DE1209472B - Process for the production of a star rain or effect powder which can be used as a gold star effect filling for fireworks - Google Patents
Process for the production of a star rain or effect powder which can be used as a gold star effect filling for fireworksInfo
- Publication number
- DE1209472B DE1209472B DED42186A DED0042186A DE1209472B DE 1209472 B DE1209472 B DE 1209472B DE D42186 A DED42186 A DE D42186A DE D0042186 A DED0042186 A DE D0042186A DE 1209472 B DE1209472 B DE 1209472B
- Authority
- DE
- Germany
- Prior art keywords
- powder
- star
- effect
- fireworks
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
Verfahren zur Herstellung eines als Goldsterneffektfüllung für Feuerwerkskörper verwendbaren Sternregen- bzw. Effektpulvers Sternregenpulver für Feuerwerkskörper wurde bisher auf der Basis von 40 bis 50010 Kalisalpeter, 5 bis 10 0/" Schwefel, 40 bis 52 "/, Kohle und 4 bis 8 0/0 eines wasserlöslichen Klebstoffs, wie z. B. Dextrin, in der Weise hergestellt, daß man die Rohstoffkomponenten in einem Kollergang mit etwa 10 bis 12 0/0 Wasser angefeuchtet und danach etwa 1 Stunde lang gemengt und verdichtet hat. Die Masse wurde dann in einem Plansichter ohne Siebe gekörnt und schließlich in einer Trockenkammer 5 Stunden getrocknet und schließlich in einer Körntrommel mit Sieben von 1,7 mm Maschenweite nochmals gekörnt, so daß das fertige Sternregenpulver eine Korngröße von 1,7 mm besaß. Das auf diese Art und Weise gewonnene Sternregenpulver wird in der Feuerwerkerei als Zusatz für verschiedene Leuchteffekte (z. B. Feuerwerks-Raketenschweif) verwendet.A process for preparing a usable as a gold star effect filling for fireworks Sternregen- or effect powder Sternenregen powder for fireworks has been based 40-50010 potassium nitrate, 5 to 10 0 / "Sulfur, 40 up to 52" /, coal and 4 to 8 0/0 a water-soluble adhesive, such as. B. dextrin, prepared in such a way that the raw material components are moistened in a pan with about 10 to 12 0/0 water and then mixed and compacted for about 1 hour. The mass was then grained in a plan sifter without sieves and finally dried in a drying chamber for 5 hours and finally again grained in a grain drum with sieves of 1.7 mm mesh size so that the finished star rain powder had a grain size of 1.7 mm. The star rain powder obtained in this way is used in fireworks as an additive for various lighting effects (e.g. fireworks rocket tail).
Infolge der nur geringen Abriebfestigkeit bzw. Beständigkeit gegen den Explosionsdruck beim Zerlegen des Feuerwerkskörpers platzen die Pulverkörner bei der Explosion des Feuerwerkskörpers leicht auseinander und werden entsprechend mehr oder weniger fein zerstäubt. Da die Pulverkörner an sich schon eine nur geringe Größe aufweisen, haben diese Pulverteilchen dann naturgemäß eine nur sehr kurze Brenndauer, die zudem auch nicht einstellbar ist.As a result of the only low abrasion resistance or resistance to the explosion pressure when dismantling the fireworks burst the powder grains at the explosion of the fireworks slightly apart and become accordingly more or less finely atomized. Since the powder grains in themselves are only slight These powder particles then naturally have only a very short one Burning time, which is also not adjustable.
Erfindungsgemäß werden diese Mängel dadurch beseitigt, daß ein in der üblichen Weise unter Zusatz eines wasserlöslichen Bindemittels hergestelltes und auf einen Feuchtigkeitsgehalt von etwa 2,5 0/, eingestelltes Kornpulver zu Staub zerrieben, mit 2 bis 3 11/0 wasserlöslichen Bindemitteln in gelöster Form sowie gegebenenfalls mit etwas Holzkohlenstaub vermengt, zu Platten gepreßt und auf eine Korngröße bis züi etwa 20 mm gebrochen wird.According to the invention, these deficiencies are eliminated by grinding a grain powder prepared in the usual way with the addition of a water-soluble binder and adjusted to a moisture content of about 2.5 % to dust, with 2 to 3 11/0 water-soluble binders in dissolved form and if necessary mixed with some charcoal dust, pressed into plates and broken down to a grain size of up to about 20 mm.
Sowohl durch die Menge der zugegebenen Bindemittel und gegebenenfalls des Holzkolilenstaubes als auch durch Variation des Preßdruckes und der Preßzeit und schließlich auch der gewählten Korngröße kann die Brennzeit der so erzielten hochabreibfesten Goldsterne innerhalb weiter Grenzen in der gewünschten bzw. erforderlichen Weise abgewandelt werden.Both by the amount of binder added and, if applicable the Holzkolilenstaubes as well as by varying the pressing pressure and the pressing time and finally the selected grain size can affect the burning time of the highly abrasion-resistant gold stars within wide limits in the desired or required Way to be modified.
in zweckmäßiger weiterer Ausbildung des erfindungsgemäßen Verfahrens wird vorgeschlagen, ebenso wie das Versetzen und Vermischen des Pulvers mit Klebmasse auch das vorausgehende Zerreiben des Pulvers zu Staub in einem Mischfaß vorzunehmen, was ohne Schwierigkeiten möglich ist, da das Pulver infolge seines relativ hohen Feuchtigkeitsgehaltes von etwa 2,50/, in einem solchen Mischfaß ohne Zuhilfenahme sonstiger mechanischer Hilfsmittel selbständig zu Staub zerfällt und was überdies den Vorteil bietet, daß das staubförmige Pulver zum Versetzen und Vermischen mit Klebmasse nicht erst aus einem anderen Gefäß od. dgl. in das Mischfaß umgefüllt zu werden braucht.in an expedient further development of the method according to the invention is suggested, as is the addition and mixing of the powder with adhesive also to carry out the previous grinding of the powder to dust in a mixing drum, which is possible without difficulty, since the powder due to its relatively high Moisture content of about 2.50 /, in such a mixing barrel without assistance other mechanical aids automatically disintegrates into dust and what else has the advantage that the powdery powder can be added and mixed with Adhesive is not first transferred from another vessel or the like into the mixing vessel needs to become.
B e i s p i e 1
Die chemische Zusammensetzung des Sternregenpulvers
beträgt *
Die weitere Verarbeitung zu abriebfesten Goldsternen gemäß der Erfindung erfolgt in der Weise, daß das Pulver im Mischfaß erst so lange gerieben wird, bis es zu Staubfeinheit zerfallen ist. Anschließend wird diesem feinen Pulver 2 bis 3 0/, wasserlöslicher Klebstoff beige,-eben und Pulver mit Klebemasse noch einmal innig durchgemischt. Diese Pulvermasse wird dann in großen Formen, z. B. 800 x 800 mm oder 1000 x 1000 mm, 20 mm hoch, zu Pulverplatten verpreßt. An den äußeren Kanten der Platten auftretende weichere Stellen werden abgebrochen, und der Übrigbleibende feste Pulverkern wird in einer Körnmaschine zu folgenden Größen aufgearbeitet: 3 bis 6 mm, 6 bis 10 mm, 10 bis 15 mm, 15 bis 20 mm.The further processing into abrasion-resistant gold stars according to the invention takes place in such a way that the powder in the mixing vessel is rubbed until it has disintegrated to a fineness of dust. This fine powder is then intimately mixed once more with 2 to 3 % water-soluble adhesive beige, -even and powder with adhesive. This mass of powder is then in large forms, e.g. B. 800 x 800 mm or 1000 x 1000 mm, 20 mm high, pressed into powder plates. Softer areas on the outer edges of the panels are broken off and the remaining solid powder core is worked up in a graining machine to the following sizes: 3 to 6 mm, 6 to 10 mm, 10 to 15 mm, 15 to 20 mm.
Claims (2)