DE1428365A1 - Abrasion marks and methods of making same - Google Patents
Abrasion marks and methods of making sameInfo
- Publication number
- DE1428365A1 DE1428365A1 DE19621428365 DE1428365A DE1428365A1 DE 1428365 A1 DE1428365 A1 DE 1428365A1 DE 19621428365 DE19621428365 DE 19621428365 DE 1428365 A DE1428365 A DE 1428365A DE 1428365 A1 DE1428365 A1 DE 1428365A1
- Authority
- DE
- Germany
- Prior art keywords
- binder
- rub
- abrasive
- vinyl acetate
- fibers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
Scheuerflecken, sowie Verfahren zur Herstellung derselben. Abrasion marks and methods of making same.
Die vorliegende Erfindung bezieht sich auf insbesondere dünne hinterlegte Scheuerflecken mit vorzugsweise flexibler Unterlage, die ihre Scheuerkraft während des Gebrauchs beibehalten, sowie ferner auf ein schnell und wirksam durchführbares Verfahren zur Herstellung derselben·The present invention relates in particular to thin deposited rub marks with preferably flexible pad that maintains its abrasive power during use, as well as quick and easy effectively feasible process for the production of the same
Der erfindungsgemäße Scheuerflecken besitzt eine Scheuerfläohe aus einer Lage von dünnen Scheuerfasern, einer dünnen Unterlage, die vorzugsweise in Größe und Form im wesentlichen mit der Scheuerfläche übereinstimmt, und einer gegen Wasser und Detergentien beständigen Zwischenschicht, die vorzugsweise aus einer homogenen Mischung eines paraffinieren Materials und eines harzartigen Copolymeren aus einem niederen Olefin und einem polarenThe scouring patch according to the invention has a scouring surface made of a layer of thin scouring fibers, one thin pad, which preferably corresponds essentially in size and shape to the scrubbing surface, and an intermediate layer which is resistant to water and detergents and which preferably consists of a homogeneous mixture a paraffinic material and a resinous one Copolymers of a lower olefin and a polar one
-2--2-
809810/0436 BAO ORiQiNAL809810/0436 BAO ORiQiNAL
Gesteht und dio an der Oberfläche der Unterlage unöl an Teilen der Scheuerfaeern haftet und die beide miteinander verbindet.Confesses and dio adheres to the surface of the pad unoil on parts of the abrasive pulp and the connects both.
Solche Sclieuerflecken können hergestellt werden, indem auf eina Unterlage ein geschmolzenes thermoplastisches vrsssarfesteo Bindemittel aufgetragen und anschließend Kit einer dttnnsn Lage aus fas^rartigem Scheuersnaterial zunammongebracht und derart :su3am3iengspreßt wird, daß ein wesentliche*? Teil der Scheuerfasern in das gesehmol— sene Binöemitttäl eingebettet und nach Abkühlen unter dessen 3clme.lr,pimkt durch das verfestigt© Bindemittel ίεοΐ Kit dar Unterlage verbunden wird.Such close spots can be made by a molten thermoplastic vrsssarfesteo binder is applied to a base and then Kit of a dttnnsnnn layer of fibrous abrasive material brought to an ammunition and in such a way: su3am3iengspreßt that an essential *? Part of the abrasive fibers in the gesehmol— sene Binöemitttäl embedded and after cooling under its 3clme.lr, pimps through the solidified © binder ίεοΐ Kit that connects to the pad.
soll ßis Brfindmjg, deren Vorteile und lichlraitsn in Suaaiamenhang mit den Zeichnungen naher "beschristen werden? es zeigernshould ßis Brfindmjg, their advantages and lichlraitsn in Suaaiamenhang with the drawings closer "will be constrained? show it
3?igo 1 - ain© v-yrßinfachte Seitenansicht einer Vorrich tung siiT Herstellung der erfindungsgemäßen Sehßuorfleckenj3? Igo 1 - ain © v-yrß Simplified side view of a device tion siiT production of the invention Visual stains j
Fig. 2 - eine Seitenansicht einer weiteren Vorrichtung zur Herstellung der erfindungsgemäßen Scheuer flecken auf eine abgewandelte Welse?Fig. 2 - a side view of a further device for producing the scourer according to the invention spots on a modified catfish?
Fig. 3 - eine seitliche Teilansicht eines erfindungsgeFig. 3 - a partial side view of a erfindungsge
-3--3-
809810/0436 BAD ORIGINAL809810/0436 ORIGINAL BATHROOM
Handgriff; Fig· 4 » eine Seitenansicht einer anderen Form des er-Handle; Fig · 4 »a side view of another form of the
findungsgemäßen Scheuerfleckens; Fig. 5 - eine Teildraufsioht auf den erfindungsgemäßeninventive rub stains; Fig. 5 - a partial plan view of the inventive
Bei der in Fig. 1 gezeigten Vorrichtung werden eine naßfeste Papierunterlagebahn 21 von einerRolle 23 und eine zur Urzeugung der Handgriffe bestimmte Bahn 13 aus naßfestem Papier mit geringerer Bahnbreite von einer Rolle 11 kontinuierlich abgezogen. Die Bahn 13 wird unter einem beheizten Abgabebehälter 15 hindurchgeführt, aus dessen Öffnung 17 in regelmäßigen Abständen ein geschmolzenes wasserfestes Bindemittel 19 abgegeben wird. Als Bindemittel dient hier οine homogene Masse aus Paraffin, einen Mischpolymeren aus Äthylen und Vinylacetat und Abietinsäure· Die Bahn 13 wird anschließend mittels Umlenkwalzen 29 und 31 mit ihrer mit geschmolzenem Bindemittel versehenen Fläche auf die Unterlagebahn 21 aufgelegt und mit dieser durch Andruckwalzen 25 und 27 bei ^leich^zeitigem Erhärten de· Bindemittels 19 fest verbunden. Die kombinierte Bahn wird mittels der Umlenkwalzen 33 undIn the apparatus shown in Fig. 1, a wet strength paper backing sheet 21 is fed from a roll 23 and a web 13 made of wet strength paper with a smaller web width of one to create the handles Roll 11 withdrawn continuously. The web 13 is passed under a heated dispensing container 15, from the opening 17 of which a molten waterproof binder 19 is released at regular intervals. A homogeneous mass of paraffin serves as a binding agent, a mixed polymer of ethylene and vinyl acetate and abietic acid · The web 13 is then by means of deflection rollers 29 and 31 with their melted binder provided surface is placed on the underlay web 21 and firmly connected to this by pressure rollers 25 and 27 with the binding agent 19 hardening slightly. the combined web is by means of the guide rollers 33 and
-4--4-
809810/0436 BAD809810/0436 BATH
unter -einem zweiten Vorratstank 37 . ainflurx»ihgeftllirfc# aus äem ein,, vorzugsweise gleiches, gesdaaiolsenes wasserfestes Bindemittel 19 auf die der Bah» gegenüberliegende Pläene der Unterlege bahn 21 vorzugsweise "bei 90 "bis 140° C in Fora :einea- die' gesamte Pläche !abdeckenden Filmes aufgebracht wird. Von der Holle 41 wird eine Stahlwollofler SelieuerfaaerTialm 39 aTig«aoger», auf ü@n geseliiaoiisenen Binciemittelfilm aufgelegt unä mittels Anärucicwalssen 43 und 45 in giesan eingedrückt, so ^aS als Seheuerfaaeim min4@stens teilweise vom Bindemittel 19 toeöeckt Bind. ' 2ur Verfestigung ά&& Bindeiaittels 19 können laeeoafier© Salhlsvalzen vorgesehen werden oder die Andrückwalze 45 kann, geiaäß Fig. 1, eine KUUIf urtktion iibernefemön· Di« hätenf'öTMigen Seiieuerflecken können anechließenö mit Betargentien 47 besprüht «erden« Das etwa damit aufge- -laraclite Iiosungsmittel kann durch TrockenvorriclifungeB entfernt werden«, .Mit Sehneiöevorrichtungen 51 kann die Bann schlieSlicli, vorzugsweise an den Befestigungsstellen der Handgriffe, in "fertige Sskeuerf lecken zerschnitt en werden.under a second storage tank 37. ainflurx "ihgeftllirfc # from äem a ,, preferably the same, gesdaaiolsenes waterproof binder 19 on the Bah» opposite Pläene the underlay sheet 21 is preferably "90" to 140 ° C in Fora: einea- the 'entire Pläche covering film is applied! . Of the hell 41 is a Stahlwollofler SelieuerfaaerTialm 39 atig "aoger" on ü @ n geseliiaoiisenen Binciemittelfilm placed UNAE pressed by Anärucicwalssen 43 and 45 in giesan, so as ^ aS Seheuerfaaeim @ min4 least in part from the binder 19 toeöeckt Bind. '2UR solidification ά && Bindeiaittels 19 laeeoafier © Salhlsvalzen may be provided or the pressure roller 45 may, geiaäß Fig. 1, a KUUIf urtktion iibernefemön · Di "hätenf'öTMigen Seiieuerflecken can anechließenö with Betargentien 47 sprayed" ground "This example thus listed -laraclite Iiosungsmittel can be removed by TrockenvorriclifungeB ".With Sehneiöevorrichtungen 51, the spell schlieSlicli, preferably cut lick at the fastening points of the handles, in" finished Sskeuerf ene.
In Pig, 2 wird eine mit verfestigtem wasserfesten Bindemittel 57 l»eschich.tet© naßfeste Bapier unterlagebahn 55 ^o^ cl«r Holle 53 abgezogen, ülaer die Umlenkwalzen 59 .und 61 auf sine von der Bolle 65In Pig, 2 is one with solidified waterproof binder 57 l »eschich.tet © wet-strength paper underlay web 55 ^ o ^ cl «r Holle 53 peeled off, ülaer die Deflection rollers 59 and 61 on sine von der Bolle 65
809810/0^36 BADOfflQfiüf ■809810/0 ^ 36 BADOfflQfiüf ■
aogene Scheuerfasermahn 63 aufgelegt» Bas Bindemittel 57 wird auf der Heizwalze 67 durch Wärmeleistung der Stahlwollfaserbahn 63 geschmolzen und die Scheuerfasarn mittels der Andruckwalze 69 in das geschmolzene Bindemittel 57 eingedrückt, daa sich auf Abt Kühlwalze 75 "beim Andrücken der kombinierten Bahn mittels der Anäruckwalzen 71 und 73 verfestigt. Anschließend können gemiiß Fig. 1 Vorrichtungen zum Aufbringen Ton Seife, Trooknungs- und Schneiäeeinriciitungen vorgesehen osin«aogene Scheuerfasermahn "issued 63 Bas binder 57 on the heating roller 67 63 melted by the heat capacity of the steel wool fiber web and the Scheuerfasarn pressed into the melted binder 57 by means of the pressing roller 69, daa to Abt cooling roller 75 'when pressing the combined path by means of Anäruckwalzen 71 and 73. Then, as shown in Fig. 1, devices for applying clay, soap, drying and snow-making devices can be provided.
3 zeigt eine Ausführungsforai ä*m erfin&ungsgsmäßen Scheuerballens oder -ilackeno heotehcnd aus einer Stahlwollschicht 39# einer Harsbindemittelschicht 19* einer Papierunteriage 21, einer aweiten hariiertigen Bindern!ttelßchicht 19 und einem Handgriff 13« Durch lsichtss Biegen des Scheuerfleckens kann man die Finger zwischen Handgriff 12 und Unterlage 21 der Scheuervorrichtung einschieben«.3 shows an embodiment of a scouring pad or lacquer according to the invention, consisting of a steel wool layer 39, a hardening agent layer 19, a paper backing 21, an additional hardened binding agent layer 19 and a handle 13 and insert pad 21 of the scrubbing device «.
Obwohl die Scheuerflecken gemäß Fig. 3 besonders leicht hergestellt werden können, erscheint es zuweilen wünschenswert, eine Scheuervorrichtung mit einem Handgriff herzustellen, bei dem zum Einschieben der Finger kein Verbiegen des Scheuerfleckens notwendig ist. Ein derartiger Scheuerflecken ist in Fig. 4 gezeigt, in dsr die Stahlwoll- oder Scheuerfaserschicht 39» die Bindemittelschichten 19 undAlthough the rub marks according to FIG. 3 are particularly light can be made, it sometimes appears desirable to make a scrubbing device with a handle, in which you do not need to bend the rub stain to insert your fingers. Such a rub stain is shown in Fig. 4, in dsr the steel wool or abrasive fiber layer 39 »the binder layers 19 and
-6--6-
809810/0A3G BAD ORIGINAL,809810 / 0A3G BAD ORIGINAL,
Sie Bapieruntsrlage 21 ait Abbildung 3 übereinstimmen«. Ber. Handgriff 77 kann zur Verpackung an einer oder an beiden Ecken 79 und 81 flachgefaltet werden. Dieser Handgriff ist auch in Abb. 5 gössigt.You paper submission 21 agree with Figure 3 «. Ber. Handle 77 can be used for packaging on or on both corners 79 and 81 are folded flat. This The handle is also shown in Fig. 5.
erfinSiangsgeraaß feergeotellte Scheuer flecken bestehterfinSiangsgeraaß feergeotellen chafing stains
also aas einer Scheuer fas er schicht,· einer dünnen Unterlage uvA einem ^asoorfssfcsn und vorzugsweise gogQn Rsini- so aas a scouring layer, a thin pad uvA a ^ asoorfssfcsn and preferably gogQn Rsini
ce^gfendsftUiigem. Bindemittel, das die Scheuer-' fest mit äer Unt-srlsgs verbindet» . Die .erfinclungs—ce ^ gfendsftUiigem. Binding agent that prevents the abrasion firmly connected with the sub-srlsgs ». The "discovery"
n Scheuer:fl3o3ce'a können, einen daran befestigten ixBitasn imß. öle O-estalt- einer Holle, eines S--fereifeBos einss Bogeiis c-äejp exiles einseinen Fleckens oder lallena habe η o - . 'n Scheuer: fl3o3ce'a able to imß an attached ixBitasn. öle O-estalt- a hell, an S - fereifeBo s einss Bogeiis c-äejp exiles one of its spots or lallena got η o -. '
Ils Scl"ö\i©rfiasßrK "foaatehsn voraugsweise aus öünnfaeeriger obwohl aueh andere. Metallfasern und Fasern ausIls Scl "ö \ i © rfiasßrK" foaatehsn preferably from Öünnfaeeriger although others too. Metal fibers and fibers
Kunststoffen verwendet warden können. Die Fasern äer Stslilwolle haben vorzugsweise einen Durchmessar von stwa 0?05 bis 0,08 mia und können leicht verfilzt sain» ¥orsi;igsir*eis'3 sollen die Fasern jedoch im wesentlichen gleichgerichtet sein« Die StahlwolD-schicht iat gewöhnlich stwa 1 Ms β mm dick und gelegentlich noch dünner gepreßt» Die für Stahlwolle gebräuchliche söge— nannte "Eichte" der erfindungsgemäß bevorzugten Stahl-Plastics can be used. The fibers of silk wool preferably have a diameter of about 0 ? 05 to 0.08 mia and can easily matted sain "¥ orsi; igsi r * eis'3 are the fibers but substantially rectified his" The StahlwolD-layer iat usually stwa 1 Ms β mm thick pressed even thinner and, occasionally, "The for Steel wool, so-called "gauge" of the steel wool preferred according to the invention
-7--7-
80 98 10/043G BAD ORIQFNAi 80 98 10 / 043G BAD ORIQFNAi
— "7 —- "7 -
wolle beträgt etwa OyO1 bis 0,2 g/cm2.wool is about O y O1 to 0.2 g / cm 2 .
Die unterlage 21 kann aus einem beliebigen geeigneten Bogen- oder Polienmaterial bestehen, wobei vorzugsweise eine Folie auf Zelluloseba3is, wie Papier9 verwendet wird. Die Unterlage soll durch entsprechende Vorbehandlung eine hohe Naßfestigkeit aufweisen, so daß sie durch Einwirkung von Wasser nicht zu leicht beeinträchtigt wird«. Ein hierfür bekanntes Verfahren besteht z.B. λ im Aufbringen ainer Emulsion aus verschiedenen synthetischen, organischen Kunststoffen, ZeB. Aminoharesen auf Papier. Geeignete Papierunterlagen besitzen eine Dicke von Oj02 bis 0,3 mm* 3)i3 Unterlage kann nach'Wunsch glatt, gerippt oder u'igleichzsäßig profiliert sein, sie ist jedoch gewöhnlich im wesentlichen flach. Obwohl für den Handgriff auch andere Materialien verwendet werden können, wird dieser gewöhnlich'ebenfalls aus widerstandsfähigem Papier iJeatehen, das annähernd gleiche Eigenschaften wie die Unterlage aufweist. ™The base 21 can consist of any suitable sheet or polypropylene material, preferably a cellulose-based film, such as paper 9 , being used. The substrate should have a high wet strength through appropriate pretreatment, so that it is not too easily impaired by the action of water «. A this known method is, for example, in applying λ ainer emulsion from various synthetic organic plastics, ZeB. Aminoharesis on paper. Suitable paper supports have a thickness of 0.12 to 0.3 mm * 3) The support can be smooth, ribbed or profiled as desired, but it is usually essentially flat. Although other materials can also be used for the handle, this is usually also made of durable paper, which has approximately the same properties as the base. ™
Das die Unterlage und die Scheuerfasern verbindende wasserfeste Bindemittel ist vorzugsweise ©in thermoplastisches harzartiges Material, das leicht geschmolzen, aufgetragen und durch Abkühlen verfestigt werden kann und in verfestigtem Zustand die Scheuerfasern fest umschließt und feat 'an aer Unterlage fcaftet. Die Bindemittels chieht ist im allge-The waterproof one connecting the base and the abrasive fibers Binder is preferably applied in thermoplastic resinous material that is easily melted and can be solidified by cooling and, in the solidified state, firmly encloses the abrasive fibers and feats the underlay fcaftet. The binder layer is generally
-8--8th-
• v 809810/0435• v 809810/0435
BADBATH
meinen 0,02 bis 0,3 ism dick, jedoch können auch größere Schichtdicken verwendet werden» Baa Bindemittel wird gewöhnlich in geschmolzenem Zustand und vorzugsweise "bei einer Temperatur von 90 bis 140° C aufgebracht und durch Abkühlen unter 50° C verfestigt. Zur Befestigung des Handgriffes und der Scheuerfaserschicht- auf der Unterlage wird zweckmäßig dasselbe Bindemittel benutzt, wenn ein Fapierhandgriff verwendet wird.mean 0.02 to 0.3 ism thick, but larger ones can also be used Layer thicknesses are used »Baa binder is common in the molten state and preferably "at applied at a temperature of 90 to 140 ° C and solidified by cooling below 50 ° C. To attach the The same binding agent is expediently used when the handle and the abrasive fiber layer on the base a paper handle is used.
Zur Befestigung der Scheuerfaserschicht auf der Papierunterlage werden vorzugsweise Bindemittel aus einem paraffinisehen Material und einem harzartigen Gopolymeren eines niederen Olefins und eines polaren Comonomeren verwendet, da sich herausgestellt hat, daß diese aucli bei dauerndem Eeiben der vollständig nassen und mit Reinigungsmitteln Scheuerflecken auf köpfen und dergleichen dieTo attach the abrasive fiber layer to the paper backing, binders made from a paraffinic layer are preferably used Material and a resinous copolymer of a lower olefin and a polar comonomer used, since it has been found that this also lasts Rub the completely wet and with detergent Abrasion marks on heads and the like
sehr fest binden» Unter den niederen Olefinen mit bis zu 5 Kohlenstoffatomen im Molekül wird insbesondere iithylen verwendet» Als polares Comonomeres werden solche bevorzugt, die mit dem niederen Olefin leicht mit dem Paraffin mischbare Copolymere ergeben, wie u.a« Vinylester von niederen !fettsäuren, wie Vinylacetat, sowie Vinylchlorid, Acrylnitril und andere Derivate niederer olefinischen Alkohole, insbesondere des Vinyl- oder Allylalkohol. Vorzugsweise werden Copolymere niedererbind very tightly »Among the lower olefins with up to 5 carbon atoms in the molecule, in particular Ethylene used. Preferred polar comonomers are those which readily react with the lower olefin Paraffin-miscible copolymers result, such as vinyl esters of lower! fatty acids, such as vinyl acetate, as well as vinyl chloride, acrylonitrile and other lower derivatives olefinic alcohols, especially vinyl or allyl alcohol. Preferably copolymers become lower
-9--9-
80 98 1 0/0A3Q; BAD80 98 10/0A3Q; BATH
Olefine mit niederen Fettsäureestern niederer olefinischer Alkohole, wie Vinylalkohol und höher, insbe sondere die Acetale aber auch andere Ester, wie Propionate verwendet.Olefins with lower fatty acid esters of lower olefinic ones Alcohols, such as vinyl alcohol and higher, in particular special the acetals but also other esters such as propionate are used.
'Die vorzugsweise verwendeten Copolymeren aus Äthylen und Vinylacetat haben einen Gehalt von 5 bis 50 $ und vorzugsweise 25 bis 40 # polymerisiertes Vinylacetat\ sie können durch Copolymerisation einer Mischung aus Äthylen und Vinylacetat in Gegenwart eines geeigneten Katalysators wie Sauerstoff oder organisches Peroxyd bei einem Druck von 1000 bis 2100 atm und Temperaturen von 150 bis 250° C hergestellt werden. Derartige Produkte werden von der Firma E.I. du Pont de Nemours and Company, INc, Wilmington, Delaware unter der Bezeichnung "Elvax" hergestellt.The preferably used copolymers of ethylene and vinyl acetate have a content of 5 to 50 $ and preferably 25 to 40 # polymerized vinyl acetate \ they can by copolymerizing a mixture of ethylene and vinyl acetate in the presence of a suitable catalyst such as oxygen or organic peroxide at a pressure of 1000 to 2100 atm and temperatures of 150 to 250 ° C can be produced. Such products are manufactured by EI du Pont de Nemours and Company, Inc., Wilmington, Delaware under the name "Elvax".
Als paraffinisches Material werden vorzugsweise feste Paraffine verwendet, die amorph oder kristallin sein können. Auch Mikrowachse und andere Erdölprodukte sind geeignet. Derartige Wachse oder Paraffine bilden in Mischung mit dem Copolymeren ein wasserfestes Bindemittel mit ungewöhnlich guten Klebeigenschaften.Solid paraffins, which can be amorphous or crystalline, are preferably used as the paraffinic material. Microwaxes and other petroleum products are also suitable. Such waxes or paraffins, when mixed with the copolymer, form a waterproof binder with unusually good adhesive properties.
Es wurde weiter gefunden, daß die Verwendung von Abietin-It was further found that the use of abietin
80 98 1 0/0 A3 G BADOFHGft&t.80 98 1 0/0 A3 G BADOFHGft & t.
säureprodukten, wie Abietinsäure und deren Isomere, hydrierter Abietinsäuren, aromatisierter Abietinsäure und Abietinsäureestern in Verbindung mit dem Paraffin und dem Copolymeren vorteilhaft isto Diese Stoffe, steigern die Kleinigkeit des Bindemittels und verbessern deaaen Haftung an ä&n Stahlwollfasern vor deren vollständigen Verfestigung. Dies ermöglicht eine Steigerung der Her-iatellungsgeschwindigkeit der erfindungsgeiaäSen Placken* Die Abietinsäure kann aus Kolophonium gewonnen werden und auch modifiziertes Kolophonium und SblophoniuiBderivate können verwendet werden»acid products, such as abietic acid and isomers thereof, hydrogenated abietic, flavored abietic and Abietinsäureestern in conjunction with the paraffin and the copolymer is o These substances advantageous to increase the small matter of the binder and improve deaaen adhesion to similar and n steel wool fibers before their complete solidification. This enables an increase in the speed of production of the plaques according to the invention.
Sie Mengenverhältnisse von Copolymer em,. Paraffinmaterial ■ und Abietinsäureprodukt werden zweckmäßig so gewählt, daß eine gleichmäßige Misctaung oder Lösung entsteht, die ©ine gut haftende homogene Schaelse ergibt und beim Erliitaen nicht übermäßig flüssig wird» Ss wurde gefunden, iia8 hierfür 15 bis 60 # öopolymeres, 20 Ms 80 # Paraffinmaterial und 5 bis 40 i* Abietinsäureprodukt verwendet werden können« Vorzugsweise verwendete Mischungen enthalten 30 bis 50 fo eines Copolymeren ais Äthylen vcaä Vinylacetat, 20 bis 40 JS Fai*affinvaohs und 20 bis 40 # Abietinsäureprodukt, a«,Bo stabilisiertes Kolophonium«,You proportions of copolymer em ,. Paraffin material and abietic acid product are expediently chosen so that a uniform mixture or solution results, which results in well-adhering, homogeneous pods and does not become excessively liquid when it is achieved and 5 to 40 can be used i * Abietinsäureprodukt "Preferably mixtures used contain 30 to 50 fo ais a copolymer ethylene vinyl acetate vcaä, 20 to 40 JS Fai * affinvaohs and 20 to 40 # Abietinsäureprodukt, a" Bo stabilized rosin "
Hach dem Aufbringen der Stahlwolle auf die Unterlage kann die Sclieuerfasorschicht mit Reinigungsmitteln besprühtAfter applying the steel wool to the backing can the Sclieuerfasorschicht sprayed with cleaning agents
-11--11-
80 9810/043G BADORiGfNAl.80 9810 / 043G BADORiGfNAl.
werden» Vorzugsweise werden gewöhnlich organische Reinigungsmittel, wie Katriumsalze höherer AlkylbenzolsuXfonate, Blockeopolymere aus Äthylen und Eropylenoxyd (Pluronic), Alkalisalze des Laurylsulfats, Katriumsalz des Talgfettsäureamids des If-methyltaurins (Igepon 3?), Batriuraseife oder Kaliumseife oder höhere Fettsäuren mit t2 "bis 18 Kohlenstoffatomen, wie die aus Mischungen von Talgfett und Kokosnußöl erhaltenen, verwendete Anorganische Reinigungsmittel wie Pentanatriumtripolyphosphat, Tetranatriumpyrophosphat und andere können zur Ergänzung oder als Ersatz organischer Reinigungsmittel verwendet werden« Es wird jedoch vorgezogen, wenigstens teilweise Seife oder andere synthetische organische Waschmittel zu verwenden. Die Reinigungsmittel können in Form einer sich zu einem harten Überzug verfestigenden Schmelze oder als "Lösung oder Dispersion, Z0 B« als wässrige Seifenlösung aufgemacht werden» Bei dieser zuletzt erwähnten Anwendung verhindert die wasserfeste Bindemittelschicht eine Absorption der Reinigungsmittel durch die Unterlage und hält es zur Unterstützung der ReinigungOrganic cleaning agents such as sodium salts of higher alkylbenzene sulfonates, block copolymers of ethylene and propylene oxide (Pluronic), alkali salts of lauryl sulfate, sodium salt of tallow fatty acid amide of if-methyltaurine (Igepon 3?), batriurase soap or potassium soap with t2 "or higher fatty acids or higher fatty acids are usually preferred Carbon atoms, such as the inorganic detergents used, such as pentasodium tripolyphosphate, tetrasodium pyrophosphate and others obtained from mixtures of tallow fat and coconut oil, can be used to supplement or replace organic detergents. It is preferred, however, to use at least some of the soap or other synthetic organic detergents can be made up in the form of a melt solidifying to form a hard coating or as a "solution or dispersion, Z 0 B" as an aqueous soap solution. In this last-mentioned application, the waterproof binder layer prevents e The cleaning agent is absorbed by the pad and holds it to aid cleaning
der gescheuerten Gegenstände an den Scheuerfasern. Nach dee Aufbringen einer Reinigungsmittellösung oder -dispersion kann überschüssiges Dispergier- oder Lösungsmittel, vorzugsweise durch Hitze und/oder Preßluft entr fernt werden.of the scoured objects on the scouring fibers. After applying a detergent solution or -dispersion can contain excess dispersant or solvent, removed preferably by heat and / or compressed air.
-12--12-
809810/04-30 BAD ORJGH809810 / 04-30 BAD ORJGH
Zusätzlich zu den "bisher beschriebenen Bestandteilen aefs erf inöungs^ejaLißen Sclieuerf !©bksns können auch .andere-. au:? dem Reinigutfgsraittelsektor bekannte Hilfsstoffe"verwendet «erden, wi© Parfüm© ? iarbetoffe, Fluoreszenzauf- In addition to the "previously described components aefs erf inöungs ^ ejaLißen Sclieuerf! © bksns" also .other-. Auxiliaries known from the cleaning goods sector "can be used, such as perfume © ? substances, fluorescent
lleiclmittel8 Schauin?erstärf£@rs Rostverhtitungs— Bakterizide rmS. l^ingiciileo Biese können je nach Stabilitäi: entweder susaisMen mit- dsa. Reinigungsmittel odor getrermt davon aufgemacht werden.» Die Papierunter- !®{ζβ mid äer Handgriff Miiinen gsfärtot od,er mit Kennzeichnungen oder Ge''wa'Jichsan¥/ßisuiigen Ijsdruckt werden»lleiclmittel 8 Schauin? erstärf £ @ r s Rostverhtitungs- bactericides RMS. l ^ ingiciileo piping can, depending on the stability: either susaisMen mit- dsa. Cleaning agents odor can be opened separately. " The paper under-! ® {ζβ mid äer handle Miiinen gsfärtot od, he can be printed with labels or Ge''wa'Jichsan ¥ / ßisuiigen Ijsdruckt »
Bio "besonderen Vorteile tier erfinöungsgeinäßen Scheuerflecken hestehcjn äarin, öa@ sie wirksam im Gt"braueh sind, au Reinigungs- uncl Scheuerarbeiten "besonders geeignet und doch so preiswcsrt sind, daß sie nach einmaligem Gebrauch 55Ui' Reinigung der Töpfe und Pfannen einer Kahlzeit weggeworfen werden könnon? Die heschriebanen Verfahren gestatten die rEoche und automatische Erzeugung von Scheuerflecken in groilem Maßstab und erlauben damit eine Senkung der Produktioni?kosten, die einen Verkauf zur einmaligen Anwendung geet&ttet. Die Hausfrau kann auf diese Weise zu jeder Reinigung von iSichenartikeln eine neue Scheuervorrichtung verwenden«,Bio "special advantages of animal scouring stains according to the invention, that they are effective in the brewing, are particularly suitable for cleaning and scouring work" and yet are so inexpensive that they are thrown away after a single use könnon? the heschriebanen methods allow rEoche and automatic generation of scouring spots in groilem scale, thereby allowing a reduction in Produktioni? costs that geet a sale for single use and kills. the housewife can in this way at any cleaning iSichenartikeln a new S c year device use",
Die Tatsache, caß die erfindungs^gemmßen ScheuerfleckenThe fact that the inventive rub stains were made
8O981Q/OA30
BAD ORIGINAL 8O981Q / OA30
BATH ORIGINAL
Scheuerflecken, einschließlich des gefalteten Griffes gewöhnlich weniger als 6 mm stark sind, trögt zu ihrer Flexibilität bei. Pie Unterlage und die wasserfeste Bindemittelschicht verhindert ein Aueinanderreißen der Soheuerfasersohicht beim Gebrauch. Di© Unterlage und der Handgriff ermöglichen der Hausfrau ,die Scheuervorrichtung zu benutzen, ohne dabei mit den Scheuerfasern, t insbesondere der Stahlwolle oder dem Wasser in Berührung zu kommen.Abrasion marks, including the folded handle, which are usually less than 6 mm thick, add to their flexibility. Pie underlay and the waterproof binder layer prevent the torn fiber layer from tearing apart during use. Di © pad and the handle enable the housewife to use the scrubbing device without the scouring fibers, in particular t of steel wool or the water to come into contact.
Sie Brauchbarkeit einer derartigen Scheuervorrichtung hängt stark von der Haftung zwischen Unterlage und Scheuerfaserschicht ab. Diese Bindung muß wasser- und reinigungsmittelfest und doch genügend biegsam sein, so daß das Bindemittel während des Gebrauchs nicht übermäßig abblättert. Die erfindungsgemäßen verwendeten wasserfesten Bindemittel genügen diesen Anforderungen. Die Scheuerfasern werden sogar dann nicht in einem unerwünschten Ausmaß von der Unterlage getrennt, wenn sie einer Zugkraft ausgesetzt werden, wie dies während schwierigen Reinigungsoperationen an Pfannenkanten geschieht. Auch die vorzugsweise aus Papier bestehende Unterlage wird während der Verwendung nicht zusammengeknüllt oder zerrissen. Derart verbesserte Verbrauchseigenschaften derThe usefulness of such a scrubbing device strongly depends on the adhesion between the base and the abrasive fiber layer. This bond must be resistant to water and cleaning agents yet be pliable enough that the binder will not peel excessively during use. The waterproof used according to the invention Binders meet these requirements. The abrasive fibers are not even then in an undesirable manner Extent separated from the support when subjected to tensile force, such as during difficult Cleaning operations are carried out on the edges of the pan. Even the base, which is preferably made of paper, is not crumpled up or torn during use. Such improved consumption properties of the
• -14-• -14-
8 0 98 10/0 A3 G8 0 98 10/0 A3 G
erfindungsgemäß hergestellten Scheuer flecken sind hauptsächlich auf die Wirksamkeit des darin verwendeten wasserfesten Bindemittels zurückzuführen.Chafing stains made in accordance with the invention are mainly due to the effectiveness of the waterproof binder used in it.
Das erfindungsgemäße Yerfahren ist anderen Methoden zur Erzeugung der gegenwärtig verwendeten Scheuerfleckjan, bei denen übliche Klebstoffe wie Kautschukkleber, in Lösungsmitteln gelöste Kleber und Emulsionen verwendet werden, erheblich überlegen. Durch Aufbringen des Bindemittels in geschmolzener Form entfallen aufwendige Wiedergewinnungsanlagen für Lösungsmittel, die zudem häufig toxisch sind» Auch die die Aufwendung für Heizen und Kühlen übersteigenden Aufwendungen für Trocknung werden vermieden« Durch Kühlung wird eine rasche Haftung des Bindemittels auf den Scheuerfasern erzeugt, .und das Verfahren kann erheblich beschleunigt werden, so daß die Produktionskapazitäten erheblich verbessert werden« Da im geschmolzenen Bindemittel kein Wasser vorhanden ist, tritt bei metallischen Scheuerfasern keine Korrosion ein, sondern diese behalten ein ansprechendes glänzendes Aussehen,, Darüber hinaus erzeugt das gleichzeitige Kühlen und Einpressen der Scheuer fas er η in das wasserfeste Bindemittel eine der Anwendung nur einer dieser Maßnahmen überlegene Bindung« The inventive Yerfahren is other methods for Production of the currently used Scheuerfleckjan, in which common adhesives such as rubber adhesive, in Solvent dissolved adhesives and emulsions are used be considerably superior. By applying the binder in molten form, there is no need for costly recovery systems for solvents, which are also often toxic »Including the expenditure for heating and cooling Excessive drying costs are avoided «By cooling, the binding agent adheres quickly generated on the abrasive fibers, and the process can be accelerated considerably, so that the production capacities can be significantly improved «Since there is no water in the molten binder, metallic Abrasive fibers do not corrode, but keep an appealing, shiny appearance In addition, the simultaneous cooling and pressing of the abrasive fibers η into the waterproof binder creates a binding superior to the application of only one of these measures «
Das erfindungsgemäße Verfahren erlaubt nicht nur die kontinuierliche Erzeugung von zugeschnittenen Scheuerflecken,The inventive method not only allows continuous Creation of cut-to-size rub stains,
8 0 98 10/ 0 4 3 G.
BAD ORlOfNAt. 8 0 98 10/0 4 3 G.
BAD ORlOfNAt.
- V - 15 - "- V - 15 - "
sondern auch von gegebenenfalls aufrollbaren bahnförmigen Scheuerflecken oder -streifen, die für einige Verwendungszwecke den zugeschnittenen Scheuerflecken unter Umständen vorzuziehen sind. Die band- oder rollenförmigen Scheuerstreifen können auch vorgeschnitten oder teilweise vorgeschnitten sein, um eine Abtrennung einzelner nur noch durch die gemeinsame Unterlage zusammengehaltener Scheuerflecken unmitiielbar vor der Verwendung au erleichtern.but also of web-shaped rolls that can optionally be rolled up Rub marks or streaks that work for some uses the cut rub stains under certain circumstances are preferable. The tape or roll-shaped abrasive strips can also be pre-cut or partially pre-cut in order to only separate individual parts Immediately facilitate the joint support of chafing stains held together before use.
Das folgende Beispiel beschreibt ein Verfahren zur Erzeugung der erfindungsgemäßen Scheuerflecken, die bereits erfolgreich benutzt werden. Wenn nichts anderes angegeben ist, beziehen sich alle Mengenverhältnisse auf Gewichtsangaben.The following example describes a method for producing the rub marks according to the invention, which has already been successful to be used. Unless stated otherwise, all quantitative ratios relate to weight data.
30 Teile Paraffinwachs mit einem Schmelzpunkt von annähernd 70° C, '30 Teile filtriertes stabilisiertes Kolophonium ("Staybelite resin" von Hercules Powder Co., Wilmington, Delaware) und 40 Teile eines Aethylen-Vinylacetatcopolymeren mit einem Aethylen/Vinylacetat-Verhältnis von etwa 67 ί 33 werden miteinander gemischt und bei 115°C -geschmolzen« Die geschmolzene Mischung wird mittels einer Aufbringevorrichtung auf eine Papierunterlage aufgebracht. Daer Beschichtungsgewicht wird so reguliert, daß ein kreppartige» Papier mit großer Jfaßf estigkeit und einem Gkrundge-wicht -won etwa 17 kg pro Ries vorzugsweise mit einem30 parts of paraffin wax with a melting point of approximately 70 ° C., 30 parts of filtered stabilized rosin ("Staybelite resin" from Hercules Powder Co., Wilmington, Delaware) and 40 parts of an ethylene-vinyl acetate copolymer with an ethylene / vinyl acetate ratio of about 67 ί 33 are mixed with one another and melted at 115 ° C. The melted mixture is applied to a paper base using an application device. The coating weight is regulated so that a crepe-like paper with great strength and a basic weight of about 17 kg per ream, preferably with one
-16-809810/0430 -16- 809810/0430
Oberzugsgewicht von 20 bis 25 kg pro Hies beschichtet wird* Fach der Beschichtung wird eine Stahlwollschicht auf die beschichtete Seite des Papiers aufgebracht, indem das beschichtete Papier und die Stahlwolle über eine beheizte Walze geführt werden« Die erwärmte Stahlwolle bettet sich von selbst in die Bindemittelschieht ein und wird beim darauffolgenden Kühlen und Anpressen bei 10° C durch Verfestigung des Bindemittels fest mit der Unterlage verbunden*Top coat weight of 20 to 25 kg per layer is coated * Compartment of the coating, a steel wool layer is applied to the coated side of the paper by guiding the coated paper and steel wool over a heated roller. «The heated steel wool embeds itself in the binder and during the subsequent cooling and pressing at 10 ° C, the bonding agent solidifies it firmly with the base *
Anschließend wird eine 33$ige wässrige .Lösung einer Mischung von Kalium- und Fatriumseife mit einer automatischen Aufbürstvorrichtung auf die Stahlwolle aufgebürstete Die Seife ist eine Mischung aus gleichen Teilen Kokosöl- und TaIgfettsäure, in denen das verseifende Alkalimetall eine 9 s 1 Mischung von Kalium und Natrium ist. Je Quadrataentimeter Scheuerflecken werden 0,05 g Seifenlösung angewandt, so daß etwa 0,017 g trockene Seife auf dieser Fläche verbleibenο Die überschüssige Feuchtigkeit wird durch Druckluft bei*50° G entfernt und die Scheuerflecken werden anschließend geschnitten und verpackt.A 33% aqueous solution of a mixture is then added of potassium and sodium soap with an automatic brushing device The soap is brushed onto the steel wool and is a mixture of equal parts coconut oil and day fatty acid, in which the saponifying alkali metal is a 9 s 1 mixture of potassium and sodium. Each square centimeter Rub stains are applied 0.05 g of soap solution, so that about 0.017 g of dry soap remains on this surface o The excess moisture is removed removed by compressed air at * 50 ° G and the abrasion marks are then cut and packaged.
Die erfindungsgemäß hergestellten Scheuerflecken wurden im Iiaboratorium mit,der Praxis angepaßten P^fverfahreii getestet und waren sur Entfernung ypn starken Ablagerungen verbrannter nahrungsmittel aus Töpjfen und Pfannen ^ Sie polierten außerdem genau jso gut oder heaeer alp die getföhnliehen handelsüblichenThe rub stains made in accordance with the invention were in the laboratory with practice-adapted procedures tested and were sur removal of ypn heavy deposits burnt food from pots and pans ^ They also polished exactly jso good or heaeer alp die get blown commercially available
Claims (1)
New York, g.Y.. / V.St.A, Colgate-Falmclive Company
New York, gY. / V.St.A,