DE102008046749A1 - Panel i.e. floor panel, manufacturing method, involves imprinting and drying cover layer, and subjecting two side edges of each panel to machine cutting treatment for producing connecting profiles - Google Patents

Panel i.e. floor panel, manufacturing method, involves imprinting and drying cover layer, and subjecting two side edges of each panel to machine cutting treatment for producing connecting profiles Download PDF

Info

Publication number
DE102008046749A1
DE102008046749A1 DE102008046749A DE102008046749A DE102008046749A1 DE 102008046749 A1 DE102008046749 A1 DE 102008046749A1 DE 102008046749 A DE102008046749 A DE 102008046749A DE 102008046749 A DE102008046749 A DE 102008046749A DE 102008046749 A1 DE102008046749 A1 DE 102008046749A1
Authority
DE
Germany
Prior art keywords
layer
panel
abrasion
weight
resistant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
DE102008046749A
Other languages
German (de)
Other versions
DE102008046749B4 (en
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Flooring Technologies Ltd
Original Assignee
Flooring Technologies Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Flooring Technologies Ltd filed Critical Flooring Technologies Ltd
Priority to DE200810046749 priority Critical patent/DE102008046749B4/en
Publication of DE102008046749A1 publication Critical patent/DE102008046749A1/en
Application granted granted Critical
Publication of DE102008046749B4 publication Critical patent/DE102008046749B4/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The method involves grinding an upper side (1) of a large sized timber material board i.e. wood fiberboard. The upper side is primed with a water-based primer to form a primer layer. A color layer is imprinted on a lower side (2) of the board. The color and primer layers are dried. A decoration layer is imprinted on the upper side and dried. A cover layer consisting of acid-hardening lacquer is imprinted on the upper side and dried. The board is partitioned into panels. Two side edges (I, II) of each panel is subjected to machine cutting treatment for producing connecting profiles (8, 9). An independent claim is also included for a panel comprising a decoration layer.

Description

Die Erfindung betrifft ein Verfahren zum Herstellen von Paneelen aus einer großformatigen Holzwerkstoffplatte, insbesondere einer Holzfaserplatte, mit einer Oberseite und einer Unterseite.The The invention relates to a method for producing panels a large-format wood-based panel, in particular a fiberboard, with a top and a bottom.

Ein solches Verfahren ist beispielsweise aus der DE 10 2006 024 305 B3 bekannt. Zur Herstellung eines Paneels, insbesondere eines Wand-, Decken- oder Bodenpaneels aus aufgeteilten Holzwerkstoffplatten mit Seitenkanten, die auf der Ober- und/oder Unterseite ein Dekor aufweisen, das mit einem hitzeaktivierbaren Kunstharz beschichtet ist und der Aufbau aus Holzwerkstoffplatte, Dekor und Kunstharzschicht untereinander verpresst ist, wird mittels einer Prägewalze und mindestens einer Gegendruckwalze eine Struktur in die hitzeaktivierbare Kunstharzschicht auf der Oberseite des Paneels eingeprägt.Such a method is for example from the DE 10 2006 024 305 B3 known. For producing a panel, in particular a wall, ceiling or floor panel of split wood-based panels with side edges, which have a decor on the top and / or bottom, which is coated with a heat-activated resin and the structure of wood-based panel, decor and synthetic resin layer with each other is pressed, is impressed by means of an embossing roller and at least one counter-pressure roller, a structure in the heat-activatable resin layer on top of the panel.

Aus der DE 10 2004 043 355 B4 ist ein Imprägnat bekannt, das ein mit Aminoplastharz gefülltes Dekorpapier aufweist. Auf der Oberseite des Dekorpapiers ist eine abriebfeste Schicht aus Korundpartikeln und einem Aminoplastharz aufgebracht. Darüber ist eine Abdeckschicht aus einem Aminoplastharz angeordnet. Das Imprägnat zeichnet sich dadurch aus, dass in der abriebfesten Schicht grobkörnige Cellulosepartikel mit einem Durchmesser von 70–150 μm und in dem Aminoplastharz der Abdeckschicht feinkörnige Cellulosepartikel mit einem Durchmesser von 10–25 μm eingelagert sind.From the DE 10 2004 043 355 B4 An impregnate is known which has a decorative paper filled with aminoplast resin. On the top of the decorative paper, an abrasion-resistant layer of corundum particles and an aminoplast resin is applied. In addition, a cover layer of an aminoplast resin is arranged. The impregnate is characterized in that in the abrasion-resistant layer coarse-grained cellulose particles with a diameter of 70-150 microns and in the aminoplast resin of the covering layer fine-grained cellulose particles are embedded with a diameter of 10-25 microns.

Aus der DE 102 52 863 B4 ist eine Spanplatte bekannt, die auf der Oberseite ein aufgedrucktes Holz- oder Fliesendekor aufweist, das mit zwei Kunstharzschichten abgedeckt ist, die papierfrei sind. Die unmittelbar auf das Dekor aufgebrachte Kunstharzschicht weist zur Erhöhung der Abriebfestigkeit Korundpartikel auf.From the DE 102 52 863 B4 For example, a chipboard is known which has on top a printed wood or tile decor covered with two layers of synthetic resin which are paperless. The synthetic resin layer applied directly to the decor has corundum particles to increase the abrasion resistance.

Der lagenförmige Papieraufbau herkömmlicher Laminate wird insbesondere bei Fußbodenpaneelen immer mehr durch den direkten Aufdruck des Dekors ergänzt oder substituiert. Neben dem direkten Dekordruck kommt es zunehmend auf die Widerstandsfähigkeit der Oberfläche gegen Abrieb und Kratzer an. Dazu sind die Verschleißschutzschichten vorgesehen, die als korundhaltige Papierlage (Overlay) oder als aushärtbare Lackschicht vorgesehen sind, wobei auch in der Lackschicht optional Korund oder andere abriebfeste Partikel eingebettet sein können. Solche Lacke enthalten meist Initiatoren zur Vernetzung unter Einwirkung energiereicher Strahlen, beispielsweise UV- oder Elektronenstrahlen.Of the layered paper construction of conventional laminates is getting more and more, especially in floor panels the direct imprint of the decor is supplemented or substituted. In addition to the direct decor pressure is increasingly on the resilience the surface against abrasion and scratches. These are the Wear protection layers provided as corundum Paper layer (overlay) or provided as a curable lacquer layer, although optionally in the paint layer corundum or other abrasion resistant Particles can be embedded. Such paints included usually initiators for crosslinking under the action of high energy Radiation, for example UV or electron beams.

Durch die teuren Fotoinitiatoren bei UV-härtbaren Lacken sind diese recht kostenintensiv, was die Fertigungskosten erhöht. Werden elektronenstrahlhärtbare Lacke verwendet, ist bei der Fertigung eine kostenintensive Abschirmung des Elektronenstrahles mittels Stickstoff notwendig. Die Fertigungsanlage ist nicht nur in der Anschaffung teuer, sondern auch die Wartungs- und Instandhaltungskosten sowie der Energieverbrauch sind recht hoch.By the expensive photoinitiators in UV-curable coatings are This is quite expensive, which increases the production costs. If electron beam curable varnishes are used, is included the production of a costly shielding of the electron beam by means of nitrogen necessary. The manufacturing plant is not only expensive to purchase, but also the maintenance and repair costs as well as the energy consumption are quite high.

Für minderwertigere Fußbodenpaneele werden zunehmend auch Folien auf das Substrat, beispielsweise eine Holzwerkstoffplatte, kaschiert. Die Folien werden auch als Finishfolie oder als Folienpaket bezeichnet. Die Folie umfasst eine hartimprägnierte Celluloselage, auf die ein Dekor aufgedruckt ist und die einseitig eine Verschleißschutzschicht aufweist, die als wasserbasierter Acrylat-Lack ausgeführt ist. Dem Acrylat-Lack sind abriebfeste Partikel beigegeben. Zusätzlich ist die Verschleißschutzschicht mit einer Schicht eines säurehärtenden Lackes abgedeckt. Solche Folien können auch zur Herstellung von Wand- und Deckenpaneelen verwendet werden. Dann wird auf die abriebfesten Partikel verzichtet.For Inferior floor panels are increasingly becoming films on the substrate, such as a wood-based panel, laminated. The films are also referred to as a finish foil or foil package. The film comprises a hard-impregnated cellulose layer, on which a decor is printed and the one side a wear protection layer which is designed as a water-based acrylate varnish is. Abrasion-resistant particles are added to the acrylate paint. additionally is the wear protection layer with a layer of a acid-hardening paint covered. Such slides can also be used for the production of wall and ceiling panels be used. Then the abrasion-resistant particles are dispensed with.

Die Herstellung solcher Paneele findet in einem dezentralen Prozess statt. Zunächst muss das Papier hergestellt und dann darauf das Dekor aufgedruckt werden. Anschließend muss das Papier imprägniert und der Verschleißschutz aufgebracht werden und letztendlich diese sodann hergestellte Folie auf die Trägerplatte aufkaschiert werden. Durch die aufwendige Logistik sind die Herstellkosten recht hoch.The Production of such panels takes place in a decentralized process instead of. First, make the paper and then on it the decor will be printed. Then the paper has to be impregnated and the wear protection applied and finally this then produced film on the Carrier plate are laminated. By the elaborate Logistics, the manufacturing costs are quite high.

Von dieser Problemstellung ausgehend soll das Verfahren zur Herstellung von Paneelen aus einer großformatigen Holzwerkstoffplatte vereinfacht werden.From Based on this problem, the process for the preparation of panels made of a large-format wood-based panel be simplified.

Zur Problemlösung zeichnet sich ein gattungsgemäßes Verfahren durch folgende Schritte aus:

  • a) Schleifen der Oberfläche von zumindest der Oberseite,
  • b) Grundieren der Oberseite mit einem wasserbasierten Primer,
  • c) Aufdrucken einer einen Gegenzug ausbildenden Farbschicht auf die Unterseite,
  • d) Trocknen der Primerschicht und der Farbschicht,
  • e) Aufdrucken einer Dekorschicht auf zumindest die Oberseite,
  • f) Trocknen der Dekorschicht,
  • g) Aufdrucken einer aus einem säurehärtenden Lack bestehenden Abdeckschicht auf zumindest die Oberseite,
  • h) Trocknen der Abdeckschicht,
  • i) Aufteilen der Holzwerkstoffplatte in die gewünschte Paneelgröße,
  • j) spanabhebende Bearbeitung mindestens zweier sich gegenüberliegender Seitenkanten jedes Paneels zur Erzeugung von Verbindungsprofilen.
To solve the problem, a generic method is characterized by the following steps:
  • a) grinding the surface of at least the top,
  • b) priming the top with a water-based primer,
  • c) printing on the underside a color layer forming a counter-coating,
  • d) drying the primer layer and the color layer,
  • e) printing a decorative layer on at least the top,
  • f) drying the decorative layer,
  • g) printing a covering layer consisting of an acid-hardening lacquer on at least the upper side,
  • h) drying the cover layer,
  • i) dividing the wood-based panel into the desired panel size,
  • j) machining at least two opposing side edges of each panel to create connection profiles.

Bei diesem Verfahren insbesondere vorteilhaft ist es, dass der Schichtaufbau papierfrei gestaltet ist, sodass die aus dem Papierwachstum an sich entstehenden Nachteile eliminiert werden. Außerdem ist ein solches Paneel wesentlich kostengünstiger herstellbar. Da der Schichtaufbau ohne Verpressen oder Aushärtung der Lacke durch Anwendung energiereicher Strahlung erzeugt werden kann, wird der Herstellungsprozess optimiert. Die Durchlaufzeit derartiger Produkte ist deutlich verkürzt und Fehlereinflüsse, die aus einer dezentralen Herstellung einzelner Aufbauten resultieren, werden beseitigt.at This method is particularly advantageous in that the layer structure paper-free, so that the resulting from paper growth itself Disadvantages are eliminated. Besides, there is such a panel much cheaper to produce. Because of the layer structure without compression or curing of the paints by application of high-energy Radiation can be generated, the manufacturing process is optimized. The lead time of such products is significantly reduced and error, resulting from a decentralized manufacturing individual constructions result are eliminated.

Wenn das Paneel als Fußbodenpaneel verwendet werden soll, wird nach dem Trocknen der Dekorschicht eine aus einem wasserbasierten Acrylat-Lack bestehende abriebfeste Schicht auf zumindest die Oberseite aufgedruckt, die insbesondere vorzugsweise vor dem Aufdrucken der Abdeckschicht getrocknet wird.If the panel is to be used as a floor panel after drying the decorative layer one of a water-based acrylate varnish existing abrasion-resistant layer printed on at least the top, in particular preferably before the printing of the cover layer is dried.

Dem wasserbasierten Acrylat-Lack werden vor dem Aufdrucken abriebfeste Partikel, beispielsweise Korund, mit einer Größe von 50–500 μm beigegeben, die vorzugsweise vor dem Trocknen der abriebfesten Schicht aufgestreut werden. Insbesondere vorteilhaft ist es, wenn die Partikelgröße 220 μm beträgt.the water-based acrylate paint are abrasion resistant before printing Particles, for example corundum, with one size of 50-500 microns added, preferably before be sprinkled on drying the abrasion-resistant layer. Especially advantageous it is when the particle size is 220 microns is.

Das Gesamtgewicht der abriebfesten Partikel beträgt bezogen auf das Gewicht der abriebfesten Schicht vorzugsweise 25–50%, und insbesondere vorzugsweise 30%.The Total weight of the abrasion-resistant particles is based preferably 25-50% by weight of the abrasion resistant layer, and especially preferably 30%.

Zur Erzeugung von Verbindungsprofilen werden die sich gegenüberliegenden Seitenkanten der Holzwerkstoffplatte vorzugsweise spanabhebend bearbeitet.to Generation of connection profiles will be the opposite Side edges of the wood-based panel preferably machined.

Vor dem Aufbringen der Primerschicht wird die Oberseite um etwa 0,1 mm abgeschliffen und dann mit vorzugsweise 10–50 g/m2 Primer beschichtet. Insbesondere vorteilhaft ist es, wenn die Oberseite mit 20 g/m2 Primer beschichtet wird.Before applying the primer layer, the top surface is abraded by about 0.1 mm and then coated with preferably 10-50 g / m 2 primer. It is particularly advantageous if the top is coated with 20 g / m 2 primer.

Die den Gegenzug bildende Farbschicht wird vorzugsweise mit einem Flächegewicht von 10–30 g/m2 aufgedruckt, wobei ein Flächengewicht von 20 g/m2 besonders vor teilhaft ist. Außer als die Dekorschicht kann ein- oder mehrfarbig aufgedruckt sein. Für die Dekorschicht wird vorzugsweise ein Dispersionslack verwendet.The color layer forming the counter-coating is preferably printed with a surface weight of 10-30 g / m 2 , with a weight per unit area of 20 g / m 2 being particularly advantageous. Except as the decorative layer can be printed in one or more colors. For the decorative layer, a dispersion varnish is preferably used.

Die abriebfeste Schicht wird mit einem Flächegewicht von vorzugsweise 60 bis 120 g/m2 und insbesondere Vorzugsweise mit 80 g/m2 aufgedruckt.The abrasion-resistant layer is printed with a weight per unit area of preferably 60 to 120 g / m 2 and in particular preferably 80 g / m 2 .

Vor dem Aufteilen der Paneele wird die Holzwerkstoffplatte vorzugsweise zwischengelagert, insbesondere abgestapelt.In front dividing the panels, the wood-based panel is preferably stored, in particular stacked.

Ein nach dem vorstehenden Verfahren hergestelltes Paneel mit einem Kern aus Holzwerkstoff, insbesondere aus Holzfaser (MDF oder HDF), einer eine Dekorschicht aufweisenden Oberseite, einer mit einem Gegenzug versehenen Unterseite und mit an sich gegenüberliegenden Seitenkanten vorgesehenen, zueinander korrespondierenden Verbindungsprofilen zeichnet sich dadurch aus, dass die Dekorschicht und der Gegenzug aufgedruckt sind und die Dekorschicht von einer Lackschicht abgedeckt ist.One Panel made by the above process with a core made of wood material, in particular of wood fiber (MDF or HDF), one of Decorative layer having top, one provided with a return Bottom and with opposite side edges provided, mutually corresponding connection profiles is characterized by the fact that the decorative layer and the counter-pull are printed on and the decorative layer covered by a lacquer layer is.

Zwischen der Dekorschicht und der Lackschicht ist vorzugsweise eine aus einem wasserbasierten Acrylat-Lack bestehende abriebfeste Schicht angeordnet, die auch aufgedruckt ist.Between the decorative layer and the lacquer layer is preferably one of a water-based acrylate paint existing abrasion-resistant layer arranged which is also printed.

Die ein- oder mehrfarbige Dekorschicht besteht vorzugsweise aus einem Dispersionslack. Unter der Dekorschicht kann eine Primerschicht mit einem Gewicht von 10–50 g/m2, vorzugsweise mit einem Gewicht von 20 g/m2 vorgesehen sein.The single or multi-colored decorative layer preferably consists of a dispersion varnish. Under the decorative layer, a primer layer with a weight of 10-50 g / m 2 , preferably with a weight of 20 g / m 2 may be provided.

Der Gegenzug an der Unterseite des Paneels weist vorteilhaft ein Gewicht von 10 bis 30 g/m2 und insbesondere von 20 g/m2 auf. Die abriebfeste Schicht kann ein Gewicht von 60 bis 120 g/m2, vorzugsweise 80 g/m2 aufweisen. In der abriebfesten Schicht können abriebfeste Partikel, vorzugsweise aus Korund, mit einer Größe von 50–500 μm und insbesondere mit einer Größe von 220 μm vorgesehen werden. Das Gesamtgewicht der Partikel bezogen auf das Lackgewicht der abriebfesten Schicht beträgt vorzugsweise 25–50%, und insbesondere 30%.The counter-pull on the underside of the panel advantageously has a weight of 10 to 30 g / m 2 and in particular of 20 g / m 2 . The abrasion-resistant layer may have a weight of 60 to 120 g / m 2 , preferably 80 g / m 2 . Abrasion-resistant particles, preferably of corundum, with a size of 50-500 μm and in particular with a size of 220 μm can be provided in the abrasion-resistant layer. The total weight of the particles based on the coating weight of the abrasion-resistant layer is preferably 25-50%, and in particular 30%.

Mit Hilfe einer Zeichnung soll ein Ausführungsbeispiel der Erfindung nachfolgend näher erläutert werden.With Help a drawing is an embodiment of the Invention will be explained in more detail below.

Es zeigt:It shows:

1 – die perspektivische Darstellung eines Paneels, 1 The perspective view of a panel,

2 – den Querschnitt durch eine großformatige Holzwerkstoffplatte, 2 - the cross section through a large-format wood-based panel,

3 – die Einzelheit III aus 2. 3 - detail III 2 ,

Die als Trägerplatte dienende Holzwerkstoffplatte 20 ist eine MDF-(medium density fiber) oder HDF-(high density fiber)Platte mit einer Oberseite 1 und einer Unterseite 2. Die einzelnen Schichten werden flüssig auf die Oberseite 1 und die Unterseite 2 aufgetragen. Zunächst wird die Oberseite 1 zur Glättung der Oberfläche um etwa 0,1 mm abgeschliffen. Dann wird auf die Oberseite 1 eine Schicht 4 aus einem wasserbasierten Primer aufgetragen. Gleichzeitig oder in einer weiteren Station wird auf der Unterseite 2 eine den Gegenzug ausbildende Farbschicht 3 aufgetragen, durch die bei der fertiggestellten Platte eine Schüsselung verhindert wird.Serving as a carrier plate wood material board 20 is a MDF (medium density fiber) or HDF (high density fiber) plate with a top surface 1 and a bottom 2 , The individual layers become liquid on top 1 and the bottom 2 applied. First, the top is 1 ground to smooth the surface by about 0.1 mm. Then it's on top 1 a layer 4 applied from a water-based primer. At the same time or in another station will be on the bottom 2 a color layer forming the counterpart 3 applied by the at the finished plat te a bowl is prevented.

Nach dem Trocknen der Primerschicht 4 und der Farbschicht 3 wird auf die Primerschicht 4 eine ein- oder mehrfarbige Dekorschicht 7 aus einem Dispersionslack aufgedruckt, die anschließend getrocknet wird. Bei dem Dispersionslack handelt es sich um eine handelsübliche wasserlösliche Farbe. Auf die Dekorschicht 7 wird anschließend eine aus einem säurehärtenden Lack bestehende Abdeckschicht 6 aufgedruckt. Wenn die Holzwerkstoffplatte 20 dazu vorgesehen ist, dass sie anschließend zu Fußbodenpaneelen aufgeteilt werden soll, wird nach dem Trocknen der Dekorschicht 7 auf diese noch eine aus einem wasserbasierten Acrylat-Lack bestehende abriebfeste Schicht 5 aufgedruckt. Vor dem Aufdrucken der Abdeckschicht 6 wird die abriebfeste Schicht 5 getrocknet. Anschließend wird die Holzwerkstoffplatte 20 in einzelne Paneele gewünschter Größe durch Sägen aufgeteilt.After drying the primer layer 4 and the color layer 3 is on the primer layer 4 a single or multi-colored decorative layer 7 printed from a dispersion varnish, which is then dried. The dispersion paint is a commercially available water-soluble paint. On the decorative layer 7 then becomes a covering layer consisting of an acid-hardening lacquer 6 printed. If the wood-based panel 20 is intended to be subsequently divided into floor panels, is after drying the decorative layer 7 on this still made of a water-based acrylate paint abrasion resistant layer 5 printed. Before printing the cover layer 6 becomes the abrasion resistant layer 5 dried. Subsequently, the wood-based panel 20 divided into individual panels of desired size by sawing.

Nach der Aufteilung der Holzwerkstoffplatte in Paneele gewünschter Größe, werden die sich gegenüberliegenden Seitenkanten I, II spanabhebend, insbesondere fräsend bearbeitet und mit zueinander korrespondierenden Verbindungsprofilen 8, 9 ausgestattet. Bei dem in 1 gezeigten Paneel ist eine einfache Feder-Nut-Profilierung vorgesehen. Die Feder 8 und die Nut 9 können mit integrierten Verriegelungsmitteln versehen sein, sodass zwei Paneele leimlos miteinander verbunden werden können. Eine solche Profilierung ist beispielsweise in der DE 10 2006 048 471 A1 , der EP 1 367 194 A2 oder der EP 1 420 125 A2 offenbart.After the division of the wood-based panel into panels of desired size, the opposite side edges I . II machined, in particular milled processed and with mutually corresponding connection profiles 8th . 9 fitted. At the in 1 shown panel is provided a simple spring-groove profiling. The feather 8th and the groove 9 can be provided with integrated locking means, so that two panels can be connected to each other without glue. Such a profiling is for example in the DE 10 2006 048 471 A1 , of the EP 1 367 194 A2 or the EP 1 420 125 A2 disclosed.

Als Lacke kommen Lacke der Firma La. u. B. Lacke und Beratung GmbH, Brentanostr. 58, D-63755 Alzenau (genannt: Laub) infrage, die folgende Spezifikation aufweisen:
3 K Primer 60-6398As varnishes come coatings from La. u. B. Lacke and Consulting GmbH, Brentanostr. 58, D-63755 Alzenau (called: Laub), which have the following specification:
3K Primer 60-6398

Dieser Primer ist ein Vorstrich, der über zwei Härtungsmechanismen ausgehärtet wird und dem daher sowohl Laub Acid 90-1920 als auch zusätzlich Laub Print Härter 60-31 zugesetzt werden muss. Er wurde vorwiegend für einen Zweischichtaufbau in Kombination mit einem säurehärtenden Decklack entwickelt. Die Überlackierbarkeit mit dem jeweiligen Lacksystem ist in jedem Fall vorab zu prüfen.This Primer is a primer that has two curing mechanisms is cured and therefore both foliage Acid 90-1920 as well as additional foliage Print Hardener 60-31 added must become. He became predominantly for a two-layer construction developed in combination with an acid-hardening topcoat. The recoatability with the respective paint system is in any case to be checked in advance.

Der Primer für die Primärschicht 4 enthält Festkörper von 48 +– 3%. Die Auslaufzeit (4 mm) beträgt 33 +– 5 s.The primer for the primary layer 4 contains solids of 48 + - 3%. The flow time (4 mm) is 33 + - 5 s.

Für die abriebfeste Schicht 5 wird Laub Acid verwendet, dem handelsübliche Partikel 10 aus Korund beigegeben werden. Für die Abdeckschicht 6 wird ebenfalls Laub Acid verwendet. Optional kann auf die Abdeckschicht 6 eine weitere Schicht (nicht gezeigt) mit einer Porenstruktur unter Verwendung von Laub Pore aufgebracht werden. Für die Verwendung der Laub-Lacke ist als Zugabe Laub-Härter vorgesehen.For the abrasion-resistant layer 5 Laub acid is used, the commercial particle 10 be added from corundum. For the cover layer 6 Foliage Acid is also used. Optionally, on the cover layer 6 another layer (not shown) having a pore structure can be applied using foliage pore. For the use of foliage paints foliage hardener is provided as an addition.

Als Dispersionslack für die Dekorschicht 7 kommen handelsübliche wasserlösliche Farben beispielsweise der Firmen Hartmann oder Treffer in Frage.As dispersion varnish for the decorative layer 7 Commercially available water-soluble inks, for example from Hartmann or Hit, come into question.

Da der Lackaufbau nur ein geringes Zugverhalten aufweist, kann die Gegenzugschicht 3 sehr dünn ausgestaltet sein und trotzdem eine Schüsselung wirksam verhindert werden.Since the paint system has only a low tensile behavior, the Gegenzugschicht 3 be designed very thin and yet effectively prevented a bowl.

11
Oberseitetop
22
Unterseitebottom
33
Farbschicht/GegenzugColor layer / return
44
Primerschichtprimer layer
55
abriebfeste Schichtabrasion resistant layer
66
Abdeckschichtcovering
77
Dekorschichtdecorative layer
88th
Profil/FederProfile / spring
99
Profil/NutProfile / groove
1010
abriebfeste Partikel/Korundpartikelabrasion resistant Particles / corundum
2020
Trägerplatte/HolzwerkstoffplatteCarrier plate / wood material board
II
Seitenkanteside edge
IIII
Seitenkanteside edge

ZITATE ENTHALTEN IN DER BESCHREIBUNGQUOTES INCLUDE IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list The documents listed by the applicant have been automated generated and is solely for better information recorded by the reader. The list is not part of the German Patent or utility model application. The DPMA takes over no liability for any errors or omissions.

Zitierte PatentliteraturCited patent literature

  • - DE 102006024305 B3 [0002] - DE 102006024305 B3 [0002]
  • - DE 102004043355 B4 [0003] DE 102004043355 B4 [0003]
  • - DE 10252863 B4 [0004] - DE 10252863 B4 [0004]
  • - DE 102006048471 A1 [0031] DE 102006048471 A1 [0031]
  • - EP 1367194 A2 [0031] - EP 1367194 A2 [0031]
  • - EP 1420125 A2 [0031] - EP 1420125 A2 [0031]

Claims (38)

Verfahren zum Herstellen von Paneelen aus einer großformatigen Holzwerkstoffplatte, insbesondere Holzfaserplatte, mit einer Oberseite (1) und einer Unterseite (2) mit folgenden Schritten: a) Schleifen der Oberfläche von zumindest der Oberseite (1), b) Grundieren der Oberseite (1) mit einem wasserbasierten Primer, c) Aufdrucken einer einen Gegenzug ausbildenden Farbschicht (3) auf die Unterseite (2), d) Trocknen der Primerschicht (4) und der Farbschicht (3), e) Aufdrucken einer Dekorschicht (7) auf zumindest die Oberseite (1), f) Trocknen der Dekorschicht (7), g) Aufdrucken einer aus einem säurehärtenden Lack bestehenden Abdeckschicht (6) auf zumindest die Oberseite (1), h) Trocknen der Abdeckschicht (6), i) Aufteilen der Holzwerkstoffplatte in die gewünschte Paneelgröße, j) spanabhebende Bearbeitung mindestens zweier sich gegenüberliegender Seitenkanten (I, II) jedes Paneels zur Erzeugung von Verbindungsprofilen (8, 9).Process for producing panels from a large-format wood-based panel, in particular wood-fiber panel, with a top side ( 1 ) and a bottom ( 2 ) comprising the following steps: a) grinding the surface of at least the upper side ( 1 ), b) priming the top ( 1 ) with a water-based primer, c) imprinting a color layer forming a counter-coating ( 3 ) on the underside ( 2 ), d) drying the primer layer ( 4 ) and the color layer ( 3 ), e) imprinting a decorative layer ( 7 ) on at least the top ( 1 ), f) drying the decorative layer ( 7 g) printing on a covering layer consisting of an acid-hardening lacquer ( 6 ) on at least the top ( 1 h) drying the cover layer ( 6 i) splitting the wood-based panel into the desired panel size, j) machining at least two opposing side edges (i) I . II ) of each panel for generating connection profiles ( 8th . 9 ). Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass nach dem Trocknen der Dekorschicht (7) eine aus einem wasserbasierten Acrylat-Lack bestehende abriebfeste Schicht (5) auf zumindest die Oberseite (1) aufgedruckt wird.A method according to claim 1, characterized in that after drying the decorative layer ( 7 ) an abrasion-resistant layer consisting of a water-based acrylate lacquer ( 5 ) on at least the top ( 1 ) is printed. Verfahren nach Anspruch 2, dadurch gekennzeichnet, dass die abriebfeste Schicht (5) vor dem Aufdrucken der Abdeckschicht (6) getrocknet wird.Method according to claim 2, characterized in that the abrasion-resistant layer ( 5 ) before printing the cover layer ( 6 ) is dried. Verfahren nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, dass alle sich gegenüberliegenden Seitenkanten (I, II) zur Erzeugung von Verbindungsprofilen (8, 9) spanabhebend bearbeitet werden.Method according to one of claims 1 to 3, characterized in that all opposite side edges ( I . II ) for the generation of connection profiles ( 8th . 9 ) are machined. Verfahren nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, dass die Oberfläche der Oberseite (1) um etwa 0,1 mm abgeschliffen wird.Method according to one of claims 1 to 4, characterized in that the surface of the top ( 1 ) is abraded by about 0.1 mm. Verfahren nach einem oder mehreren der vorstehenden Ansprüche, dadurch gekennzeichnet, dass die Oberseite (1) mit 10 bis 50 g/m2 Primer beschichtet wird.Method according to one or more of the preceding claims, characterized in that the upper side ( 1 ) is coated with 10 to 50 g / m 2 primer. Verfahren nach Anspruch 6, dadurch gekennzeichnet, dass die Oberseite (1) mit 20 g/m2 Primer beschichtet wird.Method according to claim 6, characterized in that the upper side ( 1 ) is coated with 20 g / m 2 primer. Verfahren nach einem oder mehreren der vorstehenden Ansprüche, dadurch gekennzeichnet, dass die den Gegenzug bildende Farbschicht mit einem Flächengewicht von 10 bis 30 g/m2 aufgedruckt wird.Method according to one or more of the preceding claims, characterized in that the color layer forming the counter-coating is printed with a basis weight of 10 to 30 g / m 2 . Verfahren nach Anspruch 8, dadurch gekennzeichnet, dass die Farbschicht (3) mit einem Flächengewicht von 20 g/m2 aufgedruckt wird.Method according to claim 8, characterized in that the color layer ( 3 ) is printed with a basis weight of 20 g / m 2 . Verfahren nach einem oder mehreren der vorstehenden Ansprüche, dadurch gekennzeichnet, dass die Dekorschicht (7) ein- oder mehrfarbig aufgedruckt wird.Method according to one or more of the preceding claims, characterized in that the decorative layer ( 7 ) is printed in one or more colors. Verfahren nach einem oder mehreren der vorstehenden Ansprüche, dadurch gekennzeichnet, dass zum Aufdruck der Dekorschicht (7) ein Dispersionslack verwendet wird.Method according to one or more of the preceding claims, characterized in that for printing the decorative layer ( 7 ) a dispersion varnish is used. Verfahren nach einem oder mehreren der Ansprüche 2 bis 11, dadurch gekennzeichnet, dass die abriebfeste Schicht (5) mit einem Flächengewicht von 60 bis 120 g/m2 aufgedruckt wird.Method according to one or more of claims 2 to 11, characterized in that the abrasion-resistant layer ( 5 ) is printed with a basis weight of 60 to 120 g / m 2 . Verfahren nach Anspruch 12, dadurch gekennzeichnet, dass das Flächengewicht 80 g/m2 beträgt.A method according to claim 12, characterized in that the basis weight is 80 g / m 2 . Verfahren nach einem oder mehreren der Ansprüche 2 bis 13, dadurch gekennzeichnet, dass dem wasserbasierten Acrylat-Lack vor dem Aufdrucken abriebfeste Partikel (10) mit einer Größe von 50–500 μm beigegeben werden.Method according to one or more of claims 2 to 13, characterized in that the water-based acrylate lacquer before printing abrasion-resistant particles ( 10 ) are added with a size of 50-500 microns. Verfahren nach einem oder mehreren der Ansprüche 2 bis 13, dadurch gekennzeichnet, dass vor dem Trocknen auf die abriebfeste Schicht (5) abriebfeste Partikel (10) mit einer Größe von 50 bis 500 μm aufgestreut werden.Method according to one or more of claims 2 to 13, characterized in that before drying on the abrasion-resistant layer ( 5 ) Abrasion-resistant particles ( 10 ) are sprinkled with a size of 50 to 500 microns. Verfahren nach Anspruch 14 oder 15, dadurch gekennzeichnet, dass die Partikelgröße 220 μm beträgt.Method according to claim 14 or 15, characterized that the particle size is 220 microns. Verfahren nach einem der Ansprüche 14 bis 16, dadurch gekennzeichnet, dass das Gesamtgewicht der abriebfesten Partikel (10) bezogen auf das Gewicht der abriebfesten Schicht (5) 25 bis 50% beträgt.Method according to one of claims 14 to 16, characterized in that the total weight of the abrasion-resistant particles ( 10 ) based on the weight of the abrasion-resistant layer ( 5 ) Is 25 to 50%. Verfahren nach Anspruch 17, dadurch gekennzeichnet, dass das Gesamtgewicht der abriebfesten Partikel (10) bezogen auf das Gewicht der abriebfesten Schicht (5) 30% beträgt.A method according to claim 17, characterized in that the total weight of the abrasion-resistant particles ( 10 ) based on the weight of the abrasion-resistant layer ( 5 ) Is 30%. Verfahren nach einem oder mehreren der vorstehenden Ansprüche, dadurch gekennzeichnet, dass die Holzwerkstoffplatte vor dem Aufteilen der Paneele zwischengelagert, insbesondere abgestapelt wird.Method according to one or more of the preceding Claims, characterized in that the wood-based material board stored before dividing the panels, in particular stacked becomes. Paneel mit einem Kern aus Holzwerkstoff, insbesondere aus Holzfaser (MDF oder HDF), einer eine Dekorschicht (7) aufweisenden Oberseite (1), einer mit einem Gegenzug (3) versehenen Unterseite (2) und mit an sich gegenüberliegenden Seitenkanten (I, II) vorgesehenen, zueinander korrespondierenden Verbindungsprofilen (8, 9), wobei die Dekorschicht (7) und der Gegenzug (3) aufgedruckt sind und die Dekorschicht (7) von einer Lackschicht (6) abgedeckt ist.Panel with a core of wood-based material, in particular of wood fiber (MDF or HDF), one of a decorative layer ( 7 ) having top ( 1 ), one with a return ( 3 ) provided underside ( 2 ) and with opposite side edges ( I . II ), mutually corresponding connection profiles ( 8th . 9 ), wherein the decorative layer ( 7 ) and the return ( 3 ) and the decorative layer ( 7 ) of a lacquer layer ( 6 ) is covered. Paneel nach Anspruch 20, dadurch gekennzeichnet, dass zwischen der Dekorschicht (7) und der Lackschicht (6) eine aus einem wasserbasierten Acrylat-Lack bestehende abriebfeste Schicht (5) angeordnet ist.Panel according to claim 20, characterized in that between the decorative layer ( 7 ) and the lacquer layer ( 6 ) an abrasion-resistant layer consisting of a water-based acrylate lacquer ( 5 ) is arranged. Paneel nach Anspruch 21, dadurch gekennzeichnet, dass die abriebfeste Schicht (5) aufgedruckt ist.Panel according to claim 21, characterized in that the abrasion-resistant layer ( 5 ) is printed. Paneel nach einem der Ansprüche 20 bis 22, dadurch gekennzeichnet, dass unter der Dekorschicht (7) eine Primerschicht (4) angeordnet ist.Panel according to one of claims 20 to 22, characterized in that below the decorative layer ( 7 ) a primer layer ( 4 ) is arranged. Paneel nach Anspruch 23, dadurch gekennzeichnet, dass die Primerschicht (4) ein Gewicht von 10 bis 50 g/m2 aufweist.Panel according to claim 23, characterized in that the primer layer ( 4 ) has a weight of 10 to 50 g / m 2 . Paneel nach Anspruch 24, dadurch gekennzeichnet, dass die Primerschicht (4) ein Gewicht von 20 g/m2 aufweist.Panel according to claim 24, characterized in that the primer layer ( 4 ) has a weight of 20 g / m 2 . Paneel nach einem oder mehreren der Ansprüche 20 bis 25, dadurch gekennzeichnet, dass der Gegenzug (3) ein Gewicht von 10 bis 30 g/m2 aufweist.Panel according to one or more of claims 20 to 25, characterized in that the counter-pull ( 3 ) has a weight of 10 to 30 g / m 2 . Paneel nach Anspruch 26, dadurch gekennzeichnet, dass der Gegenzug (3) ein Gewicht von 20 g/m2 aufweist.Panel according to claim 26, characterized in that the counter-pull ( 3 ) has a weight of 20 g / m 2 . Paneel nach einem der Ansprüche 20 bis 27, dadurch gekennzeichnet, dass die abriebfeste Schicht (5) ein Gewicht von 60 bis 120 g/m2 aufweist.Panel according to one of claims 20 to 27, characterized in that the abrasion-resistant layer ( 5 ) has a weight of 60 to 120 g / m 2 . Paneel nach Anspruch 28, dadurch gekennzeichnet, dass die abriebfeste Schicht (5) ein Gewicht von 80 g/m2 aufweist.Panel according to claim 28, characterized in that the abrasion-resistant layer ( 5 ) has a weight of 80 g / m 2 . Paneel nach einem oder mehreren der Ansprüche 21 bis 29, dadurch gekennzeichnet, dass in der abriebfesten Schicht (5) abriebfeste Partikel (10) eingebettet sind.Panel according to one or more of claims 21 to 29, characterized in that in the abrasion-resistant layer ( 5 ) Abrasion-resistant particles ( 10 ) are embedded. Paneel nach Anspruch 30, dadurch gekennzeichnet, dass die abriebfesten Partikel (10) aus Korund sind.Panel according to claim 30, characterized in that the abrasion-resistant particles ( 10 ) are made of corundum. Paneel nach Anspruch 30 oder 31, dadurch gekennzeichnet, dass die Partikel (10) eine Größe von 50 bis 500 μm aufweisen.Panel according to claim 30 or 31, characterized in that the particles ( 10 ) have a size of 50 to 500 microns. Paneel nach Anspruch 32, dadurch gekennzeichnet, dass die Partikel (10) eine Größe von 220 μm aufweisen.Panel according to claim 32, characterized in that the particles ( 10 ) have a size of 220 microns. Paneel nach einem oder mehreren der Ansprüche 30 bis 33, dadurch gekennzeichnet, dass das Gesamtgewicht der Partikel (10) bezogen auf das Lackgewicht der abriebfesten Schicht 25 bis 50% beträgt.Panel according to one or more of claims 30 to 33, characterized in that the total weight of the particles ( 10 ) Based on the paint weight of the abrasion-resistant layer is 25 to 50%. Paneel nach Anspruch 34, dadurch gekennzeichnet, dass das Gesamtgewicht der Partikel (10) bezogen auf das Lackgewicht der abriebfesten Schicht (5) 30% beträgt.Panel according to Claim 34, characterized in that the total weight of the particles ( 10 ) based on the paint weight of the abrasion-resistant layer ( 5 ) Is 30%. Paneel nach einem oder mehreren der Ansprüche 20 bis 35, dadurch gekennzeichnet, dass die Dekorschicht (7) aus einem Dispersionslack besteht.Panel according to one or more of claims 20 to 35, characterized in that the decorative layer ( 7 ) consists of a dispersion varnish. Paneel nach einem oder mehreren der Ansprüche 20 bis 36, dadurch gekennzeichnet, dass die Dekorschicht (7) ein- oder mehrfarbig ist.Panel according to one or more of claims 20 to 36, characterized in that the decorative layer ( 7 ) is one or more colors. Paneel nach einem oder mehreren der Ansprüche 21 bis 37, dadurch gekennzeichnet, dass das Paneel ein Fußbodenpaneel ist.Panel according to one or more of the claims 21 to 37, characterized in that the panel is a floor panel is.
DE200810046749 2008-09-11 2008-09-11 Process for the manufacture of panels from a large-format wood-based panel Expired - Fee Related DE102008046749B4 (en)