DE1291647B - Heated car window and process for its manufacture - Google Patents

Heated car window and process for its manufacture

Info

Publication number
DE1291647B
DE1291647B DEV27765A DEV0027765A DE1291647B DE 1291647 B DE1291647 B DE 1291647B DE V27765 A DEV27765 A DE V27765A DE V0027765 A DEV0027765 A DE V0027765A DE 1291647 B DE1291647 B DE 1291647B
Authority
DE
Germany
Prior art keywords
strips
resistance
pane
car window
galvanic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DEV27765A
Other languages
German (de)
Inventor
Karla Heinz
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Compagnie de Saint Gobain SA
Original Assignee
Compagnie de Saint Gobain SA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to DE19641480445 priority Critical patent/DE1480445B1/en
Application filed by Compagnie de Saint Gobain SA filed Critical Compagnie de Saint Gobain SA
Priority to DEV27765A priority patent/DE1291647B/en
Priority to FR10518A priority patent/FR1464585A/en
Priority claimed from BE662903A external-priority patent/BE662903A/fr
Priority to ES0312177A priority patent/ES312177A1/en
Priority to DE19661555053 priority patent/DE1555053B1/en
Priority to NO00170497A priority patent/NO130228B/no
Priority to FR127930A priority patent/FR93853E/en
Priority to US682173A priority patent/US3553833A/en
Priority to BE706440D priority patent/BE706440A/xx
Priority to CH1588067A priority patent/CH466056A/en
Priority to ES347156A priority patent/ES347156A2/en
Priority to SE15636/67A priority patent/SE326805B/xx
Priority to NL6715459.A priority patent/NL156294B/en
Priority to GB51819/67A priority patent/GB1209777A/en
Publication of DE1291647B publication Critical patent/DE1291647B/en
Pending legal-status Critical Current

Description

Die Erfindung bezieht sich auf eine heizbare Autoscheibe mit zwischen Sammelschienen an den Scheibenkanten auf der Scheibenoberfläche verlaufenden, in ihr eingebrannten Widerstandsstreifen, die durch galvanischen Niederschlag verstärkt sind.The invention relates to a heatable car window with between Busbars running along the edge of the pane on the surface of the pane, in their burned-in resistance strips, which are reinforced by galvanic precipitation are.

Da solche zum Einbrennen- in die Glasoberfläche geeignete elektrisch leitende Zusammensetzungen in der Regel aus einer feinverteilten Aufschlämmung metallischer Teilchen und einer niedrigschmelzenden Fritte in einem organischen Bindemittel bestehen, ist insbesondere, wenn aus Gründen guter Sichtverhältnisse sehr feine Widerstandsstreifen aufgebracht werden sollen, der elektrische Widerstand dieser Streifen nach dem Einbrennen verhältnismäßig hoch. Bei größeren Längen der Streifen wird darum in der Regel die für das Freihalten der Scheibe von Kondensbelägen bzw. Schnee oder Eis notwendige Erwärmung der Scheibe nicht erreicht.Since those suitable for burning into the glass surface are electrically Conductive compositions usually consist of a finely divided slurry of metallic materials Particles and a low-melting frit in an organic binder, is especially useful when there are very fine resistance strips for reasons of good visibility are to be applied, the electrical resistance of these strips after baking relatively high. In the case of longer lengths of the strips, the necessary to keep the pane free of condensation, snow or ice The pane did not heat up.

Man hat bereits in Erwägung gezogen, die Widerstandsstreifen nicht über die ganze Scheibenlänge, sondern nur auf kleineren Bereichen, und zwar nur auf für die Durchsicht wichtigen Bereichen anzuordnen. Eine solche Anordnung der Heizleiter lediglich auf ausgewählten Feldern ist jedoch aus ästhetischen Gründen nicht immer angebracht. Außerdem wirkt sie für das Auge störender, als wenn sich die Heizleiter über die gesamte Scheibe erstrecken.It has already been considered not to use the resistance strips over the entire length of the disc, but only on smaller areas, and only to be placed on areas that are important for the review. Such an arrangement of the Heating conductors only on selected fields, however, is for aesthetic reasons not always appropriate. In addition, it is more annoying to the eye than when it is itself the heating conductors extend over the entire pane.

Um längere Heizleiter verwenden zu können, muß der spezifische elektrische Widerstand der Heizleiter erniedrigt werden. Zu diesem Zweck hat man bereits in Erwägung gezogen, die Widerstandsstreifen nach dem Einbrennen galvanisch zu verstärken. Durch eine solche galvanische Verstärkung kann je nach Behandlungsdauer der spezifische Widerstand in weiten Grenzen variiert und damit die gewünschte Heizleistung pro Flächeneinheit der Glasscheibe erreicht werden. Die Heizleiter können in den erforderlichen Grenzen beliebig lang gemacht und so beispielsweise waagerecht von einer Seitenkante zur anderen Seitenkante der Scheibe durchgeführt werden. Auf der anderen Seite wird nunmehr jedoch die Scheibe über ihre ganze Länge gleichmäßig beheizt, was eine stärkere Leistungsaufnahme zur Folge hat. Durch den stärkeren Stromverbrauch wird aber die Stromquelle des Fahrzeuges, d. h. die Lichtmaschine bzw. die Batterie, stärker belastet. Dadurch kann der Stromverbrauch solcher Heizscheiben die Leistungsfähigkeit üblicher Batterien überschreiten.In order to be able to use longer heating conductors, the specific electrical Resistance of the heating conductors can be reduced. For this purpose one already has in Considered galvanic reinforcement of the resistance strips after baking. With such a galvanic reinforcement, the specific Resistance varies within wide limits and thus the desired heating output per Area unit of the glass pane can be achieved. The heating conductors can be in the required Borders made as long as you want and so, for example, horizontally from one side edge to the other side edge of the pane. On the other hand will now, however, the disc is heated evenly over its entire length, which is a stronger one Power consumption. Due to the higher power consumption, however, the Vehicle power source, d. H. the alternator or the battery, more heavily loaded. As a result, the power consumption of such heating panels can make the performance more common Batteries exceed.

Zum allgemeinen Stand der Technik gehört ferner ein elektrisches Widerstandsheizgerät, bei dem auf eine vorher vorgespannte Glasscheibe mit Hilfe des Metallspritzverfahrens (Schoop-Verfahrens) verhältnismäßig breite Streifen von Aluminium oder einer Aluminiumlegierung aufgebracht werden.The general state of the art also includes an electrical resistance heater, in which on a previously toughened glass pane with the help of the metal spraying process (Schoop process) relatively wide strips of aluminum or an aluminum alloy be applied.

Es liegt im Wesen des Metallspritzverfahrens, daß das Widerstandsmaterial nicht gleichmäßig aufgebracht werden kann. Man versuchte deshalb, diese unvermeidlichen Unregelmäßigkeiten zu beseitigen, indem man eine besondere Schaltung der Widerstandsstreifen in Aussicht nahm, durch die nach dem i Stromverzweigungsgesetz die Aufteilung des Stromes auf die beiden Schleifenhälften sich automatisch regeln soll.It is in the nature of metal spraying that the resistor material cannot be applied evenly. One tried, therefore, to these inevitable Eliminate irregularities by making a special circuit of the resistance strips envisaged the division of the Current to the two loop halves should regulate itself automatically.

Der Erfindung liegt die Aufgabe zugrunde, eine heizbare Autoscheibe mit zwischen Sammelschienen i an den Scheibenkanten auf der Scheibenoberfläche verlaufenden, in ihr eingebrannten Widerstandsstreifen, die durch galvanischen Niederschlag verstärkt sind, zu schaffen, bei der beliebige Muster der Widerstandsstreifen vorhanden sind, andererseits aber die Stromaufnahme der Heizscheiben in den für die Versorgungsaggregate zulässigen Grenzen bleibt.The invention is based on the object of a heatable car window with between busbars i at the pane edges on the pane surface, Resistance strips burned into it, reinforced by galvanic precipitation are to be created in which any pattern of resistance strips is available, on the other hand, however, the power consumption of the heating panels in the supply units permissible limits remains.

Gelöst wird diese Aufgabe dadurch, daß der galvanische Niederschlag außerhalb von für die Durchsicht ausgewählten Bereichen willkürlich verstärkt und damit die Erwärmung der Widerstandsstreifen im wesentlichen auf diese Durchsichtsbereiche konzentriert ist.This object is achieved in that the galvanic deposit randomly amplified and outside of areas selected for review thus the heating of the resistance strips essentially on these see-through areas is focused.

Obwohl sich also die Heizleiter über die gesamte Scheibe erstrecken können, beschränkt sich die eigentliche Heizwirkung der Widerstandsstreifen nur auf gewisse Bereiche, durch die hindurch ein einwandfreier Durchblick gewährleistet wird.So although the heating conductors extend over the entire pane can, the actual heating effect of the resistance strips is only limited to certain areas through which a perfect view is guaranteed will.

Von besonderem Vorteil sind die erfindungsgemäßen heizbaren Autoscheiben bei ihrer Verwendung als Rückwandscheiben. Im allgemeinen blickt der Fahrer eines Kraftfahrzeuges lediglich über den vor ihm angebrachten Rückblickspiegel durch die Rückwandscheibe auf die hinter ihm liegende Straße. Infolgedessen dient in der Regel auch nicht die ganze Rückwandscheibe, sondern nur ein bevorzugter Bereich dieser Scheibe für den Durchblick. Aus diesem Grunde bedeutet es auch keinen Nachteil, daß die Scheibe nur auf einem ausgewählten Bereich völlig frei bleibt. Vielmehr ist damit den tatsächlichen Anforderungen voll Genüge getan. Im übrigen führt bei Dauerbeheizung der Scheibe die Heizwirkung der Widerstandsstreifen zu einer Verminderung des Beschlages auch außerhalb des eigentlichen Sichtfeldes. In jedem Falle entsteht aber im Bereiche der konzentrischen Erwärmung in kürzester Zeit eine Durchblickmöglichkeit.The heatable car windows according to the invention are of particular advantage when used as rear wall panels. In general, the driver looks at one Motor vehicle only through the rearview mirror attached in front of him Rear wall window onto the street behind him. As a result, usually serves also not the entire rear panel, but only a preferred area of this Disc for a clear view. For this reason it does not mean a disadvantage that the disc remains completely free only in a selected area. Much more is thus fully satisfied with the actual requirements. Incidentally, leads to Continuous heating of the pane reduces the heating effect of the resistance strips the fitting outside of the actual field of vision. In each case arises but in the area of concentric heating, an opportunity to see through in a very short time.

Ein Verfahren zur Herstellung einer solchen Autoscheibe durch Auftragen von bis zu entlang den Scheibenkanten verlaufenden Sammelschienen durchgehenden, gleichmäßig schmalen, aus einer elektrisch leitenden Einbrennmasse bestehenden Widerstandsstreifen, Einbrennen bei erhöhter Temperatur und nachfolgende galvanische Verstärkung der Widerstandsstreifen kennzeichnet sich in weiterer Ausbildung der Erfindung dadurch, daß vor bzw. nach einer kurzen Galvanisierungsbehandlung der Gesamtfläche der eingebrannten Widerstandsstreifen, während der der Widerstand in der Sichtzone auf den gewünschten Wert gebracht wird, das Sichtfeld im Galvanisierungsbad mit einem von den Ionen des Verstärkungsmetalls nicht durchdringbarem Material abgedeckt und die Galvanisierungsbehandlung fortgesetzt wird. Man kann das Verfahren entsprechend den Unteransprüchen in bei der Galvanisierung an sich bekannter Weise modifizieren.A method of making such a car window by application of continuous busbars running along the edges of the panes, evenly narrow resistance strips made of an electrically conductive stoving compound, Burn-in at elevated temperature and subsequent galvanic reinforcement of the Resistance strips are characterized in a further embodiment of the invention in that that before or after a short electroplating treatment of the total area of the baked Resistance strip, during which the resistance in the viewing zone to the desired Value is brought to the field of view in the electroplating bath with one of the ions the reinforcement metal is covered with non-penetrable material and the electroplating treatment is continued. You can use the method according to the subclaims in at modify the electroplating in a manner known per se.

Die Zeichnung zeigt in den beiden Figuren zwei verschiedene Ausführungsformen einer gemäß der Erfindung hergestellten heizbaren Autoscheibe. Zur Verdeutlichung sind die Unterschiede zwischen den als Heizwiderstand wirkenden leitenden Streifen oder Abschnitten dieser Streifen und den mit einem stärkeren Metallauftrag versehenen Abschnitten stark herausgehoben.The drawing shows two different embodiments in the two figures a heated automobile window produced according to the invention. For clarification are the differences between the conductive strips that act as a heating resistor or sections of these strips and those provided with a thicker metal coating Sections strongly highlighted.

In F i g. 1 ist eine als Autorückwandscheibe geeignete Glasscheibe 1 wiedergegeben, die mit den zueinander parallelen leitenden Streifen 2 versehen ist. Die Streifen 2 sind nach einem nach dem Stande der Technik bekannten Verfahren aufgebracht. Sie münden in die entlang den Seitenkanten der Scheibe 1 aufgebrachten Stromzuführungsstreifen 3, die über nicht dargestellte Anschlüsse an die Stromquelle angeschlossen sind. Im gestrichelt eingezeichneten Sichtfeld 5 weisen die Streifen 2 keine oder nur eine geringe metallische Verstärkung auf, während sie außerhalb des Sichtfeldes mit einer dickeren Metallschicht versehen sind.In Fig. 1 is a glass pane suitable as a car rear panel 1 reproduced, which are provided with the conductive strips 2 parallel to one another is. The strips 2 are made according to a method known in the art upset. They open into the along the side edges of the pane 1 upset Power supply strips 3, which have connections, not shown, to the power source are connected. The stripes point in the field of view 5 shown in dashed lines 2 little or no metallic reinforcement while outside of the field of view are provided with a thicker metal layer.

Die Stromzuführungsstreifen 3 sind zweckmäßigerweise im gleichen Arbeitsgang wie die leitenden Streifen aufgebracht und bestehen aus dem gleichen Material wie diese. Sie sind im vorliegenden Fall so angebracht, daß sie beim Einbau in die Karosserie von der Gummieinfassung verdeckt werden.The power supply strips 3 are expediently in the same operation as applied to the conductive strips and made of the same material as these. In the present case, they are attached in such a way that they are installed in the body be covered by the rubber surround.

Sollte es aus ästhetischen Erwägungen erwünscht sein, die leitenden Streifen nicht nur auf einem schmalen Bereich, sondern auf der gesamten Scheibenfläche anzuordnen, so kann man die in F i g. 2 dargestellte Anordnung wählen. In diesem Fall sind die den Sichtbereich durchlaufenden leitenden Streifen 6 in ähnlicher Weise ausgebildet wie im Beispiel nach der F i g. 1. Außerdem sind jedoch oberhalb und unterhalb dieser Streifen 6 weitere Widerstandsstreifen 7 angeordnet. Diese Widerstandsstreifen 7 weisen vorzugsweise keine oder nur eine sehr geringe metallische Verstärkung auf. Infolgedessen ist ihr Widerstand sehr hoch, so daß der Stromdurchgang durch sie verhältnismäßig gering ist.Should it be desirable for aesthetic considerations, the senior Stripes not only on a narrow area, but on the entire surface of the pane to arrange, so one can in F i g. 2 select the arrangement shown. In this In the case of the conductive strips 6 passing through the viewing area are similar Way designed as in the example according to FIG. 1. In addition, however, are above and below these strips 6 further resistance strips 7 are arranged. These Resistance strips 7 preferably have little or no metallic material Reinforcement on. As a result, their resistance is very high, so that the passage of current by it is relatively low.

Bei der Anordnung nach F i g. 1 brauchen die einzelnen leitenden Streifen nicht unbedingt alle parallel geschaltet zu sein, sondern sie können auch in beliebiger Weise einzeln oder gruppenweise in Reihenschaltung angeordnet sein.In the arrangement according to FIG. 1 need the individual conductive strips not necessarily all to be connected in parallel, but they can also be in any Way be arranged individually or in groups in series.

Claims (7)

Patentansprüche: 1. Heizbare Autoscheibe mit zwischen Sammelschienen an den Scheibenkanten auf der Scheibenoberfläche verlaufenden, in ihr eingebrannten Widerstandsstreifen, die durch galvanischen Niederschlag verstärkt sind, d a d u r c h g e k e n n -zeichnet, daß der galvanische Niederschlag außerhalb von für die Durchsicht ausgewählten Bereichen willkürlich verstärkt und damit die Erwärmung der Widerstandsstreifen im wesentlichen auf diese Durchsichtsbereiche konzentriert ist. Claims: 1. Heatable car window with between busbars running along the edges of the pane on the pane surface, burnt into it Resistance strips that are reinforced by galvanic precipitation, d a d u r c h g e k e n n - indicates that the galvanic precipitation outside of for the viewing of selected areas arbitrarily amplified and thus the warming the resistance strip is essentially concentrated on these see-through areas is. 2. Verfahren zur Herstellung einer Autoscheibe nach Anspruch 1 durch Auftragen von bis zu entlang den Scheibenkanten verlaufenden Sammelschienen durchgehenden, gleichmäßig schmalen, aus einer elektrisch leitenden Einbrennmasse bestehenden Widerstandsstreifen, Einbrennen bei erhöhter Temperatur und nachfolgende galvanische Verstärkung der Widerstandsstreifen, dadurch gekennzeichnet, daß vor bzw. nach einer kurzen Galvanisierungsbehandlung der Gesamtfläche der eingebrannten Widerstandsstreifen, während der der Widerstand in der Sichtzone auf den gewünschten Wert gebracht wird, das Sichtfeld im Galvanisierungsbad mit einem von den Ionen des Verstärkungsmetalls nicht durchdringbaren Material abgedeckt und die Galvanisierungsbehandlung fortgesetzt wird. 2. A method for producing a car window according to claim 1 by application of continuous busbars running along the edges of the panes, evenly narrow resistance strips made of an electrically conductive stoving compound, Burn-in at elevated temperature and subsequent galvanic reinforcement of the Resistance strips, characterized in that before or after a short electroplating treatment the total area of the burned-in resistor strips during which the resistor is applied is brought to the desired value in the viewing zone, the viewing field in the electroplating bath covered with a material which cannot be penetrated by the ions of the reinforcing metal and the electroplating treatment is continued. 3. Verfahren nach Anspruch 2, dadurch gekennzeichnet, daß die Abdeckung der ausgewählten Zonen durch eine sich wenigstens an ihren Randbereichen über elastisch verformbare Streifen dicht an die Scheibe, gegebenenfalls durch Saugwirkung, anlegende Platte od. dgl. erfolgt. 3. The method according to claim 2, characterized in that the coverage of the selected zones by a at least at their edge areas via elastically deformable strips close to the Disc, if necessary by suction, applying plate or the like. Takes place. 4. Verfahren nach Anspruch 2, dadurch gekennzeichnet, daß in den ausgewählten Zonen wenigstens auf den Streifen ein haftender Überzug aufgebracht wird. 4th Method according to Claim 2, characterized in that in the selected zones an adhesive coating is applied to at least the strip. 5. Verfahren nach Anspruch 4, dadurch gekennzeichnet, daß ein Überzug aus einem leicht wieder entfernbaren Material verwendet wird. 5. Procedure according to claim 4, characterized in that a coating from a light again removable material is used. 6. Verfahren zur Herstellung einer Autoscheibe nach Anspruch 1 durch Auftragen von bis zu entlang den Scheibenkanten verlaufenden Sammelschienen durchgehenden, gleichmäßig schmalen, aus einer elektrisch leitenden Einbrennmasse bestehenden Widerstandsstreifen, Einbrennen bei erhöhter Temperatur und nachfolgende galvanische Verstärkung der Widerstandsstreifen, dadurch gekennzeichnet, daß durch Ausbildung und Anordnung der Kathoden im Galvanisierungsbad im Sichtbereich der Scheibe die Feldliniendichte und damit der galvanische Niederschlag des Verstärkungsmaterials niedriger gehalten wird als in den übrigen Bereichen der Scheibe. 6. Method of manufacturing a car window according to claim 1 by applying up to along the edges of the pane Busbars continuous, evenly narrow, made of an electrically conductive one Burning-in compound existing resistance strips, burn-in at elevated temperature and subsequent galvanic reinforcement of the resistance strips, characterized in that through the formation and arrangement of the cathodes in the electroplating bath in the visible area the field line density and thus the galvanic precipitation of the reinforcement material is kept lower than in the other areas of the disc. 7. Verfahren nach Anspruch 2 bis 6, dadurch gekennzeichnet, daß als Galvanisierungsbad ein Kupferionen enthaltender Elektrolyt verwendet wird.7. Procedure according to Claim 2 to 6, characterized in that a copper ion is used as the galvanizing bath containing electrolyte is used.
DEV27765A 1964-04-23 1965-02-12 Heated car window and process for its manufacture Pending DE1291647B (en)