DE1204808B - Mold release agents for producing molded bodies from plastic

Info

Publication number: DE1204808B
Application number: DEL36908A
Authority: DE
Inventors: Dr-Ing Emil Keunecke
Original assignee: Leybold Hochvakuum Anlagen GmbH
Current assignee: Leybold Hochvakuum Anlagen GmbH
Priority date: 1960-08-26
Filing date: 1960-08-26
Publication date: 1965-11-11

Description

BUNDESREPUBLIK DEUTSCHLANDFEDERAL REPUBLIC OF GERMANY

DEUTSCHESGERMAN

PATENTAMTPATENT OFFICE

AUSLEGESCHRIFTEDITORIAL

Int. σ.:Int. σ .:

B29cB29c

Deutsche Kl.: 39 a2-1/04 German class: 39 a2- 1/04

Nummer: 1204 808Number: 1204 808

Aktenzeichen: L 36908 X/39 a2File number: L 36908 X / 39 a2

Anmeldetag: 26. August 1960 Filing date: August 26, 1960

Auslegetag: 11. November 1965Opening day: November 11, 1965

Die Erfindung bezieht sich auf ein Trennmittel zum Herstellen von Formkörpern aus Kunststoff, vorzugsweise aus Gießharzen, in Formen.The invention relates to a release agent for producing molded articles made of plastic, preferably from casting resins, in molds.

Kunststoff-Formkörper werden in weitem Umfange aus Polymerisations- und Kondensationsprodukten in Formen durch Gießen, Pressen oder Spritzen hergestellt. Eine besondere Schwierigkeit besteht dabei in der Erreichung einer einwandfreien Trennung des Kunststoff-Formkörpers von der Oberfläche der Herstellungsform, welche aus den verschiedensten Werkstoffen gebildet werden kann. Zur Erleichterung der Trennung zwischen Formkörper und Formoberfläche sind unter anderem bereits Silikonöle angewendet worden, denen jedoch ein Nachteil dadurch anhaftet, daß bei dem zur Herstellung von hochwertigen Formkörpern meist angewendeten Vakuumgießverfahren beim Eingießen des Gießharzes ein teilweises Verdampfen des Trennmittels an der Formoberfläche auftritt, wodurch an der Oberfläche des Formkörpers unerwünschte Blasen entstehen können. aoPlastic moldings are widely made from polymerization and condensation products in Molds made by casting, pressing or injection. There is a particular difficulty in the achievement of a perfect separation of the plastic molding from the surface of the production mold, which can be formed from a wide variety of materials. To facilitate the Separation between the molded body and the surface of the mold, silicone oils, among other things, have already been used been, which, however, has a disadvantage in that in the production of high-quality moldings The most common vacuum casting process when pouring the casting resin is a partial evaporation of the release agent occurs on the mold surface, whereby on the surface of the molded body unwanted bubbles can arise. ao

Die Erfindung geht von der Aufgabenstellung aus, ein Trennmittel anzugeben, welches eine einwandfreie Oberfläche der Kunststoff-Formkörper, insbesondere bei deren Herstellung im Vakuumgießverfahren, ermöglicht. Das Kennzeichnende wird darin gesehen, daß als Trennmittel ein in seiner Zusammensetzung bekanntes Schmierfett Verwendung findet, welches aus hochmolekularen Kohlenwasserstoffen, die frei von allen Anteilen mit Molekulargewichten unterhalb 500 sind, mit einem Gehalt von 12 bis 25 Gewichtsprozent, bezogen auf die Gesamtmenge, an Lithiumseifen aliphatischer Säuren mit mindestens 18 C-Atomen je Molekül besteht und ebenfalls bekannte Schmiermittelzusätze, wie feinverteiltes Siliziumoxyd, Molybdändisulfid oder Silikone enthält. Ein derartiges Schmiermittel ist bereits zu einem anderen Zweck, nämlich für die Abdichtung von Schliffverbindungen und Hähnen an Vakuumapparaturen in weitem Umfang verwendet und in dem deutschen Patent 1 005 226 geschützt worden. Überraschenderweise hat sich jedoch gezeigt, daß dieses bekannte Schmierfett auch als vorzüglich geeignetes Trennmittel bei der Herstellung von Kunststoff-Formkörpern angewendet werden kann. Dabei ist es möglich, daß das Trennmittel ausschließlich aus dem vorbekannten Schmierfett besteht, man kann jedoch gegebenenfalls andere Mischungen mit ähnlichen günstigen Ergebnissen herstellen, bei denen das bekannte Schmierfett lediglich in für die Gesamtwirkung bestimmendem Anteil vorhanden ist.The invention is based on the task of specifying a release agent which is flawless Surface of the plastic molded body, in particular when they are produced in the vacuum casting process, allows. The characteristic is seen in the fact that a release agent is known in its composition as a release agent Lubricating grease is used, which is made from high molecular weight hydrocarbons that are free of all proportions with molecular weights below 500, with a content of 12 to 25 percent by weight, based on the total amount of lithium soaps of aliphatic acids with at least 18 carbon atoms per molecule and also known lubricant additives, such as finely divided silicon oxide, Contains molybdenum disulfide or silicone. Such a lubricant is already used for another purpose, namely for the sealing of ground joints and taps on vacuum equipment to a large extent used and protected in German Patent 1 005 226. Surprisingly, however, it has has shown that this known lubricating grease is also an eminently suitable release agent in production of plastic moldings can be used. It is possible that the release agent consists exclusively of the previously known lubricating grease, but others can be used if necessary Prepare mixtures with similar beneficial results in which the known grease only is present in a proportion determining the overall effect.

Die Vorteile bei der Anwendung des vorgeschlagenen Trennmittels liegen in der besonders glatten und Formtrennmittel zum Herstellen von
Formkörpern aus KunststoffThe advantages of using the proposed release agent lie in the particularly smooth and mold release agent for producing
Molded articles made of plastic

Anmelder:Applicant:

Leybold-Hochvakuum-Anlagen G. m. b. H.,
Köln-Bayental, Bonner Str. 504Leybold high vacuum systems G. mb H.,
Cologne-Bayental, Bonner Str. 504

Als Erfinder benannt:
Dr.-Ing. Emil Keunecke, KölnNamed as inventor:
Dr.-Ing. Emil Keunecke, Cologne

fehlerfreien Oberfläche der Kunststoff-Formkörper sowie in einer wirkungsvollen Reinigung der Gießform. Die Kunststoff-Formung kann wegen der Temperaturbeständigkeit des Trennmittels auch bei höheren Temperaturen oberhalb 140° C erfolgen, und dies erweist sich insbesondere bei der Formung mancher Epoxyharze als vorteilhaft.flawless surface of the plastic moldings as well as effective cleaning of the casting mold. The plastic molding can because of the temperature resistance of the release agent even at higher Temperatures above 140 ° C take place, and this is particularly evident in the molding of some Epoxy resins as advantageous.

Eine zweckmäßige Verbesserung des Trennmittels kann durch an sich bekannte Zusätze, wie z. B. feinverteiltes Siliziumdioxyd, welches beispielsweise durch thermische Zersetzung von Siliziumhalogeniden gewonnen wird (so aus Siliziumchlorid), erreicht werden. In ähnlich vorteilhafter Weise läßt sich gegebenenfalls auch eine Beimischung an Molybdändisulfid verwenden. Da bereits aus den hochmolekularen Wasserstoffen alle Anteile mit Molekulargewichten unterhalb von 500 entfernt sind, erweist es sich allgemein als erforderlich, auch die weiteren Zusatzstoffe, wie Siliziumdioxyd oder Molybdändisulfid, in ähnlicher Weise von gas- oder dampfförmigen Bestandteilen zu befreien. Dies kann durch Erhitzen und Abkühlen unterhalb VioTorr, vorzugsweise im Hochvakuum, erfolgen.A useful improvement of the release agent can be made by additives known per se, such as. B. finely divided Silicon dioxide, which is obtained, for example, from the thermal decomposition of silicon halides will be achieved (so made of silicon chloride). In a similarly advantageous manner, if necessary also use an admixture of molybdenum disulphide. Since already from the high molecular weight hydrogen all fractions with molecular weights below 500 are removed, it turns out to be generally required, the other additives, such as silicon dioxide or molybdenum disulfide, in a similar manner to free from gaseous or vaporous components. This can be done by heating and cooling below VioTorr, preferably in a high vacuum, take place.

Man kann dem Trennmittel außerdem für bestimmte Anwendungszwecke Silikone beifügen, welche eine ähnliche Vorbehandlung hinsichtlich der Entfernung von Anteilen mit niedrigeren Molekulargewichten erfahren haben.You can also add silicones to the release agent for certain purposes, which a similar pretreatment in terms of removing lower molecular weight fractions have experienced.

Claims

Claim:

The use of a known lubricant, consisting of high molecular weight hydrocarbons, which are free of all fractions with molecular weights below 500, with a grade from 12 to 25 percent by weight, based on

509 737/354

3 43 4

Lithium soaps of aliphatic acids with at least bodies made of plastic, preferably made of cast

18 carbon atoms in the molecule, and optionally resin, in forms.

consisting of known lubricant additives, such as

finely divided silicon oxide, molybdenum sulfide or publications under consideration:

Silicones as release agents in the manufacture of molds. 5 German Patent No. 1005 226.