DE1414803C - Method and device for the extrusion or transfer molding of anisotropic flexible permanent magnetic strips

Info

Publication number: DE1414803C
Authority: DE
Inventors: Robert Edward Ma rietta Ohio Schornstheimer (V St A)
Original assignee: The B F Goodrich Company, Akron, Ohio (V St A )
Publication date: 1971-06-03

Description

1 21 2

Die Erfindung betrifft ein Verfahren und eine in verstärktem Maße in die gewünschte Orientierung Vorrichtung zum Strang- oder Spritzpressen von gedreht werden. Diese Orientierung verläuft parallel anisotropen biegsamen Dauermagneten mit recht- zu der größten Fläche des fertigen Dauermagneteckigem Querschnitt aus in einem biegsamen Binde- Streifens. The invention relates to a method and to a greater degree in the desired orientation Device for extrusion or transfer molding to be rotated. This orientation is parallel anisotropic flexible permanent magnets with right - to the largest area of the finished permanent magnet - angular cross-section in a flexible binding strip.

mittel eingelagerten, plättchenförmigen dauermagne- 5 Zur weiteren Verbesserung der magnetischen tischen Eindomänenteilchen. Es ist bekannt, derartige Eigenschaften kann der Streifen vor dem Magnetisiebiegsame Streifen durch Walzen, Spritzpressen oder ren zur weiteren Verringerung seiner kleineren AbStrangpressen zu erzeugen. Durch die dabei auftre- messung durch Preßwalzen geführt und gewalzt tenden mechanischen Kräfte werden die eine platt- werden.medium embedded, platelet-shaped permanent mag- 5 To further improve the magnetic single-domain particles. It is known that such properties can be achieved by the strip before it is magnetically flexible Strip by rolling, transfer molding or rening to further reduce its smaller size extrusion to create. As a result of the impingement measurement, it is guided and rolled through the press rollers Mechanical forces will tend to flatten them.

chenförmige Gestalt aufweisenden dauermagneti- io Gegenstand der Erfindung ist weiter eine Strang-Chen-like shape having permanent magnet io the subject of the invention is further a strand

schen Teilchen im wesentlichen parallel zu den die oder Spritzpreßdüse zum Durchführen des geschil-rule particles essentially parallel to the die or injection molding nozzle for carrying out the schil-

Druckeinwirkung ausübenden Flächen ausgerichtet; derten Verfahrens.Pressure applied surfaces aligned; the other procedure.

anschließend werden sie in einer bevorzugten Magne- Diese Düse ist erfindungsgemäß gekennzeichnet tisierungsrichtung senkrecht zu den Plättchenebenen durch einen zusammenhängenden Körper mit Einmagnetisiert. 15 und Austrittsöffnungen mit im wesentlichen recht-Derartige durch die elastomeren Bindemittel bieg- eckigen, unter sich etwa gleichen, zueinander etwa samen Magnete ergeben nur geringe Magnetkräfte, senkrecht stehenden Querschnitten, die jeweils eine die im allgemeinen geringer sind als diejenigen eines kleine und dazu senkrechte große Seite aufweisen Magneten gleicher Größe, der ohne Bindemittel derart, daß die große Seite der Eintrittsöffnung etwa hergestellt und beispielsweise ein keramischer ge- ao parallel zur kleinen Seite der Austrittsöffnung und sinterter Magnet ist. umgekehrt die kleine Seite der Eintrittsöffnung etwa ) Diese geringen Magnetkräfte resultieren im wesent- parallel zur großen Seite der Austrittsöffnung verliehen daraus, daß ζ. B. in einer Strangpreßform, die läuft und beide Querschnitte durch glatte Wandungen lediglich eine einfache Rechtecköffnung aufweist, allmählich und im wesentlichen unter Konstanthalderen größere Ausdehnung breit ist, in der Nähe der 35 tung des Gesamtquerschnitts ineinander übergehen, größeren Ausdehnung das aus dem rohrförmigen In der Zeichnung sind Ausführungsbeispiele einer Mundstück des Extruders austretende Material nahe- Preßeinrichtung und einer Preßdüse zum Durchzu keine Verformung erfährt, sondern praktisch un- führen des Verfahrens dargestellt. Es zeigt
behindert die Strangpreßform durchfließt. Daher . Fig. 1 in schematischer Darstellung in Seitenergibt sich mit einer solchen einfachen Rechteckform 30 ansieht eine Preßeinrichtung zum Durchführen des in diesem mittleren Bereich nur eine verhältnismäßig erfindungsgemäßen Verfahrens,
geringe Orientierung der magnetischen Teilchen, die F i g. 2 eine Ansicht der Einlaßöffnung einer Preßauf alle Fälle geringer ist als an den beiden Rand- düse,They are then magnetized in a preferred magnetization direction perpendicular to the platelet planes by a coherent body with magnetization. 15 and outlet openings with essentially right-like magnets, which are bendable through the elastomeric binding agent, are approximately equal to one another and approximately identical to one another, result in only low magnetic forces, perpendicular cross-sections, each of which is generally smaller than that of a small and perpendicular one large side have magnets of the same size, which are made without binding agent in such a way that the large side of the inlet opening is approximately produced and, for example, a ceramic magnet that is ao parallel to the small side of the outlet opening and is sintered. vice versa the small side of the inlet opening for example) These low magnetic forces result essentially parallel to the large side of the outlet opening from the fact that ζ. B. in an extrusion mold that runs and both cross-sections through smooth walls only has a simple rectangular opening, gradually and substantially under Konstanthalderen larger expansion is wide, in the vicinity of the 35 direction of the total cross-section merge, larger expansion from the tubular In the The drawing shows exemplary embodiments of a material exiting the mouthpiece of the extruder - pressing device and a pressing nozzle for passing through no deformation, but rather a practical illustration of the method. It shows
hinders the extrusion form flowing through. Hence . Fig. 1 shows a schematic representation in pages with such a simple rectangular shape 30 shows a pressing device for carrying out the method according to the invention, which is only one relatively in this central area,
poor orientation of the magnetic particles shown in FIG. 2 a view of the inlet opening of a press is in any case smaller than at the two edge nozzles,

bezirken, in denen eine stärkere Verformung des F i g. 3 den Längsschnitt nach Linie 3-3 der F i g. 2,districts in which a greater deformation of the F i g. 3 shows the longitudinal section along line 3-3 of FIG. 2,

Materials und damit auch die gewünschte Orientie- 35 F i g. 4 den Längsschnitt nach Linie 4-4 der F i g. 2,Materials and thus also the desired orientation 35 F i g. 4 shows the longitudinal section along line 4-4 of FIG. 2,

rung erreicht werden kann. Bei der Magnetisierung F i g. 5 eine Ansicht der Austrittsöffnung der intion can be achieved. With the magnetization F i g. 5 shows a view of the outlet opening of the FIG

in der bevorzugten Richtung senkrecht zu den Platt- den F i g. 2 bis 4 gezeigten Preßdüse undin the preferred direction perpendicular to the plates F i g. 2 to 4 shown compression nozzle and

chenebenen lassen sich daher nur geringe Magnet- F i g. 6 eine der F i g. 5 entsprechende Ansicht mitsurface planes can therefore only be small magnetic F i g. 6 one of the F i g. 5 corresponding view with

kräfte erreichen. der Darstellung einer etwas abgewandelten Austritts-achieve strength. the representation of a slightly modified exit

Der Hauptzweck der vorliegenden Erfindung be- 40 Öffnung.The main purpose of the present invention is opening.

steht darin, die Ebenen der im allgemeinen plättchen- Für das Verfahren und die Vorrichtung nach deiit states the levels of the generally platelet For the method and apparatus according to dei

oder streifenartigen Magnetpartikelchen innerhalb Erfindung sind alle dauermagnetischen Werkstoffeor strip-like magnetic particles within the invention are all permanent magnetic materials

der plastischen elastomeren Werkstoffe besser als bei geeignet, deren Teilchen nach Zerkleinerung auf Ein-plastic elastomeric materials are better suited than those whose particles after comminution

den bekannten Verfahren parallel zueinander aus- domänengröße eine plättchenförmige Gestalt mitthe known methods have a platelet-like shape parallel to one another from domain size

zurichten und das in einer Weise, welche das fort- 45 einer senkrecht zur Plättchenebene liegenden magne-and in such a way that the continued 45 of a magnetic lying perpendicular to the plane of the

laufcndc Herstellen solcher Magnete in wirtschaft- tischen Vorzugsrichtung aufweisen, beispielsweise derRunning the production of such magnets in an economically preferred direction, for example the

licher Weise gewährleistet, hexagonal kristallisierende Werkstoff BariumferritLicher way guaranteed, hexagonally crystallizing material barium ferrite

Das erfindungsgemäße Verfahren zum Strang- oder nach Zerkleinerung auf eine Korngröße von etwaThe inventive method for strand or after comminution to a grain size of about

Spritzpressen von anisotropen biegsamen Dauer- 0,7 bis 4 μτη. Dieser feinverteilte dauermagnetischeInjection molding of anisotropic flexible continuous 0.7 to 4 μτη. This finely divided permanent magnetic

magnetstreifen besteht darin, daß mit dem Ausgangs- 50 Werkstoff wird durch ein elastomeres BindemittelMagnetic strip consists in the fact that the starting material is 50 with an elastomeric binding agent

gemisch aus einem elastomercn Bindemittel und darin zusammengehalten, welches aus einem natürlichenMixture of an elastomeric binder and held together in it, which consists of a natural

eingemischten dauermagnetischen plättchenförmigen oder synthetischen Gummi, Polyvinylacetat, PoIy-mixed in permanent magnetic platelet-shaped or synthetic rubber, polyvinyl acetate, poly-

Eindomänenteilchcn in der Preßdüse zunächst ein vinylchlorid, Polyäthylen oder einem anderen ge-Single-domain particles in the press nozzle initially contain a vinyl chloride, polyethylene or another

Strcifcn mit rcchteckförmigcm Querschnitt geformt eigneten Stoff besteht. Der Einfachheit halber sollStrcifcn with a rectangular cross-section shaped suitable material consists. For simplicity should

und dieser anschließend unter Konstanthaltung der 55 die Erfindung unter Zugrundelegung der Verwendungand this then, keeping constant 55, the invention based on the use

Qucrschniltsfläche derart verformt wird, daß die eines plastisch gemachten Polyvinylchlorids alsCross-sectional area is deformed so that that of a plasticized polyvinyl chloride as

ursprünglich größere Abmessung des Querschnitts Bindemittel für die fcinverteiltcn Magnctpartikelchcnoriginally larger dimension of the cross-section of the binder for the distributed magnetic particles

allmählich so lange verringert und die ursprünglich beschrieben werden, welche 90 % oder weniger desgradually decreased as long and the originally described, which 90% or less des

kleinere Abmessung gleichzeitig allmählich so lange Gesamtgewichts der Mischung ausmachen. Es wirdsmaller dimension at the same time gradually making up the total weight of the mixture as long. It will

vergrößert wird, bis ein Streifen mit rcchtcckför- 60 besonders darauf aufmerksam gemacht, daß die Eris enlarged until a strip with reverse feed 60 particularly draws attention to the fact that the he

migem Querschnitt von vertauschtem Seitenverhältnis findung keinesfalls auf die Verwendung von PoIy-medium cross-section with an interchanged aspect ratio, the use of poly-

entstanden ist, und daß dieser Streifen anschließend vinylchlorid als Bindemittel und auf die angegebenehas arisen, and that this strip then vinyl chloride as a binder and on the specified

durch ein senkrecht zur größten Fläche gerichtetes Menge der zugemischten Magnetpartikelchen be-by an amount of the mixed magnetic particles directed perpendicular to the largest surface

Magnctfuld magnetisiert wird. schränkt ist.Magnctfuld is magnetized. is restricted.

Dadurch ergibt sich ein Ausgleich der bei den 65 TJm biegsame Magnete aus fcinvcrtciltcm Barium-This compensates for the flexible magnets made of barium

bekannten Verfahren ungleichmäßigen Verformung ferrit und Polyvinylchlorid als Bindemittel hcrzustcl-known methods uneven deformation ferrite and polyvinyl chloride as binders hcrstcl-

des Materials durch ein stärkeres Durcharbeiten des len, werden diese Werkstoffe in geeigneter Weise mitof the material by working through the len more intensely, these materials are appropriately dealt with

Pulvcrgcmischs, wodurch die magnetischen Teilchen Hilfe üblicher Vorrichtungen zusammengemischt.Powder mixing, whereby the magnetic particles are mixed together using conventional devices.

z.B. mit Hilfe einer Mühle, die zum Zusammenmischen von Gummi und Kunststoffen benutzt wird. Dieses Gemisch wird anschließend in eine übliche Strang- oder Spritzpreßvorrichtung eingefüllt, die in F i g. 1 mit 10 bezeichnet ist. Das Pulvergemisch wird durch den Einfülltrichter 11 dieser Vorrichtung eingegeben und mittels der im Gehäuse 12 eingebauten, nicht sichtbaren Strangpreßschnecke durch eine Preßdüse 14 als Strang ausgepreßt.e.g. with the help of a mill that is used to mix rubber and plastics. This mixture is then poured into a conventional extrusion or transfer molding device, which in F i g. 1 is denoted by 10. The powder mixture is introduced through the funnel 11 of this device and by means of the not visible extrusion screw built into the housing 12 through a compression nozzle 14 pressed out as a strand.

In den üblichen Strangpreßvorrichtungen ist die Ausbildung der Preßdüse 14 so gewählt, daß dem Pulvergemisch unmittelbar die gewünschte Querschnittsform des austretenden Stranges gegeben wird. Weiter oben wurde ausgeführt, daß auf diese Weise die dauermagnetischen Teilchen innerhalb des austretenden Stranges nur unbedeutend ausgerichtet sind und daher die Magnetkraft etwa begrenzt ist durch den prozentualen Gewichtsanteil an Magnetmaterial, welches von dem plastischen Bindemittel ohne nachteilige Verringerung der Biegsamkeit und Festigkeit des Stranges aufgenommen werden kann.In the usual extrusion devices, the formation of the extrusion nozzle 14 is chosen so that the Powder mixture is given immediately the desired cross-sectional shape of the emerging strand. Above it was stated that in this way the permanent magnetic particles within the exiting Strand are only insignificantly aligned and therefore the magnetic force is approximately limited by the percentage by weight of magnetic material, which from the plastic binder without disadvantageous Reduction in flexibility and strength of the strand can be added.

Mit der Erfindung wird die gewünschte Orientierung der magnetischen Partikelchen in einem wesentlich größeren Umfang zustandegebracht, als dies bisher mit üblichen Strangpreßformen erreicht werden konnte, weil das Material während des Durchlaufs durch die Strangpreßform veranlaßt wird, nacheinander eine Lage einzunehmen, in welcher die größten Dimensionen allgemein mit dem Fortschreiten der Durchgangsbewegung ausgerichtet werden und in Lagen parallel mit den oberen und unteren Flächen des Strangpreßlings gelangen. Zu diesem Zweck besitzt die Form 14 eine Eintrittsöffnung mit im allgemeinen Rechteckform, wie F i g. 2 zeigt, wobei die Seitenerstreckungen ungleich sind und die größere Seitenerstreckung vorzugsweise mehrmals größer als die der kleinen Seite ist. Die Austrittsöffnung 16 der Form 14 besitzt gleichfalls Rechteckform, jedoch mit Abmessungen im umgekehrten Verhältnis zu denjenigen der Eintrittsöffnung 15. Das bedeutet, daß. wenn die größere Erstreckung der Eintrittsöffnung in Fig. 2 in der Höhenrichtung liegt, die größere Erstreckung der Austrittsöffnung unter einem rechten Winkel dazu und somit in der Breite jener öffnung liegt. Umgekehrt stimmt die kleine Dimension oder Breite der Eintrittsöffnung mit der Höhe der Austrittsöffnung überein. Diese Eintritts- und Ausrittsöffnungen der Form sind durch einen gleichförmigen und stoßfrei verlaufenden Materialdurchgangskarial in der Form mit überall etwa gleicher Querschnittsgröße verbunden. With the invention, the desired orientation of the magnetic particles becomes essential in one brought about greater scope than has previously been achieved with conventional extrusion molds because the material is caused to pass through the extrusion die, sequentially to occupy a position in which the greatest dimensions generally increase with the advancement of the Continuous motion will be aligned and in layers parallel with the top and bottom surfaces of the extrusion arrive. For this purpose, the mold 14 has an inlet opening with generally Rectangular shape, like F i g. 2 shows, the side extensions being unequal and the greater Side extension is preferably several times greater than that of the small side. The outlet opening 16 of the Form 14 also has a rectangular shape, but with dimensions in inverse proportion to those of the inlet opening 15. This means that. if the larger extension of the inlet opening in Fig. 2 is in the vertical direction, the greater extent of the outlet opening below a right Angle to it and thus in the width of that opening. Conversely, the small dimension or is correct The width of the inlet opening corresponds to the height of the outlet opening. These entry and exit openings of the shape are through a uniform and seamless material passage carial connected in shape with approximately the same cross-sectional size everywhere.

Die im Ausführungsbeispiel einstückig dargestellte Form 14 kann auch aus mehreren Teilen bestehen, welche auswechselbar zusammengesetzt sein können, wie dies bei üblichen Strangpreßformen bekannt ist.The form 14 shown in one piece in the exemplary embodiment can also consist of several parts, which can be interchangeably assembled, as is known in conventional extrusion molds.

Die Wirkung der Verwendung einer in den Fi g. 2 bis 5 dargestellten und bei einer Strangpreßvorrichtung 10 verwendeten Preßdüse bei dem gekennzeichneten Material besteht darin, daß das Ausgangsgemisch in dem in jedem Querschnitt rcchteckförmigcn Hohlraum der Preßdüse von einer Stärke, die mehrmals größer ist als die endgültige Stärke, allmählich furtschreitend gestreckt und während des Durchgangs durch die Form auf größere Breite gebracht wird. Da das die Partikelchen zusammenhaltende Bindemittel elastomerer Natur ist, erlaubt es eine relative Bewegung der plüttchcnförmigen Partikelchen. Die Verengungsbewegimg innerhalb der Preßdüse bewirkt, daß jedes der plattenförmigen Dauermagnetteilchen, deren Ebenen normalerweise regellos verteilt gerichtet sind, allmählich so einschwenkt, bis ihre Ebenen am Austrittsende der Preßdüse im wesentlichen parallel zueinander und zu den beiden größeren Flächen des Dauermagnetstreifens stehen. Da die magnetische Vorzugsrichtung der Dauermagnetteilchen nach Art des Bariumferrits senkrecht zur Plättchenebene steht, wird der aus derThe effect of using one of the Figs. 2 to 5 shown and in an extrusion device 10 used compression nozzle in the marked material is that the starting mixture in the rectangular in each cross-section Cavity of the die of a thickness several times greater than the final thickness, gradually Strengthened as you walk and made wider during the passage through the form will. Since the binder holding the particles together is of an elastomeric nature, it allows a relative movement of the platelet-shaped particles. The narrowing movement within the Compression nozzle causes each of the plate-shaped Permanent magnet particles, the planes of which are normally directed randomly distributed, gradually swiveled in until their planes at the exit end of the Compression nozzle essentially parallel to each other and to the two larger surfaces of the permanent magnet strip stand. Because the preferred magnetic direction of the permanent magnet particles is like barium ferrite is perpendicular to the plane of the platelets, the

ίο Preßdüse ausgetretene Dauermagnetstreifen durch ein senkrecht zu seinen beiden größeren Flächen gerichtetes Magnetfeld aufmagnetisiert.ίο leaked permanent magnetic strips through the press nozzle magnetized by a magnetic field directed perpendicular to its two larger surfaces.

Die Magnetkraft eines solchen biegsamen Magneten ist im Vergleich zu der eines aus dem gleichen Magnetwerkstoff und mit dem gleichen Querschnitt durch Strangpressen mittels einer Preßdüse bekannter Art erzeugten Magneten günstiger, weil die Ausrichtung der Dauermagnetteilchen wesentlich vollständiger erfolgt als bei den bekannten biegsamenThe magnetic force of such a flexible magnet is compared to that of one of the same Magnetic material and magnets produced with the same cross-section by extrusion by means of a compression nozzle of a known type cheaper because the alignment the permanent magnet particles take place much more completely than with the known flexible ones

ao Magneten, bei denen die Plättchenebenen der Teilchen gegenüber den Flächen des Stranges teilweise noch regellos geneigt sind.ao magnets, in which the platelet planes of the particles are partially inclined towards the surfaces of the strand at random.

Die Ausrichtung der Partikelchen und daher die Kraft des sich ergebenden Magneten kann weiter dadurch gesteigert werden, daß der aus einer erfindungsgemäßen Preßdüse austretende Streifen der Einwirkung eines oder mehrerer Paare zusammenwirkender Walzen ausgesetzt wird, welche die Dicke des Streifens vermindern, ohne dabei vor den Stirnflächen der Walzen einen dammartigen Aufwurf zu bilden. Dieses Auswalzen kann durchgeführt werden, solange der Streifen warm ist oder auch in kaltem Zustand und kann daher entweder unmittelbar im Anschluß an den Austritt aus der Preßdüse oder auch später durchgeführt werden. Die Wirkung der Walzen besteht darin, die plättchenförmigen Dauermagnetteilchen noch besser in parallele Lage mit den gegenüberliegenden Flächen des gepreßten Streifens zu bringen und damit die bereits in der Preßdüse begonnene Ausrichtung zu vervollständigen. Weiter werden durch diese Behandlung die plättchenförmigen Teilchen noch stärker aneinandergepreßt, was in Zusammenwirkung mit der Ausrichtung zu einer Vergrößerung der Magnetkraft des gepreßten Streifens führt.The orientation of the particles and therefore the force of the resulting magnet can be further thereby be increased that the emerging from a compression nozzle according to the invention strip of The action of one or more pairs of co-operating rollers is subjected to the thickness of the strip without causing a dam-like throw in front of the end faces of the rollers form. This rolling out can be carried out while the strip is warm or cold State and can therefore either immediately after the exit from the press nozzle or also to be done later. The action of the rollers is to remove the platelet-shaped permanent magnet particles even better in parallel with the opposite faces of the pressed strip to bring and thus to complete the alignment already begun in the press nozzle. Continue the platelet-shaped particles are pressed together even more strongly by this treatment, which in conjunction with the alignment leads to an enlargement the magnetic force of the pressed strip.

Die in Fig. 1 dargestellte Vorrichtung zeigt ein Paar zusammenwirkender Walzen 17, welche die Dicke des aus der erfindungsgemäßen Strangpreßform austretenden gepreßten Streifens vermindern.The device shown in Fig. 1 shows a Pair of cooperating rollers 17, which the thickness of the extrusion mold according to the invention reduce escaping pressed strip.

Selbstverständlich können mehr als ein Paar solcher Walzen vorgesehen werden, falls dies gewünscht oder erforderlich ist. Es ist weiter möglich, daß dann, wenn die endgültige Dicke des aus der Strangpreßform austretenden Preßstreifens geringer ist als im späteren Magneten gefordert wird, zwei oder mehrere derartige gepreßte Streifen mit oder ohne Verwendung eines geeigneten Lösungs- oder Bindemittels zwischen Walzcnpaaren zusammengewalzt werden können.Of course, more than one pair of such rollers can be provided if desired or is required. It is further possible that when the final thickness of the die is from the extrusion die exiting press strip is less than is required in the later magnet, two or more such pressed strips with or without the use of a suitable solvent or binder can be rolled together between pairs of rollers.

Der aus den Walzen austretende Streifen kann unmittelbar durch eine Magnetisierungsvorrichtung 18 geführt werden, in welcher der Streifen unter einem rechten Winkel zu seiner Oberfläche magnetisiert wird. Diese Magnetisierung wird vorzugsweise durch-The strip emerging from the rollers can be passed directly through a magnetization device 18 in which the strip magnetizes at a right angle to its surface will. This magnetization is preferably carried out by

geführt, wenn der Streifen kurzzeitig stillsteht, ohne daß dadurch eine Behinderung der laufenden Fertigung eintritt. Um dies zustandezubriiigen, ist der Magnetisierungsapparat 18 vorzugsweise so aiisgcbil-if the strip stands still for a short time without that this hinders ongoing production. In order to achieve this, the Magnetization apparatus 18 preferably so designed

dct, daß sich das erforderliche Magnetfeld in einem Bruchteil einer Sekunde aufbringen läßt, wozu ein Magnetisierungsapparat mit Kondensatorentladung benutzt werden kann, welcher im Handel erhältlich ist und daher nicht im einzelnen beschrieben zu werden braucht. Es ist nicht nötig, die Magnetisierung unmittelbar auszuführen, nachdem der zu magnetisierende Streifen seine endgültige Form erhalten hat. Die Magnetisierung kann auch später, nach beliebiger Zeit, dadurch durchgeführt werden, daß der Streifen einem entsprechend starken Magnetfeld in der obengenannten Richtung ausgesetzt wird.dct that the required magnetic field is in a Can be applied for a fraction of a second, including a magnetization apparatus with capacitor discharge which is commercially available and therefore need not be described in detail needs. It is not necessary to carry out the magnetization immediately after the one to be magnetized Strip has received its final shape. The magnetization can also be done later, after any Time to be carried out by the fact that the strip has a correspondingly strong magnetic field in the above Direction is suspended.

Der kurzzeitige Stillstand des Streifens während der Magnetisierung kann durch beliebige Maßregeln ohne Unterbrechung der fortlaufenden Herstellung aus der Strangpreßvorrichtung bzw. den Walzen bewirkt werden. Beispielsweise kann ein genügender Abstand zwischen den Walzen 17 und dem Magnetisierungsappart 18 vorgesehen sein, so daß sich eine Mateiialschleife während des kurzzeitigen Anhaltens des Materials im Magnetisierungsapparat bilden kann, wobei der Transport des Streifens durch den Magnetisierungsapparat durch geeignete Antriebsrollen erfolgt, welche durch die Schaltzeiten des Magnetisierungsapparates gesteuert werden.The brief standstill of the strip during the magnetization can be done by any measures without interrupting the continuous production from the extrusion device or the rollers will. For example, there can be a sufficient distance between the rollers 17 and the magnetization apparatus 18 may be provided so that a Mateiialschleife during the brief stop of the material in the magnetization apparatus, the transport of the strip through the The magnetization apparatus is carried out by means of suitable drive rollers, which are determined by the switching times of the magnetization apparatus being controlled.

Es ist für die Erfindung nicht wesentlich, daß der Querschnitt der Austrittsöffnung der Preßform ein einfaches Rechteck ist. Es kann auch eine Ausbildung vorgesehen werden, welche die Form eines abgeflachten U-Profils bildet, wie dies beispielsweise der Querschnitt der Austritlsöffnung 19 der in Fig. 6 dargestellten Prcßdüsc 20 zeigt. Auch andere Rechteckformen sind denkbar, wie sie aus der gewünschten Form des endgültigen Magneten resultieren. Weiter braucht die Austrittsöffnung nicht die genaue bzw. endgültige Form des stranggepreßten Streifens zu erzeugen. Es können beispielsweise geeignete Druckplatten oder Rollen anschließend an die Strangpreßform 14 angebaut sein, um den Dauermagnetstreifen in die gewünschte Querschnittsform zu bringen, sobald ei aus der Strangpreßvorrichtung ausgetreten ist. Es wird dabei daran erinnert, daß das Bindemittel für die Magnctpartikclchcn sich beim Austritt aus der Stranupreßforni noch im plastischen Zustand befindet und daher leicht weiter verformt werden kann.It is not essential for the invention that the cross section of the outlet opening of the mold is a is simple rectangle. A design can also be provided which has the shape of a flattened U-profile forms, as is the case, for example, the cross-section the outlet opening 19 of the press nozzle 20 shown in FIG. Other rectangular shapes too are conceivable as they result from the desired shape of the final magnet. Next needs the exit opening does not produce the exact or final shape of the extruded strip. For example, suitable pressure plates or rollers can then be attached to the extrusion mold 14 be attached to bring the permanent magnet strip into the desired cross-sectional shape as soon as ei has emerged from the extruder. It is remembered that the binder for the Magnetic particles are still in the plastic state when they exit the Stranuprßforni and can therefore easily be further deformed.

Die Erfindung ist beschrieben worden an Hand der Herstellung von langgestreckten, biegsamen Magneten aus mit Polyvinylchlorid gebundenen plättchenförmigen Bariumferritteilchen. Die Erfindung ist nicht auf die Benutzung dieser Werkstoffe beschränkt. Außerdem ist es nicht in allen Fällen notwendig, daß unmittelbar anschließend an den Austritt des Streifens aus der erfindungsgemäßen Preßdüse die weitere Reduzierung der Dicke durch zusammenwirkende Walzen erfolgt. Diese Art der Kombination der Behandlung ist lediglich eine bevorzugte Ausbildungsform. Es ist klar, daß an Stelle der Verwendung von Walzen zur Verbesserung der Ausrichtung der Partikelchen diese Ausrichtung auch durch Vergrößerung der Länge der Preßdüsc erreicht werden kann.The invention has been described with reference to the manufacture of elongated, flexible magnets made of platelet-shaped barium ferrite particles bound with polyvinyl chloride. The invention is not limited to the use of these materials. In addition, it is not necessary in all cases that immediately following the exit of the strip from the press nozzle according to the invention the further one Reduction of the thickness takes place through interacting rollers. This type of combination treatment is only a preferred form of training. It is clear that instead of using Rollers to improve the alignment of the particles this alignment also by magnification the length of the press nozzle can be achieved.

so daß die einzelnen Partikelchen eine längere Durchgangszeit durch die Düse und damit eine längere Zeitspanne zum Erreichen der gewünschten Ausrichtung haben. An Stelle von Walzen können auch andere Preßeinrichtungen benutzt werden, die einenso that the individual particles have a longer transit time through the nozzle and thus a longer period of time to achieve the desired orientation to have. Instead of rollers, other pressing devices can be used, the one

ίο die Dicke vermindernden Preßdruck ausüben können.ίο can exert pressure reducing the thickness.

Claims

Patent claims:

* 5 1. Extrusion or transfer molding process

of anisotropic flexible permanent magnetic strips with a rectangular cross-section in one flexible binder embedded, platelet-shaped permanent magnetic single-domain particles, which are aligned by mechanical forces so that one perpendicular to the largest surface lying magnetic preferred direction is created, characterized in that in the Press nozzle first a strip with rectangular

»5 mm cross-section formed and this afterwards while keeping the cross-sectional area constant is deformed in such a way that the originally larger dimension of the cross-section gradually reduced so long and the original smaller dimension is gradually increased at the same time until a stripe with rectangular cross-section of reversed aspect ratio was created, and that this The strip is then magnetized by a magnetic field directed perpendicular to the largest surface will.

2. The method according to claim 1, characterized in that that the strip prior to magnetization to further reduce its smaller size is passed through press rolls.

3. Extrusion or transfer molding nozzle for performing the method according to claim 1 or 2, characterized by a coherent body with inlet and outlet openings with im essentially rectangular, approximately equal to each other, approximately perpendicular to each other, Cross-sections each having a small and a large side perpendicular to it such that the large side of the inlet opening approximately parallel to the small side of the outlet opening and vice versa the small side of the inlet opening is approximately parallel to the large side of the outlet opening and both cross-sections through smooth walls gradually and substantially under Keeping the overall cross-section constant.

1 sheet of drawings