DE10338577A1 - Container for holding bulk materials consists of a fabric impregnated with an agent preventing accumulation of static electricity - Google Patents

Container for holding bulk materials consists of a fabric impregnated with an agent preventing accumulation of static electricity Download PDF

Info

Publication number
DE10338577A1
DE10338577A1 DE2003138577 DE10338577A DE10338577A1 DE 10338577 A1 DE10338577 A1 DE 10338577A1 DE 2003138577 DE2003138577 DE 2003138577 DE 10338577 A DE10338577 A DE 10338577A DE 10338577 A1 DE10338577 A1 DE 10338577A1
Authority
DE
Germany
Prior art keywords
container
fibers
electrostatic
tissue
fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE2003138577
Other languages
German (de)
Inventor
Ekkehard Steinecke
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to DE2003138577 priority Critical patent/DE10338577A1/en
Publication of DE10338577A1 publication Critical patent/DE10338577A1/en
Withdrawn legal-status Critical Current

Abstract

The container for holding bulk materials consists of a fabric impregnated with an agent preventing accumulation of static electricity. An independent claim is also included for a method for producing the proposed container.

Description

Die Erfindung geht aus von einem Behälter für Schüttgut und einem Verfahren zur Herstellung eines Behälters für Schüttgut nach den Oberbegriffen der Ansprüche 1 und 11.The Invention is based on a container for bulk material and a method for producing a container for bulk material according to the preambles of claims 1 and 11.

Aus dem Stand der Technik sind flexible Behälter für Schüttgut aus Polyestergewebe beispielsweise zur Lagerung von Pulver, Granulat, Mehl, Futtermittel und Holzpellets bekannt. Die Behälter werden an einem geeigneten Gestell aufgehängt oder über eine sonstige Vorrichtung angeordnet. Üblicherweise werden sie an der oben offenen Seite befüllt. Über einen Auslaß an der Unterseite des Behälters kann das Schüttgut entnommen werden.Out The prior art flexible container for bulk material of polyester fabric, for example for storage of powder, granules, flour, feed and wood pellets known. The containers are suspended on a suitable rack or other device arranged. Usually they are filled at the top open side. About an outlet at the Bottom of the container can the bulk material be removed.

Als nachteilig erweist sich bei den Behältern aus Kunstfasergewebe oder sonstigen Geweben, dass sich das Gewebe beim Befüllen des Behälters und bei der Entnahme von Schüttgut elektrostatisch aufladen kann. Kommt es zu einer Entladung mit Funkenflug, so kann dies bei einer bestimmten Mischung aus Staub und Luft zu einer Explosion führen.When disadvantageous proves in the containers of synthetic fiber fabric or other tissues, that the tissue during filling of the Container and during the removal of bulk material can charge electrostatically. Does it come to a discharge with flying sparks, so this may happen with a certain mixture of dust and air too cause an explosion.

Nach den Richtlinien der Berufsgenossenschaft und der EU-Richtlinie 94/9/EG, welche die Bezeichnung ATEX-Richtlinie trägt, ist das Material für die Behälter von Schüttgütern so zu wählen, dass derartige Explosionen weitestgehend ausgeschlossen werden können.To the guidelines of the professional association and the EU directive 94/9 / EG, which bears the name ATEX directive is the material for the containers of Bulk goods like that to choose, that such explosions can be largely excluded.

Aus dem Stand der Technik sind Behälter für Schüttgut bekannt, bei denen in das Gewebe in Kett- und Schussrichtung in bestimmten Abständen Karbonfäden oder Metallfäden eingewoben sind. Dadurch reduziert sich der Oberflächenwiderstand des Gewebes und die elektrische Leitfähigkeit wird erhöht. Bei derartigen Geweben beträgt der Oberflächenwiderstand typischerweise 2,2 × 109 Ohm. Die Gewebe derartiger Behälter können sich damit nicht so stark aufladen wie Behälter aus reinem Kunstfasergewebe. Als nachteilig erweist sich jedoch, dass das Einweben von Karbon- oder Metallfäden mit relativ hohem Aufwand und hohen Kosten verbunden ist.Containers for bulk goods are known from the prior art, in which carbon threads or metal threads are woven into the fabric in warp and weft directions at specific intervals. This reduces the surface resistance of the fabric and increases the electrical conductivity. For such fabrics, the surface resistivity is typically 2.2 × 10 9 ohms. The fabric of such containers can not charge as much as containers made of pure synthetic fabric. However, it proves to be disadvantageous that the weave of carbon or metal threads is associated with relatively high costs and high costs.

Darüber hinaus haben die aus dem Stand der Technik bekannten flexiblen Behälter den Nachteil, dass sie die gelagerten Nahrungs- oder Futtermittel nicht vor Nagetieren wie Mäusen und Ratten oder auch vor Mardern schützen. Die Tiere können über das Gestell oder sonstige Vorrichtungen an den Behälter gelangen oder auf den Behälter klettern. Durch Verbiss können sie den Behälter beschädigen, dadurch in den Behälter gelangen und die gelagerten Nahrungs- oder Futtermittel fressen. Abgesehen von den daraus resultierenden Verlusten können die Tiere die Nahrungs- und Futtermittel mit Bakterien, Viren, Salmonellen oder sonstigen Verunreinigungen versehen, was zu einer verminderten Qualität führt. Aus diesem Grund werden bislang zusätzliche Mittel wie beispielsweise Gifte oder Vorrichtungen zur Erwärmung des Behälters auf 80°C eingesetzt, um die Tiere von den gelagerten Nahrungs- und Futtermitteln fern zu halten.Furthermore have the known from the prior art flexible container the Disadvantage that they do not store the stored food or feed from rodents like mice and rats or guardians. The animals can talk about that Get rack or other devices to the container or on the container climb. By biting can she the container damage, thereby in the container and eat the stored food or feed. Apart from the resulting losses, the Feed the food and feed with bacteria, viruses, salmonella or other impurities, resulting in a diminished quality leads. Out This reason will be additional so far Means such as poisons or devices for heating the container at 80 ° C used to remove the animals from the stored food and feed keep away.

Die Erfindung und ihre VorteileThe invention and their benefits

Demgegenüber haben der erfindungsgemäße Behälter für Schüttgut mit den Merkmalen des Anspruchs 1 und das erfindungsgemäße Verfahren mit den Merkmalen des Anspruchs 11 den Vorteil, dass der Widerstand des Gewebes des Behälters um mindestens eine Größenordnung reduziert wird und sich die Leitfähigkeit entsprechend erhöht. Der Oberflächenwiderstand eines mit einem Antielektrostatikum imprägnierten Gewebes liegt beispielsweise bei 3 × 108 Ohm. Geringere Werte sind darüber hinaus möglich. Zur Imprägnierung werden das Gewebe oder die Fasern zur Herstellung des Gewebes mit einem geeigneten Antielektrostatikum behandelt. Die Behandlung erfolgt beispielsweise in einem Tauchbad, im Sprühverfahren oder in einem Foulard. Als Antielektrostatikum eignen sich beispielsweise eine Mischung aus Alkylphosphat und Kaliumsalz, Polyglykolethersulfat oder sekundäre Natriumalkylsulfonate. Dabei liegt das Antielektrostatikum typischerweise als wässrige Zubereitung vor.In contrast, the inventive container for bulk goods with the features of claim 1 and the inventive method with the features of claim 11 have the advantage that the resistance of the tissue of the container is reduced by at least one order of magnitude and increases the conductivity accordingly. The surface resistance of an anti-electrostatic impregnated fabric is, for example, 3 × 10 8 ohms. Lower values are also possible. For impregnation, the fabric or fibers are treated with a suitable anti-electrostatic agent to produce the fabric. The treatment is carried out, for example, in a dipping bath, by spraying or in a padder. Suitable antistatic agents are, for example, a mixture of alkyl phosphate and potassium salt, polyglycol ether sulfate or secondary sodium alkyl sulfonates. The anti-electrostatic agent is typically present as an aqueous preparation.

Da das erfindungsgemäße Verfahren mit geringerem Aufwand verbunden ist als das Einweben von Karbonfäden oder sonstigen Fäden, zeichnet sich der erfindungsgemäße Behälter nicht nur durch einen geringeren Oberflächenwiderstand sondern auch durch einen geringeren Mehrpreis bei der Herstellung aus. Der Mehrpreis eines erfindungsgemäßen Behälters beträgt lediglich die Hälfte bis ein Viertel des Mehrpreises eines Behälters mit eingewobenen Karbon- oder Metallfäden. Der Mehrpreis bezieht sich auf die Kosten, die zusätzlich zu den Kosten der Herstellung eines Behälters ohne spezielle Vorkehrungen zur Reduzierung des Oberflächenwiderstands anfallen.There the inventive method associated with less effort than the weaving of carbon threads or other threads, the container of the invention does not only by a lower surface resistance but also by a lower extra cost in the production. The extra price a container according to the invention is only the half up to a quarter of the extra cost of a container with woven-carbon or metal threads. The extra charge refers to the cost in addition to the cost of producing a container without special precautions for reducing the surface resistance attack.

Der erfindungsgemäße Behälter hat außerdem den Vorteil, dass aufgrund der verbesserten Leitfähigkeit eine elektrische Spannung angelegt werden kann. Berührt ein Nagetier, das sich im Kontakt zum Boden oder einem sonstigen Teil mit Massepotential befindet, den Behälter, so fließt ein elektrischer Strom. Dies wird von dem Tier als unangenehm empfunden. Es wird sich daher von dem Behälter fern halten. Bei dem Anlegen der Spannung ist darauf zu achten, dass eine Entladung durch Funkenflug vermieden wird, um die Explosionsgefahr auszuschließen. Es kann daher von Vorteil sein, anstelle einer konstanten Spannung Spannungspulse induktiv oder kapazitiv einzukoppeln. Zur Ableitung der elektrostatischen Ladung kann eine Halbleiteranordnung vorgesehen sein. Diese sorgt dafür, dass die Spannungspulse nicht über die Erdung des Behälters abfließen.The container according to the invention also has the advantage that due to the improved conductivity, an electrical voltage can be applied. If a rodent, which is in contact with the ground or another part with ground potential, touches the container, an electric current flows. This is perceived by the animal as unpleasant. It will therefore keep away from the container. When applying the voltage, care must be taken to avoid discharge by flying sparks in order to prevent the risk of explosion. It may therefore be advantageous instead of egg ner constant voltage voltage pulses inductively or capacitively coupled. For deriving the electrostatic charge, a semiconductor device may be provided. This ensures that the voltage pulses do not flow off via the ground of the container.

Das erfindungsgemäße Verfahren kann bei beliebigen Behältern aus Kunstfasern, Naturfasern oder Gemischen aus Kunst- und Naturfasern angewendet werden.The inventive method can with any containers made of synthetic fibers, natural fibers or mixtures of synthetic and natural fibers be applied.

Hierzu zählen typischerweise Polyestergewebe aber auch Gewebe aus Polyacryl- oder Polyamidfasern.For this counting typically polyester fabric but also fabric made of polyacrylic or polyamide fibers.

Nach einer vorteilhaften Ausgestaltung der Erfindung wird das Gewebe thermofixiert und mit dem Antielektrostatikum imprägniert. Die zugehörigen Arbeitsschritte können nacheinander oder gleichzeitig ablaufen. Darüber hinaus kann der Behälter mit einer Substanz versehen werden, die die Entflammbarkeit ausschließt oder deren Wahrscheinlichkeit reduziert. Dieser Arbeitsschritt kann ebenfalls gleichzeitig, vorab oder anschließend an die oben genannten Schritte ablaufen.To An advantageous embodiment of the invention is the tissue heat-set and impregnated with the anti-electrostatic agent. The associated Work steps can run sequentially or simultaneously. In addition, the container can with a substance that excludes the flammability or their probability is reduced. This step can also be done simultaneously, in advance or afterwards proceed to the above steps.

Das Antielektrostatikum kann in kontinuierlicher oder diskontinuierlicher Arbeitsweise appliziert werden. Zur Optimierung des Antikelektrostatikeffektes ist eine wässrige Zubereitung des Antielektrostatikums mit einer Konzentration zwischen 5 bis 20 g pro Liter, besonders bevorzugt 7 bis 10 g pro Liter, geeignet. Die Behandlung erfolgt beispielsweise im neutralen pH-Bereich, während 10 bis 15 Minuten bei 30 bis 35° C. Nach dem Entwässern wird wie üblich getrocknet. Die Flottenkonzentration des Antielektrostatikums wird so gewählt, dass 0,8 bis 1 % des Antielektrostatikums auf den Fasern oder dem Gewebe verbleiben. Die Trocknung kann wie üblich vorgenommen werden.The Anti-static can be continuous or discontinuous Operation be applied. To optimize the anti-static effect is a watery Preparation of the anti-electrostatic with a concentration between 5 to 20 g per liter, more preferably 7 to 10 g per liter. The treatment takes place, for example, in the neutral pH range, during 10 to 15 minutes at 30 to 35 ° C. After draining is dried as usual. The liquor concentration of the anti-electrostatic is chosen so that 0.8 to 1% of the Antielektratatikums remain on the fibers or the tissue. The drying can be done as usual be made.

Darüber hinaus kann das Antielektrostatikum auch bei wesentlich höheren Temperaturen von mehr als 100°C, beispielsweise 180°C, und in höheren Konzentrationen appliziert werden. In diesem Fall kann eine kürzere Behandlungsdauer ausreichend sein. Bei höheren Temperaturen kann das Antielektrostatikum besser in die Fasern des Gewebes eindringen, so dass es auch beim Waschen des Behälters am Behälter verbleibt. Bei derartig hohen Temperaturen kann der zusätzliche Arbeitsschritt des Thermofixierens entfallen. Beim Thermofixieren wird das Gewebe mit Wasserdampf behandelt, um es geschmeidiger zu machen. Dies ist bei einem Gewebe von Vorteil, das sehr dicht gewoben ist und eine hohe Fadendichte aufweist. Bei einer Temperatur von über 100°C zum Applizieren des Antielektrostatikums wird das Gewebe automatisch mit Wasserdampf behandelt.Furthermore The anti-electrostatic can also at much higher temperatures of more than 100 ° C, for example 180 ° C, and in higher concentrations be applied. In this case, a shorter treatment duration may be sufficient. At higher Temperatures can make the anti-static better in the fibers of the Tissue penetrate, making it even when washing the container on container remains. At such high temperatures, the additional Step of thermofixing omitted. When thermosetting the fabric is steamed to make it smoother do. This is advantageous for a fabric that is very tightly woven is and has a high thread density. At a temperature of over 100 ° C for application of the anti-electrostatic, the tissue is automatically steamed treated.

Die Behandlung mit dem Antielektrostatikum kann auch bei einem bereits fertig gestellten Behälter erfolgen. Damit kann das Antielektrostatikum auch bei Behältern appliziert werden, welche sich bereits im Einsatz befunden haben.The Treatment with the anti-electrostatic can also be at one already finished container done. Thus, the anti-static agent can also be applied to containers, which have already been in use.

Weitere Vorteile und vorteilhafte Ausgestaltungen der Erfindung sind den Ansprüchen entnehmbar.Further Advantages and advantageous embodiments of the invention are the claims removable.

Claims (22)

Behälter für Schüttgut aus einem Gewebe dadurch gekennzeichnet, dass ein mit einem Antielektrostatikum imprägniertes Gewebe vorgesehen ist.Container for bulk material from a tissue, characterized in that a fabric impregnated with an anti-static material is provided. Behälter nach Anspruch 1, dadurch gekennzeichnet, dass das Antielektrostatikum Alkylphosphat und Kaliumsalz enthält.container according to claim 1, characterized in that the anti-electrostatic Alkyl phosphate and potassium salt contains. Behälter nach Anspruch 1, dadurch gekennzeichnet, dass das Antielektrostatikum Polyglykolethersulfat enthält.container according to claim 1, characterized in that the anti-electrostatic Polyglykolethersulfat contains. Behälter nach Anspruch 1, dadurch gekennzeichnet, dass das Antielektrostatikum sekundäre Natriumalkylsulfonate enthält.container according to claim 1, characterized in that the anti-electrostatic secondary sodium alkylsulfonates contains. Behälter nach Anspruch 4, dadurch gekennzeichnet, dass die sekundären Natriumalkylsulfonate eine mittlere Kettenlänge von 15 C-Atomen haben.container according to claim 4, characterized in that the secondary sodium alkylsulfonates a average chain length of 15 carbon atoms. Behälter nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, dass das Gewebe aus Polyester-, Polyacryl- oder Polyamidfasern besteht.container according to one of the preceding claims, characterized the fabric consists of polyester, polyacrylic or polyamide fibers. Behälter nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, dass das Gewebe aus Naturfasern oder einem Gemisch aus Naturfasern und Kunstfasern besteht.container according to one of the claims 1 to 5, characterized in that the fabric of natural fibers or a mixture of natural fibers and synthetic fibers. Behälter nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, dass eine Vorrichtung vorgesehen ist, um den Behälter elektrisch zu erden.container according to one of the preceding claims, characterized a device is provided for electrically grounding the container. Behälter nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, dass eine Vorrichtung vorgesehen ist, um den Behälter mit elektrischen Spannungspulsen zu beaufschlagen.container according to one of the preceding claims, characterized in that a device is provided to the container with electrical voltage pulses to act on. Behälter nach Anspruch 9, dadurch gekennzeichnet, dass ein Transformator, ein Halbleiter oder ein hochohmiger Widerstand vorgesehen sind.container according to claim 9, characterized in that a transformer, a semiconductor or a high resistance resistor are provided. Verfahren zur Herstellung eines Behälters für Schüttgüter aus Fäden oder Fasern, welche zu einem Gewebe gewoben werden nach einem der Ansprüche 1 bis 10, dadurch gekennzeichnet, dass die Fäden oder Fasern oder das aus den Fäden oder Fasern gewobene Gewebe mit einem Antielektrostatikum imprägniert wird.A method for producing a container for bulk materials from filaments or fibers, which are woven into a fabric according to one of claims 1 to 10, characterized in that the Threads or fibers or the woven from the threads or fibers tissue is impregnated with an anti-static agent. Verfahren nach Anspruch 11, dadurch gekennzeichnet, dass das Gewebe zunächst thermofixiert und anschließend mit dem Antielektrostatikum imprägniert wird.Method according to claim 11, characterized in that that the tissue first heat-set and then impregnated with the anti-electrostatic agent becomes. Verfahren nach Anspruch 11 oder 12, dadurch gekennzeichnet, dass das Antielektrostatikum im Foulardverfahren oder durch Sprühen appliziert wird.Method according to claim 11 or 12, characterized that the anti-electrostatic agent is applied by padding or by spraying. Verfahren nach Anspruch 11 oder 12, dadurch gekennzeichnet, dass die Behandlung mit dem Antielektrostatikum auf der Lisseuse erfolgt.Method according to claim 11 or 12, characterized that the treatment with the anti-electrostatic on the lisseuse he follows. Verfahren nach einem der Ansprüche 11 bis 14, dadurch gekennzeichnet, dass das Antielektrostatikum als wässrige Zubereitung vorliegt.Method according to one of claims 11 to 14, characterized that the anti-electrostatic agent is present as an aqueous preparation. Verfahren nach Anspruch 15, dadurch gekennzeichnet, dass die Konzentration der wässrigen Zubereitung 5 bis 20 g/l beträgt.Method according to claim 15, characterized in that that the concentration of the aqueous preparation 5 to 20 g / l. Verfahren nach einem der Ansprüche 11 bis 16, dadurch gekennzeichnet, dass die Behandlung mit dem Antielektrostatikum im neutralen pH-Bereich während 10 bis 15 Minuten bei 30–35°C erfolgt.Method according to one of claims 11 to 16, characterized that the treatment with the anti-static in the neutral pH range during 10 until 15 minutes at 30-35 ° C. Verfahren nach Anspruch 17, dadurch gekennzeichnet, dass die Fasern, Fäden oder das Gewebe nach der Behandlung entwässert und getrocknet werden.Method according to claim 17, characterized in that that the fibers, threads or the tissue is dehydrated and dried after treatment. Verfahren nach einem der Ansprüche 11 bis 18, dadurch gekennzeichnet, dass 0,8 bis 1% des Antielektrostatikums auf den Fasern, Fäden oder dem Gewebe verbleiben.Method according to one of claims 11 to 18, characterized that 0.8 to 1% of the Antielektratatikums on the fibers, filaments or the Tissue remain. Verfahren nach einem der Ansprüche 11 bis 19, dadurch gekennzeichnet, dass als Antielektrostatikum eine Mischung aus Alkylphosphat und Kaliumsalz verwendet wird.Method according to one of claims 11 to 19, characterized that as an anti-static a mixture of alkyl phosphate and Potassium salt is used. Verfahren nach einem der Ansprüche 11 bis 19, dadurch gekennzeichnet, dass als Antielektrostatikum Polyglykolethersulfat verwendet wird.Method according to one of claims 11 to 19, characterized that polyglycol ether sulfate is used as the anti-static agent. Verfahren nach einem der Ansprüche 11 bis 19, dadurch gekennzeichnet, dass als Antielektrostatikum sekundäre Natriumalkylsulfonate verwendet werden.Method according to one of claims 11 to 19, characterized that secondary sodium alkylsulfonates are used as the anti-electrostatic agent.
DE2003138577 2003-08-19 2003-08-19 Container for holding bulk materials consists of a fabric impregnated with an agent preventing accumulation of static electricity Withdrawn DE10338577A1 (en)