DE1241608B - Process for the uniform dispersion of dyes, pigments or fillers in polyolefins or polystyrene - Google Patents

Process for the uniform dispersion of dyes, pigments or fillers in polyolefins or polystyrene

Info

Publication number
DE1241608B
DE1241608B DE1964E0027592 DEE0027592A DE1241608B DE 1241608 B DE1241608 B DE 1241608B DE 1964E0027592 DE1964E0027592 DE 1964E0027592 DE E0027592 A DEE0027592 A DE E0027592A DE 1241608 B DE1241608 B DE 1241608B
Authority
DE
Germany
Prior art keywords
butene
poly
mixed
pigments
carbon black
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DE1964E0027592
Other languages
German (de)
Inventor
Harry Wesley Coover Jun
Richard Leon Mcconnell
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Eastman Kodak Co
Original Assignee
Eastman Kodak Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Eastman Kodak Co filed Critical Eastman Kodak Co
Publication of DE1241608B publication Critical patent/DE1241608B/en
Pending legal-status Critical Current

Description

BUNDESREPUBLIK DEUTSCHLANDFEDERAL REPUBLIC OF GERMANY

DEUTSCHESGERMAN

PATENTAMTPATENT OFFICE

AUSLEGESCHRIFTEDITORIAL

Int CL:Int CL:

COSfCOSf

Deutsche Kl 39 b-22/06 German Kl 39 b -22/06

Nummer 1 241 608Number 1 241 608

Aktenzeichen· E 27592IV c/39 bFile number E 27592IV c / 39 b

Anmeldetag 12 August 1964Filing date August 12, 1964

Auslegetag 1 Juni 1967Opening day 1 June 1967

Die Erfindung bezieht sich auf ein Verfahren zum gleichförmigen Dispergieren der verschiedensten Zusätze in Polyolefinen oder PolystyrolThe invention relates to a method for uniform dispersion of various additives in polyolefins or polystyrene

Den in der Praxis verwendeten Polyolefinen, wie Polyäthylen und Polypropylen, werden vor ihrer Verarbeitung in Gebrauchsgegenstande bekanntlich die verschiedensten Zusätze beigemischt So wird den Polymeren beispielsweise oftmals Ruß zugesetzt, um den oxydativen Abbau der Polymeren zu verzogern, oder aber den Polymeren werden farbige Pigmente, wie z. B Kadmiumgelb, zugesetzt, um sie zu farben Gleichgültig nun, ob es sich bei dem Zusatz um einen Farbstoff, Füllstoff, em Streckmittel oder einen Oxydationsverzogerer handelt, ist es zur Erzielung optimaler Ergebnisse erforderlich, den Zusatz gleichformig in dem Polymeren zu dispergieren Durch eine besondere gute Dispergierung von Pigmenten beispielsweise wird eine verbesserte Witterungsbestandigkeit, werden tiefere Faibtone und eine verbesserte Verarbertbarkeit erzielt Dies gilt insbesondere fur das Verspinnen von Pigmente enthaltenden Hochpolymeren The polyolefins used in practice, such as Polyethylene and polypropylene are known to be used in everyday objects before they are processed various additives mixed in. This is how the For example, carbon black is often added to polymers in order to delay the oxidative degradation of the polymers, or the polymers are colored pigments, such as. B Cadmium yellow added to color them It doesn't matter whether the addition is a Dye, filler, extender or an oxidation retarder is what is needed to achieve this For optimal results, it is necessary to uniformly disperse the additive in the polymer by means of a particularly good dispersion of pigments, for example, improved weather resistance, deeper color tones and improved processability are achieved. This is especially true for the spinning of high polymers containing pigments

Zur Erzielung besonders gleichförmiger Dispersionen von Pigmenten oder anderen Zuschlagen in Olefinpolymerisaten ist es bekannt, den Olefinpolymensaten Konzentrate aus Pigmenten oder Zuschlagen und polymeren Stoffen zuzusetzen Zur Dispergierung von Pigmenten m Polyäthylen und Polypropylen ist es beispielsweise bekannt, Pigmentkonzentrate aus Pigment und Athylen-Propylen-Mischpolymensaten oder Pigment und Polypropylen, insbesondere amorphen Polypropylen, zu verwendenTo achieve particularly uniform dispersions of pigments or other slamming into olefin polymers, it is known to add the Olefinpolymensaten concentrates of pigments or slamming and polymeric substances for dispersing pigments m polyethylene and polypropylene, it is known, for example, pigment concentrates from pigment and ethylene-propylene Mischpolymensaten or Pigment and polypropylene, especially amorphous polypropylene, to be used

Überraschenderweise wurde nun gefunden, daß sich als Trägermaterial bei der Herstellung der Konzentrate besonders gut Homo- und Misch polymerisate des 1-Butens eignen und den bekannten, bisher verwendeten Tragermatenalien deshalb überlegen sind, weil sie sich leichter verarbeiten lassen und die Herstellung von Dispersionen besonders guter Qualltat ermöglichenSurprisingly, it has now been found that the carrier material used in the production of Concentrates are particularly suitable homo- and mixed polymers of 1-butene and the known, therefore superior to previously used carrier materials because they are easier to process and enable the production of dispersions of particularly good quality

Demzufolge betrifft die Erfindung ein Verfahren zum gleichförmigen Dispergieren von Farbstoffen, Pigmenten oder Füllstoffen m Polyolefinen oder Polystyrol, welches dadurch gekennzeichnet ist, daß der zu dispergieiende Stoff in Form eines Konzentrates in einem Homo- oder Mischpolymerisat des 1-Butens als Trägermaterial verwendet wirdAccordingly, the invention relates to a method for uniformly dispersing dyes, pigments or fillers in polyolefins or polystyrene, which is characterized in that the substance to be dispersed is in the form of a concentrate is used in a homopolymer or copolymer of 1-butene as a carrier material

Als besonders vorteilhaft hat sich die Verwendung von Konzentraten ei wiesen, die aus Homo- oder Mischpolymerisaten des 1-Butens und mindestens etwa 5 Gewichtsprozent, vorzugsweise etwa 10 bis etwa 90 Gewichtsprozent, aus dem in dem PolyäthylenThe use has proven to be particularly advantageous of concentrates egg pointed, which from homo- or copolymers of 1-butene and at least about 5 weight percent, preferably about 10 to about 90 weight percent, of that in the polyethylene

Verfahren zum gleichförmigen Dispergieren von
Farbstoffen, Pigmenten oder Füllstoffen in
Polyolefinen oder Polystyrol
Method for uniformly dispersing
Dyes, pigments or fillers in
Polyolefins or polystyrene

AnmelderApplicant

Eastman Kodak Company, Rochester, N. YEastman Kodak Company, Rochester, N.Y.

(V St A )(V St A)

Vertreterrepresentative

Dr -Ing W Wolff, H Bartels
und Dr J. Brandes, Patentanwälte,
München 2, Thierschstr 8
Dr -Ing W Wolff, H Bartels
and Dr J. Brandes, patent attorneys,
Munich 2, Thierschstr 8

Als Erfinder benanntNamed as the inventor

Harry Wesley Coover jun ,Harry Wesley Coover jun,

Richard Leon McConnell, Kingsport, TennRichard Leon McConnell, Kingsport, Tenn

(V. St A)(V. St A)

Beanspruchte Priorität
V St ν Amerika vom 19 August 1963
(303130)
Claimed priority
V St ν America from 19 August 1963
(303130)

odei Polypropylen zu dispergierenden Stoff bestehen odei polypropylene to be dispersed substance

Als Mischpolymerisate kommen ζ B in Frage Polymerisate des 1-Butens mit monomeren Olefinen, wie Äthylen, Propylen, 1-Penten, 1-Hexen und 4-Methyl-1-penten As copolymers, ζ B are polymers of 1-butene with monomeric olefins, such as ethylene, propylene, 1-pentene, 1-hexene and 4-methyl-1-pentene

Im übrigen sind auch ausgehend von anderen a-Olefinen als den genannten sowie Dienen mit 1 bis Kohlenstoffatomen und 1-Buten Mischpolymerisate herstellbar, die zur Durchfuhrung des Verfahrens der Erfindung geeignet sind In dem Maße, wie der Anteil der von 1-Buten verschiedenen Monomeren steigt, nimmt jedoch die durch das 1-Buten bedingte Wirkung ab Es hat sich gezeigt, daß Mischpolymerisate mit 75 bis 99% 1-Buten sehr gute Ergebnisse liefern Auch mit Mischpolymerisaten, die nur etwa 20% 1-Buten enthalten, lassen sich noch gute Ergebnisse erzielen Poly-1-butenkonzentrate, die etwa 10 bis etwa 60 Gewichtsprozent Zusätze enthalten, haben sich als besonders geeignet erwiesen Mit diesen Konzentraten lassen sich ζ Β ausgezeichnete Dispersionen m Polyolefinen oder Polystyrol erhaltenIncidentally, are also starting from others α-olefins as those mentioned as well as serving with 1 to Carbon atoms and 1-butene copolymers can be produced for carrying out the process of the invention are suitable to the extent that the proportion of monomers other than 1-butene is used increases, but the effect caused by the 1-butene decreases. It has been found that copolymers with 75 to 99% 1-butene give very good results Even with copolymers that only have about Containing 20% 1-butene, you can still get good results achieve poly-1-butene concentrates that are about 10 contain up to about 60 percent by weight additives proved to be particularly suitable These concentrates can be used to produce ζ Β excellent dispersions m polyolefins or polystyrene obtained

Das benotigte Poly-1-buten kann durch Poly:
sation von 1-Buten zu einem stereoregularen
meren m Anwesenheit von gewöhnlichen K
The required poly-1-butene can be obtained through poly:
sation of 1-butene to a stereoregular
meren m presence of ordinary K

709709

i 241i 241

nationskatalysatoren hergestellt werden Das Molekulargewicht des Poly-1-butens ist nicht kritisch. So können Polymere mit Eigenviskositaten von etwa 0,2 bis etwa 5,0 verwendet werden Obgleich auch der mit einem Kohlenwasserstoff extrahierbare Teil 5 des Poly-1-butenpolymeren verwendet werden kann, wird vorzugsweise doch der kristalline Teil oder das gesamte nicht extrahierte Polymere verwendetnation catalysts are produced The molecular weight of poly-1-butene is not critical. Polymers with inherent viscosities of about 0.2 to about 5.0 are used, although the hydrocarbon extractable portion 5 is also used of the poly-1-butene polymer can be used, is preferably the crystalline part or that all unextracted polymers used

Die Konzentrate lassen sich leicht herstellen, indem dei zu dispergierende Zusatz m das in Pulverform, als Granulat oder m Form von Tabletten vorliegende Poly-1-buten eingemischt wird Geeignete Vorrichtungen hierfür sind ζ B Henschellmischer, Banburymischer, Extruder oder heiße Walzen, wie sie zum Vermischen verschiedener Bestandteile mit plastischen Stoffen benutzt werden Zusätze wie ζ Β Stabilisatoren, Antioxydantien, Plastifizierungsmittel und Gleit- oder Schmiermittel, wie sie normalerweise in Polyolefinen verwendet werden, beeinträchtigen die gunstigen Eigenschaften der Poly-1-butenkonzentrate nicht wesentlich Die Konzentrate können in Form von Pulvern, als Granulat oder in Tablettenform m den obenerwähnten Vorrichtungen in die polymeren Verbindungen den anderen polymeren Matenahen eingemischt werdenThe concentrates can easily be made by the additive to be dispersed in powder form, as Granules or poly-1-butene in the form of tablets is mixed in. Suitable devices for this purpose ζ B Henschell mixers, Banbury mixers, Extruders or hot rollers such as those used for mixing various ingredients with plastic ones Additives such as stabilizers, antioxidants, plasticizers and lubricants are used or lubricants such as those normally found in polyolefins are used, affect the cheap Properties of the poly-1-butene concentrates are not significant. The concentrates can be in the form of of powders, as granules or in tablet form m the above-mentioned devices in the polymeric Compounds are mixed in with the other polymeric materials

Zusätze, die erfindungsgemaß in polymeren Veibindungen dispergiert werden können, sind ζ Β Ruß, Calciumcarbonat, Magnesiutncarbonat, Sihcmmdioxyd, Asbest, Chinaton, Zinkoxyd, Eisenoxyd, Lignin, Anthrazitkohle, bituminöse Kohle, Silikate, Holzmehl, Korkstaub, Cellulose oder färbende BestandteileAdditives according to the invention in polymeric compounds can be dispersed are ζ Β soot, Calcium carbonate, magnesium carbonate, silicon dioxide, Asbestos, China clay, zinc oxide, iron oxide, lignin, anthracite coal, bituminous coal, silicates, wood flour, Cork dust, cellulose or coloring ingredients

Die folgenden Beispiele sollen das Verfahren der Erfindung naher veranschaulichenThe following examples are intended to further illustrate the process of the invention

Dispersion besaß nach der gleichen Testmethode bewertet die Bewertungsziffer D, d h, die Dispersion war von sehr maßiger QualitätThe dispersion was rated D using the same test method , that is , the quality of the dispersion was very moderate

In der folgenden Tabelle werden die physikalischen Eigenschaften eines Polypropylen-Homopolymensats, das 3% Ruß enthielt und aus dem Poly-1-butenkonzentrat hergestellt war, mit den Eigenschaften fur ein unpigmentiertes Polypropylen verglichenThe following table lists the physical Properties of a polypropylene homopolymer containing 3% carbon black and made from the poly-1-butene concentrate was compared with the properties for an unpigmented polypropylene

Poly
propylen
Poly
propylene
PolyPoly
Eigenschaftenproperties 1,91.9 propylen
mit
3 »/o Ruß
propylene
with
3 »/ o soot
SchmelzflußMelt flow 2,02.0 1,81.8 EigenviskositatInherent viscosity 7272 2,02.0 DurometerharteDurometer hard 7575 Izod-Schlagfestigkeit (23°C)Izod impact strength (23 ° C) 0,50.5 gekerbtnotched 2323 0,50.5 ungekerbtunnotched -4-4 2222nd Versprodungstemperatur, 0CEmbrittlement temperature, 0 C 13 30013 300 22 Steifheit, kg/cm2 Stiffness, kg / cm 2 1400314003

Beispiel 1example 1

3535

Poly-1-buten einer Eigenviskositat von 2,5 wurde mit 25 Gewichtsprozent dei folgenden Zusätze vermischt. Ruß, Phthalocyanmgrun, Phthalocyaninblau, Asbest, Calciumcarbonat, Sihciumdioxyd, Cellulose, Korkstaub, Kadmiumgelb, Kadmiumrot, Benzidingelb, Anthrazitkohle, bituminöse Kohle, Eisenoxyd, Azulen, N-NitrosodiathylammPoly-1-butene with an inherent viscosity of 2.5 was mixed with 25 percent by weight of the following additives. Soot, phthalocyanine green, phthalocyanine blue, asbestos, calcium carbonate, silicon dioxide, cellulose, Cork dust, cadmium yellow, cadmium red, benzidine yellow, anthracite coal, bituminous coal, iron oxide, Azulene, N-nitroso diethyl lamb

Den Mischungen wurden weiterhin 0,4% Dilaurylttuodipropionat und 0,1% 4,4'-Butyliden-bis-(6-tert butyl-m-kresol) als Stabilisatoren zugesetzt Es wurden Dispersionen ausgezeichneter Beschaffenheit erhalten Ausgezeichnete Dispersionen wurden weiterhin mit 10%, 20%, 40%, 50% und 60% der Zusätze erhalten Weiterhin wurden Poly-1-butenkonzentrate unter Verwendung eines Polymeren mit einer Eigenviskosität von 0,2, 0,8, 1,2, 1,5, 1,7, 2,0, 3,5 und 5,0 hergestellt Mit sämtlichen der genannten PoIy-1-butene ließen sich Konzentrate herstellen, in denen die Zusätze ausgezeichnet dispergiert warenThe mixtures were also given 0.4% dilauryl tuodipropionate and 0.1% 4,4'-butylidene-bis- (6-tert-butyl-m-cresol) added as stabilizers. Dispersions of excellent quality were obtained Excellent dispersions were also obtained with 10%, 20%, 40%, 50% and 60% of the additives Furthermore, poly-1-butene concentrates were made using a polymer with an inherent viscosity of 0.2, 0.8, 1.2, 1.5, 1.7, 2.0, 3.5 and 5.0 made with all of the named poly-1-butenes concentrates in which the additives were excellently dispersed could be produced

Das unter Verwendung von 25% Ruß hergestellte Konzentrat wurde mit Polypropylen einei Eigenviskositat von 2,0 in einem Verhältnis gemischt, daß die Gesamtmischung 3% Ruß enthielt. Wurde eine Ideine Tablette hiervon zwischen zwei Glasplatten zu einem dünnen Film geschmolzen, so zeigte sich, daß der Ruß gleichfoimig verteilt war Die Dispersion besaß eine Bewertungsziffer A nach der Methode von Western Electric Standards (Western Electric Manufacturing Standard 17000 Section 1059), d h, sie war ausgezeichnet Em zum Vergleich hergestelltes fiffi|ypropylenkonzentrat, das 25% Ruß enthielt, wufde mit weiterem Polypropylen bis zu einer Konzentration von 3% Ruß vermischt Die erhaltene Aus den in der Tabelle zusammengestellten Daten ergibt sich, daß die Steifheit des Polymeren verbessert wurde, wahrend die Versprodungstemperatui praktisch unverändert blieb Ähnliche Ergebnisse wurden erzielt, wenn die anderen Poly-1-butenkonzentrate mit Polypropylen vermischt wurdenThe concentrate made using 25% carbon black was mixed with polypropylene having an inherent viscosity of 2.0 in a ratio such that the total mixture contained 3% carbon black. Was a Ideine tablet thereof is melted into a thin film between two glass plates, so, it was found that the carbon black was dispersed gleichfoimig The dispersion had a score A to the method of Western Electric Standards (Western Electric Manufacturing Standard 17000 Section 1059), that is, they It was excellent. A comparison made carbon-propylene concentrate containing 25% carbon black was mixed with further polypropylene up to a concentration of 3% carbon black. The data obtained in the table shows that the stiffness of the polymer was improved while the embrittlement temperature remained practically unchanged. Similar results were obtained when the other poly-1-butene concentrates were mixed with polypropylene

Beispiel 2Example 2

Ein wie im Beispiel 1 beschrieben hergestelltes, 20% Ruß enthaltendes Konzentrat wurde mit Polyäthylen niedriger Dichte m einem Banburymischer zu einer 2% Ruß enthaltenden Mischung verarbeitet Die Dispersion des Rußes m der Masse war ausgezeichnet, und Formkörper aus der Masse, insbesondere gepreßte Gegenstande, waren gleichmäßig gefärbt Das Polymere besaß eine ausgezeichnete Widerstandsfähigkeit gegenüber der Einwirkung von Sonnenlicht und war nicht spröde. Ähnliche gute Ergebnisse wurden erzielt, wenn das Poly-1-buten-Ruß-Konzentrat mit Polyäthylen mittlerer und hoher Dichte vermischt wurde. Die erhaltenen Dispersionen waren viel besser als jene, die mit den üblichen Polyathylen-Ruß-Konzentrationen hergestellt werden konntenA product prepared as described in Example 1, 20% of carbon black-containing concentrate was mixed with low density polyethylene m a Banbury mixer to a 2% carbon black mixture containing processed The dispersion of the carbon black m is the mass was excellent, and moldings of the composition, in particular molded object were uniformly colored. The polymer was excellent in resistance to exposure to sunlight and was not brittle. Similar good results were obtained when the poly-1-butene-carbon black concentrate was mixed with medium and high density polyethylene. The dispersions obtained were much better than those which could be made with the usual concentrations of polyethylene carbon black

Beispiel 3Example 3

25% und 50% Calcmmcarbonat enthaltende Poly-1-butenkonzentrate wurden mit Polyäthylen, Polypropylen und einem 80 20-Propylen-l-Buten-Mischpolymerisat vermischt Es wurden gleichförmig weiße Massen mit ausgezeichneten physikalischen Eigenschaften hergestelltPoly-1-butene concentrates containing 25% and 50% calcium carbonate were with polyethylene, polypropylene and a 80 20-propylene-1-butene copolymer mixed. Uniformly white compositions with excellent physical properties were obtained manufactured

Beispiel 4Example 4

Em 20% Phthalocyaninblau enthaltendes PoIy-1-butenkonzentrat wurde mit Polypropylen in einem Verhältnis gemischt, daß ein Polymeres mit 2% Pigment entstand Das pigmentierte Polypropylen wurde zu Faden versponnen Die erhaltenen Faden waren von gleichmaßiger Färbung und besaßen ausgezeichnete physikalische Eigenschaften Ähnliche Ergebnisse wurden erhalten, als die Phthalocyanmgrun- und Rußkonzentrate mit Polyäthylen, Polypropylen oder einem 90 10-Propylen-l-Buten-Mischpolymensat vermischt und die erhaltenen Massen zu Faden versponnen wurdenEm poly-1-butene concentrate containing 20% phthalocyanine blue was mixed with polypropylene in a ratio that a polymer with 2% The pigment was formed. The pigmented polypropylene was spun into threads. The threads obtained were uniform in color and excellent physical properties Similar results were obtained when the phthalocyanine base and carbon black concentrates with polyethylene, polypropylene or a 90 10-propylene-1-butene mixed polymer mixed and the masses obtained were spun into thread

Beispiel 5Example 5

Em 20% Kadmmmrot enthaltendes Poly-1 butenkonzentrat wurde nut so viel Polystyrol vermischt, daß die Konzentration des Pigments in dem Polystyrol 0,5 % betrug Zu Tassen verpreßtes Material war gleichmaßig gefärbt Ähnliche Ergebnisse wurden erhalten, wenn die Pigmentkonzentration im Polystyrol 5 bzw 10% betrug.Em poly-1 butene concentrate containing 20% cadaveric red was mixed with enough polystyrene that the concentration of the pigment in the polystyrene Material pressed into cups was uniformly colored. Similar results were obtained obtained when the pigment concentration in the polystyrene 5 and 10%, respectively.

B e ι s ρ ι e 1 6B e ι s ρ ι e 1 6

Ein 50% Ruß enthaltendes Poly-1-butenkonzentrat wurde mit einem kautschukartigen Äthylen-Propylen-Mischpolymensat einer Eigenviskositat von 1,9, das 60 Molprozent Äthylen enthielt, in einem Verhältnis gemischt, daß eme Endkonzentration von 20% Ruß in der Mischung erhalten wurde Die Verteilung des Rußes war außerordentlich gleichmaßig Ähnliche gute Dispersionen wurden erhalten, wenn andere kautschukartige Mischpolymerisate, wie Äthylen-Propylen-, Äthylen-1-Buten- oder Propylen-1-Buten-Mischpolymerisate, verwendet wurden Gute Eigebmsse wurden auch erzielt, wenn Benzidmgelb, Phthalocyamngrun, Phthalocyanmblau und Kadmiumrot enthaltende Konzentrate mit den genannten Mischpolymerisaten in solchen Verhaltmssen vermischt wurden, daß die endgültigen Massen 0,2 bis 10 Gewichtsprozent des Pigments enthieltenA poly-1-butene concentrate containing 50% carbon black was with a rubbery ethylene-propylene mixed polymer 1.9 inherent viscosity containing 60 mole percent ethylene in a ratio mixed so that a final concentration of 20% carbon black was obtained in the mixture Carbon black was extremely uniform. Similar good dispersions were obtained when others rubber-like copolymers, such as ethylene-propylene, Ethylene-1-butene or propylene-1-butene copolymers, Good results were also achieved when Benzidmgelb, Phthalocyamngrun, Concentrates containing phthalocyanine blue and cadmium red with the copolymers mentioned mixed in proportions such that the final masses are 0.2 to 10 percent by weight of the pigment

Beispiel 7Example 7

Em 40% Asbest enthaltendes Poly-1-butenkonzentrat wurde mit Polypropylen in einem Verhältnis gemischt, daß die Endmischung 20% Asbest enthielt. Aus dieser Mischung gepreßte Gegenstande waren relativ steif und besaßen eine ausgezeichnete Kerbschlagfestigkeit Em poly-1-butene concentrate containing 40% asbestos was with polypropylene in a ratio mixed so that the final mixture contained 20% asbestos. Articles pressed from this mixture were relatively stiff and had excellent impact strength

Beispiel 8Example 8

Ein I-Buten-Propylen-Mischpolymensat, das 90% 1-Buteneinheiten enthielt, wurde mit 40 Gewichtsprozent Ruß vermischt Wurde dieses Konzentrat mit Polypropylen oder Polyäthylen vermischt, wurden Produkte erhalten, in denen der Ruß außerordentlich gleichförmig dispergiert vorlagA butene-propylene mixed polymer which is 90% 1-butene units was 40 percent by weight Mixed carbon black If this concentrate was mixed with polypropylene or polyethylene, Obtained products in which the carbon black was extremely uniformly dispersed

Ähnlich gute Ergebnisse wurden erhalten, wenn Phthalocyanmblau-l-Buten-Propylen-Mischpolymensatkonzentrate in Polypropylen und Polyäthylen dispergiert wurdenSimilar good results were obtained when phthalocyanine blue-1-butene-propylene mixed polymer concentrates dispersed in polypropylene and polyethylene

Beispiel 9Example 9

Es wurden vergleichsweise drei verschiedene Farbkonzentrate, ausgehend von Ruß und Poly-1-buten, einem amorphen Polypropylen und einem Äthylen-Propylen-Mischpolymerisat, hergestelltIn comparison, three different color concentrates were based on carbon black and poly-1-butene, an amorphous polypropylene and an ethylene-propylene copolymer, manufactured

Das Poly-1-buten besaß einen Schmelzfluß von 0,7, ließ sich leicht mit dem Ruß vermählen und lieferte rasch eme gleichförmige Dispersion. Demgegenüber wurden bei Verwendung des amorphen Polypropylens, das einen Schmelzfluß von 2700 besaß, und bei Verwendung des Äthylen-Propylen-Mischpolymensates, das einen Schmelzfluß von 0,1 besaß, nur klebrige, an der Mischvorrichtung anhaftende Dispersionen erhalten The poly-1-butene had a melt flow rate of 0.7, easily milled with the carbon black, and yielded quickly eme uniform dispersion. In contrast when using the amorphous polypropylene having a melt flow rate of 2700 and when using of the ethylene-propylene mixed polymer, which had a melt flow rate of 0.1, only sticky the mixing device adhering dispersions obtained

Die drei Farbkonzentrate wurden mittels heißer Walzen m Polyäthylen niedriger Dichte mit einem Schmelzmdex von 1,9 eingemahlen, so daß Massen mit 2,5% Ruß erhalten wurden Auch bei der Einarbeitung der Farbkonzentrate in das Polyäthylen zeigte sich, daß sich das unter Verwendung von Poly-1-buten hergestellte Farbkonzentrat bedeutend leichter verarbeiten ließ als die beiden anderen Konzentrate The three color concentrates were heated by means of Rollers milled in low density polyethylene with a melting mdex of 1.9, so that masses with 2.5% carbon black were also obtained during incorporation the color concentrates in the polyethylene showed that this can be achieved using poly-1-butene The color concentrate produced was significantly easier to process than the other two concentrates

Aus den erhaltenen Polyathylenmassen wurden Folien einer Starke von 0,15 mm hergestellt Die Qualität der Folien war hinsichtlich der Dispergierung der Rußpartikeln recht unterschiedlich, wie aus den m der folgenden Tabelle wiedergegebenen Daten hervorgehtFilms with a thickness of 0.15 mm were produced from the polyethylene compositions obtained The quality of the films was in terms of dispersion of the soot particles are quite different, as shown in the data shown in the following table emerges

Polyäthylen nutPolyethylene groove

Poly-1-buten-Poly-1-butene

Farbkonzentrat Polyäthylen mit
Athylen-Propylen-Mischpolymensat
Color concentrate polyethylene with
Ethylene-propylene mixed polymer

FarbkonzenttatColor concentrate

Polyäthylen nutPolyethylene groove

FarbkonzentratColour concentrate

aus amorphemmade of amorphous

PolypropylenPolypropylene

Rußdispergierung hinsichtlich erkennbarer Rußpartikeln . .Soot dispersion with regard to recognizable soot particles . .

Gleichförmigkeit der Färbung . .Uniformity of coloration. .

Anzahl von Rußpartikeln mit einem Durchmesser von ubei 75 MikronNumber of soot particles with a diameter of at 75 microns

ausgezeichnet gut maßig gut
gut
excellent good moderately good
Well

schlecht
gut
bad
Well

3636

Claims (1)

Patentanspruch.Claim. Verfahren zum gleichförmigen Dispergieren von Farbstoffen, Pigmenten oder Füllstoffen m Polyolefinen oder Polystyrol, dadurch gekennzeichnet, daß der zu dispergierende Stoff in Form eines Konzentrates m einem Homo- oder Mischpolymerisat des 1-Butens als Tragermaterial verwendet wird.Process for uniformly dispersing dyes, pigments or fillers in polyolefins or polystyrene, characterized in that the substance to be dispersed in In the form of a concentrate m a homo- or mixed polymer of 1-butene as a carrier material is used. In Betracht gezogene Druckschriften
Deutsche Auslegeschrift Nr. 1082 045;
USA-Patentschrift Nr. 3 000 841;
ausgelegte Unterlagen des belgischen Patents
Nr. 626 813
Documents considered
German Auslegeschrift No. 1082 045;
U.S. Patent No. 3,000,841;
interpreted documents of the Belgian patent
No. 626 813
709 588/389 5 67 © Bundesdruckerei Berlin709 588/389 5 67 © Bundesdruckerei Berlin
DE1964E0027592 1963-08-19 1964-08-12 Process for the uniform dispersion of dyes, pigments or fillers in polyolefins or polystyrene Pending DE1241608B (en)