DE10347578A1 - Dachstein, which contains at least two layers - Google Patents

Dachstein, which contains at least two layers Download PDF

Info

Publication number
DE10347578A1
DE10347578A1 DE2003147578 DE10347578A DE10347578A1 DE 10347578 A1 DE10347578 A1 DE 10347578A1 DE 2003147578 DE2003147578 DE 2003147578 DE 10347578 A DE10347578 A DE 10347578A DE 10347578 A1 DE10347578 A1 DE 10347578A1
Authority
DE
Germany
Prior art keywords
dachstein
coating
sand
binder
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE2003147578
Other languages
German (de)
Inventor
Andreas Dr. Ing. Drechsler
Michael Dipl.-Ing. Heise
Heinz-Werner Dr. Ing. Vissmann
Stephan Dipl.-Ing. Westphal
Henner Dipl.-Ing. Patzwall
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BMI Technical Services GmbH
Lafarge Roofing Technical Centers Ltd
Original Assignee
Lafarge Roofing Technical Centers GmbH
Lafarge Roofing Technical Centers Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lafarge Roofing Technical Centers GmbH, Lafarge Roofing Technical Centers Ltd filed Critical Lafarge Roofing Technical Centers GmbH
Priority to DE2003147578 priority Critical patent/DE10347578A1/en
Priority to PCT/EP2004/011144 priority patent/WO2005037725A2/en
Publication of DE10347578A1 publication Critical patent/DE10347578A1/en
Withdrawn legal-status Critical Current

Abstract

Die Erfindung betrifft einen Dachstein, der aus zwei Schichten oder Lagen besteht. Die untere Lage ist ein Grundkörper bzw. Betondachsteinrohling, während die obere Lage eine Beschichtung ist, die wenigstens Sand und ein Bindemittel enthält. Der Sand in der Beschichtung weist Körner verschiedener Größe auf. Der Durchmesser der größten Körner ist dabei maximal gleich groß wie die Dicke der Beschichtung, während die kleinsten Körner einen Durchmesser aufweisen, der minimal ein Drittel der Dicke der Beschichtung beträgt.The invention relates to a roof tile, which consists of two layers or layers. The bottom layer is a concrete roof tile blank, while the top layer is a coating containing at least sand and a binder. The sand in the coating has grains of different sizes. The diameter of the largest grains is at most equal to the thickness of the coating, while the smallest grains have a diameter which is at least one third of the thickness of the coating.

Description

Die Erfindung betrifft einen Dachstein nach dem Oberbegriff des Patentanspruchs 1.The The invention relates to a roof tile according to the preamble of the claim 1.

Für die Dachdeckung werden häufig Betondachsteine verwendet, die aus einem hydraulischen Bindemittel, insbesondere Zement, und einem mineralischen Zuschlag bestehen. Die Herstellung dieser Betondachsteine erfolgt in der Regel im Strangpress- oder Extrusionsverfahren, wobei Biberschwänze, Falzdachsteine und Pfannen entstehen.For roofing become common Concrete roof tiles used, consisting of a hydraulic binder, cement, and a mineral aggregate. The production of these concrete roof tiles is usually carried out in extruded or extrusion processes, wherein beaver tails, rebate roof tiles and pans arise.

Bei diesem Strangpressverfahren wird auf Unterformen eine kontinuierliche Betonschicht aufgebracht und anschließend mittels Formgebungswalze und Glätter verdichtet und gegebenenfalls profiliert. Die verdichtete Frischbetonschicht wird anschließend in einer Schneidestation zu Dachstein-Formstücken gleicher Länge mit einem kopfseitigen und einem fußseitigen Rand geschnitten, wobei der fußseitige Rand zugerichtet wird.at This extrusion process is continuous on sub-forms Applied concrete layer and then by means of shaping roller and smoother compacted and optionally profiled. The compacted fresh concrete layer will follow in a cutting station to roof tile fittings of the same length with a head-end and a foot-side Edge cut, with the foot side Edge is made.

Die nach diesem Verfahren hergestellten Betondachsteine weisen sowohl am kopfseitigen Rand als auch am fußseitigen Rand eine Schnittfläche auf, die mit Poren und anderen Unregelmäßigkeiten versehen ist. Die Rauigkeit und Porosität dieser Schnittflächen sind wesentlich größer als die der verdichteten Oberseite, sodass dementsprechend die Stirnflächen dieser Betondachsteine eine schlechtere Qualität als die verdichtete Oberseite aufweisen. Außerdem neigen diese Schnittflächen verstärkt zu Ausblühungen.The Concrete roof tiles produced by this process have both on the head-side edge as well as on the foot-side edge a cut surface, the with pores and other irregularities is provided. The roughness and porosity of these cut surfaces are much larger than that of the compacted top, so that accordingly the end faces of this Concrete roof tiles a worse quality than the compacted top exhibit. Furthermore these cut surfaces tend reinforced to efflorescence.

Es ist bereits ein Verfahren zur Herstellung von Betondachsteinen bekannt, mit dem der fußseitige Rand dieser Dachsteine eine bessere Witterungsbeständigkeit und Festigkeit erhält und außerdem die Ausblühungen an dieser Stelle vermieden werden ( DE 35 22 846 C3 ). Hierbei wird beim Zuschneiden der Frischbetonschicht der fußseitige Randabschnitt vorverdichtet, und beim Zurichten wird am fußseitigen Rand des Dachstein-Formstücks innerhalb einer wenigstens 2 bis 8 mm tiefen Randzone, die an die Stirnfläche angrenzt, eine weitere Materialverdichtung vorgenommen. Außerdem wird durch diese Materialverdichtung eine von der unteren, der Unterform benachbarten Schnittkante ausgehende und sich bis zur Oberseite des Formstücks erstreckende Abrundung oder Abschrägung erzeugt. Die nach diesem Strangpressverfahren hergestellten Dachsteine weisen auf ihrer der Bewitterung ausgesetzten Oberseite eine relativ raue Oberfläche auf. Hierdurch wird die Ansiedlung von Algen, Flechten und Moosen begünstigt.A method for the production of concrete roof tiles is already known, with which the foot-side edge of these tiles is better weather resistance and strength and also the efflorescence is avoided at this point ( DE 35 22 846 C3 ). Here, when cutting the fresh concrete layer of the foot-side edge portion is precompressed, and during trimming, a further material compaction is made at the foot-side edge of the Dachstein molding within at least 2 to 8 mm deep edge zone adjacent to the end face. In addition, by this material compaction out of the lower, the lower mold adjacent cutting edge outgoing and extending up to the top of the fitting rounding or bevel generated. The roof tiles produced by this extrusion process have a relatively rough surface on their exposed to weathering top. This promotes the settlement of algae, lichens and mosses.

Es ist indessen auch ein Strangpressverfahren bekannt, mit dem man Produkte erhält, die aus zwei übereinander gelagerten Schichten aus Mörtel unterschiedlicher Zusammensetzung und Eigenschaften bestehen ( US 5 017 320 ). Mit diesem Verfahren können auch Betondachsteine hergestellt werden, die eine Beschichtung aufweisen. Kennzeichnend für dieses Verfahren ist, dass aufeinander folgende und voneinander unabhängige Extrusionen von Mörtel oder Beton erfolgen. Dies geschieht mit Hilfe von zwei hintereinander angeordneten Formstationen, deren Formwerkzeuge vom Profil her aufeinander abgestimmt sind. In der ersten Formstation wird die Betonmischung mittels einer Stachelwelle und eines profilierten Formwerkzeugs unter hohem Druck auf die Unterformen aufextrudiert. In der zweiten Formstation wird auf die gleiche Weise eine Beschichtungsmasse auf den profilierten Frischbetonstrang aufextrudiert. Durch diese Beschichtungsmasse wird verhindert, dass sich auf der Oberfläche von Dachsteinen Mikroorganismen ausbreiten und eine starke Verschmutzung dieser Oberfläche auftritt.However, it is also an extrusion process known, with which one receives products consisting of two superimposed layers of mortar of different composition and properties ( US 5 017 320 ). With this method, concrete roof tiles can be produced which have a coating. Characteristic of this method is that successive and independent extrusion of mortar or concrete. This is done with the help of two successively arranged forming stations whose molds are matched in profile from each other. In the first forming station, the concrete mixture is extruded by means of a spiked shaft and a profiled molding tool under high pressure on the lower molds. In the second forming station, a coating composition is extruded onto the profiled fresh concrete strand in the same way. By this coating mass prevents microorganisms spread on the surface of roof tiles and a strong contamination of this surface occurs.

Ein weiteres Verfahren für die Herstellung eines Betondachsteins mit einer aufextrudierten und/oder aufgewalzten Oberflächenbeschichtung ist aus der DE 39 32 573 C2 bekannt. Der Betondachstein besteht hierbei aus einer Grundschicht in Form einer Mischung von hydraulischen Bindemitteln, wie Portlandzement, Sand und Wasser sowie aus einer bis zu mehreren Millimetern dicken Beschichtung auf der Basis hydraulischer Bindemittel, wobei die Beschichtung im plastischen Zustand auftragbar ist. Der Betondachstein weist auf sämtlichen Flächenbereichen – außer auf der von der Bewitterungsseite abgekehrten Unterseite – die aufextrudierte und/oder aufgewalzte Beschichtung sowie eventuelle Zusatzschichten auf. Die Beschichtung als solche enthält: Zement, Sand mit einer Sieblinie bis zu 2 mm, zementverträgliche, polymere Verbindungen aus durch Polymerisation von ungesättigten, monomeren Verbindungen, Füllstoffe und Wasser im Verhältnis 1:1,2 bis 3,5:0,5 bis 0,05:0,15 bis 0,03:0,60 bis 0,22 sowie Farbstoffe mit Farbzuschlägen in der üblichen Zugabenmenge.Another method for the production of a concrete tile with an extruded and / or rolled surface coating is known from DE 39 32 573 C2 known. The concrete roof tile here consists of a base layer in the form of a mixture of hydraulic binders, such as Portland cement, sand and water as well as a coating up to several millimeters thick based on hydraulic binders, the coating can be applied in the plastic state. The concrete roof tile has on all surface areas - except on the side facing away from the weathering underside - the extruded and / or rolled-on coating and any additional layers. The coating as such contains: cement, sand with a sieving line up to 2 mm, cement-compatible, polymeric compounds from by polymerization of unsaturated, monomeric compounds, fillers and water in the ratio 1: 1.2 to 3.5: 0.5 to 0 , 05: 0.15 to 0.03: 0.60 to 0.22 and dyes with color additions in the usual amount of addition.

Der Erfindung liegt die Aufgabe zugrunde, eine Beschichtung für Dachsteine und dergleichen zu schaffen, die verbesserte rheologische Eigenschaften besitzt.Of the Invention is based on the object, a coating for roof tiles and the like to provide the improved rheological properties has.

Diese Aufgabe wird gemäß den Merkmalen des Patentanspruchs 1 gelöst.These Task is performed according to the characteristics of Patent claim 1 solved.

Die Erfindung betrifft somit einen Dachstein, der aus zwei Schichten oder Lagen besteht. Die untere Lage ist ein Grundkörper bzw. Betondachsteinrohling, während die obere Lage eine Beschichtung ist, die wenigstens Sand und ein Bindemittel enthält. Der Sand in der Beschichtung weist Körner verschiedener Größe auf. Der Durchmesser der größten Körner ist dabei maximal gleich groß wie die Dicke der Beschichtung, während die kleinsten Körner einen Durchmesser aufweisen, der minimal ein Drittel der Dicke der Beschichtung beträgt.The invention thus relates to a roof tile, which consists of two layers or layers. The bottom layer is a concrete roof tile blank, while the top layer is a coating containing at least sand and a binder. The sand in the coating has grains of different sizes. The diameter of the largest grains is at most equal to the thickness of the coating, while the smallest grains have a diameter which is at least one third of the thickness of the coating.

Der mit der Erfindung erzielte Vorteil besteht insbesondere darin, dass die Beschichtung nahezu kräftefrei auf einem Betondachsteinrohling aufgetragen werden kann und außerdem formstabil ist. Die Eigenschaften, betreffend die Erscheinungen, welche bei einer Deformation oder beim Fließen unter Einwirkung äußerer Kräfte auftreten, die so genannten rheologischen Eigenschaften, sind erheblich verbessert. Durch das nahezu kräftefreie Aufbringen der Schicht werden Materialdurchmischungen vermieden. Da die zweite Schicht auf einem mechanisch noch nicht sehr stabilen Grundkörper aufgebracht wird, ist ein geringer Extrusionswiderstand wichtig. Außerdem lässt sich die Dicke der Beschichtung auf bis zu 1 mm reduzieren, was zu einer erheblichen Einsparung der Beschichtungsmasse und zu einer entsprechenden Senkung der Materialkosten führt. Obgleich die Beschichtungsmasse in sehr geringer Schichtdicke aufbringbar ist, gewährleistet sie dennoch eine vollständige und qualitativ hochwertige Versiegelung insbesondere der Oberfläche eines Dachsteins. Bei profilierten Dachsteinen fließt die frisch aufgetragene Beschichtungsmasse nicht von den gewölbten Bereichen der Mittelkrempe und des Deckfalzes hinab in die Wasserläufe des Dachsteins.Of the obtained with the invention advantage is in particular that the coating almost free of forces can be applied on a concrete tile blank and also dimensionally stable is. The properties, concerning the phenomena, which at a deformation or flow under the action of external forces, the so-called rheological properties are significantly improved. By the almost power-free Applying the layer material mixtures are avoided. Because the second layer on a mechanically not very stable body is applied, a low extrusion resistance is important. In addition, can be reduce the thickness of the coating down to 1 mm, resulting in a considerable savings in the coating composition and a corresponding Lowering material costs leads. Although the coating material can be applied in a very small layer thickness is guaranteed you still a complete and high-quality sealing especially the surface of a Dachstein. For profiled roof stones, the freshly applied flows Coating compound not from the arched areas of the center brim and the Deckfalzes down into the waterways of the Dachstein.

Die Erfindung wird anhand der nachfolgend genannten Darstellungen im Einzelnen beschrieben. Es zeigen:The Invention is based on the following representations in the Individual described. Show it:

1 eine Kurvendarstellung des Extrusionswiderstands in Abhängigkeit vom Verhältnis Schichtdicke Sext zu maximalem Durchmesser eines Sandkorns DmaxSand in einer Sandmischung; 1 a graph of the extrusion resistance as a function of the ratio layer thickness S ext to maximum diameter of a sand grain D max sand in a sand mixture ;

2 eine Kurvendarstellung des Extrusionswiderstands in Abhängigkeit vom Verhältnis der Höhe des Extrusionsspalts einer Extrusionsmaschine zum maximalen Durchmesser DmaxSand in einer Sandmischung; 2 a graph of the extrusion resistance as a function of the ratio of the height of the extrusion gap of an extrusion machine to the maximum diameter D max sand in a sand mixture ;

3 eine Prinzipdarstellung des Verfahrens zum Herstellen von Dachsteinen und zum Aufbringen einer Beschichtung auf die Oberfläche dieser Dachsteine. 3 a schematic representation of the method for producing roof tiles and for applying a coating on the surface of these tiles.

Die 1 zeigt den Extrusionswiderstand in Abhängigkeit vom Verhältnis der angestrebten Beschichtungsstärke Sext zum maximalen Durchmesser DmaxSand eines Sandkorns in einer Sandkornmischung, und zwar einmal bei herkömmlichen Verhältnissen und einmal gemäß der Erfindung. Die obere Kurve I stellt hierbei die herkömmlichen Verhältnisse dar, während die untere Kurve II die erfindungsgemäßen Verhältnisse darstellt. Herkömmlich bedeutet, dass nur Sand und Wasser miteinander vermischt sind, während bei der Erfindung Sand, Wasser und Zement miteinander vermischt sind. Die verwendete Sandmischung enthält in beiden Fällen in Gleichverteilung Sandkörner von einer vorgegebenen Minimalgröße bis zu einer vorgegebenen Maximalgröße.The 1 shows the extrusion resistance as a function of the ratio of the desired coating thickness S ext to the maximum diameter D max sand of a grain of sand in a sand grain mixture , once under conventional conditions and once according to the invention. The upper curve I represents the conventional conditions, while the lower curve II represents the conditions according to the invention. Conventionally means that only sand and water are mixed together, while in the invention sand, water and cement are mixed together. The sand mixture used contains in both cases in equal distribution grains of sand from a predetermined minimum size to a predetermined maximum size.

Wie man aus der Kurve II erkennt, weist die Beschichtungsmasse bei Verwendung eines Sandgrößtkorns mit einem Durchmesser Dmax, der halb so groß ist wie die aufzutragende Schichtdicke Sext, einen relativ geringen Extrusionswiderstand A. U. (= Arbitrary Units) auf, wenn es keine Überlappung des Kornbereichs des Zements und der Füllstoffe mit dem des Sands gibt. Für Sext ist bei der Kurvendarstellung der 1 eine Stärke von 1 mm angenommen. Dieser relativ niedrige Extrusionswiderstand ist deshalb überraschend, weil normalerweise der Extrusionswiderstand bei einem Größtkorn von Dmax = 0,5-facher Schichtstärke ein Maximum durchläuft – wie die Kurve I zeigt – und somit besonders ungünstig ist im Hinblick auf die Zerstörung der empfindlichen Oberfläche des Frischbetonstrangs. Eine Erklärung des überraschenden Effekts könnte darin bestehen, dass die Eigenschaften der Ausfallkörnung die Gesetzmäßigkeit der Strangextrusion kompensieren. Die Dicke Sext der Beschichtung muss bei der Extrusion in sehr engen Grenzen gehalten werden, um die Kurve II zu erhalten. Erreicht die Schichtstärke den dreifachen Größtkorn-Durchmesser, beginnt der Feinmörtel zu fließen. Eine unzureichende Definition der Dichtungsstrukturen und Beeinträchtigungen des ästhetischen Erscheinungsbildes des Dachsteins sind die Folge. Es ist deshalb nicht möglich, das Verhältnis Sext : DmaxSand zu "7" zu wählen, obwohl dort der Extrusionswiderstand noch niedriger ist.As can be seen from the curve II, when using a sand particle with a diameter D max , which is half as large as the layer thickness S ext to be applied, the coating composition has a relatively low extrusion resistance AU (= arbitrary units), if there is no overlap of the Grain range of the cement and the fillers with that of the sand are. For S ext is in the graph of the 1 assumed a thickness of 1 mm. This relatively low extrusion resistance is surprising because normally the extrusion resistance at a maximum grain of D max = 0.5 times the layer thickness passes through a maximum - as the curve I shows - and thus is particularly unfavorable in terms of the destruction of the sensitive surface of the fresh concrete strand , An explanation of the surprising effect could be that the properties of the failure granules compensate for the law of strand extrusion. The thickness S ext of the coating must be kept within very narrow limits during extrusion in order to obtain the curve II. When the layer thickness reaches three times the largest grain diameter, the fine mortar begins to flow. An inadequate definition of the sealing structures and impairment of the aesthetic appearance of the Dachstein are the result. It is therefore not possible to choose the ratio S ext : D maxSand to "7", although there the extrusion resistance is even lower.

Sinkt dagegen die Schichtstärke unter das 1,5-Fache des maximalen Korndurchmessers, findet eine zunehmende Separation von Zementleim – einer nicht-festen Mischung aus Zement und Wasser – und Sand statt, und die Oberflächenqualität verschlechtert sich drastisch. Überlappen sich die Sieblinie der Zemente und Füllstoffe mit der Sieblinie des Sands, steigt die Tendenz zur Blasenbildung stark an. Versucht man die Blasenbildung durch Wasserreduzierung der Mischung zu kompensieren, steigt der Extrusionswiderstand stark an. Unter Sieblinie wird hierbei die Korngrößenverteilung eines Schüttguts verstanden.Sinks contrast, the layer thickness below 1.5 times the maximum grain diameter, find one increasing separation of cement paste - a non-solid mixture made of cement and water - and Sand takes place, and the surface quality deteriorates drastically. overlap the grading curve of the cements and fillers with the grading curve of sand, the tendency to blistering increases sharply. Tries to compensate for bubble formation by water reduction of the mixture, the extrusion resistance increases strongly. Under Sieblinie is here the particle size distribution a bulk material understood.

In der 2 ist der Extrusionswiderstand noch einmal über dem Verhältnis von Größe des Extrusionsspalts und dem maximalen Durchmesser des Sands aufgetragen. Man erkennt hierbei, dass die Kurve einen ähnlichen Verlauf wie die Kurve in 1 hat. Dies war zu erwarten, weil der Extrusionsspalt die Beschichtungsdicke bestimmt.In the 2 the extrusion resistance is again plotted against the ratio of size of the extrusion gap and the maximum diameter of the sand. It can be seen that the curve is similar to the curve in 1 Has. This was to be expected because the extrusion gap determines the coating thickness.

Der vorstehend beschriebene Effekt hat sich auch bei Versuchen eingestellt, bei denen die aus der DE 35 22 846 C3 bekannten Betondachsteinrohlinge im Bereich des Rundschnitts beschichtet wurden. Hierzu wurden eine zweite Formstation zum Aufextrudieren der Beschichtungsmasse und eine zweite Schneidstation eingebaut, in welcher der aufextrudierte Beschichtungsmassestrang durch ein zweites Rundschnittmesser zertrennt wurde. Die Durchtrennung des Beschichtungsmassenstrangs erfolgte dabei im Bereich der mit Beschichtungsmasse ausgefüllten Lücke zwischen jeweils zwei im Unterformstrang benachbarten Rohlingen.The effect described above has also set in experiments in which the from DE 35 22 846 C3 known concrete roof blanks were coated in the region of the round section. For this purpose, a second forming station for extruding the coating composition and a second cutting station were installed, in which the extruded coating mass strand was divided by a second round cut knife. The separation of the coating composition strand was carried out in the region of the gap filled with the coating composition between two blanks each adjacent to the sub-molding strand.

In der 3 ist dies schematisch näher dargestellt, wobei mit den Buchstaben A bis K bestimmte Positionen einer Anlage für die Herstellung von Dachsteinen bezeichnet sind.In the 3 this is shown schematically in more detail, with the letters A to K certain positions of a plant for the production of roof tiles are called.

Mit A ist eine Position bezeichnet, bei welcher extrudierbarer Beton für die Herstellung des Grundkörpers eines Dachsteins zugeführt wird.With A is a position designating extrudable concrete for the Production of the basic body supplied to a Dachstein becomes.

Position B bezeichnet eine erste Werkzeugbox 1, an welcher die Extrusion des Grundkörpers mit Unterschichtwerkzeugen erfolgt.Position B indicates a first toolbox 1 at which the extrusion of the base body takes place with underlay tools.

Bei Position C befindet sich ein geschlossener Unterschichtstrang 2. Bei Position D ist eine erste Schneidstation 3 vorgesehen, wo der Grundkörper mit einem profilierten Geradschnittmesser 4 und mit einem Unterschicht-Rundschnittmesser 5 geschnitten wird. Bei Position E wird eine Lücke 6 für den Schnittabfall geöffnet. Position F zeigt den fertigen Grundkörper 7 eines Dachsteins. Bei Position G wird die Lücke im Strang wieder geschlossen. Anschließend ist bei Position H eine Formstation 8 vorgesehen, mit der ein Strang Oberschichtmaterial mittels Oberschichtwerkzeugen auf dem Grundkörper extrudiert wird. Bei Position I befindet sich ein Strang auf einer Oberschicht auf dem Grundkörper, wobei die Lücke 11 zwischen zwei Grundkörpern 9, 10 geschlossen ist.At position C is a closed sublayer strand 2 , At position D is a first cutting station 3 provided where the main body with a profiled straight cut knife 4 and with a lower layer round cut knife 5 is cut. At position E becomes a gap 6 opened for cutting waste. Position F shows the finished basic body 7 a Dachstein. At position G, the gap in the strand is closed again. Subsequently, at position H is a forming station 8th provided with a strand upper layer material is extruded by means Oberschichtwerkzeugen on the body. At position I, there is a strand on a top layer on the main body, with the gap 11 between two basic bodies 9 . 10 closed is.

Bei Position J befindet sich eine zweite Schneidstation, auf der die Oberschicht mit einem Standard-Geradschnittmesser 12 sowie mit einem beheizten oder wasserbesprühten Oberschicht-Rundschnittmesser 13 geschnitten wird.At position J there is a second cutting station on which the top layer is fitted with a standard straight cut knife 12 as well as with a heated or water-sprayed upper layer round cut knife 13 is cut.

Bei Position K ist der fertig extrudierte, zweilagige Betondachstein mit vollständig bedecktem Rundschnitt gezeigt.at Position K is the finished extruded, two-ply concrete roof tile with complete covered in a round shape.

Claims (18)

Dachstein, der wenigstens zwei Lagen enthält, von denen die eine Lage ein Grundkörper und die andere Lage eine Beschichtung auf diesem Grundkörper ist, wobei die Beschichtung wenigstens Sand und ein Bindemittel enthält, dadurch gekennzeichnet, dass der Durchmesser des Größtkorns des Sands maximal gleich groß wie die Dicke der Beschichtung ist und minimal ein Drittel hiervon beträgt.Dachstein, which contains at least two layers, of which one layer is a base body and the other layer is a coating on this base body, wherein the coating contains at least sand and a binder, characterized in that the diameter of the largest grain of the sand maximally the same size the thickness of the coating is at least a third thereof. Dachstein nach Anspruch 1, dadurch gekennzeichnet, dass sich die Kornbereichsgröße des Bindemittels und die Kornbereichsgröße des Sands nicht überlappen.Dachstein according to claim 1, characterized that the grain size of the binder and do not overlap the grain area size of the sand. Dachstein nach Anspruch 1, dadurch gekennzeichnet, dass sich die Korngrößenverteilung des Bindemittels und die Korngrößenverteilung des Sands maximal 10 % überlappen.Dachstein according to claim 1, characterized that the grain size distribution of the binder and the particle size distribution of the sand do not overlap more than 10%. Dachstein nach Anspruch 1, dadurch gekennzeichnet, dass die Beschichtung eine Dicke von 0,5 bis 3 mm hat.Dachstein according to claim 1, characterized that the coating has a thickness of 0.5 to 3 mm. Dachstein nach Anspruch 1, dadurch gekennzeichnet, dass die Beschichtung auf dem Grundkörper überall die gleiche Stärke aufweist.Dachstein according to claim 1, characterized that the coating on the body has the same thickness everywhere. Dachstein nach Anspruch 1, dadurch gekennzeichnet, dass das Bindemittel ein Gemisch aus wenigstens zwei Substanzen enthält.Dachstein according to claim 1, characterized that the binder is a mixture of at least two substances contains. Dachstein nach Anspruch 6, dadurch gekennzeichnet, dass das Bindemittel Portlandzement und Flugasche enthält.Dachstein according to claim 6, characterized the binder contains Portland cement and fly ash. Dachstein nach Anspruch 6, dadurch gekennzeichnet, dass das Bindemittel Portlandzement und Kalksteinmehl enthält.Dachstein according to claim 6, characterized that the binder contains Portland cement and limestone powder. Dachstein nach Anspruch 1, dadurch gekennzeichnet, dass das Bindemittel Hüttensand enthält.Dachstein according to claim 1, characterized that the binder is blastfurnace slag contains. Dachstein nach Anspruch 1, dadurch gekennzeichnet, dass die Beschichtung einen Bindemittelleim aufweist.Dachstein according to claim 1, characterized that the coating has a binder glue. Dachstein nach Anspruch 10, dadurch gekennzeichnet, dass der Bindemittelleim aus Zement und Wasser besteht.Dachstein according to claim 10, characterized that the binder cement is made of cement and water. Dachstein nach Anspruch 1 und Anspruch 10, dadurch gekennzeichnet, dass das Volumen des Bindemittelleims größer ist als das Porenvolumen des Sands.Dachstein according to claim 1 and claim 10, characterized characterized in that the volume of the binder core is larger as the pore volume of the sand. Dachstein nach Anspruch 1, dadurch gekennzeichnet, dass ein Verflüssiger vorgesehen ist, der aus Polycarboxylatether besteht.Dachstein according to claim 1, characterized that a liquefier is provided, which consists of polycarboxylate ether. Dachstein nach Anspruch 1, dadurch gekennzeichnet, dass die Beschichtung 0,5 % bis 2,5 % mineralische Pigmente enthält.Dachstein according to claim 1, characterized in that the coating 0.5% to 2.5% contains mineral pigments. Dachstein nach Anspruch 1, dadurch gekennzeichnet, dass der Grundkörper eine Rohdichte > 2,15 g/cm3 aufweist.Dachstein according to claim 1, characterized in that the base body has a density of> 2.15 g / cm 3 . Dachstein nach Anspruch 1, dadurch gekennzeichnet, dass die Beschichtung vor und während der Extrusion folgende Bestandteile aufweist: a) 100 Teile Quarzsand mit Sandkörnern von einem Durchmesser zwischen 0,1 und 0,6 mm b) 70 Teile Portlandzement c) 14 Teile Flugasche mit einer Körnung kleiner 80 mm oder 14 Teile Kalksteinmehl gleicher Körnung d) 3 Teile Eisenoxid-Pigment e) 1 Teil Betonverflüssiger der Stoffklasse Polycarboxylatether f) 35 Teile Wasser.Dachstein according to claim 1, characterized that the coating before and during the extrusion has the following components: a) 100 parts Quartz sand with grains of sand of a diameter between 0.1 and 0.6 mm b) 70 parts Portland cement c) 14 parts of fly ash with a grain less than 80 mm or 14 parts of limestone powder of the same grain size d) 3 parts iron oxide pigment e) 1 part of concrete liquefier Class of polycarboxylate ether f) 35 parts water. Dachstein nach Anspruch 1, dadurch gekennzeichnet, dass der Grundkörper vor und während der Extrusion folgende Bestandteile aufweist: a) 100 Teile Flusssand der Körnung 0–4 mm b) 25 Teile Portlandzement c) 1 Teil Eisenoxidpigment d) 10 Teile Wasser.Dachstein according to claim 1, characterized that the main body before and during the extrusion has the following components: a) 100 parts River sand of the grain 0-4 mm b) 25 parts Portland cement c) 1 part iron oxide pigment d) 10 parts water. Dachstein nach Anspruch 16 und Anspruch 17, dadurch gekennzeichnet, dass der Portlandzement zu der Klasse CEM I 42,5 oder CEM II AS gehört.Dachstein according to claim 16 and claim 17, characterized characterized in that the Portland cement to the class CEM I 42.5 or CEM II AS belongs.
DE2003147578 2003-10-14 2003-10-14 Dachstein, which contains at least two layers Withdrawn DE10347578A1 (en)