DE102009020707A1 - Coated granules for the regeneration of bone material - Google Patents

Coated granules for the regeneration of bone material Download PDF

Info

Publication number
DE102009020707A1
DE102009020707A1 DE200910020707 DE102009020707A DE102009020707A1 DE 102009020707 A1 DE102009020707 A1 DE 102009020707A1 DE 200910020707 DE200910020707 DE 200910020707 DE 102009020707 A DE102009020707 A DE 102009020707A DE 102009020707 A1 DE102009020707 A1 DE 102009020707A1
Authority
DE
Germany
Prior art keywords
liposomes
collagen
granules
coated
vitamins
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE200910020707
Other languages
German (de)
Inventor
Antonis Alexakis
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Alexakis Antonis Dr med dent
Original Assignee
Alexakis Antonis Dr med dent
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Alexakis Antonis Dr med dent filed Critical Alexakis Antonis Dr med dent
Priority to DE200910020707 priority Critical patent/DE102009020707A1/en
Priority to PCT/EP2010/002887 priority patent/WO2010130409A2/en
Publication of DE102009020707A1 publication Critical patent/DE102009020707A1/en
Withdrawn legal-status Critical Current

Abstract

Die Erfindung betrifft ein mit Collagen oder Liposomen oder Collagenliposomen beschichtetes und mit Tetracyclinpulver und/oder Statin gemischtes Granulat (3) zur Förderung der Knochenneubildung, insbesondere im Kiefer, bestehend aus einem vom menschlichen oder tierischen Körper resorbierbaren Material, wobei das Granulat (3) eine auf einer menschlichen oder tierischen Knochenunterlage (1) hohlraumfüllende Granulatform aufweist. Die Liposome können mit Vitaminen, Spurenelementen oder anderen Substanzen geladen werden, die Mangelerscheinungen in der zu regenerierenden Region beheben und somit die Regeneration ermöglichen bzw. beschleunigen.The invention relates to a coated with collagen or liposomes or collagen liposomes and mixed with tetracycline powder and / or statin granules (3) for promoting new bone formation, especially in the jaw, consisting of a resorbable from the human or animal body material, wherein the granules (3) a having on a human or animal bone backing (1) cavity-filling granule shape. The liposomes can be loaded with vitamins, trace elements or other substances that eliminate deficiency symptoms in the region to be regenerated and thus facilitate or accelerate regeneration.

Description

Die Erfindung betrifft ein beschichtetes Granulat zur Förderung der Knochenbildung gemäß dem Oberbegriff des Anspruchs 1.The The invention relates to a coated granules for conveying the bone formation according to the preamble of claim 1.

In der Medizin gibt es eine Vielzahl von Anwendungsfällen, in denen es wünschenswert ist, dass Knochenmaterial vom menschlichen oder tierischen Patienten selbst neu gebildet wird. Es ist bekannt, dass Osteoblasten bestrebt sind, in Hohlräume hineinzuwachsen. Diese Erkenntnis macht man sich beispielsweise in der Zahnmedizin zunutze, wenn der Kieferknochen z. B. durch Parodontitis angegriffen und teilweise zerstört ist.In There are a variety of applications in medicine which it is desirable is that bone material from the human or animal patient itself is formed again. It is known that osteoblasts strive are in cavities grow into. This realization is made, for example in dentistry, if the jaw bone z. B. by periodontitis attacked and partially destroyed is.

Es ist bekannt, das der für das gezielte Wachstum der Osteoblasten am menschlichen oder tierischen Kieferknochen benötigten Hohlraum durch resorbierbare Granulate gebildet wird.It is known that for the targeted growth of osteoblasts on human or animal Jawbone needed Cavity is formed by resorbable granules.

Es gibt einige Materialien, die in Granulatform als Füllkörper zur Verfügung stehen um Knochendefekte zu füllen oder zum Kieferaufbau in Höhe und/oder Breite.It are some materials that in granular form as a filler to disposal stand to fill bone defects or to the jaw structure in height and / or Width.

Manche dieser Materialien resorbieren sich sehr schnell, so dass das Ziel der Auffüllung oder des Aufbaues nicht erreicht werden kann. Andere wiederum, die sich zwar sehr langsam resorbieren, lassen in den höheren Schichten keine Osteoblasten wachsen, da dort kein Nährboden vorhanden ist.Some These materials absorb very quickly, leaving the target the replenishment or the structure can not be achieved. Others, the Although very slow to absorb, leave in the higher layers no osteoblasts grow, as there is no nutrient medium.

Auf diese Weise kann das Ziel nicht vollständig erreicht werden.On this way, the goal can not be fully achieved.

Der Erfindung liegt die Aufgabe zugrunde, ein grundsätzlich neuartiges Granulat vorzuschlagen. Diese Aufgabe wird mit den Merkmalen des Anspruchs 1 gelöst. Vorteilhafte Weiterbildungen der Erfindung sind in den Unteransprüchen angegeben.Of the Invention is based on the object, a fundamentally novel granules propose. This object is achieved with the features of the claim 1 solved. Advantageous developments of the invention are specified in the subclaims.

Der Erfindung liegt der Gedanke zugrunde, das vom Körper vollständig resorbierbare Granulat dauerhaft formstabil auszubilden. Bevorzugt wird das erfindungsgemäße Granulat als Massenprodukt in unterschiedlichen Körnungsgrößen hergestellt. Dabei sind die Körner derart ausgeformt, das sie, ohne Veränderungen verwenden zu müssen, an die entsprechenden Körperteile aufgebracht werden können.Of the The invention is based on the idea that the body completely resorbable granules permanently form stable. Preference is given to the granules according to the invention produced as a mass product in different grain sizes. There are the grains formed in such a way that she, without having to use changes to the corresponding body parts can be applied.

Ein weiterer Vorteil des erfindungsgemäßen Granulates ist die Beschichtung, sowie Das gleichmäßige Vermischen von Tetracyclinpulver und/oder Statin auf die gesamte Granulatmasse.

  • Vorteil 1: Die Beschichtung saugt das Blut des Patienten auf und so sind Körperzellen an jeder Höhe und Tiefe verfügbar. Auf diese Art können im gesamten Hohlraum gleichzeitig Gefäße wachsen, die wichtig sind, damit die Osteoblasten sich ernähren können und neue Knochen bilden können.
  • Vorteil 2: Durch die Beschichtung kleben die mit Blut getränkten Partikel zusammen und so bildet sich eine homogene Masse ohne Hohlräume. So ist das neue Knochenwachstum am Schnellsten zu gewährleisten.
  • Vorteil 3: Die aufgefüllte oder aufgebaute Granulatmenge klebt an der vorhandenen Knochenunterlage oder Zahnwurzel und das erleichtert ebenfalls die Regeneration. Bevorzugt weist das Beschichtungsmaterial eine Klebeeigenschaft auf, durch das das eingebrachte Granulat an einer vorgegebenen Position am Körper fixierbar ist.
  • Vorteil 4: Das Tatrcyclynpulver und Staun verhindert anfangs, dass die Osteoklasten (Zellen die das Knochen abbauen) das Granulat abbauen und so haben die Osteoblasten (Knochen bildende Zellen) ausreichende Zeitraum sich mit der Knochenbildung zu beschäftigen.
  • Vorteil 5: Die Liposomebeschichtung kann mit Vitaminen, Spurenelemente und anderen Substanzen geladen werden, somit kann der lokale herrsehende Mangel, an Vitaminen, bei Paradontal erkrankten Patienten behoben werden, und die Regeneration der verloren gegangenen Knochen beschleunigen.
Another advantage of the granules according to the invention is the coating, as well as the uniform mixing of tetracycline powder and / or statin on the entire granulate mass.
  • Advantage 1: The coating absorbs the patient's blood and thus body cells are available at any height and depth. In this way, vessels can grow at the same time in the entire cavity, which are important for the osteoblasts to be able to feed themselves and to form new bones.
  • Advantage 2: Due to the coating, the blood-soaked particles stick together, forming a homogeneous mass without cavities. Thus, the new bone growth is the fastest to ensure.
  • Advantage 3: The filled-up or built-up granules stick to the existing bone backing or tooth root, which also facilitates regeneration. Preferably, the coating material has an adhesive property by which the introduced granules can be fixed to the body at a predetermined position.
  • Benefit 4: The Tatrcyclyn powder and stasis initially prevents the osteoclasts (cells that degrade the bone) from degrading the granules and so the osteoblasts (bone-forming cells) have sufficient time to deal with bone formation.
  • Advantage 5: The liposome coating can be loaded with vitamins, trace elements, and other substances to address local deficiency, vitamins, periodontal disease, and accelerate the regeneration of lost bones.

Gemäß einer vorteilhaften Weiterbildung der Erfindung ist vorgesehen, dass als Beschichtungsmaterial Collagen oder Liposome oder eine Collagenliposomen Mischung verwendet wird, insbesondere eine Mischung aus Collagen 1 und Collagen 3, oder Collagen 1 Liposomen und Collagen 3 Liposomen. Es ist jedoch auch denkbar, lediglich Collagen 1 oder ausschließlich Collagen 3 zu verwenden sowie lediglich Collagen 1 Liposomen, oder ausschließlich Collagen 3 Liposomen Collagen hat nicht nur Dichtungseigenschaften, sondern fixiert den Formkörper zumindest vorläufig durch seine Klebewirkung. Die Liposomenbeschichtung kann mit Vitaminen und Spurenelemente geladen werden, um Mangel an solchen Substanzen in der zu regenerienden Region zu beheben.According to one advantageous development of the invention is provided that as Coating material Collagen or liposomes or a collagen liposomes Mixture is used, in particular a mixture of collagen 1 and collagen 3, or collagen 1 liposomes and collagen 3 liposomes. However, it is also conceivable, only collages 1 or only collages 3 and only collagen 1 liposomes, or exclusively collagen 3 liposome collagen not only has sealing properties, but fixes the molding at least for the time being by its adhesive effect. The liposome coating can with vitamins and trace elements are loaded to lack of such substances in the region to be regenerated.

Gemäß einer bevorzugten Ausführungsform enthält das Granulat allogenes Material, mit Collagen oder Liposomen oder Collagenliposomen beschichtet oder besteht vollständig aus Allogenmaterial mit Collagen oder Liposomen oder Collagenliposomen beschichtet. Insbesondere ist es denkbar, das Granulat aus Spenderknochen mit Collagen oder Liposome oder Collagenliposomen beschichtet oder aus Knochen von Knochenbanken mit Collagen oder Liposome oder Collagenliposomen beschichtet auszubilden. Auch ist die Verwendung von FDBA (freeze dried bone allacrafts) oder von DFDBA (decalcified freeze dried bone allocrafts) von Vorteil. Durch die Ausbildung des Granulates aus einem Material von einem genetisch differenten Individuum derselben Spezies kann das Knochenwachstum optimal verlaufen. Die Wahrscheinlichkeit entzündlicher Reaktionen wird vorteilhaft reduziert. Die Liposome können mit Vitaminen und Spurenelemente geladen werden.According to a preferred embodiment, the granules contain allogeneic material, coated with collagen or liposomes or collagen liposomes, or consist entirely of allogenic material coated with collagen or liposomes or collagen liposomes. In particular, it is conceivable that the granules of donor bone are coated with collagen or liposomes or collagen liposomes or form bone-coated bone with collagen or liposomes or collagen liposomes. Also, the use of FDBA (freeze-dried bone allacrafts) or of DFDBA (decalcified freeze-dried bone allocrafts) is advantageous. By forming the granules from a material from a genetically different individual of the same species, bone growth can be optimally sustained fen. The likelihood of inflammatory reactions is advantageously reduced. The liposomes can be loaded with vitamins and trace elements.

Auch die Verwendung von xenogenen Materialien mit Collagen oder Liposomen oder Collagenliposomen beschichtet zur Herstellung des Granulates hat sich als vorteilhaft erwiesen. Zur Herstellung von Formteilen, die für den Menschen geeignet sind, eignen sich insbesondere Knochen von Rind, Schwein, und Pferd mit Collagen oder Liposome oder Collegenliposome beschichtet Es ist jedoch auch möglich, das Granulat aus Algen mit Collagen oder Liposome oder Collagenliposome beschichtet, insbesondere Algenextrakten, Korallen oder Muscheln mit Collagen oder Collagenliposome beschichtet herzustellen.Also the use of xenogenic materials with collagen or liposomes or collagen liposomes coated to produce the granules proved to be advantageous. For the production of molded parts, the for the Bovine bovine, Pig, and horse with collagen or liposomes or college liposome However, it is also possible that Granules from algae with collagen or liposomes or collagen liposomes coated, in particular algae extracts, corals or shells to produce coated with collagen or collagen liposomes.

Die Schalen von Muscheln eignen sich besonders zur Herstellung von Granulaten, da sie aus einem Calcium-Protein-Gemisch bestehen und besonders gut vom Körper resorbiert werden können.The Shells of mussels are particularly suitable for the production of granules, because they consist of a calcium-protein mixture and especially good of the body can be absorbed.

Die Liposome können mit Vitaminen und Spurenelemente geladen werden.The Liposomes can loaded with vitamins and trace elements.

Daneben ist es auch möglich, das Granulat aus autogenem Material mit Collagen oder Liposome oder Collagenliposomen beschichtet herzustellen. Hierbei ist die Wahrscheinlichkeit des Auftretens von entzündlichen Reaktionen des Körpers des Patienten am geringsten.Besides it is also possible the granules of autogenous material with collagen or liposomes or Coated produce collagen liposomes. Here's the probability the appearance of inflammatory Reactions of the body of the patient least.

Weiterhin ist es möglich, alloplastische Materialien wie Calciumphosphate mit Collagen oder Liposomen oder Collegenliposomen beschichtet, Keramiken oder Bioglaser mit Collagen oder Liposome oder Collagenliposomen beschichtet zur Herstellung des erfindungsgemäßen formstabilen Granulates zu verwenden.Farther Is it possible, alloplastic materials such as calcium phosphates with collagen or Coated liposomes or college liposomes, ceramics or bioglass coated with collagen or liposomes or collagen liposomes Preparation of the dimensionally stable according to the invention To use granules.

Weitere Vorteile und zweckmäßige Ausführungen sind den weiteren Ansprüchen, der Figurenbeschreibung und der Zeichnung zu entnehmen.Further Advantages and expedient designs are the further claims, to take the figure description and the drawing.

Die 1 zeigt einen Knochendefekt, der mit dem Collagen oder Liposomen oder Collagenliposomen beschichteten Granulat aufgefüllt ist.The 1 shows a bone defect filled with collagen or liposome or collagen liposome coated granules.

Es ist ein von Parodontitis teilweise zerstörter Kieferknochen. Wird der Kieferknochen 1 nicht wieder hergestellt, kann es zum Ausfallen des in dem Kieferknochen 1 gehaltenen Zahns 2 kommen. Zum Zwecke der Knochenneubildung ist auf den Kieferknochen 1 ein mit Collagen oder Liposomen oder Collagenliposomen beschichtetes Granulat 3 und Tetracychnpulver und/oder Statin gemischt eingesetzt.It is a jawbone partially destroyed by periodontitis. Will the jawbone 1 not restored, it may fail in the jawbone 1 held tooth 2 come. For the purpose of bone regeneration is on the jawbone 1 a granulate coated with collagen or liposomes or collagen liposomes 3 and mixed tetracycline powder and / or statin.

In 1 ist das Granulat 3 geschnitten dargestellt. Es bildet oberhalb des Kieferknochens 1 einen Hohlraum 4 aus, in den zunächst Fibroblasten und dann die Osteoblasten des Kieferknochens 1 in Pfeilrichtung 5 hineinwachsen können. Um zu verhindern, dass Zellen der Knochenhaut 6 oder Zellen des Zahnfleisches 7 in den Hohlraum 4 eindringen können, ist das Granulat 3 gegenüber dem Zahn 2 sowie gegenüber dem Kieferknochen 1 mithilfe von Collagen 8 abgedichtet.In 1 is the granules 3 shown cut. It forms above the jawbone 1 a cavity 4 out, in the first fibroblasts and then the osteoblasts of the jawbone 1 in the direction of the arrow 5 can grow into. To prevent cells of the periosteum 6 or cells of the gum 7 in the cavity 4 can penetrate is the granules 3 opposite to the tooth 2 as well as opposite the jawbone 1 using collages 8th sealed.

Das Granulat 3 besteht in dem gezeigten Ausführungsbeispiel aus einem Muschelgranulat, das über die Collagenbeschichtung oder Liposomen oder Collagenliposomenbeschichtung an die spezielle Situation am Körper des Patienten angepasst werden kann.The granules 3 consists in the embodiment shown of a mussel granules, which can be adapted via the collagen coating or liposomes or collagen liposome coating to the specific situation on the body of the patient.

Um das Granulat 3 in die dargestellte Position einbringen zu können, wird zunächst der obere Zahnfleischlappen 7 aufgeklappt. Gegebenenfalls wird die Oberfläche des Kieferknochens aufgeraut, um das Wachstum des Knochens 1 zu fördern. Daraufhin wird das Granulat 3 mit seiner Collagenbeschichtung oder Liposomen oder eine Collagenliposomenbeschichtung 8 an die entsprechende Stelle aufgebracht am Kieferknochen 1 und/oder Zahn 2 fixiert. Daraufhin wird der Zahnfleischlappen 7 wieder in die in 1 dargestellte Position geklappt und an der Außenseite des Granulates 3 fixiert. An der Außenseite des Granulates 3 wächst die Knochenhaut 6 entlang in Pfeilrichtung 10, so dass nach einiger Zeit die ursprüngliche Kiefersituation mit vollständigem Kieferknochen 1, Knochenhaut 6 und Zahnfleisch 7 wiederhergestellt ist.To the granules 3 To be able to bring into the position shown, first, the upper gingival flap 7 opened. Optionally, the surface of the jawbone is roughened to increase the growth of the bone 1 to promote. Then the granules 3 with its collagen coating or liposomes or a collagen liposome coating 8th applied to the appropriate place on the jawbone 1 and / or tooth 2 fixed. Then the gingival flap becomes 7 back in the 1 shown position folded and on the outside of the granules 3 fixed. On the outside of the granules 3 the periosteum grows 6 along in the direction of the arrow 10 , so that after some time the original jaw situation with complete jawbone 1 , Periosteum 6 and gums 7 is restored.

Eine zweite Operation zur Entfernung des Granulates 1 nach erfolgter Knochenneubildung ist nicht erforderlich, da das Granulat 1 mit Collagen 8 vom Körper vollständig abgebaut wird.A second operation to remove the granules 1 after the formation of new bone is not necessary because the granules 1 with collages 8th completely decomposed by the body.

11
Kieferknochenjawbone
22
Zahntooth
33
Granulatgranules
44
Hohlraumcavity
55
Pfeilrichtungarrow
66
Knochenhautperiosteum
77
Zahnfleischgums
88th
Collagencollagen
99
Pfeilrichtungarrow

Claims (6)

Granulat mit Collagen oder Liposomen oder Collagenliposomen beschichtet und mit Tetracyclinpulver und/oder Stativ gemischt (3) zur Förderung der Knochenneubildung, insbesondere im Kiefer, bestehend aus einem vom menschlichen oder tierischem Körper resorbierbaren Material, wobei das Granulat (3) eine auf einer menschlichen oder tierischen Knochenunterlage (1) Hohlräume auffüllt. Die Liposome können mit Vitaminen Spurenelemente oder andere Substanzen geladen werden die Mangelerscheinungen an der zu regeneriende Region beheben Und so mit die Heilung ermöglichen bzw. beschleunigen.Granules coated with collagen or liposomes or collagen liposomes and mixed with tetracycline powder and / or tripod ( 3 ) for promoting the formation of new bone, in particular in the jaw, consisting of a material absorbable by the human or animal body, the granules ( 3 ) one on a human or animal bone pad ( 1 ) Fills up cavities. The liposomes can be loaded with vitamins trace elements or other substances that fix deficiency symptoms in the region to be regenerated And thus enable or accelerate the healing process. Granulat nach Anspruch 1, dadurch gekennzeichnet, dass das Dichtungsmaterial (8) aus Collagen oder Liposomen oder Collagenliposomen besteht, oder zumindest Collagen oder Liposome oder Collagenliposome enthält, vorzugsweise Collagen 1 und/oder Collagen 1 Liposome (und/oder Collagen 3 und/oder Collagen 3 Liposome. Die Liposome können mit Vitaminen, Spurenelemente oder andere Substanzen geladen werden die Mangelerscheinungen an der zu regeneriende Region beheben Und so mit die Heilung ermöglichen bzw. beschleunigen.Granules according to claim 1, characterized in that the sealing material ( 8th ) consists of collagen or liposomes or collagen liposomes, or at least contains collagen or liposomes or collagen liposomes, preferably collagen 1 and / or collagen 1 liposomes (and / or collagen 3 and / or collagen 3 liposomes.) The liposomes may contain vitamins, trace elements or other substances the deficiency symptoms on the region to be regenerated are corrected and thus enable or accelerate the healing process. Granulat nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, dass das Granulat mit Collagen oder Liposome oder Collagenliposomen beschichtet ist (3) und mit Tetracyclinpulver und/oder Stativ gemischt allogenes Material enthält oder vollständig aus allogenem Material besteht Die Liposome können mit Vitaminen, Spurenelemente oder andere Substanzen geladen werden die Mangelerscheinungen an der zu regeneriende Region beheben und so mit die Heilung ermöglichen bzw. beschleunigen.Granules according to one of the preceding claims, characterized in that the granules are coated with collagen or liposomes or collagen liposomes ( 3 ) and mixed with tetracycline powder and / or a tripod contains allogeneic material or consists entirely of allogeneic material The liposomes can be loaded with vitamins, trace elements or other substances which eliminate deficiency symptoms at the region to be regenerated and thus facilitate or accelerate the healing. Granulat nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, das dass Granulat mit Collagen oder Liposome oder Collagenliposomen beschichtet ist und mit Tetracyclinpulver und/oder Statin gemischt (3) xenogenes Material, insbesondere Muschelschalen, enthält oder vollständig aus xenogenem Material besteht. Die Liposome können mit Vitaminen, Spurenelemente oder andere Substanzen geladen werden die Mangelerscheinungen an der zu regeneriende Region beheben und so mit die Heilung ermöglichen bzw. beschleunigen.Granules according to one of the preceding claims, characterized in that the granules are coated with collagen or liposomes or collagen liposomes and mixed with tetracycline powder and / or statin ( 3 ) contains xenogenic material, in particular mussel shells, or consists entirely of xenogenic material. The liposomes can be loaded with vitamins, trace elements or other substances to remedy the deficiency symptoms in the region to be regenerated and thus enable or accelerate the healing process. Granulat nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, das dass Granulat mit Collagen oder Liposome oder Collagenliposomen beschichtet und mit Tetracyclinpulver und/oder Statin gemischt (3) autogenes Material enthällt oder vollständig aus autogenem Material besteht. Die Liposome können mit Vitaminen, Spurenelemente oder andere Substanzen geladen werden die Mangelerscheinungen an der zu regeneriende Region Beheben Und so mit die Heilung ermöglichen bzw. beschleuningenGranules according to one of the preceding claims, characterized in that the granules are coated with collagen or liposomes or collagen liposomes and mixed with tetracycline powder and / or statin ( 3 ) contains autogenous material or consists entirely of autogenous material. The liposomes can be loaded with vitamins, trace elements or other substances that deficiency symptoms on the region to be regenerated And thus enable or accelerate the healing Granulat mit Collagen oder Liposome oder Collagenliposomen beschichtet und Tetracyclinpulver und/oder Statingemischt nach einen der voorhergehenden Ansprüche, dadurch gekennzeichnet, das dass Granulat (3) alloplastisches Material enthält oder vollständig aus alloplastischem Material besteht. Die Liposome können mit Vitaminen, Spurenelemente oder andere Substanzen Geladen werden die Mangelerscheinungen an der zu regeneriende Region beheben Und so mit Heilung ermöglichen bzw. beschleunigen.Granules coated with collagen or liposomes or collagen liposomes and tetracycline powder and / or mixed according to one of the preceding claims, characterized in that the granules ( 3 ) contains alloplastic material or consists entirely of alloplastic material. The liposomes can be loaded with vitamins, trace elements or other substances to remedy the deficiency symptoms in the region to be regenerated and thus enable or accelerate healing.
DE200910020707 2009-05-11 2009-05-11 Coated granules for the regeneration of bone material Withdrawn DE102009020707A1 (en)