DE102013109661A1 - Verfahren zum Herstellen eines beschichteten Bauteils und beschichtetes Bauteil - Google Patents
Verfahren zum Herstellen eines beschichteten Bauteils und beschichtetes Bauteil Download PDFInfo
- Publication number
- DE102013109661A1 DE102013109661A1 DE201310109661 DE102013109661A DE102013109661A1 DE 102013109661 A1 DE102013109661 A1 DE 102013109661A1 DE 201310109661 DE201310109661 DE 201310109661 DE 102013109661 A DE102013109661 A DE 102013109661A DE 102013109661 A1 DE102013109661 A1 DE 102013109661A1
- Authority
- DE
- Germany
- Prior art keywords
- layer
- ceramic material
- base body
- fiber
- coated component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Die Erfindung betrifft ein Verfahren zum Herstellen eines beschichteten Bauteils, mit folgenden Schritten: Bereitstellen eines Grundkörpers aus einem faserverstärkten Kunststoff und Aufbringen einer Schicht aus einem keramischen Material direkt auf den Grundkörper. Des Weiteren betrifft die Erfindung ein beschichtetes Bauteil mit einem Grundkörper aus einem faserverstärkten Kunststoff und einer direkt auf dem Grundkörper angeordneten Schicht aus einem keramischen Material.
Description
- Die Erfindung betrifft ein Verfahren zum Herstellen eines beschichteten Bauteils und ein beschichtetes Bauteil.
- Hintergrund
- Im Stand der Technik sind verschiedene Verfahren zum Herstellen von beschichteten Bauteilen bekannt.
- Das Dokument
DE 93 05 806 U1 betrifft ein Verfahren zum Herstellen einer Druckwalze. Hierbei wird auf einen Grundkörper aus einem thermoplastischen faserverstärkten Kunststoff mittels Plasmaspritzen eine Schicht aus Kupfer oder einer Kupferlegierung erzeugt. - In dem Dokument
DE 10 2009 048 709 A1 ist ein weiteres Verfahren zum Herstellen eines Verbundbauteils aus einem faserverstärkten Kunststoff und einem Metall beschrieben. - Während Metalle und Metalllegierungen direkt auf einen faserverstärkten Kunststoff aufgebracht werden können, ist dies für keramische Materialien nicht möglich. Beim Auftragen eines keramischen Materials auf einen Grundkörper aus faserverstärkten Kunststoff wird im Stand der Technik immer zunächst eine Zwischenschicht aus einem Haftmittel auf dem Grundkörper gebildet. Als Haftmittel wird beispielsweise Zink verwendet. Es ist somit ein zusätzlicher Verfahrensschritt zum Herstellen erforderlich und es wird Material für das Haftmittel verbraucht.
- Zusammenfassung
- Aufgabe ist es, verbesserte Technologien zum Beschichten von Bauelementen anzugeben. Insbesondere soll ein korrosionsfreier Haftgrund für eine Beschichtung bereitgestellt werden.
- Die Aufgabe wird durch das Verfahren nach dem unabhängigen Anspruch 1 und das Bauteil nach dem unabhängigen Anspruch 10 gelöst. Vorteilhafte Ausführungsformen sind Gegenstand von abhängigen Ansprüchen.
- Nach einem Aspekt ist ein Verfahren zum Herstellen eines beschichteten Bauteils bereitgestellt. Das Verfahren umfasst die folgenden Schritte. Es wird ein Grundkörper aus einem faserverstärkten Kunststoff bereitgestellt. Eine Schicht aus einem keramischen Material wird direkt auf den Grundkörper aufgebracht. Ein Bereich zwischen dem Grundkörper und der Schicht aus keramischem Material ist frei von einer Zwischenschicht. Insbesondere ist der Bereich frei von einem Haftmittel.
- Nach einem weiteren Aspekt ist ein beschichtetes Bauteil mit einem Grundkörper aus einem faserverstärkten Kunststoff und einer direkt auf dem Grundkörper angeordneten Schicht aus einem keramischen Material gebildet.
- Die Vermeidung des Aufbringens eines Haftmittels führt zu weniger Verfahrensschritten, was das Verfahren schneller und kostengünstiger macht. Darüber hinaus sind die Eigenschaften des Bauteils verbessert. Eine Korrosion des Haftmittels, die im Stand der Technik oft vorkam, wird vermieden.
- Ein faserverstärkter Kunststoff (FVK) (auch: Faser-Kunststoff-Verbund oder Faserverbundkunststoff) ist ein Werkstoff, der Verstärkungsfasern enthält, die einer Kunststoffmatrix eingebettet sind. Die Matrix umgibt die Verstärkungsfasern, die durch Adhäsiv- oder Kohäsivkräfte an die Matrix gebunden sind.
- Der Grundkörper kann beispielsweise aus einem glasfaserverstärkten Kunststoff (GFK) bestehen. Alternativ kann der Grundkörper aus einem kohlenstofffaserverstärkten Kunststoff (CFK), einem faserverstärktem Polyamid (PA) oder einem faserverstärktem Epoxidharz (EP) bestehen.
- Die Schicht aus keramischem Material kann zu einer Durchschlagfestigkeit des Bauteils von bis zu 40 kV führen. Des Weiteren ermöglicht die Schicht aus keramischen Material eine thermische Isolierung des darunter liegenden Grundkörpers. Es schützt so beispielsweise vor großer Wärme. Die Schicht aus keramischem Material ist darüber hinaus verschleißbeständig, sehr hart, druckfest und hat eine hohe Schichtfestigkeit.
- Die Schicht aus keramischem Material kann einlagig oder mehrlagig auf den Grundkörper aufgebracht werden. Es kann des Weiteren vorgesehen sein, mehrere Schichten aus unterschiedlichen keramischen Materialien auf den Grundkörper aufzubringen.
- Die Schicht aus keramischem Material kann mit einer Schichtdicke von etwa 100 µm bis etwa 3 mm aufgebracht werden. Die Schicht aus keramischem Material kann nach einem Aushärten eine Haftzugfestigkeit von größer oder gleich 10 N/mm2 aufweisen.
- Es kann vorgesehen sein, dass der Grundkörper auf einem Substrat bereitgestellt wird. Das Substrat kann ein Metall, beispielsweise Aluminium, eine Metalllegierung, beispielsweise Stahl, oder ein Nichtmetall enthalten. Das Substrat kann vollständig aus einem der vorgenannten Materialien bzw. Materialklassen bestehen.
- Es kann vorgesehen sein, dass die Schicht aus keramischem Material auf den Grundkörper aufgespritzt wird. Vorteilhafterweise kann vorgesehen sein, dass die Schicht aus keramischem Material mittels thermischen Spritzens auf den Grundkörper aufgebracht wird. Beim thermischen Spritzen werden Zusatzwerkstoffe, so genannte Spritzzusätze, innerhalb oder außerhalb eines Spritzbrenners ab-, an- oder aufgeschmolzen. Die Zusatzwerkstoffe werden in einem Gasstrom in Form von Spritzpartikeln beschleunigt und auf die Oberfläche des zu beschichtenden Grundkörpers aufgebracht. Hierbei kann eine Schichtbildung stattfinden. Geeignete thermische Spritzverfahren sind beispielsweise Hochgeschwindigkeits-Flammspritzen (HVOF), Vakuum-Plasma-Spritzen (VPS) und atmosphärisches Plasmaspritzen (APS). Als Betriebsgase für das atmosphärische Plasmaspritzen können Argon, Wasserstoff, Stickstoff oder eine Kombination hiervon verwendet werden. Des Weiteren können beim atmosphärischen Plasmaspritzen Stickstoff, ein Stickstoff-Argon-Gemisch, ein Argon-Wasserstoff-Gemisch oder Argon als Fördergas eingesetzt werden. Eine Kühlung kann durch Druckluft, Kohlenstoffdioxid (CO2) oder einer Kombination hiervon erfolgen.
- Nach einer Ausführungsform kann vorgesehen sein, dass die Schicht aus keramischem Material aus einem oxidkeramischen Material gebildet wird, beispielsweise Titandioxid (TiO2), Chromoxid (Cr2O3) oder Aluminiumoxid (Al2O3). Alternativ kann die Schicht aus keramischem Material aus einer Ingenieurkeramik oder einer technischen Keramik gebildet werden.
- Es kann vorgesehen sein, dass die Schicht aus einem keramischen Material in Pulverform auf den Grundkörper aufgebracht wird, beispielsweise mittels thermischen Spritzens. Das Pulver kann einen Reinheitsgrad von mehr als 95% haben, bevorzugt von 98% bis 99,95%. Das Pulver kann in Form einer nachfolgend genannten Pulverformen bereitgestellt werden: vermischtes Keramikmaterial, wasserverdüstes Keramikmaterial, gasverdüstes Keramikmaterial, umhülltes Keramikmaterial, chemisch umhülltes Keramikmaterial, agglomeriertes Keramikmaterial, agglomeriertes und gesintertes Keramikmaterial, agglomeriertes und hohlkugeliges Keramikmaterial, agglomeriertes und verdichtetes Keramikmaterial, geschmolzenes und gebrochenes Keramikmaterial, geschmolzenes und gebrochenes und vermischtes Keramikmaterial sowie gesintertes und gebrochenes Keramikmaterial. Körner des Pulvers können folgende Korngrößen aufweisen: 10/5 µm, 22/5 µm, 45/16 µm, 25/5 µm, 45/20 µm und 30/10 µm. Körner des Pulvers können auch Korngrößen in beliebiger Kombination der vorgenannten Korngrößen aufweisen. Wenn das Pulver mittels thermischen Spritzens auf den Grundkörper aufgebracht wird, kann hierbei eine interne axiale Pulverzufuhr, eine interne radiale Pulverzufuhr oder eine externe Pulverzufuhr erfolgen.
- Alternativ kann die Schicht aus keramischem Material in Form einer Suspension aufgebracht werden, beispielsweise als wasserbasierte Suspension oder als alkoholbasierte Suspension.
- Der Grundkörper kann ein Harzmaterial enthalten. Das Harzmaterial kann beispielsweise ein Arminharz, ein Phenolharz, ein Polyesterharz, ein Vinylesterharz, ein Polyamidharz, ein Epoxydharz, ein Anhydridharz und ein Bismaleimit-Triazin-Harz sein. Der Grundkörper kann des Weiteren eine beliebige Kombination der vorgenannten Harze enthalten.
- Weiterhin kann vorgesehen sein, dass der Grundkörper mit Fasern in Kreuzlagen bereitgestellt wird. Die Fasern können in Kreuzlagen gewickelt und / oder gelegt sein. Beispielsweise können die Kreuzlagen mit abschließenden Umfangslagen gebildet sein.
- Der Grundkörper kann einen Faseranteil zwischen etwa 20 Vol.-% und etwa 60 Vol.-% aufweisen, bevorzugt zwischen etwa 30 Vol.-% und etwa 50 Vol.-%. Die Fasern können aus Glas, Kohlenstoff, Keramik, Kunststoff und / oder Naturfasern bestehen. Glasfasern können beispielsweise aus R-Glas, E-Glas, C-Glas, D-Glas und S-Glas bestehen.
- Die vorstehend im Zusammenhang mit dem Verfahren beschriebenen Merkmale gelten in analoger Weise auch für das Bauteil.
- Das Bauelement kann ein rotationssymmetrisches Bauteil sein, beispielsweise eine Walze mit einem zylinderförmigen Grundkörper, auf dem direkt eine Schicht aus keramischem Material angeordnet ist. Das Bauteil kann beispielsweise eine Rasterwalze für einen Flexodruck, eine Behandlungswalze für eine Corona-Behandlung oder ein Adapter zur Anwendung für den Flexodruck sein.
- Beschreibung beispielhafter Ausführungsformen
- Weitere Ausführungsformen werden im Folgenden unter Bezugnahme auf Figuren einer Zeichnung näher erläutert. Hierbei zeigen:
-
1 eine schematische Darstellung einer Walze, -
2 eine schematische Darstellung einer weiteren Walze, -
3 eine schematische Darstellung einer anderen Walze, -
3 eine schematische Darstellung einer Walze nach einer weiteren Ausführungsform, -
4 eine schematische Darstellung einer Walze nach noch einer anderen Ausführungsform, -
6 eine schematische Darstellung eines Bauteils und -
7 eine schematische Darstellung eines weiteren Bauteils. - Im Folgenden werden für gleiche Komponenten gleiche Bezugszeichen verwendet.
-
1 zeigt eine schematische Darstellung einer Walze mit einem rohrförmigen Substrat1 , einer Schicht aus einem faserverstärkten Material2 und einer Schicht aus einem keramischen Material3 . An beiden Enden der Walze sind Zapfen4 angeordnet. Das Substrat1 kann beispielsweise aus Stahl oder Aluminium bestehen. Die Schicht aus faserverstärktem Kunststoff2 dient als Isolationsbarriere. Sie kann verschiedene Faserarten umfassen, beispielsweise Glasfasern, Kohlenstofffasern, Keramikfasern, Kunststofffasern und / oder Naturfasern. Die Fasern sind in ein Arminharz eingebettet und in gewickelten Kreuzlagen auf das rohrförmige Substrat1 aufgebracht. Auf der faserverstärkten Schicht2 ist direkt die Schicht aus einem keramischen Material3 aufgebracht. Die keramische Schicht3 stellt eine Wärmedämmung bereit. Als Keramik ist in dieser Ausführungsform eine Oxidkeramik vorgesehen. -
2 zeigt eine weitere Ausführungsform einer Walze. Bei dieser Ausführungsform ist das rohrförmige Substrat1 verkürzt, sodass ein Zwischenbereich5 zwischen den Enden des Substrats1 und den Zapfen4 gebildet ist. - In
3 ist eine Walze mit einem durchgehenden rohrförmigen Substrat1 dargestellt. -
4 zeigt eine Walze mit einer faserverstärkten Schicht2 , auf der direkt eine keramische Schicht3 angeordnet ist. Die faserverstärkte Schicht ist auf einem Substrat6 aus einem Vollmaterial aufgebracht, beispielsweise aus Stahl oder Aluminium. -
5 zeigt eine Walze mit einem verkürzten rohrförmigen Substrat1 , einer faserverstärkten Schicht2 und einer keramischen Schicht3 . An beiden Enden der Walze ist eine Aufnahme7 gebildet. -
6 und7 zeigen schematische Darstellungen für Bauteile mit beliebigen Formen. Auf einem faserverstärkten Grundkörper9 ist jeweils direkt eine Schicht aus einem keramischen Material8 angeordnet, beispielsweise aus einer Oxidkeramik. Gemäß der Ausführungsform nach7 ist der faserverstärkte Grundkörper9 auf einem Substrat10 angeordnet. - Die in der vorstehenden Beschreibung, den Ansprüchen und den Figuren offenbarten Merkmale können sowohl einzeln als auch in beliebiger Kombination miteinander für die Verwirklichung der Erfindung relevant sein.
- ZITATE ENTHALTEN IN DER BESCHREIBUNG
- Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.
- Zitierte Patentliteratur
-
- DE 9305806 U1 [0003]
- DE 102009048709 A1 [0004]
Claims (10)
- Verfahren zum Herstellen eines beschichteten Bauteils, mit folgenden Schritten: – Bereitstellen eines Grundkörpers aus einem faserverstärkten Kunststoff und – Aufbringen einer Schicht aus einem keramischen Material direkt auf den Grundkörper.
- Verfahren nach Anspruch 1, wobei die Schicht aus keramischem Material mittels thermischen Spritzens auf den Grundkörper aufgebracht wird.
- Verfahren nach Anspruch 1 oder 2, wobei die Schicht aus keramischem Material aus einem oxidkeramischen Material gebildet wird.
- Verfahren nach einem der vorangehenden Ansprüche, wobei die Schicht aus einem keramischen Material in Pulverform auf den Grundkörper aufgebracht wird.
- Verfahren nach einem der vorangehenden Ansprüche, wobei die Schicht aus keramischem Material einlagig oder mehrlagig auf den Grundkörper aufgebracht wird.
- Verfahren nach einem der vorangehenden Ansprüche, wobei der Grundkörper aus einem glasfaserverstärkten Kunststoff bereitgestellt wird.
- Verfahren nach einem der vorangehenden Ansprüche, wobei der Grundkörper ein Harzmaterial enthält.
- Verfahren nach einem der vorangehenden Ansprüche, wobei der Grundkörper mit in Kreuzlagen gewickelten Fasern bereitgestellt wird.
- Verfahren nach einem der vorangehenden Ansprüche, wobei der Grundkörper einen Faseranteil zwischen 20 Vol.-% und 60 Vol.-% aufweist.
- Beschichtetes Bauteil mit einem Grundkörper aus einem faserverstärkten Kunststoff und einer direkt auf dem Grundkörper angeordneten Schicht aus einem keramischen Material.