DE1286235C2 - THREAD ALIGNMENT CORE FOR REELS IN MESSAGE TECHNOLOGY - Google Patents
THREAD ALIGNMENT CORE FOR REELS IN MESSAGE TECHNOLOGYInfo
- Publication number
- DE1286235C2 DE1286235C2 DE1964V0025405 DEV0025405A DE1286235C2 DE 1286235 C2 DE1286235 C2 DE 1286235C2 DE 1964V0025405 DE1964V0025405 DE 1964V0025405 DE V0025405 A DEV0025405 A DE V0025405A DE 1286235 C2 DE1286235 C2 DE 1286235C2
- Authority
- DE
- Germany
- Prior art keywords
- core
- layer
- braking
- polyethylene
- adjustment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Unebenheiten dieser Oberfläche ausfüKsnden Schicht aus heiß vulkanisierbarer Silikonkautschukpaste ver-A layer of hot-vulcanizable silicone rubber paste is applied to unevenness in this surface.
aus Molybdändisulfid zu versehen (DT-Gbm sehen, die nach einer gewissen Verlaufszeit ausvul-made of molybdenum disulphide (see DT-Gbm, which after a certain time
17 47 461). kanisiert wird, d. h. nach einer Zeitspanne, während17 47 461). is caned, d. H. after a period of time while
Vorgeschlagen wurde ein Spulenkern für die der der aufgebrachte Streifen so weit in den lack-Hochfrequenztechnik,
der in den Spulenkörper mit 5 überzogenen Gewindegängen verlaufen ist, bis die
einem am Kern festhaftenden Überzug aus elasti- Gewindespitzen gerade noch von der Paste bedeckt
schem Werkstoff einschraubbar ist, wobei der Über- sind. Die zu einem kompakten Silikonkautschukzug
ausschließlich aus auf dem Kern ausvulkanisier- streifen ausvulkanisierte Silikonkautschukpaste haftem
Silikonkautschuk besteht und eine radial unter- tet am Kern an und bildet in diesem kompakten
schiedliche Wandstärke mit einer axialen, wulstarti- io Zustand die Spielausgleich- und Bremsschicht,
gen Verdickung aufweist, welche die Spitzen des Es ist bekannt, zur Verbesserung der Haftung von
Kerngewindes gerade noch unter Andeutung des Ge- kaltvernetzbaren Silikonkautschukpasten auch auf
windeverlaufs überragt. Bei der Herstellung dieses metallischen bzw. keramischen Substraten die jeweils
Spulenkernes wird vorzugsweise so vorgegangen, daß zu beschichtende Substratoberfiäche einer Vorbewenigstens
ein axial verlaufender Streifen aus einer 15 handlung mit einem Haftmittel zu unterziehen, wobei
unvulkanisierten Silikonkautschukpaste auf einen zur weiteren Haftungsverbesserung die Oberfläche
radial symmetrischen, ebenfalls nicht vulkanisierten vorher aufgerauht werden kann. Das Haftmittel wird
Überzug, hergestellt aus einer Silikonkautschuk- auf die Oberfläche aufgestrichen oder -gepinselt oder
dispersion niedriger Viskosität, aufgebracht wird, kann durch Tauchen oder Spritzen aufgebracht werworauf
Streifen und Überzug gleichzeitig vulkanisiert 20 den. Bei diesem Haftmittel handelt es sich um eine
werden. Die Spulenkerne zeichnen sich durch eine alkoholische Lösung von Kieselsäurederivaten und
sehr gute Haftfestigkeit der auf den Spulenkern un- anderen Zusätzen bzw. eine Lösung eines Silikonmittelbar
aufvulkanisierten (d. h. ohne Verwendung Produktes in Aceton und Isopropanol. Solche Haftvon
irgendwelchen Klebemitteln festgelegten) Silikon- mittel sollen dazu dienen, diejenige Kraft, welche bei
kautschukschicht aus, was insofern überraschend ist, 25 einer Trennung des Silikonkautschuks vom Substrat
als ein Festhaften des Silikonkautschuks auf der je Flächeneinheit aufzuwenden ist, zu erhöhen (VorUnterlage
nicht vorhergesehen werden konnte, weil läufige Merkblätter »Silopren-Haftmittel Z und Silogerade eine besondere Eigenschaft von Silikon- pren-Haftmittel E« vom März 1959 sowie »Siloprenkautschuk
seine antiadhäsive, d.h. nichtklebende Haftmittel Versuchsprodukt LK 2093« vom Januar
Oberfläche ist (DT-PS 12 76 833). 30 1963 und »Silopren-Haftmittel Z« vom Februar 1964A coil core was proposed for which the applied strip was made so far in the lacquer high-frequency technique, which ran into the coil body with 5 coated threads until the material, which is firmly adhered to the core, made of elastic thread tips, can just be screwed in with the paste , where the over- are. The compact silicone rubber cable consists exclusively of silicone rubber paste that is vulcanized to the core and is attached to the core radially underneath.
gene has thickening, which protrudes over the tips of the thread, in order to improve the adhesion of the core thread, just indicating the cold-crosslinkable silicone rubber paste, even on the course of the thread. In the manufacture of these metallic or ceramic substrates, the respective coil core is preferably proceeded in such a way that the substrate surface to be coated is subjected to a preliminary at least one axially extending strip from a treatment with an adhesive, whereby unvulcanized silicone rubber paste is applied to a surface that is radially symmetrical to further improve adhesion, also not vulcanized can be roughened beforehand. The adhesive is a coating made from a silicone rubber that is painted or brushed onto the surface or a low viscosity dispersion is applied, can be applied by dipping or spraying, on which the strip and the coating are vulcanized at the same time. This adhesive is a will. The coil cores are characterized by an alcoholic solution of silica derivatives and very good adhesive strength of the silicone agents vulcanized onto the coil core or a solution of a silicone agent (ie without the use of product in acetone and isopropanol serve to increase the force that has to be exerted in the case of a rubber layer, which is surprising in so far as a separation of the silicone rubber from the substrate as a firm adherence of the silicone rubber to the unit of area (this document could not be foreseen because current leaflets »Silopren adhesives Z and Silogerade are a special property of silicone pren adhesive E "from March 1959 and" Siloprene rubber its anti-adhesive, ie non-adhesive test product LK 2093 "from January surface (DT-PS 12 76 833), 30 1963 and" Siloprene adhesive Z "from February 1964
Die Erfindung stellt eine vorteilhafte Weiterbildung der Firma Farbenfabriken Bayer AG). Diese Funk-The invention represents an advantageous further development of the company Farbenfabriken Bayer AG). This radio
des vorstehend geschilderten Vorschlages dar, und tion hat die erfindungsgemäß vorgesehene, vor demof the proposal outlined above, and tion has the inventively provided, before
zwar unter besonderer Berücksichtigung dessen, daß Aufbringen des Streifens aus Silikonkautschukpastewith special consideration of the fact that the strip of silicone rubber paste is applied
das Einbetten einer vulkanisierbaren, viskosen SiIi- ausgehärtete Lackschicht nicht. Im Sinne der Erfin-embedding a vulcanizable, viscous SiIi-cured lacquer layer does not. In the sense of the
konkautschukpaste in die Gewindegänge von Ge- 35 dung ist daher unter »ausgehärteter Lackschicht« nurConcrete rubber paste in the thread turns of Gung is therefore only under the "hardened layer of varnish"
windekernen wegen ihrer geringen Fließfähigkeit ge- eine solche zu verstehen, welche nicht als Haftmittel,Because of their low flowability, convolute cores are to be understood as such, which are not used as adhesives,
wisse Schwierigkeiten macht. also die Adhäsionskräfte zwischen Beschichtung undmakes certain difficulties. so the adhesive forces between coating and
Es war daher die der Erfindung zugrunde liegende Substrat vergrößernder Kleber wirkt, sondern ausAufgabe, einen Gewindeabgleichkern für Spulen der schließlich die nachstehend angegebene Funktion Nachrichtentechnik mit einer festhaftenden, elasti- 40 aufweist.It was therefore the substrate-enlarging adhesive on which the invention is based acts, but from the task a thread matching core for coils which finally has the following function Communication technology with a firmly adhering, elastic 40 has.
sehen Spielausgleich- und Bremsschicht aus Silikon- Die auf der rauhen Oberfläche des Gewindekernes kautschuk zu schaffen, der auf sehr einfache Weise aufgebrachte und ausgehärtete Lackschicht dient und in großer Stückzahl herstellbar ist, zügig ver- ausschließlich als Gleitschicht für die in die Gewindestellt werden kann und in seiner Stellung nach er- gänge des Abgleichkernes einzubringende, vulkanifolgter Abstimmung so fixiert ist, daß weder Schüt- 45 sierbare, hochviskose Silikonkautschukpaste. Auf telvorgänge noch Temperaturschwankungen den Grund der glatten Oberfläche des ausgehärteten Kern aus seiner Abstimmlage bringen können. Diese Lackes wird das Verlaufen der vernetzbaren Kunst-Aufgabe wird gemäß der Erfindung dadurch gelöst, stoffpaste trotz ihrer hohen Viskosität in den Gedaß eine ausgehärtete Lackschicht die Trägerunter- windegängen des Kernes in einem Maße ermöglage für die Spielausgleich- und Bremsschicht bildet. 50 licht, welches eine zuverlässige Verankerung bzw. Vorzugsweise besteht dabei die Lackschicht aus Haftung des Spielausgleich- und Bremsstreifens Phenol-Formaldehyd-Kondensationsharz. sicherstellt. Durch die Lackierung der an sich porö-see backlash compensation and braking layer made of silicone die on the rough surface of the thread core To create rubber, which is used in a very simple way applied and cured lacquer layer and can be produced in large numbers, quickly exclusively as a sliding layer for those in the threaded position can be and in its position to be introduced after the adjustment core, volcanic followers The vote is fixed in such a way that neither pourable, highly viscous silicone rubber paste. on or temperature fluctuations cause the smooth surface of the hardened Can bring the core out of its coordination position. This varnish will run the networkable art task is achieved according to the invention by putting material paste into the Gedass despite its high viscosity a cured layer of lacquer enabled the girders to wind underneath the core to a certain extent for the backlash compensation and braking layer. 50 light, which is a reliable anchorage resp. The lacquer layer preferably consists of the adhesion of the clearance compensation and braking strips Phenol-formaldehyde condensation resin. ensures. Due to the painting of the inherently porous
Gemäß der Erfindung wird die rauhe Oberfläche sen und rauhen Oberfläche eines beispielsweise aus von Gewindekernen aus beispielsweise keramischem Ferrit bestehenden Spulenabgleichkernes wird der Ferrit mit einem die Abmessungstoleranzen und die 55 nicht zu erwartende vorteilhafte Effekt erzielt, daß elektrischen Eigenschaften des Kernes nicht verwen- die Haftfestigkeit für einen aufzuvulkanisierenden dungsnachteilig beeinflussenden, homogenen Lack- Silikonkautschukstreifen beträchtlich verbessert ist. überzug, beispielsweise Phenol-Formaldehyd-Kon- Diese Tatsache ist auf das günstigere Verlaufen der densationsharz, versehen, der dann unter an sich unvulkanisierten Silikonkautschukpaste in den lakbekannten Bedingungen ausgehärtet wird. Das Auf- 60 kierten Gewindegängen, die bis zu ihrem Grund von tragen des Lacküberzuges kann dabei durch ein an der Paste ausgefüllt werden, und der damit größeren sich bekanntes Tauchverfahren erfolgen. Der Lack- Berührungsfläche zwischen dem Streifen und der überzug weist dabei eine Mindeststärke auf, die lackierten Gewindeoberfläche zurückzuführen. Bei etwa einer monomolekularen Schicht entspricht, nicht behandelter Oberfläche, d. h. bei nicht lak- und hat höchstens eine Stärke, die vorzugsweise 65 kiertem Gewindekern ist es der an sich hochviskosen 0,01 mm beträgt. Masse, welche zur Bildung des Bremsstreifens aufAccording to the invention, the rough surface is sen and a rough surface is made of, for example of thread cores made of, for example, ceramic ferrite existing coil adjustment core is the Ferrite with one of the dimensional tolerances and the 55 unexpected beneficial effect achieved that electrical properties of the core do not use the adhesive strength for a vulcanized disadvantageously influencing, homogeneous lacquer silicone rubber strips is considerably improved. coating, for example phenol-formaldehyde-con This fact is due to the more favorable course of the Densationsharz, provided, which then under unvulcanized silicone rubber paste in the lac-known Conditions is cured. The up-60 grooved threads that go down to the bottom of wearing the lacquer coating can be filled in by a on the paste, and the thus larger known immersion process take place. The paint contact area between the strip and the The coating has a minimum thickness to return the painted thread surface. at corresponds approximately to a monomolecular layer, untreated surface, d. H. at not lac- and has at most one thickness, which is preferably the thread core with a high viscosity Is 0.01 mm. Mass, which is used to form the braking strip
Der so vorbehandelte und mit einer ausgehärteten den Kern aufgetragen wird, auf Grund ihrer großenThe so pretreated and with a hardened the core is applied, due to their large size
Lackschicht versehene Kern wird mit einem Streifen inneren Reibung nur begrenzt bzw. überhaupt nichtThe core provided with a layer of lacquer is only limited or not at all with a strip of internal friction
möglich, in die Gewindegänge des Kernes genügend rasch und tief einzudringen.possible to penetrate the threads of the core sufficiently quickly and deeply.
Die Haftfestigkeit des ausvulkanisierten Silikonkautschuks beruht also in keiner Weise auf einem Klebevorgang, sondern auf der reinen Adhäsionswirkung zwischen dem Kautschuk und der angrenzenden Fläche. Obwohl die unmittelbare Haftfestigkeit des Silikonkautschuks auf der Lackunterlage geringer sein mag als auf der unbehandelten und rohen Kernoberfläche, wird infolge der durch die lackierte Oberfläche erzielten größeren Eindringtiefe der Silikonkautschukpaste in die Gewindegänge des Kernes eine Verbindung zwischen der Spielausgleich- und Bremsschicht einerseits und den Kern andererseits erreicht, weiche in der Summenwirkung eine bessere Haftfestigkeit und Funktionsfähigkeit des ausvulkanisierten Silikonkautschukstreifens gewährleistet. The adhesive strength of the fully vulcanized silicone rubber is in no way based on one Gluing process, but on the pure adhesion effect between the rubber and the adjacent one Area. Although the direct adhesive strength of the silicone rubber on the lacquer base is lower may be as on the untreated and raw core surface, is as a result of being painted by the Surface achieved greater penetration depth of the silicone rubber paste into the threads of the Core a connection between the backlash compensation and braking layer on the one hand and the core on the other hand, achieved soft in the total effect a better adhesive strength and functionality of the vulcanized silicone rubber strip.
Die erfindungsgemäße Ausbildung einer Kernbremse als ein auf einer lackierten Oberfläche am Kern festhaftender ausvulkanisierter Silikonkautschukstreifen macht sich in vorteilhafter Weise die idealen und praktisch von der Temperatur unabhängigen Eigenschaften des Kautschukmaterials zunutze, was bei den bekannten Abgleichkernen nicht der Fall ist. Darüber hinaus ist die einfache Herstcllungsmöglichkeit insbesondere für die wirtschaftliche Herstellung großer Stückzahlen geeignet und läßt vor allem eine wesentlich gleichmäßigere Beschichtung mit reproduzierbaren Funktionseigenschaften zu, wobei weitgehend gleichbleibende Funktionsmerkmale sichergestellt sind. Darüber hinaus S kann der erfindungsgemäße Kern im Spulenkörper selbst nach wiederholtem Verstellen zügig verschraubt werden, wobei der Kern jedesmal in seiner Abstimmlage fixiert ist.The inventive design of a core brake as a on a painted surface on The core of firmly adhering vulcanized silicone rubber strips is made in an advantageous manner use ideal properties of the rubber material that are practically independent of temperature, which is not the case with the known adjustment cores. In addition, it is easy to manufacture particularly suitable for the economical production of large quantities and Above all, it allows a much more uniform coating with reproducible functional properties to, whereby largely constant functional features are ensured. Furthermore The core according to the invention can be quickly screwed into the coil body even after repeated adjustments the core is fixed in its tuning position each time.
Im nachstehenden wird an Hand der ZeichnungThe following is based on the drawing
ίο ein Ausführungsbeispiel der Erfindung näher erläutert. ίο an embodiment of the invention explained in more detail.
Mit der Bezugsziffer 1 ist die auf einer Gewindekerrsoberfläche aufgetragene und ausgehärtete Phenol-Formaldehydharz-Lackschicht bezeichnet, welche die Kernoberfläche vollständig umschließt. Diese Schicht bildet einen Überzug von geringer Dicke, vorzugsweise kleiner als 0,01 mm. Mit der Bezugsziffer 2 ist die Spielausgleich- und Bremsschicht aus Silikonkautschuk bezeichnet. Diese Schicht 2 ist auf die lackierte Kernmantelfläche 1 als Streifen aus viskoser, vernetzbarer Silikonkautschukpaste so aufgebracht, daß die Schicht in den Gewindegängen derart verläuft, daß die Gewindespitzen mit Silikonkautschukmasse gerade noch überzogen sind. In diesem Zustand wird die aufgebrachte Schicht ausvulkanisiert, und sie bildet so eine Kernbremse mit konstanter Bremswirkung auch bei wechselnder Verstellrichtung des Kernes.The reference number 1 denotes the phenol-formaldehyde resin lacquer layer applied and cured to a thread barrel surface denotes, which completely encloses the core surface. This layer forms a coating of small thickness, preferably smaller than 0.01 mm. The reference number 2 is the backlash compensation and braking layer made of silicone rubber designated. This layer 2 is on the coated core surface 1 as a strip of viscous, crosslinkable silicone rubber paste applied in such a way that the layer in the threads runs that the thread tips are just covered with silicone rubber compound. In In this state, the applied layer is fully vulcanized, and it thus forms a core brake constant braking effect even with changing direction of adjustment of the core.
Hierzu 1 Blatt Zeichnungen1 sheet of drawings
Claims (2)
(DT-Gbm 17 04 657). 65 Schließlich ist es bekannt, bei Gewindeabgleich-The layer applied to the mass core is not hardened to the numerous, well-known development hardened, but its paste-like state also belongs, between core and coil body to compensate for play between core and coil at -5 ° an intermediate layer of foamed, solid artificial container, the core position can be the coordination material, preferably polystyrene, polyethylene, polyder induction coil for different operating vinyl plastic and polyurethane, which conditions are not reliably fixed. The formed as an inserted strip or on the core core position can rather be applied firmly by shaking processes (DT-PS 9 74 417). or relative temperature fluctuations 55 Furthermore, the backlash compensation and braking layer has to be slightly changed, since the static friction of the in is brought about by the fact that a paste-like textile fibers incorporated into the coating mass in a mixture of polyvinyl chloride, a highly polymer-intensive shaking processes and ren plasticizers, for example on propylene adipate, an increase in the Temperature changed the viscosity of the base, and a blowing agent on the thread paste-like coating mass. This balancing core applied as a strip and knocked-out lash adjuster and braking element is thus foamed, so that there is a non-balancing core adhering to the core, which results in the two requirements of porous strips with a closed shell for quick adjustability or mobility and and so on there are no open pores on the surface of the strip that could not be relocated (FR-PS 12 02 357).
(DT-Gbm 17 04 657). 65 Finally, it is known that in thread matching