DE1263236B - Glass, in particular as a material for optical components - Google Patents

Glass, in particular as a material for optical components

Info

Publication number
DE1263236B
DE1263236B DE1960L0035349 DEL0035349A DE1263236B DE 1263236 B DE1263236 B DE 1263236B DE 1960L0035349 DE1960L0035349 DE 1960L0035349 DE L0035349 A DEL0035349 A DE L0035349A DE 1263236 B DE1263236 B DE 1263236B
Authority
DE
Germany
Prior art keywords
percent
weight
sio
oxides
zro
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DE1960L0035349
Other languages
German (de)
Inventor
Dipl-Chem Heinz Broemer
Norbert Meinert
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ernst Leitz Wetzlar GmbH
Original Assignee
Ernst Leitz Wetzlar GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ernst Leitz Wetzlar GmbH filed Critical Ernst Leitz Wetzlar GmbH
Priority to DE1960L0035349 priority Critical patent/DE1263236B/en
Priority to FR845302A priority patent/FR1287381A/en
Priority to GB362561A priority patent/GB914250A/en
Publication of DE1263236B publication Critical patent/DE1263236B/en
Pending legal-status Critical Current

Description

Gegenstand vorliegender Erfindung sind Gläser mit _, . , , , ,,, , ,,,.. ,The present invention relates to glasses with _,. ,,, ,,,, ,,, .. ,

hohem Brechungsindex bei kleiner Dispersion, die Glas, insbesondere als Werkstoff fur optischehigh refractive index with small dispersion, the glass, especially as a material for optical

frei von radioaktiven Stoffen sind und die sich durch Bauelemente
eine gute chemische Beständigkeit auszeichnen.
are free of radioactive substances and which are separated by components
are characterized by good chemical resistance.

Gläser mit den angegebenen optischen Eigen- 5Glasses with the specified optical properties 5

schäften sind an sich bereits bekannt. Diese Gläser ■ — businesses are already known per se. These glasses ■ -

sind auf reiner Borat- bzw. Borosilikatbasis erschmolzen und enthalten bei Brechungsindizes von Anmelder:
etwa 1,7 und kleiner Dispersion, d. h. hohem Wert, „ . ,
neben einem großen Anteil an Oxiden Seltener io trnst Leitz °- m- b"H·'
Erden bzw. Thoriumoxid einen Anteil an Glas- 6330 Wetzlar, Laufdorfer Weg
are melted on a pure borate or borosilicate basis and contain:
about 1.7 and smaller dispersion, ie high value, “. ,
in addition to a large proportion of oxides, rarer io trnst Leitz ° - m - b " H · '
Earth or thorium oxide a share of glass 6330 Wetzlar, Laufdorfer Weg

bildnern, d. h. B2-O3 und SiO2 in Höhe von mindestens form, ie B 2 O 3 and SiO 2 in the amount of at least

35 Gewichtsprozent, wobei die Borsäure bei weitem Ajs Erfjn<jer benannt·35 percent by weight, with boric acid by far A j s E r fj n < j e r

überwiegt. . , _, „ . ' .. ,__. TT predominates. . , _, ". '.., __. TT

Dieser große Anteil an Glasbildnern hat eine .5 Dipl.-Chem. Heinz Bromer, 6331 Hermannstein;This large proportion of glass formers has a .5 Dipl.-Chem. Heinz Bromer, 6331 Hermannstein;

weniger gute chemische Beständigkeit zur Folge. Norbert Meinen, 6330 Wetzlarless good chemical resistance as a result. Norbert Meinen, 6330 Wetzlar

Besonders gegen Handschweiß sind diese Glastypen These types of glass are particularly effective against hand perspiration

sehr empfindlich und verursachen dadurch bei ihrer .-very sensitive and therefore cause your .-

Verarbeitung in der optischen Industrie große Aus-Processing in the optical industry large

schußquoten und infolgedessen eine Verteuerung 20 + SiO2 + P2O5) = 30 bis 45 Gewichtsprozentshot quotas and consequently an increase in price 20 + SiO 2 + P 2 O 5 ) = 30 to 45 percent by weight

der betreffenden Erzeugnisse. Dieser Nachteil wird beträgt, mit der Maßgabe, daß sowohlof the products concerned. This disadvantage is, provided that both

durch die Erfindung vermieden. „„ r. ^ -^ ι« •-. · u*avoided by the invention. "" R. ^ - ^ ι «• -. U *

Die Gläser nach der Erfindung, die insbesondere 6^ + ^O5 Z 10 GewichtsprozentThe glasses according to the invention, in particular 6 ^ + ^ O 5 Z 10 percent by weight

als Werkstoff für optische Bauelemente geeignet als auchsuitable as a material for optical components as well

sind, sind dadurch gekennzeichnet, daß sie bestehen 25 SiO2 + P2O5 ^ 10 Gewichtsprozentare characterized in that they consist of 25 SiO 2 + P 2 O 5 ^ 10 percent by weight

aus . beträgt; off . amounts to;

GewichtsprozentWeight percent

QjQ 3 I3J5 jg 2. unter Beachtung der jeweiligen aufgeführtenQjQ 3 I 3 J 5 jg 2. taking into account the respective listed

2 ' Gehaltsgrenzen der La2O3-GeImIt sich aus der 2 'Content limits of the La 2 O 3 -GeImIt result from the

B2O3 3 bis 29 3° UngleichungB 2 O 3 3 to 29 3 ° inequality

P2O5 3 bis 7 La O = (11 ~ P2°s) P 2 O 5 3 to 7 La O = (11 ~ P2 ° s)

La2O3 22 bis 45 °'18 La 2 O 3 22 to 45 ° '18

MgO Obis 5 ergibt; MgO Obis 5 gives;

r n ■ „ , . _n 3. unter Beachtung der jeweiligen aufgeführten r n ■ ",. _ n 3. taking into account the respective listed

Lau υ Dis ^u Gehaltsgrenzen die Summe der Oxide (MgO Lau υ Dis ^ u content limits the sum of the oxides (MgO

SrO O bis 25 + CaO + SrO + BaO) = 13 bis 35 Gewichts-SrO O to 25 + CaO + SrO + BaO) = 13 to 35 weight

BaO Obis3O Prozent beträgt;BaO Obis30 percent;

ZnO und/oder CdO O bis 10 4° 4> unter BeachtunS der jeweiligen angeführten Gehaltsgrenzen die Summe der Oxide [(ZnO und/ZnO and / or CdO O to 10 4 ° 4> taking into account the respective specified content limits, the sum of the oxides [(ZnO and /

ZrO2 O bis 6,5 oder CdO) + ZrO2 + (Ta2O5 und/oder Nb2O5)]ZrO 2 O up to 6.5 or CdO) + ZrO 2 + (Ta 2 O 5 and / or Nb 2 O 5 )]

τ, Γ» αϊ a ^ TvTU r\ η u· in bis zu 26 Gewichtsprozent beträgt; ferner inτ, Γ » αϊ a ^ TvTU r \ η u · in is up to 26 percent by weight; also in

Ia2O, und/oder Nb1Os O bis 10 . r· n j ο j· ο j <-» -j * ι,Ia 2 O, and / or Nb 1 Os O to 10. r · nj ο j · ο j <- »-j * ι,

251 2 5 dem Fall, daß die Summe der Oxide unter 3) 251 2 5 in the event that the sum of the oxides under 3)

Al2O3 O bis 2,5 45 größer als 30 Gewichtsprozent ist, bei Gegen-Al 2 O 3 O to 2.5 45 is greater than 30 percent by weight,

jn Q O bis 10 wart ^er ^x^e Ζη(λ CdO, ZrO2 bzw. Nb2O5 j n QO to 10 waiting ^ he ^ x ^ e Ζ η CdO, ZrO 2 and Nb 2 O 5

2 3 der Gehalt von Ta2O5 mindestens 5 Gewichts- 2 3 the content of Ta 2 O 5 at least 5 weight

SnO2 O bis 2,5 prozent beträgt.SnO 2 O is up to 2.5 percent.

wo ei 50 In der Fi g. 1 ist in einem Dreistoffdiagramm für where ei 50 in fig. 1 is in a ternary diagram for

1. unter Beachtung der jeweiligen aufgeführten die Stoffe SiO2, B2O3 und P2O5 der Bereich dargestellt,1. taking into account the respective listed substances SiO 2 , B 2 O 3 and P 2 O 5, the range is shown,

Gehaltsgrenzen die Summe der Oxide (B2O3 innerhalb dessen die Anteile an diesen drei StoffenContent limits the sum of the oxides (B 2 O 3 within which the proportions of these three substances

liegen sollen. In der F i g. 2 ist die Abhängigkeit des La2 O3-Anteils vom P2O5-Gehalt dargestellt.should lie. In FIG. 2 shows the dependence of the La 2 O 3 content on the P 2 O 5 content.

In der folgenden Tabelle 1 sind einige Beispiele für Gläser nach der Erfindung aufgeführt. Dabei sind im oberen Teil der Tabelle die Anteile der einzelnen Glasbildner entsprechend der F i g. 1 gesondert aufgeführt.Some examples of glasses according to the invention are listed in Table 1 below. Included are in the upper part of the table the proportions of the individual glass formers according to the F i g. 1 separately listed.

Tabelle (in Gewichtsprozent)Table (in percent by weight)

SiO2 (auf*100%). B2O3 (auf 100%) P2O5 (auf 100%)SiO 2 (to * 100%). B 2 O 3 (to 100%) P 2 O 5 (to 100%)

SiO2 SiO 2

B2O3 B 2 O 3

Ca(PO3)2 Ca (PO 3 ) 2

La2O3 La 2 O 3

MgO MgO

CaO CaO

BaO BaO

ZnO ZnO

ZrO2 ZrO 2

Ta2O5 Ta 2 O 5

ne n e

''e '' e

Kennziffer Code number

Schmelz-Nr. P/V/13 PT 14 P/Br7 P BrEnamel no. P / V / 13 PT 14 P / Br7 P Br

74,5 17,874.5 17.8

7,7 29,07.7 29.0

7,07.0

4,2 42,04.2 42.0

11,811.8

5,0 1,05.0 1.0

1,7074 51,7 11.7074 51.7 1

17.8 74,517.8 74.5

7,77.7

7.0 29,07.0 29.0

4,2 42,04.2 42.0

11,811.8

5,0 1.05.0 1.0

1,71611.7161

53,4 253.4 2

25,0 51,6 23,425.0 51.6 23.4

7,5 15,57.5 15.5

9,8 22,39.8 22.3

5,0 17,2 10,05.0 17.2 10.0

4,04.0

3,73.7

5,05.0

1,7137 49,91.7137 49.9

51,6 25,0 23,4 15,551.6 25.0 23.4 15.5

7,57.5

9,8 22,39.8 22.3

5.0 17,2 10,05.0 17.2 10.0

4,04.0

3,73.7

5,05.0

1,7150 49,41.7150 49.4

Es hat sich gezeigt, daß es notwendig ist, bei hohem Glasbildneranteil, insbesondere bei gesteigertem Gehalt an P2O5, Calciumoxid zu verwenden. Die Phosphorsäure kann in das Glas als HPO3,It has been shown that it is necessary to use calcium oxide when there is a high proportion of glass former, especially when the content of P 2 O 5 is increased. The phosphoric acid can be found in the glass as HPO 3 ,

P2O5 oder aber mindestens teilweise als Meta- und/P 2 O 5 or at least partially as meta- and /

oder Orthophosphate von Metallen der II. Gruppeor orthophosphates of metals of group II

des Periodischen Systems (Mg, Ca, Sr, Ba, Zn, Cd)of the periodic system (Mg, Ca, Sr, Ba, Zn, Cd)

eingebracht werden.be introduced.

In Weiterführung der vorliegenden Erfindung können den Gläsern noch weitere Oxide zugegeben werden, die zum Einstellen der gewünschten optischen Werte bzw. zur Erhöhung der chemischen Beständigkeit dienen. Beispielsweise kommen folgende Oxide in den angegebenen Grenzen dafür in Frage:In a further development of the present invention, further oxides can also be added to the glasses to set the desired optical values or to increase the chemical resistance to serve. For example, the following oxides can be used within the specified limits:

Gewichtsprozent Al2O3 0 bis 2,5Weight percent Al 2 O 3 0 to 2.5

In2O3 0 bis 10In 2 O 3 0 to 10

SnO2 0 bis 2,5SnO 2 0 to 2.5

Ferner können zur leichteren Schmelzbarkeit Kryolith und/oder CaF2, zur Entfärbung bekannte Stoffe wie As2O3 in den üblichen Mengen dem Schmelzansatz beigegeben werden.
In der Tabelle 2 sind eine Reihe von Gläsern an-
Furthermore, to make it easier to melt, cryolite and / or CaF 2 , and known substances such as As 2 O 3 for decolorization can be added to the melt in the usual quantities.
Table 2 shows a number of glasses

geführt, die gemäß vorliegender Erfindung im Versuch in kleineren Einheiten erschmolzen wurden. In dieser Tabelle sind auch einige Gläser angeführt, bei denen der Phosphorsäureanteil größer ist, als er nach der Gleichung (1) sein soll. Diese Gläser lassen sich jedoch nur in kleineren Einheiten erschmelzen, wie aus der F i g. 2 zu ersehen ist.performed, which were melted in the experiment in smaller units according to the present invention. This table also lists some glasses in which the proportion of phosphoric acid is greater than it should be according to the equation (1). However, these glasses can only be melted in smaller units, as shown in FIG. 2 can be seen.

Tabelle 2 (in Gewichtsprozent)Table 2 (in percent by weight)

SiO2 (auf 100%) B2O3 (aufc-100%) P2O5 (auf 100%)SiO 2 (to 100%) B 2 O 3 (to 100%) P 2 O 5 (to 100%)

SiO2 SiO 2

B2O3 B 2 O 3

Ca(PO3), Ca (PO 3 ),

La2O3 La 2 O 3

CaO CaO

BaO BaO

ZnO ZnO

ZrO2 ZrO 2

ih. ih.

>'e > 'e

Kennziffer Code number

MgO MgO

Ta2O5 Ta 2 O 5

p/vp / v

17,817.8

74,574.5

7,77.7

7,07.0

29,029.0

4,24.2

42,042.0

17,817.8

1,7081 54,2 21.7081 54.2 2

P/VP / V

16,3 67,4 16,316.3 67.4 16.3

7,0 29,07.0 29.0

9,8 22,0 14,2 12,09.8 22.0 14.2 12.0

5,05.0

1,01.0

1,6746 56,31.6746 56.3

P/VP / V

16,8 69,0 14,216.8 69.0 14.2

7,0 29,07.0 29.0

8,4 27,0 14,68.4 27.0 14.6

8,08.0

5,05.0

1,01.0

1,6846 55,51.6846 55.5

Schmelz-Nr.Enamel no.

PV 2PV 2

17,1
70,7
12,2
17.1
70.7
12.2

7,0
29,0
7.0
29.0

7,0
32,0
15,0
7.0
32.0
15.0

4,04.0

5,05.0

1,01.0

1,6951
54,8
1.6951
54.8

U 106U 106

23,2
63,7
13,1
23.2
63.7
13.1

6,4
17,6
6.4
17.6

5,0
40,0
5.0
40.0

7,5
12,5
10,0
7.5
12.5
10.0

1,01.0

1,7438
49,4
1.7438
49.4

P/Br 8P / Br 8

P/V 28P / V 28

38,338.3 66,766.7 38,338.3 10,010.0 23,423.4 23,323.3 11,511.5 20,020.0 11,511.5 3,03.0 9,89.8 9,89.8 22,322.3 22,322.3 17,217.2 17,217.2 10,010.0 10,010.0 4,04.0 4,04.0 3,73.7 3,73.7 1,71421.7142 1,71611.7161 49,849.8 48,848.8 1616 1111 5,05.0 5,05.0 5,05.0 5,05.0

Tabelle 2 (Fortsetzung) (in Gewichtsprozent)Table 2 (continued) (in percent by weight)

Schmelz-Nr.Enamel no.

P V 29P V 29

SiO2 (auf 100%) B2O3 (auf 100%) P2O5 (auf 100%)SiO 2 (to 100%) B 2 O 3 (to 100%) P 2 O 5 (to 100%)

SiO2 SiO 2

B2O3 B 2 O 3

P2O5 P 2 O 5

Ca(PO3J2 Ca (PO 3 J 2

La2O3 La 2 O 3

MgO MgO

CaO CaO

BaO BaO

ZnO ZnO

ZrO2 ZrO 2

SnO2 SnO 2

Ta2O5 Ta 2 O 5

Al2O3 Al 2 O 3

Y2O3 Y 2 O 3

In2O3 In 2 O 3

i'c i'c

Kennziffer Code number

45,0 45,0 10,0 13,5 13,545.0 45.0 10.0 13.5 13.5

4,2 22,34.2 22.3

5,0 18,8 10,05.0 18.8 10.0

4,04.0

3,73.7

5,05.0

1,7168 49,2 121.7168 49.2 12

P<V30P <V30 P V 26aP V 26a Sp Tr 12Sp Tr 12 SpTr 16SpTr 16 Sp/Tr 21Sp / Tr 21 Sp Tr 20Sp Tr 20 PT 6PT 6 U 95U 95 45,045.0 10,010.0 15,015.0 40,040.0 15,015.0 15,015.0 23,923.9 28,628.6 45,045.0 66,766.7 70,070.0 45,045.0 70,070.0 70,070.0 66,766.7 57,257.2 10,010.0 23,323.3 15,015.0 15,015.0 15,015.0 15,015.0 9,49.4 14,214.2 13,513.5 3,03.0 6,06.0 16,016.0 6,06.0 6,06.0 8,98.9 10,010.0 13,513.5 20,020.0 28,028.0 18,018.0 28,028.0 28,028.0 24,824.8 20,020.0 - - 6,06.0 6,06.0 6,06.0 6,06.0 - - 4,24.2 9,89.8 - - - - 4,94.9 7,07.0 22,322.3 22,322.3 36,036.0 36,036.0 26,026.0 26,026.0 39,739.7 42,542.5 5.05.0 - - - - - - - 18,818.8 17,217.2 17,517.5 17,517.5 17,517.5 17,517.5 7,47.4 5,55.5 10,010.0 15,015.0 - - - - 7,97.9 7.57.5 6,56.5 10,010.0 - - - - 4,94.9 5,05.0 6,26.2 2,72.7 6,56.5 6,56.5 6,56.5 6,56.5 0,50.5 0,50.5 - - - - - - - 2,02.0 1,01.0 - - - —·- · 10,010.0 - - - - - - - - 10,010.0 - - 1,71761.7176 1,70671.7067 1,71101.7110 1,70701.7070 1,70701.7070 1,70501.7050 1,71231.7123 1,72311.7231 49,149.1 50,450.4 52,452.4 51,851.8 52,652.6 53,053.0 53,353.3 52,252.2 1212th 1010 1717th 1818th 1717th 1717th 2121 2222nd

P V16P V16

18,718.7

73,073.0

8,48.4

6,76.7

26,226.2

4,2 38,24.2 38.2

15,715.7

— 9,0- 9.0

1,7265 51,2 231.7265 51.2 23

In der Tabelle 3 sind Gläser angeführt, die in größeren Einheiten erschmolzen wurden.Table 3 lists glasses that were melted in larger units.

Tabelle 3 (in Gewichtsprozent)Table 3 (in percent by weight)

P/VlP / Vl P/T 3P / T 3 Schmelz-Nr.
P,T13
Enamel no.
P, T13
PT 16PT 16 P/T 18P / T 18
SiO2 (auf 100%)
B2O3 (auf 100%)
P2O5 (auf 100%)
SiO2
B2O3
Mg(PO3),
Ca(PO3J2
Ba3(PO4),
La2O3
CaO
BaO
ZnO
ZrO2
SnO2
;;„
SiO 2 (to 100%)
B 2 O 3 (to 100%)
P 2 O 5 (to 100%)
SiO 2
B 2 O 3
Mg (PO 3 ),
Ca (PO 3 J 2
Ba 3 (PO 4 ),
La 2 O 3
CaO
BaO
ZnO
ZrO 2
SnO 2
;; "
17,5
72,5
10,0
7,0
29,0
5,6
37,0
15,4
5,0
1,0
1,7054
54,2
24
17.5
72.5
10.0
7.0
29.0
5.6
37.0
15.4
5.0
1.0
1.7054
54.2
24
29,0
57,9
13,1
9,3
18,5
5,4
42,2
10,3
10,0
2,5
1,8
1,7285
51,6
25
29.0
57.9
13.1
9.3
18.5
5.4
42.2
10.3
10.0
2.5
1.8
1.7285
51.6
25th
31,3
60,2
8,5
11,0
21,2
2,3
5,6
39,3
9,0
3,5
6,1
2,0
1,7236
51,9
26
31.3
60.2
8.5
11.0
21.2
2.3
5.6
39.3
9.0
3.5
6.1
2.0
1.7236
51.9
26th
17,8
74,5
7,7
7,0
29,0
4,2
42,0
11,8
3,0
1,0
2,0
1,7163
53,4
2
17.8
74.5
7.7
7.0
29.0
4.2
42.0
11.8
3.0
1.0
2.0
1.7163
53.4
2
20,0
71,5
8,5
7,0
25,0
4,2
43,0
9,0
5,3
3,5
3,0
1,7316
51,8
28
20.0
71.5
8.5
7.0
25.0
4.2
43.0
9.0
5.3
3.5
3.0
1.7316
51.8
28
J' J ' c
Kennziffer
c
Code number

IOIO

Diese Gläser sind innerhalb der oben angeführten weiteren Grenzeh für die einzelnen Bestandteile gekennzeichnet durch folgende Zusammensetzung:These glasses are within the further limits listed above for the individual components characterized by the following composition:

GewichtsprozentWeight percent

B2O3 18,5 bis 29,0B 2 O 3 18.5 to 29.0

SiO2 , 7,0 bis 11,0SiO 2 , 7.0 to 11.0

P2O5 , 3,0 bis 4,2P 2 O 5 , 3.0 to 4.2

La2O3 37,0 bis 43,0La 2 O 3 37.0 to 43.0

MgO 0,0 bis 1,5MgO 0.0 to 1.5

CaO : 9,5 bis 17,0CaO: 9.5 to 17.0

BaO 0,0 bis 10,0BaO 0.0 to 10.0

ZnO 2,5 bis 6,1ZnO 2.5 to 6.1

SnO2 . 0,0 bis 2,0SnO 2 . 0.0 to 2.0

Die in den Tabellen angeführten Gläser sollen den Gegenstand der Erfindung sieht begrenzen, sie stellen nur eine Auswahl dar. Das La2O3 in diesen Gläsern kann mindestens teilweise durch Thoriumoxid ersetzt werden, falls die Radioaktivität des Thoriums die Verwendung dieser Gläser nicht beeinträchtigt. Einige Beispiele dafür sind in der Tabelle 4 angeführt.The glasses listed in the tables are intended to limit the subject matter of the invention, they represent only a selection. The La 2 O 3 in these glasses can at least partially be replaced by thorium oxide if the radioactivity of the thorium does not impair the use of these glasses. Some examples are given in Table 4.

Tabelle 4Table 4

SiO2 (auf 100%)...
B2O3 (auf 100%) · ·
P2O5 (auf 100%) ..
SiO 2 (to 100%) ...
B 2 O 3 (to 100%) · ·
P 2 O 5 (to 100%) ..

SiO2 SiO 2

B2O3 B 2 O 3

P2O5 P 2 O 5

Ca(PO3), Ca (PO 3 ),

La2O3 La 2 O 3

CaO CaO

ZnO ZnO

ZrO2 ZrO 2

ThO2 ThO 2

KennzifferCode number

Schmelz-Nr.Enamel no. Sp/Tr 18Sp / Tr 18 Sp/Tr 19Sp / Tr 19 15,015.0 15,015.0 70,070.0 70,070.0 15,015.0 15,015.0 6,06.0 6,06.0 28,028.0 28,028.0 6,06.0 6,06.0 16,016.0 17,517.5 17,517.5 6,56.5 6,56.5 36,036.0 20,020.0 1,6991,699 1,7051.705 52,952.9 53,053.0 1717th 1717th

M/PM / P

17,8 74,517.8 74.5

7,77.7

7,0 29,07.0 29.0

4,24.2

11,811.8

5,05.0

1,0 42,01.0 42.0

1,694 54,31.694 54.3

3030th

3535

4040

4545

Zur Erzielung farbloser Gläser werden für die Schmelzeinlagen möglichst reine Rohstoffe verwendet. Die Gläser werden vorzugsweise in Platingefäßen erschmolzen. Die Einschmelztemperatur liegt zwischen 1250 und 1300° C; geläutert wird bei etwa 1350° C. Dann wird bis zu einer Abgußtemperatur von etwa 950° C heruntergerührt und in angewärmte Stahlformen abgegossen. Das Austempern erfolgt 2O0C oberhalb des Transformationspunktes, der jeweils für die einzelnen Gläser zu ermitteln ist.To achieve colorless glasses, raw materials that are as pure as possible are used for the enamel inserts. The glasses are preferably melted in platinum vessels. The melting temperature is between 1250 and 1300 ° C; It is refined at around 1350 ° C. Then it is stirred down to a casting temperature of around 950 ° C and poured into warmed steel molds. The austempering is carried 2O 0 C above the transformation point, which is to identify each of the different glasses.

Claims (4)

Patentansprüche:Patent claims: 1. Glas, insbesondere als Werkstoff für optische Bauelemente, dadurch gekennzeichnet, daß es aus1. Glass, in particular as a material for optical components, characterized in that it off GewichtsprozentWeight percent SiO2 3 bis 29SiO 2 3 to 29 B2O3 3 bis 29B 2 O 3 3 to 29 P2O5 3 bis 7P 2 O 5 3 to 7 GewichtsprozentWeight percent La2O3 22 bis 45La 2 O 3 22 to 45 MgO 0 bis 5MgO 0 to 5 CaO 0 bis 20CaO 0 to 20 SrO 0 bis 25SrO 0 to 25 BaO 0 bis 30BaO 0 to 30 ZnO und/oder CdO 0 bisZnO and / or CdO 0 bis ZrO2
Ta2O5
Al2O3
In2O3
ZrO 2
Ta 2 O 5
Al 2 O 3
In 2 O 3
10 0 bis 6,510 0 to 6.5 und/oder Nb2O5 0 bis 10and / or Nb 2 O 5 0 to 10 0 bis 2,50 to 2.5 0 bis 100 to 10 SnO2 0 bis 2,5SnO 2 0 to 2.5 besteht, wobeiconsists, where 1. unter Beachtung der jeweiligen aufgeführten Gehaltsgrenzen die Summe der Oxide (B2O3 + SiO2 + P2O5) = 30 bis 45 Gewichtsprozent beträgt, mit der Maßgabe, daß sowohl1. taking into account the respective specified content limits, the sum of the oxides (B 2 O 3 + SiO 2 + P 2 O 5 ) = 30 to 45 percent by weight, with the proviso that both B2O3 + P2O5 ^ 10 Gewichtsprozent als auchB 2 O 3 + P 2 O 5 ^ 10 weight percent as well SiO2 + P2O5 ^ 10 GewichtsprozentSiO 2 + P 2 O 5 ^ 10 weight percent beträgt;amounts to;
2. unter Beachtung der jeweiligen aufgeführten Gehaltsgrenzen der La2O3-Gehalt sich aus der Ungleichung2. taking into account the respective listed content limits, the La 2 O 3 content is derived from the inequality _ ^ (11-Ρ,Ο,)_ ^ (11-Ρ, Ο,) La, O3 =La, O 3 = " 0,18"0.18 ergibt;results; 3. unter Beachtung der jeweiligen aufgeführten Gehaltsgrenzen die Summe der Oxide (MgO + CaO + SrO + BaO) = 13 bis 35 Gewichtsprozent beträgt;3. The sum of the oxides (MgO + CaO + SrO + BaO) = 13 to 35 percent by weight; 4. unter Beachtung der jeweiligen angeführten Gehaltsgrenzen die Summe der Oxide [(ZnO und/oder CdO) + ZrO2 + (Ta2O5 und/oder Nb2O5)] bis zu 26 Gewichtsprozent beträgt; ferner für den Fall, daß die Summe der Oxide unter 3) größer als 30 Gewichtsprozent ist, bei Gegenwart der Oxide ZnO, CdO, ZrO2 bzw. Nb2O5 der Gehalt von Ta2O5 mindestens 5 Gewichtsprozent beträgt.4. taking into account the respective specified content limits, the sum of the oxides [(ZnO and / or CdO) + ZrO 2 + (Ta 2 O 5 and / or Nb 2 O 5 )] is up to 26 percent by weight; furthermore, in the event that the sum of the oxides under 3) is greater than 30 percent by weight, in the presence of the oxides ZnO, CdO, ZrO 2 or Nb 2 O 5, the content of Ta 2 O 5 is at least 5 percent by weight. 2. Glas nach Anspruch 1, gekennzeichnet durch folgende Zusammensetzung:2. Glass according to claim 1, characterized by the following composition: GewichtsprozentWeight percent B2O3 18,5 bis 29,0B 2 O 3 18.5 to 29.0 SiO2 7,0 bis -11,0SiO 2 7.0 to -11.0 P2O5 3,0 bis 4,2P 2 O 5 3.0 to 4.2 La2O3 37,0 bis 43,0La 2 O 3 37.0 to 43.0 CaO 9,5 bis 17,0CaO 9.5 to 17.0 ZnO 2,5 bis 6,1ZnO 2.5 to 6.1 MgO 0,0 bis 1,5MgO 0.0 to 1.5 BaO 0,0 bis 10,0BaO 0.0 to 10.0 ZrO2 0,0 bis 3,0ZrO 2 0.0 to 3.0 SnO2 0,0 bis 2,0SnO 2 0.0 to 2.0 Hierzu 1 Blatt Zeichnungen1 sheet of drawings 809 518/267 3.68 © Bundesdruckerei Berlin809 518/267 3.68 © Bundesdruckerei Berlin
DE1960L0035349 1960-02-13 1960-02-13 Glass, in particular as a material for optical components Pending DE1263236B (en)