DE102011053599A1

DE102011053599A1 - Method for manufacturing metal wool mat for cleaning purpose, involves combining metal fibers for metal wool, and compacting metal wool mechanically to metal wool mat, particularly by rolling on certain millimeter thickness

Info

Publication number: DE102011053599A1
Application number: DE102011053599A
Authority: DE
Inventors: Hubert Reuschenbach
Original assignee: Delu Ako Minky GmbH
Current assignee: Delu Ako Minky GmbH
Priority date: 2011-09-14
Filing date: 2011-09-14
Publication date: 2013-03-14

Abstract

The method involves combining metal fibers (4) for metal wool, and compacting the metal wool mechanically to a metal wool mat (1), particularly by rolling on certain millimeter thickness. Acrylic (2) is added in the metal wool mat. The acrylic has a temperature between 60 degree Celsius and 200 degree Celsius. The acrylic is supplied from a front side (5) or back side (6) of the metal wool mat on its two surfaces. The treatment of the metal wool mat is repeated with acrylic. An independent claim is included for a cleaning device provided with a handle portion.

Description

Die vorliegende Erfindung betrifft ein Verfahren zur Herstellung einer Metallwollematte für Reinigungszwecke, bei dem Metallfasern zu Metallwolle zusammengefügt werden und die Metallwolle mechanisch zu einer Metallmatte verdichtet wird, vorzugsweise durch Walzen auf einige Millimeter Dicke.The present invention relates to a process for producing a metal wool mat for cleaning purposes, in which metal fibers are assembled into metal wool and the metal wool is mechanically compacted to a metal mat, preferably by rolling to a few millimeters thickness.

Eine derartige Metallwollematte ist beispielsweise aus der DE 102 33 670 A1 bekannt. Die bekannte Metallwollematte besteht aus Stahlwolle, die mit einer Trägerschicht aus textilem Material vernadelt oder verklebt ist. Das Trägermaterial dient zur mechanischen Stabilisierung der Stahlwolleschicht, die ansonsten zu schnell ausfasern könnte und unbrauchbar würde. Außerdem dient die Trägerschicht zur Befestigung des aus Stahlwolle und Trägerschicht bestehenden Reinigungsteils an einem Halteteil, welches beispielsweise aus Hartkunststoff, Holz oder Schaumstoff bestehen kann. Das Reinigungsteil kann fest mit dem Halteteil verklebt oder lösbar daran befestigt sein, insbesondere durch Klettverschluss.Such a metal wool mat is for example from DE 102 33 670 A1 known. The known metal wool mat is made of steel wool, which is needled or glued to a carrier layer of textile material. The carrier material serves to mechanically stabilize the steel wool layer, which otherwise could fray too quickly and become unusable. In addition, the carrier layer is used to attach the existing steel wool and backing layer cleaning part to a holding part, which may for example consist of hard plastic, wood or foam. The cleaning member may be firmly bonded to the holding member or releasably secured thereto, in particular by Velcro.

Aufgabe der Erfindung ist es eine Metallwollematte für Reinigungszwecke anzugeben, die einfach aufgebaut ist, und ein kostengünstiges Verfahren zu ihrer Herstellung anzugeben.The object of the invention is to provide a metal wool mat for cleaning purposes, which is simple in construction, and to provide a cost-effective method for their preparation.

Die erfindungsgemäße Lösung sieht vor, dass der Metallwollematte während ihrer Herstellung Acryl zugefügt wird, welches dann die Metallfasern der Metallwollematte miteinander verbindet. Das Acryl trägt somit durch die Verbindung zwischen den Metallfasern zur mechanischen Stabilisierung der Metallwollematte bei. Mit Vorteil kann daher bei der erfindungsgemäßen Metallwollematte auf eine Trägerschicht zur Stabilisierung der Metallwolle verzichtet werden. Dennoch ist die erfindungsgemäße Metallwollematte mechanisch so stabil, dass sie lange für Reinigungszwecke verwendet werden kann, ohne auszufasern oder sich aufzulösen.The solution according to the invention provides that the metal wool mat during its production is added acrylic, which then connects the metal fibers of the metal wool mat together. The acrylic thus contributes to the mechanical stabilization of the metal wool mat by the connection between the metal fibers. Advantageously, it is therefore possible to dispense with the metal wool mat according to the invention on a support layer for stabilizing the metal wool. Nevertheless, the metal wool mat according to the invention is mechanically stable so that it can be used for cleaning for a long time without fraying or dissolving.

Das erfindungsgemäße Verfahren eignet sich für alle in Frage kommenden Metallwollen, insbesondere Stahlwolle, vorzugsweise Edelstahlwolle und Metallwollen aus Kupfer, Messing, Aluminium, Nickel und der gleichen Metallen. Auch alle Arten von Acryl, sowohl wasserlösliche, als auch in anderen Lösemitteln lösliche Acryle eignen sich für die vorliegende Erfindung.The inventive method is suitable for all eligible metal wool, especially steel wool, preferably stainless steel wool and metal wool of copper, brass, aluminum, nickel and the same metals. Also, all types of acrylic, both water-soluble and other solvent-soluble acrylics are suitable for the present invention.

Nach der Gewinnung von Metallfasern aus einem Metallstab durch Abschaben mittels eines Messers gewinnt man die Metallwolle, welche zu einem Strang von gut 1 cm Dicke und ca. 50 cm Breite geformt wird. Dieser Metallwollestrang wird sodann vorzugsweise durch Walzen auf eine Dicke von einigen Millimetern, vorzugsweise 3 mm Dicke mechanisch verdichtet.After the extraction of metal fibers from a metal rod by scraping by means of a knife to win the metal wool, which is formed into a strand of more than 1 cm thick and about 50 cm wide. This metal wool strand is then preferably mechanically compacted by rolling to a thickness of a few millimeters, preferably 3 mm thickness.

Die verdichtete Metallwollematte läuft durch eine Acrylbehandlungsstation, wo das Acryl durch Düsen auf eine oder beide Seiten des Metallwollbandes aufgesprüht wird. Auch Aufdampfen oder Einnebeln der Metallwollematte mit Acryl ist möglich. Dabei werden vorzugsweise beide Oberflächen des Metallwollbandes, d. h. die Vorder- und die Rückseite mit Acryl behandelt. Auf diese Weise kann das Acryl tief in die Metallwolleschicht eindringen und sich dort Verfestigen, wobei die Metallfasern der Metallwollematte miteinander verbunden werden.The compacted metal wool mat passes through an acrylic treatment station where the acrylic is sprayed through nozzles onto one or both sides of the metal wool tape. Also vapor deposition or fogging of the metal wool mat with acrylic is possible. In this case, preferably both surfaces of the metal wool tape, d. H. the front and the back are treated with acrylic. In this way, the acrylic can penetrate deeply into the metal wool layer and solidify there, whereby the metal fibers of the metal wool mat are joined together.

Zum Aufsprühen bzw. Aufdampfen bzw. Einnebeln der Metallwollematte wird das Acryl erhitzt, wobei eine Temperatur zwischen 60°C und 200°C am besten geeignet ist. Bei Metallwollematten mit geringer Metallfaserdichte kann das Acryl mit einer geringeren Temperatur im Bereich der unteren Temperaturgrenze aufgebracht werden. Bei Metallwollematten mit höherer Metallfaserdichte empfiehlt sich eine höhere Temperatur im Bereich der oberen Grenze des genannten Temperaturbereichs, weil das heißere Acryl dünnflüssiger ist und auch bei hoher Metallfaserdichte die Metallfasern tief im Inneren der Metallfasermatte erreichen kann.For spraying or vaporization or fogging of the metal wool mat, the acrylic is heated, with a temperature between 60 ° C and 200 ° C is most suitable. For low metal fiber density metal wool mats, the acrylic may be applied at a lower temperature near the lower temperature limit. In the case of metal wool mats with a higher metal fiber density, a higher temperature is recommended within the upper limit of the stated temperature range because the hotter acrylic is less viscous and can reach the metal fibers deep inside the metal fiber mat even at high metal fiber density.

Vorzugsweise wird die Acrylbehandlung noch einmal oder mehrmals wiederholt, sobald sich das Acryl aus der vorhergehenden Behandlung verfestigt hat. Durch mehrmalige Behandlung kann die Festigkeit und Haltbarkeit der Metallwollematte noch verbessert werden.Preferably, the acrylic treatment is repeated once or more once the acrylic has solidified from the previous treatment. By repeated treatment, the strength and durability of the metal wool mat can be improved.

In einer Weiterbildung der Erfindung ist nach der Acrylbehandlung ein weiterer Fertigungsschritt vorgesehen, der darin besteht, dass die Metallwollematte auf ihrer Rückseite mit Kunststofffasern besprüht wird. Die Kunststofffasern werden in einer entsprechenden Arbeitsstation durch das Herauspressen von heißer Kunststoffmaße aus sehr feinen Düsen erzeugt und durch Aufsprühen auf die Metallwollematte mit der Metallwolle verbunden. Eine so behandelte Rückseite eignet sich unter Umständen noch besser zur Befestigung der Metallwollematte an einem Griffteil, welches zur Befestigung an seiner Unterseite mit Klettmaterial versehen ist.In a further development of the invention, a further production step is provided after the acrylic treatment, which consists in that the metal wool mat is sprayed on its back with plastic fibers. The plastic fibers are produced in a corresponding work station by pressing out hot plastic material from very fine nozzles and connected by spraying onto the metal wool mat with the metal wool. Under certain circumstances, a reverse side treated in this way is even better suited for fastening the metal wool mat to a handle part which is provided with hook and loop material for attachment to its underside.

Die erfindungsgemäße Metallwollematte kann nach der Acrylbehandlung noch verbessert werden, indem sie mit einem Reinigungsmittel, insbesondere mit Seife versehen wird. Für die Reinigung von verschmutzten Oberflächen ist dann lediglich die Zugabe von etwas Wasser erforderlich, so dass die Seife oder das Reinigungsmittel wirksam wird. Der Benutzer kann somit auf die zusätzliche Bereitstellung eines Reinigungsmittels verzichtet.The metal wool mat according to the invention can be further improved after the acrylic treatment by providing it with a cleaning agent, in particular with soap. For the cleaning of soiled surfaces then only the addition of some water is required, so that the soap or detergent is effective. The user can thus dispense with the additional provision of a cleaning agent.

Zu der Erfindung gehört auch eine Metallwollematte als solche und insbesondere in der Form eines Reinigungspads, welches an einem Griffteil einer Reinigungsvorrichtung befestigt werden kann. Das Griffteil der erfindungsgemäßen Reinigungsvorrichtung kann aus einem relativ weichen und elastischen Schaumstoff bestehen, welcher besonders gut zur Aufnahme von Reinigungsflüssigkeit oder Wasser geeignet ist und außerdem aufgrund seiner Elastizität an alle denkbaren Konturen von zu reinigenden Oberflächen angepasst werden kann.The invention also includes a metal wool mat as such and in particular in the form of a cleaning pad which is attached to a handle part a cleaning device can be attached. The handle part of the cleaning device according to the invention may consist of a relatively soft and elastic foam, which is particularly well suited for receiving cleaning fluid or water and also can be adapted due to its elasticity to all conceivable contours of surfaces to be cleaned.

In einer bevorzugten Ausführungsform ist das Griffteil in Form eines Quaders ausgebildet, der einige Zentimeter Dicke, etwas mehr Breite und noch etwas mehr Länge aufweist. Das Griffteil kann aber auch aus härteren Materialien, insbesondere Gummi oder Kunststoff bestehen, die nicht so leicht verschleißen wie der weiche Schaumstoff und daher über einen längeren Zeitraum zur Reinigung verwendet werden könne. Dies ist insbesondere unter dem Aspekt der Nachhaltigkeit vorteilhaft. Für bestimmte Einsatzwecke ist es auch vorteilhaft, wenn das Griffteil aus härterem Material besteht. Selbstverständlich kann die Form des Griffteils an spezielle Aufgaben angepasst werden und daher, je nach der Form der zu reinigenden Oberfläche, verschiedenste Formen aufweisen.In a preferred embodiment, the grip part is designed in the form of a cuboid, which has a thickness of a few centimeters, a little more width and a little more length. But the handle can also be made of harder materials, especially rubber or plastic, which does not wear as easily as the soft foam and therefore could be used for a longer period for cleaning. This is particularly advantageous in terms of sustainability. For certain purposes, it is also advantageous if the handle is made of harder material. Of course, the shape of the handle can be adapted to specific tasks and therefore, depending on the shape of the surface to be cleaned, have a variety of shapes.

Ein Reinigungspad wird durch Ausschneiden aus einer Metallwollematte der weiter oben beschriebenen Art hergestellt und an die Form des Griffteils angepasst. Vorzugsweise ist das Reinigungspad rechteckig ausgestaltet, ggf. mit abgerundeten Ecken.A cleaning pad is made by cutting out of a metal wool mat of the type described above and adapted to the shape of the handle part. Preferably, the cleaning pad is rectangular, possibly with rounded corners.

Zur Befestigung kann das Griffteil mit dem Reinigungspad auf einfache Weise verklebt sein. Da aber das Griffteil bei der bestimmungsgemäßen Verwendung erfahrungsgemäß weniger schnell verschleißt als das Reinigungspad, empfiehlt sich eine Ausführungsform, bei der das Reinigungspad lösbar mit dem Griffteil verbunden ist. Dies hat den Vorteil, dass ein verschlissenes Reinigungspad vom Griffteil abgetrennt und das Griffteil dann mit einem frischen Reinigungspad versehen weiterbenutzt werden kann. Dieser Vorgang kann so lange wiederholt werden, bis auch das Griffteil verschlissen ist.For attachment, the handle part can be adhesively bonded to the cleaning pad in a simple manner. However, experience has shown that the grip part wears less quickly than the cleaning pad when used as intended, so an embodiment in which the cleaning pad is detachably connected to the grip part is recommended. This has the advantage that a worn cleaning pad can be separated from the grip part and the grip part then provided with a fresh cleaning pad. This process can be repeated until the handle is worn.

Eine lösbare Verbindung besteht vorzugsweise darin, dass das Griffteil mit einer Schicht aus Klettmaterial verbunden ist, an welchem das Reinigungspad angedrückt wird. Dabei entsteht eine relativ feste mechanische Verbindung zwischen dem Griffteil und dem Reinigungspad. Das Klettmaterial weist eine Vielzahl von kleinen Häkchen auf, die sich mit den Metallfasern des Reinigungspads verhaken und dieses somit festhalten. Das erfindungsgemäße Reinigungspad bietet dabei den Vorteil, dass die Metallfasern so fest miteinander verbunden sind, dass die mit den kleinen Häkchen des Klettmaterials verbundenen Fasern nicht aus dem Verbund der Metallwollematte herausgerissen werden. Ein besonderes Vlies oder textiles Trägermaterial, welches wie beim Stand der Technik zwischen der Metallwollematte und dem Klettmaterial angeordnet wäre, ist bei der erfindungsgemäßen Reinigungsvorrichtung nicht erforderlich.A releasable connection is preferably that the handle part is connected to a layer of Velcro material, on which the cleaning pad is pressed. This creates a relatively strong mechanical connection between the handle and the cleaning pad. The Velcro material has a plurality of small hooks, which hook with the metal fibers of the cleaning pad and thus hold this. The cleaning pad according to the invention offers the advantage that the metal fibers are so firmly connected to each other that the fibers connected to the small hooks of the hook and loop material are not torn out of the composite of the metal wool mat. A special fleece or textile carrier material, which would be arranged as in the prior art between the metal wool mat and the Velcro material is not required in the cleaning device according to the invention.

Statt eine Schicht aus Klettmaterial mit dem Griffteil zu verkleben oder sonst wie daran zu befestigen, kann das Klettmaterial mit Vorteil auch an das Griffteil angespritzt sein. Dabei wird in einem Arbeitsgang das Klettmaterial hergestellt und gleichzeitig mit dem Griffteil verbunden. Ein besonderer Arbeitsschritt zur Befestigung des Klettmaterials ist dabei nicht erforderlich, wodurch die Herstellungskosten der erfindungsgemäßen Reinigungsvorrichtung noch weiter verringert werden können.Instead of gluing a layer of Velcro material with the handle part or otherwise as to attach it, the Velcro material can be injected with advantage also to the handle part. The Velcro material is produced in one operation and connected simultaneously with the handle. A particular operation for fixing the Velcro material is not required, whereby the manufacturing cost of the cleaning device according to the invention can be further reduced.

Sollte ein spezielles Klettmaterial in Verbindung mit einem speziellen Metallwollematerial ausnahmsweise keine ausreichend feste Verbindung zwischen dem Reinigungspad und dem Griffteil gewährleisten, kann die Festigkeit der Verbindung dadurch verbessert werden, dass eine mit Kunststofffasern versehene Rückseite des Reinigungspads zur Befestigung am Klettmaterial des Griffteils dient. Die Kunststofffasern können auf einfache und kostengünstige Weise auf die Rückseite der Metallwollematte aufgesprüht werden. Dabei kann die Art der Kunststofffasern, insbesondere deren Dicke oder Elastizität noch besser an die kleinen Häkchen des Klettmaterials angepasst werden, um so eine optimale mechanische Verbindung zu gewährleisten.If a special Velcro material in connection with a special metal wool material exceptionally not ensure a sufficiently strong connection between the cleaning pad and the handle, the strength of the compound can be improved by a provided with plastic fibers back of the cleaning pads for attachment to the Velcro material of the handle. The plastic fibers can be sprayed on the back of the metal wool mat in a simple and cost-effective manner. In this case, the type of plastic fibers, in particular their thickness or elasticity can be better adapted to the small hooks of the Velcro material, so as to ensure an optimal mechanical connection.

Um die mit Kunststofffasern versehene Rückseite der Reinigungspads von der für Reinigungszwecke vorgesehenen Vorderseite noch leichter unterscheiden zu können, ist vorgesehen, dass die Kunststofffasern gegenüber der Metallwolle farblich kontrastierend ausgestaltet sind. So kann der Benutzer an der Farbe der jeweiligen Oberfläche erkennen, welche Seite zur Befestigung am Griffteil und welche zum Reinigung vorgesehen ist.In order to make it even easier to distinguish the rear side of the cleaning pads provided with synthetic fibers from the front side provided for cleaning purposes, it is provided that the plastic fibers are made to have a contrasting color in relation to the metal wool. Thus, the user can recognize the color of the respective surface, which side is provided for attachment to the handle part and which for cleaning.

Bei nicht mit Kunststofffasern versehenen Reinigungspads sind selbstverständlich beide Seiten für Reinigungszwecke geeignet und der Benutzer kann nach dem Verschleiß einer Seite das Reinigungspad abtrennen und die benutzte Seite am Griffteil befestigen, so dass die noch ungebrauchte frische Oberfläche für die weitere Reinigung verwendet werden kann.For cleaning pads not provided with plastic fibers, of course, both sides are suitable for cleaning purposes, and after wear of one side, the user can cut off the cleaning pad and attach the used side to the handle so that the still unused fresh surface can be used for further cleaning.

Ein Ausführungsbeispiel der Erfindung wird nachfolgend anhand der Zeichnungen näher erläutert. Die Figuren zeigen im Einzelnen.An embodiment of the invention will be explained in more detail with reference to the drawings. The figures show in detail.

1: eine erfindungsgemäße Metallwollematte während der Behandlung mit Acryl; 1 a metal wool mat according to the invention during the treatment with acrylic;

2: ein aus der erfindungsgemäßen Metallwollematte hergestelltes Reinigungspad; 2 a cleaning pad made from the metal wool mat of the invention;

3: eine erfindungsgemäße Reinigungsvorrichtung mit Griffteil und Reinigungspad. 3 : a cleaning device according to the invention with handle part and cleaning pad.

Nach der nicht gezeigten Herstellung von Metallfasern durch Abschaben der Metallfasern mittels eines Messers von einem Metalldraht oder einer Metallstange werden die Metallfasern zu einem länglichen Band geformt, welches mittels Walzen mechanisch verdichtet wird. Dabei entsteht eine Metallwollematte 1 mit ca. 50 cm Breite und ca. 3 mm Dicke.After the production of metal fibers, not shown, by scraping the metal fibers by means of a knife from a metal wire or a metal rod, the metal fibers are formed into an elongated band which is mechanically compacted by means of rolling. This creates a metal wool mat 1 about 50 cm wide and about 3 mm thick.

Diese Metallwollematte 1 wird in einer Behandlungsstation mit Acryl 2 behandelt. Das Acryl 2 wird auf Temperaturen zwischen 60°C und 200°C aufgeheizt und durch Düsen 3 gepresst, von wo es auf die Metallwollematte 1 aufgesprüht wird. Dabei werden die Metallfasern 4, von denen in 1 und 2 eine einzige exemplarisch mit dem Bezugszeichen 4 bezeichnet ist, mit dem Acryl 2 benetzt, welches beim Abkühlen erstarrt und die Metallfasern 4 fest miteinander verbindet. Bei Metallwollematten 1 mit geringer Metallfaserdichte wird eine geringere Temperatur von etwas über 60°C empfohlen, während bei Metallwollematten 1 mit höherer Metallfaserdichte eine höhere Temperatur in der Nähe von 200°C empfohlen wird. Statt durch Aufsprühen kann das Acryl auch je nach Temperatur und Düsengröße aufgedampft oder durch Einnebeln der Metallwollematte 1 in diese eingebracht werden.This metal wool mat 1 is in a treatment station with acrylic 2 treated. The acrylic 2 is heated to temperatures between 60 ° C and 200 ° C and through nozzles 3 from where it pressed on the metal wool mat 1 is sprayed on. In the process, the metal fibers become 4 of which in 1 and 2 a single example with the reference numeral 4 is designated with the acrylic 2 wetted, which solidifies on cooling and the metal fibers 4 firmly together. For metal wool mats 1 With low metal fiber density, a lower temperature of just over 60 ° C is recommended, while with metal wool mats 1 With higher metal fiber density a higher temperature near 200 ° C is recommended. Instead of spraying, the acrylic can also be vapor-deposited depending on the temperature and nozzle size or by misting the metal wool mat 1 be introduced into this.

Es wird mindestens eine Oberfläche der Metallwollematte 1 mit Acryl behandelt, also entweder die Vorderseite 5 oder die Rückseite 6. Vorzugsweise werden aber beide Seiten 5, 6 der Metallwollematte 1 mit Acryl 2 behandelt, so dass dieses von beiden Seiten in das Innere der Metallwollematte 1 eindringen und so seine verbindende Kraft zwischen den Metallfasern 4 über die gesamte Dicke der Metallwollematte 1 entfalten kann.There will be at least one surface of the metal wool mat 1 treated with acrylic, so either the front 5 or the back 6 , Preferably, however, both sides 5 . 6 the metal wool mat 1 with acrylic 2 treated so that this from both sides into the interior of the metal wool mat 1 penetrate and so its connecting force between the metal fibers 4 over the entire thickness of the metal wool mat 1 can unfold.

Zur Verbesserung der verbindenden Wirkung des Acryls 2 kann die Behandlung mit Acryl 2 wiederholt werden, ggf. mehrmals.To improve the connective effect of the acrylic 2 can the treatment with acrylic 2 be repeated, if necessary several times.

2 zeigt eine Reinigungspad 7, welches durch Ausschneiden aus einer Metallwollematte 1 gewonnen wurde. Das Reinigungspad hat eine Dicke von 3 mm, eine Breite und eine Länge von jeweils einigen Zentimetern, wobei eine rechteckige Form entsteht. Die unten liegende Vorderseite 5 des Reinigungspads 7 dient zur Reinigung und kann hierfür mit etwa Seife versehen sein, die in Verbindung mit Wasser aktiviert werden kann. Die Rückseite 6 des Reinigungspads 7 ist mit Kunststofffasern besprüht, die zur Verbesserung der Verbindung des Reinigungspads 7 mit einem Griffteil 8 dienen. Die Dichte der Kunststofffasern ist dabei nicht so hoch, dass ein Vlies oder eine trennende Schicht aus Kunststofffasern entsteht. Vielmehr werden nur so wenige Kunststofffasern aufgebracht, dass an der Oberfläche der Rückseite stets auch Metallfasern der Metallwollematte 1 vorhanden sind. 2 shows a cleaning pad 7 which by cutting out of a metal wool mat 1 was won. The cleaning pad has a thickness of 3 mm, a width and a length of a few centimeters each, creating a rectangular shape. The lower front 5 of the cleaning pad 7 is used for cleaning and may be provided with soap for this, which can be activated in conjunction with water. The backside 6 of the cleaning pad 7 is sprayed with plastic fibers, which improve the connection of the cleaning pad 7 with a handle part 8th serve. The density of the plastic fibers is not so high that a fleece or a separating layer of plastic fibers is formed. Rather, only so few plastic fibers are applied that on the surface of the back always metal fibers of the metal wool mat 1 available.

3 zeigt das genannte Griffteil 8, welches zusammen mit dem Reinigungspad 7 eine erfindungsgemäße Reinigungsvorrichtung 9 bildet. Das Griffteil hat die Form eines Quaders mit einigen Zentimetern Dicke, etwas größerer Breite und noch etwas größerer Länge. Das Griffteil 8 ist mit einer Schicht aus Klettmaterial 10 verklebt. Das Klettmaterial kann aber in einer alternativen Ausführungsform auch an das Griffteil 8 direkt angespritzt werden. 3 shows the said handle part 8th , which together with the cleaning pad 7 a cleaning device according to the invention 9 forms. The handle has the shape of a cuboid with a few centimeters thick, slightly larger width and a little larger length. The handle part 8th is with a layer of Velcro material 10 bonded. The Velcro material can but in an alternative embodiment also to the handle part 8th be sprayed directly.

Als Klettmaterial 10 sind insbesondere die unter den Handelsnamen „Velcro” und „Aplix” bekannten Materialien geeignet.As Velcro material 10 In particular, the materials known by the trade names "Velcro" and "Aplix" are suitable.

Das Reinigungspad 7 ist mit seiner Rückseite 6 an dem Klettmaterial 10 befestigt, wobei die auf der Rückseite 6 aufgespritzten Kunststofffasern mit dem Miniaturhäkchen des Klettmaterials 10 besonders gut verhaken. Um die Vorderseite 5 des Reinigungspads 7 von seiner mit Kunststofffasern versehenen Rückseite 6 unterscheiden zu können, sind die Kunststofffasern in einer anderen Farbe eingefärbt als die Metallfasern der Metallwollematte 1 des Reinigungspads 7.The cleaning pad 7 is with his back 6 on the Velcro material 10 attached, with the ones on the back 6 sprayed plastic fibers with the miniature hook of the Velcro material 10 hooked particularly well. To the front 5 of the cleaning pad 7 from its backside provided with plastic fibers 6 To be able to distinguish, the plastic fibers are dyed in a different color than the metal fibers of the metal wool mat 1 of the cleaning pad 7 ,

ZITATE ENTHALTEN IN DER BESCHREIBUNG QUOTES INCLUDE IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list of the documents listed by the applicant has been generated automatically and is included solely for the better information of the reader. The list is not part of the German patent or utility model application. The DPMA assumes no liability for any errors or omissions.

Zitierte PatentliteraturCited patent literature

DE 10233670 A1 [0002]

Claims

Method for producing a metal wool mat ( 1 ) for cleaning purposes, in which metal fibers ( 4 ) are combined to metal wool and the metal wool mechanically to a metal wool mat ( 1 ) is compacted, preferably by rolling to a few millimeters thickness characterized in that the metal wool mat ( 1 ) Acrylic ( 2 ) is added.

Process according to claim 1, characterized in that the acrylic ( 2 ) has a temperature between 60 ° C and 200 ° C.

Process according to claim 2, characterized in that the acrylic ( 2 ) in metal wool mats ( 1 ) lower metal fiber density at a lower temperature and metal wool mats ( 1 ) higher metal fiber density with higher temperature is added.

Method according to one of the preceding claims, characterized in that the acrylic ( 2 ) by spraying, evaporating or misting at least one surface of the front side ( 5 ) or the back ( 6 ) of the metal wool mat ( 1 ) is supplied.

A method according to claim 4, characterized in that the acrylic from the front ( 5 ) or the back ( 6 ) of the metal wool mat ( 1 ) is supplied to its two surfaces.

Method according to one of the preceding claims, characterized in that the treatment of the metal wool mat ( 1 ) with acrylic ( 2 ) is repeated at least once.

Method according to one of the preceding claims, characterized in that the metal wool mat ( 1 ) after the acrylic treatment on its backside ( 6 ) is sprayed with plastic fibers.

Method according to one of the preceding claims, characterized in that the metal wool mat ( 1 ) after the acrylic treatment with a cleaning agent, in particular soap is provided.

Metal wool mat, characterized in that compacted metal wool with acrylic ( 2 ), which is the metal fibers ( 4 ) of the metal wool mat ( 1 ) connects to each other.

Metal wool mat according to claim 9, characterized in that its rear side ( 6 ) is provided with plastic fibers.

Metal wool mat according to claim 9 or 10, characterized in that it is provided with a cleaning agent, preferably with soap.

Cleaning device with a handle part ( 8th ) and one on the handle part ( 8th ), preferably rectangular cleaning pad ( 7 ), characterized in that the cleaning pad ( 7 ) from one to the handle part ( 8th ) adapted section of a metal wool mat ( 1 ) according to one of the preceding claims.

Cleaning device according to claim 12, characterized in that the handle part ( 8th ) is configured substantially in the shape of a cuboid with a few centimeters in thickness.

Cleaning device according to claim 12 or 13, characterized in that the cleaning pad ( 7 ) with the handle part ( 8th ) is glued.

Cleaning device according to one of claims 12 to 14, characterized in that the handle part ( 8th ) with a layer of Velcro material ( 10 ) connected is.

Cleaning device according to claim 15, characterized in that the Velcro material ( 10 ) to the handle part ( 8th ) is injected.

Cleaning device according to claim 15 or 16, characterized in that a rear side provided with plastic fibers ( 6 ) of the cleaning pad ( 7 ) for attachment to the Velcro material ( 10 ) of the grip part ( 8th ) serves.

Cleaning device according to claim 17, characterized in that the plastic fibers are opposite the metal wool ( 1 ) are designed in contrasting colors.