsbades, liegt zweckmäßig säuren, Vinylchlorid, Vinylfluorid, Vinylbromid, Viny-the volume of the equipment bath, is appropriately acids, vinyl chloride, vinyl fluoride, vinyl bromide, vinyl
zwischen 0,1 und 10%, wobei 3,0% bevorzugt sind. 65 Ijdenchlorid, l-Chlor-l-bromäthylen, Methacrylnitril,between 0.1 and 10%, with 3.0% being preferred. 65 Ijdenchlorid, l-chloro-l-bromoethylene, methacrylonitrile,
Es kann jedoch auch ein höherer Prozentsatz ver- Acrylamid und Methacrylamid, Λ-ChloracrylamidHowever, a higher percentage can also be used. Acrylamide and methacrylamide, Λ-chloroacrylamide
wendet werden, jedoch ist dies nicht wirtschaftlich, oder Monoalkylsubstitutionsprodukte davon, Methyl-are used, but this is not economical, or monoalkyl substitution products thereof, methyl
und auch das Ausrüstungsbad wird dadurch ziemlich vinylketon, Vinylcarboxylate, wie Vinylacetat, Vinyl-and also the finishing bath becomes quite vinyl ketone, vinyl carboxylates, such as vinyl acetate, vinyl
3 43 4
chloracetat, Vinylpropionat und Vinylstearat, N-Vi- Vor dem Eintauchen der Probe in das Färbebadchloroacetate, vinyl propionate and vinyl stearate, N-Vi- Before immersing the sample in the dye bath
nylimide, wie N-Vinylphthalimid und N-Vinylsuccin- und nach dem 2stündigen Kochen wurde die Konzen-nylimide, such as N-vinylphthalimide and N-vinylsuccin- and after boiling for 2 hours the concentration
imid, Methylenmalonsäureester, Itaconsäure und Ita- tration an Farbstoff in dem Färbebad unter Ver-imide, methylenemalonic acid ester, itaconic acid and itation of dye in the dyebath with
consäureester, N-Vinylcarbazol, Vinylfuran, Alkyl- Wendung eines Spektralphotometers bestimmt. Dieconic acid ester, N-vinylcarbazole, vinylfuran, alkyl turn of a spectrophotometer determined. the
vinylester, Vinylsulfonsäure, Äthylen, α,/9-Dicarbon- 5 Konzentration an Farbstoff betrug zu Beginnvinyl ester, vinyl sulfonic acid, ethylene, α, / 9-dicarbon- 5 concentration of dye was at the beginning
säuren oder deren Anhydride oder Derivate, wie Di- 26 Gewichtsprozent der Faserprobe. Nach Beendigungacids or their anhydrides or derivatives, such as di- 26% by weight of the fiber sample. After completion
äthylcitraconat, Diäthylmessaconat, Styrol, Vinyl- des Färbens wurde festgestellt, daß die KonzentrationEthyl citraconate, diethyl messaconate, styrene, vinyl dyeing was found to be the concentration
naphthalin, vinylsubstituierte, tertiäre, heterocyclische des Farbstoffs in dem Färbebad 18,8 %, bezogen aufnaphthalene, vinyl-substituted, tertiary, heterocyclic of the dye in the dyebath 18.8% based on
Amine, wie Vinylpyridine und alkylsubstituierte das Gewicht der Probe, betrug, was anzeigt, daß dieAmines such as vinyl pyridines and alkyl substituted was the weight of the sample, indicating that the
Vinylpyridine, beispielsweise 2-Vinylpyridin, 4-Vinyl- io Farbstoffaufnahme der Probe 7,2 °/0, bezogen auf dasVinylpyridines, for example 2-vinylpyridine, 4-vinyl io dye uptake of the sample 7.2 ° / 0 , based on the
pyridin, 2-Methyl-5-pyridine wie 2-Vinylpyridin, 4-Vi- Gewicht der Probe, betrug. Dies war eine Kontroll-pyridine, 2-methyl-5-pyridine such as 2-vinylpyridine, 4-Vi weight of the sample. This was a control
nylpyridin, 2-Methyl-5-vinylpyridin usw., 1-Vinyl- probe, bei welcher kein Reduktionsmittel im Aus-nylpyridine, 2-methyl-5-vinylpyridine, etc., 1-vinyl sample, in which no reducing agent is used
imidazol und alkylsubstituierte 1-Vinylimidazole, wie rüstungsbad vorlag. 'imidazole and alkyl-substituted 1-vinylimidazoles, as was the armor bath. '
2-, 4-, oder 5-Methyl-l-vinylimidazol und andere (b) 40 g von Fasern, die aus 92 % Acrylnitril und2-, 4-, or 5-methyl-l-vinylimidazole and others (b) 40 g of fibers, which are composed of 92% acrylonitrile and
5C = Cc enthaltende polymerisierbar Materialien. 15 8% Vinylacetat zusammengesetzt waren, wurden aus5C = Cc containing polymerizable materials. 15 8% vinyl acetate were made up
Das Polymerisat kann ein tertiäres oder höheres dem Spinnsystem entfernt und durch ein Standard-Mischpolymerisat sein, beispielsweise Produkte, die ausrüstungsbad geführt, welches aus einem gewöhndurch die Interpolymerisation von Acrylnitril und liehen Weichmacher, einem gewöhnlichen Schmälzzwei oder mehreren irgendwelcher der vorstehend mittel und einem gewöhnlichen antistatisch machenden angegebenen Monomeren mit Ausnahme von Acryl- 20 Mittel und 2,1 Volumprozent Natriumhydrosulfit benitril erhalten worden, insbesondere und vorzugsweise stand; sie fielen zusammen und wurden getrocknet, umfaßt das ternäre Polymerisat Acrylnitril, Methacryl- Diese 40-g-Probe wurde dann in ein Färbebad einnitril und 2-Vinylpyridin. Die ternären Polymerisate gebracht, wobei das Verhälntis von Färbebad zu enthalten vorzugsweise 80 bis 98% Acrylnitril, 1 bis Fasern 40:1 betrug, und das Färbebad 16 % basischen 10°/0 eines Vinylpyridins oder eines 1-Vinylimidazols 25 Blaufarbstoff, 5°/o Ammoniumacetat und 1% Essig- und 1 bis 18 °/0 einer anderen Substanz, wie Methacryl- säure, jeweils bezogen auf das Gewicht der Probe, nitril oder Vinylchlorid. enthielt. Dieses Färbebad wurde auf den SiedepunktThe polymer can be a tertiary or higher spinning system removed and through a standard copolymer, for example products, the equipment bath, which consists of a customary plasticizer borne by the interpolymerization of acrylonitrile and a common two or more of any of the above agents and a common antistatic making specified monomers with the exception of acrylic 20 agent and 2.1 volume percent sodium hydrosulfite benitrile have been obtained, in particular and preferably stood; they collapsed and were dried, the ternary polymer comprises acrylonitrile, methacrylic This 40 g sample was then mononitrile and 2-vinylpyridine in a dyebath. The ternary polymers accommodated, wherein the Verhälntis preferably contain from dyebath 80 to 98% acrylonitrile, 1 to fibers 40: was 1, and the dyeing bath 16% basic 10 ° / 0 of a vinylpyridine or 1-vinylimidazole of 25 Blue dye, 5 ° / o ammonium acetate and 1% acetic acid and 1 to 18 ° / 0 of another substance, such as methacrylic acid, in each case based on the weight of the sample, nitrile or vinyl chloride. contained. This dyebath was brought to the boiling point
Das Polymerisat kann auch eine Mischung aus gebracht und 2 Stunden darauf gehalten. Die Fasereinem
Polyacrylnitril oder einem binären Mischpoly- probe wurde dann entnommen, gespült und getrocknet,
merisat aus 80 bis 99% Acrylnitril und 1 bis 20% 30 Vor dem Eintauchen der Probe in das Färbebad
mindestens einer anderen ^ C = C =c enthaltenden und nach dem 2stündigen Kochen wurde die Konzen-Substanz
mit 2 bis 50 Gewichtsprozent eines Misch- tration des Farbstoffs in dem Färbebad durch Verpolymerisats
von 10 bis 70% Acrylnitril und 80 bis wenduno; eines Spektralphotometers bestimmt. Die
90% mindestens eines anderen ;C = Cc ent- Farbstoffkonzentration zu Beginn betrug etwa 16%,
haltenden polymerisierbaren Monomeren sein. Wenn 35 berechnet auf das Gewicht der Probe. Nach Beendigung
das polymere Material eine Mischung umfaßt, ist des Färbens wurde festgestellt, daß die Konzentration
es vorzugsweise eine Mischung eines Mischpoly- des Farbstoffs in dem Färbebad 3,8 %, bezogen auf
merisats von 90 bis 98 % Acrylnitril und 2 bis 10 % das Gewicht der Probe, betrug, was anzeigte, daß die
eines anderen monoolefinischen Monomeren, wie Aufnahme der Probe an basischem Farbstoff 12,2 %,
Vinylacetat, welches gegenüber Farbstoff nicht auf- 4° bezogen auf das Gewicht der Probe, betrug,
nahmefähig ist, mit einer genügenden Menge einesThe polymer can also be brought into a mixture and kept on it for 2 hours. The fiber of a polyacrylonitrile or a binary mixed poly sample was then removed, rinsed and dried, merisate of 80 to 99% acrylonitrile and 1 to 20% the 2-hour boiling, the concentrate substance with 2 to 50 percent by weight of a mixed tration of the dye in the dyebath by polymerizing 10 to 70% acrylonitrile and 80 to wenduno; determined by a spectrophotometer. The 90% of at least one other; C = Cc ent- dye concentration at the beginning was about 16%, retaining its polymerizable monomers. If 35 is calculated on the weight of the sample. After completion of the dyeing the polymeric material comprises a mixture, it was found that the concentration of it is preferably a mixture of a mixed poly of the dye in the dyebath 3.8%, based on merisate of 90 to 98% acrylonitrile and 2 to 10% the The weight of the sample was, indicating that that of another monoolefinic monomer, such as basic dye uptake of the sample, was 12.2%, vinyl acetate which was not at -4 ° relative to dye based on the weight of the sample,
is capable of taking with a sufficient amount of one
Mischpolymerisats aus 10 bis 70 % Acrylnitril und Beispiel 2
80 bis 90% eines vinylsubstituierten tertiären heterocyclischen Amins, wie Vinylpyridid oder 1-Vinyl- 40 g von Fasern, bestehend aus einer Mischung aus
imidazol, um eine anfärbbare Mischung zu ergeben, 45 88% eines Mischpolymerisats, hergestellt aus 94%
welche einen Gesamtgehalt, an vinylsubstituiertem Acrylnitril und 6% Vinylacetat, und 12% eines antertiärem
heterocyclischen! Amin von 2 bis 10 %, be- deren Mischpolymerisats, aufgebaut aus 50 % Acrylzogen
auf das Gewicht der Mischung, besitzt. nitril und 50 % Methyl-vinylpyridin, wurden von demCopolymer of 10 to 70% acrylonitrile and example 2
80 to 90% of a vinyl-substituted tertiary heterocyclic amine, such as vinyl pyridide or 1-vinyl 40 g of fibers, consisting of a mixture of imidazole to give a dyeable mixture, 45 88% of a copolymer made from 94% which have a total content of of vinyl-substituted acrylonitrile and 6% vinyl acetate, and 12% of an antertiary heterocyclic! Amine from 2 to 10%, whose copolymer, composed of 50% acrylic, based on the weight of the mixture, possesses. nitrile and 50% methyl-vinylpyridine, were derived from the
Die Erfindung wird nachstehend an Hand von Bei- Spinnsystem entfernt, nachdem sie durch ein Standardspielen näher veranschaulicht. Die Prozentsätze sind, 50 Ausrüstungsbad geführt worden sind, welches zuwenn nichts anderes angegeben ist, auf Gewichtsbasis sammengesetzt ist aus einem üblichen Weichmacher, bezogen. einem üblichen Schmälzmittel, einem üblichen anti-Beisüiell statisch machenden Mittel und 2,1 VolumprozentThe invention is removed below from Bei-Spinnsystem after going through a standard game illustrated in more detail. The percentages are 50 equipment baths have been passed, which to when unless otherwise specified, is composed on a weight basis of a common plasticizer, based. a common lubricant, a common anti-accessory static-making agents and 2.1 percent by volume
Natriumhydrosulfit; sie fielen zusammen und wurdenSodium hydrosulfite; they collapsed and became
(a) 40 g einer Faser, die aus mindestens 80 % Acryl- 55 getrocknet. Diese 40-g-Probe wurde dann in ein Färbenitril zusammengesetzt ist, wurden aus dem Spinn- bad eingebracht, welches aus 16% basischem Blausystem entfernt, nachdem sie durch ein Standard- farbstoff, 5 % Ammoniumacetat und 1 % Essigsäure, ausrüstungsbad geleitet worden waren, welches aus jeweils berechnet auf das Gewicht der Probe, bestand, einem Weichmacher, einem Schmälzmittel und einem wobei das Verhältnis von Färbebad zu Faser 40:1 antistatisch machenden Mittel zusammengesetzt war, 60 betrug. Dieses Färbebad wurde auf den Siedepunkt sie fielen zusammen und wurden getrocknet. Diese gebracht und darauf 2 Stunden lang gehalten. Die 40 g wurden dann in ein Färbebad bei einem Ver- Faserprobe wurde dann entfernt, gespült und gehältnis von Färbebad zu Faser von 40:1 eingebracht, trocknet.(a) 40 g of a fiber made from at least 80% acrylic 55 dried. This 40 g sample was then converted into a dye nitrile is composed, were brought in from the spinning bath, which consists of 16% basic blue system removed after being replaced by a standard dye, 5% ammonium acetate and 1% acetic acid, equipment bath, which consisted of each calculated on the weight of the sample, a plasticizer, a lubricant and an wherein the ratio of dyebath to fiber is 40: 1 was composed of an antistatic agent, was 60. This dyebath was brought to the boiling point they collapsed and were dried. This brought and held for 2 hours. the 40 g was then placed in a dye bath at one point. Fiber sample was then removed, rinsed and retained Brought in from dyebath to fiber of 40: 1, dries.
welches aus 26% basischen Blaufarbstoffs, 5% Am- Vor dem Eintauchen der Probe in das Färbebadwhich consists of 26% basic blue dye, 5% Am- Before immersing the sample in the dye bath
moniumacetat und 1% Essigsäure bestand. Dieses 65 und nach dem 2stündigen Kochen wurde die Farb-monium acetate and 1% acetic acid. This 65 and after 2 hours of cooking, the color
Färbebad wurde auf den Siedepunkt gebracht und stcffkonzentration in dem Färbebad durch Ver-The dyebath was brought to the boiling point and the concentration in the dyebath was
darauf 2 Stunden lang gehalten. Die Faser wurde wendune eines Spsktralphotometers bestimmt. Diethen held for 2 hours. The fiber was determined using a spectrophotometer. the
dann herausgenommen, gespült und getrocknet. Farbstoffkonzentration betrug am Anfang 16%, be-then removed, rinsed and dried. Dye concentration was 16% at the beginning, but
rechnet auf das Gewicht der Probe. Nach Beendigung des Färbens wurde bestimmt, daß die Farbstoffkonzentration im Färbebad 40J0, berechnet auf das Gewicht der Probe, betrug, was anzeigte, daß die Aufnahme der Probe an basischem Farbstoff 12°/0, berechnet auf das Gewicht der Probe, betrug.counts on the weight of the sample. After completion of dyeing, it was determined that the dye concentration in the dye bath 4 0 J 0, calculated on the weight of the sample, was, which indicated that the absorption of the sample on a basic dye 12 ° / 0, calculated on the weight of the sample was, .
Das Verfahren von Beispiel 1 (b) wurde mit der Abänderung wiederholt, daß 0,2 Volumprozent Natriumhydrosulfit in dem Ausrüstungsbad verwendet wurden. Die Konzentration des Farbstoffs in dem Färbebad betrug, nachdem die Färbearbeitsweise vollendet war, 5,8 °/0, was eine Aufnahme an basischem Farbstoff von 10,2 % anzeigte.The procedure of Example 1 (b) was repeated except that 0.2 volume percent sodium hydrosulfite was used in the equipment bath. The concentration of the dye in the dye bath after the Färbearbeitsweise was completed, 5.8 ° / 0, indicating uptake of basic dye of 10.2%, was.
B e i s ρ i e 1 4B e i s ρ i e 1 4
Das Verfahrea-,yon Beispiel 1 (b) wurde mit der ao Abänderung wiederholt, daß 3 Volumprozent Natriumhydrosulfit in dem Ausrüstungsbad und 26 Gewichtsprozent basischen Blaufarbstcffs, bezogen auf die Probe, verwendet wurden. Die Konzentration an Farbstoff in dem Farbbad betrug nach Beendigung der Färbearbeitsweise 10,3 %, was eine Aufnahme an basischem Farbstoff von 15,7% anzeigte.The method of example 1 (b) was carried out with the ao Amendment repeats that 3 percent by volume sodium hydrosulfite in the finish bath and 26 percent by weight basic blue color, based on the sample. The focus on Dye in the dye bath after completion of the dyeing procedure was 10.3% indicating an uptake basic dye of 15.7%.
Das Verfahren von Beispiel 4 wurde mit der Abänderung wiederholt, daß 4 Volumprozent Natriumhydrosulfit in dem Ausrüstungsbad verwendet wurden. Die Farbstoffkonzentration in dem Färbebad betrug nach Beendigung der Färbearbeitsweise 11%, was eine Aufnahme an basischem Farbstoff von 15% anzeigte. The procedure of Example 4 was repeated except that 4 volume percent sodium hydrosulfite were used in the equipment bath. The dye concentration in the dyebath was after completion of the dyeing procedure 11%, which indicated an uptake of basic dye of 15%.
Die Arbeitsweise von Beispiel 4 wurde mit der Abänderung wiederholt, daß 5 Volumprozent Natriumhydrosulfit in dem Ausrüstungsbad verwendet wurden. Die Farbstoffkonzentration in dem Färbebad betrug nach Vollendung der Färbearbeitsweise 10,3 %, was eine Aufnahme an basischem Farbstoff von 15,7 % anzeigte.The procedure of Example 4 was repeated with the modification that 5 percent by volume of sodium hydrosulfite were used in the equipment bath. The dye concentration in the dyebath was after completion of the dyeing procedure 10.3%, which means an uptake of basic dye of 15.7% indicated.
Das Verfahren von Beispiel 4 wurde mit der Abänderung wiederholt, daß 3 Volumprozent Natriumsulfoxylatformaldehyd in dem Ausrüstungsbad verwendet wurden. Die Farbstoffkonzentration in dem Färbebad betrug nach Vollendung der Färbearbeitsweise 11,4 0I0, was eine Aufnahme an basischem Farbstoff von 14,6 % anzeigte.The procedure of Example 4 was repeated except that 3 volume percent sodium sulfoxylate formaldehyde was used in the equipment bath. The dye concentration in the dyebath after completion of the dyeing procedure was 11.4 0 I 0 , which indicated an uptake of basic dye of 14.6%.
Die Arbeitsweise von Beispiel 7 wurde mit der Abänderung wiederholt, daß 4 bzw. 5 Volumprozent Natriumsulfoxylatformaldehyd in dem Ausrüstungsbad verwendet wurden. Die Farbstoffkonzentration in den Färbebädern betrug nach Vollendung der Färbearbeitsweisen 10,5 bzw. 10,9 %, was eine Aufnahme an basischem Farbstoff von 15,5 bzw. 15,1 % anzeigte.The procedure of Example 7 was repeated with the modification that 4 and 5 percent by volume, respectively Sodium sulfoxylate formaldehyde were used in the equipment bath. The dye concentration in the dye baths after completion of the dyeing procedures was 10.5 and 10.9%, which indicates an uptake basic dye of 15.5 and 15.1%, respectively.
Die Arbeitsweise von Beispiel 7 wurde mit der Abänderung wiederholt, daß 3, 4 bzw. 5 Volumprozent Natrium-m-bisulfit dem Ausrüstungsbad zugesetzt wurden. Die Farbstcffkonzentration in den Färbebädern betrug nach Beendigung der Färbearbeitsweisen 10,0, 10,6 bzw. 10,7 0I0, was eine Aufnahme an basischem Farbstoff von 16,0, 15,4 bzw. 15,3% anzeigte. The procedure of Example 7 was repeated with the modification that 3, 4 and 5 percent by volume of sodium m-bisulfite were added to the finishing bath. The Farbstcffkonzentration in the dyebaths was after completion of the Färbearbeitsweisen 10.0, 10.6 or 10.7 0 I 0, indicating uptake of basic dye of 16.0, 15.4 or 15.3%.
Die Arbeitsweise von Beispiel 7 wurde mit der Abänderung wiederholt, daß 3, 4 bzw. 5 Volumprozent Zinkhydrosulfit in dem Ausrüstungsbad verwendet wurden. Die Farbstcffkonzentration in den Färbe-' bädern betrug nach Beendigung der Färbearbeitsweisen 14,9, 15,0 bzw. 15,6%, was eine Aufnahme an basischem Farbstoff von 11,0, 11,0 bzw. 10,4% anzeigte. The procedure of Example 7 was repeated except that 3, 4 and 5 percent by volume, respectively Zinc hydrosulfite were used in the equipment bath. The dye concentration in the dye bathing was 14.9, 15.0 and 15.6% after completion of the dyeing procedures, which indicates an uptake basic dye of 11.0, 11.0 and 10.4%, respectively.
Beim Vergleich der Ergebnisse der Aufnahme von basischem Farbstoff von Fasern, welche im Ausrüstungsbad mit einem Reduktionsmittel behandelt wurden, mit dem Kontrollversuch, bei dem im Ausrüstungsbad kein Reduktionsmittel vorhanden war, wird die überragende Verbesserung der Aufnahmefähigkeit an basischem Farbstoff offensichtlich. In verschiedenen Fällen betrug die Verbesserung mehr als 100 0I0, was sehr zur weiteren Verwendung von Acrylfasern auf dem Textilgebiet dient.When comparing the results of the uptake of basic dye by fibers which have been treated with a reducing agent in the finishing bath with the control experiment in which no reducing agent was present in the finishing bath, the overwhelming improvement in the basic dye absorption capacity is evident. In various cases the improvement was more than 100 0 I 0 , which is very useful for the further use of acrylic fibers in the textile field.
Claims (2)
Family
ID=