DE10349105B3 - Filling the joints between tiles in floor or wall coverings comprises coating the tiles with a silane-based release lacquer before grouting the joints - Google Patents

Filling the joints between tiles in floor or wall coverings comprises coating the tiles with a silane-based release lacquer before grouting the joints Download PDF

Info

Publication number
DE10349105B3
DE10349105B3 DE2003149105 DE10349105A DE10349105B3 DE 10349105 B3 DE10349105 B3 DE 10349105B3 DE 2003149105 DE2003149105 DE 2003149105 DE 10349105 A DE10349105 A DE 10349105A DE 10349105 B3 DE10349105 B3 DE 10349105B3
Authority
DE
Germany
Prior art keywords
groups
silane
hydrolytically
dissolved
release lacquer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
DE2003149105
Other languages
German (de)
Inventor
Thomas Dr. Burkhart
Olaf Quirmbach
Thorsten Landau
Ralf Schmidt
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
KCH GROUP GMBH, 56427 SIERSHAHN, DE
Original Assignee
SGL Acotec GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SGL Acotec GmbH filed Critical SGL Acotec GmbH
Priority to DE2003149105 priority Critical patent/DE10349105B3/en
Application granted granted Critical
Publication of DE10349105B3 publication Critical patent/DE10349105B3/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

Filling the joints between ceramic, artificial stone, stoneware, concrete or marble tiles in floor or wall coverings comprises coating the tiles with a release lacquer comprising a silane (I), or a siloxane polycondensation product of (I), in a solvent; allowing the lacquer to dry; filling the joints with grout; allowing the grout to dry; and mechanically removing excess grout. Filling the joints between ceramic, artificial stone, stoneware, concrete or marble tiles in floor or wall coverings comprises coating the tiles with a release lacquer comprising a silane (I), or a siloxane polycondensation product of (I), in a solvent; allowing the lacquer to dry; filling the joints with grout; allowing the grout to dry; and mechanically removing excess grout. Rx-Si-A4-x (I) A : OH or a hydrolyzable group; R : a nonhydrolyzable group; x : 0-3, but must be 1 or more in at least 50% of the silane. An independent claim is also included for a release lacquer as above.

Description

Die Erfindung betrifft ein Verfahren zum Verfugen von Platten, Fliesen oder Kacheln aus Keramik, Kunststein, Steinzeug, Beton oder Marmor, welches die Entfernung von überschüssigem Verfugungsmaterial von den Oberflächen der verfugten Platten, Fliesen oder Kacheln wesentlich erleichtert.The Invention relates to a method for grouting panels, tiles or ceramic, artificial stone, stoneware, concrete or marble tiles, which is the removal of excess grouting material from the surfaces the grouted slabs, tiles or tiles much easier.

Techniken zum Verfugen von Platten sind seit langem bekannt. Dabei werden die zwischen den mit Abstand verlegten Platten entstandenen Zwischenräume (Fugen) mit einem Verfugungsmaterial verschlossen, um das Eindringen von Feuchtigkeit, Schmutz und Schadstoffen zu verhindern und die Haltbarkeit des gesamten Plattenverbandes sowie seine Haftung auf dem Untergrund zu erhöhen. Außerdem wird- ggf. durch die Wahl eines geeigneten Verfugungsmaterials- die Wärmedehnung der einzelnen Platten ermöglicht, jedoch Rissbildung in den Platten bzw. im Untergrundes vermieden. Es können Platten aus verschiedenen Werkstoffen eingesetzt werden, beispielsweise Keramikplatten, Steinzeugfließen, Kunststoffplatten, Kunststeinplatten, Marmorplatten, Betonplatten oder dergleichen, aber auch Platten aus Metall oder thermoplastischen Werkstoffen (Polyethylen od. dgl.). Die Wahl des Verfugungsmaterials richtet sich nach der jeweiligen Art und Belastung der Platten. So verwendet man beispielsweise vergießfähiges Verfugungsmaterial (Schlämmkitt) auf der Basis von Kunstharzen wie Polyester-, Epoxid-, Furan- oder Phenolharzen oder auf der Basis von hydraulisch reagierenden Bindemitteln wie Zement oder zementhaltiger Fugmasse. Gerade bei Wandplatten oder -fliesen sollte das Verfugungsmaterial zwar noch selbstverlaufend sein, jedoch nicht so flüssig, dass es aus den Fugen herausläuft. Weiterhin ist es auch bekannt, Fugen mit dauerelastischen Verfugungsmaterial zu füllen.techniques for grouting boards have long been known. In doing so the gaps (joints) created between the spaced boards sealed with a grouting material to prevent the ingress of Prevent moisture, dirt and pollutants and durability of the entire panel association and its liability on the subsurface to increase. Moreover is - if necessary by choosing a suitable grouting material - the thermal expansion of the individual plates, however, the formation of cracks in the panels or in the subsurface was avoided. It can be plates made of different materials, for example Ceramic plates, stoneware tiles, Plastic panels, artificial stone panels, marble panels, concrete panels or the like, but also plates made of metal or thermoplastic materials (Polyethylene or the like). The choice of the grouting material judges depending on the type and load of the panels. So used for example pourable grouting material (slurry putty) based on synthetic resins such as polyester, epoxy, furan or Phenolic resins or based on hydraulically reacting binders such as Cement or cementitious grout. Especially with wall panels or - The grouting material should still be self-leveling be, but not so fluid, that it runs out of joint. Farther it is also known to grout with permanently elastic grouting material to fill.

In der Regel geschieht das Verfugen manuell, indem das Verfugungsmaterial mit einem geeigneten und der Fugenbreite angepassten Werkzeug wie beispielsweise einer Fugenkelle oder einem Fugenspachtel den Fugenhohlraum hinein gedrückt wird, oder es wird eine Handpresse benutzt mit einer Kartusche mit einer Spitze, deren Öffnung der Fugenbreite entspricht. Weiterhin bekannt sind Maschinen, mit denen – insbesondere bei größeren Fugenbreiten – das Verfugungsmaterial in die Hohlräume zwischen den Platten gepresst wird.In Usually the grouting is done manually using the grouting material with a suitable tool adapted to the joint width such as for example a joint trowel or a joint filler the joint cavity is pushed in or a hand press is used with a cartridge with a Tip whose opening corresponds to the joint width. Machines are also known with to them - especially for larger joint widths - the grouting material into the cavities between the plates are pressed.

Bei der Verfugung von Sechseck-Platten wird üblicherweise das Rüttelverfahren genutzt ( DE 23 48 301 C3 , EP 04 89 271 A1 , EP 03 40 598 B1 ). Bei dem Rüttelverfahren kann die Säure kittschicht, welche sich auf dem Mörtelbett befindet, von ihrer Viskosität so eingestellt sein, dass während des Verdichtungsvorgangs mittels Rüttelgerät der Säurekitt in den Fugen zwischen den Platten hochsteigt und diese vollkommen ausfüllt.The vibration method is usually used when grouting hexagonal plates ( DE 23 48 301 C3 . EP 04 89 271 A1 . EP 03 40 598 B1 ). In the shaking process, the viscosity of the acid kit layer on the mortar bed can be adjusted so that the acid putty rises in the joints between the plates during filling and fills them up completely during the compaction process.

Ist dies nicht der Fall, dann können die schmalen Fugen über eine nachträgliche Schlämmverfugung verschlossen werden. Dabei wird wie folgt vorgegangen. Nach dem Verlegen der Platten wird zunächst solange gewartet, bis der Plattenbelag begehbar ist. Danach werden die mit Zementschleier bzw. Mörtelresten verschmutzten Plattenoberflächen mit verdünnten organischen handelsüblichen Säuren neutralisiert und gereinigt. Sodann werden die Fugen mit dem entsprechenden Verfugungsmaterial, welches auf Kunstharz oder auf einem hydraulisch abbindenden Material (Zement/Sand) basiert, mit einem Gummi- oder Kunststoffspachtel/Schaber in die Fugen eingeschlämmt. Danach können die Platten mit einem Schwamm und Wasser nachgewaschen und so von den Resten des Verfugungsmaterials befreit werden. Dabei ist Vorsicht geboten, damit die frischen Fugen nicht beschädigt werden. Diese Art von Schlämmtechnik kann nur bei hydraulisch abbindenden Verfugungsmaterialien und bei mit Wasser emulgierbaren Epoxidharzen angewendet werden. Doch selbst bei diesen Materialien ist es notwendig, die Platten nach Beendigung der Schlämmverfugung zügig (innerhalb von maximal 4 Stunden) mit dem Schwamm nachzuwaschen. Wenn zu lange gewartet wird, bilden sich bei der Verwendung von hydraulisch abbindenden Verfugesystemen Zementschleier, die sich nur noch über aggressive sogenannte Zementschleier-Entferner schwer entfernen lassen.is if not, then you can the narrow joints over an ex post Schlämmverfugung be closed. The procedure is as follows. After this Laying the slabs first waited until the slab is accessible. After that those with cement veil or mortar residues dirty board surfaces with diluted organic commercial Acids neutralized and cleaned. Then the joints with the appropriate grouting material, which on synthetic resin or on a hydraulically setting material (Cement / sand) based, with a rubber or plastic spatula / scraper slurried into the joints. After that you can the plates are washed with a sponge and water and so on the remains of the grouting material are freed. Be careful offered so that the fresh joints are not damaged. This kind of slurry technique can only be used with hydraulically setting jointing materials and water-emulsifiable epoxy resins can be used. But itself with these materials it is necessary to finish the panels the slurry joint quickly (within of a maximum of 4 hours) with the sponge. If too long is formed when using hydraulically setting Cement veil jointing systems that are only aggressive difficult to remove so-called cement veil remover.

Diese Schlämmverfugung ist besonders problematisch bei strukturierten Fliesen und Platten und solchen mit porigen Oberflächen, da nach Schlämmende die Platten Restschleier aufweisen können. Ein weiterer Nachteil dieses Verfahrens besteht darin, dass diese Art der Schlämmverfugung für Verfugungsmaterialien auf Basis von Furanharzen, Phenolharzen, ungesättigten Polyesterharzen, Vinylesterharzen und nicht mit Wasser emulgierbare Epoxidharzen nicht angewandt werden kann. Auch farbig eingestellte, insbesondere schwarze, hydraulisch abbindende Verfugungsmassen bzw. mit Wasser emulgierbare Epoxidharze können für die Schlämmverfugung nur bedingt benutzt werden.This Schlämmverfugung is particularly problematic with structured tiles and those with porous surfaces, there after muddy end the panels can have residual veils. Another disadvantage This procedure consists of this type of grout grouting for grouting materials based on furan resins, phenolic resins, unsaturated polyester resins, vinyl ester resins and water-emulsifiable epoxy resins are not used can. Also colored, especially black, hydraulic setting jointing compounds or water-emulsifiable epoxy resins can for the Schlämmverfugung can only be used to a limited extent.

Auch bei der Verfugetechnik mittels Fugkelle oder Rüttelverfahren läßt es sich nicht vermeiden, dass Reste des Verfugungsmaterials auf die Plattenoberfläche gelangen und somit diese verschmutzen.Also in the jointing technique using a trowel or vibrating method, it can be do not prevent residues of the grouting material from getting onto the board surface and thus pollute it.

Um Verfugungsmaterial auf Basis der obenstehend genannten Kunstharze bzw. farbig eingestellte, insbesondere schwarze und/oder leitfähige hydraulisch abbindende Verfugungsmassen zu applizieren, behilft man sich zur Zeit mit dem sogenannten Trennlackverfahren der SGL ACOTEC GmbH. In diesem Verfahren wird ein Trennlack aus in organischen Lösungsmitteln gelösten thermoplastischen Copolymeren verwendet.In order to apply grouting material on the basis of the above-mentioned synthetic resins or colored, in particular black and / or conductive, hydraulically setting grouting compounds, the so-called Release lacquer process from SGL ACOTEC GmbH. In this process, a release lacquer made of thermoplastic copolymers dissolved in organic solvents is used.

Diese Copolymere (1) sind Copolymere aus Mono- und Diolefinen (2) oder Copolymere von Mono- bzw. Diolefinen mit anderen Vinylmonomeren, wie z. B. Ethylen-Propylen-Copolymere, lineares Polyethylen niederer Dichte (LLDPE) und Mischungen desselben mit Polyethylen niederer Dichte (LDPE), Propylen-Buten-1-Copolymere, Propylen-Isobutylen-Copolymere, Ethylen-Buten-1-Copolymere, Ethylen-Hexen-Copolymere, Ethylen-Methylpenten-Copolymere, Ethylen-Hepten-Copoly-mere, Ethylen-Octen-Copolymere, Propylen-Butadien-Copolymere, Isobutylen-Isopren-Co-polymere, Ethylen-Alkylacrylat-Copolymere, Ethylen-Alkylmethacrylat-Copoolymere, Ethylen-Vinylacetat-Copolymere und deren Copolymere mit Kohlenstoffmonoxid, oder Ethylen-Acrylsäure-Copolymere und deren Salze (Ionomere), sowie Terpolymere von Ethylen mit Propylen und einem Dien, wie Hexadien, Dicyclopentadien oder Ethylidennorbornen; ferner Mischungen solcher Copolymere untereinander und mit unter 1) genannten Polymeren, z. B. Polypropylen/Ethylen-Propylen-Copolymere, LDPE/Ethylen-Vinylacetat-Copolymere, LDPE/Ethylen-Acrylsäure-Copolymere, LLDPE/ Ethylen-Vinylacetat-Copolymere, LLDPE/Ethylen-Acrylsäure-Copolymere und alternierend oder statistisch aufgebaute Polyalkylen/Kohlenstoffmonoxid-Copolymere und deren Mischungen mit anderen Polymeren wie z. B. Polyamiden.This Copolymers (1) are copolymers of mono- and diolefins (2) or Copolymers of mono- or diolefins with other vinyl monomers, such as z. B. ethylene-propylene copolymers, linear low density polyethylene (LLDPE) and blends thereof with low density polyethylene (LDPE), propylene-butene-1 copolymers, Propylene-isobutylene copolymers, Ethylene-butene-1 copolymers, ethylene-hexene copolymers, ethylene-methylpentene copolymers, Ethylene-heptene copolymers, ethylene-octene copolymers, propylene-butadiene copolymers, Isobutylene-isoprene copolymers, ethylene-alkyl acrylate copolymers, Ethylene-alkyl methacrylate copolymers, ethylene-vinyl acetate copolymers and their copolymers with carbon monoxide, or ethylene-acrylic acid copolymers and their salts (ionomers), and terpolymers of ethylene with propylene and a diene such as hexadiene, dicyclopentadiene or ethylidene norbornene; furthermore mixtures of such copolymers with one another and with under 1) mentioned polymers, for. B. polypropylene / ethylene-propylene copolymers, LDPE / ethylene-vinyl acetate copolymers, LDPE / ethylene acrylic acid copolymers, LLDPE / Ethylene-vinyl acetate copolymers, LLDPE / ethylene-acrylic acid copolymers and alternating or randomly constructed polyalkylene / carbon monoxide copolymers and their Mixtures with other polymers such. B. polyamides.

Geeignete Mono- und Diolefine (2) sind beispielsweise Polypropylen, Polyisobutylen, Polybuten1, Poly-4-methylpenten-1, Polyisopren oder Polybutadien sowie Polymerisate von Cycloolefinen wie z.B. von Cyclopenten oder Norbornen; ferner Polyethylen (das gegebenenfalls vernetzt sein kann), z. B. Polyethylen hoher Dichte (HDPE), Polyethylen hoher Ldichte und hoher Molmasse (HDPE-HMW), Polyethylen hoher Dichte und ultrahoher Molmasse (HDPE-UHMW), Polyethylen mittlerer Dichte (MDPE, Polyethylen niederer Dichte (LDPE), lineares Polyethylen niederer Dichte (LLDPE), verzweigtes Polyethylen niederer Dichte (VLDPE).suitable Mono- and diolefins (2) are, for example, polypropylene, polyisobutylene, polybutene1, Poly-4-methylpentene-1, polyisoprene or polybutadiene and polymers of cycloolefins such as of cyclopentene or norbornene; further Polyethylene (which may or may not be cross-linked) e.g. B. polyethylene high density (HDPE), high density polyethylene and high molecular weight (HDPE-HMW), high density and ultra high molecular weight polyethylene (HDPE-UHMW), Medium density polyethylene (MDPE, low density polyethylene (LDPE), linear low density polyethylene (LLDPE), branched Low density polyethylene (VLDPE).

Weiterhin können in organischen Lösungsmitteln gelöste halogenhaltige Polymere (3) als Trennlack eingesetzt werden. Halogenhaltige Polymere (3), wie z. B. Polychloropren, Chlorkautschuk, chloriertes und bromiertes Copolymer aus Isobutylen-Isopren (Halobutylkautschuk), chloriertes oder Chlorsulfoniertes Polyethylen, Copolymere von Ethylen und chloriertem Ethylen, Epichlorhydrinhomo- und -copolymere, insbesondere Polymere aus halogenhaltigen Vinylverbindungen, wie z. B. Polyvinylchlorid, Polyvinylidenchlorid, Polyvinylfluorid, Polyvinylidenfluorid; sowie deren Copolymere, wie Vinylchlorid-Vinylidenchlorid, Vinylchlorid-Vinylacetat oder Vinylidenchlorid-Vinylacetat.Farther can in organic solvents dissolved halogen-containing polymers (3) can be used as a release lacquer. halogenated Polymers (3), such as. B. polychloroprene, chlorinated rubber, chlorinated and brominated copolymer of isobutylene-isoprene (halobutyl rubber), chlorinated or chlorosulfonated polyethylene, copolymers of ethylene and chlorinated ethylene, epichlorohydrin homo- and copolymers, in particular Polymers from halogen-containing vinyl compounds, such as. B. polyvinyl chloride, Polyvinylidene chloride, polyvinyl fluoride, polyvinylidene fluoride; such as their copolymers, such as vinyl chloride-vinylidene chloride, vinyl chloride-vinyl acetate or Vinylidene chloride, vinyl acetate.

Desweiteren kann der in organischen Lösungsmitteln gelöste Trennlack auch ein Copolymerisat (4) der unter (3) erwähnten halogenhaltigen Polymere und der unter (1) erwähnten Copolymere beruhen. Die Copolymerisate (4) können auch mit Kohlenwasserstoffharzen (z. B. C5-C9) inklusive hydrierte Modifikationen davon (z. B. Klebrigmacherharze) und Mischungen von Polyalkylenen und Stärke gemischt werden.Furthermore, the release lacquer dissolved in organic solvents can also be based on a copolymer (4) of the halogen-containing polymers mentioned under (3) and the copolymers mentioned under (1). The copolymers (4) can also be mixed with hydrocarbon resins (e.g. C 5 -C 9 ) including hydrogenated modifications thereof (e.g. tackifier resins) and mixtures of polyalkylenes and starch.

Der in organischen Lösungsmitteln gelöste Trennlack wird mehrmals auf die trockene Plattenoberfläche mit Lammfellwolle oder Nylon aufgetragen. Nach dem Trocknen des Trennlacks wird der auf Kunstharzen basierende Fugenkitt in die Fugen eingeschlämmt und mit einem gummierten Glättspan in die Fugen gedrückt. Trotz der Anwendung des Trennlacks haftet der erhärtete Fugenkitt so fest an den Plattenoberflächen, dass er nur mit einer Spachtel abgestoßen werden kann. Dies ist sehr zeitintensiv.The in organic solvents detached varnish is applied to the dry plate surface several times with lambskin wool or Applied nylon. After the release varnish has dried, it is applied to synthetic resins based grout putty slurried in the joints and with a rubberized smoothing tool pressed into the joints. The hardened joint cement adheres despite the application of the release lacquer so tight to the plate surfaces, that it can only be pushed off with a spatula. It is very time-consuming.

Mit der vorliegenden Erfindung wird ein Verfahren zur Verfugung von Boden- und Wandbelägen aus Kacheln gestellt, das die Entfernung von überschüssigem Verfugungsmaterial von den Oberflächen der verfugten Platten, Fliesen oder Kacheln wesentlich erleichtert, sowie für dieses Verfahren geeignete Trennlackzusammensetzungen.With The present invention provides a method of disposing Floor and wall coverings Tiled the removal of excess grouting material from the surfaces the grouted slabs, tiles or tiles much easier, also for this process suitable release lacquer compositions.

Überraschenderweise wurde gefunden, dass die Haftung zwischen Verfugungsmaterial und Plattenoberfläche stark vermindert wird, wenn vor der Applikation des Verfugungsmaterials auf die Oberflächen der Platten, Fliesen oder Kacheln silan- bzw. siloxanbasierende Lösungen aufgetragen wurden. Überschüssiges erhärtetes Verfugungsmitttel lässt sich dann zeitsparend und einfach mit mechanisch Mitteln von den Oberflächen der Platten, Fliesen oder Kacheln entfernen.Surprisingly it was found that the adhesion between the grouting material and the board surface was strong is reduced if before the application of the grouting material on the surfaces of slabs, tiles or tiles based on silane or siloxane solutions were applied. Excess hardened grout can be removed then time-saving and easy with mechanical means from the surfaces of the Remove slabs, tiles or tiles.

Die Silane bzw. Siloxane werden über gängige Syntheseverfahren wie z. B. den Sol-Gel-Prozess hergestellt. Das erfindungsgemäße Trennlack basiert auf einem oder mehreren Silanen mit einer Zusammensetzung entsprechend der allgemeinen der allgemeinen Formel Rx-Si-A4-x (I)worin die Reste A gleich oder verschieden sind und Hydroxylgruppen oder hydrolytisch abspaltbare Gruppen darstellen, die Reste R gleich oder verschieden sind und hydrolytisch nicht abspaltbare Gruppen darstellen und x den Wert 0, 1, 2 oder 3 hat, wobei bei mindestens 50 % der Stoffmenge der Silane x ≥ 1 ist.The silanes or siloxanes are using common synthetic methods such. B. manufactured the sol-gel process. The release lacquer according to the invention is based on one or more silanes with a composition corresponding to the general formula R x -Si-A 4-x (I) wherein the radicals A are identical or different and represent hydroxyl groups or hydrolytically removable groups, the radicals R are identical or different and represent hydrolytically non-removable groups and x has the value 0, 1, 2 or 3, with at least 50% of the amount of the Sila ne x ≥ 1.

Einzelheiten des Sol-Gel-Prozesses sind bei C. J. Brinker, G. W. Scherer: „Sol-Gel Science – The Physics and Chemistry of Sol-Gel-Processing", Academic Press, Boston, San Diego, New York, Sydney (1990) und in den DE 19 41 191 , DE 37 19 339 , DE 40 20 316 und DE 42 17 432 beschrieben. Dort sind auch spezielle Beispiele für die erfindungsgemäß einsetzbaren Silane (I) sowie deren hydrolytisch abspaltbare Reste A und hydrolytisch nicht abspaltbare Reste R angegeben.Details of the sol-gel process are available from CJ Brinker, GW Scherer: "Sol-Gel Science - The Physics and Chemistry of Sol-Gel-Processing", Academic Press, Boston, San Diego, New York, Sydney (1990) and in the DE 19 41 191 . DE 37 19 339 . DE 40 20 316 and DE 42 17 432 described. There, specific examples of the silanes (I) which can be used according to the invention and their hydrolytically removable radicals A and hydrolytically non-removable radicals R are also given.

Bevorzugte Beispiele für hydrolytisch abspaltbare Gruppen A sind Wasserstoffatome, Halogenatome (Fluor, Chlor, Brom und Iod, insbesondere Chlor und Brom), Alkoxy (insbesondere C2-4-Alkoxy, wie z. B. Ethoxy, n-Propoxy, i-Propoxy und Butoxy), Aryloxy (insbesondere C6-10-Aryloxy, z. B. Phenoxy), Alkaryloxy (z. B. Benzyloxy), Acyloxy (insbesondere C1-4-Acyloxy, wie z. B. Acetoxy und Propionyloxy) und Alkylcarbonyl (z. B. Acetyl). Ebenfalls geeignete Reste A sind Aminogruppen (z. B. Mono- oder Dialkyl-, -aryl- und -aralkylamingruppen mit den oben genannten Alkyl-, Aryl- und Aralkylresten), Amidgruppen (z. B. Benzamino) und Aldoxim- oder Ketoximgruppen. Zwei oder drei Reste A können zusammen auch eine das Si-Atom komplexierende Gruppe bilden, wie dies z. B. bei Si-Polyolkomplexen der Fall ist, die sich von Glykol, Glycerin oder Brenzkatechin ableiten. Besonders bevorzugte Reste A sind C2-4-Alkoxygruppen, insbesondere Ethoxygruppen.Preferred examples of groups A which can be split off hydrolytically are hydrogen atoms, halogen atoms (fluorine, chlorine, bromine and iodine, in particular chlorine and bromine), alkoxy (in particular C 2-4 -alkoxy, such as, for example, ethoxy, n-propoxy, i-propoxy) and butoxy), aryloxy (especially C 6-10 aryloxy, e.g. phenoxy), alkaryloxy (e.g. benzyloxy), acyloxy (especially C 1-4 acyloxy such as acetoxy and propionyloxy) and Alkylcarbonyl (e.g. acetyl). Likewise suitable radicals A are amino groups (for example mono- or dialkyl, aryl and aralkylamine groups with the above-mentioned alkyl, aryl and aralkyl radicals), amide groups (for example benzamino) and aldoxime or ketoxime groups. Two or three radicals A together can also form a group that complexes the Si atom, as described, for. B. is the case with Si polyol complexes derived from glycol, glycerol or pyrocatechol. Particularly preferred radicals A are C 2-4 alkoxy groups, especially ethoxy groups.

Die hydrolytisch nicht abspaltbaren Reste R sind vorzugsweise ausgewählt aus Alkyl (insbesondere C1-4-Alkyl, wie Methyl, Ethyl, Propyl und Butyl), Alkenyl (insbesondere C2-4-Alkenyl, wie z. B. Vinyl, 1-Propenyl, 2-Propenyl und Butenyl), Alkinyl (insbesondere C2-4-Alkinyl, wie Acethylenyl und Propargyl), Aryl(insbesondere C6-10-Aryl, wie z. B. Phenyl und Naphthyl) und den entsprechenden Alkaryl- und Arylalkylgruppen. Auch diese Gruppen können gegebenenfalls einen oder mehrere übliche Substituenten, z. B. Halogene-, Alkoxy-, Hydroxy-, Amino- oder Epoxidgruppen aufweisen.The hydrolytically non-releasable radicals R are preferably selected from alkyl (in particular C 1-4 -alkyl, such as methyl, ethyl, propyl and butyl), alkenyl (in particular C 2-4 -alkenyl, such as, for example, vinyl, 1-propenyl) , 2-propenyl and butenyl), alkynyl (especially C 2-4 alkynyl, such as acethyleneyl and propargyl), aryl (especially C 6-10 aryl, such as phenyl and naphthyl) and the corresponding alkaryl and arylalkyl groups , These groups can optionally one or more conventional substituents, for. B. Halogens, alkoxy, hydroxy, amino or epoxy groups.

Die oben genannten Alkyl-, Alkenyl- und Alkinylgruppen schließen die entsprechenden cyclischen Reste, wie z. B. Cyclopropyl, Cyclopentyl und Cyclohexyl, ein. Besonders bevorzugte Reste R sind gegebenenfalls substituierte C1-4-Alkylgruppen, insbesondere Methyl und Ethyl, und gegebenenfalls substituierte C6-10-Arylgruppen, insbesondere Phenylreste.The above-mentioned alkyl, alkenyl and alkynyl groups include the corresponding cyclic radicals, such as. B. cyclopropyl, cyclopentyl and cyclohexyl. Particularly preferred radicals R are optionally substituted C 1-4 alkyl groups, in particular methyl and ethyl, and optionally substituted C 6-10 aryl groups, in particular phenyl radicals.

Die Verwendung von Silanen mit einer oder mehreren Gruppen R, in denen Wasserstoffatome durch Heteroatome substituiert sind, empfiehlt sich insbesondere dann, wenn dem Trennlack besondere Eigenschaften wie beispielsweise Hydrophobie verliehen werden sollen. Beispielsweise kann durch Einführung von Fluoratomen (z. B. in Form von substituierten aliphatischen (insbesondere Alkyl- Resten) ein Trennlack erhalten werden, der Wasser-, Schmutz-, Staub- und Öl-abweisende Eigenschaften aufweist.The Use of silanes with one or more groups R in which Hydrogen atoms are substituted by heteroatoms, recommends especially when the release coating has special properties such as hydrophobicity. For example can by introduction fluorine atoms (e.g. in the form of substituted aliphatic (in particular alkyl residues) a release lacquer can be obtained Water, dirt, dust and oil repellent Has properties.

Beispiele für Silane der allgemeinen Formel (I) und aus diesen Silanen durch Polykondensation gebildete Siloxane sind folgende Verbindungen:
Si(OC2H5)4, Si(O-n- oder i-C3H7)4-Si(OC4H9)4, SiCl4, Si(OOCCH3)4, CH3-SiCl3, CH3-Si(OC2H5)3, C2H5-SiCl3, C2H5-Si(OC2H5)3, C3H7-Si(OC2H5)3, C6H5-Si-(OC2H5)3, C6H5-Si(OC2H5)3, (C2H5O)3-Si-C3H6-Cl, (CH3)2SiCl2, (CH3)2Si(OC2H5)2, (CH3)2Si-(OC2H5)2, (CH3)2Si(OH)2, (C6H5)2SiCl2, (C6H5)2Si(OC2H5)2, (C6H5)2Si(OC2H5)2, (i-C3H7)3SiOH, CH2=CH-Si(OOCCH3)3, CH2=CH-SiCl3, CH2=CH-Si(OC2H5)3, CH2=CHSi(OC2H5)3, HSiCl3, CH2=CH-Si(OC2H4OCH3)3, CH2=CH-CH2-Si(OC2H5)3, CH2=CH-CH2-Si(OC2H5)3, CH2=CH-CH2-Si(OOCCH3)3, CH2=C(CH3)COO-C3H7-Si-(OC2H5)3, CH2=C(CH3)-COO-C3H7-Si(OC2H5)3, n-C6H13-CH2-CH2-Si(OC2H5)3, n-C8H17-CH2-CH2-Si(OC2H5)3,

Figure 00060001
Examples of silanes of the general formula (I) and siloxanes formed from these silanes by polycondensation are the following compounds:
Si (OC 2 H 5 ) 4 , Si (On- or iC 3 H 7 ) 4 -Si (OC 4 H 9 ) 4 , SiCl 4 , Si (OOCCH 3 ) 4 , CH 3 -SiCl 3 , CH 3 -Si (OC 2 H 5 ) 3 , C 2 H 5 -SiCl 3 , C 2 H 5 -Si (OC 2 H 5 ) 3 , C 3 H 7 -Si (OC 2 H 5 ) 3 , C 6 H 5 -Si - (OC 2 H 5 ) 3 , C 6 H 5 -Si (OC 2 H 5 ) 3 , (C 2 H 5 O) 3 -Si-C 3 H 6 -Cl, (CH 3 ) 2 SiCl 2 , ( CH 3 ) 2 Si (OC 2 H 5 ) 2 , (CH 3 ) 2 Si (OC 2 H 5 ) 2 , (CH 3 ) 2 Si (OH) 2 , (C 6 H 5 ) 2 SiCl 2 , ( C 6 H 5 ) 2 Si (OC 2 H 5 ) 2 , (C 6 H 5 ) 2 Si (OC 2 H 5 ) 2 , (iC 3 H 7 ) 3 SiOH, CH 2 = CH-Si (OOCCH 3 ) 3 , CH 2 = CH-SiCl 3 , CH 2 = CH-Si (OC 2 H 5 ) 3 , CH 2 = CHSi (OC 2 H 5 ) 3 , HSiCl 3 , CH 2 = CH-Si (OC 2 H 4 OCH 3 ) 3 , CH 2 = CH-CH 2 -Si (OC 2 H 5 ) 3 , CH 2 = CH-CH 2 -Si (OC 2 H 5 ) 3 , CH 2 = CH-CH 2 -Si (OOCCH 3 ) 3 , CH 2 = C (CH 3 ) COO-C 3 H 7 -Si- (OC 2 H 5 ) 3 , CH 2 = C (CH 3 ) -COO-C 3 H 7 -Si (OC 2 H 5 ) 3 , nC 6 H 13 -CH 2 -CH 2 -Si (OC 2 H 5 ) 3 , n-C8H 17 -CH 2 -CH 2 -Si (OC 2 H 5 ) 3 ,
Figure 00060001

Als Lösungsmittel für die Silane oder Siloxane dienen Alkohole, bevorzugt Ethanol.As solvent for the Silanes or siloxanes serve alcohols, preferably ethanol.

Durch den Auftrag der erfindungsgemäßen Silan- bzw. Siloxan-basierenden Trennlacke allein oder ggf. in Kombination mit einem konventionellen Trennlack, basierend auf in organischen Lösemitteln gelösten thermoplastischen Copolymere (1, 4), auf die Plattenoberflächen lassen sich kunstharzbasierende bzw. hydraulisch abbindende Verfugesysteme durch Einsatz von Hochdruckreinigern leicht von den Oberflächen der Platten, Fliesen, Kacheln oder Klinker (Im folgenden werden Platten, Fliesen, Kacheln und Klinker der Einfachheit halber verallgemeinernd als „Platten" bezeichnet) entfernen. Dies trifft sowohl für keramische Platten, Fliesen, Kacheln oder Klinker zu als auch solche aus Steinzeug, Kunststein, Beton oder Marmor.By the application of the silane according to the invention or siloxane-based release lacquers alone or in combination, if necessary with a conventional release coating based on organic Solvents dissolved thermoplastic Copolymers (1, 4), on the plate surfaces can be synthetic resin-based or hydraulically setting jointing systems using high-pressure cleaners easily from the surfaces of slabs, tiles, tiles or clinker (in the following Remove slabs, tiles, tiles and clinker for the sake of simplicity, generally referred to as "slabs"). This applies to both ceramic slabs, tiles, tiles or clinker too as well made of stoneware, artificial stone, concrete or marble.

Der erfindungsgemäße Silan- oder Siloxan-basierende Trennlack wird auf die Plattenoberflächen aufgetragen und entweder bei Raumtemperatur ausgehärtet oder bei höheren Temperaturen, bevorzugt Temperaturen zwischen 50 und 280 °C mindestens 5 Sekunden lang eingebrannt. Optional wird danach noch eine Schicht eines konventionellen Trennlacks aufgetragen und trocknen gelassen. Danach werden die Fugen im Schlämmverfahren oder mittels Fugkelle oder Rüttelverfahren mit der kunstharzbasierenden oder hydraulisch abbindenden Verfugungsmasse gefüllt. Nach dem Härten der Verfugungsmasse lässt sich überschüssiges Verfugungsmaterial leicht mit mechanischen Hilfsmitteln von den Oberflächen der Platten entfernen. Für die Reinigung der Plattenoberflächen wird zweckmäßigerweise ein Hochdruckreiniger, beispielsweise ein beheizbarer Hochdruckreiniger oder eine andere den Boden mit mechanischen Mitteln reinigende Bodenreinigungsmaschine, beispielsweise eine Saugkehrmaschine oder eine Dreischeibenmaschine benutzt. Jedoch wird durch die Anwendung des erfindungsgemäßen Trennlacks auch die Entfernung überschüssigen Verfugungsmaterials von Hand mit einem mechanischen Hilfsmittel, beispielsweise einer Kelle oder einem Spachtel, wesentlich erleichtert.The silane or siloxane-based release lacquer according to the invention is applied to the plate surfaces and either cured at room temperature or baked at higher temperatures, preferably temperatures between 50 and 280 ° C., for at least 5 seconds. Optionally, a layer of a conventional release coating is then applied and left to dry. The joints are then filled with the synthetic resin-based or hydraulically setting jointing compound using the grouting method or a trowel or vibrating method. After the grouting compound has hardened, excess grouting material can easily be removed using mechanical aids Remove surfaces from the panels. A high-pressure cleaner, for example a heatable high-pressure cleaner or another floor cleaning machine that cleans the floor with mechanical means, for example a suction sweeper or a three-disc machine, is expediently used for cleaning the plate surfaces. However, the use of the release lacquer according to the invention also makes it much easier to remove excess grouting material by hand with a mechanical aid, for example a trowel or spatula.

Das Verfahren kann für Fugenbreiten von 0,2 bis 4 mm angewandt werden. Fugen mit Tiefen über 30 mm sind in mindestens zwei Arbeitsgängen zu füllen.The Procedure can for Joint widths of 0.2 to 4 mm can be used. Joints with depths over 30 mm are in at least two work steps to fill.

Die erfindungsgemäßen Trennlacke und das erfindungsgemäße Verfahren sind für die Verfugung und anschließende Reinigung von Fliesen, Kacheln, Platten, Klinkern, Spaltplatten und Mosaik aus Keramik, Kunststein, Steinzeug, Beton oder Marmor im Wand- und Bodenbereich sowohl für Innen- als auch für Außenanwendungen geeignet. Anwendungsbereiche gibt es beispielsweise in der chemischen, pharmazeutischen, Lebensmittel- und Elektronikindustrie, insbesondere in Produktionshallen, Schlachthöfen, Molkereien, Großküchen, Brauereien, Batterieräumen, Schwimm- und Heilbädern, Duschräumen, Bädern, Verkaufsräumen, Sport- und Freizeitbauten sowie anderen Bereichen, in denen chemische oder hohe mechanische Belastungen auftreten.The release lacquers according to the invention and the method according to the invention are for the grouting and subsequent Cleaning of tiles, tiles, slabs, clinker, split tiles and mosaic made of ceramic, artificial stone, stoneware, concrete or marble in the wall and floor area for both indoor and outdoor applications suitable. There are areas of application, for example, in chemical, pharmaceutical, Food and electronics industry, especially in production halls, slaughterhouses, dairies, Commercial kitchens, breweries, Battery rooms, Swimming pools and spas, shower rooms, bathrooms, sales rooms, sports and recreational buildings as well as other areas where chemical or high mechanical loads occur.

Wegen der erleichterten Entfernung überschüssiger Verfugungsmasse von den Plattenoberflächen ist das erfindungsgemäße Verfahren besonders geeignet, farbige, insbesondere schwarze und/oder leitfähige hydraulisch abbindende Verfugungsmassen zu applizieren.Because of the easier removal of excess grout from the plate surfaces is the inventive method particularly suitable, colored, especially black and / or conductive hydraulic to apply setting jointing compounds.

Beispiel: Verfugung eines gefliesten Bodens oder einer gefliesten WandExample: grouting one tiled floor or wall

Nach dem Verlegung der Fliesen erfolgt der Trennlackauftrag. Der erfindungsgemäße auf Silanen bzw. Siloxanen basierende Trennlack wird mit der Mohairrolle (kurze Haare) gleichmäßig und deckend auf die trockene Plattenoberfläche aufgetragen.To The separating varnish is applied when the tiles are laid. The inventive on silanes or Release varnish based on siloxanes is used with the mohair roller (short hair) evenly and applied opaque to the dry board surface.

Nach dem kompletten Abtrocknen des Trennlacks wird ein konventioneller Trennlack auf Basis von in organischen Lösemitteln gelösten thermoplastischen Copolymeren (konventioneller Trennlack) ebenfalls gleichmäßig und deckend mit der Lammfellrolle aufgetragen. Bei beiden Aufträgen müssen die Kanten der Fliesen und die Fugen frei von Trennlack bleiben.To the complete drying of the release varnish becomes a conventional one Release lacquer based on thermoplastic dissolved in organic solvents Copolymers (conventional release lacquer) also uniform and applied with the lambskin roller. For both orders, the The edges of the tiles and the joints remain free of release lacquer.

Nach dem Trocknen des Trennlacks wird der sorgfältig gemischte Fugenkitt in die Fugen eingeschlämmt und mit einem Gummifugenbrett lunkerfrei in die Fugen gedrückt. Die Schlämmmasse sollte diagonal zum Fugenverlauf aus Gründen des sparsamen Materialeinsatzes möglichst dünn abgezogen werden, da andernfalls eine unnötig große Menge überschüssigen Verfugungsmaterials wieder von der Oberfläche entfernt werden muss.To After the release varnish has dried, the carefully mixed joint filler in the joints slurried and pressed into the joints with a rubber joint board without voids. The Schlämmmasse should be diagonal to the course of the joint for reasons of economical use of material preferably be peeled off thinly otherwise an unnecessary one size Amount of excess grouting material again from the surface must be removed.

Als Fugenkitt können sowohl kunstharzbasierende oder hydraulisch abbindende Kitte verwendet werden. Nach Erhärten der Verfugungsmasse wird der Trennlack mit einem beheizten Hochdruckreiniger mit dem dazugehörigen Flächenreiniger abgestoßen.As Grout can both resin-based or hydraulically setting putties are used become. After hardening The jointing compound becomes the jointing compound with a heated high-pressure cleaner with the corresponding one surface cleaner repelled.

Obwohl die Erfindung in vorstehendem Beispiel in Zusammenhang mit der Verfugung nach dem Schlämmverfahren beschrieben wurde, sei darauf hingewiesen, dass das erfindungsgemäße Verfahren und der erfindungsgemäße Trennlack auch anwendbar ist, wenn die Fugen mittels Fugkelle oder Rüttelverfahren mit der kunstharzbasierenden oder hydraulisch abbindenden Verfugungsmasse gefüllt werden.Even though the invention in the above example in connection with the grouting after the slurry process has been described, it should be noted that the inventive method and the release lacquer according to the invention is also applicable if the joints are made using a trowel or vibrating method with the synthetic resin-based or hydraulically setting jointing compound filled become.

Claims (28)

Verfahren zum Verfüllen von Fugen zwischen einzelnen Platten aus Keramik, Kunststein, Steinzeug, Beton oder Marmor in Boden- oder Wandbelägen, umfassend die Schritte – Auftragen eines Trennlacks, der mindestens ein in einem Lösungsmittel gelöstes Silan der allgemeinen Formel Rx-Si-A4-x (I) worin die Reste A gleich oder verschieden sind und Hydroxylgruppen oder hydrolytisch abspaltbare Gruppen darstellen, die Reste R gleich oder verschieden sind und hydrolytisch nicht abspaltbare Gruppen darstellen und x den Wert 0, 1, 2 oder 3 hat, wobei bei mindestens 50 % der Stoffmenge der Silane x ≥ 1 ist, oder mindestens ein in einem Lösungsmittel gelöstes durch Polykondensation aus Silanen der Zusammensetzung (I) entstandenes Siloxan enthält, auf die Oberflächen der Platten; – Trocknenlassen des Trennlacks; – Füllen der Fugen mit einem Verfugungsmaterial; – Härtenlassen des Verfugungsmaterials und – mechanische Entfernung überschüssigen Verfugungsmaterials von den Oberflächen der Platten.A method for filling joints between individual plates made of ceramic, artificial stone, stoneware, concrete or marble in floor or wall coverings, comprising the steps - applying a release lacquer containing at least one silane of the general formula R x -Si-A 4 dissolved in a solvent -x (I) in which the radicals A are identical or different and represent hydroxyl groups or hydrolytically removable groups, the radicals R are identical or different and represent hydrolytically non-removable groups and x has the value 0, 1, 2 or 3, where at least 50% of the amount of substance of the silanes x ≥ 1, or contains at least one siloxane dissolved in a solvent by polycondensation from silanes of the composition (I), on the surfaces of the plates; - Allowing the release lacquer to dry; - filling the joints with a grouting material; - allowing the grouting material to harden and - mechanically removing excess grouting material from the surfaces of the panels. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass die hydrolytisch abspaltbaren Gruppen A in mindestens einem Silan (I) Wasserstoffatome, Halogenatome, Alkoxygruppen, Aryloxygruppen, Alkaryloxygruppen, Acyloxygruppen, Alkylcarbonylgruppen, Aminogruppen, Amidgruppen, Aldoxim- oder Ketoximgruppen sind.A method according to claim 1, characterized in that the hydrolytically removable groups A in at least one silane (I) hydrogen atoms, halogen atoms, alkoxy groups, aryloxy groups, alkaryloxy groups, acyloxy groups, alkylcarbonyl groups, amino groups, amide groups, aldoxime or are ketoxime groups. Verfahren nach Anspruch 2, dadurch gekennzeichnet, dass die hydrolytisch abspaltbaren Gruppen A in mindestens einem Silan (I) Methoxy- oder Ethoxygruppen sind.A method according to claim 2, characterized in that the hydrolytically removable groups A in at least one Silane (I) are methoxy or ethoxy groups. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass in mindestens einem Silan (I) zwei oder drei hydrolytisch abspaltbare Reste A zusammen eine das Silicium-Atom komplexierende Gruppe bilden.A method according to claim 1, characterized in that in at least one silane (I) two or three hydrolytically removable Residues A together form a group complexing the silicon atom. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass die hydrolytisch nicht abspaltbaren Gruppen R in mindestens einem Silan (I) Alkylgruppen, Alkenylgruppen, Alkinylgruppen, Arylgruppen, Alkarylgruppen, Arylalkylgruppen oder cyclische Alkyl-, Alkenyl- oder Alkinylgruppen sind.A method according to claim 1, characterized in that the hydrolytically non-removable groups R in at least a silane (I) alkyl groups, alkenyl groups, alkynyl groups, aryl groups, alkaryl groups, Arylalkyl groups or cyclic alkyl, alkenyl or alkynyl groups are. Verfahren nach Anspruch 5, dadurch gekennzeichnet, dass die hydrolytisch nicht abspaltbaren Gruppen R in mindestens einem Silan (I) Methyl,- Ethyl- oder Phenylreste sind.A method according to claim 5, characterized in that the hydrolytically non-removable groups R in at least a silane (I) are methyl, ethyl or phenyl radicals. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass in den hydrolytisch nicht abspaltbaren Gruppen R in mindestens einem Silan (I) Wasserstoffatome durch Heteroatome substituiert sind.A method according to claim 1, characterized in that in the hydrolytically non-cleavable groups R in at least a silane (I) hydrogen atom is substituted by heteroatoms are. Verfahren nach Anspruch 7, dadurch gekennzeichnet, dass in den hydrolytisch nicht abspaltbaren Gruppen R in mindestens einem Silan (I) Wasserstoffatome durch Fluoratome substituiert sind.A method according to claim 7, characterized in that in the hydrolytically non-cleavable groups R in at least a silane (I) hydrogen atoms are substituted by fluorine atoms. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass ein hydrophob wirkender Trennlack, der mindestens ein in einem Lösungsmittel gelöstes Silan der allgemeinen Formel Rx-Si-A4-x (I) oder mindestens ein in einem Lösungsmittel gelöstes durch Polykondensation aus Silanen der Zusammensetzung (I) entstandenes Siloxan enthält, benutzt wird.A method according to claim 1, characterized in that a hydrophobic separating lacquer, the at least one silane dissolved in a solvent of the general formula R x -Si-A 4-x (I) or at least one dissolved in a solvent by polycondensation from silanes of the composition (I) contains the resulting siloxane is used. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass mindestens ein Silan der Formel (I) oder mindestens ein durch Polykondensation von Silanen der Zusammensetzung (I) entstandene Siloxan in einem Alkohol gelöst ist.A method according to claim 1, characterized in that at least one silane of formula (I) or at least one by Polycondensation of silanes of the composition (I) Siloxane dissolved in an alcohol is. Verfahren nach Anspruch 10, dadurch gekennzeichnet, dass mindestens ein Silan der Formel (I) oder mindestens ein durch Polykondensation von Silanen der Zusammensetzung (I) entstandene Siloxan in Ethanol gelöst ist.A method according to claim 10, characterized in that at least one silane of formula (I) or at least one by Polycondensation of silanes of the composition (I) Siloxane dissolved in ethanol is. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass der auf die Plattenoberflächen aufgetragene, mindestens ein in einem Lösungsmittel gelöstes Silan der allgemeinen Formel Rx-Si-A4-x (I) oder mindestens ein in einem Lösungsmittel gelöstes durch Polykondensation von Silanen der Zusammensetzung (I) gebildetes Siloxan enthaltende Trennlack bei Raumtemperatur ausgehärtet oder bei Temperaturen im Bereich von 50 bis 280 °C mindestens 5 Sekunden lang eingebrannt wird.A method according to claim 1, characterized in that the applied to the plate surfaces, at least one dissolved in a solvent silane of the general formula R x -Si-A 4-x (I) or at least one dissolved in a solvent by polycondensation of silanes of the composition (I) formed release lacquer containing siloxane is cured at room temperature or baked at temperatures in the range from 50 to 280 ° C. for at least 5 seconds. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass nach dem Trocknen oder Einbrennen des mindestens ein in einem Lösungsmittel gelöstes Silan der allgemeinen Formel Rx-Si-A4-X (I) oder mindestens ein in einem Lösungsmittel gelöstes durch Polykondensation von Silanen der Zusammensetzung (I) gebildetes Siloxan enthaltenden Trennlacks noch eine weitere Schicht aus einem Trennlack aus einem in einem organischen Lösungsmittel gelösten Copolymer (1) aus Mono- und Diolefinen (2) oder aus Mono- bzw. Diolefinen mit anderen Vinylmonomeren, einem halogenhaltigen Polymer (3) oder einem Copolymerisat (4) der halogenhaltigen Polymere (3) und der Copolymere (1) aufgetragen und trocknen gelassen wird.A method according to claim 1, characterized in that after drying or baking the at least one silane dissolved in a solvent of the general formula R x -Si-A 4-X (I) or at least one dissolved in a solvent by polycondensation of silanes of the composition (I) separating varnish containing siloxane, yet another layer of a separating varnish made of a copolymer (1) dissolved in an organic solvent from mono- and diolefins (2) or from mono- or diolefins with other vinyl monomers, a halogen-containing polymer (3) or a copolymer (4) of the halogen-containing polymers (3) and the copolymers (1) is applied and allowed to dry. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass die Verfugungsmassse mittels Fugkelle oder im Rüttelverfahren oder im Schlämmverfahren aufgetragen wird.A method according to claim 1, characterized in that the grouting dimensions by means of a trowel or vibrating method or in the slurry process is applied. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass die Fugen mit einer kunstharzbasierenden oder einer hydraulisch abbindenden Verfugungsmasse gefüllt werden.A method according to claim 1, characterized in that the joints with a resin-based or a hydraulic setting compound filled become. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass die Fugen mit einer farbigen oder schwarzen oder/und leitfähig eingestellten Verfugungsmasse gefüllt werden.A method according to claim 1, characterized in that the joints are set with a colored or black or / and conductive Grouting compound filled become. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass nach dem Aushärten des Verfugungsmaterials mit einem Hochdruckreiniger oder einer mit mechanischen Mitteln den Boden reinigenden Bodenreinigungsmaschine oder von Hand mit einem mechanischen Hilfsmittel überschüssiges Verfugungsmaterial von den Oberflächen der Platten entfernt wird.A method according to claim 1, characterized in that after curing of the grouting material with a pressure washer or one with mechanical Means the floor cleaning floor cleaning machine or by hand with a mechanical aid excess grouting material from the surfaces the plates are removed. Trennlack zur Verminderung der Haftung zwischen den Oberflächen der Platten eines Boden- oder Wandbelags und einem Verfugungsmaterial zum Verfüllen der zwischen diesen Platten befindlichen Fugen, dadurch gekennzeichnet, dass er mindestens ein in einem Lösungsmittel gelöstes Silan der allgemeinen Formel Rx-Si-A4-x (I) enthält, worin die Reste A gleich oder verschieden sind und Hydroxylgruppen oder hydrolytisch abspaltbare Gruppen darstellen, die Reste R gleich oder verschieden sind und hydrolytisch nicht abspaltbare Gruppen darstellen und x den Wert 0, 1, 2 oder 3 hat, wobei bei mindestens 50 % der Stoffmenge der Silane x ≥ 1 ist, oder mindestens ein durch Polykondensation aus Silanen der Zusammensetzung (I) entstandenes Siloxan.Release lacquer to reduce the adhesion between the surfaces of the plates of a floor or wall covering and a jointing material for filling the joints between these plates, characterized in that it contains at least one silane of the general formula R x -Si-A 4- dissolved in a solvent. x (I) contains, in which the radicals A are identical or different and represent hydroxyl groups or hydrolytically removable groups, the radicals R are identical or different and represent hydrolytically non-removable groups and x has the value 0, 1, 2 or 3, where at at least 50% of the amount of the silanes x ≥ 1, or at least one siloxane formed by polycondensation from silanes of the composition (I). Trennlack nach Anspruch 18, dadurch gekennzeichnet, dass die hydrolytisch abspaltbaren Gruppen A in mindestens einem Silan (I) Wasserstoffatome, Halogenatome, Alkoxygruppen, Aryloxygruppen, Alkaryloxygruppen, Acyloxygruppen, Alkylcarbonylgruppen, Aminogruppen, Amidgruppen, Aldoxim- oder Ketoximgruppen sind.Release lacquer according to claim 18, characterized in that the hydrolytically removable groups A in at least one Silane (I) hydrogen atoms, halogen atoms, alkoxy groups, aryloxy groups, Alkaryloxy groups, acyloxy groups, alkylcarbonyl groups, amino groups, Amide groups, aldoxime or ketoxime groups. Trennlack nach Anspruch 19, dadurch gekennzeichnet, dass die hydrolytisch abspaltbaren Gruppen A in mindestens einem Silan (I) Ethoxygruppen sind.Release lacquer according to claim 19, characterized in that the hydrolytically removable groups A in at least one Silane (I) are ethoxy groups. Trennlack nach Anspruch 18, dadurch gekennzeichnet, dass in mindestens einem Silan (I) zwei oder drei hydrolytisch abspaltbare Reste A zusammen eine das Silicium-Atom komplexierende Gruppe bilden.Release lacquer according to claim 18, characterized in that in at least one silane (I) two or three hydrolytically removable Residues A together form a group complexing the silicon atom. Trennlack nach Anspruch 18, dadurch gekennzeichnet, dass die hydrolytisch nicht abspaltbaren Gruppen R in mindestens einem Silan (I) Alkylgruppen, Alkenylgruppen, Alkinylgruppen, Arylgruppen, Alkarylgruppen, Arylalkylgruppen oder cyclische Alkyl-, Alkenyl- oder Alkinylgruppen sind.Release lacquer according to claim 18, characterized in that the hydrolytically non-removable groups R in at least a silane (I) alkyl group, alkenyl group, alkynyl group, aryl group, Alkaryl groups, arylalkyl groups or cyclic alkyl, alkenyl or are alkynyl groups. Trennlack nach Anspruch 22, dadurch gekennzeichnet, dass die hydrolytisch nicht abspaltbaren Gruppen R in mindestens einem Silan (I) Methyl,- Ethyl- oder Phenylreste sind.Release lacquer according to claim 22, characterized in that the hydrolytically non-removable groups R in at least a silane (I) are methyl, ethyl or phenyl radicals. Trennlack nach Anspruch 1, dadurch gekennzeichnet, dass in den hydrolytisch nicht abspaltbaren Gruppen R in mindestens einem Silan (I) Wasserstoffatome durch Heteroatome substituiert sind.Release lacquer according to claim 1, characterized in that in the hydrolytically non-cleavable groups R in at least a silane (I) hydrogen atom is substituted by heteroatoms are. Trennlack nach Anspruch 24, dadurch gekennzeichnet, dass in den hydrolytisch nicht abspaltbaren Gruppen R in mindestens einem Silan (I) Wasserstoffatome durch Fluoratome substituiert sind.Release lacquer according to claim 24, characterized in that in the hydrolytically non-cleavable groups R in at least a silane (I) hydrogen atoms are substituted by fluorine atoms. Trennlack nach Anspruch 18, dadurch gekennzeichnet, dass mindestens ein Silan der Formel (I) oder das mindestens eine durch Polykondensation von Silanen der Formel (I) entstandene Siloxan in einem Alkohol gelöst ist.Release lacquer according to claim 18, characterized in that at least one silane of the formula (I) or the at least one siloxane formed by polycondensation of silanes of the formula (I) dissolved in an alcohol is. Trennlack nach Anspruch 26, dadurch gekennzeichnet, dass mindestens ein Silan der Formel (I) oder das mindestens eine durch Polykondensation von Silanen der Formel (I) entstandene Siloxan in Ethanol gelöst ist.Release lacquer according to claim 26, characterized in that at least one silane of the formula (I) or the at least one siloxane formed by polycondensation of silanes of the formula (I) dissolved in ethanol is. Trennlack nach Anspruch 18, dadurch gekennzeichnet, dass die Gruppen hydrolytisch nicht abspaltbaren Gruppen R hydrophobierend wirken.Release lacquer according to claim 18, characterized in that the groups R, which cannot be split off hydrolytically, are hydrophobic Act.
DE2003149105 2003-10-17 2003-10-17 Filling the joints between tiles in floor or wall coverings comprises coating the tiles with a silane-based release lacquer before grouting the joints Expired - Fee Related DE10349105B3 (en)